AUTHOR=Mu Qi , Chen Zheng , Duan Shuming , Zhang Xiaotao , Ren Xiaochen , Hu Wenping TITLE=A Low-Temperature Solution-Process High-k Dielectric for High-Performance Flexible Organic Field-Effect Transistors JOURNAL=Frontiers in Materials VOLUME=7 YEAR=2020 URL=https://www.frontiersin.org/journals/materials/articles/10.3389/fmats.2020.570002 DOI=10.3389/fmats.2020.570002 ISSN=2296-8016 ABSTRACT=

Applying high-k dielectrics can effectively reduce the operating voltage of Organic field-effect transistors (OFETs) to a few volts, thus significantly miniaturizing the dynamic power consumption of OFETs. Aluminum oxide is a promising dielectric material due to its high permittivity (k = 6–9). In this work, a simple, low-cost, low-temperature (only 85°C) solution process is used to prepare amorphous AlOx dielectric thin films for high-performance flexible OFET applications. The AlOx thin film was spin-coated and then solidified using deep ultraviolet irradiation without high-temperature annealing. The as-deposited AlOx thin film has a root mean square surface roughness of 0.47 nm and maintains a very low leakage current density of 8 × 10–9 A/cm2 at 3.5 MV/cm and high dielectric constant of about 8.3 (at 1 kHz). The complete OFET based on this dielectric can operate at a 3 V gate bias with saturation mobility of 1.8 cm2/Vs, and steep sub-threshold swing of 110 mV/dec. Our work demonstrated a low-temperature solution process to fabricate a high-k metal oxide dielectric for low-power OFET applications.