REVIEW article

Front. Chem., 06 March 2020
Sec. Polymer Chemistry
This article is part of the Research Topic Smart Hydrogels in Tissue Engineering and Regenerative Medicine View all 10 articles

Recent Advances on Magnetic Sensitive Hydrogels in Tissue Engineering

\nZhongyang Liu,&#x;Zhongyang Liu1,2Jianheng Liu,&#x;Jianheng Liu1,2Xiang Cui,&#x;Xiang Cui1,2Xing Wang
Xing Wang3*Licheng Zhang,
Licheng Zhang1,2*Peifu Tang,
Peifu Tang1,2*
  • 1Department of Orthopedics, Chinese PLA General Hospital, Beijing, China
  • 2National Clinical Research Center for Orthopedics, Sports Medicine and Rehabilitation, Beijing, China
  • 3Beijing National Laboratory for Molecular Sciences, Institute of Chemistry, Chinese Academy of Sciences, Beijing, China

Tissue engineering is a promising strategy for the repair and regeneration of damaged tissues or organs. Biomaterials are one of the most important components in tissue engineering. Recently, magnetic hydrogels, which are fabricated using iron oxide-based particles and different types of hydrogel matrices, are becoming more and more attractive in biomedical applications by taking advantage of their biocompatibility, controlled architectures, and smart response to magnetic field remotely. In this literature review, the aim is to summarize the current development of magnetically sensitive smart hydrogels in tissue engineering, which is of great importance but has not yet been comprehensively viewed.

Introduction

Tissue engineering, a branch of regenerative medicine, refers to the application of supporting cells, material scaffolds, bioactive molecules, or their combinations to repair and reconstruct tissues and organs. Hydrogels have been shown to be one of the most applicable biomaterials in tissue engineering (Kabu et al., 2015; Madl et al., 2017, 2019; Deng et al., 2019) mainly attributed to their inner 3D network microstructures, moderate biocompatibility, and good water content feature, which are analogous with those of the natural tissue (Cui Z.K. et al., 2019; Zhu et al., 2019). Meanwhile, hydrogel-based drug delivery systems for numerous therapeutic agents, with high water content, low interfacial tension with biological fluids, and soft consistency, have been shown to be more stable, economical, and efficient in comparison with conventional delivery systems (Li and Mooney, 2016; Moore and Hartgerink, 2017; Cheng et al., 2019; Fan et al., 2019; Zheng et al., 2019). Considering the above advantages, hydrogels have been conducted into the biomedical application to provide a tunable three-dimensional scaffold for cell adhesion, migration, and/or differentiation, and they could also be designed as the platform for the controlled release of cytokines and drugs in tissue engineering and drug delivery (Huang et al., 2017; Jiang et al., 2017; Hsu et al., 2019; Wei et al., 2019; Zheng et al., 2019).

Hydrogel first appeared in a literature as early as in 1894 (Van Bemmelen, 1894); however, the “hydrogel” described at that time was not the same form of hydrogels used nowadays; it was a type of a colloidal gel made from inorganic salts. Later on, the term “hydrogel” was applied for describing a 3D network of hydrophilic native polymers and gums by physical or chemical crosslinking approaches, and its application heavily relied on water availability in the environment (Lee et al., 2013). The current generation of hydrogel in the biological field was first performed by Wichterle and LÍm (1960), indicating that glycoldimethacrylate-based hydrophilic gels exhibited adjustable mechanical properties and water content. From then on, more and more hydrogels have been developed, and the smart hydrogels were then introduced in different fields of biological science, such as drug delivery, bioseparation, biosensor, and tissue engineering. Smart hydrogels are described as they respond directly to the changes of environmental conditions (Wichterle and LÍm, 1960), and numerous studies of smart hydrogels in the applications of nanotechnology, drug delivery, and tissue engineering have been put into effect in the last few decades (Li X. et al., 2019; Li Z. et al., 2019; Zhang Y. et al., 2019).

Recently, magnetically responsive hydrogel, as one kind of smart hydrogels, has been introduced into biomedical applications in improving the biological activities of cells, tissues, or organs. This is mainly attributed to its magnetic responsiveness to external magnetic field and obtaining functional structures to remotely regulate physical, biochemical, and mechanical properties of the milieu surrounding the cells, tissues, or organs (Abdeen et al., 2016; Antman-Passig and Shefi, 2016; Rodkate and Rutnakornpituk, 2016; Bannerman et al., 2017; Omidinia-Anarkoli et al., 2017; Xie et al., 2017; Silva et al., 2018; Tay et al., 2018; Wang et al., 2018; Bowser and Moore, 2019; Ceylan et al., 2019; Luo et al., 2019). Recent studies have represented that magnetic hydrogel could act as an excellent drug release and targeting system. For example, Gao et al. (2019) fabricated a magnetic hydrogel based on ferromagnetic vortex-domain iron oxide and suggested that this unique magnetic hydrogel could significantly suppress the local breast tumor recurrences. Manjua et al. (2019) developed magnetic responsive poly(vinyl alcohol) (PVA) hydrogels, which could be motivated by ON/OFF magnetic field and non-invasively regulated protein sorption and motility, indicating a promising application for tissue engineering, drug delivery, or biosensor system. Moreover, a composite magnetic hydrogel prepared by a combination of a self-healing chitosan/alginate hydrogel and magnetic gelatin microspheres could be used as a suitable platform for tissue engineering and drug delivery (Chen X. et al., 2019a). In comparison with magnetic hydrogels, various kinds of smart biomaterials (e.g., scaffolds, biofilms, other smart hydrogels), which are activated by external stimuli, such as light, pH, temperature, stress, or charge, have great potential in biomedical applications (Chen H. et al., 2019; Cui L. et al., 2019; Wu C. et al., 2019; Zhao et al., 2019; Yang et al., 2020). However, the long response time and less precisely controlled architectures of these stimuli-responsive smart biomaterials are the two main limitations.

Magnetic hydrogels are usually made of a matrix hydrogel and a magnetic component that was incorporated into the matrix. Recently, superparamagnetic and biocompatible iron oxide-based magnetic nanoparticles (MNPs) are most commonly incorporated into polymer matrices to prepare magnetically responsive hydrogels for their application in tissue engineering, such as γ-Fe2O3, Fe3O4, and cobalt ferrite nanoparticles (CoFe2O4) (Zhang and Song, 2016; Rose et al., 2017; Ceylan et al., 2019). Magnetite (Fe3O4) is a compound of two kinds of iron sites with 1/3 of Fe2+ and 2/3 of Fe3+. The intervalence charge transfer between Fe2+ and Fe3+ induces absorption throughout the ultraviolet–visible spectral region and the infrared spectral region, which generates a black appearance in color (Barrow et al., 2017). Maghemite (γ-Fe2O3), with a brown-orange color pattern, is an oxidative product of magnetite (Fe3O4) when the temperature is below 200°C (Tang et al., 2003). In terms of CoFe2O4, previous studies have shown that the concentration of 20% was toxic, whereas at 10% the toxicity was insignificant. Moreover, 10% (w/w) of CoFe2O4 could maximize magnetic response because of numerous amounts of nanoparticles, developing biocompatible biomaterials (Goncalves et al., 2015; Brito-Pereira et al., 2018). For example, Hermenegildo et al. (2019) designed a novel CoFe2O4/Methacrylated Gellan Gum/poly(vinylidene fluoride) hydrogel, which created a promising microenvironment for tissue stimulation.

In this literature review, we aim to summarize the preparation methods and current development of magnetically sensitive smart hydrogels in tissue engineering, especially in bone, cartilage, and neural tissue engineering, which are of great importance but have not yet been comprehensively reviewed.

The Fabrication Processing of Magnetic Hydrogels

Magnetic hydrogels are made of composite materials that possess biocompatibility, biodegradation, and magnetic responsiveness. The characteristics of magnetic hydrogels depend upon several issues, including the magnetic particles and the component of hydrogels used, the magnetic particles and hydrogels' concentration, and the size and uniformity of magnetic particles within the hydrogels. There are mainly three preparation methods of fabricating magnetic hydrogels: (i) blending method; (ii) in situ precipitation method; (iii) grafting-onto method (Table 1). The scheme for the main three syntheses of the magnetic hydrogels is shown in Figure 1.

TABLE 1
www.frontiersin.org

Table 1. The preparation methods of magnetic hydrogels and the parameters of magnetic field in representative references.

FIGURE 1
www.frontiersin.org

Figure 1. The schematic diagram of the main three routes for the synthesis of the magnetic hydrogels. (A) The blending method. (B) The in situ precipitation method. (C) The grafting-onto method (Created with BioRender.com).

The Blending Method

In the blending approach, magnetic particles, and hydrogels are fabricated separately. The magnetic particles are normally synthesized using a coprecipitation process. The resulting magnetic particles are then stored in an aqueous or oily liquid to prevent aggregation and oxidization. Finally, the solution of magnetic particles is mixed with the hydrogel solution for crosslinking, and the magnetic particles are encapsulated into the hydrogels. Tóth et al. (2015) modified the surface of MNPs (magnetite) with biocompatible chondroitin-sulfate-A (CSA) to develop CSA-coated MNPs. Then, CSA-coated MNPs were dispersed into hyaluronate (HyA) hydrogel to prepare the HyA-based magnetic hydrogel. It was found that the HyA-based magnetic hydrogel could be conducted in the treatment of osteoarthritis by the intra-articular injection approach. Shi et al. (2019) fabricated bisphosphonate (BP)-modified hyaluronic acid (HA)/Fe3O4 magnetic hydrogel. This novel magnetic hydrogel showed outstanding compatibility and slow degradation in vivo and held the expectation of safety in clinic usage.

The blending method has several advantages in the preparation of magnetic hydrogels. Firstly, magnetic particles (e.g., MNPs, micrometer-iron oxides) with homogenous size in hydrogels can be obtained by modifying the stirring speed, the concentration of the substances, and the fabrication period. Secondly, the preparation process is easy to be performed since the preparation and crosslinking of magnetic particles are conducted separately. However, there are also some limitations that could be addressed in the future, including the asymmetric distribution of magnetic particles within the hydrogels and the diffusion of magnetic particles when the magnetic hydrogels were submerged in a solution.

In situ Precipitation Method

In the process of the in situ precipitation, the network of the hydrogels acts as a chemically reactive substance, within which the iron ions from inorganic salts in hydrogels react with alkali solutions (e.g., NH3·H2O, NaOH; Arias et al., 2018; Liu et al., 2019) to prepare the magnetic particles. In detail, the hydrogels are firstly prepared through polymerization, temperature change, or a crosslinking reaction. Then, magnetite precursors containing iron(III) and iron(II) at a molar ratio of 1:2 are added into the hydrogels to obtain a homogenous solution. Finally, the mixture is immersed in an alkali solution to induce the crystallization of magnetite. The magnetic particles are incorporated into the hydrogels according to the following hydrolytic reaction (2 Fe3+ + Fe2+ + OH– → Fe3O4 + 4 H2O). Wang et al. (2018) designed a magnetic chitosan hydrogel by adding MNPs via in situ synthesis during chitosan hydrogel formation. The resulting magnetic hydrogel showed a magnetic response and improved morphological and mechanical features, including the homogenous distribution of MNPs and excellent wettability. Moreover, the mechanical properties (such as the compression strength, the yield strength, and the probe displacement) of the magnetic hydrogel was enhanced with the rising concentration of MNPs from 0 to 15 wt%, which was attributed to the crosslinking role of MNPs in the process. Under low-frequency alternating magnetic field (LAMF) exposure, the magnetic hydrogel laden with drugs exhibited a pulsatile drug release profile. In addition, the in situ fabricated MNPs in the magnetic hydrogel had excellent biocompatibility and no acute toxicity on MG-63 cells (human osteosarcoma cell line). Liu et al. (2019) fabricated polydopamine (PDA)-chelated carbon nanotube (CNT)-Fe3O4 (PFeCNT) nanohybrids into the acrylamide hydrogel via an in situ precipitation method to generate the PFeCNT hydrogel. This magnetic hydrogel formed an anisotropic morphology under a low static magnetic field (SMF) (30 mT) and showed conductive and mechanical features. Interestingly, under external electrical stimulation, the myoblasts cultured on the magnetic hydrogel exhibited oriented outgrowth. Arias et al. (2018) designed a magnetic bacterial cellulose (MBC) hydrogel by an in situ synthesis approach that mixed the dextran-coated Fe3O4 nanoparticles with bacterial cellulose pellicles. The resulting MBC hydrogel could be activated with saturation magnetization and exhibited a moderate Young's modulus (200−380 kPa), which was appropriate for vascular tissue engineering. Under an external magnetic field (0.3 T) stimulation, the produced gradient magnetic fields resulted in higher cell retention for the magnetically activated MBC hydrogel.

