AUTHOR=Xu Zhirong , Xu Zihui , Tao Ran , Mao Liangchen , Zhan Jing , Xiao Junfeng , Yu Tao TITLE=Combustion and Thermal Properties of Flame Retardant Polyurethane Foam With Ammonium Polyphosphate Synergized by Phosphomolybdic Acid JOURNAL=Frontiers in Materials VOLUME=9 YEAR=2022 URL=https://www.frontiersin.org/journals/materials/articles/10.3389/fmats.2022.944368 DOI=10.3389/fmats.2022.944368 ISSN=2296-8016 ABSTRACT=

Phosphomolybdic acid (PMA) as a synergist was added into polyurethane (PU) rigid foam with ammonium polyphosphate (APP) to improve its flame retardancy and thermal stability. The combustion performance of PU was studied by limiting oxygen index (LOI), UL-94, and a cone calorimeter. The thermal degradation behavior of PU was determined by thermogravimetric analysis (TG) and thermogravimetric infrared spectroscopy (TG-IR). Experimental results showed that the introduction of PMA could further improve the flame retardant performance of PU/APP composites and significantly increase the amount of carbon residue at high temperatures. Adding 3wt% PMA to PU containing 12wt% APP could make the foam pass UL-94 V-0, increase the carbon residue at 800°C by 69.16% in the air atmosphere, and decrease the THR by 24.62% compared to those of PU/15APP. TG-IR results showed that the presence of PMA reduced the production of small-molecule gas-phase products. As for the mechanical properties of PU composites, the addition of PMA influences their density and compressive strength obviously. The results suggest that PMA and APP have good synergistic flame retardancy on PU and can reduce its fire risk.