Mriganka Singh
Chih Wei Chu
Annie Ng- 1Research Center for Applied Sciences, Academia Sinica, Taipei, Taiwan
- 2Department of Electrical and Computer Engineering, School of Engineering and Digital Sciences, Nazarbayev University, Nursultan, Kazakhstan
Nowadays, the power conversion efficiency of organometallic mixed halide perovskite solar cells (PSCs) is beyond 25%. To fabricate highly efficient and stable PSCs, the performance of metal oxide charge transport layers (CTLs) is one of the key factors. The CTLs are employed in PSCs to separate the electrons and holes generated in the perovskite active layer, suppressing the charge recombination rate so that the charge collection efficiency can be increased at their respective electrodes. In general, engineering of metal oxide electron transport layers (ETLs) is found to be dominated in the research community to boost the performance of PSCs due to the resilient features of ETLs such as excellent electronic properties, high resistance to thermal temperature and moisture, ensuring good device stability as well as their high versatility in material preparation. The metal oxide hole transport layers in PSCs are recently intensively studied. The performance of PSCs is found to be very promising by using optimized hole transport materials. This review concisely discusses the evolution of some prevalent metal oxide charge transport materials (CTMs) including TiO2, SnO2, and NiOx, which are able to yield high-performance PSCs. The article begins with introducing the development trend of PSCs using different types of CTLs, pointing out the important criteria for metal oxides being effective CTLs, and then a variety of preparation methods for CTLs as employed by the community for high-performance PSCs are discussed. Finally, the challenges and prospects for future research direction toward scalable metal oxide CTM-based PSCs are delineated.
Introduction
In the 21st century, we are living in an energy-driven world. Sustainability in energy generation is one of the most challenging issues to satisfy the ever-increasing energy demands. Solar energy is readily available in nature, which exhibits a great potential to address the global energy challenge. However, the widespread use of solar energy requires the development of cost-effective and high-performance photovoltaics (PVs) for efficient energy conversion from solar to electric energy. The emergence of organometallic mixed halide perovskite solar cells (PSCs) resulted in an important breakthrough in PV technology. The recently announced record power conversion efficiency (PCE) values of single-junction PSCs and perovskite-based monolithic tandem devices are 25.5 and 29.5%, respectively (The National Renewable Energy Laboratory [NREL], 2021), which outperform other thin-film PV technologies (e.g., CIGS and CdTe) and are comparable to well-established solar technologies such as crystalline silicon photovoltaics (PCE ∼26.1%). Such impressive device efficiency of PSCs is owing to inherent perovskite properties such as large absorption coefficients, adjustable bandgaps, low exciton binding energy, large carrier diffusion lengths, and high charge mobilities (Xing et al., 2013; Wang et al., 2015). However, a number of challenges such as device long-term stability, hysteresis effect, toxicity of lead, and scalable difficulties still remain in the community (Djurišić et al., 2016; Djurišić et al., 2017; Li et al., 2018; Li et al., 2020). In general, five major areas are being investigated to come up with possible solutions for the problems mentioned above. They include (i) perovskite composition and crystal structure (Luo and Daoud, 2016; Mitchell et al., 2017), (ii) engineering of perovskite growth methods (Ng et al., 2015, 2018; Babayigit et al., 2018; Shen et al., 2018; Hu et al., 2020a), (iii) optimization of carrier transport materials and interfaces (Liu et al., 2017; Hu et al., 2020b,c; Wang et al., 2021), (iv) device architectures (Hanmandlu et al., 2018; Ren et al., 2018; Maxim et al., 2020; Shalenov et al., 2020), and (v) encapsulation (Dong et al., 2016; Fu et al., 2019; Emami et al., 2020). Some comprehensive review papers on those topics have also been published (Jiang et al., 2018; Sajid et al., 2018; Ouyang et al., 2019; Hanmandlu et al., 2020; Hu et al., 2020a; Zhou et al., 2020).
This article aims to highlight the development of the predominant metal oxides—TiO2, SnO2, and NiOx—using the charge transporting layers (CTLs) in PSCs. Special attentions are placed on these three types of metal oxides as the state-of-the-art PSCs with record-breaking efficiencies are usually associated with these metal oxide CTLs. A brief review on representative research works on PSCs has been done, indicating the highest achievable PCE for different CTL-based PSCs at different stages of time. The important criteria in selecting metal oxides as CTLs are emphasized. Varieties of effective preparation methods for metal oxide CTLs have been summarized, and their advantages and shortcomings in terms of processing conditions and possibility of future large-scale manufacturing are discussed. This work will provide a direct insight into the PV community for further optimizing of CTLs, which will be one of the critical steps for approaching practical PSCs in the commercial market.
The Efficiency Evolution of PSCs Using Different Metal Oxide CTLs
Starting from 2009, the group of Miyasaka demonstrated the photovoltaic properties of using perovskite in the dye-sensitized solar cell by employing mesoporous TiO2, exhibiting a PCE of 3.8% (Kojima et al., 2009). In early 2012, the group of Park reported a PCE of 9.7% of PSCs by introducing a sub-micrometer-thick layer of TiO2 and solid-state hole transporting materials (HTMs) (Kim et al., 2012). In the same year, a PCE more than 10% was reported by the group of Snaith (Lee et al., 2012). In 2013, the group of Grätzel demonstrated high-performance PSCs fabricated by the sequential deposition method with a certified PCE of 14.1% (Burschka et al., 2013). In the following years, the group of Seok reported a dramatical improvement in the device performance of PSCs by using different engineering approaches such as solvent engineering (certified as 16.20%) (Jeon et al., 2014), compositional engineering (certified as 17.9%) (Jeon et al., 2015), and intramolecular exchange (20.1% certified PCE) (Yang et al., 2015c). In 2016, the group of Grätzel reported the use of triple cations in perovskite materials, yielding good device reproducibility and improved device stability, leading to a high PCE of 21.1% (Saliba et al., 2016). Nowadays, the highest certified PCE as reported in literature for PSCs based on TiO2 electron-transporting layer (ETL) is 24.64% (Jeong et al., 2020). The TiO2-based ETLs are popular to be used since the early stage of PSCs owing to its high versatility of preparation techniques as well as attributing to the evolution of the architecture from the dye-sensitized solar cells. The representative research works using TiO2 as the ETL in PSCs with their achieved PCEs are summarized in Figure 1 as indicated in solid circles. Along with such a tremendous improvement in device performance, a compact layer of tin oxide (SnO2) has been demonstrated as an alternative for ETL. First, Ma et al., 2017 reported a high-temperature