First identification of potato tuber rot caused by Penicillium solitum, its silver nanoparticles synthesis, characterization and use against harmful pathogens

Potato is one of the highly consumed vegetable crop grown in different regions across Pakistan that is affected by fungal diseases. The current research was conducted to identify fungal pathogen causing mold-like disease of potato in Khyber Pakhtunkhwa (KP), Pakistan. For molecular identification and characterization of the fungal disease; potato tuber samples were collected followed by culturing on potato dextrose agar (PDA). Based on morphological features, the pathogen was identified as a Penicillium species. This result was obtained in 45 different isolates from potato tubers. Molecular identification was done using β-tubulin primers and ITS5 sequencing of 13 different isolates that releveled 98% homology with BLAST (GenBank accession no. KX958076) as Penicillium solitum (GenBank accession nos. ON307317; ON307475 and ON310801). Phylogenetic tree was constructed that showed Penicillium solitum prevalence along with Penicillium polonicum and Penicillium citrinum on potato tubers. Based on this, Penicillium solitum based silver nanoparticles (Ag NPs) were synthesized and characterized using UV-visible spectroscopy, Fourier transform infrared (FTIR) spectroscopy, X-ray diffraction (XRD), energy dispersive X-ray (EDX) and field emission scanning electron microscopy (FE SEM). UV-analysis showed a characteristic peak at 410 nm confirming synthesis of Penicillium solitum based Ag NPs. This was further confirmed by XRD followed by EDX and SEM that showed face cubic crystal structure with Ag as major constituent of 18 nm formed spherical Ag NPs. FTIR showed band stretching of O-H, N-O and C-H of biological origin. Similarly, Penicillium solitum based Ag NPs presented strong anti-bacterial and anti-fungal activity at 0.5 level of significance LSD. According to our knowledge, this is the first report of Penicillium solitum identification in Pakistan, its Ag NPs synthesis and characterization to be used against pathogens of agricultural significance.

1 Introduction

Potato belongs to family Solanaceae that is a highly valued vegetable crop due to its role in food and nutrition. In Pakistan, potato is mainly grown in Punjab followed by KP, Sindh, Gilgit Baltistan and Balochistan province (Majeed and Muhammad, 2018). The temperate climate of KP is well suited for potato production, however its growth is frequently affected by fungal diseases (Abbas et al., 2013). Penicillium; a fungal pathogen that belongs to the genus ascomycetes, causes blue mold on many edible items like cereals, grains, corn, fruits and vegetables (Kim et al., 2006). This genus includes almost 300 species with some involved in the production of important secondary metabolites (Larsen et al., 2007). Morphological characters includes fungal mycelia having uni or multinucleated hyphae separated by a septum. Conidia are borne on conidiophores, which are round and uninucleate (Kim et al., 2007). Penicillium solitum is an asexually reproducing fungus in the genus Penicillium. It is a mesophilic and psychrotolerant species. Penicillium solitum produces compounds such as polygalacturonase involved in cell wall break down; solistatinol and viridicatin, polyketide-derived compactin used as cholesterol-lowering compounds generally known as statin (Larsen et al., 2007). Penicillium solitum initially produces white colony that later turn dark blueish green on Czaek yeast extract and PDA media while it produces brownish orange color on malt extract agar. Brown-orange color on malt extract media is unique to Penicillium solitum species. Peculium solitum has been isolated from Saffron Corm in China and similarly Blue Mold on Apple Caused by Penicillium polonicum in the United States has been reported (Bradshaw et al., 2021; Zhang et al., 2020). To our knowledge this is the first report of blue mold caused by Penicillium solitum on potato in Pakistan.

