Investigation on the Controllable Synthesis of Colorized and Magnetic Polystyrene Beads With Millimeter Size via In Situ Suspension Polymerization

Juntao YanJuntao Yan1Hua WuHua Wu1Pan HuangPan Huang1Yourong WangYourong Wang1Bowang ShuBowang Shu2Xiaofang LiXiaofang Li1Deng DingDeng Ding1Ya SunYa Sun1Chunlei Wang
Chunlei Wang1*Jian Wu
Jian Wu2*Linbing SunLinbing Sun3
  • 1College of Chemistry and Environmental Engineering, Wuhan Polytechnic University, Wuhan, China
  • 2College of Advanced Interdisciplinary Studies, National University of Defense Technology, Changsha, China
  • 3College of Chemical Engineering, Nanjing Tech University, Nanjing, China

A series of colorized and magnetic polystyrene/Fe3O4 (PS/Fe3O4) composite beads with millimeter size are successfully synthesized by introducing hydrophobic Fe3O4 via in situ suspension polymerization of styrene for the first time. Effects of the hydrophobic Fe3O4 content, stirring speed, and surfactant dosage on the macromorphology and particle size of PS/Fe3O4 beads are systematically investigated to realize the controllable synthesis. Moreover, three kinds of hydrophobic pigments are also employed to synthesize colorized polystyrene, which demonstrates the versatility, simplicity, and wide applicability of the proposed method. Scanning electron microscopy (SEM) and element mapping (EM) images demonstrated that the hydrophobic Fe3O4 is well dispersed in the polystyrene matrix. Thermogravimetric analysis (TGA) shows that the resultant PS/Fe3O4 beads possess a better thermal stability than neat PS. PS/Fe3O4 beads have a promising application in the fields of colorized extruded PS board, colorized expanded PS foam particle, and board.

Introduction

As is well known that polystyrene (PS) is one of the most common plastics in the modern chemical industry, and expanded polystyrene (EPS) foam is widely used in building insulation, packaging materials, sound insulation materials, decorative materials, and other fields (Xing et al., 2013; Sun and Lawrence, 2017; Huang et al., 2018; Ito et al., 2018; Wang et al., 2018; Peng et al., 2020; Hamann et al., 2021; Cao et al., 2022; Liu and Peng, 2022). With the increasing competition of PS and EPS markets at home and abroad, requirements for the performance and function of PS and EPS are put forward in the above-mentioned fields. There are many researchers paying attention to the fabrication of multifunctional PS and EPS.

Generally speaking, many inorganic fillers are incorporated into the PS matrix to fabricate PS composites, which are expected to possess combined properties of both inorganic filler and PS; the inorganic filler can impart the PS with unique properties, such as electrical, mechanical, magnetic, colorful, thermal, flame retarding, and so on. Many PS/inorganic hybrids with improved properties have been synthesized by different methods. For example, Zhou et al. (2016) have synthesized graphene-based smoke suppression agents by a solvothermal method for improving the flame retardation of polymer composites, and the graphene-based smoke suppression agent is incorporated into the PS matrix by a masterbatch melt blending method to enhance the thermal stability and flame retardance of PS. Chen et al. (2003) have synthesized the conductive PS/graphite nanosheet nanocomposite films via in situ polymerization of monomer in the presence of sonicated expanded graphite during sonication. Nyambo et al. (2008) have achieved the flame-retarded PS by incorporating the layered double hydroxides and ammonium polyphosphate via the melt blending method. Yang et al. (2014) have prepared PS/attapulgite nanocomposites via in situ suspension polymerization in the presence of functionalized attapulgite with the redox initiation system; the mechanical properties and thermal stability of PS/attapulgite nanocomposites are effectively improved due to the stronger interfacial bonding. Faraguna et al. (2017) have achieved PS nanocomposites with functionalized carbon nanotubes by the melt and solution mixing process, and they exhibited an in-depth investigation on the dispersion, melt rheology, and electrical and thermal properties of PS-MWCNT nanocomposites, which are prepared by the melt and solution mixing method. Azizi et al. (2019) have synthesized PS-modified GO using an ammonium persulfate initiator, which is used as an adsorbent for the removal of three anionic dyes from wastewater. Nikpour et al. (2022) have fabricated PS/Fe-MOF composite beads by a two-step method consisting of the synthesis of Fe-MOF and filling Fe-MOF into the PS matrix by the phase inversion method; the achieved material is utilized to uptake and separate various pollutions. Hong et al. (2009) have fabricated PS/Fe3O4 composite particles with a diameter of 200 nm via inverse emulsion polymerization. Liu et al. (2011) have obtained monodisperse magnetic PS/Fe3O4 microspheres with a mean size of 1078 nm, which is prepared by the soap-free emulsion polymerization and magnetic colloid swelling polymerization. Naeemikhah et al. (2019) have synthesized the magnetic crosslinked PS with hydrophilic nature by the solvent-free surface-initiated atom transfer radical polymerization method, and the organically modified Fe3O4 is used as the polyaddition initiator.

Many studies regarding functional PS composites have been reported (Yan et al., 2011a; Yan et al., 2011b; Zheng et al., 2013; Umar et al., 2014; He et al., 2015; Wang et al., 2018; An et al., 2019; Li et al., 2019; Shi et al., 2021; Wang et al., 2022a; Wang et al., 2022b); moreover, PS/Fe3O4 nanomaterials and micrometer size composites have been synthesized in the above studies; however, there is no report regarding the colorized and magnetic PS/Fe3O4 beads with millimeter size. To the best of our knowledge regarding functional PS, many colorful extruding polystyrenes (XPS) are achieved by blending the PS with organic or inorganic pigments. However, due to the instability and flammability of the organic pigment, its application in PS is therefore restricted. In addition, the blending method results in poor mixing owing to the interfacial incompatibility between PS beads and inorganic pigments. Therefore, an effective method aimed at solving the above disadvantages is of great necessity.

Black pigment Fe3O4 (iron black) particles have widespread applications in the coating industry, coloration, magnetic bioseparation, drug delivery, targeted drug, toner preparation, and construction industry due to their excellent properties of alkali resistance, black color, magnetic properties, nontoxicity, superparamagnetism, high saturation magnetization, high magnetic susceptibility, and biocompatibility (Wang et al., 2011; Wang et al., 2013; Yu et al., 2017; Rahimi et al., 2020; Fang et al., 2021; Hou et al., 2022; Wang et al., 2022a). Moreover, Fe3O4 particles are naturally hydrophilic due to the abundant hydroxyl groups on the particle surface, and the hydrophobic Fe3O4 can be easily obtained by the surface modification to improve its interfacial compatibility with the monomer and polymer matrices.

