Self-Assembly Dipeptide Hydrogel: The Structures and Properties

Liangchun Li
Liangchun Li1*Li XieLi Xie1Renlin ZhengRenlin Zheng1Rongqin SunRongqin Sun2
  • 1School of Life Science and Engineering, Southwest University of Science and Technology, Mianyang, China
  • 2School of Materials Science and Engineering, Southwest University of Science and Technology, Mianyang, China

Self-assembly peptide-based hydrogels are well known and popular in biomedical applications due to the fact that they are readily controllable and have biocompatibility properties. A dipeptide is the shortest self-assembling motif of peptides. Due to its small size and simple synthesis method, dipeptide can provide a simple and easy-to-use method to study the mechanism of peptides’ self-assembly. This review describes the design and structures of self-assembly linear dipeptide hydrogels. The strategies for preparing the new generation of linear dipeptide hydrogels can be divided into three categories based on the modification site of dipeptide: 1) COOH-terminal and N-terminal modified dipeptide, 2) C-terminal modified dipeptide, and 3) uncapped dipeptide. With a deeper understanding of the relationship between the structures and properties of dipeptides, we believe that dipeptide hydrogels have great potential application in preparing minimal biocompatible materials.

Introduction

Hydrogels are cross-linked by three-dimensional networks of modified molecules that hold a large amount of water, which were first reported by Wichterle and Lím (1960). By definition, water must account for at least 10% of the total weight (or volume) of hydrogels, which is very similar to natural tissue. Due to the high water content, favorable structural features, and biocompatibility, hydrogels have great potential in biomedical applications such as drug delivery, tissue engineering, sensing, and cell culture scaffolds (Ahmed, 2015; Ghosal et al., 2018; Zou et al., 2020). Based on the different gelation mechanisms, hydrogels can be classified into chemical hydrogels and physical hydrogels (Mahinroosta et al., 2018). The chemical hydrogels are cross-linked via covalent bonds, resulting in high mechanical strength, structural stability, shape memory, and irreversible properties (Liyan et al., 2018). The irreversible properties deprive them of self-healing and impair their injectability (Tu et al., 2019). More importantly, those limit cell proliferation and migration and hence limited application in three-dimensional cell culture (Wang et al., 2019, 2020). Physical hydrogels, also known as supramolecular hydrogels, could be produced by a molecular self-assembly process (Li et al., 2020; Xian and Webber, 2020; Li et al., 2021b). Molecular self-assembly relies on noncovalent interactions, such as hydrogen bonding, hydrophobic interactions, aromatic π–π stacking interactions, and electrostatic interactions, which are weak and reversible (Whitesides and Boncheva, 2002; Webber and Pashuck, 2021). The dynamic reversible nature of these interactions endows them with self-healing and shear thinning properties; hence, they are particularly suitable for biomedical applications, as they are more flexible and can be easily injected (Hu X. et al., 2020; Gupta et al., 2020; Vazquez-Gonzalez and Willner, 2020).

The physical hydrogelators include natural polymers, such as polysaccharides (Dai et al., 2019; Chen et al., 2020; Lei et al., 2020), proteins (Wlodarczyk-Biegun et al., 2016; Fisher et al., 2017; Singh et al., 2017; Zhao et al., 2018), and polynucleotides (RNA and DNA) (Korah et al., 2018; Li et al., 2019b), and synthetic materials, such as poly (lactic-co-glycolic acid (PLGA) (Ko and Kwon, 2020), polyglycolic acid (PGA) (Prabhu et al., 2020), and polylactic acid (PLA) (Basu et al., 2016). These various polymers establish complex 3D networks of intermolecular interactions between building blocks to form macroscopic objects. Besides polymers, low-molecular-weight gelators (LMWGs) (generally <2000 Da) are of great interest because the associated gelators have intrinsic self-assembly ability to form different morphologies of fibers, rods, ribbons, and nanotubes, which could be used to build attractive tools for various biomedical applications on account of their high biocompatibility and low toxicity (Nolan et al., 2017; Ramin et al., 2017; Piras et al., 2021). Among the LMWGs, self-assembly peptide-based hydrogels are well known and have been the subject of many studies because the peptides are the most attractive building blocks, which can be readily controlled by changing the amino acid sequence of the peptides and by modifying the side chains of the peptides (Frick et al., 2017; Fu et al., 2021; Zhang et al., 2021). In particular, many small amino acid sequences responsible for the biological assembly proteins such as the amyloid-beta polypeptide (Aβ42) (Qiu et al., 2015), tau proteins (Pîr et al., 2017), and islet amyloid polypeptide (IAPP) (Fawver et al., 2014) indicated in Alzheimer’s disease, have been identified; hence, researchers can design self-assembly peptides through a biomimetic approach. The shortest self-assembling motif of peptides was dipeptide, for example, L-Phe-L-Phe, a dipeptide from Aβ42, which is also the most widely studied scaffold of supramolecular hydrogelators (Diaferia et al., 2019b). However, despite the easy synthesis and decoration of dipeptide, the prediction and design of dipeptide-based hydrogels are still challenging due to the complex nature of the molecular structure and hydrogel behavior (Fichman and Gazit, 2014; Frederix et al., 2015; Fuentes-Caparrós et al., 2019). Researchers have tried many strategies in dipeptide design to resolve this problem, such as the introduction of a combinational approach, which generated a structurally diverse hydrogel library with more than 2,000 peptides (Li et al., 2019a).

Recently, self-assembly hydrogels based on the longer (Levin et al., 2020; Mondal et al., 2020) or short peptides (Fleming and Ulijn, 2014; Tao et al., 2016; Guyon et al., 2018) and their related gel-based biomedical applications (Fukunaga et al., 2019; Ni and Zhuo, 2019) have been reviewed but in a very limited manner. In this review, we focus on the dipeptide derived from common amino acids that form hydrogels and the possible relationship between the structures and hydrogel behavior. We hope that with a deep understanding of the relationship between structures and properties of dipeptides, the dipeptide hydrogels would have an effective application in preparing minimal biocompatible materials.

The Structures of Self-Assembly Dipeptide Hydrogelators

To form a hydrogel, the dipeptide hydrogelator first self-assembled into some kind of one-dimensional (1D) supramolecular structures, like nanofibers and twisted nanoribbons, and then into three-dimensional (3D) networks to ensnare a great number of water molecules inside (Du et al., 2015). This demands that the structure of the dipeptide hydrogelator should greatly facilitate the formation of one-dimensional assemblies. The classic dipeptide hydrogelator is divided into three parts, as shown in Figure 1. The two same or different amino acids are linked via an amide bond to form the main chain of dipeptide hydrogelator, which can provide intermolecular hydrogen bonding in the self-assembling process. The other two parts are also important and are recognized as the side chain, which helps the gelator to self-assemble into associated 3D networks. As we know, hydrogel is one of the most typical amphiphilic materials in which solvent molecules are entrapped within the 3D networks under suitable conditions (Bahram et al., 2016). Unlike in covalently connected polymers (polypeptide or proteins), the structure of dipeptide hydrogelator is relatively simple and allows one to tune the formation easily and subtle changes can be applied to the structure that may lead to various hydrogel behaviors: gel or not gel.

FIGURE 1
www.frontiersin.org

FIGURE 1. The general structure of dipeptide hydrogelator.

The amino acids have different side chains for various hydrophilic and hydrophobic properties. There are the 20 different most common amino acids in nature and each of them has specific chemical characteristics, which have a unique role in protein structure and function. Based on the characteristics of the side chain when it is in contact with water, amino acids can be classified into three categories: hydrophobic (low propensity to be in contact with water), polar, and charged (energetically favorable contacts with water). Due to the simple synthesis of dipeptides, they have significant advantages in regulating physicochemical behavior by peptide sequence design (Bak et al., 2015). Even if there is only one amino acid difference, the self-assembled nanostructures and the resulting hydrogels can be significantly changed (Habibi et al., 2016; Zhou et al., 2019).

The side chains of the N-terminus and C-terminus generally provide an auxiliary function for a better equilibrium of solvability and self-assembly capacity, such as enhancing the hydrophobicity and the intermolecular forces. It has been proven that an efficient way to construct a supramolecular hydrogelator is to attach a π-conjugated group to a short peptide (Adams and Topham, 2010). For example, the Fmoc-Phe-Phe (Fmoc-FF) dipeptide, derived from the β-amyloid peptide, is mediated by a potent combination of hydrophobic, π–π, and hydrogen bonding interactions that result in the formation of hydrogel (Ryan and Nilsson, 2012; Rajbhandary and Nilsson, 2017).

The strategies for preparing the new generation of dipeptide hydrogels can be divided into four categories based on the modification site of dipeptide: 1) N-terminal modified dipeptide; 2) C-terminal modified dipeptide; 3) uncapped dipeptide; 4) cyclic dipeptide. This review will focus on the linear dipeptide (1–3) and other recent reviews about cyclic dipeptide can be found in articles by Yu et al. (2020) and Balachandra et al. (2021).

COOH-Terminal and N-Terminal Modified Dipeptide

To form an efficient dipeptide hydrogel, it is possible to modify a large aromatic group on the N-terminal of the dipeptide hydrogelator (Fichman and Gazit, 2014). Aromatic moieties can facilitate the self-assembly of peptides and stability of conformations and functions due to the favorite contribution of the aromatic group, such as π–π stacking and hydrophobic interactions. The aromatic group includes fluorenylmethoxycarbonyl (Fmoc), naphthalene (Nap) derivatives, phenothiazine (PTZ), carboxybenzyl (Cbz), azobenzene (Azo), and pyrene (Pyr). The literature has reported that unmodified dipeptides without aromatic capping do not form hydrogels, whereas several N-terminal modified peptides have been used as efficient hydrogelators; the detailed contents are discussed as follows.

Aromatic-Modified Dipeptide

The Fmoc group is widely used as a protecting group in peptide synthesis; thus, the Fmoc-modified dipeptide hydrogelator is readily studied. In 1995, the first Fmoc-modified dipeptide hydrogelator Fmoc-Leu-Asp was reported by the Vegners group, which forms hydrogel at 2 mg/ml in PBS and was used as a carrier for antigen presentation (Vegners et al., 1995). Following this study, several Fmoc-dipeptides as efficient hydrogelators have been reported, and mostly the Fmoc-dipeptides self-assembled into a fibrous structure in gel state (Tang et al., 2011; Sasselli et al., 2016).

