Pd@Py2PZ@MSN as a Novel and Efficient Catalyst for C–C Bond Formation Reactions

In this study, a novel catalyst is introduced based on the immobilization of palladium onto dipyrido (3,2-a:2′,3′-c) phenazine–modified mesoporous silica nanoparticles. The dipyrido (3,2-a:2′,3′-c) phenazine (Py₂PZ) ligand is synthesized in a simple method from the reaction of 1,10-phenanthroline-5,6-dione and 3,4-diaminobenzoic acid as starting materials. The ligand is used to functionalize mesoporous silica nanoparticles (MSNs) and modify their surface chemistry for the immobilization of palladium. The palladium-immobilized dipyrido (3,2-a:2′,3′-c) phenazine–modified mesoporous silica nanoparticles (Pd@Py₂PZ@MSNs) are synthesized and characterized by several characterization techniques, including TEM, SEM, FT-IR, TGA, ICP, XRD, and EDS analyses. After the careful characterization of Pd@Py₂PZ@MSNs, the activity and efficiency of this catalyst is examined in carbon–carbon bond formation reactions. The results are advantageous in water and the products are obtained in high isolated yields. In addition, the catalyst showed very good reusability and did not show significant loss in activity after 10 sequential runs.

Introduction

Carbon–carbon bond formation reactions, especially palladium-catalyzed ones, are significant reactions in organic chemistry. Among all the palladium-catalyzed carbon–carbon bond formation reactions, Heck and Suzuki reactions have attracted interests due to their high applications in various organic syntheses (Bahadorikhalili and Mahdavi, 2018; Christoffel and Ward, 2018; Mpungose et al., 2018; González-Sebastián and Morales-Morales, 2019; Sherwood et al., 2019; Tashrifi et al., 2019; Easson et al., 2020; Fusini et al., 2020). Regarding the unique advantages of Heck and Suzuki reactions, these reactions are used for the synthesis of several compounds with complex chemical structures (Bahadorikhalili et al., 2018a; Bahadorikhalili et al., 2020; Reza Hajipour and Khorsandi, 2020; Yao et al., 2020; Zhou et al., 2020). Therefore, several efforts have been focused on the introduction of novel catalysts with improved characteristics (Hajipour et al., 2018; Ma et al., 2018).

An interesting approach for designing novel catalysts for Heck and Suzuki reactions is the immobilization of palladium onto modified nanoparticles. This method enables both the advantages of homogenous and heterogenous catalysts. Several nanoparticles including nanosilica (Isfahani et al., 2013; Khalafi-Nezhad and Panahi, 2014), nitrogen-rich polymers (Targhan et al., 2020), chitosan (Kumari et al., 2017), magnetic iron oxide (Bahadorikhalili et al., 2015; Ma’mani et al., 2014), and graphene oxide (Kumari et al., 2019) have been used as a support for palladium catalysts. Mesoporous silica nanoparticles (MSNs) are an interesting ordered porous material made of silica with high surface area and unique physical and chemical properties. MSNs are chemically and physically stable and are compatible with biological systems (Mehmood et al., 2017; Narayan et al., 2018; Jeelani et al., 2020). MSNs have been used in various applications, including catalysis (Bahadorikhalili et al., 2018b; Sayahi et al., 2020), drug delivery (Bharti et al., 2015; Moreira et al., 2016), tissue engineering (Rosenholm et al., 2016), and pollutant removal from air and solutions (Li et al., 2016; Gao et al., 2017; Zarandi, 2019). Based on the high surface area and stability and ease of functionalization of MSNs, this family of nanoporous materials has extensively been used as a support for catalysts in various reactions (Han et al., 2006; Lee et al., 2009; Sarkar et al., 2019; Xu et al., 2019).

In spite of many reports on the immobilization of the catalytic agents onto modified nanoparticles, several of them hold a number of disadvantages. It is critical to investigate this field and synthesize catalysts which are efficient and selective and, in an ideal case, have the possibility of use in green solvents. As an interesting nanoparticle for the immobilization of the catalyst, MSNs are of high interest due to their advantages, including high surface area, high thermal stability, and high surface-active groups, which could be used for surface modifications. In this study, we introduce a novel palladium catalyst supported onto dipyrido (3,2-a:2′,3′-c) phenazine–modified MSNs. The catalytic activity of Pd@Py₂PZ@MSNs is evaluated in Heck and Suzuki reactions. It should be noted that the palladium should be in the 0 oxidation state to catalyze the reaction (Zhang et al., 2006). Based on that, the catalyst should have been reduced to Pd (0) for efficiently catalyzing the reaction (Xiao et al., 2021).