processing compact SnO2 ETL prepared by the conversion of SnCl2⋅2H2O precursor to SnO2 using a sol-gel method for CH3NH3PbI3-based PSCs, showing a PCE of 7.43% (Dong et al., 2015). The group of Dai and Kuang also reported a high-temperature processing SnO2 mesoporous ETL and as-synthesized colloidal solution, respectively, followed by TiCl4 surface treatment for CH3NH3PbI3-based PSCs, exhibiting an improvement in their champion device efficiency of 10.18 (Li et al., 2015) and 14.69% (Rao et al., 2015), respectively. However, at that time, the PCEs of SnO2-based PSCs are still lower than those of TiO2-based PSCs due to the introduction of a large amount of trap states during the high-temperature processing (Ke et al., 2015). The important breakthrough in achieving high device efficiency for SnO2-based PSCs was from 2015. The group of Fang firstly introduced low-temperature processing for preparing SnO2 compact layer based on the sol-gel method using SnCl2⋅2H2O as the precursor to achieve a high PCE of 17.21% for CH3NH3PbI3-based PSCs (Ke et al., 2015). Then, the group of You reported a PCE of 20.54% (certified as 19.9%), which was a record-high value in 2016 for (FAPbI3)X (MAPbBr3)1–X-based PSCs with a low-temperature processing SnO2 ETL prepared from commercially available SnO2 colloid solution (Jiang et al., 2016). In the same year, the group of Hagfeldt demonstrated a low-temperature chemical bath deposition for preparing SnO2 compact layer as ETL used in Cs-containing mixed halide-based PSCs, yielding a stabilized PCE of 20.7% (Anaraki et al., 2016). In 2017, the group of You updated the champion PCE to 21.6% (certified as 20.9%) using low-temperature processing SnO2 in (FAPbI3)1–X (MAPbBr3)-based PSCs (Jiang et al., 2017). The representative research works using SnO2 as the ETL in PSCs with their achieved PCEs are summarized in Figure 1 as indicated in solid squares. On the other hand, metal oxides based on NiOx have been commonly used as HTMs for PSCs. In 2014, Tian et al. (2014) firstly introduced the p-type NiO mesoporous for perovskite-sensitized solar cells, achieving a PCE of 1.5%. The group of Ahmadi demonstrated NiOx/Ni double layer as HTL deposited by the sputtering process in a planar n-i-p structure for PSCs, yielding a PCE of 7.28% (Abdollahi Nejand et al., 2015). In 2015, the group of Han employed a 10–20 nm NiO compact layer along with mesoporous Al2O3 scaffold as HTM in p-i-n-based PSCs, obtaining a promising efficiency of 13.5% (Chen et al., 2015a). The group of Wang reported using NiOx HTM in mesoporous n-i-p-based PSCs with a further enhanced PCE to 15.03% (Cao et al., 2015). Li et al. (2017) applied sputtered NiOx for planar PSCs, which exhibit a champion PCE of 18.5%. Furthermore, introduction of dopants, commonly Li (Qiu et al., 2017), Co (Natu et al., 2012), Mg (Chen et al., 2015b), Cu (Chen et al., 2018), Cs (Singh et al., 2020), etc., in NiOx can further enhance the charge transport properties due to improved carrier conductivity as well as better energy level alignment across the interface of perovskite and HTL. The group of He and Lei doped NiOx with Cs and Cu, yielding a PCE of 19.35 (Chen et al., 2017) and 20.5% (Yue et al., 2017) for planar p-i-n-based PSCs, respectively. Recently, a latest high PCE of 21.6% was achieved for NiOx-based PSCs in a p-i-n structure after passivating the perovskite/ETL by using CdxZn1–xSeyS1–y quantum dots (Chen et al., 2020). The representative works for NiOx-based PSCs are summarized in Figure 1 and indicated in solid triangles.
Figure 1. The evolution of perovskite solar cell using various metal oxide charge transport layers.
The Criteria of Effective Metal Oxide CTLs
The appropriate energy band alignment between CTLs and the perovskite absorbing layer is one of the fundamental criteria to ensure efficient charge extraction in PSCs. The conduction band minimum (CBM) of ETL is slightly lower than the conduction band of the perovskite, while the valence band maximum (VBM) of HTL is slighly higher than the valence band of the pervoskite so that the CTLs can extract the corresponding charge carriers readily. Meanwhile, the energy barrier between the VBM of ETL and perovskite (and barrier between CBM of HTL and perovskite) is sufficiently large to block the counter carriers generated from the perovskite layer, suppressing the opportunity of charge recombination within the devices. The built-in potential (Vbi) can be influecend by the types of CTMs and the interfacial quality between the CTL and perovskite (Lin et al., 2017; Shin et al., 2019). The larger Vbi of devices enables PSCs to have a stronger ability to separate charges and transport and collect photo-generated carriers, yielding a higher VOC. A variety of research works have demonstrated that minimizing the interfacial charge recombination between CTL and perovskite layer can effectively enhance the VOC of PSCs (Jung et al., 2019; Kaneko et al., 2019; Aidarkhanov et al., 2020). Carrier mobility is another critical factor affecting the charge transport properties. Carrier mobility should be high to avoid charge accumulation at the interfaces of CTL/perovskite. The bandgap of CTMs should be wide and possess small refractive indexes so that the amount of visible light penetrating through the CTL to the perovskite absorber layer in the PSCs can be maximized.
The morphology of CTLs should be controlled well in PSCs. The underlying ETL or HTL will determine the morphology of the perovskite film deposited on the top of CTLs for n-i-p or p-i-n device structures, respectively. It is known that the optimized morphology of the CTL-coated substrate can assist in the crystallization of the subsequent depositing perovskite layer and improve the perovskite film coverage on the CTL, inhibiting the formation of pinholes to prevent the introduction of undesired shunt paths in PSCs (Ng et al., 2016; Wang et al., 2019). Furthermore, the interfacial quality between the CTL and perovskite, which is of significant importance to determine the PCE and stability of PSCs, is strongly influenced by the surface morphology of CTLs. Intensive research works have exhibited different strategies to passivate the defects, which likely concentrate at material interfaces to suppress charge recombination and hysteresis effect (Shao and Loi, 2020). Meanwhile, the interface between the CTL and conductive electrode should also be optimized for forming of a good ohmic contact for PSCs (Babaei et al., 2020; Tseng et al., 2020).
It is noteworthy that metal oxide materials used as CTLs should be insensitive to ultraviolet light and possess very low photocatalytic effect in order to maintain a long-term stability of PSCs operating under strong sunlight. Metal oxide CTLs, unlike organic materials such as the commonly used PEDOT:PSS HTL, are usually not hygroscopic, which are more robust to moisture, allowing them to be the protection layers and preventing the perovskite active layer from degradation in the humid ambient air. Nowadays, metal oxide CTLs have shown their outstanding chemical stability, which is one of the essential factors for achieving long-lifetime PSCs for future commercialization (You et al., 2016; Lei et al., 2019; Singh et al., 2019; Thambidurai et al., 2020). Figure 2 indicates the general properties of three different CTMs as discussed in this work.
