ORIGINAL RESEARCH article

Front. Mater., 24 November 2020
Sec. Polymeric and Composite Materials
This article is part of the Research Topic Enhanced Microwave Absorption Properties of Magnetic-Dielectric Composites View all 7 articles

Effects of Heat-Treatment on the Microstructure, Electromagnetic Wave Absorbing Properties, and Mechanical Properties of SiCN Fibers

Xin LongXin LongShuai ZhangShuai ZhangChangwei Shao
Changwei Shao*Bing WangBing WangYingde Wang
Yingde Wang*
  • Science and Technology on Advanced Ceramic Fibers and Composites Laboratory, College of Aerospace Science and Engineering, National University of Defense Technology, Changsha, China

SiCN fibers can not only be used for reinforcement of composites materials but also for electromagnetic wave (EMW) absorbing applications in a high-temperature oxidizing environment above 1,200°C. In this work, the microstructural evolution and EMW absorbing properties of SiCN fibers after annealing at 1,300–1,600°C in N2 atmosphere were investigated. Results showed that the amorphous SiCN fibers presented poor EMW absorbing properties when the annealing temperature was below 1,400°C. As the annealing temperature increased to 1,500°C, the EMW absorbing properties could been largely enhanced with a minimum reflation loss value of -55.8 dB and an effective absorption bandwidth value of 2.5 GHz. The enhanced EMW absorbing properties should contribute to the formation and growth of grain boundaries and defects among the amorphous fiber matrix and turbostratic graphite carbon, which could enhance the space charge polarization at the heterogeneous interfaces and increase the conductivity of the SiCN fibers. Meanwhile, SiCN fibers retained a rather high tensile strength of ∼1.0 GPa after annealing at 1,500°C, which showed it to be a promising candidate for reinforcing the stealth ceramic matrix composites used in harsh environments.

Introduction

Polymer-derived ceramics, such as SiC, SiCN, and SiBCN, are considered as superior electromagnetic wave (EMW) absorbers that can be used in a high-temperature oxidizing environment above 1,200°C, due to their excellent high-temperature performance and adjustable semiconducting properties (Duan et al., 2016; Storch et al., 2018). Among them, a polymer-derived ceramic with a fiber morphology could be used as reinforcement for the preparation of ceramic matrix composites, showing more practical significance in structural/functional applications at high temperatures.

Several works have studied the EMW absorbing properties of commercial ceramic fibers derived from pre-ceramic polymers. For example, Mo et al. (2017) found that heat treatment could improve the EMW absorbing properties of amorphous SiC fibers (Tyranno ZMI) due to the growth of SiC nanocrystals. Ding and coworkers compared the EMW absorbing properties of Nicalon-202 and KD-Ⅰ SiC fibers, showing that KD-Ⅰ fibers with more free carbon presented better EMW absorption (Ding et al., 2011). However, at present, almost all of the available SiC fibers have shown poor EMW absorbing properties with a very large reflection loss (RL) value (>−10 dB) due to the impedance mismatch. When nitrogen was introduced into the SiC fibers, the impedance match could be improved (Long et al., 2019a). These nitrogen-doped fibers are also called SiCN fibers.

Although SiCN fibers show excellent impedance matching behavior, the EMW absorbing properties are usually poor when SiCN fibers consist of only one amorphous SiCN phase with very few high-dielectric nanocrystals (Widgeon et al., 2012; Ye et al., 2013). Nowadays, several studies have introduced high-dielectric nanocrystals (such as carbon nanotubes and graphene) into amorphous SiCN ceramics by chemically modifying the pre-ceramic polymer and finally improving the EMW absorbing properties (Liu et al., 2017a; Liu et al., 2017b). Another method includes simply heat treating the amorphous SiCN ceramics with different pyrolysis atmospheres or temperatures, where the nano-SiC and free carbon nanodomains could form in-situ (Gian et al., 2020). However, although great effort has been devoted to SiCN ceramics in the morphology of bulk and powder, few attempts have been made to improve the EMW absorbing properties of SiCN fibers.

In this work, turbostratic graphite carbon was formed in-situ in the amorphous SiCN fibers by simply heat treating them at 1,300°C–1,600°C in an N2 atmosphere. Results showed that the EMW absorbing properties of the amorphous SiCN fibers could be largely enhanced after annealing at 1,500°C, with a minimum RL value of −55.8 dB and an effective absorption bandwidth (EAB) value of 2.5 GHz. The probable EMW absorbing mechanism was proposed in this work. The microstructural evolution and mechanical properties of the SiCN fibers after annealing at different high temperatures were also investigated in detail.