Results and Discussion

In this study, SBA-15 MSNs were synthesized using the hydrothermal method and modified by (3-aminopropyl) methoxysilane. Dipyrido (3,2-a:2′,3′-c) phenazine (Py₂PZ) was synthesized in a one-step reaction between 3,4-diaminobenzoic acid and 1,10-phenanthroline-5,6-dione, which enables it to react with amine groups on the surface of MSNs via an amidation reaction to yield Py₂PZ@MSNs. The Pd@Py₂PZ@MSN catalyst was prepared using Py₂PZ@MSNs as a support, and it was fully characterized by various characterization techniques. The synthesis steps are presented in Scheme 1.

SCHEME 1

SCHEME 1. Synthesis of the Pd@Py₂PZ@MSN catalyst.

Electron microscopy images of the Pd@Py₂PZ@MSN catalyst are shown in Figure 1. The hexagonal meso-structure of the MSN backbone could be observed in the TEM image that Pd NPs appear as dark zones (Figure 1A). The rod-like structure of MSNs could clearly be observed in the SEM image (Figure 1B). In addition, the EDS analysis of the Pd@Py₂PZ@MSN catalyst confirms the presence of Pd in the structure of the catalyst (Figure 1C). As seen in Figure 1D, the XRD pattern of the Pd@Py₂PZ@MSN catalyst confirms that the crystallinity of the catalyst is similar to that of SBA-15 (Hu et al., 2016). In addition, the high-angle XRD confirms the presence of Pd NPs by two peaks of 110 and 200 planes at 2θ of 39.2 and 44.3°, respectively (Figure 1D).

FIGURE 1

FIGURE 1. (A) TEM; (B) SEM; (C) EDS; and (D) XRD results of the Pd@Py₂PZ@MSN catalyst.

To confirm the successful synthesis of Pd@Py₂PZ@MSNs, the FT-IR spectra of nanomaterials are compared (Figure 2A). In the FT-IR spectra of Pd@Py₂PZ@MSNs, a peak at 1084 cm⁻¹ represents Si–O vibrations in the structure of the catalyst. The hydroxyl groups of the catalyst could be observed at 3450 cm⁻¹, and the CH₂ stretching vibration is presented at 2927 cm⁻¹. The peak that appeared at 1739 cm⁻¹ is attributed to the C=O bond found in the ester moiety in the structure of the Pd@Py₂PZ@MSN catalyst.

FIGURE 2

FIGURE 2. (A) FT-IR; and (B) TGA results of the Pd@Py₂PZ@MSN catalyst.

The organic content in the structure of the catalyst was studied using TGA (Figure 2B). The TGA curve shows that the catalyst was thermally stable up to 250°C. A weight loss at the temperature of 250–350°C could be observed, which could be correlated to the degradation of organic moieties in the structure of the Pd@Py₂PZ@MSN catalyst. The palladium content in the structure of the catalyst was measured using ICP analysis. The results showed that the Pd content in the Pd@Py₂PZ@MSN catalyst was 0.12 mmol g⁻¹.

The surface area and pore size of the Pd@Py2PZ@MSN catalyst were characterized using BET analysis and compared with those of MSNs. Based on the BET and nitrogen adsorption–desorption results, Py₂PZ@MSNs have a high surface area of 612.37 m² g⁻¹. In addition, the pore diameter and pore volume of the synthesized nanoporous support are 5.14 nm and 0.72 cm³ g⁻¹, respectively. The surface area, pore width, and pore volumes of MSNs are 655.37 m² g⁻¹, 5.75 nm, and 0.79 cm³ g⁻¹, respectively. The decrease in surface area, pore width, and pore volume of MSNs by the synthesis of the catalyst is expected, while functionalization of the nanoparticles leads to such changes. The surface area and pore size results of MSNs and the Pd@Py₂PZ@MSN catalyst are presented in Table 1.

TABLE 1

TABLE 1. Surface area and pore size results of MSN and the Pd@Py₂PZ@MSN catalyst.

After the characterization of the Pd@Py₂PZ@MSN catalyst, the efficiency of the catalyst was examined in carbon–carbon bond formation reactions. For this purpose, the Pd@Py₂PZ@MSN catalyst was used in Heck and Suzuki reactions. Initially, the optimal reaction conditions were evaluated by performing the reaction under different reaction conditions including various solvents, bases, catalysts, and times of the reactions. To this end, the reaction of styrene and phenyl bromide was selected as a model reaction. The optimization results are presented in Table 2. According to the results, the best solvent for the reaction is water. However, the yields of the product were less in other solvents. Therefore, water was selected as the best solvent for the reaction. In addition, the results showed that the best yield of the product is obtained when the reaction is performed in the presence of 1 mol% of the catalyst. It should be noted that the presence of a base is critical for reaction performance. Therefore, the reaction was performed in the presence of several bases such as triethyl amine (TEA), NaOH, KOH, and pyridine. The results showed that TEA was the best base for the reaction. To study the role of the Pd@Py₂PZ@MSN catalyst in the reaction, a blank run was performed by all the reaction components, except the catalyst. No product was obtained in the absence of the catalyst. Therefore, the optimized reaction conditions were selected to be water as the solvent and 1.5 equivalent of triethyl amine base in the presence of 1.0 mol% of the Pd@Py₂PZ@MSN catalyst.

