Liang Zhang2- 1Ministry of Education Key Laboratory of Child Development and Disorders, Pediatric Research Institute, National Clinical Research Center for Child Health and Disorders, China International Science and Technology Cooperation Base of Child Development and Critical Disorders, Chongqing Engineering Research Center of Stem Cell Therapy, Children’s Hospital of Chongqing Medical University, Chongqing, China
- 2Department of Ultrasound, The First Affiliated Hospital of Chongqing Medical University, Chongqing, China
- 3Department of Ultrasound, Women and Children’s Hospital of Chongqing Medical University, Chongqing, China
Purpose: Poly (lactic-co-glycolic acid)-based nanoparticles (PLGA NPs) have been widely used as the carrier for sustainable drug delivery. However, the drug release from the NPs was usually incomplete and uncontrollable. Herein, a low intensity pulsed ultrasound (LIPUS) assisted SDF-1/BMP-2@nanoparticles (S/B@NPs) system was fabricated to facilitate stem cell recruitment-osteogenesis for periodontal bone regeneration.
Methods: In this work, S/B@NPs were prepared with double-emulsion synthesis method. Then the S/B release profile from NPs was evaluated with or without low intensity pulsed ultrasound treatment. Afterwards, the stem cell recruiting and osteoinductive capacities of LIPUS-S/B@NPs were detected with human periodontal ligament cells (hPDLCs) in vitro and in a rat periodontal bone defect model.
Results: The results indicated that S/B@NPs were successfully prepared and LIPUS could effectively regulate the release of S/B and increase their final releasing amount. Moreover, LIPUS-S/B@NPs system significantly promoted hPDLCs migrating and osteogenesis in vitro and recruiting rBMSCs to the rat periodontal defect and facilitated bone regeneration in vivo.
Conclusion: Our LIPUS assisted S/B@NPs system can effectively facilitate stem cell recruitment and periodontal bone regeneration. Considering its reliable safety and therapeutic effect on bone fracture, LIPUS, as an adjuvant therapy, holds great potential in the regulation of drug delivery systems for bone healing.
1 Introduction
Periodontitis is a common chronic disorder affecting health and life quality of adults (Kinane et al., 2017). Ultimately, it leads to irreversible destruction of alveolar bone due to the continuous chronic inflammation (Huang et al., 2021). In some advanced cases, it even leads to tooth loss. Nowadays many studies have focused on the regeneration of periodontal tissues. However, the effective treatments to repair the destructed periodontal bone tissues are still limited (Silva et al., 2019).
These years, stem cell therapy has emerged as one of the mainstream strategies for periodontal regeneration (Chen et al., 2012). Among various kinds of stems cells, human periodontal ligament cells (hPDLCs) with high osteogenic potential have been considered an ideal stem cell for bone tissue engineering (Zhao et al., 2022). Some researchers implanted hPDLCs loading scaffold to the damaged periodontal bone defect and achieved a certain degree of periodontal bone regeneration (Han et al., 2014). However, the tedious work of obtaining and culturing stem cells and the low survival rate of exogenous cells delivered, as well as the potential risk of infections from the donor greatly limit its application (Chen and Jin, 2010).
In situ tissue regeneration proposes a new conception of recruiting and utilizing the resident stem cells of the host for tissue regeneration (Safina and Embree, 2022). To this end, stromal cell-derived factor-1 (SDF-1) from the CXC chemokine family plays a key role in recruiting CXCR4 (CXC motif chemokine receptor type 4)-positive stem and progenitor cells in the early stage of tissue repairment (Yu et al., 2020; Ling et al., 2022). Therefore, the exogenous delivery of SDF-1 holds great potential in the process of in situ bone regeneration. After the cell recruitment, the next most important thing is to initiate their osteogenesis for further bone regeneration (Wang et al., 2023). BMP is a kind of growth factor derived from demineralized bone matrix and plays a key role in inducing bone formation (Lowery and Rosen, 2018). BMP-2 is one of the most important osteogenic growth factors in the BMP family. It has been applied for clinical fracture therapy and its ability to promote osteogenic differentiation of MSC has been demonstrated in many studies (Lo et al., 2012; Hasenbein et al., 2022).
Therefore, BMP-2 may provide an effective bio-signal for osteogenesis of the recruited stem cells. In clinic, growth factors are usually directly injected into the defect area to promote bone healing, which may cause their rapid loss in the targeted area (Wink et al., 2014; de Freitas et al., 2016). Moreover, bioactive molecules are generally unstable and easily degraded in vivo (Dumic-Cule et al., 2018), and high concentrations of BMP-2 may lead to many side effects such as ectopic osteogenesis, local inflammation and hemangioma (Wang B. et al., 2018a). Therefore, biomaterial-based carriers are needed for the incorporation and delivery of biomolecules to maintain the bioactivity of the factors and sustain their release at the targeted area (Wang et al., 2022). Poly (lactic-co-glycolic acid)-based nanoparticles (PLGA NPs) have been widely used as the carrier for drug delivery with the good biocompatibility and biodegradability of PLGA (Paul et al., 2022; Rocha et al., 2022). PLGA NPs based drug release was controllable compared to the traditional direct drug injection. However, such controllable drug release is limited because it simply delayed the release of drugs (Sawant et al., 2021).
Ultrasound, as a physical stimulus, has been widely utilized to initiate and regulate the release of drugs from their carriers in the targeted area (Li et al., 2021). However, ultrasound with excessive intensity may cause damage to bone healing, like thermal effect. As a physical therapy for bone fracture, low intensity pulsed ultrasound (LIPUS) has been widely adopted for bone healing in clinic (Yao et al., 2022). Moreover, it has been reported to promote cell migration and osteogenic differentiation. However, whether it is able to regulate the drug release from the PLGA NP carriers is unknown (Liu et al., 2020).
Herein, a PLGA NP-based drug delivery system was fabricated, which conducted controlled releases of SDF-1 and BMP-2 under LIPUS radiation. In this system, the dual release of SDF-1 and BMP-2 biomolecules was set to couple the stem cell recruitment and osteogenesis processes, and the combination of LIPUS was able to optimize the release of the biomolecules in this system while promoting bone healing with its physical therapeutic effect. The cell recruitment and osteoinductive capacities of this system were evaluated in vitro and in a rat periodontal defect model. Our research is expected to lay a theoretical foundation for the development of LIPUS assisted drug delivery system in bone tissue engineering in the future (Figure 1).
FIGURE 1. Schematic diagram depicting the design principle of the biomimetic LIPUS assisted S/B@NPs-delivery system recruiting and facilitating the osteogenesis of stem cell in rat periodontal defect area under the radiation of LIPUS.