Experimental Section

Materials

SiCN fibers were prepared according to our previous work by using electron beams curing polycarbosilane (EB-PCS) fibers as starting precursors (Long et al., 2019b). The used N2 gas (Xiangfeng Co. Ltd., China) was of high purity (>99.99%).

High-Temperature Annealing

SiCN fibers were treated in a graphite furnace at a temperature range of 1,300°C–1,600°C in an N2 atmosphere with a heating rate of 5°C/min. After holding for 1 h at the target temperature, the fibers were furnace cooled to room temperature.

Characterization

The carbon content of the obtained SiCN fibers was measured by a Horiba carbon/sulfur analyzer EMIA-320V (Horiba, Japan). The oxygen and nitrogen content was determined by a Horiba oxygen/nitrogen analyzer EMIA-820 (Horiba, Japan). The content of silicon in the samples was calculated by the subtraction method using the percentage weight. Raman spectra were recorded by a micro-Raman spectrometer Horiba HR800 (Horiba, Japan) with an Ar-Ion laser wavelength of 514.5 nm and Raman shift range of 800–2,000 cm−1. X-ray diffraction studies were carried out with a Bruker AXS D8 Advance diffractometer (Bruker, Germany) with Cu Kα radiation (k = 1.54178 A°) and a scanning speed of 0.0167°/s. The fiber morphology was observed by a HITACHI S-4800 scanning electron microscope (SEM, Japan). Transmission electron microscopy (TEM) analysis was carried out by Titan G2 60–300 with image corrector. Before observing with TEM, the fibers were grinded into powder and dispersed in alcohol by ultrasonication for 10 min, which was followed by depositing a drop of the dispersed solution on a 3 mm carbon-coated copper grid. For obtaining the relative complex permittivity of the SiCN fibers, 65 vol% fibers and 35 vol% epoxy were mixed by stirring with glass blocks for 10 min in a flask, then homogeneous fiber prepreg could be prepared, which was followed by a hot-press process at 130°C with 1 MPa. The obtained composite samples with the sizes of 22.86 × 10.16 × 3.0 mm and 15.8 × 7.9 × 3.0 mm were measured by a vector network analyzer (Agilent N5230A, America) in the range of 8–12 and 12–18 GHz, respectively. The relative complex permittivity of the SiCN fibers were calculated using the logarithmic law of mixing:

lnε=Vflnεf+Vmlnεm(1)

where ε, εf, and εm are the complex permittivity of composite samples, SiCN fibers, and epoxy matrix, respectively; Vf and Vm are the volume fraction of the SiCN fibers and epoxy matrix, respectively. The tensile strength and Young’s modulus of SiCN fibers with 25 mm length was measured at room temperature using a universal strength machine (Testometric Micro 350, United Kingdom) with a load cell of 5 N and a crosshead speed of 5 mm/min. Each tensile strength data point was the average of 24 monofilaments.

Results and Discussion

Composition and Microstructure of SiCN Fibers With Different Annealing Temperatures

The chemical composition of SiCN fibers with different annealing temperatures are shown in Table 1. It can be clearly seen that, the nitrogen content of the SiCN fibers decreased obviously while the carbon content increased with the annealing temperature increase, which finally caused the C/N atomic ratio to increase from 0.60 to 1.95 when the annealing temperature reached up to 1,600°C. The decreasing of the nitrogen content indicated the carbothermal reduction between the Si3N4 phase and free carbon (Eq. 2), which are the two major phases in the polymer-derived SiCN fibers (Mera et al., 2009; Prasad et al., 2012).

Si3N4 (am)+3C(s)=3SiC(s)+2N2(g)(2)
TABLE 1
www.frontiersin.org

TABLE 1. Chemical composition of SiCN fibers with different annealing temperatures.