TABLE 2

TABLE 2. Optimization of the reaction of styrene and phenyl bromide in the presence of the Pd@Py₂PZ@MSN catalyst.

To rule out the presence of leached and homogenous Pd in the reaction mixture, in a run, the reaction was performed under the optimal reaction condition. After 60 min, the conversion of the substrates to the product measured by GC was 67%. Then, the catalyst was separated from the reaction mixture, and the filtrate was stirred under the same conditions for more 60 min. The analysis of the product by GC showed that no more product has been obtained. These observations confirmed that the Pd catalyst worked in the heterogenous phase and the presence of the Pd@Py₂PZ@MSN catalyst was necessary for reaction performance.

Based on the optimized conditions, the scope and generality of the Pd@Py₂PZ@MSN catalyst were studied in Heck and Suzuki reactions. The structures and yields of the products are presented in Table 3. The high efficiency of the Pd@Py₂PZ@MSN catalyst in the mentioned reaction could clearly be observed. The catalyst is highly active in both Heck and Suzuki reactions, and advantageous results were obtained. All substrates with electron donating and electron withdrawing functionalities have given the desired products in high isolated yields. For example, entries 4–9, 18–22, and 26–28 with phenyl halides bearing electron-donating functionalities have provided the products in 84–93% yields. In addition, phenyl halides bearing electron-withdrawing functionalities (entries 10–14, 22–23, and 29–31) have successfully participated in the reaction and have given the products in 88–99% yields. In addition, a reaction was performed with 10 mmol of the substrates to evaluate the possible scale up of the reaction. The results were advantageous, and high yields of the products were obtained in the scale-up reactions. To study the possibility of the use of the catalyst in industrial applications, scale-up reaction was performed under optimized conditions. The large-scale reaction of iodobenzene with styrene and phenylboronic acid has led to 85 and 83% yields, respectively.

TABLE 3

TABLE 3. Scope and generality of the Pd@Py₂PZ@MSN catalyst in Heck and Suzuki reactions^a.

A proposed mechanism was suggested, which is presented in Scheme 2. Based on the mechanism, the presence of the catalyst is critical for reaction performance. In the first step of the reaction, the catalyst activates the Ar–X bond, followed by the addition of the alkene. In the next step, the product is obtained, and the catalyst is ready for the next cycle of the reaction by the elimination of H–X.

SCHEME 2

SCHEME 2. Proposed mechanism for Pd@Py2PZ@MSN catalyzed carbon–carbon bond formation.

A great advantage of the Pd@Py₂PZ@MSN catalyst is its reusability. For this purpose, the reaction was repeated for 10 sequential reactions, and the obtained results are presented in Figure 3. It could be seen that in both Heck and Suzuki reactions, no big loss in the activity of the catalyst is observed. It is significant to study the possible leaching of palladium from the catalyst. For studying the leaching of palladium from the Pd@Py₂PZ@MSN catalyst, a reaction was performed under the optimized reaction conditions. However, after 20 min when the reaction has not been completed, the catalyst was isolated from the reaction mixture. The reaction was continued without the catalyst for more than 3 h and based on GC analysis, no performance was observed in the reaction performance. In addition, the filtrate was studied by ICP, which did not show any leaching of palladium from the catalyst.

FIGURE 3

FIGURE 3. Recovery results of the Pd@Py₂PZ@MSN catalyst.

To show the structural stability of the catalyst during the reaction conditions, the catalyst was separated after the 5^th reaction run and washed with water and ethanol. Then, the dried 5^th re-used Pd@Py₂PZ@MSN catalyst was characterized by SEM and BET analysis. The results are presented in Figure 4; Table 4, respectively. Comparing the results of the recovered catalyst with the fresh ones confirm the good stability of the catalyst during the reactions.

FIGURE 4

FIGURE 4. SEM image of the recovered Pd@Py₂PZ@MSN catalyst.

TABLE 4

TABLE 4. Surface area and pore size results of the recovered Pd@Py₂PZ@MSN catalyst.

To better study the activity of the catalyst, Pd@Py₂PZ@MSNs were compared with the previously reported catalysts. Table 5 presents the catalysts, reaction conditions, and isolated yields of the reactions for the reaction of styrene and bromobenzene. According to the results, the best performance is observed for Pd@Py₂PZ@MSNs, and the reaction is performed under mild reaction conditions.