Figure 2. Schematic illustrations of the energy bandgap of metal oxide charge transport materials and their carrier mobility (Jiang et al., 2018; Napari et al., 2020) in the bulk materials.
Preparation Methods for Metal Oxide CTLs
Solution–Process Methods
The solution process is a commonly used method for depositing a wide range of metal oxides in thin films and different nanostructures. This method is cost-effective and vacuum-free and allows low-temperature processing. In general, most of the metal oxide CTLs employed in PSCs are deposited by spin-coating processes. Other common solution techniques include sol-gel methods (Wojciechowski et al., 2014; Zhu et al., 2014; Ke et al., 2015), sono-chemical (Rashad et al., 2014), chemical precipitation (Ghosh et al., 2006), spray pyrolysis (Yue et al., 2017), chemical combustion (Jung et al., 2015), chemical bath deposition (Xia et al., 2008), etc. A number of comprehensive reviews on solution-processed metal oxide CTLs for application in solar cells have been published in the community (Jiang et al., 2017; Cao et al., 2018; Elseman et al., 2020b).
Atomic Layer Deposition
Atomic layer deposition (ALD) is another method to prepare metal oxide CTLs with the film thickness precisely controlled at the atomic scale with excellent uniformity (Meng et al., 2011). Plenty of works have previously exhibited that ALD method is capable of forming high-quality metal oxides for PSC applications (Dong et al., 2014; Kim et al., 2016; Wang et al., 2016). The highest PCE of PSCs with metal oxide CTLs (using SnO2) formed by ALD was over 20%, along with a high VOC of 1.23 V (Correa-Baena et al., 2017).
Mechanosynthesis for Low-Dimensional Metal Oxides
Preparation of metal oxides by physical grinding methods has been used in organic solar cells and PSCs (Huang et al., 2012; Singh et al., 2018). The grinding process is clean, has low cost, and has high yield for mass production, which can produce high-level-purity and high-level-crystallinity metal oxide nanoparticles with controllable size and shape while keeping their intrinsic properties (Elseman et al., 2016; Singh et al., 2018). Grinding is a high-energy wet milling process where three-dimensional materials are broken down into lower-dimensional materials such as nanoparticles, nanorods, nanobelts, nanosheets, and nanofibers via controlling the milling conditions (solvents, temperature, and milling period) (Ibrahem et al., 2014; Ding et al., 2017). This method has been recently demonstrated for preparing TiO2, SnO2, and NiOx CTLs in PSCs (Singh et al., 2018, 2019, 2020). The as-prepared metal oxide nanomaterials can form a compact CTL in PSCs by low-temperature processing methods such as spin-coating the nanomaterial dispersion solution (Singh et al., 2018), which allows the fabrication of devices on flexible substrates or preparation of metal oxides on top of the perovskite layer without introduction of thermal degradation.
Other Deposition Methods
There are other effective deposition methods to prepare the metal oxides for PSCs. Electrodeposition (ED) is one of cost-effective and scalable deposition processes with controllable film thickness. The group of Wei employed the technique of ED to prepare an ultrathin film of TiO2 layer, yielding the PSC with a PCE of 13.6% (Su et al., 2015). In addition, other Physical vapor deposition (PVD) methods have been used to deposit the metal oxide CTLs such as magnetron sputtering (Yang et al., 2015a), pulsed layer deposition (Yang et al., 2016), and e-beam evaporation (Ma et al., 2017). The metal oxide CTL deposition route can be evaluated based on the cost and temperature. PVD and chemical vapor deposition (CVD) routes are regarded as high-cost methods due to their high-power consumption during the deposition process. There are a variety of deposition methods classified under CVD and PVD, such as thermal evaporation, pulsed laser deposition, DC and RF sputtering, plasma-enhanced CVD, metal-organic CVD, and low-pressure CVD. Compared to the techniques of PVD and CVD, chemical solution deposition is cheaper and more accessible. The chemical solution deposition process is classified into different types such as chemical bath deposition, spin-coating, dip coating, screen printing, and spray pyrolysis. The common deposition routes for metal oxide CTLs are classified in terms of the cost and the required temperature for processing, which are shown in Table 1.
Table 1. Classification of some common preparation methods for charge transport layers (CTLs) in terms of cost and processing temperatures.
Perspective
The stability of PSCs can be enhanced by incorporating metal oxide CTLs for both ETL and HTL in the same device. However, nowadays, device stability remains a challenge since the majority of PSCs employ metal oxide CTL as either ETL or HTL while using organic or fullerene-based materials as the counter-CTL. For PSCs with all-inorganic CTLs, the processing temperatures of the metal oxide layer, which is located above the perovskite, usually should be below 100°C to prevent the thermal decomposition of the perovskite absorber. Spin-coating of a dispersion solution containing pre-synthesized metal oxide nanostructures on top of the perovskite is one of the possible techniques to yield metal oxide CTL at a low temperature. Considering the commercial standards for practical PSCs, the preparation methods for metal oxide CTLs should be cost-effective and compatible with low-processing temperature for flexible substrates as well as scalable for large solar modules. The mechanical flexibility of metal oxide CTLs should be also carefully investigated together with the perovskite absorber and flexible substrates during the blending process. Meanwhile, the interfacial engineering between the perovskite absorber and the CTL should be considered as well to modify the interface properties and passivate the defects, which is an important strategy to enhance device efficiency and stability.
Data Availability Statement
The original contributions presented in the study are included in the article/supplementary material, further inquiries can be directed to the corresponding author/s.
Author Contributions
MS conceived the idea. MS and AN wrote the manuscript. AN and CC were involved in the manuscript discussion and correction. All authors contributed to the article and approved the submitted version.
Funding
CC thanks the MOST of Taiwan (grant no. MOST-107-2221-E-001-007-MY3) and Academia Sinica (AS-SS-109-05) for financial support. AN thanks the Scientific Research Grant from the Ministry of Education and Science of the Republic of Kazakhstan (grant no. AP08856931), the Nazarbayev University (grant nos. 110119FD4506 and 021220CRP0422), and the social policy grant.
Conflict of Interest
The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.