The carbothermal reduction between the Si3N4 phase and free carbon caused the consumption of free carbon, which could be observed from the Raman spectra (Figures 1A). All of the SiCN fibers with different annealing temperatures showed a G band peak at ∼1,600 cm−1 relative to the breathing mode of sp2 carbon and a D band peak at ∼1,300 cm−1 relative to the in-plane bond stretching of sp2-hybridized carbon (Mera et al., 2009; Chen et al., 2014). As the annealing temperature increased, the intensity of all of the Raman peaks decreased, which indicated the consumption of free carbon via the carbothermal reduction between the Si3N4 phase and free carbon, as a result, causing the release of nitrogen gas. Thus, the Raman spectra agreed well with the chemical composition results. For further quantitative analysis, the Raman spectra, the G band, and D band were curve-fitting with a Breit–Wigner–Fano function and Lorentzian equation, respectively. The obtained ID/IG intensity ratios derived from the curve-fitting results could be used to calculate the average size of the free carbon nanoclusters (La) with a Ferrari-Robertson equation (Zickler et al., 2006). When the free carbon nanoclusters showed a two-dimension (2D) grain growth process at a high temperature, the La could be calculated by Eq. 3, where k is the pre-exponential factor, R is the Molar gas constant, G* is the activation energy, and T is the annealing temperature (Chen et al., 2014). The logarithm of the two sides of Eq. 3 could obtain Eq. 4, indicating the ln (La2) and 1/T may satisfy the liner relationship. Figures 1B shows the plots of ln (La2) vs. 1,000/T. The results showed that the La value decreased slightly when the annealing temperature increased from 1,300°C to 1,400°C, which could have contributed to the graphitization of amorphous free carbon to form turbostratic graphite carbon (Sarkar et al., 2011). As the annealing temperature increased to above 1,400°C, the La value increased obviously, and the ln ((La2)) vs. 1/T well met the liner relationship at the temperature range of 1,400°C–1,600°C. Thus, turbostratic graphite carbon in the SiCN fibers showed a 2D grain growth process at the temperature range of 1,400°C–1,600°C. The slope from the fitted liner curing is relative to the activation energy G* for the growth of the turbostratic graphite carbon, and the value is 82 kJ/mol.

La2=kexp(GRT)(3)
ln(La2)=GR×1T+constant(4)
FIGURE 1
www.frontiersin.org

FIGURE 1. Raman spectra of SiCN fibers after annealing at different temperatures (A); the plots of La vs. 1,000/T(B).

Figure 2 shows the X-ray diffraction patterns of SiCN fibers after annealing at different temperatures. When the annealing temperature was below 1,500°C, the SiCN fibers could remain completely amorphous without diffraction peaks detected. As the annealing temperature increased up to 1,600°C, three obvious diffraction peaks at 2θ = 35.60°, 59.98°, and 71.78° could be observed, indicating the formation of a β-SiC (JPCDS #29-1129) phase. It is believed that these β-SiC phases were likely formed in-situ from the production of the carbothermal reduction between the Si3N4 phase and free carbon. Meanwhile, weak diffraction peaks related to the α-Si3N4 (JPCDS #09-0250) phase could also be detected. The formation of a crystalline phase may have increased the amount of grain boundary, and finally caused the increase of the dielectric constant as a result.

FIGURE 2
www.frontiersin.org

FIGURE 2. XRD patterns of SiCN fibers after annealing at different temperatures.

To further understand the microstructure of SiCN fibers after annealing at different temperatures, TEM micrographs were obtained, as shown in Figure 3. It can be seen that SCN-1,300 showed a totally amorphous microstructure. As the annealing temperature increased to 1,400°C, a small amount of turbostratic graphite carbon with 2–3 layers could be observed in SCN-1,400, while the fibers were still a fully amorphous micromorphology. The turbostratic graphite carbon grew to more than three layers when the annealing temperature increased to 1,500°C, and further grew as the annealing temperature went up to 1,600°C. Meanwhile, a small amount of Si3N4 grains with interplanar spacing of 0.27 nm could also be detected in SCN-1,600. These results agreed well with the quantitative analysis of the Raman spectra, and also showed the graphitization of amorphous free carbon at 1,400°C and the growth of turbostratic graphite carbon at above 1,400°C. The formation and growth of turbostratic graphite carbon could increase the amount of grain boundaries and defects among the fiber matrix and free carbon, which could lead to the enhancement of space charge polarization and interface polarization, thus, consequently, improving the EMW absorbing properties of the SiCN fibers.

FIGURE 3
www.frontiersin.org

FIGURE 3. TEM micrographs of SiCN fibers after annealing at different temperatures: SCN-1,300 (A), SCN-1,400 (B), SCN-1,500 (C), and SCN-1,600 (D).