TABLE 5

TABLE 5. Comparison of the catalytic activity of Pd@Py₂PZ@MSN with the previously reported one.

Experimental

General Remarks

All the chemicals, reagents, and solvents were purchased from Merck, Germany, and Sigma, Germany. TEM images were recorded using a CM 10 Philips instrument. ¹H (500 MHz) spectra were recorded using a Bruker Advance spectrometer in DMSO and d₆ solution with tetramethylsilane (TMS) as an internal standard. A TESCAN T3000 instrument was used to record the SEM images. An OPTIMA7300DV ICP analyzer was used for analyzing the palladium content of the catalyst. The FT-IR spectra were recorded on a Nicolet Magna FT-IR 550 spectrophotometer using potassium bromide disks. BET of the samples was analyzed using an ASAPTM micromeritics 2020 instrument. The particle size was measured using the HORIBA SZ100-Z DLS instrument. The thermogravimetric analyzer (TGA) at a heating rate of 10°C min⁻¹ over the temperature range of 40–600°C under nitrogen atmosphere was used.

Synthesis of the Py₂PZ Ligand

1,10-phenanthroline-5,6-dione (1.05 g, 5 mmol) and 3,4-diaminobenzoic acid (0.76 g, 5 mmol) were dissolved in ethanol and refluxed for 2 h. The reaction progress was monitored by TLC monitoring. After the reaction was completed, the solvent was evaporated and the product was purified by recrystallization from ethanol.

Synthesis of the Pd@Py₂PZ@MSN Catalyst

SBA-15 was synthesized according to the previously reported method (Chaudhary and Sharma, 2017). A mixture containing MSNs (0.5 g) in ethanol/deionized water (1:2, 30 ml) and HCl (pH = 4) was prepared and sonicated for 30 min. A solution of (3-aminopropyl) methoxysilane (1 g) in ethanol (30 ml) was prepared and added drop-wise to the aforementioned mixture by vigorous stirring. The reaction mixture was stirred for 24 h, and then the product was separated by filtration and washed with deionized water and ethanol. The product was dried at 70°C in vacuum for 12 h to obtain amine-modified mesoporous SBA-15.

A mixture of amine-modified mesoporous SBA-15 (0.5 g) in dichloromethane (75 ml) was sonicated for 30 min. Then, dipyrido (3,2-a:2′,3′-c) phenazine-11-carboxylic acid (1.6 g, 5 mmol) in dichloromethane (25 ml) was added and 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide (5 mmol, 1 eq) and N-hydroxysuccinnimide (5.5 mmol, 1.1 eq) were added. The reaction mixture was stirred overnight at room temperature. The product was separated from the reaction mixture and washed with ethanol and dried for 12 h in a vacuum oven.

The solid support (0.5 g) was added to dry acetone and sonicated for 30 min. Then, PdCl₂ (1 mmol) was added, and the reaction mixture was stirred at 40°C under an inert atmosphere for 24 h. The Pd@Py₂PZ@MSN catalyst was separated from the reaction mixture by centrifugation, washed thoroughly with EtOH and diethyl ether, and dried under vacuum at room temperature for 12 h.

General Procedure for the Carbon–Carbon Bond Formation Reactions

Phenyl halide (1 mmol), alkene (1.1 mmol, in case of Heck reaction), phenylboronic acid (1.0 mmol, in case of Suzuki reaction), triethyl amine (1.5 mmol), and the Pd@Py₂PZ@MSN catalyst (1.0 mol%) were added into a flask containing H₂O (5 ml) and stirred at room temperature. When the TLC monitoring showed reaction completion, the catalyst was separated from the reaction mixture and washed with water and EtOH. The product was extracted with ethyl acetate. The organic phase was collected and dried over sodium sulfate. The solvent was evaporated, and the product was purified by column chromatography using n-hexane:ethyl acetate (6:1) as the eluent to obtain the pure product.

Recovery of the Nanocatalyst

The reaction of phenyl bromide (1 mmol) and styrene (1.1 mmol) was selected as a model reaction and was performed in the presence of the Pd@Py₂PZ@MSN catalyst under optimal reaction conditions. After the reaction was completed, the catalyst was separated from the reaction mixture and washed with water and used in the next reaction under the same conditions. The reactions were performed for 10 sequential runs.

Conclusion

In conclusion, Pd@Py₂PZ@MSN as a novel catalyst was designed, synthesized, and characterized based on the immobilization of palladium onto the modified SBA-15 MSNs. The catalyst was characterized using several methods, and the structure of the catalyst was confirmed. The activity of the Pd@Py₂PZ@MSN catalyst was evaluated in Heck and Suzuki reactions. The catalyst showed the best activity in water as the solvent in the presence of triethyl amine base. Several substrates with different functionalities were used and, in all cases, the desired compounds were synthesized in good isolated yields. As an advantage, the catalyst showed very good reusability after 10 sequential runs.