With the in situ precipitation method, numerous kinds of inorganic substances could be applied in the fabrication of the hydrogel networks, with good dispersion in the hydrogel matrix. Moreover, the synthesized approach is straightforward and economical. However, this method is only appropriate for limited hydrogels that possess stable networks. This is because the alkali solution used in the process might destroy the hydrogel network and limit the application of cell encapsulation (Wang et al., 2009).

The Grafting-Onto Method

In the grafting-onto methodology, there are covalent bonds formed between the magnetic particles and the hydrogel network. In detail, several functional groups are grafted onto the surface of the magnetic particles, which act as micro- or nanocrosslinkers to generate covalent bonds with the hydrogel monomers. Hu et al. (2019) designed a magnetic hydrogel made from non-toxic polyacrylamide (PAAm) hydrogel and 3-(trimethoxysilyl)propyl methacrylate coated Fe3O4 via the grafting-onto approach. This novel magnetic hydrogel exhibited relatively high mechanical properties, including tensile strength and fracture toughness. In addition, polydimethylsiloxane (PDMS) was introduced to modify the surface of the magnetic hydrogel, and the resulting product exhibited excellent underwater performance. The PDMS-coated magnetic hydrogel kept stability even under fatigue loading, which highlighted significant potentials in the applications of artificial muscles. Messing et al. (2011) firstly fabricated methacrylic groups functionalized magnetic CoFe2O4 nanoparticles. Then the magnetic hydrogels were fabricated by adding this kind of magnetic nanoparticles into a polyacrylamide hydrogel network.

An advantage of the grafting-onto approach is that the covalent bonds are capable of encapsulating the magnetic particles within the hydrogels, which promote the stability of the magnetic hydrogel. However, the long fabrication time, the high-cost protocol, and the complicated fabrication process restrict its broader applications in the biomedical field.

Applications in Bone Tissue Engineering

The repair of large bone defects caused by traumas, infections, cancers, or other diseases is still a thorny clinical problem (Herberg et al., 2019). Previous studies have shown that osteo-inductive growth factors played a significant role in bone regeneration (Cui L. et al., 2019; Ruehle et al., 2019) however, autologous bone graft remains the gold standard in the treatment of bone defects (Bouyer et al., 2016). Considering the donor site morbidity and limited source of the donor area, the development of bone tissue engineering biomaterials is becoming more and more attractive for researchers. Most endeavors have been applied for the evaluation of MNPs-incorporated hydrogels in bone repair. As hydroxyapatite (HAP) is one of the most important components in natural bone inorganic substances, exhibits excellent biocompatibility and osteo-conductivity, and plays a key role in biomineralization (Moncion et al., 2019; Zhou et al., 2019), the magnetic HAP composite hydrogel was designed. For example, nano-HAP coated γ-Fe2O3 nanoparticles (m-nHAP) were synthesized and then added into poly(vinyl alcohol) (PVA) solution to fabricate m-nHAP/PVA hydrogels. The PVA showed excellent biocompatibility, high mechanical properties, and slow biodegradation, which were crucial for its application (Iqbal et al., 2019; Venkataprasanna et al., 2019). The pore sizes of hydrogels rose gradually followed by the increased content of m-nHAP, which was accessible for nutrient exchange. Meanwhile, the adhesion and proliferation of human osteoblasts were dramatically promoted as the m-nHAP concentration increased (Hou et al., 2013). However, the magnetic field was not introduced in this study, which might be considered as a potential promoter in improving bone tissue regeneration using this magnetic hydrogel.

Cells, such as stem cells, neural cells, and osteoblasts, are an important component in tissue engineering (Cerqueira et al., 2018; He et al., 2018; Ahmad et al., 2019; Chen M. et al., 2019; Midgley et al., 2019); therefore, MNP labeled cells are becoming more and more available in magnetically bioinspired hydrogels. Henstock et al. (2014) first added TREK1-MNPs or Arg-Gly-Asp (RGD)-MNPs into human mesenchymal stem cells (hMSCs) to fabricate MNP labeled cells, which were then seeded into either collagen hydrogels or poly(D, L-lactide-coglycolide) (PLGA) encapsulating bone morphogenetic protein-2 (BMP-2)-releasing collagen hydrogels (as shown in Figure 2A). The RGD-binding sites of cell-surface mechanoreceptors (i.e., integrins) play an important role in transferring the external stimulus into the intracellular cytoskeleton (Cartmell et al., 2002). It was worth mentioning that hydrogels containing TREK1 or RGD-MNP labeled hMSCs showed significantly more mineralization than controls; moreover, hydrogels containing functionalized MNPs and BMP-2 had thicker and more numerous mineralized domains compared to those without BMP-2 (Figures 2B–K). In order to maintain the stem cell phenotype and multiple differentiation potential ex vivo, a magnetic cell levitation method was used to label the MSCs with MNPs and then fabricated multicellular spheroids, which were implanted into type I collagen to form a magnetic hydrogel. Biological analyses showed that the 3D spheroid hydrogel system retained the functionality of MSCs, maintained the expression of stem cell markers, produced hematopoietic factors, and decreased cell-cycle progression genes, which could be able to establish an attractive platform for osteogenesis and drug delivery (Lewis et al., 2017).

FIGURE 2
www.frontiersin.org

Figure 2. The enhancement of hMSCs prelabeled with either RGD-modified or TREK-antibody-modified MNPs in hydrogel for biomineralization. (A) Schematic illustration of the experiment. (A1) The integrins or the TREK1 ion channel modified MNPs were used to label hMSCs. (A2) The MNP-labeled hMSCs were either transplanted into an ex vivo chick femur model (A2i) or incorporated into a hydrogel (A2ii). (A3) BMP-2-releasing PLGA microspheres were fabricated using an emulsion method. (A4) The combined effect of labeled cells and BMP-2-releasing hydrogels was studied. (B–E) Bone mineralization sites (green) within the cartilaginous chick fetal femur (white) were used to express the location and extent of mineralization. The experiments were conducted as follows: sham injection (B), magnetic stimulation alone (C), injection of hMSCs alone (D), and injection of hMSCs followed by magnetic stimulation (E). (F,G) The RGD tripeptide (F) or TREK-antibody (G) modified MNPs led to mineralization. (H,I) The injection of hMSCs prelabeled with either RGD-modified (H) or TREK-antibody-modified (I). MNPs in femurs showed more alkaline phosphatase activity (J) and the greatest extent of mineralization (K). *p < 0.05. Scale bar = 1 mm [reproduced with permission from Henstock et al. (2014), Copyright 2014 John Wiley and Sons].

Critical size bone defects need adequate vascularization for reconstruction (Genova et al., 2016). Therefore, Filippi et al. (2019) designed cell-loading magnetic nanocomposite hydrogels by incorporation of human adipose tissue derived stromal vascular fraction (SVF) cells into polyethylene glycol (PEG)-MNPs-based PEG hydrogels, which were further examined to enhance the activity of alkaline phosphatase (ALP), to increase the expression of osteogenesis-related genes, and to improve the mineralized extracellular matrix (ECM) formation both in vitro and in vivo. The results suggested that magnetically actuated cell-laden hydrogels demonstrated more mineralization and faster vascularization in comparison with MNPs or SMF alone. In addition, the in vitro and in vivo tissue volume examinations showed that this magnetic hydrogel was biodegradable. Further studies are needed to investigate the effect of this construct in an orthotopic bone defect model and in combination with other hard supporting materials (e.g., HAP). Although a previous review has focused on the multifunction of magnetic HAP in nanomedicine application (Mondal et al., 2017), the characteristics involved in the magnetic PEG hydrogels should be tested comprehensively.

Previous studies have shown that the cell activity in the local milieu relies on the spatiotemporal regulation of biophysical and biochemical properties (Lukashev and Werb, 1998), and the ECM plays an important role in this process (Chantre et al., 2019; Ebata et al., 2019; Park et al., 2019; Zhang Z. et al., 2019). The introduction of the ECM into the preparation of hydrogels could mimic the microenvironment for cell behaviors, which is mainly attributed to predetermined hydrogel properties, such as the ultrastructure (Johnson et al., 2011, 2014), stiffness (Massensini et al., 2015; Ghuman et al., 2016), gelation kinetics (Medberry et al., 2013; Wu et al., 2015; Lin et al., 2018), etc. Therefore, the development of mimicked matrices is imperative for the regulation of ECM characteristics that control cellular biology. Abdeen et al. (2016) designed a magnetoactive hydrogel matrix fabricated by incorporating carbonyl iron particles into a polyacrylamide (PAAM) hydrogel, and the elasticity was modulated reversibly by alternating magnetic field from −1.0 to 1.0 T. It was worth mentioning that the storage modulus of the magnetic hydrogel had shown elastic hysteresis. A conditioned medium from MSCs seeded on magnetic hydrogels promoted the tube formation of functional vessels, which provides nutrients, oxygen, and ions for biomineralization (Qiu et al., 2020), suggesting enhanced secretion of proangiogenic factors from MSC loaded hydrogels. Runx2, the most common biomarker as the early osteogenesis, was significantly enhanced when MSCs were seeded on the magnetic hydrogel at day 10.

It is reported that the structural, compositional, and functional complexity of the native interface is present between bone and tendon (Phillips et al., 2008; Seidi et al., 2011), which is particularly mechanosensitive (Klein-Nulend et al., 2005; Chen et al., 2010). Therefore, a magnetic responsive hydrogel containing methacrylated chondroitin sulfate (MA-CS), platelet lysate (PL), and MNPs was fabricated. The preparation of MA-CS MNPs showed a superparamagnetic feature at room temperature and provided methacrylic groups for crosslinking to the hydrogel matrix. Human adipose-derived stem cells (hADSCs) or human tendon-derived cells (hTDCs) were encapsulated into hydrogels, and biological performance was evaluated. It was worth mentioning that the hydrogel possessed a gradient-like 3D structure with two interconnected layers (bone and tendon) and exhibited non-degradation without magnetic field during the testing period (20 days). Both hTDCs and hADSCs were viable within this construct. Interestingly, under magnetic field stimulation, the magnetic hydrogel showed degradation, and the cellular response of hADSCs on bone-mimicking units and hTDCs on tendon-mimicking units was modulated (Silva et al., 2018). Later on, a new gradient material was designed by incorporating continuous gradients of BMP-2 loaded glycosylated MNPs into agarose hydrogels with an external magnetic field via the grafting-onto method. Then hMSCs were included in this MNP-gradient magnetic hydrogel (schematic illustration is shown in Figures 3A,B). After a 28-day culture in vitro, the cumulative release of BMP-2 in hydrogels showed sustained diffusion-driven release kinetics (Figure 3C); osteogenic genes and chondrogenic genes were both significantly increased in comparison with those at day 0 (Figures 3D,E). Moreover, dense calcium-rich nodes (Figure 3F) and two distinct calcium phosphate types (HAP and β-tricalcium phosphate, β-TCP) (Figure 3G) were observed in the bone region of the hydrogel, suggesting that more mineralization could be produced in this new MNP-gradient hydrogel and providing a novel platform for osteochondral tissue engineering (Li et al., 2018). However, this work was performed in vitro, and the overall mechanical properties and the biodegradation rate of this magnetic hydrogel should be tested in vivo in the future.