In the present study, the oleic acid-modified Fe3O4 (OA-Fe3O4) particles with hydrophobic features are introduced into the PS matrix via the in situ suspension polymerization of styrene, by which the magnetic and color properties of Fe3O4 are imparted to PS/Fe3O4 composite beads. Different Fe3O4 contents and color degrees of PS/Fe3O4 composite beads with millimeter size can be obtained by regulating the Fe3O4 dosage. Effects of the OA-Fe3O4 dosage, surfactant dosage and stirring speed on the macromorphology, particle size, and size distribution of PS/Fe3O4 composite beads are systematically investigated to realize the controllable synthesis, and the optimum process conditions are determined. Scanning electron microscopy (SEM) and element mapping (EM) images demonstrate that the modified Fe3O4 is well dispersed in the PS/Fe3O4 composite beads; thermogravimetric analysis (TGA) shows that the resultant PS/Fe3O4 composite beads possess a better thermal stability than bare PS. The novelty of this article lies in the synthesis of colorized and magnetic PS/Fe3O4 beads with millimeter size by the in situ suspension polymerization technique, which may bring about a promising future in the large-scale production of colorful and magnetic PS/Fe3O4 composite beads or EPS foam due to the simplicity and versatility of the synthetic process.

Experimental Section

Materials

Styrene (St, 99%, Shanghai Chemical Reagent Company, China) was distilled under a nitrogen atmosphere and reduced pressure prior to polymerization. Benzoyl peroxide (BPO, Sinopharm Chemical Reagent Co., Ltd., China) was purified by recrystallization before usage. Calcium-trihydroxy phosphate, tertiary calcium phosphate (TCP), sodium dodecylbenzene sulfonate (SDBS), and sodium sulfate (Na2SO4) were used as received. Oleic acid (OA, Tianjin Guangfu Chemical Reagents Company) and pentane (Sinopharm Chemical Reagents Company) were the analytical reagents. PVA with a polymerization degree of 1750 ± 50 was supplied by Sinopharm Chemical Reagents Company. The water used in this experiment was distilled followed by deionization. In addition, Fe3O4 (20 nm, 99%) was supplied by Nanjing AiPuRui Nano Material Co., Ltd. Three kinds of iron oxides, red, dark green, and China blue pigments, were supplied by Zhejiang Taizhu Group Co., Ltd.

Surface Modification of Fe3O4 Magnetic Nanoparticles

The hydrophobic Fe3O4 could be achieved by a facile water phase modification process. Firstly, 4 g of Fe3O4 nanoparticles and 150 ml of deionized water were put into a 250 ml three-neck flask equipped with a mechanical stirrer; the suspension was fully stirred at 400 rpm for 20 min, and then a certain amount of OA that used as a modifying agent was charged into the mixture system; thereafter, the flask was placed into a water bath at a constant temperature of 80°C for 1 h. The product was obtained by a magnet and was washed by deionized water and EtOH continuously for two times to remove the physically adsorbed superfluous oleic acid, after which the black precipitate was dispersed in cyclohexane and dried by nitrogen gas. Then, the OA-modified Fe3O4 with a strong hydrophobic surface was achieved and was denoted by OA-Fe3O4, which could significantly ameliorate the compatibility between inorganic particles and styrene monomer. Hydrophobic Fe2O3, dark green, and China blue inorganic pigments were also modified similar to the above procedure.

Synthesis of PS/Fe3O4 Beads via In Situ Suspension Polymerization

The colorized PS/Fe3O4 beads were successfully synthesized via in situ suspension polymerization of styrene in the presence of OA-Fe3O4, using BPO as an initiator, PVA as organic stabilizers, and TCP and Na2SO4 as inorganic stabilizers. The complex stabilizers of TCP and PVA were used to hinder the coalescence and break-up of droplets during the suspension polymerization in this article. SDBS aqueous solution was used to reduce the surface tension of the suspending medium H2O and improve the stabilization of the inorganic stabilizer at the interface of styrene and H2O. The overall schematic procedure used to synthesize the colorized PS/Fe3O4 beads and EPS/Fe3O4 beads is illustrated in Figure 1; the detailed recipes and relevant physical parameters of the PS/Fe3O4 beads are summarized in Table 1, and the synthesis procedure was described as follows: as-prepared PS/Fe3O4 beads were immersed in a blowing agent pentane to obtain the expandable polystyrene/Fe3O4 (EPS/Fe3O4) beads by means of a two-step method. Moreover, EPS/Fe3O4 beads can also be directly obtained when the blowing agent pentane was impregnated during in situ suspension polymerization of styrene by means of a one-step method, and these two methods will be discussed in detail in our future research.

FIGURE 1
www.frontiersin.org

FIGURE 1. Schematic showing the synthesis of colorized PS/Fe3O4 beads and EPS/Fe3O4 beads.

TABLE 1
www.frontiersin.org

TABLE 1. Recipes of the synthesis of PS/Fe3O4 composite beads.

To a 250 ml four-necked round-bottom flask fitted with a mechanical overhead stirrer and a condenser, 80 ml deionized water, 0.14 g TCP, 0.30 g Na2SO4, 10 ml of 0.02 wt% SDBS aqueous solution, and 10 ml of 4 wt% PVA aqueous solution were charged one by one. The above mixture was stirred at 200 rpm to activate the dispersant. In the following procedure, different dosages of OA-Fe3O4 were dispersed in the styrene and initiator BPO solution (0.24 g BPO was dissolved in 20 g styrene monomer) to form a styrene-based magnetic fluid, and then the styrene-based magnetic fluid was transferred into the above flask. The stirrer was fixed at a certain speed, and the reaction system was heated to 85°C; one portion of 0.2 g TCP was supplemented when the temperature reached 85°C and the other portion of 0.2 g TCP was supplemented after 1 h to prevent the polymerized PS/Fe3O4 beads from agglomeration with the increasing viscosity. The polymerization reaction was terminated when the colorized PS/Fe3O4 beads became hardened by sampling from the flask. Finally, the colorized PS/Fe3O4 beads were washed by dilute acid solution and water to remove the dispersant on the surface of PS/Fe3O4 beads.

Characterization

Static Contact Angle

Static contact angles of water on the powder-pressed pellets were measured with a JC2000C2 contact angle goniometer (Shanghai Zhongchen Powereach Company, China) by the sessile drop method using a microsyringe at 25°C. More contact angles were averaged to get a reliable value for each sample.