Data Availability Statement

The raw data supporting the conclusions of this article will be made available by the authors, without undue reservation.

Author Contributions

SB and MS defined the experiments. MT, MB, and HL ran the experiments and collected the data. MS, LM'M, and MM analyzed the data. SB prepared the manuscript.

Conflict of Interest

The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.

Publisher’s Note

All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors, and the reviewers. Any product that may be evaluated in this article, or claim that may be made by its manufacturer, is not guaranteed or endorsed by the publisher.

References

Bahadorikhalili, S., Ma'mani, L., Mahdavi, H., and Shafiee, A. (2018b). Copper Supported β-cyclodextrin Functionalized PEGylated Mesoporous Silica Nanoparticle -graphene Oxide Hybrid: An Efficient and Recyclable Nano-Catalyst for Straightforward Synthesis of 2-arylbenzimidazoles and 1,2,3-triazoles. Microporous Mesoporous Mater. 262, 207–216. doi:10.1016/j.micromeso.2017.11.046

CrossRef Full Text | Google Scholar

Bahadorikhalili, S., and Mahdavi, H. (2018). Palladium Magnetic Nanoparticle-Polyethersulfone Composite Membrane as an Efficient and Versatile Catalytic Membrane Reactor. Polym. Adv. Technol. 29, 1138–1149. doi:10.1002/pat.4225

CrossRef Full Text | Google Scholar

Bahadorikhalili, S., Mahdavi, M., Ma’mani, L., Shafiee, A., Mahdavi, H., and Akbarzadeh, T. (2018a). Palladium Functionalized Phosphinite Polyethyleneimine Grafted Magnetic Silica Nanoparticles as an Efficient Catalyst for the Synthesis of Isoquinolino[1,2-B]quinazolin-8-Ones. New J. Chem. 42, 5499–5507. doi:10.1039/c7nj04837h

CrossRef Full Text | Google Scholar

Bahadorikhalili, S., Ma’mani, L., Mahdavi, H., and Shafiee, A. (2015). Palladium Catalyst Supported on PEGylated Imidazolium Based Phosphinite Ionic Liquid-Modified Magnetic Silica Core-Shell Nanoparticles: a Worthy and Highly Water-Dispersible Catalyst for Organic Reactions in Water. RSC Adv. 5, 71297–71305. doi:10.1039/c5ra12747e

CrossRef Full Text | Google Scholar

Bahadorikhalili, S., Maˈmani, L., Lijan, H., and Mahdavi, M. (2020). γ-Fe₂O₃@SiO₂(CH₂)₃-HPBM-Pd as a Versatile Boosted Nanocatalyst for CarbonCarbon Bond Formation. Mater. Today Commun. 26, 101913. doi:10.1016/j.mtcomm.2020.101913

CrossRef Full Text | Google Scholar

Bharti, C., Gulati, N., Nagaich, U., and Pal, A. (2015). Mesoporous Silica Nanoparticles in Target Drug Delivery System: A Review. Int. J. Pharma Investig. 5, 124. doi:10.4103/2230-973x.160844

CrossRef Full Text | Google Scholar

Chaudhary, V., and Sharma, S. (2017). An Overview of Ordered Mesoporous Material SBA-15: Synthesis, Functionalization and Application in Oxidation Reactions. J. Porous Mater. 24, 741–749. doi:10.1007/s10934-016-0311-z

CrossRef Full Text | Google Scholar

Christoffel, F., and Ward, T. R. (2018). Palladium-catalyzed Heck Cross-Coupling Reactions in Water: A Comprehensive Review. Catal. Lett. 148, 489–511. doi:10.1007/s10562-017-2285-0

CrossRef Full Text | Google Scholar

Easson, M. W., Jordan, J. H., Bland, J. M., Hinchliffe, D. J., and Condon, B. D. (2020). Application of Brown Cotton-Supported Palladium Nanoparticles in Suzuki-Miyaura Cross-Coupling Reactions. ACS Appl. Nano Mater. 3, 6304–6309. doi:10.1021/acsanm.0c01303

CrossRef Full Text | Google Scholar

Fusini, G., Rizzo, F., Angelici, G., Pitzalis, E., Evangelisti, C., and Carpita, A. (2020). Polyvinylpyridine-Supported Palladium Nanoparticles: An Efficient Catalyst for Suzuki-Miyaura Coupling Reactions. Catalysts 10, 330. doi:10.3390/catal10030330