FIGURE 3
www.frontiersin.org

Figure 3. The improvement of aligned glycosylated MNPs within an hMSC-laden agarose hydrogel in the osteochondral tissue engineering. (A) MNPs were incorporated into heparin to develop a glycosylated group. (B) Aligned glycosylated MNPs within an hMSC-laden agarose hydrogel was fabricated by an external magnetic field. (C) The release of BMP-2 from the magnetic agarose hydrogel was analyzed over 28 days. ΔCt values for the bone region (black), the cartilage region (gray), and a day 0 control (red) for genes associated with (D) cartilage formation and (E) bone formation (mean ± 95% confidence intervals, N = 3, n = 3 for 28 day constructs. N = 3, n = 1 for day 0 control; the COL2A1 gene was only detected in one donor on day 0, but was detected for all 28-day samples). (F) Calcium nodules (red) stained by Alizarin Red S and sulfated glycosaminoglycan (blue) stained by Alcian Blue dying indicated mineralization at the bone end. (G) Roman microscopy of the cells (red), HAP (green), and β-TCP (blue) suggested mineralization at the bone end. Scale bar = 100 μm. *p < 0.05, **p < 0.01, and ***p < 0.001 [reproduced with permission from Li et al. (2018), Copyright 2018 Elsevier].

In order to evaluate various osteoblastic functions such as collagen formation, cell adhesion, and osteocalcin production, MG-63 as an experimental model was conducted by Yuan et al. (2018). In this literature, a multifunctional biomimetic 3D magnetic hydrogel was fabricated by incorporating MG-63 cells and MNPs into native collagen hydrogels. In the presence of SMFs, the proliferation, ALP formation, and mineralization of MG-63 cells were significantly enhanced; moreover, the osteogenic related gene expression of Runx2, BMP-2, and BMP-4 was also increased, indicating that this 3D magnetic hydrogel was a biocompatible platform for osteogenesis.

Due to the promotion of blood supply, regulation of bone metabolism, improvement of osteogenesis, and formation of new bone by appropriate temperature stimulation (Zanchetta and Bogado, 2001; Chen et al., 2013), appropriate hyperthermia on magnetic hydrogels highlights potential treatment for bone regeneration. Cao et al. (2018) designed a magnetic hydrogel containing MNPs and chitosan/PEG hydrogel, which showed excellent biocompatibility. It was worth mentioning that the cell viability of MSCs was decreased when the temperature was from 37 to 46°C; moreover, the MSCs could survive at below 46°C, and the growth and morphology had no significant changes. Intriguingly, when the temperature was at 43°C, the MSCs within magnetic hydrogel exhibited good cell viability and the highest ALP activity, which stands for the osteogenic differentiation capability. These findings indicate that magnetic hyperthermia hydrogel could be considered as a potential therapeutic strategy for bone regeneration after bone cancer excision.

Applications in Cartilage Tissue Engineering

Articular cartilage injury is one of the most usual types of orthopedic disease in the clinic and is challenging for surgeons because of the limitation of self-repair for articular cartilage. Recent endeavors of magnetic hydrogels have been developed to deal with the above issue. A previous study of magnetic hydrogels for potential cartilage tissue engineering was performed by Zhang et al. (2015). In this study, PVA modified Fe3O4 MNPs were first synthesized via the grafting-on method and then mixed with a hybrid hydrogel (MagGel) composed of HA, type II collagen, and PEG by mechanical dispersion. The in vitro degradation test showed that this MagGel lost structure integrity after 21 days' incubation at 37°C. It was worth mentioning that magnetic nanocomposite hydrogel showed similar microstructure and chemical components in comparison with natural hyaline cartilage and was able to support bone mesenchymal stem cells' (BMSCs) behavior in vitro, as shown in Figure 4. However, the combination of magnetic hydrogel and magnetic stimulation on cell functions was not evaluated, and the efficacy of magnetic hydrogels on cartilage tissue engineering in vivo should be further analyzed. Moreover, HA or chondroitin sulfate (CS), the two important biomolecules of polysaccharides, was used to modify the above-mentioned HAP/Fe2O3/PVA hydrogel and demonstrated the promotion of chondrocyte attachment and proliferation (Hou et al., 2015).

FIGURE 4
www.frontiersin.org

Figure 4. The characteristics of the magnetic hydrogel. (A) General view of the magnetic hydrogel. The magnified image was obtained by a scanning electron microscope (SEM). (B) Magnetic responses of the magnetic hydrogel. Blue arrows suggested the hydrogel movement orientation before the next time point. (C) Representative images of F-actin (green) by fluorescence microscopy and magnetic nanoparticles (black) by light microscopy showed the endocytosis of MNPs by BMSCs [reproduced with permission from Zhang et al. (2015), Copyright 2015 American Chemical Society].

Later on, an advanced smart cell-embedded magnetic hydrogel was designed. The commercially available, biocompatible, and dextran-modified MNPs from Micromod® company were integrated into a tri-layered agarose scaffold to fabricate a ferrogel by using a blending method. The resulting magnetic hydrogel exhibited a depth-dependent mechanics and was capable of improving cell viability and sustaining the chondrocytes in culture upon magnetic stimulation (Brady et al., 2017). Furthermore, a multilayered mimicked tissue with mimetic architecture consisted of streptavidin-coated magnetic particles (diameter between 10 and 12 nm), agarose, and type I collagen was printed upon a magnetic field by using 3D bioprinting. The new magnetic hydrogel showed similar architecture to cartilage native tissues in comparison to a conventional, single-layered 3D matrix and expressed markedly more chondrocyte-related gene in vitro (Betsch et al., 2018). These novel magnetic hydrogels highlighted the potential application of location-specific cartilage replacement tissue, and further studies could be needed to assess the concentration of MNPs and the matrix, the intensity and type of magnetic fields, modification of MNPs with biological growth factors, and the repair efficacy of the damaged cartilage in vivo.

The stem cell therapy has been introduced into the treatment of cartilage injury (Toh et al., 2014; Hu et al., 2017); however, the chondrogenic differentiation of BMSCs requires the addition of an important cytokine. The currently available cytokines, such as transforming growth factor-β3 and BMP, have the limitation of short half-life time (Stowers et al., 2013) and less mineralization (Ren et al., 2016), respectively. Kartogenin (KGN) is a small molecule compound and is capable of inducing BMSC differentiation into chondrocytes (Xu et al., 2015). Therefore, KGN was grafted onto the surface of MNPs and then mixed with cellulose nanocrystal/dextran (CNC/Dex) hydrogel. The in vitro and in vivo experiments showed that KGN-MNPs incorporated hydrogel exhibited a long-term sustained release of KGN, recruited host cells, and induced chondrogenic differentiation of BMSCs, thus improving in situ cartilage regeneration (Yang et al., 2019).

Due to the high biocompatibility, strong toughness, and cell adhesive ability of nano-HAP, many kinds of literatures have reported that nano-HAP possessed effective repair capability for articular cartilage (Reddi et al., 2011; Zhou et al., 2015; Zhu et al., 2017). A magnetic nanocomposite hydrogel made of nano-HAP particles, Fe2O3 nanoparticles, and PVA in a ratio of 1:0.5:10 was fabricated by using the ultrasonic dispersion approach and then lyophilized by a freeze–thawing crosslinking process, as shown in Figure 5A. Thanks to the Fe2O3 nanoparticles within the hydrogel, the degradation experiment showed a relatively intermediate and slow mass loss rate. Moreover, the viability of BMSCs in the magnetic hydrogel had no significant change compared to BMSCs alone (Figure 5B), and the expression of chondrocyte-related genes was significantly stimulated, as shown in Figure 5C (Huang J. et al., 2018).

FIGURE 5
www.frontiersin.org

Figure 5. The cell viability and the increased chondrogenesis-related genes in BMSCs within the magnetic hydrogel. (A) Schematic diagram of the fabrication of the magnetic hydrogel with nano-HAP particles, Fe2O3 nanoparticles, and PVA in a ratio of 1:0.5:10. (B) Cell viability of BMSCs alone, BMSCs inside PVA hydrogel, and BMSCs within magnetic hydrogel was analyzed by the CCK-8 experiment. (C) Chondrogenesis-related genes, such as SOX9, Aggrecan, and COL2A1, were analyzed by quantitative real-time polymerase chain reaction (PCR). Data were presented as means ± standard deviations. **p < 0.01 and *p < 0.05 vs. control (BMSCs cultured in medium) [reproduced with permission from Huang J. et al. (2018), Copyright 2018 American Chemical Society].

Applications in Neural Tissue Engineering

Neural tissue damages caused by either neurodegenerative diseases or high-energy trauma greatly affect the patients' quality of life worldwide. The mammalian neuronal cells show the limitation of regrowth performance and functional recovery, presenting a critical clinical challenge for surgeons (Yi et al., 2018; Zhang P.-X. et al., 2019). Most endeavors have been conducted to create a modified microenvironment for improving neural regeneration by supportive tissues and scaffolds. It has been reported that directly guiding the regenerated neurite outgrowth is able to promote neuronal regeneration and functional recovery (Huang L. et al., 2018; Shahriari et al., 2019). A hydrogel matrix containing MNPs and collagen hydrogel was designed, and then an external magnetic field was used to control the alignment of the collagen fibers remotely. After 7-day culture, neurons within a 3D aligned magnetic hydrogel complex exhibited good cell viability and more elongations and more directionality in comparison with those of without fiber alignment, indicating that 3D aligned magnetic hydrogels open up a promising possibility for directional neuronal regeneration (Antman-Passig and Shefi, 2016).

In order to rebuild the anisotropic architectures of the ECM, which support and instruct cells for neural regeneration, most aligned nanofibers with appropriate physical and biological properties have been tailored using electrospinning (Li et al., 2004; Corey et al., 2007; Ginestra, 2019; Hou et al., 2019; Idini et al., 2019; Hazeri et al., 2020). Omidinia-Anarkoli et al. (2017) developed a simple but effective strategy to create a novel “Anisogel” containing short, magnetically inspired poly(lactide-co-glycolide) (PLGA) fibers with evenly distributed elements by using a high-throughput electrospinning/micro-cutting approach, as shown in Figures 6A–E. Nerve cells attached well and extended unidirectionally within the “Anisogel” compared to that without fibers or oriented fibers, as shown in Figures 6F–I. Meanwhile, the neurons within the aligned magnetic hydrogel exhibited spontaneous electrical potential by triggering calcium signals, as shown in Figures 6J,K. Later on, magnetic responsive poly-L-lactic acid (PLLA) fibers were prepared by electrospinning and then injecting into a collagen or fibrinogen hydrogel solution. The resulting alignment of MNPs-PLLA fibers was obtained using an external magnetic field. This aligned electrospun fibers within hydrogels provided directional guidance to neurons, and the average length of neurites from dorsal root ganglions (DRGs) on magnetic fibers was significantly longer than those without MNP addition.

FIGURE 6
www.frontiersin.org

Figure 6. The preparation of the Anisogels and its effect on DRG neurites. (A) Schematic illustration of the Anisogel preparation: step I, aligned fibers were electrospun on a parallel plate; step II, the resulting fibers were rinsed with distilled water to wash off redundant gels; step III, random short fibers were added into the hydrogel precursor; step IV, Anisogels were obtained by applying an external magnetic field. (B) Representative images of aligned PLGA fibers by SEM. Scale bar = 50 μm. (C) The average diameter of 50 μm in short fibers was observed by SEM. Scale bar = 50 μm. Representative images of magnetic fibers within hydrogels by a microscope without magnetic field exposure (D) and with 100 mT of magnetic field exposure (E). Scale bars = 100 μm. (F) DRG extension in Anisogels. Scale bar = 500 μm. (G) A magnified image of DRG extension in Anisogels. Scale bar = 100 μm. (H) The length of neurite extensions was quantified. (I) The angular distribution of neurite extensions of single neuron. (J) Neurons were cultured within the aligned magnetic hydrogel. Red arrows indicated the calcium signal direction, while green arrows represented fibers. A solid circle indicated a maintained or increasing signal. (K) Normalized quantification of the calcium signals in the aligned magnetic hydrogel. *p < 0.05 [reproduced with permission from Omidinia-Anarkoli et al. (2017), Copyright 2017 John Wiley and Sons].

