Yang Luo
Hai Wang
Le-Yi Zhao
Yong-Lai Zhang- State Key Laboratory of Integrated Optoelectronics, College of Electronic Science and Engineering, Jilin University, Changchun, China
We have investigated a strong coupled system composed of a MAPbIxCl3-x perovskite film and aluminum conical nanopits array. The hybrid states formed by surface plasmons and free carriers, rather than the traditional excitons, is observed in both steady-state reflection measurements and transient absorption spectra. In particular, under near upper band resonant excitation, the bleaching signal from the band edge of uncoupled perovskite was completely separated into two distinctive bleaching signals of the hybrid system, which is clear evidence for the formation of strong coupling states between the free carrier–plasmon state. Besides this, a Rabi splitting up to 260 meV is achieved. The appearance of the lower bands can compensate for the poor absorption of the perovskite in the NIR region. Finally, we found that the lifetime of the free carrier–SP hybrid states is slightly shorter than that of uncoupled perovskite film, which can be caused by the ultrafast damping of the SPs modes. These peculiar features on the strong coupled hybrid states based on free charge carriers can open new perspectives for novel plasmonic perovskite solar cells.
Introduction
Organometal halide perovskites are emerging as a class of attractive materials for solution-processed optoelectronic devices with outstanding performance.(Jeon et al., 2015; Yang et al., 2015; Long et al., 2020; Chen et al., 2021; Privitera et al., 2021). Perovskites possess the same crystal structure of calcium titanate ABX3 (D. Weber and Naturforsch, 1978), where A and B are typical organic cations (methylammonium or formamidinium) and metal cations (Pb2+ or Sn2+) jointly bound to X, halide anions (Cl−, Br− or I−). Through compositional control of such components and ratios, various perovskite materials can be realized (Zhao and Zhu, 2016; Correa-Baena et al., 2017). Owing to the specific crystal structure, perovskites show great advantages, such as high absorption coefficient, high charge-carrier mobility, low trap density, and long charge diffusion length (Stranks et al., 2013; Xing et al., 2013). Simultaneously, through improving the architecture of the photovoltaic devices, a power conversion efficiency (PCE) of up to 25.2% is achieved (Yoo et al., 2021). Methylammonium (MA) lead trihalide perovskites with the chemical composition CH3NH3PbXnY3–n is most widely and maturely researched. Their fundamental parameters, such as photoexcited charge-carrier dynamics and carrier diffusion length, have been deeply explored. In transient absorption measurements, a long charge diffusion length >1 μm is revealed in CH3NH3PbClxI3–x perovskite films (Stranks et al., 2013). Furthermore, the nature of photogenerated species has also been expounded carefully. It is confirmed that, upon photoexcitation, excitons within the perovskite can be spontaneously dissociated into free electrons and holes, namely, conventional excitons can be displaced by free charge carriers, which are identified as dominated photogenerated species in perovskite film (Manser and Kamat, 2014). These characteristics bring many distinct advantages, making the OLHP available to high-performance solar cells, light-emitting diodes, and photodetectors.
Moreover, great progress has also been made in using surface plasmons (SPs) to further enhance the performance of plasmonic devices based on OLHP (Fang et al., 2010; Bi et al., 2013; Ren et al., 2020; Juan et al., 2021; Krisnanda et al., 2021). Affected by the SPs, the optoelectronic characteristics of the perovskite film can be significantly tuned, such as enhancement of absorption, reduction of exciton binding energy, increase of charge mobility, and so on (Saliba et al., 2015; Chan et al., 2017; Ding et al., 2018; Ma et al., 2019; Mohamed Saheed et al., 2019; Krisnanda et al., 2021). However, most of the works still survive in the weak coupling regime in which the wave function of the perovskite material is unperturbed. In contrast, only a few reports have emerged on the strong coupling between SPs and OLHP. In a strong coupling regime, the excitation energy can be rapidly exchanged between SPs modes and materials with the formation of new hybrid states separated energetically by a Rabi splitting (Qian et al., 2021; Su et al., 2021; Zhao et al., 2021). In this regime, the new states are coherently super-positioned with intriguing phenomena, such as Bose–Einstein condensation (Plumhof et al., 2014) and thresholdless lasing (Ding and Ning, 2012; Wang et al., 2021). Among the variety of research, many types of excitonic materials, for instance, J-aggregates (Hao et al., 2011; Wang et al., 2016), dye molecules (Wang et al., 2017), quantum dots (Wang et al., 2016), and two-dimensional material (Liu et al., 2016; Shan et al., 2019) are realized in a strong coupling regime with SPs. In contrast, so far little is known about the coherent hybrid system generated by the interaction of free charge carriers and SPs. Particularly, there is still limited understanding on the kinetics of hybrid SP–free charge carrier states. It is also worth emphasizing again that, on account of the small exciton binding energies, free charge carriers characterized by slow recombination and relatively high mobility can be efficiently generated in OLHP (Manser and Kamat, 2014). Thus, there is a strong incentive to harness such materials for studying strong coupling between SPs and free charge carriers.