CrossRef Full Text | Google Scholar

Gao, J., Lei, H., Han, Z., Shi, Q., Chen, Y., and Jiang, Y. (2017). Dopamine Functionalized Tannic-Acid-Templated Mesoporous Silica Nanoparticles as a New Sorbent for the Efficient Removal of Cu2+ from Aqueous Solution. Sci. Rep. 7, 45215. doi:10.1038/srep45215

PubMed Abstract | CrossRef Full Text | Google Scholar

González-Sebastián, L., and Morales-Morales, D. (2019). Cross-coupling Reactions Catalysed by Palladium Pincer Complexes. A Review of Recent Advances. J. Organomet. Chem. 893, 39–51. doi:10.1016/j.jorganchem.2019.04.021

CrossRef Full Text | Google Scholar

Hajipour, A. R., and Khorsandi, Z. (2016). Multi Walled Carbon Nanotubes Supported N-Heterocyclic Carbene-Cobalt (ΙΙ) as a Novel, Efficient and Inexpensive Catalyst for the Mizoroki-Heck Reaction. Catal. Commun. 77, 1–4. doi:10.1016/j.catcom.2015.12.027

CrossRef Full Text | Google Scholar

Hajipour, A. R., Sadeghi, A. R., and Khorsandi, Z. (2018). Pd Nanoparticles Immobilized on Magnetic Chitosan as a Novel Reusable Catalyst for green Heck and Suzuki Cross‐coupling Reaction: In Water at Room Temperature. Appl. Organometal Chem. 32, e4112. doi:10.1002/aoc.4112

CrossRef Full Text | Google Scholar

Han, Y.-F., Chen, F., Zhong, Z., Ramesh, K., Chen, L., and Widjaja, E. (2006). Controlled Synthesis, Characterization, and Catalytic Properties of Mn2O3 and Mn3O4 Nanoparticles Supported on Mesoporous Silica SBA-15. J. Phys. Chem. B 110, 24450–24456. doi:10.1021/jp064941v

PubMed Abstract | CrossRef Full Text | Google Scholar

Hu, G., Li, W., Xu, J., He, G., Ge, Y., Pan, Y., et al. (2016). Substantially Reduced Crystallization Temperature of SBA-15 Mesoporous Silica in NaNO3 Molten Salt. Mater. Lett. 170, 179–182. doi:10.1016/j.matlet.2016.02.030

CrossRef Full Text | Google Scholar

Isfahani, A. L., Mohammadpoor-Baltork, I., Mirkhani, V., Khosropour, A. R., Moghadam, M., Tangestaninejad, S., et al. (2013). Palladium Nanoparticles Immobilized on Nano-Silica Triazine Dendritic Polymer (Pdnp-nSTDP): An Efficient and Reusable Catalyst for Suzuki-Miyaura Cross-Coupling and Heck Reactions. Adv. Synth. Catal. 355, 957–972. doi:10.1002/adsc.201200707

CrossRef Full Text | Google Scholar

Jeelani, P. G., Mulay, P., Venkat, R., and Ramalingam, C. (2020). Multifaceted Application of Silica Nanoparticles. A Review. Silicon 12, 1337–1354. doi:10.1007/s12633-019-00229-y

CrossRef Full Text | Google Scholar

Khalafi-Nezhad, A., and Panahi, F. (2014). Size-Controlled Synthesis of Palladium Nanoparticles on a Silica-Cyclodextrin Substrate: A Novel Palladium Catalyst System for the Heck Reaction in Water. ACS Sustain. Chem. Eng. 2, 1177–1186. doi:10.1021/sc5000122

CrossRef Full Text | Google Scholar

Kumari, S., Layek, S., and Pathak, D. D. (2017). Palladium Nanoparticles Immobilized on a Magnetic Chitosan-Anchored Schiff Base: Applications in Suzuki–Miyaura and Heck–Mizoroki Coupling Reactions. New J. Chem. 41, 5595–5604. doi:10.1039/C7NJ00283A

CrossRef Full Text | Google Scholar

Kumari, S., Mittal, A., Kumar, A., and Sharma, S. K. (2019). Palladium Nanoparticles Immobilized on Schiff Base‐Functionalized Graphene‐Oxide: Application in Carbon‐Carbon Cross‐Coupling Reactions. ChemistrySelect 4, 10828–10837. doi:10.1002/slct.201902242

CrossRef Full Text | Google Scholar

Lee, B., Ma, Z., Zhang, Z., Park, C., and Dai, S. (2009). Influences of Synthesis Conditions and Mesoporous Structures on the Gold Nanoparticles Supported on Mesoporous Silica Hosts. Microporous Mesoporous Mater. 122, 160–167. doi:10.1016/j.micromeso.2009.02.029