2 Materials and methods
2.1 Synthesis of S/B@NPs
SDF-1/BMP-2@PLGA nanoparticles (termed S/B@NPs) were prepared by double-emulsion synthesis method (Liu et al., 2021). 50 mg PLGA (Ruixi Biological Technology, Xi’an, China) was added into 2 mL dichloromethane and vortexed to make it totally dissolved. SDF-1 and BMP-2 (Novaprotein) were dissolved in 1% bovine serum albumin (BSA, Sigma) solution and then it was added into the PLGA solution. To obtain the primary emulsion, the protein-containing solution was emulsified with sonicator (Sonics and Materials Inc., Newtown, Connecticut, United States) under ice bath for 2 min. Then 9 mL of 4% PVA solution was supplemented to it and sonicated for another 2 min. W/O/W double emulsion was so far formed. 10 mL of 2% isopropanol solution was added into the emulsion. After further magnetic stirring for 4 h and centrifugation for 5 min (10,000 rpm), the NPs were harvested and reserved for further evaluation.
2.2 Characterization of S/B@NPs
The transmission electron microscope (TEM, Hitachi, Tokyo, Japan) and scanning electron microscopy (SEM, Hitachi, Tokyo, Japan) were employed to measure the morphology and structure of the S/B@NPs. Afterwards, a Zetasizer Nano ZS instrument (Zetasizer Nano ZS90, Malvern Instruments, United Kingdom) was used to detect their hydrodynamic diameters and zeta potentials.
2.3 The protein entrapment efficiency of NPs
Bovine serum albumin (BSA, Solarbio, Beijing, China) was used as the model protein of SDF-1 and BMP-2 because of its good stability and low cost. The protein entrapment efficiency was evaluated by Micro-BCA method with the BCA kit (Beyotime, Shanghai, China). The 0.9 mL of NaOH (1 mol/L) and 0.1 mL phosphate-buffered saline (PBS) were mixed, then 5 mg of BSA@NPs was added to the mixture and shaken at room temperature. After 2 h of hydrolysis, the aforementioned solutions were neutralize using 1 mL of HCl (0.9 mol/L). Following Micro-BCA assay was performed to assess the protein concentrations using the BCA kit.
2.4 Release of SDF-1/BMP-2 from NPs under LIPUS stimulus
S/B@NPs were dissolved in PBS. Then the samples were equally divided as control and LIPUS-treated groups. The samples in LIPUS group were exposed to LIPUS irradiation (JC 200, Chongqing Haifu Technology, Chongqing, China) at a frequency of 3 MHz, an intensity of 100 mW/cm2, a duty cycle of 50% for 10 min every 6 h. The tubes were placed under 37°C shaker bath (Memmert WB14, Schwabach, Germany) at 100 rpm for 120 h. Their supernatants were collected from each tube at each timepoint. The contents of SDF-1 and BMP-2 were evaluated according to the manufacturer’s instructions with the ELISA kit (Jiubang Biotechnology Quanzhou, China). Then the release profiles were finally obtained by plotting the percentages of cumulative contents of the released SDF-1 and BMP-2 as time.
2.5 In vitro cytotoxicity assay
The cytotoxicity of NPs was measured by Cell Counting Kit-8 (CCK-8) assay. Cells were seeded in a 96-well plate and incubated with NPs of different concentrations (50, 125, 500, 1,000, and 2,000 μg/mL) for 1 and 3 days. At each timepoint, 10 µL of CCK-8 (Dojindo, Kumamoto, Japan) solution was added into each well. After 2 h incubation, the plate was placed in a microplate reader (Synergy HT, BioTek, Winooski, VT) to measure their absorbance at 450 nm. The biocompatibility of the NPs was further assessed with live/dead assay for 1 and 3 days. Briefly, cells were seeded in glass cell culture dishes and incubated with or without aforementioned concentrations of NPs. On the first and third day of incubation, the cells were stained using calcein-AM/PI kit (Beyotime), after which the cells were observed under a laser scanning confocal microscope (Nikon, Tokyo, Japan).
2.6 Cell isolation and culture
The hPDLCs were donated by Professor Jinlin Song from the Stomatological Hospital of Chongqing Medical University. 10% fetal bovine serum (FBS; Gibco, United States), 100 U/mL of penicillin and 100 μg/mL of streptomycin were supplemented to the α-Minimum Essential Medium (α-MEM; Hyclone, Logan, UT, United States) to form the complete medium for cells culture. The cells were cultured at 37°C in a humidified CO2 incubator. When reaching 60% confluency, the cells were passaged. The following experiments were conducted with cells of passage 3.
To investigate the osteoinductivity of our system, four groups were set: 1) control group, the cells were cultured in osteogenic differentiation medium (complete medium further supplemented with 50 μg/mL ascorbic acid, 10 mM ß-glycerophosphate, 10 nM dexamethasone (Solarbio, Beijing, China)); 2) the S/B group, the cells were incubated in osteogenic differentiation medium with SDF-1 and BMP-2; 3) the S/B@NPs group, the cells were incubated in osteogenic differentiation medium containing S/B@NPs; 4) the LIPUS + S/B@NPs group, the cells were cultured in osteogenic differentiation medium with S/B@NPs under LIPUS radiation at a frequency of 3 MHz, an intensity of 100 mW/cm2, a duty cycle of 50%, for 10 min every day.
2.7 Alkaline phosphatase (ALP) and alizarin red staining
ALP and alizarin red staining were conducted to assess the cell osteoinductive capacity of our system. After 7 days of osteogenic induction, the hPDLCs were fixed and stained according to the instructions of ALP staining kit (Beyotime). After staining, images were obtained under the microscope (Nikon Eclipse Ti, Tokyo, Japan). For the purpose of further evaluating its osteoinductive capacity, alizarin red solution (Solarbio) was used to detect the calcium accumulation in cells after 21 days of the osteogenic induction. After incubation for 30 min, the samples were imaged under the microscope. Then the 10% cetylpyridinium chloride (Macklin, Shanghai, China) was used to quantify calcium accumulation. The solution was then shifted to a 96-well plate, and then their optical density was detected at 405 nm under the microplate reader.
2.8 Transwell migration assay
The influence of our system on hPDLCs migration was evaluated in a 24-well transwell system (pore size: 8 μm; Merck, United States). Firstly, hPDLCs were starved for 3 h and harvested by trypsinization. Then the cells were seeded in the upper chambers of the transwell system (1 × 105 cells per chamber). The lower chambers were treated with serum-free media (Control group) or different groups (S/B group, S/B@NPs group, LIPUS + S/B@NPs group). After 24 h, 0.2% crystal violet (Solarbio) was used to stain the hPDLCs migrated to the bottom side of transwell and the microscope was employed to take the images of stained hPDLCs.
2.9 Analysis of mRNA expression
After 7-day osteoinductive culture, RNAsimple total RNA kit (Tiangen Biological Technology, Beijing, China) was used to extract the cells’ total RNA. Afterwards, Reverse transcription kit (Thermo Fisher Scientific, America) was applied to synthetize cDNA. Real-time PCR was conducted to evaluate the alkaline phosphatase (ALP), runt-related transcription factor 2 (Runx2), and collagen type I (Col1a1) mRNA expressions of hPDLCs in Real-Time PCR Detection (Bio-rad). GAPDH expression was used as the internal control. The primer sequences of aforementioned genes were listed in Table 1.