In this work, we demonstrate that strong SP–free charge carrier coupling can be achieved with CH3NH3PbClxI3–x perovskite film and SPs supported by Al conical nanopits arrays. Furthermore, under upper band resonant excitation, direct evidence of the formation of the hybrid free charge carrier–SP states is clearly shown in the transient absorption (TA) spectra. The result also proves that the band filling of the upper states follows the Burstein–Moss band filling model. Finally, we measured a shorter lifetime of the hybrid SP–free charge carrier states, which was accelerated by the ultrafast damping of the SPs character.
Experimental Section
The fabrication processes of the strong SP–free charge carrier coupled system is described in Figure 1A. First, the cleaned glasses/ITO was milled by means of a focused ion beam to define the shape of a square-like array of conical pits. Afterward, an electron beam evaporator was used for the 200-nm-thick aluminum (Al) film deposition on the patterned glasses/ITO substrates. Then, conical pit arrays with a period from 300 to 450 nm can be replicated on top of the Al film with a total area of 50 × 50 μm2. Al was selected not only simply for its cost-effectiveness and abundance, but also for the wide SP spectral range (Li et al., 2016). Here, the processed Al nanopits with uniform size (as shown in Figure 1C) show a plasmon resonance that matches with the broad absorbance spectrum of CH3NH3PbClxI3-x film. To obtain a strong coupled hybrid system between SPs and free charge carriers, the perovskite films were directly formed on Al conical nanopits. The perovskite precursor solution was prepared by dissolving 139.0 mg of PbI2 and 238.5 mg of CH3NH3I in 2 ml N,N-dimethylformamide (DMF). Then, the samples were obtained by spin-coating these precursor solutions at 3000 rpm for 30 s and annealed at 80°C for 100 min in a nitrogen-filled glove box. Figure 1D provides SEM images of the morphology of the synthesized CH3NH3PbIxCl3-x film with grain sizes ranging from 200 to 250 nm CH3NH3PbClxI3-x and CH3NH3PbI3 have similar optical properties, such as absorption spectrum, bandgaps, and Fermi levels. However, it is demonstrated that the Cl-doped perovskite film has a long charge carrier diffusion length, always leading to a higher efficiency solar cell (Xing et al., 2013). Here CH3NH3PbClxI3-x is selected rather than CH3NH3PbI3.
FIGURE 1. (A) Steps of fabrication of strong free charge carrier–SP coupling system, (B, C) SEM image of the conical nanopits on glass/ITO and Al layer, (D) SEM image of perovskite layer, (E) the mode diagram of the hybrid free charge carrier–SP system; the inset shows the crystal structure of CH3NH3PbClxI3-x perovskite.
Steady-State Measurements
Figure 2A shows the reflection spectra of Al nanopit arrays with various periods. The reflection peaks display a pronounced red shift as the period of the nanopit arrays increases, showing the SP resonance region from 490 to 750 nm. In the meantime, for each nanopit array, a shoulder peak appeared on the higher energy side of the main SPs peak. The offset of the two peaks can be attributed to the difference of the refractive index of the media above and below the Al film. The reflection spectrum of the CH3NH3PbClxI3-x perovskite film deposited on flat Al film is also shown in Figure 2A as a black line. As can be seen, the perovskite film has a strong optical absorption with a band edge at 1.65 eV. Observably, all the SP bands overlap within the reflection spectrum of CH3NH3PbClxI3-x film. Thus, when perovskite film is formed on Al nanopit arrays, the hybrid system is prepared.
FIGURE 2. (A) Reflection spectra of Al conical nanopit arrays covered by PMMA film. The lattice period is tuned from 300 to 450 nm. The black line shows the reflection spectrum of the CH3NH3PbClxI3-x perovskite film on flat Al film. (B) Reflection spectra of the perovskite layer on flat Al film and conical nanopit arrays. The lattice period is tuned from 300 to 450 nm. (C) Dispersion curve of hybrid free change carrier–SP strong coupled system. The horizontal dashed line shows the band edge of the CH3NH3PbClxI3-x perovskite film.