Fmoc-Phe-Phe, an efficient hydrogelator under physiological conditions, has attracted particular interest in contrast to the other dipeptides. Since 2006, this hydrogelator has been well characterized and widely examined for various applications. Jayawarna and coworkers have discovered the gelation properties of seven Fmoc-dipeptides made up of the combinations of the four amino acids: glycine, alanine, leucine, and phenylalanine (Jayawarna et al., 2006). Fmoc-Phe-Phe formed a hydrogel under a pH less than 8, the other five dipeptides Fmoc–Gly–Gly, Fmoc–Ala–Gly, Fmoc–Ala–Ala, Fmoc–Leu–Gly, and Fmoc–Phe–Gly could form hydrogels under the condition of pH < 4, whereas Fmoc–Gly–Phe gave crystals and did not form a gel under any of the conditions tested. Thus, the nature and architecture of the amino acid building blocks could dictate the properties of the hydrogels.

Smith and coworkers have confirmed that the Fmoc-Phe-Phe self-assembled into nanocylindrical fibrils based on π-π interlocked antiparallel β-sheets (Smith et al., 2008). Moreover, they reported that the self-assembly process could result in two apparent pKa values: the first located at pH 9.5–10.2 corresponding to the self-assembly of the dipeptide into paired fibrils consisting of antiparallel β-sheets and the second located at pH 6.2–9.5 related to forming large rigid ribbons by lateral aggregation of fibrils (Tang et al., 2009).

Adams and coworkers designed a series of orthogonal experiments to study the mechanical properties of Fmoc-Phe-Phe hydrogel prepared using different conditions (Raeburn et al., 2012). They have demonstrated that the final pH of the gels, no matter the gel formation method, is the principal determinant for mechanical properties. Moreover, they revealed that the other experimental factors, such as the ratio of organic solvent to water and the nature of the buffers, affect the rheological properties to a lesser extent. Tirelli et al. have also shown that the different homogenization techniques, such as vortex vs. manual or orbital agitation, could dramatically influence the mechanical properties and the self-assembling structures (Helen et al., 2011). All these interesting studies have suggested that the self-assembly process and its inherent mechanism of Fmoc-modified peptides are significantly complicated, and the influencing factors, such as the molecular structures, solvent compositions (including solvent type, polarity, the ratio of organic solvent to water, and the buffer components), solution conditions (pH, ionic strength, ionic type, and valence state, etc.), and external conditions (temperature, homogenization method, photo stimulus, etc.) should be thoroughly clarified.

Another extensively studied Fmoc-based dipeptide is Fmoc-Tyr-Leu (Bai et al., 2014; Fleming et al., 2014). Due to the phenolic hydroxyl of tyrosine, anions can affect the hydrogelation of Fmoc-Tyr-Leu, leading to the transformation from fibrous structures to spherical aggregation. Ultrasonication can also control the self-assembly process of Fmoc-Tyr-Leu by transforming the coiled nanofibers to form spherical aggregates, which means the stacking interactions of the fluorenyl rings are enhanced. Bai group has recently reported two oppositely charged dipeptide Fmoc-Tyr-Asp and Fmoc-Tyr-Lys, which could self-assemble into β-sheet amyloid structures and form tunable hydrogel (Jian et al., 2019). The mechanical and biodegradation properties of the hydrogels could be adjusted by changing the concentration and composition of the dipeptide. They have also demonstrated that the formed hydrogels could form, grow, and naturally release HepaRG spheroids with sizes up to 1 mm, which might be suitable to use as bioinks.

Over the years, as more and more Fmoc-modified dipeptide hydrogelators were reported, such as Fmoc-Phe-Tyr (Wang et al., 2008; Sadownik et al., 2011; Hughes et al., 2013), Fmoc-Phe-Leu (Ren et al., 2020), Fmoc-Phe-Cys (Wang and Chau, 2012), Fmoc-Phe-Val (Najafi et al., 2021), Fmoc-Tyr-Ala (Bai et al., 2014; Ren et al., 2020), Fmoc-Tyr-Ser (Hughes et al., 2012, 2013; Bai et al., 2014), Fmoc-Tyr-Thr (Hughes et al., 2012, 2013), Fmoc-Tyr-Asn (Hughes et al., 2013), and Fmoc-Gly-Ser, which also self-assembled into fibrillar structures like Fmoc-Phe-Phe, the results indicated that the π–π and hydrophobic interactions of intermolecular Fmoc groups are the main driving forces in the self-assembly process of these systems. Moreover, double Fmoc group-containing dipeptide, Fmoc-Lys (Fmoc)-Asp, as an hydrogelator with the lowest CGC ever reported, 0.002 wt% (28.3 × 10–6 M), was reported by Gazit and Wei et al. (Chakraborty et al., 2020). The conductive composite gels formed from Fmoc-Lys (Fmoc)-Asp and polyaniline (PAni) were cytocompatible and exhibited excellent DNA binding properties, suggesting its potential application in DNA biochip fabrication (Figure 2). However, the other analogies of the double Fmoc group-containing dipeptides, Fmoc-Lys (Fmoc)-Ala, Fmoc-Lys (Fmoc)-Cys, Fmoc-Lys (Fmoc)-Asn, and Fmoc-Lys (Fmoc)-His formed hydrogels, but with lower mechanical strength and considerably higher CGC value (>0.05 wt%) compared to Fmoc-Lys (Fmoc)-Asp.

FIGURE 2
www.frontiersin.org

FIGURE 2. (A) The structure of Fmoc-Lys (Fmoc)-Asp; (B, C) TEM and HRSEM images of Fmoc-Lys (Fmoc)-Asp hydrogels; (D) illustration of the probable structure of the peptide–polyaniline (PAni) formed fibers; (E) DNA binding by the composite peptide–PAni hydrogel (Chakraborty et al., 2020).

It is worth mentioning that not all the Fmoc-modified dipeptides form hydrogels in specific conditions, and most of those dipeptides generally form hydrogels at low pH, which limited the applications in biomedical eras (Fichman and Gazit, 2014; Hendi et al., 2020; Zhang and Huang, 2021). Inspired by the success of Fmoc-modified dipeptide hydrogelators, various aromatic moieties, such as phenyl, naphthalene (Nap), azobenzene, and pyrene derivatives, have been utilized to augment the hydrogelation or to introduce functionality at the N-terminus of dipeptide (Fleming and Ulijn, 2014). Among the N-terminal aromatic-modified dipeptide hydrogelators, Nap-based dipeptides have been the most widely studied. Nap-modified dipeptides can usually form hydrogels, just like Fmoc-modified dipeptides, by adjusting the solution pH. Adams and coworkers have demonstrated that the gradual removal of the charge allows lateral assembly of the molecules to form fibrous structures by π–π stacking and β-sheet formation (Chen et al., 2010a). They have also found out that the nitrile or bromo groups substituted Nap-modified dipeptide have shown better hydrogelation properties than non-substituted ones, suggesting that the electron-withdrawing nature of the bromo and nitro groups, which reduced the electron density of the π-system, has an impact on the self-assembly properties of the dipeptides via aromatic stacking interactions. Moreover, Nap-Gly-Ala and Nap-Ala-Gly self-assemble to different results as the pH of solution dropped: Nap-Gly-Ala is induced to hydrogel, but Nap-Ala-Gly is induced to crystallization (Chen et al., 2010a; Adams et al., 2010).

A Nap-based dipeptide 2Nap-Phe-Phe can pack into hollow tubes in the micellar state at high pH (McAulay et al., 2019), and when the pH decrease, gels are formed because the hollow core is lost, and lateral association leads to elliptical structures that entangle to form the gels (Draper et al., 2020). Furthermore, the micellar aggregates formed at high pH for dipeptide-based gelators can be varied by simply using different salts to raise the pH (McAulay et al., 2020). The change in cations leads to different packing in the micellar phase and the formation of different structures, thus affecting the properties of the resulting gels.

Besides Fmoc and Nap groups, several other aromatic groups have also been researched in N-terminal dipeptide modifications. Gazit and coworkers have shown that N-terminal carboxybenzyl (Cbz)-modified dipeptide Phe-Phe could form hydrogels with different structures (such as nanowires, fibers, nanospheres, and nanotoroids) by changing the starting solvent (Brown et al., 2018). A library of Cbz-modified dehydrodipeptides Cbz-L-Xaa-Z-ΔPhe-OH (Xaa = Met, Phe, Tyr, Ala, Gly) were synthesized for hydrogel screening by Ferreira et al. (Veloso et al., 2021). The Cbz-L-Met-Z-ΔPhe-OH and Cbz-L-Phe-Z-ΔPhe-OH could form self-assembly hydrogels and could be used as drug carriers for the delivery of curcumin and doxorubicin.

In recent years, naphthalimide (NI) derivatives have received increasing attention because of their unique photophysical property and photostability (Schab-Balcerzak et al., 2015). Lin group have reported four 1,8-naphthalimide (NI)-modified dipeptide hydrogelators and found out that NI-Phe-Tyr, NI-Tyr-Phe, and NI-Tyr-Tyr could form hydrogels under physiological pH conditions (Hsu et al., 2018). Furthermore, the NI-Tyr-Phe showed low cytotoxicity and could be applied as a suitable carrier for drug delivery. They have also developed NI-modified phosphate-based dipeptide NI-FYp (Chakravarthy et al., 2020) (Figure 3), which formed spherical nanoparticles in the aqueous condition firstly, and then in the condition of enzymatic catalysis, they slowly transformed into partially unzipped nanotubular structures and subsequently resulted in hydrogelation.

FIGURE 3
www.frontiersin.org

FIGURE 3. (A) The illustration of self-assembly NI-FYp dipeptide nanostructures which transformed from spherical nanoparticles into a hydrogel during the enzymatic catalytic process; (B) TEM image of NI-FYp nanoparticles in Tris-buffer (10 mM); (C) particle size distribution histogram of NI-FYp (10 mM) nanoparticles by TEM and DLS measurements; (D) TEM images of NI-FYp treated with 10 U of ALP (Chakravarthy et al., 2020).

2-Thiophene-modified diphenylalanine was reported by Draper et al. that it could form transparent hydrogel from the initially turbid gel after 3 days due to the effect of carbon dioxide, which implied that the molecular rearrangement of the gelator molecules and the self-assembly structures were becoming smaller or thinner (Draper et al., 2015).

An anthracene ring is an interesting group in the dipeptide hydrogelators researches. When the anthracene was directly linked to the N-terminal of dipeptide by amide and no other group between amide and anthracene, no formed hydrogels were discovered, while a similar structure, but with an additional OCH2 spacer between the anthracene ring and first amide bond, was an effective hydrogelator (Chen et al., 2010b; Awhida et al., 2015) (Figure 4). However, pyrene and Nap-modified dipeptide, whether those conjugated directly or with a longer spacer, were all reported to be effective hydrogelators.