TABLE 1. The primer sequences of all genes used in qPCR.
2.10 Immunofluorescence staining
The protocol of immunofluorescence staining was consistent with that reported in previous studies (Yao et al., 2022). Briefly, the hPDLCs were seeded in glass cell culture dishes used for laser scanning confocal microscopy. After treating for 5 days, the 4% PFA was used to fix the hPDLCs, and then they were permeabilized with 0.5% (v/v) Triton X-100 (Solarbio). After that, the hPDLCs were blocked employing 5% BSA. Then the anti-Runx2 (rabbit monoclonal antibody, 1:50, Abcam) solution was used to incubate the cells at 4°C overnight. Afterwards, the cells were incubated with corresponding secondary antibody (CoraLite488-conjugated goat anti-rabbit IgG, 1:100, Proteintech, Rosemont, IL) at room temperature for 1.5 h, followed by counterstained using 2-(4-amidinophenyl)-6-indolecarbamidine dihydrochloride (DAPI) (1:150, Leagene) for 5 min. Then the laser scanning confocal microscope was applied to observe the cells and images were captured. The images were processed with the ImageJ software (National Institutes of Health, Bethesda, MD, United States).
2.11 The preparation of periodontal bone defect model in vivo
The animal experiments process was reviewed and approved by the Ethics Committee of Children’s Hospital of Chongqing Medical University. Male Sprague Dawley (SD) rats of 8 weeks old were obtained from Laboratory Animal Center of Chongqing Medical University and randomly divided into 5 groups including control group, Hydroxyapatite/Beta-tricalcium phosphate (HA/β-TCP) group (termed HT group), S/B-HT group, S/B@NPs-HT group and LIPUS + S/B@NPs-HT group. 500 μL S/B@NPs suspension or S/B solution were mixed with the same amount of HT powder in EP tubes, respectively. The mixtures in the EP tubes were gently shaken at 4°C overnight.
According to the protocol reported in the previous study, the periodontal bone defect was prepared after modifications (Padial-Molina et al., 2015; Wang et al., 2023). The rats were anesthetized, and their fur around the operation region was removed, followed by the disinfection of cheek skin. To expose the masseter muscle, an incision with 1.5 cm was made alongside the lower margin of the alveolar bone. After the masseter muscle was dissected and the buccal plate was localized, accession to the buccal roots of molars was initiated with a ring drill and the bone in the defect area was removed with a ball drill. Finally, a 3 mm diameter circular defect was made and implanted with or without drug delivery systems, after which the muscle and skin over the operation area were relocated and sutured. The rats were injected with analgesia once a day for 3 days after the operation, and fed with soft food for 1 week. The LIPUS treatment at a frequency of 3 MHz, an intensity of 100 mW/cm2, a duty cycle of 50% was performed 20 min every 2 days to the rats in the LIPUS + S/B@NPs group. After 8 weeks, the rats were sacrificed and their mandibles were collected, fixed and scanned using microcomputed tomography (micro-CT, Always Imaging, Shanghai, China). Then 10% EDTA buffer was adopted for the decalcification of samples for 2 months, and the samples were further sectioned for H&E and Masson trichrome staining.
2.12 In vivo toxicity of the drug-delivery system
To assess the toxicity of our drug-delivery systems in vivo, different groups of systems (NPs-HT group, S/B@NPs-HT group, LIPUS + S/B@NPs-HT group and control group) were implanted to the periodontal defects of SD rats. LIPUS treatment was conducted to the LIPUS + S/B@NPs-HT group. 8 weeks after surgery, the viscus tissues of rats in all groups were collected, fixed and sectioned for H&E staining.
2.13 rBMSCs recruitment in vivo
To assess the cell recruitment ability of our systems in vivo, CFSE staining kit (Invitrogen, California, United States) was employed to mark rat bone marrow mesenchymal stem cells (rBMSCs). The rBMSCs were collected and resuspended in PBS containing the CFSE probe, and the solution were incubated at 37°C. After 15 min, the cells were centrifuged, resuspended in medium and then incubated for another 30 min. Then the cells were observed under the fluorescence microscope and images were captured. The periodontal bone defect model was prepared in rats as described above, followed by the injection of CFSE-labelled rBMSCs into rats’ circulation through the caudal vein. After 1 week, their mandibles were collected, fixed and sectioned with a hard tissue slicing technique. The confocal fluorescence microscope was employed to observe the CFSE-labelled rBMSCs migrated to the periodontal defect area.
2.14 Statistical analysis
The data are presented as the mean ± standard deviation (SD) and the differences between groups were evaluated with one-way analysis of variance (ANOVA). The significance level was set to p < 0.05, p < 0.01, p < 0.001 and p < 0.0001 for our experimental data analysis. A p-value of less than 0.05 was considered statistically significant. The GraphPad Prism 9.0 (GraphPad Software Inc., San Diego, CA, United States) software was used for statistical analysis of the data.
3 Results
3.1 Preparation and characterization of the S/B@NPs
As shown in Figure 2A, the core-shell structure and spherical shape of S/B@NPs could be observed under TEM. Under the SEM, it could be seen that the NPs had good dispersion and quite uniform size (Figure 2B). The average diameter and Zeta potential of NPs were 244.6 ± 64.66 nm (Figure 2C) and −9.82 ± 5.15 mV, respectively (Figure 2D). The protein entrapment efficiency of NPs is 51%.
FIGURE 2. Synthesis and characterization of S/B@NPs. (A) TEM image of S/B@NPs. (B) SEM image of S/B@NPs. (C) Particle size distributions of S/B@NPs. (D) Zeta potentials of S/B@NPs. (E) Release profiles of the SDF-1 from S/B@NPs with or without LIPUS treatment. (F) Release profiles of the BMP-2 from S/B@NPs with or without LIPUS treatment. Error bar represents the mean ± SD (n = 3).
As shown in Figures 2E, F, the LIPUS treated group displayed a higher release rate of SDF-1 and BMP-2 than the control group since the 0th h. Both groups gradually reached a plateau at about 72nd h, by which time the LIPUS group showed a significant higher amount of SDF-1 and BMP-2 released, which indicated that LIPUS could effectively regulate the release of bioactive factors from S/B@NPs.
3.2 Biocompatibility evaluation of S/B@NPs in vitro
To examine the biocompatibility of S/B@NPs, the hPDLCs were cocultured with NPs and CCK-8 assay was employed to detect their cytotoxicity. The cell viability exhibited no significant differences in groups with different concentrations of S/B@NPs on both day 1 and day 3 (Figure 3A). And from 1 day to 3 days, the cells in all groups displayed a good growth trend, which suggested that NPs displayed low cytotoxicity in the concentration from 50 to 2,000 μg/mL. As for the live/dead cell staining, all the experimental groups exhibited a lot of living cells with green fluorescence and rare dead cells with red fluorescence (Figure 3B), and no significant differences were detected among the experimental groups. From day 1 to day 3, the number of living cells significantly increased in all groups. These results were consistent with the CCK-8 results, indicating that 50–2,000 μg/mL NPs had good biocompatibility.