A key point to underlined here is the demonstration that free charge carriers generated in perovskite film and SPs in the hybrid system can enter the strong coupled regime. Because the initial study on strong coupling was focused on a series of J-aggregate molecules with unusually strong transition dipoles, which was considered as the only possible candidate for strong coupling. However, moving forward, much larger Rabi splitting has also been achieved between SPs and molecules with broad absorption spectra, such as photochromic molecules and semiconductor polymer (Schwartz et al., 2011; Orgiu et al., 2015). Actually, several studies demonstrate that the vacuum Rabi splitting depends on the energy-integrated absorption of the material, namely, a larger vacuum Rabi splitting can be achieved by using material with higher absorption cross-sections (Gambino et al., 2014). Therefore, in the following part, a clear indication of strong coupling between SPs and free charge carriers in CH3NH3PbClxI3-x perovskite film is provided.
Figure 2B shows a series of reflection spectra of the hybrid system with different Al nanopit periods. Compared with the perovskite film on flat Al film, the reflection spectra of the hybrid systems are significantly changed. In particular, at the wavelength longer than the band edge of the perovskite, extra reflection peaks corresponding to the lower bands are shown, which can lead to overcoming the poor absorption of the CH3NH3PbClxI3-x film in the NIR region. On the other side, due to the strong absorption in the visible range of the perovskite film, the reflection spectra of the hybrid system at the higher energy side only changed slightly. However, it can be seen that the peak position related to the upper bands also has a red shift with the lattice period increasing as the red arrow shown in Figure 2B. Furthermore, the dispersion diagram of the two bands is shown in Figure 2C. As expected, anticrossing behavior as remarkable experimental evidence of strong coupling is clearly observed (Dintinger et al., 2005).
However, because most light is absorbed by the perovskite layer when the wavelength (λ) of the light is shorter than the band edge of CH3NH3PbClxI3-x (λ < 760 nm), the formation of the upper bands in the hybrid systems cannot be clearly reflected from reflection spectra. The evidence of the formation of the new hybrid SP–free charge carrier states is not comprehensive. The Rabi splitting energy cannot be revealed just from steady-state measurements. Therefore, transient absorption spectroscopy was performed to gain a further insight into the formation and dynamics of the hybrid states.
TA experiments
TA spectroscopy, also named the pump-probe technique (Gao et al., 2010; Wang et al., 2013), is an effective approach to the study of charge carrier transfer and recombination dynamics of perovskite films (Zhang et al., 2015; Zhang et al., 2016). Femtosecond reflective TA spectra was carried out by a 100 fs laser pump-probe system. A Ti:sapphire amplifier system was used to provide an 800-nm wavelength laser with 100 fs pulse width and 500 Hz repetition rate. The amplified output was split into two parts. The stronger part was sent to a β-barium borate (BBO) crystal or TOPAS system to generate the pump pulse at 400 or 560 nm while the weaker part was focused on a sapphire crystal to create a continuous white light as a probe beam. The relative delay between the pump and probe beam was controlled by an optical delay line (Newport DL325). Then, the two beams were focused on the sample by a microscope objective. The probe beam reflected from the sample was collected by an optical spectrometer (Avantes AvaSpec -ULS2048CL-EVO) while the reflected pump beam was filtered. Here, we focused on the TA spectroscopy findings on the nature of the hybrid SP–free charge carrier states. To begin with, the first part of the TA measurements were performed under nonresonant conditions by the 400 nm laser pulse. Figure 3A shows the TA spectra of CH3NH3PbClxI3-x film on flat Al film. The figure consists of a negative band at 730 nm corresponding to band edge ground state bleaching, and on both sides of the bleaching, there are two positive signals due to the photoinduced absorption of hot electrons and holes (Herz, 2016). In addition, it is worth noting that the high-energy tail of the band edge bleaching spectrum is broadened and shows a blue shift in the first 10 ps, which can be explained by a dynamic Burstein−Moss shift (Manser and Kamat, 2014). Namely, after laser excitation, the conduction and valence band edges are filled with thermalized carriers; further considering the Pauli exclusion principle, the occupation of band-edge states is pushed to higher energies, leading to a dynamic Burstein–Moss band filling model.
FIGURE 3. Transient absorption spectra of CH3NH3PbClxI3-x perovskite film on flat (A) Al film and (B–D) different Al nanopit arrays with periods of 300, 350, and 375 nm under 400 nm excitation. The spectra are recorded at 10, 100, 220, 460, 660, and 1300 ps.