Due to the type, severity, and post-injury time of trauma, an injectable hydrogel matrix with minimal invasion and suitable elasticity for the regeneration of various damaged tissues has been developed (Yu and Ding, 2008; Macaya and Spector, 2012; Cheng et al., 2013; Li et al., 2014, 2015). Therefore, the rod-shaped MNP-incorporated microgels were formed, then dispersed in a biocompatible gel precursor, organized unidirectional alignments under a weak external magnetic field exposure, and finally developed a magnetoresponsive hydrogel “Anisogel.” Primary DRGs inside the Anisogels with 3 vol% microgels revealed a clear difference in the orientation of neurite outgrowth in comparison with those random microgels. In addition, fibroblasts cultured on this Anisogel showed no significant difference in cytotoxicity compared with that cultured in a medium (Rose et al., 2017). These findings were performed in vitro; therefore, further studies are needed to be conducted in vivo to evaluate the efficacy of neurite regeneration and functional recovery in vivo by the injection of the magnetic hydrogel system.

Due to the similar biophysical and biochemical features of HA to the natural ECM of the spinal cord and brain (Bignami et al., 1993), a 3D magnetic HA hydrogel was synthesized by the magnetic microparticles, 4-arm-PEG-vinylsulfone, and thiolated HA. The resulting hydrogels had similar storage modulus as the spinal cord, and primary DRG neurons inside the magnetic hydrogels with magnetic fields showed healthy morphology, with no significant difference in cell viability compared to other groups. Interestingly, the calcium influx in DRG neurons was activated via mechanosensitive TRPV4 and PIEZO2 channels under acute magnetic exposure, and the expression of PIEZO2 was reduced when DRG neurons were stimulated by chronic magnetic exposure. This tailored magnetic biomaterial provided a general strategy for the regulation of different types of cells under remote magnetic stimulation (Tay et al., 2018). Moreover, a recent study has demonstrated that a biomimetic spinal cord structure was printed by a microscale continuous projection printing method (Figure 7), and this hydrogel loaded with neural progenitor cells was capable of promoting axon regeneration in a complete spinal cord injury model in vivo (Koffler et al., 2019), providing a promising strategy in the design of novel magnetic hydrogels in the neural tissue engineering.

FIGURE 7
www.frontiersin.org

Figure 7. Schematic diagram of 3D printing by a microscale continuous projection printing method [reproduced with permission from Koffler et al. (2019), Copyright 2019 Springer Nature].

Applications in Other Organs

Besides the bone, cartilage, and nerve organs, magnetic hydrogels are also introduced into other organs, such as the heart, skin, and muscle, in order to evaluate the therapeutic potential. Namdari and Eatemadi (2017) designed a magnetic hydrogel by dissolving Fe3O4 and curcumin into the N-isopropylacrylamide-methacrylic acid (NIPAAM-MAA) hydrogel. The resulting magnetic hydrogel nanocomposite was able to reduce the doxorubicin-induced cardiac toxicity and hold the cardioprotective capability. Cezar et al. (2016) fabricated a ferrogel scaffold by using RGD peptides modified alginate and iron oxide. The magnetic ferrogel showed fatigue resistance and in combination with magnetic stimulation (6,510 Gauss, 5 min at 1 Hz every 12 h) could mechanically activate and promote severely injured muscle tissue regeneration. Rose et al. (2018) developed a magnetic hybrid hydrogel by blending the MNPs into the Gly-Arg-Gly-Asp-Ser-Pro-Cys (GRGDSPC) modified six-arm-PEG gel for fibroblast alignment, which is crucial for the wound healing.

Injectable Magnetic Hydrogel's Application in Tissue Engineering

Recently, the magnetic hydrogels as injectable systems have displayed great potential for tissue repair and magnetic drug targeting. Various kinds of cells and molecules can be encapsulated homogeneously into the magnetic hydrogels and then targeted to the pathological sites with minimal invasiveness (Wu et al., 2018; Chen X. et al., 2019b; Shi et al., 2019; Wu H. et al., 2019; Xu et al., 2019). Several polymers, including ionic-response polymers (e.g., sodium alginate), natural biocompatible polymers (e.g., chitosan), and synthetic polymers (e.g., polyacrylic acid), conjugated with the magnetic particles have been used to fabricate the injectable hydrogels for therapeutic applications (Jalili et al., 2017; Hu et al., 2018; Amini-Fazl et al., 2019). These magnetic hydrogels could be guided to the diseased sites via external magnetic fields and exert a drug release influence there. Meanwhile, this kind of magnetic hydrogel is mainly targeted for the cancer therapy due to the hyperthermia effect under the applied magnetic field.

The Metabolism of Magnetic Particles From the Magnetic Biomaterials

Although numerous studies have shown that magnetic biomaterials exhibited biocompatibility both in vitro and in vivo, the cytotoxicity and long-term fate of magnetic particles embedded within the magnetic hydrogels in vivo must be taken for consideration. No identical criteria have been made to evaluate this important issue of magnetic hydrogels since the fabrication process and physicochemical properties vary in many aspects. The Food and Drug Administration (FDA) in the United States had approved several MNPs in the clinical applications, such as the treatment of anemia caused by chronic kidney disease and the magnetic resonance imaging, and these MNPs could be removed quickly by the liver (Laconte et al., 2005; Ventola, 2017). The clearance of magnetic particles in vivo depends on the size of the particle. In detail, particles smaller than 5.5 nm could be removed quickly through the kidney (Sun et al., 2008), particles up to 200 nm could be sequestered by phagocytes of the spleen (Chen and Weiss, 1973), and particles larger than 5 μm could be cleared via the lymphatic system (Arruebo et al., 2007). In addition, magnetic fields have proven to control the anisotropic feature, constitution, and the degradation rate in the magnetic hydrogels (Huang J. et al., 2018; Silva et al., 2018). All these factors are crucial for the released amounts of magnetic particles from the magnetic constructs and the impact on organs. More efforts are needed to develop more controllable magnetic hydrogels for in vivo applications.

Conclusions and Perspectives

The magnetically responsive smart hydrogels have emerged as an immensely potential biomaterial for developing bioaligned actuators. Benefiting from their intriguing features, including but not limited to quick response, mimetic native tissues, appealing mechanical properties, and biocompatibility, magnetic hydrogels have undergone unparalleled advances in biomedical fields, such as bone, cartilage, nerve, heart, muscle tissue engineering, and so on. However, the properties of magnetic particles, such as size, shape, composition, crystallinity, and so on, should be further modified in order to avoid overheating when cell-laden hydrogels are assembled. Meanwhile, the hydrogel matrices used in magnetic hydrogels need to be further evaluated by mimicking the native architectures of tissues and organs, which holds great potential for the preclinical treatment. Therefore, combined strategies should be developed to create more and more smart hydrogels in tissue engineering (Figure 8).

FIGURE 8
www.frontiersin.org

Figure 8. Schematic illustration of combined strategies for the development of magnetic hydrogels in tissue engineering (Created with BioRender.com).

Future perspectives should focus on dealing with the existing difficulties. In addition, more attention should be taken into consideration in evaluating the magnetic hydrogels' pharmacokinetics/toxicokinetics, metabolism, biodegradation in vivo, and so on, which are of great significance in the applications of tissue engineering.

Author Contributions

PT and ZL initiated the project. ZL, JL, XC, XW, LZ, and PT searched the data and wrote, revised, and completed the manuscript.

Funding

This literature was supported by the National Key Research and Development Program of China (2016YFC1102005), the National Defense Scientific and Technological Innovation Special Zone (18-163-12-ZT-003-016-01), the National Natural Science Foundation of China (81702121, 81702153, and 8170090601), the Military Medical Science and Technology Youth Development Program (19QNP052), the Scientific Research Project of Capital Health Development (2018-4-5014), the Subsidiary of PLA Major Project (AWS17J004), the Clinical Research Support Fund of PLA general hospital (2017FC-TSYS-2006), and the China Postdoctoral Science Foundation funded project (2017M613397 and 2019M664007).

Conflict of Interest

The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.

References

Abdeen, A. A., Lee, J., Bharadwaj, N. A., Ewoldt, R. H., and Kilian, K. A. (2016). Temporal modulation of stem cell activity using magnetoactive hydrogels. Adv. Healthc. Mater. 5, 2536–2544. doi: 10.1002/adhm.201600349

PubMed Abstract | CrossRef Full Text | Google Scholar

Ahmad, T., Byun, H., Lee, J., Madhurakat Perikamana, S. K., Shin, Y. M., Kim, E. M., et al. (2019). Stem cell spheroids incorporating fibers coated with adenosine and polydopamine as a modular building blocks for bone tissue engineering. Biomaterials 230:119652. doi: 10.1016/j.biomaterials.2019.119652

PubMed Abstract | CrossRef Full Text | Google Scholar

Amini-Fazl, M. S., Mohammadi, R., and Kheiri, K. (2019). 5Fluorouracil loaded chitosan/polyacrylic acid/Fe3O4 magnetic nanocomposite hydrogel as a potential anticancer drug delivery system. Int. J. Biol. Macromol. 132, 506–513. doi: 10.1016/j.ijbiomac.2019.04.005

PubMed Abstract | CrossRef Full Text | Google Scholar

Antman-Passig, M., and Shefi, O. (2016). Remote magnetic orientation of 3D collagen hydrogels for directed neuronal regeneration. Nano Lett. 16, 2567–2573. doi: 10.1021/acs.nanolett.6b00131

PubMed Abstract | CrossRef Full Text | Google Scholar

Arias, S. L., Shetty, A., Devorkin, J., and Allain, J. P. (2018). Magnetic targeting of smooth muscle cells in vitro using a magnetic bacterial cellulose to improve cell retention in tissue-engineering vascular grafts. Acta Biomater. 77, 172–181. doi: 10.1016/j.actbio.2018.07.013

PubMed Abstract | CrossRef Full Text | Google Scholar

Arruebo, M., Fernández-Pacheco, R., Ibarra, M. R., and Santamaría, J. (2007). Magnetic nanoparticles for drug delivery. Nanotoday 2, 22–32. doi: 10.1016/S1748-0132(07)70084-1

CrossRef Full Text | Google Scholar

Bannerman, A. D., Li, X., and Wan, W. (2017). A 'degradable' poly(vinyl alcohol) iron oxide nanoparticle hydrogel. Acta Biomater. 58, 376–385. doi: 10.1016/j.actbio.2017.05.018

PubMed Abstract | CrossRef Full Text | Google Scholar

Barrow, M., Taylor, A., Fuentes-Caparros, A. M., Sharkey, J., Daniels, L. M., Mandal, P., et al. (2017). SPIONs for cell labelling and tracking using MRI: magnetite or maghemite? Biomater. Sci. 6, 101–106. doi: 10.1039/C7BM00515F

CrossRef Full Text | Google Scholar

Betsch, M., Cristian, C., Lin, Y. Y., Blaeser, A., Schoneberg, J., Vogt, M., et al. (2018). Incorporating 4D into bioprinting: real-time magnetically directed collagen fiber alignment for generating complex multilayered tissues. Adv. Healthc. Mater. 7:e1800894. doi: 10.1002/adhm.201800894

PubMed Abstract | CrossRef Full Text | Google Scholar

Bignami, A., Hosley, M., and Dahl, D. (1993). Hyaluronic acid and hyaluronic acid-binding proteins in brain extracellular matrix. Anat. Embryol. 188, 419–433. doi: 10.1007/BF00190136