FIGURE 3. Biocompatibility evaluation of LIPUS-S/B@NPs and its effect on cell migration. (A) CCK-8 results of S/B@NPs in day 1 and day 3 of culture. (B) Results of Live (green)/Dead (red) fluorescence assay of hPDLCs after 1 and 3 days of co-culture. Scale bar: 100 μm. (C) Optical images of hPDLCs recruited in the transwell assay and (D) their quantification. Error bar represents the mean ± SD (n = 3); *, p < 0.05; **, p < 0.01; ***, p < 0.001; ****, p < 0.0001.
3.3 LIPUS-S/B@NPs promoted hPDLCs migration in vitro
The recruitment of stem cells to the targeted area is the crucial first step for in situ bone regeneration. In this study, transwell migration assay was performed to evaluate the influence of LIPUS-S/B@NPs system on the migration ability of hPDLCs. As shown in Figures 3C, D, the numbers of migrated hPDLCs in the S/B group, S/B@NPs group and LIPUS + S/B@NPs group were significant increased than that of the control group. The S/B@NPs group exhibited similar migration activity compared with the S/B group, whereas LIPUS + S/B@NPs group displayed significantly increased number of migrated cells than other groups. These results indicated that our LIPUS assisted S/B@NPs system could effectively promote the migration ability of hPDLCs.
3.4 LIPUS-S/B@NPs promoted hPDLCs osteogenic differentiation in vitro
To evaluate the osteoinductive capacity of our system, ALP and alizarin red stainings were conducted. After 7 days treatment, the results of ALP staining presented that the cells in all the experimental groups exhibited more positive staining than the control group (Figure 4A). Moreover, the LIPUS + S/B@NPs group showed the deepest staining among all the groups, while no obvious difference was detected among the S/B@NPs and the S/B groups. After culture for 21 days, the results of alizarin red staining were in accordance with those of ALP staining (Figures 4A, B).
FIGURE 4. The effect of LIPUS-S/B@NPs on cell osteogenesis. (A) ALP staining and alizarin red staining images of hPDLCs. (B) Quantification of ARS staining, and gene expressions of (C) ALP, (D) Runx2, (E) Col1a1. Error bar represents the mean ± SD (n = 3); *, p < 0.05; **, p < 0.01; ***, p < 0.001; ****, p < 0.0001.
To further evaluate the osteoinductive capacity of the LIPUS-S/B@NPs-delivery system, RT–qPCR and immunofluorescence staining assays were performed to detect the expressions of representative osteogenesis-related genes and proteins. The LIPUS treated group showed the highest expressions of ALP, Runx2, and Col1a1 among groups, while their expressions in the S/B@NPs group were slightly higher than those in the S/B group (Figures 4C–E). Runx2 is a critical transcription factor during the cell osteogenic differentiation process (Komori et al., 1997). Therefore, immunofluorescence staining was conducted to further detect its expression in the cell. As shown in Figures 5A, B, the LIPUS treated group displayed the strongest green fluorescence located mainly in the nucleus among the groups. These results indicated that the LIPUS-S/B@NPs system could effectively promote cell osteogenic differentiation in vitro.
FIGURE 5. The effect of LIPUS-S/B@NPs on cell osteogenesis. (A) Immunofluorescence images stained with Runx2 (green) and DAPI (blue) and (B) its quantitative assessment. Error bar represents the mean ± SD (n = 3); *, p < 0.05; **, p < 0.01; ***, p < 0.001; ****, p < 0.0001.
3.5 LIPUS-S/B@NPs promote rBMSCs recruitment to the rat periodontal bone defect
With encouraging results in vitro, the stem cell recruiting and osteogenic capacities of the S/B@NPs delivery system were further evaluated in the rat periodontal bone defect model (Figure 6A). The rBMSCs were first labelled with CFSE probe in vitro for their further observation in vivo. The cells displayed bright green fluorescence, suggesting that they were successfully marked with CFSE. Then after the rat periodontal bone defect was prepared, the CFSE labelled rBMSCs were injected intravenously. After 1-week LIPUS treatment, the rats were sacrificed with their mandibles collected and sectioned to further evaluate the green fluorescence intensity of labelled rBMSCs migrated to the periodontal defect area. As shown in Figures 6B, C, brighter green fluorescence was observed in S/B, S/B@NPs and LIPUS + S/B@NPs groups than control and HT groups. Specifically, S/B@NPs group exhibited significantly stronger green fluorescence than S/B group; significantly, the LIPUS + S/B@NPs group displayed the brightest green fluorescence among all the groups.
FIGURE 6. The effect of LIPUS-S/B@NPs on stem cell recruitment in vivo and its biocompatibility in vivo. (A) Schematic diagram illustrating the time frame of the in vivo study. (B) Confocal fluorescence images of hard tissue sections of periodontal bone defect area in rats to observe the recruited CFSE-labelled rBMSCs (green fluorescence) and (C) quantitative analysis of the fluorescence intensity. (D) H&E staining of heart, liver, spleen, lung, kidney tissues of SD rats after 8 weeks’ treatment. Scale bar: 100 μm. Error bar represents the mean ± SD (n = 3); *, p < 0.05; **, p < 0.01; ***, p < 0.001; ****, p < 0.0001.
3.6 In vivo toxicity evaluation of the LIPUS-S/B@NPs system
As shown in Figure 6D, the H&E staining results of viscera tissue displayed that there were no obvious pathological damages of main organs in all the experimental groups compared to that in the control group 8 weeks after the operation. It suggested that the systems displayed good bio-compatibility in vivo.
3.7 LIPUS-S/B@NPs promote bone regeneration in the rat periodontal bone defect
Figure 7A shows the sagittal, vertical and cross sectional images of typical samples in each group; new bone in the defect area is marked in yellow and the implanted HA/TCP marked in blue. The control group displayed the least new bone formation and HT group displayed slightly more new bone. S/B@NPs-HT group exhibited slightly more bone regeneration than S/B-HT group. Among all the groups, LIPUS + S/B@NPs-HT group displayed the most bone regeneration. Moreover, there was less blue area in the LIPUS + S/B@NPs-HT group than other groups because the implanted HT particles, in our opinion, started to be replaced by newly-formed bone tissues. The results of bone volume fraction (BV/TV) evaluation were basically consistent with those of sectional images (Figure 7B). Microarchitectural parameters are important indexes that reflect the quality of new bone (Kimelman-Bleich et al., 2009). As shown in Figure 7B, the LIPUS + S/B@NPs-HT group displayed higher trabecular thickness (Tb. Th) than the other groups, indicating that the defect in LIPUS treated group did not only exhibited the most new bone formation, but also the highest bone quality.
FIGURE 7. LIPUS-S/B@NPs promoted periodontal regeneration in rats. (A) Sagittal, vertical and cross-section micro-CT scanning images of rat periodontal bone defects. The new bone in the defect area is marked in yellow and the HT particles in blue. Scale bar: 1 mm. (B) Quantitative analysis of bone microarchitectural parameters determined by micro-CT. Error bar represents the mean ± SD (n = 3); *, p < 0.05; **, p < 0.01; ***, p < 0.001; ****, p < 0.0001.