One of the modern researches in the field of nanotechnology is the production of nanoparticles of 1-100 nm in size that have significant applications in health, agriculture and medicine (Thul et al., 2013). Physical methods for nanoparticles synthesis such as thermal, plasma, ultrasonic irradiation, and laser ablation are costly and require extensive energy input for their production. On the other hand, chemical methods do not require as much energy, however these methods involves toxic chemicals that are considered environmentally hazardous and produce harmful by-products (Ganachari et al., 2012; Yassin et al., 2021). Biological based nanoparticles are environmentally friendly, cost-effective and follow relatively simple procedures that can serve as an alternative to chemical and physical methods. The biological approach based on algae, fungi, bacteria and plants follows the principle of green chemistry during the synthesis of nanoparticles (Adil et al., 2015) such as Ag NPs. Microorganisms such as bacteria, fungi, yeasts, and algae have been known to synthesize Ag NPs, but fungi are preferred for their large biomass and synthesis of some novel extracellular metabolites (Guilger-Casagrande and de Lima, 2019). Secondary metabolites such as alkaloids, terpenoids, organic acids, polyketides, polyphenolics and cyclodepsipeptides are reported in Penicillium genus. These bioactive compounds enhance electron donor and free radical scavenging ability resulting in capping and stabilization of nanoparticles (Rudrappa et al., 2023). Ag NPs synthesis based on Penicillium verrucosum, Penicillium citrinum and Aspergillus niger are reported (Yassin et al., 2017; Al-Zubaidi et al., 2019; Yassin et al., 2021). Green synthesized Ag NPs using Penicillium oxalicum showed cytotoxic potential against the breast cancer cell lines. Anticancer activity was noted by decreased wound closer of cancer cells and differential genes expression in tumor suppression, cell cycle arrest and Caspase-3 induced apoptosis (Gupta et al., 2023). These Ag Nps showed antimicrobial activity against Aspergillus flavus, Aspergillus niger, Penicillium albicans and Staphylococcus aureus. Similarly, Penicillium chrysogenum Ag NPs showed anti biofilm activity against opportunistic pathogenic Acinetobacter baumannii prevalent in hospital settings (Barabadi et al., 2022). In another study Penicillium verhagenii selenium nanoparticles were found most efficient for their antioxidant and anti-cancer activity. Additionally, these green selenium NPs were effective against larval instar mosquito Aedes albopictus (Nassar et al., 2023). Based on the immense importance of Penicillium species and wide application of Ag NPs, the current study is aimed at the identification and characterization of Penicillium solitum from Pakistan for the first time and its Ag NPs synthesis and characterization using UV, XRD, SEM, FTIR and EDX for their potential use against some harmful microorganisms.

2 Materials and methods

2.1 Sample collection and isolation of Penicillium solitum from diseased tubers

Diseased potato tuber samples having greenish-brown fungal infection were collected from different regions of KP Pakistan. The area included Abbottabad, Mansehra, Batakundi and Haripur. Samples that showed distinct mold like symptoms led us to collect potato tubers mostly from the north of Pakistan for its molecular identification and characterization.

For fungus isolation, infected potato tubers were washed with 70% ethanol for 15-20 seconds and later rinsed with distilled water. The infected portion of the tuber was cut and crushed using distilled water. PDA media was used for sample inoculation with serial dilution. After inoculation, the samples plates were stored at 28⁰C for 5-7 days. Samples having morphologically distinct mold like features were re-cultured on PDA medium. Re-culturing was done until homogenized colonies were obtained following the same culturing procedure.

2.2 PCR analysis of β-Tubulin and pathogenicity test

CTAB method was used for the extraction of DNA from different fungal cultures (Zhang et al., 2010). Briefly, fungal inoculum was taken in TE buffer, glass beads were added and subjected to vortex for 20 mins. It was then centrifuged at 10000 rpm for 15 mins. 200µl sample was taken and subjected to CTAB extraction method and DNA obtained was suspended in TE buffer. For Penicillium identification, β-Tubulin gene (Kim et al., 2007) was amplified at 57⁰C annealing temperature. Pathogenicity test was performed on certified potato tubers for symptoms development. The tubers were surface sterilized with 70% ethanol and washed with distilled water. A 50ul spore suspension of 3x 10⁴/ml in sterile distilled water was used to inoculate potato tubers. Tubers were stored at 25°C for 7 days for symptoms development.

2.3 Phylogenetic tree construction

We performed ITS single-end sequencing of 13 strains using Illumina sequencing technology and obtained the sequences of these strains. Newly generated 13 sequences were submitted to Gene Bank and accession numbers are provided in Table S1. Then, we performed Blastn analysis on these ITS sequencing results and corresponding 10 sequences were selected with 13 isolated strains to construct a phylogenetic tree (Figure 1). Based on the results of the pre-built phylogenetic tree, we used PhyloSuite tool (Zhang et al., 2010; Zhang et al., 2020) to align 24 sequences using MAFFT with Penecillium glabrum CBS 125543 as an outgroup species (Katoh and Standley, 2013). Maximum likelihood analyses were run with IQ-TREE2 (Minh et al., 2020), using models selected by ModelFinder (Kalyaanamoorthy et al., 2017); Using Shimodaira–Hasegawa–like approximate likelihood-ratio test (SH-aLRT) fast branch tests support in the ML tree (Hoang et al., 2018). The ITS phylogenetic tree includes 24 sequences, using the K2P+R2 as best-fit model.