References
Abdollahi Nejand, B., Ahmadi, V., and Shahverdi, H. R. (2015). New physical deposition approach for low cost inorganic hole transport layer in normal architecture of durable perovskite solar cells. ACS Appl. Mater. Interfaces 7, 21807–21818. doi: 10.1021/acsami.5b05477
Aidarkhanov, D., Ren, Z., Lim, C.-K., Yelzhanova, Z., Nigmetova, G., Taltanova, G., et al. (2020). Passivation engineering for hysteresis-free mixed perovskite solar cells. Sol. Energy Mater. Sol. Cells 215:110648. doi: 10.1016/j.solmat.2020.110648
Anaraki, E. H., Kermanpur, A., Steier, L., Domanski, K., Matsui, T., Tress, W., et al. (2016). Highly efficient and stable planar perovskite solar cells by solution-processed tin oxide. Energy Environ. Sci. 9, 3128–3134. doi: 10.1039/C6EE02390H
Babaei, A., Zanoni, K. P., Gil-Escrig, L., Pérez-Del-Rey, D., Boix, P. P., Sessolo, M., et al. (2020). Efficient vacuum deposited pin perovskite solar cells by front contact optimization. Front. Chem. 7:936. doi: 10.3389/fchem.2019.00936
Babayigit, A., D’haen, J., Boyen, H.-G., and Conings, B. (2018). Gas quenching for perovskite thin film deposition. Joule 2, 1205–1209. doi: 10.1016/j.joule.2018.06.009
Baena, J. P. C., Steier, L., Tress, W., Saliba, M., Neutzner, S., Matsui, T., et al. (2015). Highly efficient planar perovskite solar cells through band alignment engineering. Energy Environ. Sci. 8, 2928–2934. doi: 10.1039/C5EE02608C
Burschka, J., Pellet, N., Moon, S.-J., Humphry-Baker, R., Gao, P., Nazeeruddin, M. K., et al. (2013). Sequential deposition as a route to high-performance perovskite-sensitized solar cells. Nature 499, 316–319. doi: 10.1038/nature12340
Cao, J., Wu, B., Chen, R., Wu, Y., Hui, Y., Mao, B. W., et al. (2018). Efficient, hysteresis-Free, and stable perovskite solar cells with ZnO as electron-transport layer: effect of surface passivation. Adv. Mater. 30:1705596. doi: 10.1002/adma.201705596
Cao, K., Zuo, Z., Cui, J., Shen, Y., Moehl, T., Zakeeruddin, S. M., et al. (2015). Efficient screen printed perovskite solar cells based on mesoscopic TiO2/Al2O3/NiO/carbon architecture. Nano Energy 17, 171–179. doi: 10.1016/j.nanoen.2015.08.009
Chen, W., Liu, F. Z., Feng, X. Y., Djurišić, A. B., Chan, W. K., and He, Z. B. (2017). Cesium doped NiOx as an efficient hole extraction layer for inverted planar perovskite solar cells. Adv. Energy Mater. 7:1700722. doi: 10.1002/aenm.201700722
Chen, W., Pang, G., Zhou, Y., Sun, Y., Liu, F.-Z., Chen, R., et al. (2020). Stabilizing n-type hetero-junctions for NiO x based inverted planar perovskite solar cells with an efficiency of 21.6%. J. Mater. Chem. A 8, 1865–1874. doi: 10.1039/c9ta12368g
Chen, W., Wu, Y., Fan, J., Djurišić, A. B., Liu, F., Tam, H. W., et al. (2018). Understanding the doping effect on NiO: toward high-performance inverted perovskite solar cells. Adv. Energy Mater. 8:1703519. doi: 10.1002/aenm.201703519
Chen, W., Wu, Y., Liu, J., Qin, C., Yang, X., Islam, A., et al. (2015a). Hybrid interfacial layer leads to solid performance improvement of inverted perovskite solar cells. Energy Environ. Sci. 8, 629–640. doi: 10.1039/C4EE02833C
Chen, W., Wu, Y., Yue, Y., Liu, J., Zhang, W., Yang, X., et al. (2015b). Efficient and stable large-area perovskite solar cells with inorganic charge extraction layers. Science 350, 944–948. doi: 10.1126/science.aad1015
Correa-Baena, J.-P., Tress, W., Domanski, K., Anaraki, E. H., Turren-Cruz, S.-H., Roose, B., et al. (2017). Identifying and suppressing interfacial recombination to achieve high open-circuit voltage in perovskite solar cells. Energy Environ. Sci. 10, 1207–1212. doi: 10.1039/C7EE00421D
Ding, J., Abbas, S. A., Hanmandlu, C., Lin, L., Lai, C.-S., Wang, P.-C., et al. (2017). Facile synthesis of carbon/MoO3 nanocomposites as stable battery anodes. J. Power Sources 348, 270–280. doi: 10.1016/j.jpowsour.2017.03.007
Djurišić, A., Liu, F., Ng, A. M., Dong, Q., Wong, M. K., Ng, A., et al. (2016). Stability issues of the next generation solar cells. Phys. Status Solidi Rapid Res. Lett. 10, 281–299. doi: 10.1002/pssr.201600012
Djurišić, A., Liu, F., Tam, H., Wong, M., Ng, A., Surya, C., et al. (2017). Perovskite solar cells-An overview of critical issues. Prog. Quantum Electron. 53, 1–37. doi: 10.1016/j.pquantelec.2017.05.002
Dong, Q., Liu, F., Wong, M. K., Tam, H. W., Djurišić, A. B., Ng, A., et al. (2016). Encapsulation of perovskite solar cells for high humidity conditions. ChemSusChem 9, 2597–2603. doi: 10.1002/cssc.201600868
Dong, Q., Shi, Y., Wang, K., Li, Y., Wang, S., Zhang, H., et al. (2015). Insight into perovskite solar cells based on SnO2 compact electron-selective layer. J. Phys. Chem. C 119, 10212–10217. doi: 10.1021/acs.jpcc.5b00541
Dong, X., Hu, H., Lin, B., Ding, J., and Yuan, N. (2014). The effect of ALD-Zno layers on the formation of CH3NH3PbI3 with different perovskite precursors and sintering temperatures. Chem. Commun. 50, 14405–14408. doi: 10.1039/C4CC04685D
Dou, X., Sabba, D., Mathews, N., Wong, L. H., Lam, Y. M., and Mhaisalkar, S. (2011). Hydrothermal synthesis of high electron mobility Zn-doped SnO2 nanoflowers as photoanode material for efficient dye-sensitized solar cells. Chem.Mater. 23, 3938–3945. doi: 10.1021/cm201366z
