AUTHOR=Meng Yu , Zhu Xiaofei , Meng Jiao , Bai Jinghe , Chen Ruyi , Zhou Defeng , Wang Ning , Tian Dan 

TITLE=Heterointerface Effect in Accelerating the Cathodic Oxygen Reduction for Intermediate-Temperature Solid Oxide Fuel Cells

JOURNAL=Frontiers in Chemistry

VOLUME=10

YEAR=2022

URL=https://www.frontiersin.org/journals/chemistry/articles/10.3389/fchem.2022.959863

DOI=10.3389/fchem.2022.959863

ISSN=2296-2646

ABSTRACT=<p>A solid-state mixing method was adopted to prepare a new Pr<sub>0.8</sub>Sr<sub>0.2</sub>Fe<sub>0.7</sub>Ni<sub>0.3</sub>O<sub>3−δ</sub>-Pr<sub>1.2</sub>Sr<sub>0.8</sub>Fe<sub>0.4</sub>Ni<sub>0.6</sub>O<sub>4+δ</sub> (PSFN<sub>113-214</sub>) composite cathode oxide for the solid oxide fuel cells (SOFCs). Herein, heterointerface engineering was investigated for the performance enhancement. It was found that the oxygen vacancy content could be increased by mixing the PSFN<sub>214</sub> with PSFN<sub>113</sub>, which gave rise to the formation of a heterostructure, and resulted in the promotion of oxygen ion transport as well as the specific surface area. The optimum mixing ratio 5:5 resulted in the highest oxygen vacancy content and the largest specific surface area, indicating the strongest interface effect. Polarization resistance of PSFN<sub>113-214</sub> (5:5) was 0.029 Ω cm<sup>2</sup> at 800°C, which was merely 24% of PSFN<sub>113</sub> and 39% of PSFN<sub>214</sub>. The corresponding maximum power density was 0.699 W cm<sup>−2</sup>, which was nearly 1.44 times of PSFN<sub>113</sub> and 1.24 times of PSFN<sub>214</sub>. Furthermore, the voltage attenuation rate after 100 h was merely 0.0352% h<sup>−1</sup>. Therefore, the new PSFN<sub>113-214</sub> composite could be a prospective cathode oxide for SOFCs.</p>