H&E and Masson’s trichrome staining was employed to provide further complementary details regarding the defect area. As shown in Figures 8A, B, consistent with the results of micro-CT scanning, the defect area in the control group exhibited little new bone and was mostly filled with fibrous connective tissues. The HT group also displayed little new bone formation and defect was mostly filled with green staining collagen fibers. S/B-HT and S/B@NPs-HT groups displayed much more bone regeneration than the control group, in which the S/B@NPs-HT group had more new bone formation than S/B-HT group. Although the defect in S/B@NPs-HT group was mostly filled, most HT particles (indicated by yellow arrow) still existed without signs of bone remodeling initiation. The LIPUS + S/B@NPs-HT group showed much more new bone formation than the other groups, in which the defect was filled with newly formed woven bone with a well-arranged structure. Moreover, there were less HT particles (indicated by yellow arrow) in the defect area, which were completely surrounded by new bone. This indicated that the HT particles were starting to be replaced by new bone tissues, which usually happens in the late stage of bone repair. In a word, LIPUS + S/B@NPs-HT group displayed more mature bone tissues in the defect area, suggesting that our system could effectively promote periodontal bone regeneration.
FIGURE 8. LIPUS-S/B@NPs promoted periodontal regeneration in rats. (A) H&E staining images of periodontal bone tissue sections. The defect area is marked with a green dotted line. (B) Masson-trichrome staining images of periodontal bone tissue sections. The defect area is marked with a red dotted line. Scale bar in black: 500 μm; scale bar in red: 50 μm. The yellow arrows refer to the implanted HT particles area.
4 Discussion
Nowadays, natural bone tissue regeneration is increasingly considered a multistage and well-choreographed process, in which each stage requires specific biological signals (Xu et al., 2019; Ying et al., 2020). Inspired by the natural bone healing cascade, a biomimetic LIPUS assisted drug delivery system was successfully designed and fabricated in this study, which could dually release SDF-1 and BMP-2 coupling the stem cell recruitment and osteogenesis processes. In this system, the combination of LIPUS can not only facilitate cell migration and osteogenesis, but also regulate the release of SDF-1 and BMP-2 in NPs. This system successfully promotes periodontal bone defect regeneration in SD rats.
In situ bone regeneration takes full advantage of the host proficiency by utilizing the cell-free biomaterials loaded with bioactive molecules to recruit cells from the surroundings or the circulation to the target area and initiate their osteogenesis in situ, which avoids the potential risks of traditional cell-loading tissue engineering strategy (Vaquette et al., 2018). In this study, the LIPUS-S/B@NPs system could effectively promote the rBMSCs migrating to the defect area in the early stage of bone repair, which could not only be attributed to its promotion effect on SDF-1 releasing from NPs, but also its physical effect on innate cell mechanism acting on cell migration. The early recruitment of stem cells could lay a solid foundation for further cell osteogenesis and bone repair process (Mehta et al., 2012; Martino et al., 2015). On the other hand, SDF-1 and BMP-2 have been widely used to recruit stem cells and promote osteogenesis in previous studies (Wegman et al., 2015; Shen et al., 2016; Wang T. et al., 2018b). It has been demonstrated that the combined utilization of SDF-1 and BMP-2 could achieve a synergistic effect over cell migration and osteogenesis, which is consistent with our results that the system releasing SDF-1 and BMP-2 significantly promoted stem cell recruitment and osteogenesis. Inspired by the natural bone healing cascade, Tan et al. (2019) prepared a supramolecular SDF-1/BMP-2/NapFFY hydrogel to promote rBMSC migration and osteogenesis in periodontal defect. 8 weeks after the implantation of the SDF-1/BMP-2/NapFFY hydrogel in the bone defect areas of rats, the bone regeneration rate of bone volume fraction reached 56.7%. Moreover, previous studies have demonstrated that the synergistic effect of combined utilization of SDF-1 and BMP-2 over cell migration and osteogenesis might be related to the activation of MAPK and Erk signaling pathways (Hwang et al., 2015). Therefore, in this study, a drug delivery system loaded with SDF-1 and BMP-2 was designed to couple the stem cell recruitment and osteogenesis cascade simulating the natural bone healing process. And the results of in vivo study displayed that such a biomimetic strategy could effectively promoted periodontal bone regeneration.
PLGA nanoparticles are widely used bio-material candidate for drug delivery systems for its good biocompatibility and biodegradation properties as well as the controllable drug-releasing rate (Ding and Zhu, 2018; Zhao et al., 2019). Growth factors like SDF-1 and BMP-2 are unstable and easily degraded, and require long-term and repeated administrations to maintain the effective concentration of growth factors in vivo (Lee et al., 2023; Zhang et al., 2023). Moreover, intravenous administration of growth factors easily leads to their accumulation in untargeted organs (like liver and kidney), causing unnecessary toxicity and side effects. Considering these, their encapsulation with PLGA nanoparticles can protect their bioactivity and sustain their release, resulting in prolonged efficacy (Revdekar and Shende, 2021; Heredia et al., 2022). As demonstrated in this study, our results showed that the S/B@NPs group displayed better cell migration and osteogenesis effects than the S/B group, indicating that the encapsulation of growth factors with NPs could promote their efficacy.
In this study, the combination of LIPUS in our system effectively promotes the bone repairing effect of S/B@NPs. Appropriate intensities of physical stimulation can enhance cellular metabolism and phenotypic adaptation (Flück, 2006). LIPUS is a form of mild and rhythmic mechanical energy with intensity ranging from 30 to 100 mW/cm2. Such a mechanical wave is known to transmit the living tissues and cells with “non-thermal effects,” which subsequently causes a lot of downstream pathway activation and biological effects at the cellular level (O'Brien, 2007; Rego et al., 2012). It has been approved for the treatment of fresh bone fractures by the Food and Drug Administration (FDA) in 1994 and widely applied in clinic as a safe and effective bio-physical therapy (Romano et al., 2009; Assanah et al., 2023). Moreover, several studies have demonstrated that LIPUS can upregulate the expressions of genes concerning mineral metabolism, cementoblastic differentiation and fibroblast differentiation (Inubushi et al., 2008; Mostafa et al., 2009). LIPUS has also proven to be able to effectively facilitate the hPDLCs osteogenesis and migration (Wang Y. et al., 2018c; Liu et al., 2020; Ying et al., 2020). Apart from the therapeutic effect onto cellular metabolism, ultrasound has been reported to regulate the release of drugs in specific carriers. In a previous study, the researchers used LIFU to trigger drug release in nanodroplets and enhance anticancer drug delivery (Yang et al., 2022). Another study demonstrated that VEGF loading microbubbles in combination of ultrasound targeted microbubble destruction could promote bone regeneration and vascularization at calvarial bone defects, which held huge potential for clinical translation (Gong et al., 2019). In this study, LIPUS with a power of 100 mW/cm2 was used. Compared with the ultrasonic wave used in previous studies, the application of LIPUS featuring low intensity and pulsed emission is mild, safe and can avoid the possible side effects of ultrasound upon bone fracture healing to a great extent, such as thermal effect. For the first time, our study found that LIPUS could effectively improve the release of S/B@NPs. It improved the unstable release rate of drugs loaded in NPs and effectively increased their final amount releasing from NPs, which, finally, resulted in greatly enhanced periodontal regeneration in vivo. In a word, our system can efficiently deliver BMP-2 and SDF-1 to the targeted area for bone regeneration, reducing the frequency of drug administration, their toxicity and side effects. Considering the dynamic/changing demands of bio-signals throughout the natural bone healing process, the LIPUS might be applied to regulate the release of drugs in osteogenesis-targeted drug delivery systems to fulfill the changing demands of bio-signals and maximize the bone regeneration efficiency in the future.