Dynamic Light Scattering

The particle sizes and their distribution of Fe3O4 and OA-Fe3O4 were measured by dynamic light scattering (DLS) with a Malven zetasizer 3000 HSA particle sizer.

X-Ray Diffraction

X-ray diffraction (XRD) data were collected on a Rigaku D/MAX 2550 diffractometer with Cu Ka radiation.

Fourier Transform Infrared

Fourier transform infrared (FTIR) spectra of KBr powder-pressed pellets were recorded on a Nicolet Instruments Research Series 5PC Fourier transform infrared spectrometer.

Scanning Electron Microscope

The PS/Fe3O4 beads were broken at low temperature by liquid nitrogen to ensure a brittle fracture. The cross section was sprayed with gold to release the polymer surface charge for increased contrast. The cross-sectional morphology was imaged on a TESCAN MAIA 3 LMH scanning electron microscope (SEM) to examine the micro-structure. The accelerated voltage was 15 kV.

Energy-Dispersive Spectrometer and Element Mapping

Energy-dispersive spectrometer (EDS) and EM are attached to the SEM apparatus, which were employed to examine the dispersity of the modified Fe3O4 in PS/Fe3O4 beads.

Thermogravimetric Analysis

TGA was performed with a Pyris 1TGA (Perkin Elmer) under a nitrogen atmosphere at a heating rate of 10°C/min from 25 to 600°C. PS/Fe3O4 beads were milled into powder, and the sample weight was about 10 mg.

Results and Discussion

Effect of OA Dosage on the Hydrophobicity of OA-Fe3O4

Static water contact angle test was employed to evaluate the effect of OA dosage (relative to the Fe3O4 mass) on the surface property of Fe3O4, as well as to determine the optimum modifier dosage. As seen from Figure 2, when the water droplet was dropped onto a thin pellet of Fe3O4 without modification, as shown in Figure 2A, no stable water droplet was formed and the water was imbibed in the pellet, while the static contact angle of the OA-Fe3O4 increased with the increase of OA dosage, and the static contact angles of OA-Fe3O4 samples in Figures 2B–D were about 92.49°, 122.5°, and 131.68°, respectively. And the results of the static contact angle test indicated that the surface property of Fe3O4 was changed from hydrophilic to hydrophobic after the modification by OA molecules, which facilitated the dispersion of OA-Fe3O4 in the styrene monomer due to the improved compatibility. Considering the unobvious change of the static contact angle for the OA dosage of 1 wt% and 1.5 wt%, thus the OA dosage of 1 wt% was determined.

FIGURE 2
www.frontiersin.org

FIGURE 2. Water contact angle of Fe3O4 modified by OA with different dosages: (A) 0, (B) 0.5 wt%, (C) 1 wt%, and (D) 1.5 wt%.

Particle Size Analysis of Unmodified Fe3O4 and OA-Fe3O4

In order to examine the modification effect of Fe3O4, DLS measurement was utilized to provide direct evidence. The same weights of Fe3O4 and OA-Fe3O4 were dispersed in H2O and styrene monomer, respectively. The particle size and its distribution of Fe3O4 and OA-Fe3O4 are shown in Figure 3. The mean sizes of Fe3O4 and OA-Fe3O4 were 183.9 and 96.3 nm, and their size distribution widths were 33.7 and 25.6, respectively. It could be seen that both the average particle size and its distribution width distinctly decreased after the modification, which suggested that OA-Fe3O4 possessed a good interfacial compatibility with styrene monomer, and the particle agglomeration was weakened. Figure 4 shows the optical photography of OA-Fe3O4 with different contents dispersed in styrene monomer after 1 month, which demonstrated that the OA-Fe3O4 possessed a good dispersed stability in styrene monomer; moreover, interestingly, the different color of styrene could be achieved by tuning the OA-Fe3O4 dosage. The above two aspects ensured that the OA-Fe3O4 particles were well dispersed in the PS matrix by in situ suspension polymerization.

FIGURE 3
www.frontiersin.org

FIGURE 3. Particle size and its distribution: (A) unmodified Fe3O4 and (B) OA-Fe3O4.

FIGURE 4
www.frontiersin.org

FIGURE 4. Optical photography of OA-Fe3O4 dispersed in styrene monomer with different contents: (A) 0.8 wt% and (B) 1.6 wt%.

Effect of OA-Fe3O4 Content on the Macromorphology and Particle Size of PS/Fe3O4 Beads

Uniform particle size and narrow size distribution were expected for the industrial large-scale production of expandable PS. It is because of the fact that a relatively wide size distribution might require a repeated size classification procedure, which is high in cost, time-consuming, and resulted in poor production efficiency. Therefore, the effect of the OA-Fe3O4 content on the macromorphology, particle size, and size distribution of PS/Fe3O4 beads was systematically investigated. As seen from optical images of the PS/Fe3O4 composite beads in Figure 5, a series of PS/Fe3O4 composite beads with a smooth surface and spherical appearance were successfully synthesized by varying the OA-Fe3O4 content at the same synthetic condition. First, the color degree of PS/Fe3O4 composite beads became deeper with the increase of the OA-Fe3O4 content. When the OA-Fe3O4 content was 0.4 wt%, light yellow PS/Fe3O4 beads in Figure 5A were achieved. When the OA-Fe3O4 content increased from 0.8 to 1.2 and to 1.6 wt%, yellow, brown, and dark brown PS/Fe3O4 beads were obtained in Figures 5B–D, respectively. Thus, PS/Fe3O4 beads with different color degrees could be realized by tuning the OA-Fe3O4 content, which could be fabricated into various color PS products.

FIGURE 5
www.frontiersin.org

FIGURE 5. Optical photography showing the macromorphology of PS/Fe3O4 composite beads obtained with different contents of OA-Fe3O4: (A) 0.4 wt%, (C) 0.8 wt%, (E) 1.2 wt%, and (G) 1.6 wt%. Panels (B), (D), (F), and (H) are the statistical histograms showing the size distribution of panels (A), (C), (E), and (G), respectively.