FIGURE 4
www.frontiersin.org

FIGURE 4. The linker between the anthracene ring and dipeptide can affect gel formation.

Due to the redox activity of ferrocene (Fc), the Fc-modified peptides have attracted great interest in biomedicine and sensing. Qi et al. have reported that the Fc-Phe-Phe could form a self-supporting hydrogel under kinetic control by introducing a mechanical force, which showed a morphological transition from metastable nanospheres to nanofibers. The strong hydrophobic interaction of the Fc moiety was suggested to have a key role in this kinetically controlled self-assembly process. Moreover, Wang and coworkers have reported that the same Fc-modified dipeptide Fc-Phe-Phe could self-assemble into an ultra-pH-sensitive chiral hydrogel, which formed at a very narrow pH range of 5.7–5.9 (Zhang et al., 2020). The pure Fc-L-Phe-L-Phe or Fc-D-Phe-D-Phe peptide could form self-assemble into right- or left-handed nanohelices in a mixture of water and organic solvent, which indicated that molecular chirality had a great influence on the gelation of the peptides and water molecules are essential in directing the chiral self-assembly of Fc-Phe-Phe into entangled chiral nanostructures, leading to the formation of stimuli-responsive chiral hydrogels (Figure 5).

FIGURE 5
www.frontiersin.org

FIGURE 5. The molecular structure of the Fc-L-Phe-L-Phe-OH and Fc-L-Phe-L-Phe-OH; the illustration of the pH responsiveness of the hydrogel (Zhang et al., 2020).

Tetraphenylethylene (TPE), a supramolecular fluorescent material (SFM) with aggregation-induced emission characteristics, has also been reported with dipeptides as hydrogelators. Lin and his coworkers have found out that the TPE-modified dipeptide TPE-Gly-Gly could be a hydrogelator under basic media (pH = 10.5) and failed to form hydrogels at neutral pH conditions, which are considered as the main drawback for biomaterials (Yeh et al., 2016). Their subsequent studies about TPE-modified dipeptides have indicated that TPE-Phe-Phe was too hydrophobic, insoluble in any aqueous conditions, and thus difficult to form a hydrogel, while TPE-Tyr-Tyr (Figure 6A) was able to form hydrogel under a broad pH range from 3.7 to 10.2 (Talloj et al., 2020). The hydrogel formed by TPE-Tyr-Tyr showed tunable morphology via pH: as the pH of the hydrogel decreases, the nanostructure transformed from nanofiber to flat nanobelts and then to twisted nanobelts. Furthermore, the TPE-Tyr-Tyr displayed selective cell adhesion response for 3A6 cells (Human MSCs), which have potential applications in tissue engineering such as stem cell-based therapies.

FIGURE 6
www.frontiersin.org

FIGURE 6. The structure of (A) TPE-Tyr-Tyr reported by Lin group (Yeh et al., 2016); (B) TPE-Phe-Phe (TPE-FF) reported by Adams (Castilla et al., 2018); (C) from left to right, a solution of TPE-FF at 5 mg/ml at high pH, at 10 mg/ml after a heat-cool cycle (formed hydrogel), at 5 mg/ml after the addition of glucono-dlactone (GdL), at 5 mg/ml after the addition of CaCl2, and at 5 mg/ml after the addition of NaCl (18 mg/ml) (formed hydrogel) (Castilla et al., 2018).

Adams et al. have described other TPE-base dipeptides, while the TPE was linked to dipeptide via 2-[4-(1,2,2-triphenylethenyl)phenoxy]acetic acid (Figure 6B) (Castilla et al., 2018). Their hydrogel formed by TPE-Phe-Phe showed syneresis properties, and further studies have indicated that the molecular packing in the calcium chloride and sodium chloride-triggered gels is different (Figure 6C). Under high pH conditions, the TPE-Phe-Phe solution initially could form a gel after adding calcium chloride solution but dehydrated again over time, which suggested that the samples were not self-supporting. On the contrary, the addition of sodium chloride could lead to the formation of a hydrogel. This suggested that the linker between the TPE and peptide component is also important to the properties of the hydrogels. The linker of TPE in Adams’ research has more flexibility than that in Lin’s researches (Yeh et al., 2016), which means that Adams’s TPE is not highly restricted in molecular packing and the corresponding hydrogels may have different properties.

Non-Aromatic-Modified Dipeptide

Although N-terminal aromatic-modified dipeptides have shown interesting gelation properties in relation to stabilities and mechanicals, it should be noted that the literature has reported the toxicity of those groups, which may limit the biomedical applications of those gels. For example, degradation products of Fmoc-Phe-Phe showed some cytotoxicity because the highly reactive dibenzofulvalene was formed upon cleavage of the Fmoc group (Truong et al., 2015; D.; Martin and Thordarson, 2020). Naproxen-capped dipeptide Nap-Phe-Phe only showed biocompatibility at low concentrations and the IC50 value is lower than the minimum gel concentration, which suggested that the molecule was not suitable for biomedical applications (Li et al., 2013).

Haldar et al. have reported a N-(tert-butoxycarbonyl) (N-Boc)-modified dipeptide Boc-Phe-Aib (Nandi et al., 2018), which transformed into a robust hydrogel upon addition with three equivalents of sodium hydroxide and water (Figure 7). The other similar analogs of dipeptides, such as Boc-Tyr-Aib, Boc-Trp-Aib, Boc-Phe-Ala (Sangeetha and Maitra, 2005), Boc-Phe-Gly (O’Leary et al., 2011), and Boc-Aib-Phe, have all failed to form such a hydrogel under the same condition. Haldar and the coworkers have found out that the N-Boc-protected dipeptide Boc-Phe-Val could form a hydrogel in the mixtures of NH4OH and NaCl; Na2CO3 and LiOH; and NaCl and KOH (Podder et al., 2019). This result suggested that sodium and hydroxide ions both played a key role in hydrogel formation.

FIGURE 7
www.frontiersin.org

FIGURE 7. The structures of dipeptide Boc-Phe-Aib analogs and their gelation studies (Nandi et al., 2018).

Recently, self-assembly hydrocarbonyl chain-modified dipeptides (Cn-dipeptides) with lower toxicity and greater biocompatibility than those modified with Boc, Nap, and/or Fmoc have attracted more and more attention. The Adams group has studied the hydrogelation properties of various carbon chain lengths for modified dipeptide Cn-Phe-Phe and found out that C12-CO-(C13-) was the optimal group for dipeptide hydrogelators (Chen et al., 2013). In order to understand the effects of the introduction of C13- into the dipeptides, the combined computational and experimental methods were used to investigate the self-assemblies and gelations of C13-dipeptides (Hu T. et al., 2020). They have tried to introduce a modified parameter-aggregation propensity (APS), which accounted for side chain effects, to help design peptide-based gelators (Figure 8). From those experimental results, the APS values successfully demonstrated the tendency of self-assembly of the C13-dipeptides even though the models were based on a neutral environment. However, the drawback of the selected C13-dipeptides is that the hydrogels are usually formed at low pH (∼4.0), which would limit the applications of those hydrogels. Banerjee and coworkers (Baral et al., 2015) have also reported that a C12-modified dipeptide (C12-Ala-Ala) could form a hydrogel in phosphate buffer in the pH range of 7.0–8.5, whereas the natural dipeptide (Ala-Ala) could not form a gel.

FIGURE 8
www.frontiersin.org

FIGURE 8. (A) APs scoring distribution of all 400 C13-dipeptides after 50ns CG-MD simulations. (B) Average distribution to APs of specific amino acids in the N-terminus (blue) and C-terminal position (red) (Hu T. et al., 2020).

C-Terminal Modified Dipeptides

The C-terminal carboxylic acid moieties of dipeptides could usually be modified to perturb the hydrophobicity and hydrogen bond capacity of the C-termius, which showed significant effects on the self-assembling propensity, such as the hydrogelation ability and morphology of the self-assembled nanostructures.

Tuttle and Ulijn et al. have provided a combined experimental/computational method to evaluate the hydrogelation properties of various C-terminus modifications (amide vs. ester) of Fmoc-dipeptide (Sasselli et al., 2016). The approach proved that amide modification was more important than ester modification because the Fmoc-Thr-Phe-NH2 could form more stable hydrogels than Fmoc-Thr-Phe-OMe, possibly due to the extra hydrogen bonds that the amide group forms upon self-assembly. Ikeda et al. have reported C-terminal hydrazide-modified dipeptide, Cbz-Phe-Phe-NHNH2, which showed limited aqueous solubility and could not form a hydrogel, but its carbohydrate derivatives could form a hydrogel (Tsuzuki et al., 2017) (Figure 9). They have found out that the disaccharide structures (epimer or glycosidic-bond geometry) have a significant effect on the formation ability of the hydrogel and the morphology of the self-assembled structures. The hydrazide group C-terminal modified p-nitro-phenylmethoxycarbonyl (NPmoc)-based dipeptide NPmoc-Phe-Ala-NHNH2 could form a hydrogel, while the others like NPmoc-Ala-Phe-NHNH2, NPmoc-Phe-Phe-NHNH2, and NPmoc-Ala-Ala-NHNH2 failed to form hydrogel at the same conditions (Ohtomi et al., 2020). Their results also indicated that adjusting the side chain phenyl group position in the dipeptide hydrazides could vary the dimensions of the self-assembled nanostructures from 1D (fiber and tubular) to 2D (sheet).

FIGURE 9
www.frontiersin.org

FIGURE 9. The structures of C-terminal modified dipeptides by Ikeda et al.

Coutsolelos et al. have synthesized several aliphatic dipeptides bearing various protecting groups and found out that Fmoc-Ile-Ile-TPP (TPP: tetraphenyl porphyrin) formed a hydrogel in HFIP–water (2:8) solvent mixture, whereas TPP-Ile-Ile-OMe and Boc-Ile-Ile-TPP failed to form hydrogel due to the spherical assemblies in solvents (Figure 10) (Nikoloudakis et al., 2019).

FIGURE 10
www.frontiersin.org

FIGURE 10. (A) The structure of Fmoc-Ile-Ile-TPP; (B) photographs of the hydrogel formed from the Fmoc-Ile-Ile-TPP in HFIP/H2O (2/8, v/v, 1 mM); (C) FESEM image of the formed hydrogel (Nikoloudakis et al., 2019).