Figures 3B–D shows the corresponding spectra of CH3NH3PbClxI3-x film on Al nanopit arrays with different periods of 300, 350, and 375 nm. The spectra are a little changed compared with the reference sample on flat Al film. First, for the period equal to 300 nm, the spectra show a negative signal at 760 nm and a shoulder peak at 700 nm, which are possibly corresponded to the hybrid bands. However, the separation between the two new peaks is much smaller than that measured from steady-state reflection spectra, so the strong coupling regime still cannot be clearly identified. For the period equal to 350 and 375 nm, Figures 3C,D shows a bleaching band around 730 nm, which is still dominated by the ground-state bleaching from uncoupled CH3NH3PbClxI3-x film. On the red side of the bleaching band, a positive signal is observed corresponding to the thermal effect of the SPs (Hao et al., 2011) while the bleaching signals from the upper bands are also almost undetectable. In fact, similar to the previous work under nonresonant excitation (Hao et al., 2011; Wang et al., 2016), the intrinsic photophysics of the strong coupled hybrid system cannot be observed. Under such conduction, the initial relaxation process is dominated by a state-filling process and SP thermal effect as the positive signal reported in Supplementary Figure S1.
To explore the nature photophysics of the hybrid SP–free charge carrier states more deeply, TA measurements were further carried out under near upper state resonant excitation by a pulsed laser at 560 nm. Figure 4A illustrates the TA spectra of CH3NH3PbClxI3-x film on flat Al film. As a reference, the plot is similar to the spectra obtained under nonresonant excitation at 400 nm. A bleaching signal around 730 nm, which also conforms to the Burstein–Moss band filling model, shows a carrier accumulation–induced blue shift (Manser and Kamat, 2014) while the small positive signals below 680 nm are assigned to photoinduced absorption. The spectra for CH3NH3PbClxI3-x film on different periodic nanopit arrays are reported in Figures 4B–D, which more clearly suggest the formation of strong coupled hybrid SP–free charge carrier states. First, when the nanopit period equals 300 nm, the spectra show a main bleaching peak at 750 nm, corresponding to the lower hybrid band. On the contrary, the amplitude of the upper hybrid band is much smaller, showing a shoulder peak around 670 nm. Under this condition, the splitting was not obvious, which suggests the coupling strength is low. This can be further proved by the dynamic behaver of the hybrid states (see Figure 5), which is still similar to the bleaching recovery of pure perovskite film.
FIGURE 4. Transient absorption spectra of CH3NH3PbClxI3-x perovskite film on flat (A) Al film and (B–D) different Al nanopit arrays with periods of 300, 350, and 375 nm under 560 nm excitation. The spectra are recorded at 5, 55, 100, 220, 460, and 1300 ps.
FIGURE 5. Normalized bleaching dynamics under 560 nm resonant excitation of CH3NH3PbClxI3-x perovskite film on a flat Al film (measured at 737 nm) and on Al nanopit arrays with periods of 350 nm (measured at the hybrid bands of 705 and 820 nm) and 300 nm (measured at the upper band of 737 nm).
More importantly, when the nanopit period equals 350 nm, the SP resonance of Al nanopits can resonate with the free charge carriers in perovskite film. With respect to the reference sample, the TA spectra of the hybrid system show completely different properties. The band edge transition bleaching is completely separated into two bleaching signals at around 700 and 820 nm, which can be attributed to the upper and lower hybrid SP–free charge carrier states with observation of Rabi splitting energy up to 260 meV. Such behavior provides more objective, precise evidence than that observed from steady-state reflection measurements. With the period further increased to 375 nm, as shown in Figure 4D, the bleaching peak of the upper state is a little red shifted while the bleaching band of the lower state also experiences a red shift almost extending out of the detection window. By comprehensive analysis of the three different period hybrid systems, the simultaneous shifting of both upper and lower hybrid states is consistent with the characteristic strong coupling: anticrossing behavior, which further remarkably underlines the formation of the coherent hybrid SP–free charge carrier states. Another important observation that needs to be stressed here is that, under upper band resonant excitation, the lower band bleaching signal is narrowing with time. Such distinguishable narrowing of the lower band can also be described by the Burstein–Moss effect. On the other hand, the shape of the lower hybrid states does not change with the time. We, therefore, attribute that free carriers are accumulated at the lower bands of the hybrid states after 560 nm laser excitation. The understanding presented here provides new mechanisms of strong coupling between SPs and free charge carriers, which serve to shed light on designing novel ultrafast plasmonic devices.
Finally, the kinetic process of the hybrid SP–free charge carrier states is analyzed. In Figure 5, we plot the amplitude-normalized dynamics of the lower and upper hybrid bands of the coupled sample with a nanopit period of 350 nm compared with the dynamics of the band edge bleaching of perovskite film on a flat Al film. As shown, under upper band resonant excitation, the population dynamics of the hybrid states are shorter than the bleaching recovery of free charge carriers in pure perovskite film. This result show interesting differences from the lifetime measured from hybrid states composed of traditional excitons and SPs. Previous experiments confirm that the longer lifetimes of the hybrid states is intrinsic and can be even longer than the lifetime of bare excitons, which is accorded with a non-Markovian regime (Canaguier-Durand et al., 2015). However, here we should emphasize that, again, the excited-state population in CH3NH3PbClxI3-x film is dominated by free charge carriers. The ultrafast damping plasmon character (Pelton et al., 2008; Hartland, 2011) reduces the lifetime of the coherent hybrid SP–free charge carrier states. Namely, the relaxation of such new hybrid states can be expedited by SPs, leading to a shorter lifetime.