ImageJ software was employed to measure the diameter of all the PS/Fe3O4 beads in Figures 5A,C,E,G; the statistical histogram results of the corresponding samples are presented in Figures 5B,D,F,H, respectively. And the detailed results are listed in Table 2. It has been noted that the particle size distribution of PS/Fe3O4 beads in Figure 5A mainly concentrated in the range of 0.9–1.3 mm, accounting for 87.08%, and its mean size was 1.08 mm. The particle size distribution of PS/Fe3O4 beads in Figure 5C mainly concentrated in the range of 1.1–1.5 mm, accounting for 84.72%, and its mean size was 1.27 mm. The particle size distribution of PS/Fe3O4 beads in Figure 5E mainly concentrated in the range of 1.05–1.65 mm, accounting for 86.17%, and its mean size was 1.35 mm. The particle size distribution of PS/Fe3O4 beads in Figure 5G mainly concentrated in the range of 1.05–1.65 mm, accounting for 89.88%, and its mean size was 1.40 mm. Based on the above results, it has been found that the particle size distribution became wider with the increase in the OA-Fe3O4 content, and the mean size became larger as well. This phenomenon could be explained as follows: on the one hand, it is known that polymerization reaction occurred within the monomer droplet for the suspension polymerization of styrene, and the viscosity of the polymerized monomer droplet increased as the monomer conversion increased during the polymerization reaction, especially during the auto-acceleration stage of polymerization reaction (Yan et al., 2011a); thus, the coalescence possibility of the polymerized monomer droplet increased as well. On the other hand, for every polymerized monomer droplet unit containing OA-Fe3O4 nanoparticles, the increasing OA-Fe3O4 content also resulted in the viscosity increment of the polymerized monomer droplet, because the structural formula of oleic acid was CH3(CH2)7CH = CH(CH2)7COOH, and there was a “-CH = CH-” double bond in the structural formula; the “-CH = CH-” double bond took part in the polymerization reaction of styrene monomer, which might accelerate the polymerization rate of a monomer.

TABLE 2
www.frontiersin.org

TABLE 2. Size distribution of PS/Fe3O4 composite beads.

Effect of Stirring Speed on the Macromorphology and Particle Size of PS/Fe3O4 Composite Beads

It is known that the control of droplet coalescence and break-up rates are critical for the synthesis of polymer beads with uniform size. In order to realize the controllable synthesis of PS/Fe3O4 composite beads with desired particle size and narrow size distribution, the effect of stirring speed on the macromorphology and particle size of PS/Fe3O4 composite beads was examined, and a series of PS/Fe3O4 composite beads with an OA-Fe3O4 content of 2 wt% were synthesized at different stirring speeds according to the recipes in Table 1. As shown in Figure 6, the achieved PS/Fe3O4 composite beads were black with a smooth surface. In addition, the statistical histogram of the achieved PS/Fe3O4 composite beads is shown in Figure 6, and the detailed results are listed in Table 2, which vividly showed that the stirring speed could regulate the particle size and size distribution of PS/Fe3O4 composite beads. And the particle size distribution of the achieved PS/Fe3O4 beads in Figures 6A,C,E mainly concentrated in the range of 1.3–1.7, 1.1–1.5, and 0.9–1.3 mm, accounting for 93.05, 97.42, and 90.88%, respectively, and their respective mean diameters were 1.47, 1.29, and 1.15 mm. Based on the above analysis results, it could be concluded that the narrow size distribution was maintained, and the mean diameter decreased with increasing stirring speed; it is attributed to the increase in the stirring speed, which resulted in the increase in the polymerizing monomer droplet break-up rate and effectively prevented the monomer droplets from coalescence. Therefore, the better control of coalescence and break-up rates was therefore critical for the production of PS/Fe3O4 beads with uniform size.

FIGURE 6
www.frontiersin.org

FIGURE 6. Optical photography showing the macromorphology of PS/Fe3O4 composite beads with the OA-Fe3O4 content of 2 wt% obtained at different stirring speeds: (A) 180 rpm, (C) 210 rpm, and (E) 240 rpm. Panels (B), (D), and (F) are the histograms showing the size distribution of panels (A), (C), and (E), respectively.

Effect of Sodium Dodecylbenzene Sulfonate Dosage on the Particle Size of PS/Fe3O4 Composite Beads

Extensive studies had demonstrated that the major issue in the suspension polymerization system was the formation of stable monomer droplets, preferably having a uniform particle size and a narrow particle size distribution. The mean size of the polymer beads was expected to be approximately the same as that of the initial monomer droplets. If the initial monomer droplet was monodisperse, then suspension polymerization would result in a relatively narrow particle size distribution. In order to further explore the effect of surfactant SDBS dosage on the stability of styrene monomer droplets, the PS/Fe3O4 beads of samples 8 and 9 were thus synthesized only by varying the SDBS dosage according to the recipe in Table 1. As shown in Figures 7A,C, the as-prepared PS/Fe3O4 composite beads possessed an excellent spherical profile, a smooth surface, a uniform size, and a black luster. As seen from Figures 7B,D, the particle size distribution of the achieved PS/Fe3O4 beads mainly concentrated in the range of 0.9–1.1 and 0.7–0.9 mm, accounting for 90.41 and 89.01%, respectively, and their respective mean diameters were 0.97 and 0.79 mm. It is suggested that the narrow size distribution was maintained, and the mean diameter decreased with the increase in the surfactant SDBS dosage; this is due to the fact that surfactant SDBS could improve the protective efficacy of the inorganic stabilizer TCP and control the contact angle, which played a critical role in controlling the adsorption of inorganic stabilizers at the oil/water interface. Therefore, the stability and size of initial styrene monomer droplets were highly dependent on the surfactant SDBS dosage. There is a synergistic effect between surfactant SDBS and the inorganic stabilizer TCP, which codetermined the controllable synthesis of PS/Fe3O4 composite beads.

FIGURE 7
www.frontiersin.org

FIGURE 7. Optical photography showing the macromorphology of PS/Fe3O4 composite beads obtained with different dosages of SDBS aqueous solution: (A) 10 ml and (C) 20 ml. Panels (B) and (D) are the histograms showing the size distribution of panels (A) and (C), respectively.

Fourier Transform Infrared Spectrum

Fe3O4, OA-Fe3O4 nanoparticles, and PS/Fe3O4 composite beads were analyzed by FT-IR spectrum in Figure 8. The peaks at 578 and 1631 cm−1 in Figure 8A were the Fe-O vibration and hydroxyl adsorption of Fe3O4 (Wang et al., 2013). The curve seen in Figure 8B of the OA-Fe3O4 nanoparticle exhibited not only the characteristic adsorption peaks of Fe3O4 (578 cm−1) and OA (2860 and 2930 cm−1) but also the characteristic vibration peaks of RO-Fe (1452 cm−1), and the results suggested that the OA molecule was successfully grafted on the Fe3O4 nanoparticles. Based on the curve (Figure 8C) of the PS/Fe3O4 composite bead, it was noted that there were intense specific adsorption peaks of PS (3065–2830, 1601–1350, and 700 cm−1), which were attributed to the stretching vibrations of the aromatic C–H in-plane, the stretching vibrations of the aromatic C–C, and the bending vibrations of the aromatic C–C out-of-plane, respectively (Wang et al., 2010; Yang et al., 2010); moreover, the characteristic adsorption peak of Fe3O4 (578 cm−1) was detected in Figure 8C, which further demonstrated that PS/Fe3O4 composite beads were successfully synthesized via in situ suspension polymerization.