Elseman, A. M., Luo, L., and Song, Q. L. (2020a). Self-doping synthesis of trivalent Ni2O3 as a hole transport layer for high fill factor and efficient inverted perovskite solar cells. Dalton Trans. 49, 14243–14250. doi: 10.1039/D0DT03029E
Elseman, A. M., Rashad, M. M., and Hassan, A. M. (2016). Easily attainable, efficient solar cell with mass yield of nanorod single-crystalline organo-metal halide perovskite based on a ball milling technique. ACS Sustain. Chem. Eng. 4, 4875–4886. doi: 10.1021/acssuschemeng.6b01183
Elseman, A. M., Xu, C., Yao, Y., Elisabeth, M., Niu, L., Malavasi, L., et al. (2020b). Electron transport materials: evolution and case study for high-efficiency perovskite solar cells. Solar RRL 4:2000136. doi: 10.1002/solr.202000136
Elseman, A. M., Zaki, A. H., Shalan, A. E., Rashad, M. M., and Song, Q. L. (2020c). TiO2 nanotubes: an advanced electron transport material for enhancing the efficiency and stability of perovskite solar cells. Ind. Eng. Chem. Res. 59, 18549–18557. doi: 10.1021/acs.iecr.0c03415
Emami, S., Martins, J., Ivanou, D., and Mendes, A. (2020). Advanced hermetic encapsulation of perovskite solar cells: the route to commercialization. J. Mater. Chem. A 8, 2654–2662. doi: 10.1039/C9TA11907H
Fu, Z., Xu, M., Sheng, Y., Yan, Z., Meng, J., Tong, C., et al. (2019). Encapsulation of printable mesoscopic perovskite solar cells enables high temperature and long-term outdoor stability. Adv. Fun. Mater. 29:1809129. doi: 10.1002/adfm.201809129
Ghosh, M., Biswas, K., Sundaresan, A., and Rao, C. (2006). MnO and NiO nanoparticles: synthesis and magnetic properties. J. Mater. Chem. 16, 106–111. doi: 10.1039/B511920K
Hanmandlu, C., Liu, C.-C., Chen, C.-Y., Boopathi, K. M., Wu, S.-H., Singh, M., et al. (2018). Top illuminated hysteresis-free perovskite solar cells incorporating microcavity structures on metal electrodes: a combined experimental and theoretical approach. ACS Appl. Mater. Interfaces 10, 17973–17984. doi: 10.1021/acsami.8b04329
Hanmandlu, C., Singh, A., Boopathi, K. M., Lai, C.-S., and Chu, C.-W. (2020). Layered perovskite materials: key solutions for highly efficient and stable perovskite solar cells. Rep. Prog. Phys. 83:086502. doi: 10.1088/1361-6633/ab9f88
Hu, H., Singh, M., Wan, X., Tang, J., Chu, C.-W., and Li, G. (2020a). Nucleation and crystal growth control for scalable solution-processed organic–inorganic hybrid perovskite solar cells. J. Mater.Chem. A 8, 1578–1603. doi: 10.1039/C9TA11245F
Hu, H., Qin, M., Fong, P. W., Ren, Z., Wan, X., Singh, M., et al. (2020b). Perovskite quantum wells formation mechanism for stable efficient perovskite photovoltaics—A real-time phase-transition study. Adv. Mater. 32:2006238. doi: 10.1002/adma.202006238
Hu, X., Wang, H., Ying, Y., Wang, M., Zhang, C., Ding, Y., et al. (2020c). Methylammonium chloride as an interface modificator for planar-structure perovskite solar cells with a high open circuit voltage of 1.19 V. J. Power Sources 480:229073. doi: 10.1016/j.jpowsour.2020.229073
Huang, J.-H., Huang, T.-Y., Wei, H.-Y., Ho, K.-C., and Chu, C.-W. (2012). Wet-milled transition metal oxide nanoparticles as buffer layers for bulk heterojunction solar cells. RSC Adv. 2, 7487–7491. doi: 10.1039/C2RA20543B
Ibrahem, M. A., Huang, W.-C., Lan, T.-W., Boopathi, K. M., Hsiao, Y.-C., Chen, C.-H., et al. (2014). Controlled mechanical cleavage of bulk niobium diselenide to nanoscaled sheet, rod, and particle structures for Pt-free dye-sensitized solar cells. J. Mater. Chem. A 2, 11382–11390. doi: 10.1039/C4TA01881H
Jeon, N. J., Noh, J. H., Kim, Y. C., Yang, W. S., Ryu, S., and Seok, S. I. (2014). Solvent engineering for high-performance inorganic–organic hybrid perovskite solar cells. Nat. Mater. 13, 897–903. doi: 10.1038/nmat4014
Jeon, N. J., Noh, J. H., Yang, W. S., Kim, Y. C., Ryu, S., Seo, J., et al. (2015). Compositional engineering of perovskite materials for high-performance solar cells. Nature 517, 476–480. doi: 10.1038/nature14133
Jeong, M., Choi, I. W., Go, E. M., Cho, Y., Kim, M., Lee, B., et al. (2020). Stable perovskite solar cells with efficiency exceeding 24.8% and 0.3-V voltage loss. Science 369, 1615–1620. doi: 10.1126/science.abb7167
Jiang, Q., Chu, Z., Wang, P., Yang, X., Liu, H., Wang, Y., et al. (2017). Planar-structure perovskite solar cells with efficiency beyond 21%. Adv. Mater. 29:1703852. doi: 10.1002/adma.201703852
Jiang, Q., Zhang, L., Wang, H., Yang, X., Meng, J., Liu, H., et al. (2016). Enhanced electron extraction using SnO2 for high-efficiency planar-structure HC(NH2)2PbI3-based perovskite solar cells. Nat. Energy 2:16177. doi: 10.1038/nenergy.2016.177
Jiang, Q., Zhang, X., and You, J. (2018). SnO2: a wonderful electron transport layer for perovskite solar cells. Small 14:1801154. doi: 10.1002/smll.201801154
Jung, E. H., Jeon, N. J., Park, E. Y., Moon, C. S., Shin, T. J., Yang, T.-Y., et al. (2019). Efficient, stable and scalable perovskite solar cells using poly (3-hexylthiophene). Nature 567, 511–515. doi: 10.1038/s41586-019-1036-3