Conclusion
In summary, we construct a hybrid structure comprising an Al subwavelength nanopit array and perovskite film. In steady-state measurements, the reflection spectra profile of the hybrid systems characterized by two distinct bands, whose dispersions show the typical signature of strong coupling. These results experimentally demonstrate that strong coupling can be achieved with SPs and free charge carriers generated in CH3NH3PbClxI3-x film. Moreover, the nature photophysics of the new hybrid SP–free charge carrier states was studied by TA spectroscopy. Under nonresonant excitation by a 400-nm laser, the initial relaxation process is dominated by a state-filling effect, which still cannot provide the intrinsic dynamics of the hybrid state. Furthermore, under near upper band resonant excitation, the TA spectra remarkably displayed the formation of the hybrid SP–free charge carrier state, in which the upper bands can be well ascribed to the dynamic Burstein–Moss effect. We have also found that the lifetime of the hybrid SP–free charge carrier states is shorter than the bleaching recovery of pure CH3NH3PbClxI3-x film, which is different from that observed in a strong coupling system with traditional excitons conformed to a non-Markovian regime. As a possible explanation, we assume that the ultrafast damping of the SP modes accelerates the relaxation of the hybrid SP–free charge carrier states. To conclude, these new insights on strong coupling with hybrid organic-inorganic perovskites provide a new framework to develop low-cost photovoltaic and light-emitting devices and nanolasers (Sanvitto and Kena Cohen, 2016). New developments on nanoplasmonic devices working in a strong coupling regime with free charge carriers are surely on the horizon.
Data Availability Statement
The original contributions presented in the study are included in the article/Supplementary Material, further inquiries can be directed to the corresponding author.
Author Contributions
YL, HW, and Y-LZ conceived the research. YL and HW fabricated the samples. YL and L-YZ performed the measurements. All authors discussed the data and wrote the manuscript.
Funding
This work was supported by the National Key Research and Development Program of China and the National Natural Science Foundation of China (NSFC) under Grants 21903035, 22073037, and 21773087.
Conflict of Interest
The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.
Publisher’s Note
All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors, and the reviewers. Any product that may be evaluated in this article, or claim that may be made by its manufacturer, is not guaranteed or endorsed by the publisher.
Supplementary Material
The Supplementary Material for this article can be found online at: https://www.frontiersin.org/articles/10.3389/fchem.2021.818459/full#supplementary-material
References
Bi, Y.-G., Feng, J., Li, Y.-F., Zhang, X.-L., Liu, Y.-F., Jin, Y., et al. (2013). Broadband Light Extraction from White Organic Light-Emitting Devices by Employing Corrugated Metallic Electrodes with Dual Periodicity. Adv. Mater. 25, 6969–6974. doi:10.1002/adma.201302367
Canaguier-Durand, A., Genet, C., Lambrecht, A., Ebbesen, T. W., and Reynaud, S. (2015). Non-Markovian Polariton Dynamics in Organic Strong Coupling. Eur. Phys. J. D 69, 1–7. doi:10.1140/epjd/e2014-50539-x
Chan, K., Wright, M., Elumalai, N., Uddin, A., and Pillai, S. (2017). Plasmonics in Organic and Perovskite Solar Cells: Optical and Electrical Effects. Adv. Opt. Mater. 5, 1600698. doi:10.1002/adom.201600698