FIGURE 8
www.frontiersin.org

FIGURE 8. FT-IR spectrum: (A) Fe3O4, (B) OA-Fe3O4, and (C) PS/Fe3O4 composite beads.

X-Ray Diffraction Pattern Analysis

XRD patterns of Fe3O4 (a), OA-Fe3O4 (b), and PS/Fe3O4 (c) composite beads are shown in Figure 9. Based on Figure 9A, the characteristic diffraction peaks at 2 Theta of 30.2°, 35.7°, 43.3°, 53.6°, 57.2°, and 62.6° were assigned to (220), (311), (400), (422), (511), and (440) lattice planes of Fe3O4, respectively. It was clearly observed that XRD patterns in both Figures 9B,C possessed the same characteristic diffraction peak of Fe3O4, besides a broad peak at 2 Theta of 18–20° that corresponded to the amorphous peak of PS, which suggested that the crystal structure of Fe3O4 was not changed during the surface modification of Fe3O4 and in situ suspension polymerization of PS/Fe3O4. On the basis of the above analysis, it was confirmed that Fe3O4 nanoparticles were successfully incorporated into the PS matrix.

FIGURE 9
www.frontiersin.org

FIGURE 9. XRD patterns: (A) Fe3O4, (B) OA-Fe3O4, and (C) PS/Fe3O4 composite beads.

Scanning Electron Microscopy, Energy-Dispersive Spectrometer, and Element Mapping Analysis

A key issue in the synthesis of PS/Fe3O4 composite beads was to disperse OA-Fe3O4 nanoparticles within the PS matrix homogeneously; thus, SEM, EDS, and EM were employed to observe the cross-sectional morphology of PS/Fe3O4 composite beads and the distribution of OA-Fe3O4 in the PS matrix. As seen from Figures 10A,B, it is noted that the Fe3O4 nanoparticles were well distributed in the PS matrix without obvious aggregation and phase separation phenomenon, and the mean size of Fe3O4 was about 95 nm, which was consistent with the DLS measurement result of OA-Fe3O4. The EDS of PS/Fe3O4 composite beads in Figure 10E displayed that besides C and Au peaks from the conductive tape, PS, and sprayed Au, only Fe and O were detected, which demonstrated that the Fe3O4 nanoparticles existed in the PS/Fe3O4 composite beads. For proving the distribution of Fe3O4 in the PS matrix, the EM of PS/Fe3O4 composite beads is examined in Figures 10C,D; the small plots denoted the distribution of each element in the PS/Fe3O4 matrix, and it is obvious that the characteristic Fe and O elements of Fe3O4 could be clearly observed in the EM of PS/Fe3O4 composite beads with a homogeneous distribution. Based on the above analysis, it is proved that the OA-Fe3O4 nanoparticles were successfully incorporated into PS beads and were well distributed in the PS matrix, and this phenomenon was attributed to the modification of Fe3O4 by OA molecules, which immensely improved the compatibility between the styrene monomer and Fe3O4 nanoparticles; it is demonstrated that the proposed method of in situ suspension polymerization was feasible for synthesizing the PS/Fe3O4 composite beads.

FIGURE 10
www.frontiersin.org

FIGURE 10. The cross-sectional morphology of PS/Fe3O4: (A,B) SEM images, (C) and (D) EM images of O and Fe, and (E) EDS image.

Magnetic Property Testing

It is well known that the expanded PS foam particles were very easy to float due to their lightweight, static electricity, and airflow, which were very difficult to collect. The incorporation of Fe3O4 nanoparticles into the PS matrix not only imparted different color degrees to PS that could manufacture various color PS products, but also endowed with excellent magnetic property. Therefore, both the different color degree and excellent magnetic property of the PS/Fe3O4 composite beads could provide many functions for different products and applications, such as color PS beads, color-extruded PS board, color-expanded PS foam board, magnetic collection of PS/Fe3O4 composite beads or foam particles, product labeling for distinguishing different product classifications, and so on. As shown in Figure 11A, the PS/Fe3O4 composite beads without external magnetic fields were still at the bottom of the centrifuge tube. However, PS/Fe3O4 composite beads were easily collected by a magnet, and it could be concluded that the PS/Fe3O4 composite beads possessed excellent magnetic property.

FIGURE 11
www.frontiersin.org

FIGURE 11. Optical photographs showing magnetic property: (A) PS/Fe3O4 beads and (B) the directed movement under an external magnetic field.

Thermal Stability Behaviors

In order to investigate the effect of Fe3O4 dosage on the thermal stability of the resultant PS/Fe3O4 composite beads, TGA measurement was thus employed, and the TGA curves of pure PS, PS/Fe3O4 (0.8 wt%), and PS/Fe3O4 (2 wt%) composite beads are depicted in Figure 12. It could be seen that the thermal stability of pure PS, PS/Fe3O4 (0.8 wt%), and PS/Fe3O4 (2 wt%) was similar before 270°C. However, when the weight residual was 80%, the decomposition temperatures of curves (a)–(c) in Figure 12 were about 354.5, 368.5, and 379°C, respectively. When the weight residual was 50%, the decomposition temperatures of curves (a)–(c) were about 387, 393, and 402°C, respectively. On the basis of the above analysis, for the same weight residual, the decomposition temperature of PS/Fe3O4 composite beads was shifted toward higher temperatures with the increasing Fe3O4 content in comparison with pure PS beads, which demonstrated that PS/Fe3O4 composite beads possessed a better thermal stability than that of pure PS. This amelioration in the thermal stability of PS/Fe3O4 composite beads should be attributed to the incorporation of OA-Fe3O4 nanoparticles into the PS matrix, and this phenomenon could be interpreted from the following two aspects. On the one hand, OA-Fe3O4 nanoparticles possessed an excellent compatibility with styrene, so the polymerization of the styrene monomer took place on the surface of OA-Fe3O4 nanoparticles, and the physical crosslinking could be formed among the polystyrene chain segments, so the motion of the PS chain segment was confined due to the high packing density of PS chains around the Fe3O4 nanoparticles; on the other hand, the chemical bond might be formed between the polystyrene and Fe3O4 via the copolymerization of styrene and the double bond of OA molecular, so the Fe3O4 nanoparticles confined the movement of PS chain segments during the thermal degradation of polystyrene, both of which resulted in the improvement of thermal stability of PS/Fe3O4 composite beads. Similar improvement in the thermal stability of PS was observed when the modified Fe2O3 was incorporated into the PS matrix (Marinovic-Cincovic et al., 2006; Qiu et al., 2006; Qiu et al., 2007). Furthermore, the pure PS of curve (a) showed no residual weight due to complete decomposition; however, curves (b) and (c) exhibited weight residuals of about 0.76 and 1.97 wt%, respectively, which were almost identical with the original dosage; it is suggested that the Fe3O4 nanoparticles were successfully modified by the OA and fully incorporated into the PS matrix.