Uncapped Dipeptide

Although uncapped dipeptides are very attractive building blocks due to their chemical simplicity, they usually fail to form a stable hydrogel, e.g., the Phe-Phe hydrogels were reported to be metastable (Conte et al., 2016; Kurbasic et al., 2019; Kralj et al., 2020), unless the Phe benzene ring of the dipeptide was further modified by adding a p-nitro (Kurbasic et al., 2019) or p-iondin (Kralj et al., 2020) substitution. For the uncapped dipeptide composed of natural amino acids, Ventura and coworkers have reported that Ile-Phe dipeptide can form a stable hydrogel at pH 5.8 (de Groot et al., 2007); later, Marchesan et al. found out that Leu-Phe dipeptide could form a stable hydrogel in phosphate buffer (Bellotto et al., 2020). However, besides these two dipeptides, no other dipeptide hydrogelator composed of natural amino acids has been reported to form a stable hydrogel.

α,β-Dehydrophenylalanine (ΔPhe), an unsaturated analog of Phe, was found to induce conformational constraints in the peptide backbone and to usually yield a hydrogel. Chauhan et al. have reported that uncapped dipeptide Phe-ΔPhe could self-assemble into a stable hydrogel at minimal gelation concentrations of 0.2 wt% in a buffer solution at pH 7.0 (Panda et al., 2008). Yadav and Thota have reported another ΔPhe-containing dipeptide, Leu-ΔPhe, which could form a highly stable and mechanically strong hydrogel under mild physiological aqueous conditions (Thota et al., 2016). These hydrogels from ΔPhe-containing dipeptide were found to be nontoxic and were used to entrap several hydrophobic and hydrophilic drug molecules and release them in a controlled manner (Figure 11).

FIGURE 11
www.frontiersin.org

FIGURE 11. LeuΔPhe can be self-assembled into a stable hydrogel at room temperature and applied in the biomedical field (Thota et al., 2016).

The chirality of the composed amino acids affects the hydrogelation ability of the uncapped dipeptide. Marchesan et al. chose diphenylalanine as a model compound and studied the self-organization of heterochiral D-Phe-L-Phe and its halogenated derivatives (Figure 12, Kralj et al., 2020). Their studies showed that D-Phe-L-Phe self-assembled into nanofibrils and resulted in a transparent hydrogel. Besides, they also found that halogenation had significant effects on the self-assembling process. For example, fluorination induced the analogous packing to nanotube formation, and iodination was the most effective strategy to augment the stability of the hydrogel.

FIGURE 12
www.frontiersin.org

FIGURE 12. (A) and (B) Single-crystal XRD structure of D-(4-I)-Phe-L-Phe (CCDC 016374). The light blue represents the hydrophilic layers and iodine atoms (purple sphere) allowed Phe side chains in hydrophobic layers (yellow); (C) single-crystal XRD structure (CCDC 2016373) of D-(4-F)-Phe-L-Phe, which can pack to an intermediate level of bundling to generate 27 nm wide fibrils as observed by TEM (Kralj et al., 2020).

Multicomponent Self-Assembly

Multicomponent self-assembly is a hot topic at present, which generally has advantages over a single component system (Li et al., 2021a). Multicomponent self-assembly of two or more different building blocks into one ordered nanostructure can promote the formation of a wider and more complex architecture, provide the tunable mechanical properties, enhance stability, and provide spatiotemporal control of self-assembly (Raeburn and Adams, 2015; Halperin-Sternfeld et al., 2017; Makam and Gazit, 2018). Recently, multicomponent hydrogels containing dipeptides have also attracted interest due to the innovative scaffolds from multicomponent self-assembly. Some studies have reported that the multicomponent self-assembly containing dipeptides has significant effects on the mechanical properties of those formed hydrogels. For example, Tendler and coworkers have reported that the mechanical properties of hydrogels formed by two peptides Phe-Phe and di-D-2-napthylalanine could be fine-tuned via changing their relative concentration (Sedman et al., 2013). Abramovich et al. have analyzed the gelation kinetics of mixed Fmoc-Phe-Phe/pentafluorinated Fmoc-Phe (Figure 13A) and discovered that the mechanical properties were improved (Halperin-Sternfeld et al., 2017). In the same way, the mix of Fmoc-Phe-Phe and Fmoc-Arg can form new hydrogels, which demonstrated high mechanical strength with a storage modulus of up to 29 kPa in combination with the bone mineral hydroxyapatite (Ghosh et al., 2017).

FIGURE 13
www.frontiersin.org

FIGURE 13. (A) The structure of pentafluorinated Fmoc-Phe used by Halperin-Sternfeld et al. (Halperin-Sternfeld et al., 2017); (B) The structure of PEGylated (Phe-Tyf)3 hexapeptide.

Fmoc-Phe-Phe and hexapeptide-based multicomponent hydrogels were studied by the Accardo group, and they found out that the combination of Fmoc-Phe-Phe with (Phe-Tyf)3 hexapeptide or its PEGylated analog (Figure 13B) at different volumetric ratios (2/1 or 1/1 v/v) could provide hydrogels with tunable mechanical properties (Diaferia et al., 2019a). For instance, the PEGylated gel showed a decrease of the gel rigidity and slowing down of the gel formation kinetics compared to the un-PEGylated gel, and thus the mixed hydrogel Fmoc-Phe-Phe/PEG8-(Phe-Tyf)3 (1/1) have minor rigidity compared to Fmoc-Phe-Phe/PEG8-(Phe-Tyf)3 (2/1).

Ulijn and coworkers examined four different combinations of Fmoc- and pyrene (Py)-modified compounds (Fleming et al., 2014). The results showed that the combinations of two structurally different peptides (Py-Tyr-Leu/Fmoc-Ser and Fmoc-Tyr-Leu/Py-Ser) resulted in orthogonal coassembly, while the structurally similar peptides (Py-Tyr-Leu/Fmoc-Tyr-Leu and Py-Ser/Fmoc-Ser) followed the cooperative coassembly process (Figures 14A,B,D). They discovered that Pyr-Ser could perturb the intermolecular H-bonding and fiber formation associated with Fmoc-Tyr-Leu and Py-Tyr-Leu (Figures 14C,E), while Fmoc-Ser showed a disruptive effect on the self-assembly structure of Fmoc-Tyr-Leu (Figure 14E).

FIGURE 14
www.frontiersin.org

FIGURE 14. AFM of (A) the gelators Pyr-YL and Fmoc-YL; (B) the surfactants Fmoc-S and Pyr-S; (C) orthogonal Pyr-YL/Fmoc-S and Fmoc-YL/Pyr-S; (D) cooperative Pyr-YL/Fmoc-YL and Pyr-S/Fmoc-S; (E) disruptive Pyr-YL/Pyr-S and Fmoc-YL/Fmoc-S (Fleming et al., 2014).

Yan et al. utilized the combination of dipeptide Fmoc-Phe-Phe and fullerene to improve the mechanical properties of the hydrogel for a better injectable formulation for biomedical applications (Zhang et al., 2018). Due to the coassembly of dipeptide and fullerene, the aggregation of fullerene in the hydrogel was largely inhibited via the noncovalent interactions between the dipeptide and the fullerene, and at the same time, fullerene enhanced the mechanical properties of the dipeptide hydrogel. The incorporation of the fullerene profoundly improved the photodynamic therapy (PDT) efficiency compared to the untreated fullerene, and the dipeptide-fullerene hydrogels could effectively inhibit multiantibiotic-resistant Staphylococcus aureus both in vitro and in vivo.

Conclusion

Self-assembly dipeptide hydrogel is the result of coordinated noncovalent interactions among molecular, environmental, and kinetic considerations. Although some successful dipeptide hydrogels have been reported, it is still difficult to predict and control the results of molecular assembly, which are derived by various factors that are external (solvent, temperature, light, etc.) and internal (molecular geometry, hydrophobicity, electronics, etc.). Nonetheless, through the subtle design of dipeptide molecules and the modification of the N- and C-terminus, dipeptide hydrogels can have great potential applications in preparing minimal biocompatible materials.

Author Contributions

LL was responsible for data curation and writing of the original draft. LX and RZ edited the manuscript and conducted data curation. RS reviewed the manuscript.

Conflict of Interest

The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.

Publisher’s Note

All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors, and the reviewers. Any product that may be evaluated in this article, or claim that may be made by its manufacturer, is not guaranteed or endorsed by the publisher.

References

Adams, D. J., Morris, K., Chen, L., Serpell, L. C., Bacsa, J., and Day, G. M. (2010). The Delicate Balance between Gelation and Crystallisation: Structural and Computational Investigations. Soft Matter 6, 4144–4156. doi:10.1039/C0SM00409J

CrossRef Full Text | Google Scholar

Adams, D. J., and Topham, P. D. (2010). Peptide Conjugate Hydrogelators. Soft Matter 6, 3707–3721. doi:10.1039/C000813C

CrossRef Full Text | Google Scholar

Ahmed, E. M. (2015). Hydrogel: Preparation, Characterization, and Applications: A Review. J. Adv. Res. 6, 105–121. doi:10.1016/j.jare.2013.07.006

PubMed Abstract | CrossRef Full Text | Google Scholar

Awhida, S., Draper, E. R., McDonald, T. O., and Adams, D. J. (2015). Probing Gelation Ability for a Library of Dipeptide Gelators. J. Colloid Interf. Sci. 455, 24–31. doi:10.1016/j.jcis.2015.05.032

CrossRef Full Text | Google Scholar

Bahram, M., Mohseni, N., and Moghtader, M. (2016). “An Introduction to Hydrogels and Some Recent Applications,” in Emerging Concepts in Analysis and Applications of Hydrogels. Editor S. B. Majee (London: InTech). doi:10.5772/64301

CrossRef Full Text | Google Scholar

Bai, S., Pappas, C., Debnath, S., Frederix, P. W. J. M., Leckie, J., Fleming, S., et al. (2014). Stable Emulsions Formed by Self-Assembly of Interfacial Networks of Dipeptide Derivatives. ACS Nano 8, 7005–7013. doi:10.1021/nn501909j

PubMed Abstract | CrossRef Full Text | Google Scholar

Bak, A., Leung, D., Barrett, S. E., Forster, S., Minnihan, E. C., Leithead, A. W., et al. (2015). Physicochemical and Formulation Developability Assessment for Therapeutic Peptide Delivery-A Primer. AAPS J. 17, 144–155. doi:10.1208/s12248-014-9688-2

PubMed Abstract | CrossRef Full Text | Google Scholar

Balachandra, C., Padhi, D., and Govindaraju, T. (2021). Cyclic Dipeptide: A Privileged Molecular Scaffold to Derive Structural Diversity and Functional Utility. ChemMedChem. doi:10.1002/cmdc.202100149