PubMed Abstract | CrossRef Full Text | Google Scholar

Bouyer, M., Guillot, R., Lavaud, J., Plettinx, C., Olivier, C., Curry, V., et al. (2016). Surface delivery of tunable doses of BMP-2 from an adaptable polymeric scaffold induces volumetric bone regeneration. Biomaterials 104, 168–181. doi: 10.1016/j.biomaterials.2016.06.001

PubMed Abstract | CrossRef Full Text | Google Scholar

Bowser, D., and Moore, M. J. (2019). Biofabrication of neural microphysiological systems using magnetic spheroid bioprinting. Biofabrication. doi: 10.1088/1758-5090/ab41b4

PubMed Abstract | CrossRef Full Text | Google Scholar

Brady, M. A., Talvard, L., Vella, A., and Ethier, C. R. (2017). Bio-inspired design of a magnetically active trilayered scaffold for cartilage tissue engineering. J. Tissue Eng. Regen. Med. 11, 1298–1302. doi: 10.1002/term.2106

PubMed Abstract | CrossRef Full Text | Google Scholar

Brito-Pereira, R., Correia, D. M., Ribeiro, C., Francesko, A., Etxebarria, I., Pérez-Álvarez, L., et al. (2018). Silk fibroin-magnetic hybrid composite electrospun fibers for tissue engineering applications. Compos. Part B Eng. 141, 70–75. doi: 10.1016/j.compositesb.2017.12.046

CrossRef Full Text | Google Scholar

Cao, Z., Wang, D., Li, Y., Xie, W., Wang, X., Tao, L., et al. (2018). Effect of nanoheat stimulation mediated by magnetic nanocomposite hydrogel on the osteogenic differentiation of mesenchymal stem cells. Sci. China Life Sci. 61, 448–456. doi: 10.1007/s11427-017-9287-8

PubMed Abstract | CrossRef Full Text | Google Scholar

Cartmell, S. H., Dobson, J., Verschueren, S. B., and El Haj, A. J. (2002). Development of magnetic particle techniques for long-term culture of bone cells with intermittent mechanical activation. IEEE Trans. Nanobioscience 1, 92–97. doi: 10.1109/TNB.2002.806945

PubMed Abstract | CrossRef Full Text | Google Scholar

Cerqueira, S. R., Lee, Y. S., Cornelison, R. C., Mertz, M. W., Wachs, R. A., Schmidt, C. E., et al. (2018). Decellularized peripheral nerve supports schwann cell transplants and axon growth following spinal cord injury. Biomaterials 177, 176–185. doi: 10.1016/j.biomaterials.2018.05.049

PubMed Abstract | CrossRef Full Text | Google Scholar

Ceylan, H., Yasa, I. C., Yasa, O., Tabak, A. F., Giltinan, J., and Sitti, M. (2019). 3D-printed biodegradable microswimmer for theranostic cargo delivery and release. ACS Nano 13, 3353–3362. doi: 10.1021/acsnano.8b09233

PubMed Abstract | CrossRef Full Text | Google Scholar

Cezar, C. A., Roche, E. T., Vandenburgh, H. H., Duda, G. N., Walsh, C. J., and Mooney, D. J. (2016). Biologic-free mechanically induced muscle regeneration. Proc. Natl. Acad. Sci. U.S.A. 113, 1534–1539. doi: 10.1073/pnas.1517517113

PubMed Abstract | CrossRef Full Text | Google Scholar

Chantre, C. O., Gonzalez, G. M., Ahn, S., Cera, L., Campbell, P. H., Hoerstrup, S. P., et al. (2019). Porous biomimetic hyaluronic acid and extracellular matrix protein nanofiber scaffolds for accelerated cutaneous tissue repair. ACS Appl. Mater. Interfaces 11, 45498–45510. doi: 10.1021/acsami.9b17322

PubMed Abstract | CrossRef Full Text | Google Scholar

Chen, H., Qin, Z., Zhao, J., He, Y., Ren, E., Zhu, Y., et al. (2019). Cartilage-targeting and dual MMP-13/pH responsive theranostic nanoprobes for osteoarthritis imaging and precision therapy. Biomaterials 225:119520. doi: 10.1016/j.biomaterials.2019.119520

PubMed Abstract | CrossRef Full Text | Google Scholar

Chen, J., Shi, Z. D., Ji, X., Morales, J., Zhang, J., Kaur, N., et al. (2013). Enhanced osteogenesis of human mesenchymal stem cells by periodic heat shock in self-assembling peptide hydrogel. Tissue Eng. Part A 19, 716–728. doi: 10.1089/ten.tea.2012.0070

PubMed Abstract | CrossRef Full Text | Google Scholar

Chen, J. H., Liu, C., You, L., and Simmons, C. A. (2010). Boning up on wolff's law: mechanical regulation of the cells that make and maintain bone. J. Biomech. 43, 108–118. doi: 10.1016/j.jbiomech.2009.09.016

PubMed Abstract | CrossRef Full Text | Google Scholar

Chen, L. T., and Weiss, L. (1973). The role of the sinus wall in the passage of erythrocytes through the spleen. Blood 41, 529–537. doi: 10.1182/blood.V41.4.529.529

PubMed Abstract | CrossRef Full Text | Google Scholar

Chen, M., Reed, R. R., and Lane, A. P. (2019). Chronic inflammation directs an olfactory stem cell functional switch from neuroregeneration to immune defense. Cell Stem Cell 25, 501–513.e505. doi: 10.1016/j.stem.2019.08.011

PubMed Abstract | CrossRef Full Text | Google Scholar

Chen, X., Fan, M., Tan, H., Ren, B., Yuan, G., Jia, Y., et al. (2019a). Magnetic and self-healing chitosan-alginate hydrogel encapsulated gelatin microspheres via covalent cross-linking for drug delivery. Mater. Sci. Eng. C Mater. Biol. Appl. 101, 619–629. doi: 10.1016/j.msec.2019.04.012

PubMed Abstract | CrossRef Full Text | Google Scholar

Chen, X., Fan, M., Tan, H., Ren, B., Yuan, G., Jia, Y., et al. (2019b). Magnetic and self-healing chitosan-alginate hydrogel encapsulated gelatin microspheres via covalent cross-linking for drug delivery. Mater. Sci. Eng. C Mater. Biol. Appl. 101, 619–629.

PubMed Abstract | Google Scholar

Cheng, J., Amin, D., Latona, J., Heber-Katz, E., and Messersmith, P. B. (2019). Supramolecular polymer hydrogels for drug-induced tissue regeneration. ACS Nano 13, 5493–5501. doi: 10.1021/acsnano.9b00281

PubMed Abstract | CrossRef Full Text | Google Scholar

Cheng, T. Y., Chen, M. H., Chang, W. H., Huang, M. Y., and Wang, T. W. (2013). Neural stem cells encapsulated in a functionalized self-assembling peptide hydrogel for brain tissue engineering. Biomaterials 34, 2005–2016. doi: 10.1016/j.biomaterials.2012.11.043

PubMed Abstract | CrossRef Full Text | Google Scholar

Corey, J. M., Lin, D. Y., Mycek, K. B., Chen, Q., Samuel, S., Feldman, E. L., et al. (2007). Aligned electrospun nanofibers specify the direction of dorsal root ganglia neurite growth. J. Biomed. Mater. Res. A 83, 636–645. doi: 10.1002/jbm.a.31285

PubMed Abstract | CrossRef Full Text | Google Scholar

Cui, L., Zhang, J., Zou, J., Yang, X., Guo, H., Tian, H., et al. (2019). Electroactive composite scaffold with locally expressed osteoinductive factor for synergistic bone repair upon electrical stimulation. Biomaterials 230:119617. doi: 10.1016/j.biomaterials.2019.119617

PubMed Abstract | CrossRef Full Text | Google Scholar

Cui, Z. K., Kim, S., Baljon, J. J., Wu, B. M., Aghaloo, T., and Lee, M. (2019). Microporous methacrylated glycol chitosan-montmorillonite nanocomposite hydrogel for bone tissue engineering. Nat. Commun. 10:3523. doi: 10.1038/s41467-019-11511-3

PubMed Abstract | CrossRef Full Text | Google Scholar

Deng, X., Ren, Y., Hou, L., Liu, W., Jiang, T., and Jiang, H. (2019). Compound-droplet-pairs-filled hydrogel microfiber for electric-field-induced selective release. Small 15:e1903098. doi: 10.1002/smll.201903098

PubMed Abstract | CrossRef Full Text | Google Scholar

Ebata, H., Moriyama, K., Kuboki, T., and Kidoaki, S. (2019). General cellular durotaxis induced with cell-scale heterogeneity of matrix-elasticity. Biomaterials 230:119647. doi: 10.1016/j.biomaterials.2019.119647

PubMed Abstract | CrossRef Full Text | Google Scholar

Fan, C., Shi, J., Zhuang, Y., Zhang, L., Huang, L., Yang, W., et al. (2019). Myocardial-infarction-responsive smart hydrogels targeting matrix metalloproteinase for on-demand growth factor delivery. Adv. Mater. 31:e1902900. doi: 10.1002/adma.201902900

PubMed Abstract | CrossRef Full Text | Google Scholar

Filippi, M., Dasen, B., Guerrero, J., Garello, F., Isu, G., Born, G., et al. (2019). Magnetic nanocomposite hydrogels and static magnetic field stimulate the osteoblastic and vasculogenic profile of adipose-derived cells. Biomaterials 223:119468. doi: 10.1016/j.biomaterials.2019.119468

PubMed Abstract | CrossRef Full Text | Google Scholar

Gao, F., Xie, W., Miao, Y., Wang, D., Guo, Z., Ghosal, A., et al. (2019). Magnetic hydrogel with optimally adaptive functions for breast cancer recurrence prevention. Adv. Healthc. Mater. 8:1900203. doi: 10.1002/adhm.201900203

PubMed Abstract | CrossRef Full Text | Google Scholar

Genova, T., Munaron, L., Carossa, S., and Mussano, F. (2016). Overcoming physical constraints in bone engineering: ‘the importance of being vascularized'. J. Biomater. Appl. 30, 940–951. doi: 10.1177/0885328215616749

PubMed Abstract | CrossRef Full Text | Google Scholar

Ghuman, H., Massensini, A. R., Donnelly, J., Kim, S. M., Medberry, C. J., Badylak, S. F., et al. (2016). ECM hydrogel for the treatment of stroke: characterization of the host cell infiltrate. Biomaterials 91, 166–181. doi: 10.1016/j.biomaterials.2016.03.014

PubMed Abstract | CrossRef Full Text | Google Scholar

Ginestra, P. (2019). Manufacturing of polycaprolactone - graphene fibers for nerve tissue engineering. J. Mech. Behav. Biomed. Mater. 100:103387. doi: 10.1016/j.jmbbm.2019.103387

PubMed Abstract | CrossRef Full Text | Google Scholar

Goncalves, R., Martins, P., Moya, X., Ghidini, M., Sencadas, V., Botelho, G., et al. (2015). Magnetoelectric CoFe2O4/polyvinylidene fluoride electrospun nanofibres. Nanoscale 7, 8058–8061. doi: 10.1039/C5NR00453E

PubMed Abstract | CrossRef Full Text | Google Scholar

Hazeri, Y., Irani, S., Zandi, M., and Pezeshki-Modaress, M. (2020). Polyvinyl alcohol/sulfated alginate nanofibers induced the neuronal differentiation of human bone marrow stem cells. Int. J. Biol. Macromol. 147, 946–953. doi: 10.1016/j.ijbiomac.2019.10.061

PubMed Abstract | CrossRef Full Text | Google Scholar

He, J., Sun, C., Gu, Z., Yang, Y., Gu, M., Xue, C., et al. (2018). Morphology, migration, and transcriptome analysis of schwann cell culture on butterfly wings with different surface architectures. ACS Nano 12, 9660–9668. doi: 10.1021/acsnano.8b00552