FIGURE 12
www.frontiersin.org

FIGURE 12. TGA curves: (A) PS, (B) PS/Fe3O4 with an Fe3O4 content of 0.8 wt% (sample 2), and (C) PS/Fe3O4 with an Fe3O4 content of 2 wt% (sample 5).

Investigation on the Applicability and Simplicity of Polymerization Method

A series of colorized, magnetic, and millimeter-sized PS/Fe3O4 beads were successfully synthesized via in situ suspension polymerization of styrene. A versatile, scalable, and facile method was firstly reported. Three kinds of different inorganic pigments were modified according to the modification process of Fe3O4, and different colored PS beads in Figure 13 were successfully achieved via in situ suspension polymerization, which demonstrates that the modification process and polymerization process possess good versatility and applicability. Consequently, our proposed method can be applied for the industrial large-scale production of colorized PS and EPS beads, and this method may be readily extended to synthesize other classes of colored magnetic polymer hybrids based on the modified Fe3O4, such as polyvinyl chloride, polymethyl methacrylate beads, and so on.

FIGURE 13
www.frontiersin.org

FIGURE 13. Colorized PS composite beads with different modified pigments: (A,B) iron oxide red, (C,D) dark green, and (E,F) China blue.

Conclusion

In this work, colorized and magnetic PS/Fe3O4 beads with millimeter size were first synthesized via in situ suspension polymerization of styrene. Effects of the modified Fe3O4 content, stirring speed, and surfactant dosage on the particle size of PS/Fe3O4 beads were systematically examined. The particle size, size distribution, and color degree can be easily regulated by changing the OA-Fe3O4 dosage. SEM and Fe and O EM results indicate that Fe3O4 is well dispersed in the PS/Fe3O4 bead. The proposed method can be applied for the industrial large-scale production of colorized PS and EPS beads. The process for synthesizing PS/Fe3O4 beads is extended to synthesize other three kinds of colorful PS beads, which demonstrate that our proposed process is versatile, scalable, and applicable to synthesize other classes of colorized and magnetic polymer hybrids based on the modified Fe3O4, such as polyvinyl chloride, polymethyl methacrylate beads, and so on.

Data Availability Statement

The raw data supporting the conclusions of this article will be made available by the authors without undue reservation.

Author Contributions

All authors listed have made a substantial, direct, and intellectual contribution to the work and have approved it for publication.

Funding

This work was financially supported by the Key Research and Development Project of Hubei Province (No. 2020BBB068), the Unveils List System Science and Technology Project of Hubei Provincial Science and Technology Department (No. 2021BEC016), the Central Committee Guides Local Science and Technology Development Special Project of Hubei Province (No. 2019ZYYD059), the National Natural Science Foundation of China (No. 52102111), and the Nature Science Foundation of Hubei Province (No. 2021CFB218).

Conflict of Interest

The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.

Publisher’s Note

All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors, and the reviewers. Any product that may be evaluated in this article, or claim that may be made by its manufacturer, is not guaranteed or endorsed by the publisher.

References

An, W., Yin, X., Cai, M., Gao, Y., and Wang, H. (2019). Influence of Vertical Channel on Downward Flame Spread Over Extruded Polystyrene Foam. Int. J. Therm. Sci. 145, 105991. doi:10.1016/j.ijthermalsci.2019.105991

CrossRef Full Text | Google Scholar

Azizi, A., Moniri, E., Hassani, A. H., Ahmad Panahi, H., and Miralinaghi, M. (2019). Polymerization of Graphene Oxide with Polystyrene: Non-Linear Isotherms and Kinetics Studies of Anionic Dyes. Microchemical J. 145, 559–565. doi:10.1016/j.microc.2018.11.021

CrossRef Full Text | Google Scholar

Cao, X., Jia, Z., Hu, D., and Wu, G. (2022). Synergistic Construction of Three-Dimensional Conductive Network and Double Heterointerface Polarization via Magnetic FeNi for Broadband Microwave Absorption. Adv. Compos. Hybrid Mater. 283. doi:10.1007/s42114-021-00415-w

CrossRef Full Text | Google Scholar

Chen, G., Wu, C., Weng, W., Wu, D., and Yan, W. (2003). Preparation of Polystyrene/Graphite Nanosheet Composite. Polymer 44, 1781–1784. doi:10.1016/s0032-3861(03)00050-8

CrossRef Full Text | Google Scholar

Fang, D., Jin, H., Huang, X., Shi, Y., Liu, Z., and Ben, S. (2021). PPy@Fe3O4 Nanoparticles Inhibit Tumor Growth and Metastasis through Chemodynamic and Photothermal Therapy in Non-Small Cell Lung Cancer. Front. Chem. 9, 789934. doi:10.3389/fchem.2021.789934

PubMed Abstract | CrossRef Full Text | Google Scholar

Faraguna, F., Pötschk, P., and Pionteck, J. (2017). Preparation of Polystyrene Nanocomposites with Functionalized Carbon Nanotubes by Melt and Solution Mixing: Investigation of Dispersion, Melt Rheology, Electrical and thermal Properties. Polymer 132, 325–341. doi:10.1016/j.polymer.2017.11.014

CrossRef Full Text | Google Scholar

Hamann, M., Quell, A., Koch, L., and Stubenrauch, C. (2021). On How the Morphology Affects Water Release of Porous Polystyrene. Mater. Today Commun. 26, 102087. doi:10.1016/j.mtcomm.2021.102087

CrossRef Full Text | Google Scholar

He, F.-A., Wu, H.-J., Yang, X.-L., Lam, K.-H., Fan, J.-T., and Chan, L.-W. H. (2015). Novel Exfoliated Graphite Nanoplates/Syndiotactic Polystyrene Composites Prepared by Solution-Blending. Polym. Test. 42, 45–53. doi:10.1016/j.polymertesting.2015.01.002