Figure 4 shows the scanning electron microscope micrographs of SiCN fibers with different annealing temperatures. These SiCN fibers showed a rather smooth surface when the annealing temperature was below 1,500°C. Very fine nanograins with a size of 50 nm could be formed on the fiber surface when the annealing temperature reached 1,500°C. Considering that a sharp decrease of nitrogen content was detected at 1,500°C, the nanograins were likely formed in the in-situ SiC phase via the carbothermal reduction between the Si3N4 phase and free carbon. The size of these in-situ-formed SiC nanograins could grow up to near 1 μm as the annealing temperature went up to 1,600°C, indicating the enhancement of the carbothermal reduction between the Si3N4 phase and free carbon. Thus, SCN-1,600 showed a very rough surface, which is harmful for the retention of tensile strength.

FIGURE 4
www.frontiersin.org

FIGURE 4. SEM micrographs of SiCN fibers after annealing at different temperatures: SCN-1,300 (A), SCN-1,400 (B), SCN-1,500 (C) and SCN-1,600 (D).

Dielectric and Electromagnetic Wave Absorbing Properties of SiCN Fibers After Annealing at Different Temperatures

The relative complex permittivity (ε=ε'jε'') is very important for the EMW absorbing properties of SiCN fibers. The real part (ε') can present the storage ability of EMW energy, while the imaginary part (ε'') is related to the loss ability of EMW energy (Li et al., 2019). Thus, a rather high ε'' is necessary for SiCN fibers to show excellent EMW absorbing properties. Figure 5 shows the real part (ε') and imaginary part (ε'') as well as the dielectric loss (tanδ=ε''ε') at the frequency range of 8–18 GHz for SiCN fibers with different annealing temperatures. SCN-1,300 and SCN-1,400 showed similar ε' values of 9.0–10.1 during the whole testing frequency range. As the annealing temperature increased to 1,500°C, the ε' values obviously increased to 9.8–13.7 and sharply increased to 16.9–23.1 when the annealing temperature reached 1,600°C. Based on our previous analysis, it is believed that the consumption of the Si3N4 phase (with ε' and ε'' values of <9 and <0.1, respectively) via the the carbothermal reduction with free carbon could finally cause the increase of the ε' and ε'' values according to the logarithmic law of mixing (Zhao et al., 2016). Meanwhile, the formation and growth of turbostratic graphite carbon may also cause the increase of the ε' and ε'' values due to the enhancement of space charge polarization and interface polarization when large amounts of grain boundaries and defects among the fiber matrix and free carbon were formed.

FIGURE 5
www.frontiersin.org

FIGURE 5. The real (A) and imaginary (B) part of permittivity as well as the dielectric loss (C) at the frequency range of 8–18 GHz for SiCN fibers with different annealing temperatures.

Based on the metal back panel model, the RL values of the SiCN fibers with different sample thicknesses at the frequency range of 8–18 GHz could be calculated with Eq. 5 and Eq. 6. Where εr, μr, Zin, and Z0 are the permittivity, permeability, input impedance, and free-space impedance of the sample, respectively; and c, d, and f represent the speed of light in vacuum, thickness of the sample, and the microwave frequency, respectively. When the RL values are below −10 dB, it means more than 90% EMW energy could be absorbed, then the frequency range with RL values below −10 dB is called an EAB, which is also a very important parameter to evaluate the EMW absorbing properties of SiCN fibers.

Figure 6 shows the three-dimensional plots of the RL values vs frequency and thickness for SiCN fibers with different annealing temperatures. SCN-13,00 shows rather poor EMW absorbing properties with the minimum RL values of −13.1 dB at 15.1 GHz with a sample thickness of 5.0 mm and a narrow EAB of 0.8 GHz. After annealing at 1,400°C, the EMW absorbing properties of SCN-1,400 could be improved with the minimum RL values of −33.7 dB at 15.2 GHz with a sample thickness of 4.9 mm and a wider EAB of 1.5 GHz. The EMW absorbing properties could be further improved as the annealing temperature reached 1,500°C, when the minimum RL values could reach −55.8 dB at 9.3 GHz with a sample thickness of 2.3 mm and the EAB could reach a wider value of 2.5 GHz. According to the microstructure evolution analysis, the improvement of the EMW absorbing properties of SiCN fibers is consistent with the formation and growth of turbostratic graphite carbon. Thus, it is believed that the formation and growth of turbostratic graphite could form grain boundaries and defects among the amorphous fiber matrix and free carbon, which could enhance the space charge polarization at the heterogeneous interfaces and finally transform EMW energy into heat (Figure 7). Meanwhile, turbostratic graphite shows higher conductivity than amorphous free carbon, which could more easily absorb incident EMW through the forming current flow. However, when the annealing temperature reached 1,600°C, the EMW absorbing properties of the SiCN fibers become very poor with a minimum RL values of −9.1 dB, which contributed to the impedance mismatch as most of the Si3N4 phase was consumed via the carbothermal reduction after annealing at 1,600°C.