Jung, J. W., Chueh, C. C., and Jen, A. K. Y. (2015). A low-temperature, solution-processable, Cu-doped nickel oxide hole-transporting layer via the combustion method for high-performance thin-film perovskite solar cells. Adv. Mater. 27, 7874–7880. doi: 10.1002/adma.201503298
Kaneko, R., Kanda, H., Sugawa, K., Otsuki, J., Islam, A., and Nazeeruddin, M. K. (2019). Perovskite solar cells using surface-modified NiOx nanoparticles as hole transport materials in n-i-p configuration. Solar RRL 3:1900172. doi: 10.1002/solr.201900172
Ke, W., Fang, G., Liu, Q., Xiong, L., Qin, P., Tao, H., et al. (2015). Low-temperature solution-processed tin oxide as an alternative electron transporting layer for efficient perovskite solar cells. J. Am. Chem. Soc. 137, 6730–6733. doi: 10.1021/jacs.5b01994
Khan, I. M., Chattha, M. S., Khan, Z. M., and Mateen, A. (2018). Optimization of thin film thicknesses in tandem solar cells. J. Nanoelectron. Optoelectron. 13, 104–110. doi: 10.1166/jno.2018.2202
Kim, H.-S., Lee, C.-R., Im, J.-H., Lee, K.-B., Moehl, T., Marchioro, A., et al. (2012). Lead iodide perovskite sensitized all-solid-state submicron thin film mesoscopic solar cell with efficiency exceeding 9%. Sci. Rep. 2:591. doi: 10.1038/srep00591
Kim, I. S., Haasch, R. T., Cao, D. H., Farha, O. K., Hupp, J. T., Kanatzidis, M. G., et al. (2016). Amorphous TiO2 compact layers via ALD for planar halide perovskite photovoltaics. ACS Appl. Mater. Interfaces 8, 24310–24314. doi: 10.1021/acsami.6b07658
Kim, S.-K., Seok, H.-J., Kim, D.-H., Choi, D.-H., Nam, S.-J., Kim, S.-C., et al. (2020). Comparison of NiOx thin film deposited by spin-coating or thermal evaporation for application as a hole transport layer of perovskite solar cells. RSC Adv. 10, 43847–43852. doi: 10.1039/D0RA08776A
Kojima, A., Teshima, K., Shirai, Y., and Miyasaka, T. (2009). Organometal halide perovskites as visible-light sensitizers for photovoltaic cells. J. Am. Chem. Soc. 131, 6050–6051. doi: 10.1021/ja809598r
Lee, M. M., Teuscher, J., Miyasaka, T., Murakami, T. N., and Snaith, H. J. (2012). Efficient hybrid solar cells based on meso-superstructured organometal halide perovskites. Science 338, 643–647. doi: 10.1126/science.1228604
Lei, L., Yang, S., Yu, Y., Li, M., Xie, J., Bao, S., et al. (2019). Long-term stable perovskite solar cells with room temperature processed metal oxide carrier transporters. J. Mater. Chem. A 7, 21085–21095. doi: 10.1039/C9TA06875A
Li, G., Jiang, Y., Deng, S., Tam, A., Xu, P., Wong, M., et al. (2017). Overcoming the limitations of sputtered nickel oxide for high-efficiency and large-area perovskite solar cells. Adv. Sci. 4:1700463. doi: 10.1002/advs.201700463
Li, N., Niu, X., Chen, Q., and Zhou, H. (2020). Towards commercialization: the operational stability of perovskite solar cells. Chem. Soc. Rev. 49, 8235–8286. doi: 10.1039/D0CS00573H
Li, Y., Zhu, J., Huang, Y., Liu, F., Lv, M., Chen, S., et al. (2015). Mesoporous SnO2 nanoparticle films as electron-transporting material in perovskite solar cells. RSC Adv. 5, 28424–28429. doi: 10.1039/C5RA01540E
Li, Z., Klein, T. R., Kim, D. H., Yang, M., Berry, J. J., Van Hest, M. F., et al. (2018). Scalable fabrication of perovskite solar cells. Nat. Rev. Mater. 3:18017. doi: 10.1038/natrevmats.2018.17
Lin, Y., Chen, B., Zhao, F., Zheng, X., Deng, Y., Shao, Y., et al. (2017). Matching charge extraction contact for wide-bandgap perovskite solar cells. Adv. Mater. 29:1700607. doi: 10.1002/adma.201700607
Liu, C., Zhu, R., Ng, A., Ren, Z., Cheung, S. H., Du, L., et al. (2017). Investigation of high performance TiO2 nanorod array perovskite solar cells. J. Mater. Chem. A 5, 15970–15980. doi: 10.1039/C7TA03710D
Luo, S., and Daoud, W. A. (2016). Crystal structure formation of CH3NH3PbI3–xClx perovskite. Materials 9:123. doi: 10.3390/ma9030123
Ma, J., Zheng, X., Lei, H., Ke, W., Chen, C., Chen, Z., et al. (2017). Highly efficient and stable planar perovskite solar cells with large-scale manufacture of e-beam evaporated SnO2 toward commercialization. Solar RRL 1:1700118. doi: 10.1002/solr.201700118
Maxim, A. A., Sadyk, S. N., Aidarkhanov, D., Surya, C., Ng, A., Hwang, Y.-H., et al. (2020). PMMA thin film with embedded carbon quantum dots for post-fabrication improvement of light harvesting in perovskite solar cells. Nanomaterials 10:291. doi: 10.3390/nano10020291
Meng, X., Zhang, Y., Sun, S., Li, R., and Sun, X. (2011). Three growth modes and mechanisms for highly structure-tunable SnO2 nanotube arrays of template-directed atomic layer deposition. J. Mater. Chem. 21, 12321–12330. doi: 10.1039/C1JM11511A
Mitchell, R. H., Welch, M. D., and Chakhmouradian, A. R. (2017). Nomenclature of the perovskite supergroup: a hierarchical system of classification based on crystal structure and composition. Mineral. Mag. 81, 411–461. doi: 10.1180/minmag.2016.080.156
Napari, M., Huq, T. N., Hoye, R. L. Z., and MacManus-Driscoll, J. L. (2020). Nickel oxide thin films grown by chemical deposition techniques: potential and challenges in next-generation rigid and flexible device applications. InfoMat 1–41. doi: 10.1002/inf2.12146
Natu, G., Hasin, P., Huang, Z., Ji, Z., He, M., and Wu, Y. (2012). Valence band-edge engineering of nickel oxide nanoparticles via cobalt doping for application in p-type dye-sensitized solar cells. ACS Appl. Mater. Interfaces 4, 5922–5929. doi: 10.1021/am301565j