CrossRef Full Text | Google Scholar

Hong, R. Y., Feng, B., Liu, G., Wang, S., Li, H. Z., Ding, J. M., et al. (2009). Preparation and Characterization of Fe3O4/Polystyrene Composite Particles via Inverse Emulsion Polymerization. J. Alloys Compd. 476, 612–618. doi:10.1016/j.jallcom.2008.09.060

CrossRef Full Text | Google Scholar

Hou, T., Jia, Z., Dong, Y., Liu, X., and Wu, G. (2022). Layered 3D Structure Derived from MXene/Magnetic Carbon Nanotubes for Ultra-Broadband Electromagnetic Wave Absorption. Chem. Eng. J. 431, 133919–133928. doi:10.1016/j.cej.2021.133919

CrossRef Full Text | Google Scholar

Huang, K., Peng, L., Liu, B., Li, D., Ma, Q., Zhang, M., et al. (2018). Water-Borne Perovskite Quantum Dot-Loaded, Polystyrene Latex Ink. Front. Chem. 6, 453. doi:10.3389/fchem.2018.00453

PubMed Abstract | CrossRef Full Text | Google Scholar

Ito, M., Takano, K., Hanochi, H., Asaumi, Y., Yusa, S.-I., Nakamura, Y., et al. (2018). pH-Responsive Aqueous Bubbles Stabilized with Polymer Particles Carrying Poly(4-Vinylpyridine) Colloidal Stabilizer. Front. Chem. 6, 269. doi:10.3389/fchem.2018.00269

PubMed Abstract | CrossRef Full Text | Google Scholar

Li, S., Su, C., Yang, J., Wen, F., Wang, Z., Chen, R., et al. (2019). Preparation and Properties of Polycarbonate/Polystyrene Bead Alloy via Solvent Evaporation Method. ChemistrySelect 4, 13755–13759. doi:10.1002/slct.201904020

CrossRef Full Text | Google Scholar

Liu, G., Guan, Y., Ge, Y., and Xie, L. (2011). Preparation of Monodisperse Magnetic Polystyrene Microspheres and its Surface Chemical Modification. J. Appl. Polym. Sci. 120, 3278–3283. doi:10.1002/app.33495

CrossRef Full Text | Google Scholar

Liu, Y., and Peng, X. (2022). Multi-Functional Hypercrosslinked Polystyrene as High-Performance Adsorbents for Artificial Liver Blood Purification. Front. Chem. 9, 789814. doi:10.3389/fchem.2021.789814

PubMed Abstract | CrossRef Full Text | Google Scholar

Marinovic-Cincovic, M., Saponjic, Z. V., Djokovic, V., Milonjic, S. K., and Nedeljkovic, J. M. (2006). The Influence of Hematite Nano-Crystals on the thermal Stability of Polystyrene. Polym. Degrad. Stab. 91, 313–316. doi:10.1016/j.polymdegradstab.2005.04.044

CrossRef Full Text | Google Scholar

Naeemikhah, E., Ahmadi-khaneghah, A., Heydari, A., and Behniafar, H. (2019). Magnetic Crosslinked Polystyrene with Hydrophilic Nature Prepared through Surface-Initiated ATRP Technique. Colloids Surf. A: Physicochemical Eng. Aspects 582, 123866. doi:10.1016/j.colsurfa.2019.123866

CrossRef Full Text | Google Scholar

Nikpour, S., Ansari-Asl, Z., and Sedaghat, T. (2022). Fabrication and Characterization of polystyrene/Fe-MOF Composite Beads for Iodine Uptake. Inorg. Chem. Commun. 136, 109141. doi:10.1016/j.inoche.2021.109141

CrossRef Full Text | Google Scholar

Nyambo, C., Kandare, E., Wang, D., and Wilkie, C. A. (2008). Flame-Retarded Polystyrene: Investigating Chemical Interactions between Ammonium Polyphosphate and MgAl Layered Double Hydroxide. Polym. Degrad. Stab. 93, 1656–1663. doi:10.1016/j.polymdegradstab.2008.05.029

CrossRef Full Text | Google Scholar

Peng, G., Yaoqin, W., Congcong, D., Changmei, S., Rongjun, Q., Chunnuan, J., et al. (2020). Allyl and Benzyl Modified Aramid Nanofibers as an Enhancement in Polystyrene-Based Composites. Front. Chem. 8, 586763. doi:10.3389/fchem.2020.586763

PubMed Abstract | CrossRef Full Text | Google Scholar

Qiu, G., Wang, Q., Wang, C., Lau, W., and Guo, Y. (2007). Polystyrene/Fe3O4 Magnetic Emulsion and Nanocomposite Prepared by Ultrasonically Initiated Miniemulsion Polymerization. Ultrason. Sonochem. 14, 55–61. doi:10.1016/j.ultsonch.2006.03.001

PubMed Abstract | CrossRef Full Text | Google Scholar

Qiu, G., Wang, Q., Wang, C., Lau, W., and Guo, Y. (2006). Ultrasonically Initiated Miniemulsion Polymerization of Styrene in the Presence of Fe3O4 Nanoparticles. Polym. Int. 55, 265–272. doi:10.1002/pi.1937

CrossRef Full Text | Google Scholar

Rahimi, J., Niksefat, M., and Maleki, A. (2020). Fabrication of Fe3O4@PVA-Cu Nanocomposite and its Application for Facile and Selective Oxidation of Alcohols. Front. Chem. 8, 615. doi:10.3389/fchem.2020.00615

PubMed Abstract | CrossRef Full Text | Google Scholar

Shi, C., Qian, X., Jing, J., and Che, H. (2021). Functionalized CNTs with DOPO and Silicon Containing Agents: Effective Reinforcer for Thermal and Flame Retardant Properties of Polystyrene Nanocomposites. Front. Chem. 8, 627642. doi:10.3389/fchem.2020.627642

PubMed Abstract | CrossRef Full Text | Google Scholar

Sun, B., and Lawrence, K. (2017). Fabrication of Regular Polystyrene Foam Structures with Selective Laser Sintering. Mater. Today Commun. 13, 346–353. doi:10.1016/j.mtcomm.2017.10.016

CrossRef Full Text | Google Scholar

Umar, A., Abu Naim, A., and Sanagi, M. M. (2014). Synthesis and Characterization of Chitosan Grafted with Polystyrene Using Ammonium Persulfate Initiator. Mater. Lett. 124, 12–14. doi:10.1016/j.matlet.2014.03.007