RL=20log10|ZinZ0Zin+Z0|(5)
Zin=Z0(μr/εr)1/2tanhj(2πfd/c)(μrεr)1/2(6)
FIGURE 6
www.frontiersin.org

FIGURE 6. Three-dimensional plots of the RL values vs frequency and thickness: SCN-1,300 (A), SCN-1,400 (B), SCN-1,500 (C), and SCN-1,600 (D).

FIGURE 7
www.frontiersin.org

FIGURE 7. Schematic diagram of the proposed mechanism for EMW absorption.

Mechanical Properties of SiCN Fibers at a High Temperature

Comparing with other Si-based ceramics for EMW absorbing applications, SiCN fibers present excellent mechanical properties thus can meet the shortage of reinforcements for stealth ceramic matrix composites. Figure 8 shows the tensile strength and Young’s modulus of SiCN fibers after annealing at different temperatures. The SiCN fibers could retain their tensile strength when the annealing temperature was below 1,400°C. As the annealing temperature went up to 1,500°C, the tensile strength obviously decreased to ∼1.0 GPa, and lost its tensile strength when the annealing temperature reached 1,600°C. Thus, although the high-temperature treatment could enhance the EMW absorbing properties of the SiCN fibers, it could also cause a decrease of tensile strength. According to the previous analysis, SiCN fibers presented a completely amorphous microstructure at below 1,500°C, thus the ability to retain an amorphous microstructure had little effect on the tensile strength at the temperature range of 1,300°C–1,500°C. From the element analysis in Table 1, SiCN fibers showed a stable chemical composition after annealing at 1,400°C and a sharp decrease in nitrogen content when the annealing temperature reached up to above 1,500°C, which agreed well with the relationship between the tensile strength and annealing temperatures. Thus, the decrease of tensile strength was mainly contributed to the carbothermal reduction of the Si3N4 phase, which caused N2 gas release and formed defects in the fibers. On the contrary, the Young’s modulus of SiCN fibers showed a slight increase as the annealing temperature increased, which may have contributed to the densification process under a high temperature. However, the Young’s modulus of SiCN fibers presented a dramatic decrease before the full strength degradation, indicating that large amounts of pores or defects were formed due to the violent carbothermal reduction of the Si3N4 phase.

FIGURE 8
www.frontiersin.org

FIGURE 8. The Young’s modulus and tensile strength of SiCN fibers after annealing at high temperatures.

Conclusion

In this work, the microstructural evolution, dielectric properties, EMW absorbing properties, and mechanical properties of SiCN fibers after annealing at a temperature range of 1,300°C–1,600°C were studied. SiCN fibers could retain their stable chemical composition at below 1,400°C and presented a dramatic decrease of nitrogen content due to the carbothermal reduction of the amorphous Si3N4 phase when the annealing temperature went up to above 1,500°C. Meanwhile, the amorphous free carbon graphitized at a temperature of 1,300°C–1,400°C and showed a 2D grain growth process at a temperature range of 1,400°C–1,600°C. Due to formation and growth of turbostratic graphite carbon, the dielectric properties and EMW absorbing properties could be tuned by the heat treatment at different high temperatures. The minimum RL value was −55.8 dB and the EAB value was 2.5 GHz when the annealing temperature was 1,500°C. The excellent EMW absorbing properties should have contributed to the formation and growth of grain boundaries and defects among the amorphous fiber matrix and turbostratic graphite carbon, which could enhance the space charge polarization at the heterogeneous interface and increase the conductivity of the SiCN fibers. Meanwhile, the SiCN fibers retained a rather high tensile strength of ∼1.0 GPa after annealing at 1,500°C, which confirmed them as promising candidates for reinforcing the stealth ceramic matrix composites used in harsh environments.