CrossRef Full Text | Google Scholar

Li, D., Egodawatte, S., Kaplan, D. I., Larsen, S. C., Serkiz, S. M., and Seaman, J. C. (2016). Functionalized Magnetic Mesoporous Silica Nanoparticles for U Removal from Low and High pH Groundwater. J. Hazard. Mater. 317, 494–502. doi:10.1016/j.jhazmat.2016.05.093

PubMed Abstract | CrossRef Full Text | Google Scholar

Ma, R., Yang, P., and Bian, F. (2018). Magnetic Dendritic Polymer Nanocomposites as Supports for Palladium: a Highly Efficient and Reusable Catalyst for Mizoroki-Heck and Suzuki-Miyaura Coupling Reactions. New J. Chem. 42, 4748–4756. doi:10.1039/c7nj05014c

CrossRef Full Text | Google Scholar

Ma'mani, L., Miri, S., Mahdavi, M., Bahadorikhalili, S., Lotfi, E., Foroumadi, A., et al. (2014). Palladium Catalyst Supported on N-Aminoguanidine Functionalized Magnetic Graphene Oxide as a Robust Water-Tolerant and Versatile Nanocatalyst. RSC Adv. 4, 48613–48620. doi:10.1039/c4ra07130a

CrossRef Full Text | Google Scholar

Mehmood, A., Ghafar, H., Yaqoob, S., Gohar, U. F., and Ahmad, B. (2017). Mesoporous Silica Nanoparticles: a Review. J. Dev. Drugs 6, 1–14. doi:10.4172/2329-6631.1000174

CrossRef Full Text | Google Scholar

Moreira, A. F., Dias, D. R., and Correia, I. J. (2016). Stimuli-responsive Mesoporous Silica Nanoparticles for Cancer Therapy: A Review. Microporous Mesoporous Mater. 236, 141–157. doi:10.1016/j.micromeso.2016.08.038

CrossRef Full Text | Google Scholar

Movassagh, B., and Rezaei, N. (2015). A Magnetic Porous Chitosan-Based Palladium Catalyst: a green, Highly Efficient and Reusable Catalyst for Mizoroki-Heck Reaction in Aqueous media. New J. Chem. 39, 7988–7997. doi:10.1039/c5nj01337b

CrossRef Full Text | Google Scholar

Mpungose, P., Vundla, Z., Maguire, G., and Friedrich, H. (2018). The Current Status of Heterogeneous Palladium Catalysed Heck and Suzuki Cross-Coupling Reactions. Molecules 23, 1676. doi:10.3390/molecules23071676

PubMed Abstract | CrossRef Full Text | Google Scholar

Narayan, R., Nayak, U., Raichur, A., and Garg, S. (2018). Mesoporous Silica Nanoparticles: A Comprehensive Review on Synthesis and Recent Advances. Pharmaceutics 10, 118. doi:10.3390/pharmaceutics10030118

PubMed Abstract | CrossRef Full Text | Google Scholar

Nasrollahzadeh, M., Azarian, A., Ehsani, A., and Khalaj, M. (2014). Preparation, Optical Properties and Catalytic Activity of TiO 2 @Pd Nanoparticles as Heterogeneous and Reusable Catalysts for Ligand-free Heck Coupling Reaction. J. Mol. Catal. A: Chem. 394, 205–210. doi:10.1016/j.molcata.2014.06.033

CrossRef Full Text | Google Scholar

Reza Hajipour, A., and Khorsandi, Z. (2020). Asymmetric Intermolecular Heck Reaction of Aryl Halides by Pd-Histidine Organocatalysts. Mod. Chem. 8, 18. doi:10.11648/j.mc.20200802.11

CrossRef Full Text | Google Scholar

Rosenholm, J. M., Zhang, J., Linden, M., and Sahlgren, C. (2016). Mesoporous Silica Nanoparticles in Tissue Engineering - a Perspective. Nanomedicine 11, 391–402. doi:10.2217/nnm.15.212

PubMed Abstract | CrossRef Full Text | Google Scholar

Sarkar, C., Pendem, S., Shrotri, A., Dao, D. Q., Pham Thi Mai, P., Nguyen Ngoc, T., et al. (2019). Interface Engineering of Graphene-Supported Cu Nanoparticles Encapsulated by Mesoporous Silica for Size-dependent Catalytic Oxidative Coupling of Aromatic Amines. ACS Appl. Mater. Inter. 11, 11722–11735. doi:10.1021/acsami.8b18675