CrossRef Full Text | Google Scholar

Baral, A., Basak, S., Basu, K., Dehsorkhi, A., Hamley, I. W., and Banerjee, A. (2015). Time-dependent Gel to Gel Transformation of a Peptide Based Supramolecular Gelator. Soft Matter 11, 4944–4951. doi:10.1039/c5sm00808e

PubMed Abstract | CrossRef Full Text | Google Scholar

Basu, A., Kunduru, K. R., Doppalapudi, S., Domb, A. J., and Khan, W. (2016). Poly(lactic Acid) Based Hydrogels. Adv. Drug Deliv. Rev. 107, 192–205. doi:10.1016/j.addr.2016.07.004

PubMed Abstract | CrossRef Full Text | Google Scholar

Bellotto, O., Kralj, S., De Zorzi, R., Geremia, S., and Marchesan, S. (2020). Supramolecular Hydrogels from Unprotected Dipeptides: a Comparative Study on Stereoisomers and Structural Isomers. Soft Matter 16, 10151–10157. doi:10.1039/d0sm01191f

PubMed Abstract | CrossRef Full Text | Google Scholar

Brown, N., Lei, J., Zhan, C., Shimon, L. J. W., Adler-Abramovich, L., Wei, G., et al. (2018). Structural Polymorphism in a Self-Assembled Tri-aromatic Peptide System. ACS Nano 12, 3253–3262. doi:10.1021/acsnano.7b07723

PubMed Abstract | CrossRef Full Text | Google Scholar

Castilla, A., Dietrich, B., and Adams, D. (2018). Using Aggregation-Induced Emission to Understand Dipeptide Gels. Gels 4, 17. doi:10.3390/gels4010017

PubMed Abstract | CrossRef Full Text | Google Scholar

Chakraborty, P., Tang, Y., Yamamoto, T., Yao, Y., and Guterman, T. (2020). Unusual Two‐Step Assembly of a Minimalistic Dipeptide‐Based Functional Hypergelator. Adv. Mater. 32, 1906043. doi:10.1002/adma.201906043

PubMed Abstract | CrossRef Full Text | Google Scholar

Chakravarthy, R. D., Mohammed, M., and Lin, H. C. (2020). Enzyme Instructed Self‐assembly of Naphthalimide‐dipeptide: Spontaneous Transformation from Nanosphere to Nanotubular Structures that Induces Hydrogelation. Chem. Asian J. 15, 2696–2705. doi:10.1002/asia.202000575

PubMed Abstract | CrossRef Full Text | Google Scholar

Chen, J., Nichols, B. L. B., Norris, A. M., Frazier, C. E., and Edgar, K. J. (2020). All-Polysaccharide, Self-Healing Injectable Hydrogels Based on Chitosan and Oxidized Hydroxypropyl Polysaccharides. Biomacromolecules 21, 4261–4272. doi:10.1021/acs.biomac.0c01046

PubMed Abstract | CrossRef Full Text | Google Scholar

Chen, L., McDonald, T. O., and Adams, D. J. (2013). Salt-induced Hydrogels from Functionalised-Dipeptides. RSC Adv. 3, 8714–8720. doi:10.1039/c3ra40938d

CrossRef Full Text | Google Scholar

Chen, L., Morris, K., Laybourn, A., Elias, D., Hicks, M. R., Rodger, A., et al. (2010a). Self-Assembly Mechanism for a Naphthalene−Dipeptide Leading to Hydrogelation. Langmuir 26, 5232–5242. doi:10.1021/la903694a

CrossRef Full Text | Google Scholar

Chen, L., Revel, S., Morris, K., and Adams, D. J. (2010b). Energy Transfer in Self-Assembled Dipeptide Hydrogels. Chem. Commun. 46, 4267–4269. doi:10.1039/C003052J

PubMed Abstract | CrossRef Full Text | Google Scholar

Conte, M. P., Singh, N., Sasselli, I. R., Escuder, B., and Ulijn, R. V. (2016). Metastable Hydrogels from Aromatic Dipeptides. Chem. Commun. 52, 13889–13892. doi:10.1039/C6CC05821C

PubMed Abstract | CrossRef Full Text | Google Scholar

Dai, L., Cheng, T., Wang, Y., Lu, H., Nie, S., He, H., et al. (2019). Injectable All-Polysaccharide Self-Assembling Hydrogel: a Promising Scaffold for Localized Therapeutic Proteins. Cellulose 26, 6891–6901. doi:10.1007/s10570-019-02579-7

CrossRef Full Text | Google Scholar

de Groot, N. S., Parella, T., Aviles, F. X., Vendrell, J., and Ventura, S. (2007). Ile-Phe Dipeptide Self-Assembly: Clues to Amyloid Formation. Biophysical J. 92, 1732–1741. doi:10.1529/biophysj.106.096677

CrossRef Full Text | Google Scholar

Diaferia, C., Ghosh, M., Sibillano, T., Gallo, E., Stornaiuolo, M., Giannini, C., et al. (2019a). Fmoc-FF and Hexapeptide-Based Multicomponent Hydrogels as Scaffold Materials. Soft Matter 15, 487–496. doi:10.1039/C8SM02366B

PubMed Abstract | CrossRef Full Text | Google Scholar

Diaferia, C., Morelli, G., and Accardo, A. (2019b). Fmoc-diphenylalanine as a Suitable Building Block for the Preparation of Hybrid Materials and Their Potential Applications. J. Mater. Chem. B 7, 5142–5155. doi:10.1039/C9TB01043B

PubMed Abstract | CrossRef Full Text | Google Scholar

Draper, E. R., Dietrich, B., McAulay, K., Brasnett, C., Abdizadeh, H., Patmanidis, I., et al. (2020). Using Small-Angle Scattering and Contrast Matching to Understand Molecular Packing in Low Molecular Weight Gels. Matter 2, 764–778. doi:10.1016/j.matt.2019.12.028

CrossRef Full Text | Google Scholar

Draper, E. R., McDonald, T. O., and Adams, D. J. (2015). A Low Molecular Weight Hydrogel with Unusual Gel Aging. Chem. Commun. 51, 6595–6597. doi:10.1039/c5cc01334h

PubMed Abstract | CrossRef Full Text | Google Scholar

Du, X., Zhou, J., Shi, J., and Xu, B. (2015). Supramolecular Hydrogelators and Hydrogels: From Soft Matter to Molecular Biomaterials. Chem. Rev. 115, 13165–13307. doi:10.1021/acs.chemrev.5b00299

PubMed Abstract | CrossRef Full Text | Google Scholar

Fawver, J., Ghiwot, Y., Koola, C., Carrera, W., Rodriguez-Rivera, J., Hernandez, C., et al. (2014). Islet Amyloid Polypeptide (IAPP): A Second Amyloid in Alzheimer's Disease. Car 11, 928–940. doi:10.2174/1567205011666141107124538

CrossRef Full Text | Google Scholar

Fichman, G., and Gazit, E. (2014). Self-assembly of Short Peptides to Form Hydrogels: Design of Building Blocks, Physical Properties and Technological Applications. Acta Biomater. 10, 1671–1682. doi:10.1016/j.actbio.2013.08.013

PubMed Abstract | CrossRef Full Text | Google Scholar

Fisher, S. A., Baker, A. E. G., and Shoichet, M. S. (2017). Designing Peptide and Protein Modified Hydrogels: Selecting the Optimal Conjugation Strategy. J. Am. Chem. Soc. 139, 7416–7427. doi:10.1021/jacs.7b00513

PubMed Abstract | CrossRef Full Text | Google Scholar

Fleming, S., Debnath, S., Frederix, P. W. J. M., Hunt, N. T., and Ulijn, R. V. (2014). Insights into the Coassembly of Hydrogelators and Surfactants Based on Aromatic Peptide Amphiphiles. Biomacromolecules 15, 1171–1184. doi:10.1021/bm401720z

PubMed Abstract | CrossRef Full Text | Google Scholar

Fleming, S., and Ulijn, R. V. (2014). Design of Nanostructures Based on Aromatic Peptide Amphiphiles. Chem. Soc. Rev. 43, 8150–8177. doi:10.1039/C4CS00247D

PubMed Abstract | CrossRef Full Text | Google Scholar

Frederix, P. W. J. M., Scott, G. G., Abul-Haija, Y. M., Kalafatovic, D., Pappas, C. G., Javid, N., et al. (2015). Exploring the Sequence Space for (Tri-)peptide Self-Assembly to Design and Discover New Hydrogels. Nat. Chem 7, 30–37. doi:10.1038/nchem.2122

PubMed Abstract | CrossRef Full Text | Google Scholar

Frick, C., Müller, M., Wank, U., Tropitzsch, A., Kramer, B., Senn, P., et al. (2017). Biofunctionalized Peptide-Based Hydrogels Provide Permissive Scaffolds to Attract Neurite Outgrowth from Spiral Ganglion Neurons. Colloids Surf. B: Biointerfaces 149, 105–114. doi:10.1016/j.colsurfb.2016.10.003

PubMed Abstract | CrossRef Full Text | Google Scholar

Fu, K., Wu, H., and Su, Z. (2021). Self-assembling Peptide-Based Hydrogels: Fabrication, Properties, and Applications. Biotechnol. AdvancesAdv 49, 107752. doi:10.1016/j.biotechadv.2021.107752

PubMed Abstract | CrossRef Full Text | Google Scholar

Fuentes-Caparrós, A. M., McAulay, K., Rogers, S. E., Dalgliesh, R. M., and Adams, D. J. (2019). On the Mechanical Properties of N-Functionalised Dipeptide Gels. Molecules 24, 3855. doi:10.3390/molecules24213855

CrossRef Full Text | Google Scholar

Fukunaga, K., Tsutsumi, H., and Mihara, H. (2019). Self-Assembling Peptides as Building Blocks of Functional Materials for Biomedical Applications. Bcsj 92, 391–399. doi:10.1246/bcsj.20180293

CrossRef Full Text | Google Scholar

Ghosal, A., Vashist, A., Tiwari, S., Kaushik, A., Dev Jayant, R., Nair, M., et al. (2018). “Hydrogels: Smart Nanomaterials for Biomedical Applications,” in Synthesis of Inorganic Nanomaterials Micro and Nano Technologies. Editors S. Mohan Bhagyaraj, O. S. Oluwafemi, N. Kalarikkal, and S. Thomas (Duxford: Woodhead Publishing)), 283–292. doi:10.1016/B978-0-08-101975-7.00011-7