Chen, J., Zhou, Y., Fu, Y., Pan, J., Mohammed, O. F., and Bakr, O. M. (2021). Oriented Halide Perovskite Nanostructures and Thin Films for Optoelectronics. Chem. Rev. 121, 12112–12180. doi:10.1021/acs.chemrev.1c00181
Correa-Baena, J.-P., Abate, A., Saliba, M., Tress, W., Jesper Jacobsson, T., Grätzel, M., et al. (2017). The Rapid Evolution of Highly Efficient Perovskite Solar Cells. Energy Environ. Sci. 10, 710–727. doi:10.1039/C6EE03397K
Ding, K., and Ning, C. Z. (2012). Metallic Subwavelength-Cavity Semiconductor Nanolasers. Light Sci. Appl. 1–e20. doi:10.1038/lsa.2012.20
Ding, R., Wang, X.-P., Feng, J., Li, X.-B., Dong, F.-X., Tian, W.-Q., et al. (2018). Clarification of the Molecular Doping Mechanism in Organic Single-Crystalline Semiconductors and Their Application in Color-Tunable Light-Emitting Devices. Adv. Mater. 30, 1801078. doi:10.1002/adma.201801078
Dintinger, J., Klein, S., Bustos, F., Barnes, W. L., and Ebbesen, T. W. (2005). Strong Coupling between Surface Plasmon-Polaritons and Organic Molecules in Subwavelength Hole Arrays. Phys. Rev. B 71, 035424. doi:10.1103/physrevb.71.035424
Fang, H.-H., Yang, J., Ding, R., Chen, Q.-D., Wang, L., Xia, H., et al. (2010). Polarization Dependent Two-Photon Properties in an Organic Crystal. Appl. Phys. Lett. 97, 101101. doi:10.1063/1.3486683
Gambino, S., Mazzeo, M., Genco, A., Di Stefano, O., Savasta, S., Patanè, S., et al. (2014). Exploring Light-Matter Interaction Phenomena under Ultrastrong Coupling Regime. ACS Photon. 1, 1042–1048. doi:10.1021/ph500266d
Gao, B.-R., Wang, H.-Y., Hao, Y.-W., Fu, L.-M., Fang, H.-H., Jiang, Y., et al. (2010). Time-Resolved Fluorescence Study of Aggregation-Induced Emission Enhancement by Restriction of Intramolecular Charge Transfer State. J. Phys. Chem. B 114, 128–134. doi:10.1021/jp909063d
Hao, Y.-W., Wang, H.-Y., Jiang, Y., Chen, Q.-D., Ueno, K., Wang, W.-Q., et al. (2011). Hybrid-State Dynamics of Gold Nanorods/Dye J-Aggregates under Strong Coupling. Angew. Chem. 123, 7970–7974. doi:10.1002/ange.201101699
Hartland, G. V. (2011). Optical Studies of Dynamics in Noble Metal Nanostructures. Chem. Rev. 111, 3858–3887. doi:10.1021/cr1002547
Herz, L. M. (2016). Charge-Carrier Dynamics in Organic-Inorganic Metal Halide Perovskites. Annu. Rev. Phys. Chem. 67, 65–89. doi:10.1146/annurev-physchem-040215-112222
Jeon, N. J., Noh, J. H., Yang, W. S., Kim, Y. C., Ryu, S., Seo, J., et al. (2015). Compositional Engineering of Perovskite Materials for High-Performance Solar Cells. Nature 517, 476–480. doi:10.1038/nature14133
Juan, F., Wu, Y., Shi, B., Wang, M., Wang, M., Xu, F., et al. (2021). Plasmonic Au Nanooctahedrons Enhance Light Harvesting and Photocarrier Extraction in Perovskite Solar Cell. ACS Appl. Energ. Mater. 4, 3201–3209. doi:10.1021/acsaem.0c02973
Krisnanda, T., Zhang, Q., Dini, K., Giovanni, D., Liew, T. C. H., and Sum, T. C. (2021). Room Temperature Light‐Mediated Long‐Range Coupling of Excitons in Perovskites. Adv. Opt. Mater. 9, 2001835. doi:10.1002/adom.202001835
Li, J., Ueno, K., Uehara, H., Guo, J., Oshikiri, T., and Misawa, H. (2016). Dual Strong Couplings between Tpps J-Aggregates and Aluminum Plasmonic States. J. Phys. Chem. Lett. 7, 2786–2791. doi:10.1021/acs.jpclett.6b01224
Liu, W., Lee, B., Naylor, C. H., Ee, H.-S., Park, J., Johnson, A. T. C., et al. (2016). Strong Exciton-Plasmon Coupling in MoS2 Coupled with Plasmonic Lattice. Nano Lett. 16, 1262–1269. doi:10.1021/acs.nanolett.5b04588
Long, G., Sabatini, R., Saidaminov, M. I., Lakhwani, G., Rasmita, A., Liu, X., et al. (2020). Chiral-Perovskite Optoelectronics. Nat. Rev. Mater. 5, 423–439. doi:10.1038/s41578-020-0181-5