5 Conclusion
In situ tissue regeneration utilizes the cell-free biomaterials loaded with bioactive molecules to recruit the host stem cells and initiate their osteogenesis in situ, which can avoid the potential risks of traditional cell-loading tissue engineering strategy. In this study, we designed and manufactured a biomimetic LIPUS assisted drug delivery system that can dually release SDF-1 and BMP-2 to couple stem cell recruitment and osteogenesis of natural bone healing. In the system, LIPUS with a mild intensity of 100 mW/cm2 effectively avoids the side effects of ultrasound on fracture healing, and it can not only regulate the release of SDF-1 and BMP-2, but also promote cell migration and osteogenesis itself. The results showed that our system can significantly promote hPDLCs migration and osteogenesis in vitro; further in vivo evaluation displayed that it can effectively facilitate cell recruitment to target area and promote periodontal bone regeneration in SD rats. Natural bone healing is well-regulated and multistage process. For the first time, our study revealed that LIPUS can effectively regulate the release of SDF-1/BMP-2 from PLGA NPs. Considering its reliable safety and therapeutic effect on fracture, LIPUS, as an adjuvant therapy, holds great potential in the regulation of drug delivery systems for bone healing.
Data availability statement
The raw data supporting the conclusion of this article will be made available by the authors, without undue reservation.
Ethics statement
The animal study was reviewed and approved by the Ethics Committee of Children’s Hospital of Chongqing Medical University.
Author contributions
SY, conceptualization, methodology, and writing-original draft. HZ and YH, data curation and formal analysis. LZ, investigation and analysis data. TG and HY, validation. DW, supervision. KY, writing-review and editing, project administration, and acquisition. All authors contributed to the article and approved the submitted version.
Funding
This work was supported by the Natural Science Foundation Project of CQ (Grant No. CSTB2022NSCQ-MSX0812).
Acknowledgments
We thank Professor Jinlin Song from the Stomatological Hospital of Chongqing Medical University for providing the hPDLCs.
Conflict of interest
The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.
Publisher’s note
All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article, or claim that may be made by its manufacturer, is not guaranteed or endorsed by the publisher.
References
Assanah, F., Grassie, K., Anderson, H., Xin, X., Rowe, D., and Khan, Y. (2023). Ultrasound-derived mechanical stimulation of cell-laden collagen hydrogels for bone repair. J. Biomed. Mater Res. A 111, 1200–1215. doi:10.1002/jbm.a.37508
Chen, F.-M., and Jin, Y. (2010). Periodontal tissue engineering and regeneration: Current approaches and expanding opportunities. Tissue Eng. Part B Rev. 16 (2), 219–255. doi:10.1089/ten.TEB.2009.0562
Chen, F.-M., Sun, H.-H., Lu, H., and Yu, Q. (2012). Stem cell-delivery therapeutics for periodontal tissue regeneration. Biomaterials 33 (27), 6320–6344. doi:10.1016/j.biomaterials.2012.05.048
De Freitas, R. M., Susin, C., Tamashiro, W. M. D. S. C., Chaves De Souza, J. A., Marcantonio, C., Wikesjö, U. M., et al. (2016). Histological analysis and gene expression profile following augmentation of the anterior maxilla using rhBMP-2/ACS versus autogenous bone graft. J. Clin. Periodontol. 43 (12), 1200–1207. doi:10.1111/jcpe.12601
Ding, D., and Zhu, Q. (2018). Recent advances of PLGA micro/nanoparticles for the delivery of biomacromolecular therapeutics. Mater Sci. Eng. C Mater Biol. Appl. 92, 1041–1060. doi:10.1016/j.msec.2017.12.036
Dumic-Cule, I., Peric, M., Kucko, L., Grgurevic, L., Pecina, M., and Vukicevic, S. (2018). Bone morphogenetic proteins in fracture repair. Int. Orthop. 42 (11), 2619–2626. doi:10.1007/s00264-018-4153-y
Flück, M. (2006). Functional, structural and molecular plasticity of mammalian skeletal muscle in response to exercise stimuli. J. Exp. Biol. 209 (Pt 12), 2239–2248. doi:10.1242/jeb.02149
Gong, Y., Li, S., Zeng, W., Yu, J., Chen, Y., and Yu, B. (2019). Controlled in vivo bone formation and vascularization using ultrasound-triggered release of recombinant vascular endothelial growth factor from poly(D,L-lactic-co-glycolicacid) microbubbles. Front. Pharmacol. 10, 413. doi:10.3389/fphar.2019.00413
Han, J., Menicanin, D., Gronthos, S., and Bartold, P. M. (2014). Stem cells, tissue engineering and periodontal regeneration. Aust. Dent. J. 59 (Suppl. 1), 117–130. doi:10.1111/adj.12100
Hasenbein, I., Sachse, A., Hortschansky, P., Schmuck, K. D., Horbert, V., Anders, C., et al. (2022). Single application of low-dose, hydroxyapatite-bound BMP-2 or GDF-5 induces long-term bone formation and biomechanical stabilization of a bone defect in a senile sheep lumbar osteopenia model. Biomedicines 10 (2), 513. doi:10.3390/biomedicines10020513
Heredia, N. S., Vizuete, K., Flores-Calero, M., Pazmiño, V. K., Pilaquinga, F., Kumar, B., et al. (2022). Comparative statistical analysis of the release kinetics models for nanoprecipitated drug delivery systems based on poly(lactic-co-glycolic acid). PLoS One 17 (3), e0264825. doi:10.1371/journal.pone.0264825
Huang, Q., Huang, X., and Gu, L. (2021). Periodontal bifunctional biomaterials: Progress and perspectives. Mater. (Basel) 14 (24), 7588. doi:10.3390/ma14247588
Hwang, H.-D., Lee, J.-T., Koh, J.-T., Jung, H.-M., Lee, H.-J., and Kwon, T.-G. (2015). Sequential treatment with SDF-1 and BMP-2 potentiates bone formation in calvarial defects. Tissue Eng. Part A 21 (13-14), 2125–2135. doi:10.1089/ten.TEA.2014.0571