PubMed Abstract | CrossRef Full Text | Google Scholar

Sayahi, M. H., Bahadorikhalili, S., Saghanezhad, S. J., Miller, M. A., and Mahdavi, M. (2020). Sulfonic Acid-Functionalized Poly(4-Styrenesulfonic Acid) Mesoporous Graphene Oxide Hybrid for One-Pot Preparation of Coumarin-Based Pyrido[2,3-D]pyrimidine-Dione Derivatives. Res. Chem. Intermed 46, 491–507. doi:10.1007/s11164-019-03962-6

CrossRef Full Text | Google Scholar

Sherwood, J., Clark, J. H., Fairlamb, I. J. S., and Slattery, J. M. (2019). Solvent Effects in Palladium Catalysed Cross-Coupling Reactions. Green. Chem. 21, 2164–2213. doi:10.1039/c9gc00617f

CrossRef Full Text | Google Scholar

Sobhani, S., Zeraatkar, Z., and Zarifi, F. (2015). Pd Complex of an NNN Pincer Ligand Supported on γ-Fe2O3@SiO2 Magnetic Nanoparticles: a New Catalyst for Heck, Suzuki and Sonogashira Coupling Reactions. New J. Chem. 39, 7076–7085. doi:10.1039/c5nj00344j

CrossRef Full Text | Google Scholar

Targhan, H., Hassanpour, A., Sohrabnezhad, S., and Bahrami, K. (2020). Palladium Nanoparticles Immobilized with Polymer Containing Nitrogen-Based Ligand: A Highly Efficient Catalyst for Suzuki-Miyaura and Mizoroki-Heck Coupling Reactions. Catal. Lett. 150, 660–673. doi:10.1007/s10562-019-02981-7

CrossRef Full Text | Google Scholar

Tashrifi, Z., Bahadorikhalili, S., Lijan, H., Ansari, S., Hamedifar, H., and Mahdavi, M. (2019). Synthesis and Characterization of γ-Fe2O3@SiO2-(CH2)3-PDTC-Pd Magnetic Nanoparticles: a New and Highly Active Catalyst for the Heck/Sonogashira Coupling Reactions. New J. Chem. 43, 8930–8938. doi:10.1039/c9nj01562k

CrossRef Full Text | Google Scholar

Xiao, J., Zhang, H., Ejike, A. C., Wang, L., Tao, M., and Zhang, W. (2021). Phenanthroline Functionalized Polyacrylonitrile Fiber with Pd(0) Nanoparticles as a Highly Active Catalyst for the Heck Reaction. Reactive Funct. Polym. 161, 104843. doi:10.1016/j.reactfunctpolym.2021.104843

CrossRef Full Text | Google Scholar

Xu, J., Qu, Z., Wang, Y., and Huang, B. (2019). HCHO Oxidation over Highly Dispersed Au Nanoparticles Supported on Mesoporous Silica with superior Activity and Stability. Catal. Today 327, 210–219. doi:10.1016/j.cattod.2018.04.051

CrossRef Full Text | Google Scholar

Yao, T., Zhang, F., Zhang, J., and Liu, L. (2020). Palladium-Catalyzed Intermolecular Heck-type Dearomative [4 + 2] Annulation of 2H-Isoindole Derivatives with Internal Alkynes. Org. Lett. 22, 5063–5067. doi:10.1021/acs.orglett.0c01643

PubMed Abstract | CrossRef Full Text | Google Scholar

Zarandi, A. F. (2019). Air Pollution Method: A New Method Based on Ionic Liquid Passed on Mesoporous Silica Nanoparticles for Removal of Manganese Dust in the Workplace Air. Anal. Methods Environ. Chem. J. 2, 5–14. doi:10.24200/amecj.v2.i01.52

CrossRef Full Text | Google Scholar

Zhang, Z., Zha, Z., Gan, C., Pan, C., Zhou, Y., Wang, Z., et al. (2006). Catalysis and Regioselectivity of the Aqueous Heck Reaction by Pd(0) Nanoparticles under Ultrasonic Irradiation. J. Org. Chem. 71 (11), 4339–4342. doi:10.1021/jo060372b

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhou, B., Wang, H., Cao, Z. Y., Zhu, J. W., Liang, R. X., Hong, X., et al. (2020). Dearomative 1,4-difunctionalization of Naphthalenes via Palladium-Catalyzed Tandem Heck/Suzuki Coupling Reaction. Nat. Commun. 11, 4380. doi:10.1038/s41467-020-18137-w

PubMed Abstract | CrossRef Full Text | Google Scholar

Zolfigol, M. A., Azadbakht, T., Khakyzadeh, V., Nejatyami, R., and Perrin, D. M. (2014). C(sp2)-C(sp2) Cross Coupling Reactions Catalyzed by an Active and Highly Stable Magnetically Separable Pd-Nanocatalyst in Aqueous media. RSC Adv. 4, 40036–40042. doi:10.1039/c4ra06097k

CrossRef Full Text | Google Scholar