Ma, C., Liu, C., Huang, J., Ma, Y., Liu, Z., Li, L.-J., et al. (2019). Plasmonic‐Enhanced Light Harvesting and Perovskite Solar Cell Performance Using Au Biometric Dimers with Broadband Structural Darkness. Sol. RRL 3, 1900138. doi:10.1002/solr.201900138
Manser, J. S., and Kamat, P. V. (2014). Band Filling with Free Charge Carriers in Organometal Halide Perovskites. Nat. Photon 8, 737–743. doi:10.1038/nphoton.2014.171
Mohamed Saheed, M. S., Mohamed, N. M., Mahinder Singh, B. S., and Jose, R. (2019). Surface Plasmon Assisted Electron-Hole Migration for High Photocurrent Density Generation in a Perovskite Solar Cell. ACS Appl. Energ. Mater. 2, 8707–8714. doi:10.1021/acsaem.9b01675
Orgiu, E., George, J., Hutchison, J. A., Devaux, E., Dayen, J. F., Doudin, B., et al. (2015). Conductivity in Organic Semiconductors Hybridized with the Vacuum Field. Nat. Mater 14, 1123–1129. doi:10.1038/nmat4392
Pelton, M., Aizpurua, J., and Bryant, G. (2008). Metal‐nanoparticle Plasmonics. Laser Photon. Rev. 2, 136–159. doi:10.1002/lpor.200810003
Plumhof, J. D., Stöferle, T., Mai, L., Scherf, U., and Mahrt, R. F. (2014). Room-temperature Bose-Einstein Condensation of Cavity Exciton-Polaritons in a Polymer. Nat. Mater 13, 247–252. doi:10.1038/nmat3825
Privitera, A., Righetto, M., Cacialli, F., and Riede, M. K. (2021). Perspectives of Organic and Perovskite‐Based Spintronics. Adv. Opt. Mater. 9, 2100215. doi:10.1002/adom.202100215
Qian, Z., Shan, L., Zhang, X., Liu, Q., Ma, Y., Gong, Q., et al. (2021). Spontaneous Emission in Micro- or Nanophotonic Structures. PhotoniX 2, 21. doi:10.1186/s43074-021-00043-z
Ren, H., Ren, X., Niu, K., Wang, S., Huang, Z., and Wu, X. (2020). Optical-Electrical-Thermal Optimization of Plasmon-Enhanced Perovskite Solar Cells. Phys. Chem. Chem. Phys. 22, 17068–17074. doi:10.1039/D0CP02220A
Saliba, M., Zhang, W., Burlakov, V. M., Stranks, S. D., Sun, Y., Ball, J. M., et al. (2015). Plasmonic-Induced Photon Recycling in Metal Halide Perovskite Solar Cells. Adv. Funct. Mater. 25, 5038–5046. doi:10.1002/adfm.201500669
Sanvitto, D., and Kéna-Cohen, S. (2016). The Road towards Polaritonic Devices. Nat. Mater 15, 1061–1073. doi:10.1038/nmat4668
Schwartz, T., Hutchison, J. A., Genet, C., and Ebbesen, T. W. (2011). Reversible Switching of Ultrastrong Light-Molecule Coupling. Phys. Rev. Lett. 106, 196405. doi:10.1103/physrevlett.106.196405
Shan, H., Yu, Y., Wang, X., Luo, Y., Zu, S., Du, B., et al. (2019). Direct Observation of Ultrafast Plasmonic Hot Electron Transfer in the Strong Coupling Regime. Light Sci. Appl. 8, 9. doi:10.1038/s41377-019-0121-6
Stranks, S. D., Eperon, G. E., Grancini, G., Menelaou, C., Alcocer, M. J. P., Leijtens, T., et al. (2013). Electron-Hole Diffusion Lengths Exceeding 1 Micrometer in an Organometal Trihalide Perovskite Absorber. Science 342, 341–344. doi:10.1126/science.1243982
Su, R., Fieramosca, A., Zhang, Q., Nguyen, H. S., Deleporte, E., Chen, Z., et al. (2021). Perovskite Semiconductors for Room-Temperature Exciton-Polaritonics. Nat. Mater. 20, 1315–1324. doi:10.1038/s41563-021-01035-x
Wang, H., Toma, A., Wang, H.-Y., Bozzola, A., Miele, E., Haddadpour, A., et al. (2016). The Role of Rabi Splitting Tuning in the Dynamics of Strongly Coupled J-Aggregates and Surface Plasmon Polaritons in Nanohole Arrays. Nanoscale 8, 13445–13453. doi:10.1039/C6NR01588C
Wang, H., Wang, H.-Y., Bozzola, A., Toma, A., Panaro, S., Raja, W., et al. (2016). Dynamics of Strong Coupling between J-Aggregates and Surface Plasmon Polaritons in Subwavelength Hole Arrays. Adv. Funct. Mater. 26, 6198–6205. doi:10.1002/adfm.201601452
Wang, H., Wang, H.-Y., Toma, A., Yano, T.-a., Chen, Q.-D., Xu, H.-L., et al. (2016). Dynamics of Strong Coupling between Cdse Quantum Dots and Surface Plasmon Polaritons in Subwavelength Hole Array. J. Phys. Chem. Lett. 7, 4648–4654. doi:10.1021/acs.jpclett.6b02059