Data Availability Statement

The raw data supporting the conclusions of this article will be made available by the authors, without undue reservation.

Author Contributions

XL and SZ wrote the manuscript; CS and YW revised and analyzed the microstructural evolution of SiCN fibers; BW analyzed the EMW absorbing properties of SiCN fibers.

Funding

This work is supported by the National Natural Science Foundation of China (51203184, 51872329), the Aid Program for Science and Technology Innovative Research Team in Higher Educational Institutions of Hunan Province, and the Aid Program for Innovative Group of National University of Defense Technology.

Conflict of Interest

The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.

References

Chen, Y., Yang, X., Cao, Y., Gan, Z., and An, L. (2014). Quantitative study on structural evolutions and associated energetics in polysilazane-derived amorphous silicon carbonitride ceramics. Acta Mater. 72, 22–31. doi:10.1016/j.actamat.2014.03.049.

CrossRef Full Text | Google Scholar

Ding, D., Zhou, W., Zhang, B., Luo, F., and Zhu, D. (2011). Complex permittivity and microwave absorbing properties of SiC fiber woven fabrics. J. Mater. Sci. 46 (8), 2709–2714. doi:10.1007/s10853-010-5140-x.

CrossRef Full Text | Google Scholar

Duan, W., Yin, X., Li, Q., Schlier, L., Greil, P., and Travitzky, N. (2016). A review of absorption properties in silicon-based polymer derived ceramics. J. Eur. Ceram. Soc. 36 (15), 3681–3689. doi:10.1016/j.jeurceramsoc.2016.02.002.

CrossRef Full Text | Google Scholar

Gian, D. S., Tavonatti, C., Kundanati, L., Pugno, N., and Biesuz, M. (2020). Effect of the pyrolysis atmosphere on the mechanical properties of polymer derived SiOC and SiCN. J. Am. Ceram. Soc. 103 (11), 6519–6530. doi:10.1111/jace.17392

CrossRef Full Text | Google Scholar

Li, Y., Liu, X., Nie, X., Yang, W., Wang, Y., Yu, R., et al. (2019). Multifunctional organic-inorganic hybrid aerogel for self-cleaning, heat-insulating, and highly efficient microwave absorbing material. Adv. Funct. Mater. 29 (10), 1807624. doi:10.1002/adfm.201807624.

CrossRef Full Text | Google Scholar

Liu, X., Yu, Z., Ishikawa, R., Chen, L., Liu, X., Yin, X., et al. (2017a). Single-source-precursor derived RGO/CNTs-SiCN ceramic nanocomposite with ultra-high electromagnetic shielding effectiveness. Acta Mater. 130, 83–93. doi:10.1016/j.actamat.2017.03.031.

CrossRef Full Text | Google Scholar

Liu, X., Yu, Z., Ishikawa, R., Chen, L., Yin, X., Ikuhara, Y., et al. (2017b). Single-source-precursor synthesis and electromagnetic properties of novel RGO-SiCN ceramic nanocomposites. J. Mater. Chem. C 5 (31), 7950–7960. doi:10.1039/c7tc00395a.

CrossRef Full Text | Google Scholar

Long, X., Shao, C., and Wang, J. (2019a). Continuous SiCN fibers with interfacial SiCxNy phase as structural materials for electromagnetic absorbing applications. ACS Appl. Mater. Interfaces 11 (25), 22885–22894. doi:10.1021/acsami.9b06819.

PubMed Abstract | CrossRef Full Text | Google Scholar

Long, X., Shao, C., Wang, S. S., and Wang, J. (2019b). Nanochannel diffusion-controlled nitridation of polycarbosilanes for diversified SiCN fibers with interfacial gradient-SiCxNy phase and enhanced high-temperature stability. ACS Appl. Mater. Interfaces 11 (13), 12993–13002. doi:10.1021/acsami.9b00828.

PubMed Abstract | CrossRef Full Text | Google Scholar

Mera, G., Riedel, R., Poli, F., and Müller, K. (2009). Carbon-rich SiCN ceramics derived from phenyl-containing poly (silylcarbodiimides). J. Eur. Ceram. Soc. 29 (13), 2873–2883. doi:10.1016/j.jeurceramsoc.2009.03.026.