PubMed Abstract | CrossRef Full Text | Google Scholar

Henstock, J. R., Rotherham, M., Rashidi, H., Shakesheff, K. M., and El Haj, A. J. (2014). Remotely activated mechanotransduction via magnetic nanoparticles promotes mineralization synergistically with bone morphogenetic protein 2: applications for injectable cell therapy. Stem Cells Transl. Med. 3, 1363–1374. doi: 10.5966/sctm.2014-0017

PubMed Abstract | CrossRef Full Text | Google Scholar

Herberg, S., Mcdermott, A. M., Dang, P. N., Alt, D. S., Tang, R., Dawahare, J. H., et al. (2019). Combinatorial morphogenetic and mechanical cues to mimic bone development for defect repair. Sci. Adv. 5:eaax2476. doi: 10.1126/sciadv.aax2476

PubMed Abstract | CrossRef Full Text | Google Scholar

Hermenegildo, B., Ribeiro, C., Pérez-Álvarez, L., Vilas, J. L., Learmonth, D. A., Sousa, R. A., et al. (2019). Hydrogel-based magnetoelectric microenvironments for tissue stimulation. Colloids Surf. B Biointerfaces 181, 1041–1047. doi: 10.1016/j.colsurfb.2019.06.023

PubMed Abstract | CrossRef Full Text | Google Scholar

Hou, R., Nie, L., Du, G., Xiong, X., and Fu, J. (2015). Natural polysaccharides promote chondrocyte adhesion and proliferation on magnetic nanoparticle/PVA composite hydrogels. Colloids Surf. B Biointerfaces 132, 146–154. doi: 10.1016/j.colsurfb.2015.05.008

PubMed Abstract | CrossRef Full Text | Google Scholar

Hou, R., Zhang, G., Du, G., Zhan, D., Cong, Y., Cheng, Y., et al. (2013). Magnetic nanohydroxyapatite/PVA composite hydrogels for promoted osteoblast adhesion and proliferation. Colloids Surf. B Biointerfaces 103, 318–325. doi: 10.1016/j.colsurfb.2012.10.067

PubMed Abstract | CrossRef Full Text | Google Scholar

Hou, Y., Wang, X., Zhang, Z., Luo, J., Cai, Z., Wang, Y., et al. (2019). Repairing transected peripheral nerve using a biomimetic nerve guidance conduit containing intraluminal sponge fillers. Adv. Healthc. Mater. 8:e1900913. doi: 10.1002/adhm.201900913

PubMed Abstract | CrossRef Full Text | Google Scholar

Hsu, R. S., Chen, P. Y., Fang, J. H., Chen, Y. Y., Chang, C. W., Lu, Y. J., et al. (2019). Adaptable microporous hydrogels of propagating ngf-gradient by injectable building blocks for accelerated axonal outgrowth. Adv. Sci. 6:1900520. doi: 10.1002/advs.201900520

PubMed Abstract | CrossRef Full Text | Google Scholar

Hu, Q., Ding, B., Yan, X., Peng, L., Duan, J., Yang, S., et al. (2017). Polyethylene glycol modified PAMAM dendrimer delivery of kartogenin to induce chondrogenic differentiation of mesenchymal stem cells. Nanomedicine 13, 2189–2198. doi: 10.1016/j.nano.2017.05.011

PubMed Abstract | CrossRef Full Text | Google Scholar

Hu, X., Nian, G., Liang, X., Wu, L., Yin, T., Lu, H., et al. (2019). Adhesive tough magnetic hydrogels with high Fe3O4 content. ACS Appl. Mater. Interfaces 11, 10292–10300. doi: 10.1021/acsami.8b20937

PubMed Abstract | CrossRef Full Text | Google Scholar

Hu, X., Wang, Y., Zhang, L., Xu, M., Zhang, J., and Dong, W. (2018). Magnetic field-driven drug release from modified iron oxide-integrated polysaccharide hydrogel. Int. J. Biol. Macromol. 108, 558–567. doi: 10.1016/j.ijbiomac.2017.12.018

PubMed Abstract | CrossRef Full Text | Google Scholar

Huang, J., Liang, Y., Jia, Z., Chen, J., Duan, L., Liu, W., et al. (2018). Development of magnetic nanocomposite hydrogel with potential cartilage tissue engineering. ACS Omega 3, 6182–6189. doi: 10.1021/acsomega.8b00291

PubMed Abstract | CrossRef Full Text | Google Scholar

Huang, L., Zhu, L., Shi, X., Xia, B., Liu, Z., Zhu, S., et al. (2018). A compound scaffold with uniform longitudinally oriented guidance cues and a porous sheath promotes peripheral nerve regeneration in vivo. Acta Biomater. 68, 223–236. doi: 10.1016/j.actbio.2017.12.010

PubMed Abstract | CrossRef Full Text | Google Scholar

Huang, Q., Zou, Y., Arno, M. C., Chen, S., Wang, T., Gao, J., et al. (2017). Hydrogel scaffolds for differentiation of adipose-derived stem cells. Chem. Soc. Rev. 46, 6255–6275. doi: 10.1039/C6CS00052E

PubMed Abstract | CrossRef Full Text | Google Scholar

Idini, M., Wieringa, P., Rocchiccioli, S., Nieddu, G., Ucciferri, N., Formato, M., et al. (2019). Glycosaminoglycan functionalization of electrospun scaffolds enhances schwann cell activity. Acta Biomater. 96, 188–202. doi: 10.1016/j.actbio.2019.06.054

PubMed Abstract | CrossRef Full Text | Google Scholar

Iqbal, H., Khan, Z. U., Razzaq, A., Khan, N. U., Menaa, B., Khan, B. A., et al. (2019). Fabrication, physical characterizations and in vitro antibacterial activity of cefadroxil-loaded chitosan/poly(vinyl alcohol) nanofibers against Staphylococcus aureus clinical isolates. Int. J. Biol. Macromol. 144, 921–931. doi: 10.1016/j.ijbiomac.2019.09.169

PubMed Abstract | CrossRef Full Text | Google Scholar

Jalili, N. A., Jaiswal, M. K., Peak, C. W., Cross, L. M., and Gaharwar, A. K. (2017). Injectable nanoengineered stimuli-responsive hydrogels for on-demand and localized therapeutic delivery. Nanoscale 9, 15379–15389. doi: 10.1039/C7NR02327H

PubMed Abstract | CrossRef Full Text | Google Scholar

Jiang, B., Yang, J., Rahoui, N., Taloub, N., and Huang, Y. D. (2017). Functional polymer materials affecting cell attachment. Adv. Colloid Interface Sci. 250, 185–194. doi: 10.1016/j.cis.2017.09.002

PubMed Abstract | CrossRef Full Text | Google Scholar

Johnson, T. D., Dequach, J. A., Gaetani, R., Ungerleider, J., Elhag, D., Nigam, V., et al. (2014). Human versus porcine tissue sourcing for an injectable myocardial matrix hydrogel. Biomater. Sci. 2014:60283d. doi: 10.1039/C3BM60283D

PubMed Abstract | CrossRef Full Text | Google Scholar

Johnson, T. D., Lin, S. Y., and Christman, K. L. (2011). Tailoring material properties of a nanofibrous extracellular matrix derived hydrogel. Nanotechnology 22:494015. doi: 10.1088/0957-4484/22/49/494015

PubMed Abstract | CrossRef Full Text | Google Scholar

Kabu, S., Gao, Y., Kwon, B. K., and Labhasetwar, V. (2015). Drug delivery, cell-based therapies, and tissue engineering approaches for spinal cord injury. J. Control. Release 219, 141–154. doi: 10.1016/j.jconrel.2015.08.060

PubMed Abstract | CrossRef Full Text | Google Scholar

Klein-Nulend, J., Bacabac, R. G., and Mullender, M. G. (2005). Mechanobiology of bone tissue. Pathol. Biol. 53, 576–580. doi: 10.1016/j.patbio.2004.12.005

PubMed Abstract | CrossRef Full Text | Google Scholar

Koffler, J., Zhu, W., Qu, X., Platoshyn, O., Dulin, J. N., Brock, J., et al. (2019). Biomimetic 3D-printed scaffolds for spinal cord injury repair. Nat. Med. 25, 263–269. doi: 10.1038/s41591-018-0296-z

PubMed Abstract | CrossRef Full Text | Google Scholar

Laconte, L., Nitin, N., and Bao, G. (2005). Magnetic nanoparticle probes. Mater. Today 8, 32–38. doi: 10.1016/S1369-7021(05)00893-X

CrossRef Full Text | Google Scholar

Lee, S. C., Kwon, I. K., and Park, K. (2013). Hydrogels for delivery of bioactive agents: a historical perspective. Adv. Drug Deliv. Rev. 65, 17–20. doi: 10.1016/j.addr.2012.07.015

PubMed Abstract | CrossRef Full Text | Google Scholar

Lewis, N. S., Lewis, E. E., Mullin, M., Wheadon, H., Dalby, M. J., and Berry, C. C. (2017). Magnetically levitated mesenchymal stem cell spheroids cultured with a collagen gel maintain phenotype and quiescence. J. Tissue Eng. 8:2041731417704428. doi: 10.1177/2041731417704428

PubMed Abstract | CrossRef Full Text | Google Scholar

Li, C., Armstrong, J. P., Pence, I. J., Kit-Anan, W., Puetzer, J. L., Correia Carreira, S., et al. (2018). Glycosylated superparamagnetic nanoparticle gradients for osteochondral tissue engineering. Biomaterials 176, 24–33. doi: 10.1016/j.biomaterials.2018.05.029

PubMed Abstract | CrossRef Full Text | Google Scholar

Li, D., Wang, Y., and Xia, Y. (2004). Electrospinning nanofibers as uniaxially aligned arrays and layer-by-layer stacked films. Adv. Mater. 16, 361–366. doi: 10.1002/adma.200306226

CrossRef Full Text | Google Scholar

Li, J., and Mooney, D. J. (2016). Designing hydrogels for controlled drug delivery. Nat. Rev. Mater. 1:16071. doi: 10.1038/natrevmats.2016.71

PubMed Abstract | CrossRef Full Text | Google Scholar

Li, X., Wang, Y., Li, A., Ye, Y., Peng, S., Deng, M., et al. (2019). A novel pH- and salt-responsive N-succinyl-chitosan hydrogel via a one-step hydrothermal process. Molecules 24:E4211. doi: 10.3390/molecules24234211

PubMed Abstract | CrossRef Full Text | Google Scholar

Li, X., Zhou, J., Liu, Z., Chen, J., Lu, S., Sun, H., et al. (2014). A PNIPAAm-based thermosensitive hydrogel containing SWCNTs for stem cell transplantation in myocardial repair. Biomaterials 35, 5679–5688. doi: 10.1016/j.biomaterials.2014.03.067

PubMed Abstract | CrossRef Full Text | Google Scholar

Li, Y., Fang, X., and Jiang, T. (2015). Minimally traumatic alveolar ridge augmentation with a tunnel injectable thermo-sensitive alginate scaffold. J. Appl. Oral Sci. 23, 215–223. doi: 10.1590/1678-775720140348

PubMed Abstract | CrossRef Full Text | Google Scholar

Li, Z., Chen, H., Li, B., Xie, Y., Gong, X., Liu, X., et al. (2019). Photoresponsive luminescent polymeric hydrogels for reversible information encryption and decryption. Adv. Sci. 6:1901529. doi: 10.1002/advs.201901529

PubMed Abstract | CrossRef Full Text | Google Scholar

Lin, T., Liu, S., Chen, S., Qiu, S., Rao, Z., Liu, J., et al. (2018). Hydrogel derived from porcine decellularized nerve tissue as a promising biomaterial for repairing peripheral nerve defects. Acta Biomater. 73, 326–338. doi: 10.1016/j.actbio.2018.04.001

PubMed Abstract | CrossRef Full Text | Google Scholar

Liu, K., Han, L., Tang, P., Yang, K., Gan, D., Wang, X., et al. (2019). An anisotropic hydrogel based on mussel-inspired conductive ferrofluid composed of electromagnetic nanohybrids. Nano Lett. 19, 8343–8356. doi: 10.1021/acs.nanolett.9b00363