FIGURE 1

Figure 1 Scanning electron microscopy of Penicillium solitum.

2.4 Biomass preparation and synthesis of Ag NPs

The method described by (Zonooz and Salouti, 2011) was slightly modified for microbial mediated synthesis of Ag NPs. The Penicillium solitum strain ON307317 identified in the current research study was cultured on PD broth and incubated at 28°C and 210 rpm. After 7 days of incubation, the culture was centrifuged at 9000 rpm for 20 min and the biomass was collected. This biomass was added to 250mL of autoclaved distilled water for 3 days of incubation at 28°C. After incubation, the solution was filtered again, and this filtrate was used for the biosynthesis of Ag NPs. For Ag NPs synthesis, about 30 ml of cell-free supernatant and 20 ml silver nitrate (AgNO₃) solution were incubated at 28°C and 150 rpm for 72 h. After the incubation period, the solution was observed for visual color change. The flasks turned from opaque white to dark brown that indicated the presence of bio synthesized Ag NPs (Zonooz and Salouti, 2011; Patil et al., 2019).

2.5 UV–vis spectral analysis of Ag NPs

Ag NPs synthesized by Penicillium solitum cell-free culture supernatant was monitored by UV–vis Spectrophotometer (UV-1602, BMS) within a range of 200–800 nm (Nayak et al., 2011).

2.6 FTIR spectral analysis of synthesized Ag NPs

Bio reduction of Ag⁺ ions using the cell-free culture supernatant of Penicillium solitum was monitored by FTIR (Thermo Scientific, USA) and the spectra were recorded at an interval between 4000 and 400 cm⁻¹ (Dinesh et al., 2021; Rose et al., 2019).

2.7 FE SEM analysis of Ag NPs

For taking the FE SEM images of the biosynthesized Ag NPs, a drop of suspension was placed on specimen stubs. The micrographs for Ag NPs were obtained at 10kV under (5–10 torr) vacuum pressure and the presence of metallic Ag in the solution was analyzed by EDS by using MIRA3 TESCAN model electron microscope (Yousaf et al., 2022).

2.8 XRD measurement of Penicillium solitum Ag NPs

To examine the crystal structure of biosynthesized Ag NPs, XRD patterns were collected using Cu radiation at 40 kV/20 mA using continuous scanning 2θ mode on an X-ray diffractometer (BRUKER D8).

The average crystallite sizes of samples were calculated using Scherrer’s formula:

$$\text{D}=\text{ Kλ}/\text{ β}1/2\text{ cosθ}$$

D represents size of the particle, K is constant, λ is wavelength, β is full width at half maxima and θ is Bragg’s angle. The acquired diffraction patterns were plotted by using Origin software for structural analysis of Penicillium solitum nanoparticles (Du et al., 2015).

2.9 Antimicrobial activity of Ag NPs

The agar well diffusion method was used for the antimicrobial activity of Penicillium solitum synthesized Ag NPs (Chavez-Esquivel et al., 2021). Fresh fungal culture of Aspergillus flavus AG1 was spread on PDA and bacterial cultures of Streptomyces scabies and Pseudomonas syringe DC3000 were spread on Nutrient agar plates for the formation of fungal and bacterial lawns. Six wells were prepared consisting of 20 µg/µL, 40 µg/µL and 60 µg/µL concentrations of P. solitum NPs. For positive control, Kanamycin was used against the bacterial cultures and Voriconazole was used against fungal strain. For negative control, distilled water was used. 60µL of AgNO₃ (1mg/mL) was used in each plate. The bacterial plates were then incubated for 24 hrs. at 37°C and fungal cultures were incubated for 5 days at 28°C. Antimicrobial activity was determined by measuring the diameter of the zone of inhibition for Ag NPs activity (Shahzadi et al., 2022; Yousaf et al., 2022).

2.10 Statistical analysis

The data for antimicrobial activity was analyzed by R software (R Core Team, 2023). Data measurements were averaged with standard error ( ± SE). One-way analysis of variance (ANOVA) was performed at p < 0.05 using least significant difference (LSD) test.