CrossRef Full Text | Google Scholar

Ghosh, M., Halperin-Sternfeld, M., Grigoriants, I., Lee, J., Nam, K. T., and Adler-Abramovich, L. (2017). Arginine-Presenting Peptide Hydrogels Decorated with Hydroxyapatite as Biomimetic Scaffolds for Bone Regeneration. Biomacromolecules 18, 3541–3550. doi:10.1021/acs.biomac.7b00876

PubMed Abstract | CrossRef Full Text | Google Scholar

Gupta, D., Gangwar, A., Jyoti, K., Sainaga Jyothi, V. G. S., Sodhi, R. K., Mehra, N. K., et al. (2020). Self Healing Hydrogels: A New Paradigm Immunoadjuvant for Delivering Peptide Vaccine. Colloids Surf. B: Biointerfaces 194, 111171. doi:10.1016/j.colsurfb.2020.111171

PubMed Abstract | CrossRef Full Text | Google Scholar

Guyon, L., Lepeltier, E., and Passirani, C. (2018). Self-assembly of Peptide-Based Nanostructures: Synthesis and Biological Activity. Nano Res. 11, 2315–2335. doi:10.1007/s12274-017-1892-9

CrossRef Full Text | Google Scholar

Habibi, N., Kamaly, N., Memic, A., and Shafiee, H. (2016). Self-assembled Peptide-Based Nanostructures: Smart Nanomaterials toward Targeted Drug Delivery. Nano Today 11, 41–60. doi:10.1016/j.nantod.2016.02.004

PubMed Abstract | CrossRef Full Text | Google Scholar

Halperin-Sternfeld, M., Ghosh, M., Sevostianov, R., Grigoriants, I., and Adler-Abramovich, L. (2017). Molecular Co-assembly as a Strategy for Synergistic Improvement of the Mechanical Properties of Hydrogels. Chem. Commun. 53, 9586–9589. doi:10.1039/C7CC04187J

PubMed Abstract | CrossRef Full Text | Google Scholar

Helen, W., de Leonardis, P., Ulijn, R. V., Gough, J., and Tirelli, N. (2011). Mechanosensitive Peptidegelation: Mode of Agitation Controls Mechanical Properties and Nano-Scale Morphology. Soft Matter 7, 1732–1740. doi:10.1039/C0SM00649A

CrossRef Full Text | Google Scholar

Hendi, A., Umair Hassan, M., Elsherif, M., Alqattan, B., Park, S., Yetisen, A. K., et al. (2020). Healthcare Applications of pH-Sensitive Hydrogel-Based Devices: A Review. Ijn 15, 3887–3901. doi:10.2147/IJN.S245743

PubMed Abstract | CrossRef Full Text | Google Scholar

Hsu, S.-M., Chakravarthy, R. D., Cheng, H., Wu, F.-Y., Lai, T.-S., and Lin, H.-C. (2018). The Role of Aromatic Side Chains on the Supramolecular Hydrogelation of Naphthalimide/dipeptide Conjugates. New J. Chem. 42, 4443–4449. doi:10.1039/c7nj03565a

CrossRef Full Text | Google Scholar

Hu, T., Zhang, Z., Hu, H., Euston, S. R., and Pan, S. (2020a). A Comprehensive Study on Self-Assembly and Gelation of C13-Dipeptides-From Design Strategies to Functionalities. Biomacromolecules 21, 670–679. doi:10.1021/acs.biomac.9b01386

PubMed Abstract | CrossRef Full Text | Google Scholar

Hu, X., Liao, M., Gong, H., Zhang, L., Cox, H., Waigh, T. A., et al. (2020b). Recent Advances in Short Peptide Self-Assembly: from Rational Design to Novel Applications. Curr. Opin. Colloid Interf. Sci. 45, 1–13. doi:10.1016/j.cocis.2019.08.003

CrossRef Full Text | Google Scholar

Hughes, M., Birchall, L. S., Zuberi, K., Aitken, L. A., Debnath, S., Javid, N., et al. (2012). Differential Supramolecular Organisation of Fmoc-Dipeptides with Hydrophilic Terminal Amino Acid Residues by Biocatalytic Self-Assembly. Soft Matter 8, 11565–11574. doi:10.1039/c2sm26092a

CrossRef Full Text | Google Scholar

Hughes, M., Debnath, S., Knapp, C. W., and Ulijn, R. V. (2013). Antimicrobial Properties of Enzymatically Triggered Self-Assembling Aromatic Peptide Amphiphiles. Biomater. Sci. 1, 1138–1142. doi:10.1039/C3BM60135H

PubMed Abstract | CrossRef Full Text | Google Scholar

Jayawarna, V., Ali, M., Jowitt, T. A., Miller, A. F., Saiani, A., Gough, J. E., et al. (2006). Nanostructured Hydrogels for Three-Dimensional Cell Culture through Self-Assembly of Fluorenylmethoxycarbonyl-Dipeptides. Adv. Mater. 18, 611–614. doi:10.1002/adma.200501522

CrossRef Full Text | Google Scholar

Jian, H., Wang, M., Dong, Q., Li, J., Wang, A., Li, X., et al. (2019). Dipeptide Self-Assembled Hydrogels with Tunable Mechanical Properties and Degradability for 3D Bioprinting. Acs Appl. Mater. Inter. 11, 46419–46426. doi:10.1021/acsami.9b13905

PubMed Abstract | CrossRef Full Text | Google Scholar

Ko, Y.-G., and Kwon, O. H. (2020). Reinforced Gelatin-Methacrylate Hydrogels Containing Poly(lactic-Co-Glycolic Acid) Nanofiber Fragments for 3D Bioprinting. J. Ind. Eng. Chem. 89, 147–155. doi:10.1016/j.jiec.2020.04.021

CrossRef Full Text | Google Scholar

Korah, L. V., Anilkumar, G., and Thomas, S. (2018). “Hydrogels, DNA, and RNA Polypeptides for the Preparation of Biomaterials,” in Fundamental Biomaterials: Polymers Woodhead Publishing Series in Biomaterials. Editors S. Thomas, P. Balakrishnan, and M. S. Sreekala (Duxford: Woodhead Publishing), 85–104. doi:10.1016/B978-0-08-102194-1.00005-0

CrossRef Full Text | Google Scholar

Kralj, S., Bellotto, O., Parisi, E., Garcia, A. M., Iglesias, D., Semeraro, S., et al. (2020). Heterochirality and Halogenation Control Phe-Phe Hierarchical Assembly. ACS Nano 14, 16951–16961. doi:10.1021/acsnano.0c06041

PubMed Abstract | CrossRef Full Text | Google Scholar

Kurbasic, M., Semeraro, S., Garcia, A. M., Kralj, S., Parisi, E., Deganutti, C., et al. (2019). Microwave-Assisted Cyclization of Unprotected Dipeptides in Water to 2,5-Piperazinediones and Self-Assembly Study of Products and Reagents. Synthesis 51, 2829–2838. doi:10.1055/s-0037-1612376

CrossRef Full Text | Google Scholar

Lei, K., Li, Z., Zhu, D., Sun, C., Sun, Y., Yang, C., et al. (2020). Polysaccharide-based Recoverable Double-Network Hydrogel with High Strength and Self-Healing Properties. J. Mater. Chem. B 8, 794–802. doi:10.1039/c9tb01679a

PubMed Abstract | CrossRef Full Text | Google Scholar

Levin, A., Hakala, T. A., Schnaider, L., Bernardes, G. J. L., Gazit, E., and Knowles, T. P. J. (2020). Biomimetic Peptide Self-Assembly for Functional Materials. Nat. Rev. Chem. 4, 615–634. doi:10.1038/s41570-020-0215-y

CrossRef Full Text | Google Scholar

Li, F., Han, J., Cao, T., Lam, W., Fan, B., Tang, W., et al. (2019a). Design of Self-Assembly Dipeptide Hydrogels and Machine Learning via Their Chemical Features. Proc. Natl. Acad. Sci. USA 116, 11259–11264. doi:10.1073/pnas.1903376116

PubMed Abstract | CrossRef Full Text | Google Scholar

Li, F., Tang, J., Geng, J., Luo, D., and Yang, D. (2019b). Polymeric DNA Hydrogel: Design, Synthesis and Applications. Prog. Polym. Sci. 98, 101163. doi:10.1016/j.progpolymsci.2019.101163

CrossRef Full Text | Google Scholar

Li, J., Kuang, Y., Shi, J., Gao, Y., Zhou, J., and Xu, B. (2013). The Conjugation of Nonsteroidal Anti-inflammatory Drugs (NSAID) to Small Peptides for Generating Multifunctional Supramolecular Nanofibers/hydrogels. Beilstein J. Org. Chem. 9, 908–917. doi:10.3762/bjoc.9.104

PubMed Abstract | CrossRef Full Text | Google Scholar

Li, L., Sun, R., Zheng, R., and Huang, Y. (2021b). Anions-responsive Supramolecular Gels: A Review. Mater. Des. 205, 109759. doi:10.1016/j.matdes.2021.109759

CrossRef Full Text | Google Scholar

Li, L., Sun, R., and Zheng, R. (2021a). Tunable Morphology and Functionality of Multicomponent Self-Assembly: a Review. Mater. Des. 197, 109209. doi:10.1016/j.matdes.2020.109209

CrossRef Full Text | Google Scholar

Li, Y., Zhu, C., Dong, Y., and Liu, D. (2020). Supramolecular Hydrogels: Mechanical Strengthening with Dynamics. Polymer 210, 122993. doi:10.1016/j.polymer.2020.122993

CrossRef Full Text | Google Scholar

Lu, L., Yuan, S., Wang, J., Shen, Y., Deng, S., Xie, L., et al. (2018). The Formation Mechanism of Hydrogels. Curr. Stem Cel Res. Ther. 13, 490–496. doi:10.2174/1574888X12666170612102706

PubMed Abstract | CrossRef Full Text | Google Scholar

Mahinroosta, M., Jomeh Farsangi, Z., Allahverdi, A., and Shakoori, Z. (2018). Hydrogels as Intelligent Materials: A Brief Review of Synthesis, Properties and Applications. Mater. Today Chem. 8, 42–55. doi:10.1016/j.mtchem.2018.02.004

CrossRef Full Text | Google Scholar

Makam, P., and Gazit, E. (2018). Minimalistic Peptide Supramolecular Co-assembly: Expanding the Conformational Space for Nanotechnology. Chem. Soc. Rev. 47, 3406–3420. doi:10.1039/C7CS00827A

PubMed Abstract | CrossRef Full Text | Google Scholar

Martin, A. D., and Thordarson, P. (2020). Beyond Fmoc: a Review of Aromatic Peptide Capping Groups. J. Mater. Chem. B 8, 863–877. doi:10.1039/C9TB02539A

