AUTHOR=Zheng Jin , Peng Jiangying , Zheng Zhexin , Zhou Menghan , Thompson Emily , Yang Junyou , Xiao Wanli 

TITLE=Synthesis and high temperature thermoelectric properties of Yb0.25Co4Sb12-(Ag2Te)x(Sb2Te3)1−x nanocomposites

JOURNAL=Frontiers in Chemistry

VOLUME=3

YEAR=2015

URL=https://www.frontiersin.org/journals/chemistry/articles/10.3389/fchem.2015.00053

DOI=10.3389/fchem.2015.00053

ISSN=2296-2646

ABSTRACT=<p>Nanocomposites are becoming a new paradigm in thermoelectric study: by incorporating nanophase(s) into a bulk matrix, a nanocomposite often exhibits unusual thermoelectric properties beyond its constituent phases. To date most nanophases are binary, while reports on ternary nanoinclusions are scarce. In this work, we conducted an exploratory study of introducing ternary (Ag<sub>2</sub>Te)<sub>x</sub>(Sb<sub>2</sub>Te<sub>3</sub>)<sub>1−x</sub> inclusions in the host matrix of Yb<sub>0.25</sub>Co<sub>4</sub>Sb<sub>12</sub>. Yb<sub>0.25</sub>Co<sub>4</sub>Sb<sub>12</sub>-4wt% (Ag<sub>2</sub>Te)<sub>x</sub>(Sb<sub>2</sub>Te<sub>3</sub>)<sub>1−x</sub> nanocomposites were prepared by a melting-milling-hot-pressing process. Microstructural analysis showed that poly-dispersed nanosized Ag-Sb-Te inclusions are distributed on the grain boundaries of Yb<sub>0.25</sub>Co<sub>4</sub>Sb<sub>12</sub> coarse grains. Compared to the pristine nanoinclusion-free sample, the electrical conductivity, Seebeck coefficient, and thermal conductivity were optimized simultaneously upon nanocompositing, while the carrier mobility was largely remained. A maximum <italic>ZT</italic> of 1.3 was obtained in Yb<sub>0.25</sub>Co<sub>4</sub>Sb<sub>12</sub>-4wt% (Ag<sub>2</sub>Te)<sub>0.42</sub>(Sb<sub>2</sub>Te<sub>3</sub>)<sub>0.58</sub> at 773 K, a ~ 40% increase compared to the pristine sample. The electron and phonon mean-free-path were estimated to help quantify the observed changes in the carrier mobility and lattice thermal conductivity.</p>