CrossRef Full Text | Google Scholar

Wang, C., Jia, Z., He, S., Zhou, J., Zhang, S., Tian, M., et al. (2022a). Metal-Organic Framework-Derived CoSn/NC Nanocubes as Absorbers for Electromagnetic Wave Attenuation. J. Mater. Sci. Technol. 108, 236–243. doi:10.1016/j.jmst.2021.07.049

CrossRef Full Text | Google Scholar

Wang, C., Yan, J., Cui, X., Cong, D., and Wang, H. (2010). Preparation and Characterization of Magnetic Hollow PMMA Nanospheres via In Situ Emulsion Polymerization. Colloids Surf. A: Physicochem. Eng. Asp. 363, 71–77. doi:10.1016/j.colsurfa.2010.04.016

CrossRef Full Text | Google Scholar

Wang, C., Yan, J., Cui, X., and Wang, H. (2011). Synthesis of Raspberry-Like Monodisperse Magnetic Hollow Hybrid Nanospheres by Coating Polystyrene Template with Fe3O4@SiO2 Particles. J. Colloid Interf. Sci. 354, 94–99. doi:10.1016/j.jcis.2010.09.078

CrossRef Full Text | Google Scholar

Wang, C., Yan, J., Li, Z., Wang, H., and Cui, X. (2013). Investigation on Raspberry-Like Magnetic-Hollow Silica Nanospheres and its Preliminary Application for Drug Delivery. J. Nanopart Res. 15, 1937. doi:10.1007/s11051-013-1937-2

CrossRef Full Text | Google Scholar

Wang, L., Wang, C., Liu, P., Jing, Z., Ge, X., and Jiang, Y. (2018). The Flame Resistance Properties of Expandable Polystyrene Foams Coated with a Cheap and Effective Barrier Layer. Constr. Building Mater. 176, 403–414. doi:10.1016/j.conbuildmat.2018.05.023

CrossRef Full Text | Google Scholar

Wang, Z., Zhang, T., Wang, J., Yang, G., Li, M., and Wu, G. (2022b). The Investigation of the Effect of Filler Sizes in 3D-BN Skeletons on thermal Conductivity of Epoxy-Based Composites. Nanomaterials 12 (3), 446. doi:10.3390/nano12030446

PubMed Abstract | CrossRef Full Text | Google Scholar

Xing, Z., Wang, M., Du, G., Xiao, T., Liu, W., Qiang, D., et al. (2013). Preparation of Microcellular Polystyrene/Polyethylene alloy Foams by Supercritical CO2 Foaming and Analysis by X-ray Microtomography. J. Supercrit. Fluids 82, 50–55. doi:10.1016/j.supflu.2013.06.003

CrossRef Full Text | Google Scholar

Yan, J., Miao, X., Zhang, Q., Cui, X., Li, J., and Wang, H. (2011a). One-Step Preparation of Black Polystyrene Particles via In Situ Suspension Polymerization. Polym. Eng. Sci. 51, 294–301. doi:10.1002/pen.21829

CrossRef Full Text | Google Scholar

Yan, J., Wang, C., Gao, Y., Zheng, Z., Zhong, S., Miao, X., et al. (2011b). Anchoring Conductive Polyaniline on the Surface of Expandable Polystyrene Beads by Swelling-Based and In Situ Polymerization of Aniline Method. Chem. Eng. J. 172, 564–571. doi:10.1016/j.cej.2011.06.009

CrossRef Full Text | Google Scholar

Yang, H., Zhang, L., Ma, W., Pu, H., and Gong, F. (2014). Polystyrene/Attapulgite Nanocomposites Prepared Viain Sitususpension Polymerization with Redox Initiation System. J. Appl. Polym. Sci. 132, 41567–41575. doi:10.1002/app.41567

CrossRef Full Text | Google Scholar

Yang, Z.-P., Gong, X.-Y., and Zhang, C.-J. (2010). Recyclable Fe3O4/hydroxyapatite Composite Nanoparticles for Photocatalytic Applications. Chem. Eng. J. 165, 117–121. doi:10.1016/j.cej.2010.09.001

CrossRef Full Text | Google Scholar

Yu, L., Yang, H., Wang, Y., and Jiang, W. (2017). Magnetically Enhanced Superhydrophobic Functionalized Polystyrene Foam for the High Efficient Cleaning of Oil Spillage. Powder Technol. 311, 257–264. doi:10.1016/j.powtec.2017.01.084

CrossRef Full Text | Google Scholar

Zheng, Z., Li, W., Sun, H., Cheng, Z., Yan, J., Wang, H., et al. (2013). Preparation and Characterization of Polystyrene/Modified Carbon Black Composite Beads via In Situ Suspension Polymerization. Polym. Compos. 34, 1110–1118. doi:10.1002/pc.22519

CrossRef Full Text | Google Scholar

Zhou, K., Gui, Z., and Hu, Y. (2016). The Influence of Graphene Based Smoke Suppression Agents on Reduced Fire Hazards of Polystyrene Composites. Compo. A: Appl. Sci. Manuf. 80, 217–227. doi:10.1016/j.compositesa.2015.10.029

CrossRef Full Text | Google Scholar

Keywords: colorized polystyrene bead, Fe3O4, micrometer size, controllable synthesis, in situ suspension polymerization

Citation: Yan J, Wu H, Huang P, Wang Y, Shu B, Li X, Ding D, Sun Y, Wang C, Wu J and Sun L (2022) Investigation on the Controllable Synthesis of Colorized and Magnetic Polystyrene Beads With Millimeter Size via In Situ Suspension Polymerization. Front. Chem. 10:891582. doi: 10.3389/fchem.2022.891582

Received: 07 March 2022; Accepted: 08 April 2022;
Published: 27 May 2022.

Edited by:

Tingchao He, Shenzhen University, China

Reviewed by:

Guanglei Wu, Qingdao University, China
Yanhu Zhan, Liaocheng University, China

Copyright © 2022 Yan, Wu, Huang, Wang, Shu, Li, Ding, Sun, Wang, Wu and Sun. This is an open-access article distributed under the terms of the Creative Commons Attribution License (CC BY). The use, distribution or reproduction in other forums is permitted, provided the original author(s) and the copyright owner(s) are credited and that the original publication in this journal is cited, in accordance with accepted academic practice. No use, distribution or reproduction is permitted which does not comply with these terms.

*Correspondence: Chunlei Wang, wangchunlei_best@163.com; Jian Wu, wujian15203@163.com

Disclaimer: All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article or claim that may be made by its manufacturer is not guaranteed or endorsed by the publisher.