3 Results and discussion

3.1 Isolation and PCR analysis of blue mold of potato

Potato tubers from Batakundi, Mansehra, Abbottabad and Haripur with mold like symptoms were collected from different areas of northern KP and grown on PDA media. Cultured plates with colonies showing morphological distinct features were picked up and cultured again. These symptoms on potato tubers were never characterized that are frequently observed in potato fields of KP Pakistan. Different fields of 4 major potato growing area in KP were selected; including 8 fields in Mansehra; 3 fields in Abbottabad; 2 fields in Batakundi and Haripur each (Figure 2). Morphological features for the disease showed greenish black patches as in case of Penicillium Blue mold (Kim et al., 2006). After 7 days of incubation at 28°C fungal colonies appeared on PDA media from infected tubers (Figure 3). Three times plate cultures were picked up and subjected to PCR, sequencing analysis. PCR result was obtained with β-tubulin (Kim et al., 2007) identified isolates as Penicillium species showing approximately 550 bp band size (Figure 4).

FIGURE 2

Figure 2 Diseased tubers from KP Pakistan; (A) Batakundi (B) Mansehra (C) Haripur (D) Abbottabad (E) Map of Pakistan-KP showing clear symptoms of greenish mold and rotted browning caused by Penicillium.

FIGURE 3

Figure 3 Penicillium cultures from Batakundi, Manshera, Abbottabad and Haripur, KP, Pakistan with species and accession numbers from left to right row wise P. citrinum ON310800 (GeneBank); P. citrinum ON310830 (GeneBank); P. citrinum ON310858 (GeneBank); P. citrinum ON310859 (Gene Bank); P. solitum ON307317 (GeneBank); P. solitum ON307475 (GeneBank); P. citrinum ON352773 (GeneBank) P. citrinum ON310863 (GeneBank); P. polonicum ON310860 (GeneBank); P. citrinum ON31148 P. citrinum ON311281 P. citrinum ON318976 P. solitum ON310801 (GeneBank database).

FIGURE 4

Figure 4 PCR of selected Penicillium isolates using β tubulin primers on DNA extracted from different potato samples showing blue mold symptoms.

3.2 Phylogenetic tree for Penicillium soltium characterization

The phylogenic tree constructed using ITS4 primers sequencing (Macrogen) indicated the ancestor for all of the strains as Penecillium cyclopium (UBOCC-A-119009). Penicillium citrinum followed by Penicillium solitum were found more frequent in our study as closely related species of Penicillium. The phylogenetic consisted of 5 clades/clusters. Clade 1 consists of prime ancestor species Penicillium cyclopium and Penicillium polonicum. Clade 2 contain Penicillium polonicum, Penecillium lapidosum. Clade 3 show all the descendants of Penicillium polonicum and should be classified as Penicillium polonicum. Clade 4 is comprised of Penicillium citrinum only and contain more than 50% of the field-collected strains in this clade (7/13). Clade 5 consists of Penicillium solitum only. Isolate ON310860 is the youngest of all Penicillium species, which is recently differentiated and deserves further study. Species present in each clade are closely related to each other (Figure 5). Our study indicated Penecillium cyclopium as the prime ancestor of 13 penicillium species isolates of blue mold on potato.

FIGURE 5

Figure 5 Phylogenetic tree obtained by Maximum Likelihood (ML) inferred from Internal transcribed spacer (ITS). Best-scoring ML tree obtained by IQ-tree. Only SH-aLRT support (%) values greater than 70% are shown. The names of the newly described species are in bold. Branch lengths are proportional to distance. The tree is outgroup with P. glabrumm CBS 125543.

3.3 Pathogenicity test re-created the symptoms of Penicillium solitum

To regenerate blue mold disease, potato tubers were inoculated with Penicillium soltium (Figure 1). After 7 days, disease symptoms on potato tubers appeared as blue green patches of mycelia when inoculated with Penicillium solitum and after 10 days, these patches transformed into black indentation with dark green patches in cross section upon dissection. The colonization pattern of Penicillium solitum, Penicillium polonicum, and Penicillium citrinum is almost same but in case of Penicillium solitum, dark green colony appeared that didn’t change its color over time whereas Penicillium polonicum and Penicillium citrinum appeared blue green or light green and changed color to dark green or black on PDA media. We therefore conclude that although Penicillium solitum, Penicillium polonicum and Penicillium citrinum are prevalent in potato diseased samples, however this is the first report of Penicillium solitum prevalence in potato field in Pakistan (Figure 6).

FIGURE 6

Figure 6 Pathogenicity test with diseased symptoms of Penicillium solitum on certified tubers.

