AUTHOR=Zhang Jin , Zeng Huaqiang , Wang Cheng , Tang Zibo 

TITLE=Effect of Al3Zr Dispersoid on Microstructure and Mechanical Properties of Al-Cu-Li Alloy During Composite Spinning-Extrusion Forming

JOURNAL=Frontiers in Materials

VOLUME=9

YEAR=2022

URL=https://www.frontiersin.org/journals/materials/articles/10.3389/fmats.2022.822589

DOI=10.3389/fmats.2022.822589

ISSN=2296-8016

ABSTRACT=<p>The regulation of blank microstructure is the key to manufacturing high-quality ring cylinder by composite spinning - extrusion forming. In this paper, the precipitation morphologies of three Al<sub>3</sub>Zr dispersions were obtained by changing the heat treatment process, and their effects on the microstructure and mechanical properties of Al-Cu-Li alloy ring cylinder were investigated. The results show that the microstructure and mechanical properties of ring cylinder are affected by the different precipitation distribution of Al<sub>3</sub>Zr dispersoids in the blank. When the Al<sub>3</sub>Zr dispersoids precipitated and dispersed, the cracking of ring cylinder was eliminated, the thickness of coarse-grained layer decreases obviously, and the elongation is increased by 33.5%. In the T83 state, the average length of the T<sub>1</sub> phase decreased from 100.3 to 77.5 nm, while the tensile strength and yield strength of ring cylinder increased by 16 and 20 MPa, respectively.</p>