PubMed Abstract | CrossRef Full Text | Google Scholar

Lukashev, M. E., and Werb, Z. (1998). ECM signalling: orchestrating cell behaviour and misbehaviour. Trends Cell Biol. 8, 437–441. doi: 10.1016/S0962-8924(98)01362-2

PubMed Abstract | CrossRef Full Text | Google Scholar

Luo, Y., Wei, X., Wan, Y., Lin, X., Wang, Z., and Huang, P. (2019). 3D printing of hydrogel scaffolds for future application in photothermal therapy of breast cancer and tissue repair. Acta Biomater. 92, 37–47. doi: 10.1016/j.actbio.2019.05.039

PubMed Abstract | CrossRef Full Text | Google Scholar

Macaya, D., and Spector, M. (2012). Injectable hydrogel materials for spinal cord regeneration: a review. Biomed. Mater. 7:012001. doi: 10.1088/1748-6041/7/1/012001

PubMed Abstract | CrossRef Full Text | Google Scholar

Madl, C. M., Lesavage, B. L., Dewi, R. E., Dinh, C. B., Stowers, R. S., Khariton, M., et al. (2017). Maintenance of neural progenitor cell stemness in 3D hydrogels requires matrix remodelling. Nat. Mater. 16, 1233–1242. doi: 10.1038/nmat5020

PubMed Abstract | CrossRef Full Text | Google Scholar

Madl, C. M., Lesavage, B. L., Dewi, R. E., Lampe, K. J., and Heilshorn, S. C. (2019). Matrix remodeling enhances the differentiation capacity of neural progenitor cells in 3D hydrogels. Adv. Sci. 6:1801716. doi: 10.1002/advs.201801716

PubMed Abstract | CrossRef Full Text | Google Scholar

Manjua, A. C., Alves, V. D., Crespo, J. G., and Portugal, C. A. M. (2019). Magnetic responsive PVA hydrogels for remote modulation of protein sorption. ACS Appl. Mater. Interfaces 11, 21239–21249. doi: 10.1021/acsami.9b03146

PubMed Abstract | CrossRef Full Text | Google Scholar

Massensini, A. R., Ghuman, H., Saldin, L. T., Medberry, C. J., Keane, T. J., Nicholls, F. J., et al. (2015). Concentration-dependent rheological properties of ECM hydrogel for intracerebral delivery to a stroke cavity. Acta Biomater. 27, 116–130. doi: 10.1016/j.actbio.2015.08.040

PubMed Abstract | CrossRef Full Text | Google Scholar

Medberry, C. J., Crapo, P. M., Siu, B. F., Carruthers, C. A., Wolf, M. T., Nagarkar, S. P., et al. (2013). Hydrogels derived from central nervous system extracellular matrix. Biomaterials 34, 1033–1040. doi: 10.1016/j.biomaterials.2012.10.062

PubMed Abstract | CrossRef Full Text | Google Scholar

Messing, R., Frickel, N., Belkoura, L., Strey, R., Rahn, H., Odenbach, S., et al. (2011). Cobalt ferrite nanoparticles as multifunctional cross-linkers in PAAm ferrohydrogels. Macromolecules 44, 2990–2999. doi: 10.1021/ma102708b

CrossRef Full Text | Google Scholar

Midgley, A. C., Wei, Y., Li, Z., Kong, D., and Zhao, Q. (2019). Nitric-oxide-releasing biomaterial regulation of the stem cell microenvironment in regenerative medicine. Adv. Mater. 32:e1805818. doi: 10.1002/adma.201805818

PubMed Abstract | CrossRef Full Text | Google Scholar

Moncion, A., Harmon, J. S., Li, Y., Natla, S., Farrell, E. C., Kripfgans, O. D., et al. (2019). Spatiotemporally-controlled transgene expression in hydroxyapatite-fibrin composite scaffolds using high intensity focused ultrasound. Biomaterials 194, 14–24. doi: 10.1016/j.biomaterials.2018.12.011

PubMed Abstract | CrossRef Full Text | Google Scholar

Mondal, S., Manivasagan, P., Bharathiraja, S., Santha Moorthy, M., Kim, H. H., Seo, H., et al. (2017). Magnetic hydroxyapatite: a promising multifunctional platform for nanomedicine application. Int. J. Nanomedicine 12, 8389–8410. doi: 10.2147/IJN.S147355

PubMed Abstract | CrossRef Full Text | Google Scholar

Moore, A. N., and Hartgerink, J. D. (2017). Self-assembling multidomain peptide nanofibers for delivery of bioactive molecules and tissue regeneration. Acc. Chem. Res. 50, 714–722. doi: 10.1021/acs.accounts.6b00553

PubMed Abstract | CrossRef Full Text | Google Scholar

Namdari, M., and Eatemadi, A. (2017). Cardioprotective effects of curcumin-loaded magnetic hydrogel nanocomposite (nanocurcumin) against doxorubicin-induced cardiac toxicity in rat cardiomyocyte cell lines. Artif. Cells Nanomed. Biotechnol. 45, 731–739. doi: 10.1080/21691401.2016.1261033

PubMed Abstract | CrossRef Full Text | Google Scholar

Omidinia-Anarkoli, A., Boesveld, S., Tuvshindorj, U., Rose, J. C., Haraszti, T., and De Laporte, L. (2017). An injectable hybrid hydrogel with oriented short fibers induces unidirectional growth of functional nerve cells. Small. 13:1702207. doi: 10.1002/smll.201702207

PubMed Abstract | CrossRef Full Text | Google Scholar

Park, D., Wershof, E., Boeing, S., Labernadie, A., Jenkins, R. P., George, S., et al. (2019). Extracellular matrix anisotropy is determined by TFAP2C-dependent regulation of cell collisions. Nat. Mater. 19, 227–238. doi: 10.1038/s41563-019-0504-3

PubMed Abstract | CrossRef Full Text | Google Scholar

Phillips, J. E., Burns, K. L., Le Doux, J. M., Guldberg, R. E., and García, A. J. (2008). Engineering graded tissue interfaces. 105, 12170–12175. doi: 10.1073/pnas.0801988105

PubMed Abstract | CrossRef Full Text | Google Scholar

Qiu, P., Li, M., Chen, K., Fang, B., Chen, P., Tang, Z., et al. (2020). Periosteal matrix-derived hydrogel promotes bone repair through an early immune regulation coupled with enhanced angio- and osteogenesis. Biomaterials 227:119552. doi: 10.1016/j.biomaterials.2019.119552

PubMed Abstract | CrossRef Full Text | Google Scholar

Reddi, A. H., Becerra, J., and Andrades, J. A. (2011). Nanomaterials and hydrogel scaffolds for articular cartilage regeneration. Tissue Eng. Part B Rev. 17, 301–305. doi: 10.1089/ten.teb.2011.0141

PubMed Abstract | CrossRef Full Text | Google Scholar

Ren, X., Weisgerber, D. W., Bischoff, D., Lewis, M. S., Reid, R. R., He, T.-C., et al. (2016). Nanoparticulate mineralized collagen scaffolds and BMP-9 induce a long-term bone cartilage construct in human mesenchymal stem cells. Adv. Healthc. Mater. 5, 1821–1830. doi: 10.1002/adhm.201600187

PubMed Abstract | CrossRef Full Text | Google Scholar

Rodkate, N., and Rutnakornpituk, M. (2016). Multi-responsive magnetic microsphere of poly(N-isopropylacrylamide)/carboxymethylchitosan hydrogel for drug controlled release. Carbohydr. Polym. 151, 251–259. doi: 10.1016/j.carbpol.2016.05.081

PubMed Abstract | CrossRef Full Text | Google Scholar

Rose, J. C., Cámara-Torres, M., Rahimi, K., Köhler, J., Möller, M., and De Laporte, L. (2017). Nerve cells decide to orient inside an injectable hydrogel with minimal structural guidance. Nano Lett. 17, 3782–3791. doi: 10.1021/acs.nanolett.7b01123

PubMed Abstract | CrossRef Full Text | Google Scholar

Rose, J. C., Gehlen, D. B., Haraszti, T., Kohler, J., Licht, C. J., and De Laporte, L. (2018). Biofunctionalized aligned microgels provide 3D cell guidance to mimic complex tissue matrices. Biomaterials 163, 128–141. doi: 10.1016/j.biomaterials.2018.02.001

PubMed Abstract | CrossRef Full Text | Google Scholar

Ruehle, M. A., Li, M. A., Cheng, A., Krishnan, L., Willett, N. J., and Guldberg, R. E. (2019). Decorin-supplemented collagen hydrogels for the co-delivery of bone morphogenetic protein-2 and microvascular fragments to a composite bone-muscle injury model with impaired vascularization. Acta Biomater. 93, 210–221. doi: 10.1016/j.actbio.2019.01.045

PubMed Abstract | CrossRef Full Text | Google Scholar

Seidi, A., Ramalingam, M., Elloumi-Hannachi, I., Ostrovidov, S., and Khademhosseini, A. (2011). Gradient biomaterials for soft-to-hard interface tissue engineering. Acta Biomater. 7, 1441–1451. doi: 10.1016/j.actbio.2011.01.011

PubMed Abstract | CrossRef Full Text | Google Scholar

Shahriari, D., Loke, G., Tafel, I., Park, S., Chiang, P. H., Fink, Y., et al. (2019). Scalable fabrication of porous microchannel nerve guidance scaffolds with complex geometries. Adv. Mater. 31:e1902021. doi: 10.1002/adma.201902021

PubMed Abstract | CrossRef Full Text | Google Scholar

Shi, L., Zeng, Y., Zhao, Y., Yang, B., Ossipov, D., Tai, C. W., et al. (2019). Biocompatible injectable magnetic hydrogel formed by dynamic coordination network. ACS Appl. Mater. Interfaces. 11, 46233–46240. doi: 10.1021/acsami.9b17627

PubMed Abstract | CrossRef Full Text | Google Scholar

Silva, E. D., Babo, P. S., Costa-Almeida, R., Domingues, R. M. A., Mendes, B. B., Paz, E., et al. (2018). Multifunctional magnetic-responsive hydrogels to engineer tendon-to-bone interface. Nanomedicine 14, 2375–2385. doi: 10.1016/j.nano.2017.06.002

PubMed Abstract | CrossRef Full Text | Google Scholar

Stowers, R. S., Drinnan, C. T., Chung, E., and Suggs, L. J. (2013). Mesenchymal stem cell response to TGF-β1 in both 2D and 3D environments. Biomater. Sci. 1, 860–869. doi: 10.1039/c3bm60057b

CrossRef Full Text | Google Scholar

Sun, C., Lee, J. S., and Zhang, M. (2008). Magnetic nanoparticles in MR imaging and drug delivery. Adv. Drug Deliv. Rev. 60, 1252–1265. doi: 10.1016/j.addr.2008.03.018

PubMed Abstract | CrossRef Full Text | Google Scholar

Tang, J., Myers, M., Bosnick, K. A., and Brus, L. E. (2003). Magnetite Fe3O4 nanocrystals: spectroscopic observation of aqueous oxidation kinetics. J. Phys. Chem. B 107, 7501–7506. doi: 10.1021/jp027048e

CrossRef Full Text | Google Scholar

Tay, A., Sohrabi, A., Poole, K., Seidlits, S., and Di Carlo, D. (2018). A 3D Magnetic hyaluronic acid hydrogel for magnetomechanical neuromodulation of primary dorsal root ganglion neurons. Adv. Mater. 10:e1800927. doi: 10.1002/adma.201800927

CrossRef Full Text | Google Scholar

Toh, W. S., Foldager, C. B., Pei, M., and Hui, J. H. (2014). Advances in mesenchymal stem cell-based strategies for cartilage repair and regeneration. Stem Cell Rev. Rep. 10, 686–696. doi: 10.1007/s12015-014-9526-z

PubMed Abstract | CrossRef Full Text | Google Scholar

Tóth, I. Y., Veress, G., Szekeres, M., Illés, E., and Tombácz, E. (2015). Magnetic hyaluronate hydrogels: preparation and characterization. J. Magn. Magn. Mater. 380, 175–180. doi: 10.1016/j.jmmm.2014.10.139

CrossRef Full Text | Google Scholar

Van Bemmelen, J. M. (1894). Das hydrogel und das krystallinische hydrat des kupferoxyds. Zeitschrift für anorganische Chemie 5, 466–483. doi: 10.1002/zaac.18940050156

CrossRef Full Text | Google Scholar

Venkataprasanna, K. S., Prakash, J., Vignesh, S., Bharath, G., Venkatesan, M., Banat, F., et al. (2019). Fabrication of chitosan/PVA/GO/CuO patch for potential wound healing application. Int. J. Biol. Macromol. doi: 10.1016/j.ijbiomac.2019.10.029

PubMed Abstract | CrossRef Full Text | Google Scholar

Ventola, C. L. (2017). Progress in nanomedicine: approved and investigational nanodrugs. P T. 42, 742–755.