3.4 Preparation of Penicillium soltium Ag NPs

Once the prevalence of penicillium solitum was confirmed from potato growing fields in Pakistan, green Ag NPs based on Penicillium solitum extract were prepared. Silver nanoparticles were synthesized by stirring mixture of aqueous silver nitrate solution (1mg/mL) and Penicillium solitum extract in 2:3 ratio constantly at 28⁰C (Nayak et al., 2011; Yassin et al., 2021). The pH was adjusted to 11. After a while, the yellow color reaction mixture gradually changed into a dark-brown suspension (Figures 7, 8). This showed that silver ions in the reaction have been transformed into silver (Niraimathi et al., 2013).

FIGURE 7

Figure 7 Biogenic pathway of the synthesis of Ag NPs using extracellular extract of Penicillium solitum.

FIGURE 8

Figure 8 Synthesis of Penicillium solitum Ag NPs. (A) AgNO₃ (B) Fungal Biomass (C) Ag NPs.

3.5 UV-vis spectroscopy for Ag NPs

UV-vis spectroscopy is a primary but an important method that shows Ag NPs formation at the initial synthesis stage. Ag NPs characteristic peak depend upon the shape, size, and distribution of Ag NPs based on surface plasmon resonance (SPR). The maximum absorbance peak of Penicillium solitum extract was recorded at 280 nm that is attributed to aromatic structures in proteins or amino acids (Figure 9; Barabadi et al., 2022). The peak shifted to 410 nm that confirmed the synthesis Ag NPs (Figure 9; Sasidharan et al., 2020). The peak at 410 nm can be attributed to the phenomenon of SPR when the conduction electrons on the bio-fabricated Ag surface oscillate collectively in response to specific wavelength of light. The observed peak at 410 nm indicated secondary metabolites mediated reduction and capping of Ag NPs by Penicillium solitum. A similar characteristic peak was observed in a previous study due to SPR in Ag NPs synthesis mediated by Penicillium oxalicum (Gupta et al., 2023). Similarly, UV–vis spectrum of Ag NPs produced by P. citrinum exhibited an absorption band at around 400–420 nm, suggesting the synthesis of Ag NPs by the fungus (Yassin et al., 2017).

FIGURE 9

Figure 9 UV-Visible spectrum of Penicillium solitum filtrate and Ag NPs.

3.6 XRD of Ag NPs

The diffractogram of Ag NPs is represented in Figure 10. The XRD pattern of synthesized Ag NPs by the reduction of silver ions with aqueous extracts of Penicillium solitum showed distinctive peaks in the spectrum with 2θ values ranging from 20°–80°. Indexing of the peaks was carried out by comparing with the crystal faces of Ag (ICSD No.04-0783) of face center cubic. The diffraction pattern of Penicillium solitum Ag NPs displayed four strong peaks at 2θ values the characteristic peaks at 36.14°, 44.26°, 64.42° and 77.44° correspond to the (111), (200), (220) and (311) structure. Four distinct diffraction peaks of silver were observed at Bragg’s planes (111, 200, 220, 311) for Penicillium brasilianum Ag NPs. These values represent the face-centered cubic structure of synthesized Ag NPs. A similar diffraction pattern was obtained with Penicillium diversum Ag NPs that showed biological components such as proteins, enzymes or metabolites in Ag NPs crystals formation (Ganachari et al., 2012; Rudrappa et al., 2023). Another study also indicated 2θ values corresponded to silver crystalline structure of Penicillium atramentosum KM based Ag NPs (Sarsar et al., 2015).

FIGURE 10

Figure 10 XRD pattern of Ag NPs of Penicillium solitum.

3.7 FE SEM of Penicillium solitum Ag NPs

SEM is used to characterize the surface morphology, size, aggregation, distribution of nanoparticles where electron beam is utilized as imaging probe. It provided high-resolution image of synthesized Ag NPs at the nanometer scale, the role of bio matrix, or encapsulation of Ag NPs that contribute to nanoparticle size (Gupta et al., 2019). The microscopic structure of synthesized silver nanoparticles was found to be 18 nm. The micrograph displayed that Ag NPs were amorphous in shape. Elemental composition present in the sample was presented with the help of EDX analysis. Ag was found 95.35% by weight in synthesized Ag NPs. This showed the presence of high amount of silver in Ag NPs (Figure 11). EDX showed a convincing peak for oxygen with a relative mass percentage of 3.17% which confirmed its presence as a major constituent of nanoparticles. The presence of oxygen could be assigned to emission of X-rays from free amino groups from Penicillium solitum. Similarly, 1.35% carbon presence in EDX indicated the presence of sugars in the fungal mass extract (Dinesh et al., 2021).