PubMed Abstract | CrossRef Full Text | Google Scholar

McAulay, K., Dietrich, B., Su, H., Scott, M. T., Rogers, S., Al-Hilaly, Y. K., et al. (2019). Using Chirality to Influence Supramolecular Gelation. Chem. Sci. 10, 7801–7806. doi:10.1039/C9SC02239B

PubMed Abstract | CrossRef Full Text | Google Scholar

McAulay, K., Ucha, P. A., Wang, H., Fuentes-Caparrós, A. M., Thomson, L., Maklad, O., et al. (2020). Controlling the Properties of the Micellar and Gel Phase by Varying the Counterion in Functionalised-Dipeptide Systems. Chem. Commun. 56, 4094–4097. doi:10.1039/d0cc01252a

PubMed Abstract | CrossRef Full Text | Google Scholar

Mondal, S., Das, S., and Nandi, A. K. (2020). A Review on Recent Advances in Polymer and Peptide Hydrogels. Soft Matter 16, 1404–1454. doi:10.1039/c9sm02127b

PubMed Abstract | CrossRef Full Text | Google Scholar

Najafi, H., Tamaddon, A. M., Abolmaali, S., Borandeh, S., and Azarpira, N. (2021). Structural, Mechanical, and Biological Characterization of Hierarchical Nanofibrous Fmoc-Phenylalanine-Valine Hydrogels for 3D Culture of Differentiated and Mesenchymal Stem Cells. Soft Matter 17, 57–67. doi:10.1039/d0sm01299h

PubMed Abstract | CrossRef Full Text | Google Scholar

Nandi, S. K., Maji, K., and Haldar, D. (2018). Self-Healing Hydrogel from a Dipeptide and HCl Sensing. ACS Omega 3, 3744–3751. doi:10.1021/acsomega.8b00358

PubMed Abstract | CrossRef Full Text | Google Scholar

Ni, M., and Zhuo, S. (2019). Applications of Self-Assembling Ultrashort Peptides in Bionanotechnology. RSC Adv. 9, 844–852. doi:10.1039/C8RA07533F

CrossRef Full Text | Google Scholar

Nikoloudakis, E., Mitropoulou, K., Landrou, G., Charalambidis, G., Nikolaou, V., Mitraki, A., et al. (2019). Self-assembly of Aliphatic Dipeptides Coupled with Porphyrin and BODIPY Chromophores. Chem. Commun. 55, 14103–14106. doi:10.1039/c9cc06125h

PubMed Abstract | CrossRef Full Text | Google Scholar

Nolan, M. C., Fuentes Caparrós, A. M., Dietrich, B., Barrow, M., Cross, E. R., Bleuel, M., et al. (2017). Optimising Low Molecular Weight Hydrogels for Automated 3D Printing. Soft Matter 13, 8426–8432. doi:10.1039/c7sm01694h

PubMed Abstract | CrossRef Full Text | Google Scholar

O'Leary, L. E. R., Fallas, J. A., Bakota, E. L., Kang, M. K., and Hartgerink, J. D. (2011). Multi-hierarchical Self-Assembly of a Collagen Mimetic Peptide from Triple helix to Nanofibre and Hydrogel. Nat. Chem 3, 821–828. doi:10.1038/nchem.1123

PubMed Abstract | CrossRef Full Text | Google Scholar

Ohtomi, T., Higashi, S. L., Mori, D., Shibata, A., Kitamura, Y., and Ikeda, M. (2020). Effect of Side Chain Phenyl Group on the Self‐assembled Morphology of Dipeptide Hydrazides. Pept. Sci. 113, e24200. doi:10.1002/pep2.24200

CrossRef Full Text | Google Scholar

Panda, J. J., Mishra, A., Basu, A., and Chauhan, V. S. (2008). Stimuli Responsive Self-Assembled Hydrogel of a Low Molecular Weight Free Dipeptide with Potential for Tunable Drug Delivery. Biomacromolecules 9, 2244–2250. doi:10.1021/bm800404z

PubMed Abstract | CrossRef Full Text | Google Scholar

Piras, C. C., Kay, A. G., Genever, P. G., and Smith, D. K. (2021). Self-assembled Low-Molecular-Weight Gelator Injectable Microgel Beads for Delivery of Bioactive Agents. Chem. Sci. 12, 3958–3965. doi:10.1039/D0SC06296K

PubMed Abstract | CrossRef Full Text | Google Scholar

Pîrşcoveanu, D. F. V., Pirici, I., Tudorică, V., Bălşeanu, T. A., Albu, V. C., Bondari, S., et al. (2017). Tau Protein in Neurodegenerative Diseases - a Review. Rom. J. Morphol. Embryol. 58, 1141–1150.

PubMed Abstract | Google Scholar

Podder, D., Nandi, S. K., Sasmal, S., and Haldar, D. (2019). Synergistic Tricolor Emission-Based White Light from Supramolecular Organic-Inorganic Hybrid Gel. Langmuir 35, 6453–6459. doi:10.1021/acs.langmuir.9b00456

PubMed Abstract | CrossRef Full Text | Google Scholar

Prabhu, S., Bubbly, S. G., and Gudennavar, S. B. (2020). Synthetic Polymer Hydrogels as Potential Tissue Phantoms in Radiation Therapy and Dosimetry. Biomed. Phys. Eng. Express 6, 055008. doi:10.1088/2057-1976/aba209

PubMed Abstract | CrossRef Full Text | Google Scholar

Qiu, T., Liu, Q., Chen, Y.-X., Zhao, Y.-F., and Li, Y.-M. (2015). Aβ42 and Aβ40: Similarities and Differences. J. Pept. Sci. 21, 522–529. doi:10.1002/psc.2789

PubMed Abstract | CrossRef Full Text | Google Scholar

Raeburn, J., and Adams, D. J. (2015). Multicomponent Low Molecular Weight Gelators. Chem. Commun. 51, 5170–5180. doi:10.1039/c4cc08626k

PubMed Abstract | CrossRef Full Text | Google Scholar

Raeburn, J., Pont, G., Chen, L., Cesbron, Y., Lévy, R., and Adams, D. J. (2012). Fmoc-diphenylalanine Hydrogels: Understanding the Variability in Reported Mechanical Properties. Soft Matter 8, 1168–1174. doi:10.1039/c1sm06929b

CrossRef Full Text | Google Scholar

Rajbhandary, A., and Nilsson, B. L. (2017). Investigating the Effects of Peptoid Substitutions in Self‐assembly of Fmoc‐diphenylalanine Derivatives. Biopolymers 108, e22994. doi:10.1002/bip.22994

PubMed Abstract | CrossRef Full Text | Google Scholar

Ramin, M. A., Latxague, L., Sindhu, K. R., Chassande, O., and Barthélémy, P. (2017). Low Molecular Weight Hydrogels Derived from Urea Based-Bolaamphiphiles as New Injectable Biomaterials. Biomaterials 145, 72–80. doi:10.1016/j.biomaterials.2017.08.034

CrossRef Full Text | Google Scholar

Ren, P., Li, J., Zhao, L., Wang, A., Wang, M., Li, J., et al. (2020). Dipeptide Self-Assembled Hydrogels with Shear-Thinning and Instantaneous Self-Healing Properties Determined by Peptide Sequences. Acs Appl. Mater. Inter. 12, 21433–21440. doi:10.1021/acsami.0c03038

PubMed Abstract | CrossRef Full Text | Google Scholar

Ryan, D. M., and Nilsson, B. L. (2012). Self-assembled Amino Acids and Dipeptides as Noncovalent Hydrogels for Tissue Engineering. Polym. Chem. 3, 18–33. doi:10.1039/C1PY00335F

CrossRef Full Text | Google Scholar

Sadownik, J. W., Leckie, J., and Ulijn, R. V. (2011). Micelle to Fibre Biocatalytic Supramolecular Transformation of an Aromatic Peptide Amphiphile. Chem. Commun. 47, 728–730. doi:10.1039/c0cc03796f

PubMed Abstract | CrossRef Full Text | Google Scholar

Sangeetha, N. M., and Maitra, U. (2005). Supramolecular Gels: Functions and Uses. Chem. Soc. Rev. 34, 821–836. doi:10.1039/B417081B

PubMed Abstract | CrossRef Full Text | Google Scholar

Sasselli, I. R., Pappas, C. G., Matthews, E., Wang, T., Hunt, N. T., Ulijn, R. V., et al. (2016). Using Experimental and Computational Energy Equilibration to Understand Hierarchical Self-Assembly of Fmoc-Dipeptide Amphiphiles. Soft Matter 12, 8307–8315. doi:10.1039/c6sm01737a

PubMed Abstract | CrossRef Full Text | Google Scholar

Schab-Balcerzak, E., Siwy, M., Filapek, M., Kula, S., Malecki, G., Laba, K., et al. (2015). New Core-Substituted with Electron-Donating Group 1,8-naphthalimides towards Optoelectronic Applications. J. Lumin. 166, 22–39. doi:10.1016/j.jlumin.2015.04.025

CrossRef Full Text | Google Scholar

Sedman, V. L., Chen, X., Allen, S., Roberts, C. J., Korolkov, V. V., and Tendler, S. J. B. (2013). Tuning the Mechanical Properties of Self‐assembled Mixed‐peptide Tubes. J. Microsc. 249, 165–172. doi:10.1111/jmi.12005

PubMed Abstract | CrossRef Full Text | Google Scholar

Singh, N., Kumar, M., Miravet, J. F., Ulijn, R. V., and Escuder, B. (2017). Peptide-Based Molecular Hydrogels as Supramolecular Protein Mimics. Chem. Eur. J. 23, 981–993. doi:10.1002/chem.201602624

PubMed Abstract | CrossRef Full Text | Google Scholar

Smith, A. M., Williams, R. J., Tang, C., Coppo, P., Collins, R. F., Turner, M. L., et al. (2008). Fmoc-Diphenylalanine Self Assembles to a Hydrogel via a Novel Architecture Based onπ-πInterlockedβ-Sheets. Adv. Mater. 20, 37–41. doi:10.1002/adma.200701221

CrossRef Full Text | Google Scholar

Talloj, S. K., Mohammed, M., and Lin, H.-C. (2020). Construction of Self-Assembled Nanostructure-Based Tetraphenylethylene Dipeptides: Supramolecular Nanobelts as Biomimetic Hydrogels for Cell Adhesion and Proliferation. J. Mater. Chem. B 8, 7483–7493. doi:10.1039/d0tb01147a