CrossRef Full Text | Google Scholar

Mo, R., Yin, X., Ye, F., Liu, X., Cheng, L., and Zhang, L. (2017). Mechanical and microwave absorbing properties of Tyranno®ZMI fiber annealed at elevated temperatures. Ceram. Int. 43 (12), 8922–8931. doi:10.1016/j.ceramint.2017.04.030.

CrossRef Full Text | Google Scholar

Prasad, R. M., Mera, G., Morita, K., Müller, M., Kleebe, H.-J., Gurlo, A., et al. (2012). Thermal decomposition of carbon-rich polymer-derived silicon carbonitrides leading to ceramics with high specific surface area and tunable micro-and mesoporosity. J. Eur. Ceram. Soc. 32 (2), 477–484. doi:10.1016/j.jeurceramsoc.2011.08.020.

CrossRef Full Text | Google Scholar

Sarkar, S., Gan, Z., An, L., and Zhai, L. (2011). Structural evolution of polymer-derived amorphous SiBCN ceramics at high temperature. J. Phys. Chem. C 115 (50), 24993–25000. doi:10.1021/jp203287h.

CrossRef Full Text | Google Scholar

Storch, M., Vrankovic, D., Graczyk-Zajac, M., and Riedel, R. (2018). The influence of pyrolysis temperature on the electrochemical behavior of porous carbon-rich SiCN polymer-derived ceramics. Solid State Ionics 315, 59–64. doi:10.1016/j.ssi.2017.11.032.

CrossRef Full Text | Google Scholar

Widgeon, S., Mera, G., Gao, Y., Stoyanov, E., Sen, S., Navrotsky, A., et al. (2012). Nanostructure and energetics of carbon-rich SiCN ceramics derived from polysilylcarbodiimides: role of the nanodomain interfaces. Chem. Mater. 24, 1181–1191. doi:10.1021/cm2038238.

CrossRef Full Text | Google Scholar

Ye, F., Zhang, L., Yin, X., Zhang, Y., Kong, L., Li, Q., et al. (2013). Dielectric and EMW absorbing properties of PDCs-SiBCN annealed at different temperatures. J. Eur. Ceram. Soc. 33 (8), 1469–1477. doi:10.1016/j.jeurceramsoc.2013.01.006.

CrossRef Full Text | Google Scholar

Zhao, B., Guo, X., Zhao, W., Deng, J., Shao, G., Fan, B., et al. (2016). Yolk–shell Ni@SnO2 composites with a designable interspace to improve the electromagnetic wave absorption properties. ACS Appl. Mater. Interfaces 8 (42), 28917–28925. doi:10.1021/acsami.6b10886.

PubMed Abstract | CrossRef Full Text | Google Scholar

Zickler, G. A., Smarsly, B., Gierlinger, N., Peterlik, H., and Paris, O. (2006). A reconsideration of the relationship between the crystallite size La of carbons determined by X-ray diffraction and Raman spectroscopy. Carbon 44 (15), 3239–3246. doi:10.1016/j.carbon.2006.06.029.

CrossRef Full Text | Google Scholar

Keywords: SiCN fibers, microstructural evolution, dielectric properties, electromagnetic wave absorbing, high temperature

Citation: Long X, Zhang S, Shao C, Wang B and Wang Y (2020) Effects of Heat-Treatment on the Microstructure, Electromagnetic Wave Absorbing Properties, and Mechanical Properties of SiCN Fibers. Front. Mater. 7:563891. doi: 10.3389/fmats.2020.563891

Received: 20 May 2020; Accepted: 22 October 2020;
Published: 24 November 2020.

Edited by:

Biao Zhao, Zhengzhou University of Aeronautics, China

Reviewed by:

Abu Zayed M. Saliqur Rahman, The Ohio State University, United States
Xiaomeng Fan, Northwestern Polytechnical University, China

Copyright © 2020 Long, Zhang, Shao, Wang and Wang. This is an open-access article distributed under the terms of the Creative Commons Attribution License (CC BY). The use, distribution or reproduction in other forums is permitted, provided the original author(s) and the copyright owner(s) are credited and that the original publication in this journal is cited, in accordance with accepted academic practice. No use, distribution or reproduction is permitted which does not comply with these terms.

*Correspondence: Changwei Shao, chwshao@126.com; Yingde Wang, wangyingde@nudt.edu.cn

Disclaimer: All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article or claim that may be made by its manufacturer is not guaranteed or endorsed by the publisher.