FIGURE 11

Figure 11 SEM images of (A) Ag NPs and (B) EDX of Ag NPs.

3.8 FTIR of Ag NPs

The chemical composition of synthesized Ag NPs is characterized by Fourier transform infrared spectroscopy (FTIR). FTIR shows the metabolites that are involved in reduction and capping of Ag NPs, and also shows the presence of chemical residue at the surface of Ag NPs (Mourdikoudis et al., 2018). The FTIR spectrum of Penicillium solitum filtrate gave distinctive peaks at 3283 and 1635 cm^-1. A broad peak at 3283 cm^-1 showed stretching vibrations of O-H of phenolic group and N-H bend of amine group (Nassar et al., 2023). This signifies the involvement of aromatic proteins in the formation of Ag NPs. A strong peak at 1635 cm-1 corresponds to C=O of polysaccharide or N-H stretching of amide present in fungal biomass (Rudrappa et al., 2023). These functional groups in Penicillium solitum biomass filtrate play a critical role in reducing and capping of Ag NPs. The results of Ag NPs FTIR analysis of this study showed different stretches of bonds at various peaks of 1120, 1383, 1539, and 2922 cm^-1. Ag NPs spectrum showed significant peak at 1,120 cm⁻¹ indicating O–H stretch (Karthik et al., 2014). The band at 1383 cm⁻¹ (Jyoti et al., 2016) amplifies the N-O symmetry stretching typical of the nitro compounds. The peak at 1,539 cm⁻¹ corresponds to the aromatic ring of the terpenoid saponin structure (Wan Mat Khalir et al., 2020). Bandat 2922 cm⁻¹ region arising from C–H stretching of aromatic compounds (Jyoti et al., 2016) was observed (Figure 12). During the synthesis of Penicillium solitum Ag NPs, biomolecules including enzymes, proteins and polysaccharides showed a strong affinity towards nanoparticles. Similar results were reported for Penicillium brasilianum and Penicillium verhagenii where amino acids, sugars and other biomolecules from fungal filtrate resulted in nanoparticles synthesis (Nassar et al., 2023; Rudrappa et al., 2023). Additionally, fungi-based metabolites provided electrostatic attraction between the nanoparticles and the biomolecules thus enhancing the formation of stable Ag NPs (Gupta et al., 2023).

FIGURE 12

Figure 12 FTIR pattern of Penicillium solitum filtrate and Ag NPs.

3.9 Antifungal and antibacterial activity of Ag NPs

The potential impact of fungal nanoparticles against plant pathogens is comparatively higher than other microbial NPs due to their greater production of bioactive molecules involved in the synthesis of green NPs. It is previously reported that Fusarium oxysporum, Rhizopus stolonifer and Penicillium fellutanum fungal strains were successfully used for the synthesis of silver NPs (Nanda et al., 2015; Ali et al., 2020). To check the antimicrobial potential of Penicillium solitum, the Ag NPs synthesized was subjected to antimicrobial activity against different phyto-pathogens including Aspergillus flavus, Streptomyces scabies and Pseudomonas syringe DC3000. The maximum zone of inhibition was significant with 1.90, 1.92 and 1.98 diameter (mm) respectively with 60 ug/ul compared to kanamycin and Voriconazole (60ug/ul). The Ag NPs of Penicillium solitum showed strong antimicrobial activity against Streptomyces scabies (gram-positive), Pseudomonas syringae DC3000 (gram-negative) and Aspergillus flavus based on one-way ANOVA with LSD at 0.05 level of significance (Figures 13, 14; R Core Team, 2023). It was found that NADPH-mediated nitrate reductase enzymes are responsible for the formation of Ag NPs for the reduction of silver ions from fungal species (Kumar et al., 2007). Biomolecules of fungal origin such as proteins and amino acid residues provide amino groups, carboxyl groups or hydroxyl groups having nucleophilic affinity that play an essential role in Ag NPs formation and enhanced antimicrobial activity (Elgorban et al., 2016). Both gram-positive and gram-negative bacteria are composed of an outer layer of peptidoglycans, however gram-negative bacteria contain an extra layer of lipopolysaccharides. Similarly, fungus cell wall is mainly composed of complex polysaccharides while its cell membrane is composed of ergosterols, fatty acids or glycophospholipids. Biogenic Ag NPs penetrate fungus and bacteria cell wall and adhere to cell membrane. These Ag NPs move inside the cell and disrupt metabolic and cellular processes including DNA degradation (Shahzadi et al., 2022). The key mechanism of Ag NPs against bacteria and fungus includes production of reactive oxygen species (ROS) such as hydroxyl radical, superoxide and hydrogen peroxide. Excessive ROS causes protein dysfunction, lipid peroxidation and DNA damage, finally causing cell apoptosis (Figure 15; Yousaf et al., 2022; Rudrappa et al., 2023). Based on this, synthesized Ag NPs from Aspergillus versicolor showed strong activity against Sclerotinia sclerotiorum and Botrytis cinerea in strawberry plants. Similar results were obtained with Aspergillus niger Ag NPs against Penicillin digitatum, Aspergillus flavus, and Fusarium oxysporum isolated from different crop species (Al-Zubaidi et al., 2019). This indicates a step forward towards nano-based fungicides/bactericides against phyto-pathogens.