Wang, H., Wang, H. Y., Wang, L., Chen, Q. D., Xu, H. L., Carrara, A., et al. (2017). Multimode Coherent Hybrid States: Ultrafast Investigation of Double Rabi Splitting between Surface Plasmons and Sulforhodamine 101 Dyes. Adv. Opt. Mater. 5, 1600857. doi:10.1002/adom.201600857
Wang, J., Xu, H., Su, R., Peng, Y., Wu, J., Liew, T. C. H., et al. (2021). Spontaneously Coherent Orbital Coupling of Counterrotating Exciton Polaritons in Annular Perovskite Microcavities. Light Sci. Appl. 10, 45. doi:10.1038/s41377-021-00478-w
Wang, L., Zhu, S.-J., Wang, H.-Y., Wang, Y.-F., Hao, Y.-W., Zhang, J.-H., et al. (2013). Unraveling Bright Molecule-like State and Dark Intrinsic State in Green-Fluorescence Graphene Quantum Dots via Ultrafast Spectroscopy. Adv. Opt. Mater. 1, 264–271. doi:10.1002/adom.201200020
Weber, D., and Naturforsch, Z. (1978). CH3NH3SnBrxI3-x (x = 0-3), ein Sn(II)-System mit kubischer Perowskitstruktur/CH3NH3SnBrxI3-x(x = 0-3), a Sn(II)-System with Cubic Perovskite Structure. B: J. Chem. Sci. 33, 862–865. doi:10.1515/znb-1978-0809
Xing, G., Mathews, N., Sun, S., Lim, S. S., Lam, Y. M., Grätzel, M., et al. (2013). Long-Range Balanced Electron- and Hole-Transport Lengths in Organic-Inorganic CH 3 NH 3 PbI 3. Science 342, 344–347. doi:10.1126/science.1243167
Yang, W. S., Noh, J. H., Jeon, N. J., Kim, Y. C., Ryu, S., Seo, J., et al. (2015). High-Performance Photovoltaic Perovskite Layers Fabricated through Intramolecular Exchange. Science 348, 1234–1237. doi:10.1126/science.aaa9272
Yoo, J. J., Seo, G., Chua, M. R., Park, T. G., Lu, Y., Rotermund, F., et al. (2021). Efficient Perovskite Solar Cells via Improved Carrier Management. Nature 590, 587–593. doi:10.1038/s41586-021-03285-w
Zhang, Z.-Y., Chen, X., Wang, H.-Y., Xu, M., Gao, B.-R., Chen, Q.-D., et al. (2015). Elucidating the Band Structure and Free Charge Carrier Dynamics of Pure and Impurities Doped CH3NH3PbI3−xClx Perovskite Thin Films. Phys. Chem. Chem. Phys. 17, 30084–30089. doi:10.1039/C5CP04333F
Zhang, Z.-Y., Wang, H.-Y., Zhang, Y.-X., Hao, Y.-W., Sun, C., Zhang, Y., et al. (2016). The Role of Trap-Assisted Recombination in Luminescent Properties of Organometal Halide Ch3nh3pbbr3 Perovskite Films and Quantum Dots. Sci. Rep. 6, 27286. doi:10.1038/srep27286
Zhao, Y., Yang, Y., and Sun, H.-B. (2021). Nonlinear Meta-Optics towards Applications. PhotoniX 2, 3. doi:10.1186/s43074-021-00025-1
Keywords: strong coupling, rabi splitting, perovskite, aluminum plasmonic states, transient absorption spectra, free charge carriers
Citation: Luo Y, Wang H, Zhao L-Y and Zhang Y-L (2022) Dynamics of Strong Coupling Between Free Charge Carriers in Organometal Halide Perovskites and Aluminum Plasmonic States. Front. Chem. 9:818459. doi: 10.3389/fchem.2021.818459
Received: 19 November 2021; Accepted: 06 December 2021;
Published: 14 January 2022.
Edited by:
Yun-Fei Li, Hebei University of Technology, ChinaReviewed by:
Yawei Hao, China Academy of Engineering Physics, ChinaYing Jiang, Hunan University, China
Copyright © 2022 Luo, Wang, Zhao and Zhang. This is an open-access article distributed under the terms of the Creative Commons Attribution License (CC BY). The use, distribution or reproduction in other forums is permitted, provided the original author(s) and the copyright owner(s) are credited and that the original publication in this journal is cited, in accordance with accepted academic practice. No use, distribution or reproduction is permitted which does not comply with these terms.
*Correspondence: Hai Wang, wanghai03@jlu.edu.cn