PubMed Abstract | CrossRef Full Text | Google Scholar

Tang, C., Smith, A. M., Collins, R. F., Ulijn, R. V., and Saiani, A. (2009). Fmoc-Diphenylalanine Self-Assembly Mechanism Induces Apparent pKa Shifts. Langmuir 25, 9447–9453. doi:10.1021/la900653q

PubMed Abstract | CrossRef Full Text | Google Scholar

Tang, C., Ulijn, R. V., and Saiani, A. (2011). Effect of Glycine Substitution on Fmoc-Diphenylalanine Self-Assembly and Gelation Properties. Langmuir 27, 14438–14449. doi:10.1021/la202113j

PubMed Abstract | CrossRef Full Text | Google Scholar

Tao, K., Levin, A., Adler-Abramovich, L., and Gazit, E. (2016). Fmoc-modified Amino Acids and Short Peptides: Simple Bio-Inspired Building Blocks for the Fabrication of Functional Materials. Chem. Soc. Rev. 45, 3935–3953. doi:10.1039/C5CS00889A

PubMed Abstract | CrossRef Full Text | Google Scholar

Thota, C. K., Yadav, N., and Chauhan, V. S. (2016). "A Novel Highly Stable and Injectable Hydrogel Based on a Conformationally Restricted Ultrashort Peptide". Sci. Rep. 6, 31167. doi:10.1038/srep31167

PubMed Abstract | CrossRef Full Text | Google Scholar

Truong, W. T., Su, Y., Gloria, D., Braet, F., and Thordarson, P. (2015). Dissolution and Degradation of Fmoc-Diphenylalanine Self-Assembled Gels Results in Necrosis at High Concentrations In Vitro. Biomater. Sci. 3, 298–307. doi:10.1039/C4BM00244J

PubMed Abstract | CrossRef Full Text | Google Scholar

Tsuzuki, T., Kabumoto, M., Arakawa, H., and Ikeda, M. (2017). The Effect of Carbohydrate Structures on the Hydrogelation Ability and Morphology of Self-Assembled Structures of Peptide-Carbohydrate Conjugates in Water. Org. Biomol. Chem. 15, 4595–4600. doi:10.1039/C7OB00816C

PubMed Abstract | CrossRef Full Text | Google Scholar

Tu, Y., Chen, N., Li, C., Liu, H., Zhu, R., Chen, S., et al. (2019). Advances in Injectable Self-Healing Biomedical Hydrogels. Acta Biomater. 90, 1–20. doi:10.1016/j.actbio.2019.03.057

PubMed Abstract | CrossRef Full Text | Google Scholar

Vázquez‐González, M., and Willner, I. (2020). Stimuli‐Responsive Biomolecule‐Based Hydrogels and Their Applications. Angew. Chem. Int. Ed. 59, 15342–15377. doi:10.1002/anie.201907670

CrossRef Full Text | Google Scholar

Vegners, R., Shestakova, I., Kalvinsh, I., Ezzell, R. M., and Janmey, P. A. (1995). Use of a Gel-Forming Dipeptide Derivative as a Carrier for Antigen Presentation. J. Pept. Sci. 1, 371–378. doi:10.1002/psc.310010604

PubMed Abstract | CrossRef Full Text | Google Scholar

Veloso, S. R. S., Jervis, P. J., Silva, J. F. G., Hilliou, L., Moura, C., Pereira, D. M., et al. (2021). Supramolecular Ultra-short Carboxybenzyl-Protected Dehydropeptide-Based Hydrogels for Drug Delivery. Mater. Sci. Eng. C 122, 111869. doi:10.1016/j.msec.2021.111869

CrossRef Full Text | Google Scholar

Wang, M., Wang, C., Chen, M., Xi, Y., Cheng, W., Mao, C., et al. (2019). Efficient Angiogenesis-Based Diabetic Wound Healing/Skin Reconstruction through Bioactive Antibacterial Adhesive Ultraviolet Shielding Nanodressing with Exosome Release. ACS Nano 13, 10279–10293. doi:10.1021/acsnano.9b03656

PubMed Abstract | CrossRef Full Text | Google Scholar

Wang, W., and Chau, Y. (2012). Self-Assembly Mediated Platform for Rapid and Facile Preparation of Peptide-Functionalized Nanoparticles with High Stability. Chem. Mater. 24, 946–953. doi:10.1021/cm202860h

CrossRef Full Text | Google Scholar

Wang, W., Yang, Z., Patanavanich, S., Xu, B., and Chau, Y. (2008). Controlling Self-Assembly within Nanospace for Peptide Nanoparticle Fabrication. Soft Matter 4, 1617–1620. doi:10.1039/B801890A

PubMed Abstract | CrossRef Full Text | Google Scholar

Wang, Y., Zhang, W., Gong, C., Liu, B., Li, Y., Wang, L., et al. (2020). Recent Advances in the Fabrication, Functionalization, and Bioapplications of Peptide Hydrogels. Soft Matter 16, 10029–10045. doi:10.1039/D0SM00966K

PubMed Abstract | CrossRef Full Text | Google Scholar

Webber, M. J., and Pashuck, E. T. (2021). (Macro)molecular Self-Assembly for Hydrogel Drug Delivery. Adv. Drug Deliv. Rev. 172, 275–295. doi:10.1016/j.addr.2021.01.006

PubMed Abstract | CrossRef Full Text | Google Scholar

Whitesides, G. M., and Boncheva, M. (2002). Beyond Molecules: Self-Assembly of Mesoscopic and Macroscopic Components. Proc. Natl. Acad. Sci. 99, 4769–4774. doi:10.1073/pnas.082065899

PubMed Abstract | CrossRef Full Text | Google Scholar

Wichterle, O., and Lím, D. (1960). Hydrophilic Gels for Biological Use. Nature 185, 117–118. doi:10.1038/185117a0

CrossRef Full Text | Google Scholar

Włodarczyk‐Biegun, M. K., Werten, M. W. T., Posadowska, U., Storm, I. M., de Wolf, F. A., van den Beucken, J. J. J. P., et al. (2016). Nanofibrillar Hydrogel Scaffolds from Recombinant Protein‐based Polymers with Integrin‐ and Proteoglycan‐binding Domains. J. Biomed. Mater. Res. 104, 3082–3092. doi:10.1002/jbm.a.35839

CrossRef Full Text | Google Scholar

Xian, S., and Webber, M. J. (2020). Temperature-responsive Supramolecular Hydrogels. J. Mater. Chem. B 8, 9197–9211. doi:10.1039/d0tb01814g

PubMed Abstract | CrossRef Full Text | Google Scholar

Yeh, M.-Y., Huang, C.-W., Chang, J.-W., Huang, Y.-T., Lin, J.-H., Hsu, S.-M., et al. (2016). A Novel Nanostructured Supramolecular Hydrogel Self-Assembled from Tetraphenylethylene-Capped Dipeptides. Soft Matter 12, 6347–6351. doi:10.1039/C6SM00755D

PubMed Abstract | CrossRef Full Text | Google Scholar

Yu, C., Kai, T., Wei, J., Pandeeswar, M., Sigal, R.-L., and Ehud, G. (2020). Self-Assembly of Cyclic Dipeptides: Platforms for Functional Materials. Protein Pept. Lett. 27, 688–697.

PubMed Abstract | Google Scholar

Zhang, G., Zhang, L., Rao, H., Wang, Y., Li, Q., Qi, W., et al. (2020). Role of Molecular Chirality and Solvents in Directing the Self-Assembly of Peptide into an Ultra-pH-sensitive Hydrogel. J. Colloid Interf. Sci. 577, 388–396. doi:10.1016/j.jcis.2020.05.087

CrossRef Full Text | Google Scholar

Zhang, Y., and Huang, Y. (2021). Rational Design of Smart Hydrogels for Biomedical Applications. Front. Chem. 8, 615665. doi:10.3389/fchem.2020.615665

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhang, Y., Zhang, H., Zou, Q., Xing, R., Jiao, T., and Yan, X. (2018). An Injectable Dipeptide-Fullerene Supramolecular Hydrogel for Photodynamic Antibacterial Therapy. J. Mater. Chem. B 6, 7335–7342. doi:10.1039/c8tb01487f

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhang, Z., Ai, S., Yang, Z., and Li, X. (2021). Peptide-based Supramolecular Hydrogels for Local Drug Delivery. Adv. Drug Deliv. Rev. 174, 482–503. doi:10.1016/j.addr.2021.05.010

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhao, Y., Wang, Z., Mei, C., Jiang, Z., Feng, Y., Gao, R., et al. (2018). Protein Enables Conformation Transition of a Hydrogel Based on Pentapeptide and Boosts Immune Response In Vivo. Bioconjug. Chem. 29, 1519–1524. doi:10.1021/acs.bioconjchem.8b00044

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhou, P., Wang, J., Wang, M., Hou, J., Lu, J. R., and Xu, H. (2019). Amino Acid Conformations Control the Morphological and Chiral Features of the Self-Assembled Peptide Nanostructures: Young Investigators Perspective. J. Colloid Interf. Sci. 548, 244–254. doi:10.1016/j.jcis.2019.04.019

CrossRef Full Text | Google Scholar

Zou, P., Chen, W.-T., Sun, T., Gao, Y., Li, L.-L., and Wang, H. (2020). Recent Advances: Peptides and Self-Assembled Peptide-Nanosystems for Antimicrobial Therapy and Diagnosis. Biomater. Sci. 8, 4975–4996. doi:10.1039/D0BM00789G

PubMed Abstract | CrossRef Full Text | Google Scholar

Keywords: hydrogel, dipeptide, self-assembly, ultrashort peptide, biocompatible

Citation: Li L, Xie L, Zheng R and Sun R (2021) Self-Assembly Dipeptide Hydrogel: The Structures and Properties. Front. Chem. 9:739791. doi: 10.3389/fchem.2021.739791

Received: 12 July 2021; Accepted: 09 August 2021;
Published: 01 September 2021.

Edited by:

Mosae Selvakumar Paulraj, Asian University for Women, Bangladesh

Reviewed by:

Keli Zhong, Bohai University, China
Subhamay Pramanik, University of Kansas, United States

Copyright © 2021 Li, Xie, Zheng and Sun. This is an open-access article distributed under the terms of the Creative Commons Attribution License (CC BY). The use, distribution or reproduction in other forums is permitted, provided the original author(s) and the copyright owner(s) are credited and that the original publication in this journal is cited, in accordance with accepted academic practice. No use, distribution or reproduction is permitted which does not comply with these terms.

*Correspondence: Liangchun Li, lilc76@gmail.com

Disclaimer: All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article or claim that may be made by its manufacturer is not guaranteed or endorsed by the publisher.