FIGURE 13

Figure 13 Zones of inhibition with different concentrations of Penicillium solitum Ag NPs (ug/mL). (A) Pseudomonas syringae DC3000 (B) Streptomyces scabies (C) Aspergillus flavus.

FIGURE 14

Figure 14 Antibacterial activity of Penicillium solitum Ag NPs. Bacterial and fungal zone of inhibition with Ag NPs at 20, 40 and 60 ug/ul Ag NPs (A) Streptomyces scabies (B) Pseudomonas syringae (C) Aspergillus flavus. Data is represented as means ± SE from 3 replicates. Different letters represent significant differences at p ≤ 0.05 Fisher LSD.

FIGURE 15

Figure 15 Schematic representation of antimicrobial mechanism of Penicillium solitum Ag NPs.

4 Conclusion

In the current study, Penicillium solitum was isolated from diseased potato tubers for the first time in Pakistan. Ag NPs were synthesized using Penicillium solitum aqueous extract. Ag NPs showed UV peak at 410 nm. XRD and SEM confirmed the face cubic crystal with Ag NPs of 18 nm. FTIR showed biogenic Ag NPs formed based on fungal extract. Significant antimicrobial activity was found against plant pathogens Aspergillus flavus, Streptomyces scabies and Pseudomonas syringae. This report shows for the first time that Penicillium solitum based Ag NPs could be used as a potential drug against harmful pathogens. This further requires secondary metabolites pathway elucidation for synthesis of Ag NPs for their successful implementation in agriculture practices.

Data availability statement

The datasets presented in this study can be found in online repositories. The names of the repository/repositories and accession number(s) can be found in the article/Supplementary Material.

Author contributions

SS: Investigation, Methodology, Writing – original draft. XS: Methodology, Data curation, Formal Analysis, Writing – review & editing. SB: Data curation, Formal Analysis, Methodology, Software, Writing – original draft. HZ: Validation, Writing – review & editing. BI: Writing – review & editing, Data curation, Formal Analysis. IS: Writing – review & editing. ZM: Writing – review & editing. SN: Writing – review & editing. MS: Writing – review & editing. AB: Writing – review & editing, Conceptualization.

Acknowledgments

The authors are thankful to Uzair Ahmed, for technical assisting in data generation.

Conflict of interest

The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.

Publisher’s note

All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article, or claim that may be made by its manufacturer, is not guaranteed or endorsed by the publisher.

Supplementary material

The Supplementary Material for this article can be found online at: https://www.frontiersin.org/articles/10.3389/fpls.2023.1255480/full#supplementary-material

References

Abbas, F. A., Naz, F., Irshad, G. (2013). Important fungal diseases of potato and their management-a brief review. Mycopathology. 11, 45–50.

Google Scholar

Adil, S. F., Assal, M. E., Khan, M., Al-Warthan, A., Siddiqui, M. R. H., Liz-Marzán, L. M. (2015). Biogenic synthesis of metallic nanoparticles and prospects toward green chemistry. Dalton Trans. 44 (21), 9709–9717. doi: 10.1039/C4DT03222E

PubMed Abstract | CrossRef Full Text | Google Scholar

Ali, M. A., Ahmed, T., Wu, W., Hossain, A., Hafeez, R., Islam Masum, M. M., et al. (2020). Advancements in plant and microbe-based synthesis of metallic nanoparticles and their antimicrobial activity against plant pathogens. Nanomaterials. 10 (6), 1146. doi: 10.3390/nano10061146

CrossRef Full Text | Google Scholar

Al-Zubaidi, S., Al-Ayafi, A., Abdelkader, H. (2019). Biosynthesis, characterization and antifungal activity of silver nanoparticles by Aspergillus Niger isolate. J. Nanotech. Res. 2, 22–35. doi: 10.26502/fjnr002

