AUTHOR=Ahsan Muhammad Tayyab , Usman Muhammad , Ali Zeeshan , Javed Sofia , Ali Rashad , Farooq Muhammad U. , Akram Muhammad Aftab , Mahmood Asif TITLE=3D Hierarchically Mesoporous Zinc-Nickel-Cobalt Ternary Oxide (Zn0.6Ni0.8Co1.6O4) Nanowires for High-Performance Asymmetric Supercapacitors JOURNAL=Frontiers in Chemistry VOLUME=8 YEAR=2020 URL=https://www.frontiersin.org/journals/chemistry/articles/10.3389/fchem.2020.00487 DOI=10.3389/fchem.2020.00487 ISSN=2296-2646 ABSTRACT=

Increased efforts have been devoted recently to develop high-energy-density supercapacitors (SC) without renouncing their power efficiency. Herein, a hierarchically mesoporous nanostructure of zinc-nickel-cobalt oxide (ZNCO) nanowires (NWs) is constructed by hierarchical aggregation of ZNCO nanoparticles. It is worth noting that cobalt and nickel rich lattice imparts higher charge storage capability by enhanced reversible Faradaic reaction while zinc provides structural stability and higher conductivity. Moreover, particulate nature of ZNCO NWs allows deep diffusion of electrolyte thus enabling reversible charge storage under higher current densities. The as-prepared ZNCO NWs exhibited excellent specific capacitance of 2082.21 F g−1 at the current density of 1 A g−1 with high stability up to 5,000 charge-discharge cycles. Further, the asymmetric SC device was assembled using ZNCO NWs (ZNCO NWs//MWCNTs) which exhibited high energy density of 37.89 Wh kg−1 and excellent capacitance retention up to 88.5% over 1,000 cycles. This work presents ways to construct multi-component high-energy-density materials for next-generation energy storage devices.