Ng, A., Ren, Z., Hu, H., Fong, P. W., Shen, Q., Cheung, S. H., et al. (2018). A Cryogenic Process for Antisolvent-Free High-Performance Perovskite Solar Cells. Adv. Mater. 30:1804402. doi: 10.1002/adma.201804402
Ng, A., Ren, Z., Shen, Q., Cheung, S. H., Gokkaya, H. C., Bai, G., et al. (2015). Efficiency enhancement by defect engineering in perovskite photovoltaic cells prepared using evaporated PbI2/CH3NH3I multilayers. J. Mater. Chem.A 3, 9223–9231. doi: 10.1039/C4TA05070C
Ng, A., Ren, Z., Shen, Q., Cheung, S. H., Gokkaya, H. C., So, S. K., et al. (2016). Crystal engineering for low defect density and high efficiency hybrid chemical vapor deposition grown perovskite solar cells. ACS Appl. Mater. Interfaces 8, 32805–32814. doi: 10.1021/acsami.6b07513
Ouyang, D., Huang, Z., and Choy, W. C. (2019). Solution-processed metal oxide nanocrystals as carrier transport layers in organic and perovskite solar cells. Adv. Fun. Mater. 29:1804660. doi: 10.1002/adfm.201804660
Qiu, Z., Gong, H., Zheng, G., Yuan, S., Zhang, H., Zhu, X., et al. (2017). Enhanced physical properties of pulsed laser deposited NiO films via annealing and lithium doping for improving perovskite solar cell efficiency. J. Mater. Chem. C 5, 7084–7094. doi: 10.1039/C7TC01224A
Rao, H. S., Chen, B. X., Li, W. G., Xu, Y. F., Chen, H. Y., Kuang, D. B., et al. (2015). Improving the extraction of photogenerated electrons with SnO2 nanocolloids for efficient planar perovskite solar cells. Adv. Fun. Mater. 25, 7200–7207. doi: 10.1002/adfm.201501264
Rashad, M., Hassan, A., Nassar, A., Ibrahim, N., and Mourtada, A. (2014). A new nano-structured Ni (II) Schiff base complex: synthesis, characterization, optical band gaps, and biological activity. Appl. Phys. A 117, 877–890. doi: 10.1007/s00339-014-8448-6
Ren, Z., Zhou, J., Zhang, Y., Ng, A., Shen, Q., Cheung, S. H., et al. (2018). Strategies for high performance perovskite/crystalline silicon four-terminal tandem solar cells. Sol. Energy Mater. Sol. Cells 179, 36–44. doi: 10.1016/j.solmat.2018.01.004
Sajid, S., Elseman, A. M., Huang, H., Ji, J., Dou, S., Jiang, H., et al. (2018). Breakthroughs in NiOx-HTMs towards stable, low-cost and efficient perovskite solar cells. Nano Energy 51, 408–424. doi: 10.1016/j.nanoen.2018.06.082
Sajid, S., Elseman, A. M., Wei, D., Ji, J., Dou, S., Huang, H., et al. (2019). NiO@ carbon spheres: a promising composite electrode for scalable fabrication of planar perovskite solar cells at low cost. Nano Energy 55, 470–476. doi: 10.1016/j.nanoen.2018.11.004
Saliba, M., Matsui, T., Seo, J.-Y., Domanski, K., Correa-Baena, J.-P., Nazeeruddin, M. K., et al. (2016). Cesium-containing triple cation perovskite solar cells: improved stability, reproducibility and high efficiency. Energy Environ. Sci. 9, 1989–1997. doi: 10.1039/C5EE03874J
Shalenov, E. O., Dzhumagulova, K. N., Ng, A., and Jumabekov, A. N. (2020). Performance optimization of back-contact perovskite solar cells with quasi-interdigitated electrodes. Sol. Energy 205, 102–108. doi: 10.1016/j.solener.2020.05.034
Shao, S., and Loi, M. A. (2020). The Role of the Interfaces in Perovskite Solar Cells. Adv. Mater. Interfaces 7:1901469. doi: 10.1002/admi.201901469
Shen, Q., Ng, A., Ren, Z., Gokkaya, H. C., Djurisic, A. B., Zapien, J. A., et al. (2018). Characterization of low-frequency excess noise in CH3NH3PbI3-based solar cells grown by solution and hybrid chemical vapor deposition techniques. ACS Appl. Mater. Interfaces 10, 371–380. doi: 10.1021/acsami.7b10091
Shin, S., Lee, S., and Seok, S. I. (2019). Exploring wide bandgap metal oxides for perovskite solar cells. APL Mater. 7:022401. doi: 10.1063/1.5055607
Singh, M., Chiang, C.-H., Boopathi, K. M., Hanmandlu, C., Li, G., Wu, C.-G., et al. (2018). A novel ball milling technique for room temperature processing of TiO2 nanoparticles employed as the electron transport layer in perovskite solar cells and modules. J. Mater. Chem. A 6, 7114–7122. doi: 10.1039/C8TA00303C
Singh, M., Ng, A., Ren, Z., Hu, H., Lin, H.-C., Chu, C.-W., et al. (2019). Facile synthesis of composite tin oxide nanostructures for high-performance planar perovskite solar cells. Nano Energy 60, 275–284. doi: 10.1016/j.nanoen.2019.03.044
Singh, M., Yang, R.-T., Weng, D.-W., Hu, H., Singh, A., Mohapatra, A., et al. (2020). Low-temperature processed bipolar metal oxide charge transporting layers for highly efficient perovskite solar cells. Sol. Energy Mater. Sol. Cells 221:110870.
Su, T.-S., Hsieh, T.-Y., Hong, C.-Y., and Wei, T.-C. (2015). Electrodeposited ultrathin TiO2 blocking layers for efficient perovskite solar cells. Sci. Rep. 5:16098. doi: 10.1038/srep16098
Thambidurai, M., Shini, F., Harikesh, P., Mathews, N., and Dang, C. (2020). Highly stable and efficient planar perovskite solar cells using ternary metal oxide electron transport layers. J. Power Sources 448:227362. doi: 10.1016/j.jpowsour.2019.227362
The National Renewable Energy Laboratory [NREL] (2021). Best Research-Cell Efficiencies Chart. Available online at: www.nrel.gov/pv/assets/pdfs/bestresearch-cell-efficiencies.20200218.pdf. (accessed April 2021).