Inubushi, T., Tanaka, E., Rego, E. B., Kitagawa, M., Kawazoe, A., Ohta, A., et al. (2008). Effects of ultrasound on the proliferation and differentiation of cementoblast lineage cells. J. Periodontol. 79 (10), 1984–1990. doi:10.1902/jop.2008.080081
Kimelman-Bleich, N., Pelled, G., Sheyn, D., Kallai, I., Zilberman, Y., Mizrahi, O., et al. (2009). The use of a synthetic oxygen carrier-enriched hydrogel to enhance mesenchymal stem cell-based bone formation in vivo. Biomaterials 30 (27), 4639–4648. doi:10.1016/j.biomaterials.2009.05.027
Kinane, D. F., Stathopoulou, P. G., and Papapanou, P. N. (2017). Periodontal diseases. Nat. Rev. Dis. Prim. 3, 17038. doi:10.1038/nrdp.2017.38
Komori, T., Yagi, H., Nomura, S., Yamaguchi, A., Sasaki, K., Deguchi, K., et al. (1997). Targeted disruption of results in a complete lack of bone formation owing to maturational arrest of osteoblasts. Cell 89 (5), 755–764. doi:10.1016/s0092-8674(00)80258-5
Lee, H.-Y., Kang, J.-I., Lee, H.-L., Hwang, G.-Y., Kim, K.-N., and Ha, Y. (2023). Concentration-Dependent efficacy of recombinant human bone morphogenetic protein-2 using a HA/β-TCP hydrogel carrier in a mini-pig vertebral oblique lateral interbody fusion model. Int. J. Mol. Sci. 24 (1), 892. doi:10.3390/ijms24010892
Li, Y., Du, M., Fang, J., Zhou, J., and Chen, Z. (2021). UTMD promoted local delivery of miR-34a-mimic for ovarian cancer therapy. Drug Deliv. 28 (1), 1616–1625. doi:10.1080/10717544.2021.1955041
Ling, L., Hou, J., Liu, D., Tang, D., Zhang, Y., Zeng, Q., et al. (2022). Important role of the SDF-1/CXCR4 axis in the homing of systemically transplanted human amnion-derived mesenchymal stem cells (hAD-MSCs) to ovaries in rats with chemotherapy-induced premature ovarian insufficiency (POI). Stem Cell Res. Ther. 13 (1), 79. doi:10.1186/s13287-022-02759-6
Liu, S., Zhang, W., Chen, Q., Hou, J., Wang, J., Zhong, Y., et al. (2021). Multifunctional nanozyme for multimodal imaging-guided enhanced sonodynamic therapy by regulating the tumor microenvironment. Nanoscale 13 (33), 14049–14066. doi:10.1039/d1nr01449h
Liu, S., Zhou, M., Li, J., Hu, B., Jiang, D., Huang, H., et al. (2020). LIPUS inhibited the expression of inflammatory factors and promoted the osteogenic differentiation capacity of hPDLCs by inhibiting the NF-κB signaling pathway. J. Periodontal Res. 55 (1), 125–140. doi:10.1111/jre.12696
Lo, K. W. H., Ulery, B. D., Ashe, K. M., and Laurencin, C. T. (2012). Studies of bone morphogenetic protein-based surgical repair. Adv. Drug Deliv. Rev. 64 (12), 1277–1291. doi:10.1016/j.addr.2012.03.014
Lowery, J. W., and Rosen, V. (2018). The BMP pathway and its inhibitors in the skeleton. Physiol. Rev. 98 (4), 2431–2452. doi:10.1152/physrev.00028.2017
Martino, M. M., Briquez, P. S., Maruyama, K., and Hubbell, J. A. (2015). Extracellular matrix-inspired growth factor delivery systems for bone regeneration. Adv. Drug Deliv. Rev. 94, 41–52. doi:10.1016/j.addr.2015.04.007
Mehta, M., Schmidt-Bleek, K., Duda, G. N., and Mooney, D. J. (2012). Biomaterial delivery of morphogens to mimic the natural healing cascade in bone. Adv. Drug Deliv. Rev. 64 (12), 1257–1276. doi:10.1016/j.addr.2012.05.006
Mostafa, N. Z., Uludağ, H., Dederich, D. N., Doschak, M. R., and El-Bialy, T. H. (2009). Anabolic effects of low-intensity pulsed ultrasound on human gingival fibroblasts. Arch. Oral Biol. 54 (8), 743–748. doi:10.1016/j.archoralbio.2009.04.012
O'brien, W. D. (2007). Ultrasound-biophysics mechanisms. Prog. Biophys. Mol. Biol. 93 (1-3), 212–255. doi:10.1016/j.pbiomolbio.2006.07.010
Padial-Molina, M., Rodriguez, J. C., Volk, S. L., and Rios, H. F. (2015). Standardized in vivo model for studying novel regenerative approaches for multitissue bone-ligament interfaces. Nat. Protoc. 10 (7), 1038–1049. doi:10.1038/nprot.2015.063
Paul, P. S., Cho, J.-Y., Wu, Q., Karthivashan, G., Grabovac, E., Wille, H., et al. (2022). Unconjugated PLGA nanoparticles attenuate temperature-dependent β-amyloid aggregation and protect neurons against toxicity: Implications for alzheimer's disease pathology. J. Nanobiotechnology 20 (1), 67. doi:10.1186/s12951-022-01269-0
Rego, E. B., Takata, T., Tanne, K., and Tanaka, E. (2012). Current status of low intensity pulsed ultrasound for dental purposes. Open Dent. J. 6, 220–225. doi:10.2174/1874210601206010220
Revdekar, A., and Shende, P. (2021). Block copolymers in alzheimer's disease therapy: A perceptive to revolutionize biomaterials. J. Control Release 340, 271–281. doi:10.1016/j.jconrel.2021.11.007
Rocha, C. V., Gonçalves, V., Da Silva, M. C., Bañobre-López, M., and Gallo, J. (2022). PLGA-based composites for various biomedical applications. Int. J. Mol. Sci. 23 (4), 2034. doi:10.3390/ijms23042034
Romano, C. L., Romano, D., and Logoluso, N. (2009). Low-intensity pulsed ultrasound for the treatment of bone delayed union or nonunion: A review. Ultrasound Med. Biol. 35 (4), 529–536. doi:10.1016/j.ultrasmedbio.2008.09.029
Safina, I., and Embree, M. C. (2022). Biomaterials for recruiting and activating endogenous stem cells in situ tissue regeneration. Acta Biomater. 143, 26–38. doi:10.1016/j.actbio.2022.03.014
Sawant, A., Kamath, S., Kg, H., and Kulyadi, G. P. (2021). Solid-in-Oil-in-Water emulsion: An innovative paradigm to improve drug stability and biological activity. AAPS PharmSciTech 22 (5), 199. doi:10.1208/s12249-021-02074-y
Shen, X., Zhang, Y., Gu, Y., Xu, Y., Liu, Y., Li, B., et al. (2016). Sequential and sustained release of SDF-1 and BMP-2 from silk fibroin-nanohydroxyapatite scaffold for the enhancement of bone regeneration. Biomaterials 106, 205–216. doi:10.1016/j.biomaterials.2016.08.023