PubMed Abstract | Google Scholar

Wang, Y., Li, B., Xu, F., Han, Z., Wei, D., Jia, D., et al. (2018). Tough magnetic chitosan hydrogel nanocomposites for remotely stimulated drug release. Biomacromolecules 19, 3351–3360. doi: 10.1021/acs.biomac.8b00636

PubMed Abstract | CrossRef Full Text | Google Scholar

Wang, Y., Li, B., Zhou, Y., and Jia, D. (2009). In situ mineralization of magnetite nanoparticles in chitosan hydrogel. Nanoscale Res. Lett. 4, 1041–1046. doi: 10.1007/s11671-009-9355-1

PubMed Abstract | CrossRef Full Text | Google Scholar

Wei, Z., Volkova, E., Blatchley, M. R., and Gerecht, S. (2019). Hydrogel vehicles for sequential delivery of protein drugs to promote vascular regeneration. Adv. Drug Deliv. Rev. 149-150, 95–106 doi: 10.1016/j.addr.2019.08.005

PubMed Abstract | CrossRef Full Text | Google Scholar

Wichterle, O., and LÍm, D. (1960). Hydrophilic gels for biological use. Nature 185, 117–118. doi: 10.1038/185117a0

CrossRef Full Text | Google Scholar

Wu, C., Huang, J., Chu, B., Deng, J., Zhang, Z., Tang, S., et al. (2019). Dynamic and hierarchically structured networks with tissue-like mechanical behavior. ACS Nano 13, 10727–10736. doi: 10.1021/acsnano.9b05436

PubMed Abstract | CrossRef Full Text | Google Scholar

Wu, H., Liu, L., Song, L., Ma, M., Gu, N., and Zhang, Y. (2019). Enhanced tumor synergistic therapy by injectable magnetic hydrogel mediated generation of hyperthermia and highly toxic reactive oxygen species. ACS Nano 13, 14013–14023. doi: 10.1021/acsnano.9b06134

PubMed Abstract | CrossRef Full Text | Google Scholar

Wu, H., Song, L., Chen, L., Zhang, W., Chen, Y., Zang, F., et al. (2018). Injectable magnetic supramolecular hydrogel with magnetocaloric liquid-conformal property prevents post-operative recurrence in a breast cancer model. Acta Biomater. 74, 302–311. doi: 10.1016/j.actbio.2018.04.052

PubMed Abstract | CrossRef Full Text | Google Scholar

Wu, J., Ding, Q., Dutta, A., Wang, Y., Huang, Y. H., Weng, H., et al. (2015). An injectable extracellular matrix derived hydrogel for meniscus repair and regeneration. Acta Biomater. 16, 49–59. doi: 10.1016/j.actbio.2015.01.027

PubMed Abstract | CrossRef Full Text | Google Scholar

Xie, W., Gao, Q., Guo, Z., Wang, D., Gao, F., Wang, X., et al. (2017). Injectable and self-healing thermosensitive magnetic hydrogel for asynchronous control release of doxorubicin and docetaxel to treat triple-negative breast cancer. ACS Appl. Mater. Interfaces 9, 33660–33673. doi: 10.1021/acsami.7b10699

PubMed Abstract | CrossRef Full Text | Google Scholar

Xu, X., Shi, D., Shen, Y., Xu, Z., Dai, J., Chen, D., et al. (2015). Full-thickness cartilage defects are repaired via a microfracture technique and intraarticular injection of the small-molecule compound kartogenin. Arthritis Res. Ther. 17, 20–20. doi: 10.1186/s13075-015-0537-1

PubMed Abstract | CrossRef Full Text | Google Scholar

Xu, Y., Patsis, P. A., Hauser, S., Voigt, D., Rothe, R., Gunther, M., et al. (2019). Cytocompatible, injectable, and electroconductive soft adhesives with hybrid covalent/noncovalent dynamic network. Adv. Sci. 6:1802077. doi: 10.1002/advs.201802077

PubMed Abstract | CrossRef Full Text | Google Scholar

Yang, W., Zhu, P., Huang, H., Zheng, Y., Liu, J., Feng, L., et al. (2019). Functionalization of novel theranostic hydrogels with kartogenin-grafted USPIO nanoparticles to enhance cartilage regeneration. ACS Appl. Mater. Interfaces. doi: 10.1021/acsami.9b12288

PubMed Abstract | CrossRef Full Text | Google Scholar

Yang, Y. N., Lu, K. Y., Wang, P., Ho, Y. C., Tsai, M. L., and Mi, F. L. (2020). Development of bacterial cellulose/chitin multi-nano fi bers based smart films containing natural active microspheres and nanoparticles formed in situ. Carbohydr. Polym. 228:115370. doi: 10.1016/j.carbpol.2019.115370

PubMed Abstract | CrossRef Full Text | Google Scholar

Yi, J., Jiang, N., Li, B., Yan, Q., Qiu, T., Swaminatha Iyer, K., et al. (2018). Painful terminal neuroma prevention by capping PRGD/PDLLA conduit in rat sciatic nerves. Adv. Sci. 5:1700876. doi: 10.1002/advs.201700876

PubMed Abstract | CrossRef Full Text | Google Scholar

Yu, L., and Ding, J. (2008). Injectable hydrogels as unique biomedical materials. Chem. Soc. Rev. 37, 1473–1481. doi: 10.1039/b713009k

PubMed Abstract | CrossRef Full Text | Google Scholar

Yuan, Z., Memarzadeh, K., Stephen, A. S., Allaker, R. P., Brown, R. A., and Huang, J. (2018). Development of a 3D collagen model for the in vitro evaluation of magnetic-assisted osteogenesis. Sci. Rep. 8:16270. doi: 10.1038/s41598-018-33455-2

PubMed Abstract | CrossRef Full Text | Google Scholar

Zanchetta, J. R., and Bogado, C. E. (2001). Raloxifene reverses bone loss in postmenopausal women with mild asymptomatic primary hyperparathyroidism. J. Bone Miner. Res. 16, 189–190. doi: 10.1359/jbmr.2001.16.1.189

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhang, N., Lock, J., Sallee, A., and Liu, H. (2015). Magnetic nanocomposite hydrogel for potential cartilage tissue engineering: synthesis, characterization, and cytocompatibility with bone marrow derived mesenchymal stem cells. ACS Appl. Mater. Interfaces 7, 20987–20998. doi: 10.1021/acsami.5b06939

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhang, P.-X., Han, N., Kou, Y.-H., Zhu, Q.-T., Liu, X.-L., Quan, D.-P., et al. (2019). Tissue engineering for the repair of peripheral nerve injury. Neural Regen. Res. 14, 51–58. doi: 10.4103/1673-5374.243701

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhang, Y., Chen, K., Li, Y., Lan, J., Yan, B., Shi, L. Y., et al. (2019). High-strength, self-healable, temperature-sensitive, MXene-containing composite hydrogel as a smart compression sensor. ACS Appl. Mater. Interfaces. 11, 47350–47357. doi: 10.1021/acsami.9b16078

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhang, Z., Qu, R., Fan, T., Ouyang, J., Lu, F., and Dai, J. (2019). Stepwise adipogenesis of decellularized cellular extracellular matrix regulates adipose tissue-derived stem cell migration and differentiation. Stem Cells Int. 2019:1845926. doi: 10.1155/2019/1845926

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhang, Z. Q., and Song, S. C. (2016). Thermosensitive/superparamagnetic iron oxide nanoparticle-loaded nanocapsule hydrogels for multiple cancer hyperthermia. Biomaterials 106, 13–23. doi: 10.1016/j.biomaterials.2016.08.015

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhao, X., Liu, Y., Shao, C., Nie, M., Huang, Q., Li, J., et al. (2019). Photoresponsive delivery microcarriers for tissue defects repair. Adv Sci. 6:1901280. doi: 10.1002/advs.201901280

PubMed Abstract | CrossRef Full Text | Google Scholar

Zheng, L., Li, C., Huang, X., Lin, X., Lin, W., Yang, F., et al. (2019). Thermosensitive hydrogels for sustained-release of sorafenib and selenium nanoparticles for localized synergistic chemoradiotherapy. Biomaterials 216:119220. doi: 10.1016/j.biomaterials.2019.05.031

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhou, K., Yu, P., Shi, X., Ling, T., Zeng, W., Chen, A., et al. (2019). Hierarchically porous hydroxyapatite hybrid scaffold incorporated with reduced graphene oxide for rapid bone ingrowth and repair. ACS Nano 13, 9595–9606. doi: 10.1021/acsnano.9b04723

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhou, T., Wu, J., Liu, J., Luo, Y., and Wan, Y. (2015). Fabrication and characterization of layered chitosan/silk fibroin/nano-hydroxyapatite scaffolds with designed composition and mechanical properties. Biomed. Mater. 10:045013. doi: 10.1088/1748-6041/10/4/045013

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhu, W., Guo, D., Peng, L., Chen, Y. F., Cui, J., Xiong, J., et al. (2017). Repair of rabbit cartilage defect based on the fusion of rabbit bone marrow stromal cells and Nano-HA/PLLA composite material. Artif. Cells Nanomed. Biotechnol. 45, 115–119. doi: 10.3109/21691401.2016.1138482

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhu, Y., Zhang, Q., Shi, X., and Han, D. (2019). Hierarchical hydrogel composite interfaces with robust mechanical properties for biomedical applications. Adv. Mater. 45:e1804950. doi: 10.1002/adma.201804950

CrossRef Full Text | Google Scholar

Keywords: magnetic particle, magnetic hydrogel, magnetic field, tissue engineering, functional recovery

Citation: Liu Z, Liu J, Cui X, Wang X, Zhang L and Tang P (2020) Recent Advances on Magnetic Sensitive Hydrogels in Tissue Engineering. Front. Chem. 8:124. doi: 10.3389/fchem.2020.00124

Received: 20 September 2019; Accepted: 10 February 2020;
Published: 06 March 2020.

Edited by:

Clemens Kilian Weiss, Fachhochschule Bingen, Germany

Reviewed by:

Rocktotpal Konwarh, Addis Ababa Science and Technology University, Ethiopia
Vincenzo Guarino, Italian National Research Council, Italy
Emilio Isaac Alarcon, University of Ottawa, Canada

Copyright © 2020 Liu, Liu, Cui, Wang, Zhang and Tang. This is an open-access article distributed under the terms of the Creative Commons Attribution License (CC BY). The use, distribution or reproduction in other forums is permitted, provided the original author(s) and the copyright owner(s) are credited and that the original publication in this journal is cited, in accordance with accepted academic practice. No use, distribution or reproduction is permitted which does not comply with these terms.

*Correspondence: Xing Wang, wangxing@iccas.ac.cn; Licheng Zhang, zhanglcheng218@126.com; Peifu Tang, pftang301@163.com

These authors have contributed equally to this work

Disclaimer: All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article or claim that may be made by its manufacturer is not guaranteed or endorsed by the publisher.