Tian, H., Xu, B., Chen, H., Johansson, E. M., and Boschloo, G. (2014). Solid-state perovskite-sensitized p-Type mesoporous nickel oxide solar cells. ChemSusChem 7, 2150–2153. doi: 10.1002/cssc.201402032
Tilley, S. D., Schreier, M., Azevedo, J., Stefik, M., and Graetzel, M. (2014). Ruthenium oxide hydrogen evolution catalysis on composite cuprous oxide water-splitting photocathodes. Adv. Fun. Mater. 24, 303–311. doi: 10.1002/adfm.201301106
Tseng, C.-C., Chen, L.-C., Chang, L.-B., Wu, G.-M., Feng, W.-S., Jeng, M.-J., et al. (2020). Cu2O-HTM/SiO2-ETM assisted for synthesis engineering improving efficiency and stability with heterojunction planar perovskite thin-film solar cells. Sol. Energy 204, 270–279. doi: 10.1016/j.solener.2020.04.077
Wang, C., Zhao, D., Grice, C. R., Liao, W., Yu, Y., Cimaroli, A., et al. (2016). Low-temperature plasma-enhanced atomic layer deposition of tin oxide electron selective layers for highly efficient planar perovskite solar cells. J. Mater. Chem. A 4, 12080–12087. doi: 10.1039/C6TA04503K
Wang, H., Liu, H., Ye, F., Chen, Z., Ma, J., Liang, J., et al. (2021). Hydrogen peroxide-modified SnO2 as electron transport layer for perovskite solar cells with efficiency exceeding 22%. J. Power Sources 481:229160. doi: 10.1016/j.jpowsour.2020.229160
Wang, H., Wang, Y., and Wang, X. (2012). Pulsed laser deposition of the porous nickel oxide thin film at room temperature for high-rate pseudocapacitive energy storage. Electrochem. Commun. 18, 92–95. doi: 10.1016/j.elecom.2012.02.023
Wang, K., Tian, Y., Jiang, H., Chen, M., and Xu, S. (2019). Surface Treatment on Nickel Oxide to Enhance the Efficiency of Inverted Perovskite Solar Cells. Intern. J. Photoenergy 2019:4360816. doi: 10.1155/2019/4360816
Wang, K.-C., Shen, P.-S., Li, M.-H., Chen, S., Lin, M.-W., Chen, P., et al. (2014). Low-temperature sputtered nickel oxide compact thin film as effective electron blocking layer for mesoscopic NiO/CH3NH3PbI3 perovskite heterojunction solar cells. ACS Appl. Mater. Interfaces 6, 11851–11858. doi: 10.1021/am503610u
Wang, Y., Zhang, Y., Zhang, P., and Zhang, W. (2015). High intrinsic carrier mobility and photon absorption in the perovskite CH3NH3PbI3. Phys. Chem. Chem. Phys. 17, 11516–11520. doi: 10.1039/C5CP00448A
Wojciechowski, K., Saliba, M., Leijtens, T., Abate, A., and Snaith, H. J. (2014). Sub-150 C processed meso-superstructured perovskite solar cells with enhanced efficiency. Energy Environ. Sci. 7, 1142–1147. doi: 10.1039/C3EE43707H
Wu, S., Cheng, C., Jin, J., Wang, J., and Peng, T. (2018). Low-Temperature processed nanostructured rutile TiO2 array films for perovskite solar cells with high efficiency and stability. Solar RRL 2:1700164. doi: 10.1002/solr.201700164
Xia, X., Tu, J., Zhang, J., Wang, X., Zhang, W., and Huang, H. (2008). Electrochromic properties of porous NiO thin films prepared by a chemical bath deposition. Sol. Energy Mater. Sol. Cells 92, 628–633. doi: 10.1016/j.solmat.2008.01.009
Xing, G., Mathews, N., Sun, S., Lim, S. S., Lam, Y. M., Grätzel, M., et al. (2013). Long-range balanced electron-and hole-transport lengths in organic-inorganic CH3NH3PbI3. Science 342, 344–347. doi: 10.1126/science.1243167
Yang, B., Mahjouri-Samani, M., Rouleau, C. M., Geohegan, D. B., and Xiao, K. (2016). Low temperature synthesis of hierarchical TiO2 nanostructures for high performance perovskite solar cells by pulsed laser deposition. Phys. Chem. Chem. Phys. 18, 27067–27072. doi: 10.1039/C6CP02896A
Yang, D., Yang, R., Zhang, J., Yang, Z., Liu, S. F., and Li, C. (2015a). High efficiency flexible perovskite solar cells using superior low temperature TiO2. Energy Environ. Sci. 8, 3208–3214. doi: 10.1039/C5EE02155C
Yang, D., Yang, Z., Qin, W., Zhang, Y., Liu, S. F., and Li, C. (2015b). Alternating precursor layer deposition for highly stable perovskite films towards efficient solar cells using vacuum deposition. J. Mater. Chem. A 3, 9401–9405. doi: 10.1039/C5TA01824B
Yang, W. S., Noh, J. H., Jeon, N. J., Kim, Y. C., Ryu, S., Seo, J., et al. (2015c). High-performance photovoltaic perovskite layers fabricated through intramolecular exchange. Science 348, 1234–1237. doi: 10.1126/science.aaa9272
You, J., Meng, L., Song, T.-B., Guo, T.-F., Yang, Y. M., Chang, W.-H., et al. (2016). Improved air stability of perovskite solar cells via solution-processed metal oxide transport layers. Nat. Nanotechnol. 11, 75–81. doi: 10.1038/nnano.2015.230
Yue, S., Liu, K., Xu, R., Li, M., Azam, M., Ren, K., et al. (2017). Efficacious engineering on charge extraction for realizing highly efficient perovskite solar cells. Energy Environ. Sci. 10, 2570–2578. doi: 10.1039/C7EE02685D
Zhang, K., Rossi, C., Alphonse, P., and Tenailleau, C. (2008). Synthesis of NiO nanowalls by thermal treatment of Ni film deposited onto a stainless steel substrate. Nanotechnol. 19:155605. doi: 10.1088/0957-4484/19/15/155605
Zhou, Y., Li, X., and Lin, H. (2020). To Be Higher and Stronger—Metal oxide electron transport materials for perovskite solar cells. Small 16:1902579. doi: 10.1002/smll.201902579
Keywords: metal oxides, electron transport layers, hole transport layers, cost-effective, stability, perovskite solar cells
Citation: Singh M, Chu CW and Ng A (2021) Perspective on Predominant Metal Oxide Charge Transporting Materials for High-Performance Perovskite Solar Cells. Front. Mater. 8:655207. doi: 10.3389/fmats.2021.655207
Received: 18 January 2021; Accepted: 24 February 2021;
Published: 23 April 2021.
Edited by:
Dingshan Yu, Sun Yat-sen University, ChinaReviewed by:
Yongbo Yuan, Central South University, ChinaAhmed Mourtada Elseman, Central Metallurgical Research and Development Institute (CMRDI), Egypt
Copyright © 2021 Singh, Chu and Ng. This is an open-access article distributed under the terms of the Creative Commons Attribution License (CC BY). The use, distribution or reproduction in other forums is permitted, provided the original author(s) and the copyright owner(s) are credited and that the original publication in this journal is cited, in accordance with accepted academic practice. No use, distribution or reproduction is permitted which does not comply with these terms.
*Correspondence: Annie Ng, annie.ng@nu.edu.kz; Chih Wei Chu, gchu@gate.sinica.edu.tw