Silva, L. M., Brenchley, L., and Moutsopoulos, N. M. (2019). Primary immunodeficiencies reveal the essential role of tissue neutrophils in periodontitis. Immunol. Rev. 287 (1), 226–235. doi:10.1111/imr.12724
Tan, J., Zhang, M., Hai, Z., Wu, C., Lin, J., Kuang, W., et al. (2019). Sustained release of two bioactive factors from supramolecular hydrogel promotes periodontal bone regeneration. ACS Nano 13 (5), 5616–5622. doi:10.1021/acsnano.9b00788
Vaquette, C., Pilipchuk, S. P., Bartold, P. M., Hutmacher, D. W., Giannobile, W. V., and Ivanovski, S. (2018). Tissue engineered constructs for periodontal regeneration: Current status and future perspectives. Adv. Healthc. Mater 7 (21), e1800457. doi:10.1002/adhm.201800457
Wang, B., Guo, Y., Chen, X., Zeng, C., Hu, Q., Yin, W., et al. (2018a). Nanoparticle-modified chitosan-agarose-gelatin scaffold for sustained release of SDF-1 and BMP-2. Int. J. Nanomedicine 13, 7395–7408. doi:10.2147/IJN.S180859
Wang, H., Chang, X., Ma, Q., Sun, B., Li, H., Zhou, J., et al. (2023). Bioinspired drug-delivery system emulating the natural bone healing cascade for diabetic periodontal bone regeneration. Bioact. Mater 21, 324–339. doi:10.1016/j.bioactmat.2022.08.029
Wang, H., Hu, B., Li, H., Feng, G., Pan, S., Chen, Z., et al. (2022). Biomimetic mineralized hydroxyapatite nanofiber-incorporated methacrylated gelatin hydrogel with improved mechanical and osteoinductive performances for bone regeneration. Int. J. Nanomedicine 17, 1511–1529. doi:10.2147/IJN.S354127
Wang, T., Guo, S., and Zhang, H. (2018b). Synergistic effects of controlled-released BMP-2 and VEGF from nHAC/PLGAs scaffold on osteogenesis. Biomed. Res. Int. 2018, 1–12. doi:10.1155/2018/3516463
Wang, Y., Li, J., Qiu, Y., Hu, B., Chen, J., Fu, T., et al. (2018c). Low-intensity pulsed ultrasound promotes periodontal ligament stem cell migration through TWIST1-mediated SDF-1 expression. Int. J. Mol. Med. 42 (1), 322–330. doi:10.3892/ijmm.2018.3592
Wegman, F., Poldervaart, M. T., Van Der Helm, Y. J., Oner, F. C., Dhert, W. J., and Alblas, J. (2015). Combination of bone morphogenetic protein-2 plasmid DNA with chemokine CXCL12 creates an additive effect on bone formation onset and volume. Eur. Cell Mater 30, 1–11. doi:10.22203/ecm.v030a01
Wink, J. D., Gerety, P. A., Sherif, R. D., Lim, Y., Clarke, N. A., Rajapakse, C. S., et al. (2014). Sustained delivery of rhBMP-2 by means of poly(lactic-co-glycolic acid) microspheres: Cranial bone regeneration without heterotopic ossification or craniosynostosis. Plast. Reconstr. Surg. 134 (1), 51–59. doi:10.1097/PRS.0000000000000287
Xu, X.-Y., Li, X., Wang, J., He, X.-T., Sun, H.-H., and Chen, F.-M. (2019). Concise review: Periodontal tissue regeneration using stem cells: Strategies and translational considerations. Stem Cells Transl. Med. 8 (4), 392–403. doi:10.1002/sctm.18-0181
Yang, D., Chen, Q., Zhang, M., Feng, G., Sun, D., Lin, L., et al. (2022). Drug-loaded acoustic nanodroplet for dual-imaging guided highly efficient chemotherapy against nasopharyngeal carcinoma. Int. J. Nanomedicine 17, 4879–4894. doi:10.2147/IJN.S377514
Yao, H., Zhang, L., Yan, S., He, Y., Zhu, H., Li, Y., et al. (2022). Low-intensity pulsed ultrasound/nanomechanical force generators enhance osteogenesis of BMSCs through microfilaments and TRPM7. J. Nanobiotechnology 20 (1), 378. doi:10.1186/s12951-022-01587-3
Ying, S., Tan, M., Feng, G., Kuang, Y., Chen, D., Li, J., et al. (2020). Low-intensity Pulsed Ultrasound regulates alveolar bone homeostasis in experimental Periodontitis by diminishing Oxidative Stress. Theranostics 10 (21), 9789–9807. doi:10.7150/thno.42508
Yu, B., Dong, B., He, J., Huang, H., Huang, J., Wang, Y., et al. (2020). Bimodal imaging-visible nanomedicine integrating CXCR4 and VEGFa genes directs synergistic reendothelialization of endothelial progenitor cells. Adv. Sci. (Weinh) 7 (24), 2001657. doi:10.1002/advs.202001657
Zhang, Z., Wang, F., Huang, X., Sun, H., Xu, J., Qu, H., et al. (2023). Engineered sensory nerve guides self-adaptive bone healing via NGF-TrkA signaling pathway. Adv. Sci. (Weinh) 10, e2206155. doi:10.1002/advs.202206155
Zhao, C., Zou, T., Tang, R., and Zhu, C. (2022). Placenta-specific 8 (PLAC8) mediates inflammation and mobility of the hPDLCs via MEK/ERK signaling pathway. Int. Immunopharmacol. 103, 108459. doi:10.1016/j.intimp.2021.108459
Keywords: LIPUS, nanoparticle, stem cell, recruitment-osteogenesis, periodontal bone regeneration
Citation: Yan S, Wang D, Zhang L, Gan T, Yao H, Zhu H, He Y and Yang K (2023) LIPUS-S/B@NPs regulates the release of SDF-1 and BMP-2 to promote stem cell recruitment-osteogenesis for periodontal bone regeneration. Front. Bioeng. Biotechnol. 11:1226426. doi: 10.3389/fbioe.2023.1226426
Received: 21 May 2023; Accepted: 26 June 2023;
Published: 04 July 2023.
Edited by:
Chengcheng Niu, Central South University, ChinaReviewed by:
Yaqing Chen, Shanghai Jiao Tong University, ChinaZhou Yang, The Affiliated Hospital of Southwest Medical University, China
Copyright © 2023 Yan, Wang, Zhang, Gan, Yao, Zhu, He and Yang. This is an open-access article distributed under the terms of the Creative Commons Attribution License (CC BY). The use, distribution or reproduction in other forums is permitted, provided the original author(s) and the copyright owner(s) are credited and that the original publication in this journal is cited, in accordance with accepted academic practice. No use, distribution or reproduction is permitted which does not comply with these terms.
*Correspondence: Ke Yang, yangke@hospital.cqmu.edu.cn