CrossRef Full Text | Google Scholar

Barabadi, H., Mohammadzadeh, A., Vahidi, H., Rashedi, M., Saravanan, M., Talank, N., et al. (2022). Penicillium chrysogenum-Derived Silver Nanoparticles: Exploration of Their Antibacterial and Biofilm Inhibitory Activity Against the Standard and Pathogenic Acinetobacter baumannii Compared to Tetracycline. J. Clust Sci. 33, 1929–1942. doi: 10.1007/s10876-021-02121-5

CrossRef Full Text | Google Scholar

Bradshaw, M., Bartholomew, H., Lichtner, F. J., Gaskins, V., Jurick, W. (2021). First report of blue mold caused by Penicillium polonicum on apple in the United States. Plant Dis. 106 (2), 762. doi: 10.1094/PDIS-06-21-1136-PDN

CrossRef Full Text | Google Scholar

Chavez-Esquivel, G., Cervantes-Cuevas, H., Ybieta-Olvera, L. F., Briones, M. C., Acosta, D., Cabello, J. (2021). Antimicrobial activity of graphite oxide doped with silver against Bacillus subtilis, Candida albicans, Escherichia coli, and Staphylococcus aureus by agar well diffusion test: Synthesis and characterization. Materials Sci. Engr. 123, 111934. doi: 10.1016/j.msec.2021.111934

CrossRef Full Text | Google Scholar

Dinesh, B., Monisha, N., Shalini, H. R., Prathap, G. K., Poyya, J., Hampapura, S., et al. (2021). Antibacterial activity of silver nanoparticles synthesized using endophytic fungus—Penicillium cinnamopurpureum. Spectrosc. Letters. 55 (1), 20–34. doi: 10.3390/nano13061010

CrossRef Full Text | Google Scholar

Du, L., Xu, Q., Huang, M., Xian, L., Feng, J. X. (2015). Synthesis of small silver nanoparticles under light radiation by fungus Penicillium oxalicum and its application for the catalytic reduction of methylene blue. Materials Chem. Physics. 160, 40–47. doi: 10.1016/j.matchemphys.2015.04.003

CrossRef Full Text | Google Scholar

Elgorban, A. M., Aref, S. M., Seham, S. M., Elhindi, K. M., Bahkali, A. H., Sayed, S. R., et al. (2016). Extracellular synthesis of silver nanoparticles using Aspergillus versicolor and evaluation of their activity on plant pathogenic fungi. Mycosphere. 7, 844–852. doi: 10.5943/mycosphere/7/6/15

CrossRef Full Text | Google Scholar

Ganachari, S. V., Bhat, R., Deshpande, R., Venkataraman, A. (2012). Extracellular biosynthesis of silver nanoparticles using fungi penicillium diversum and their antimicrobial activity studies. BioNanoSci. 2, 316–321. doi: 10.1007/s12668-012-0046-5

CrossRef Full Text | Google Scholar

Guilger-Casagrande, M., de Lima, R. (2019). Synthesis of silver nanoparticles mediated by fungi: A review. Front. Bioeng Biotechnol. 7. doi: 10.3389/fbioe.2019.00287

PubMed Abstract | CrossRef Full Text | Google Scholar

Gupta, A., Koirala, A. R., Gupta, B., Parajuli, N. (2019). Improved method for separation of silver nanoparticles synthesized using the Nyctanthes arbor-tristis shrub. Acta Chemica Malaysia. 3 (1), 35–42. doi: 10.2478/acmy-2019-0005

CrossRef Full Text | Google Scholar

Gupta, P., Rai, N., Verma, A., Saikia, D., Singh, S. P., Kumar, R. (2023). Green-based approach to synthesize silver nanoparticles using the fungal endophyte Penicillium oxalicum and their antimicrobial, antioxidant, and in vitro anticancer potential. ACS Omega. 7, 46653–46673. doi: 10.1021/acsomega.2c05605

CrossRef Full Text | Google Scholar

Hoang, D. T., Chernomor, O., Von Haeseler, A., Minh, B. Q., Vinh, L. S. (2018). UFBoot2: improving the ultrafast bootstrap approximation. Mol. Biol. Evol. 35 (2), 518–522. doi: 10.1093/molbev/msx281

PubMed Abstract | CrossRef Full Text | Google Scholar

Jyoti, K., Baunthiyal, M., Singh, A. (2016). Characterization of silver nanoparticles synthesized using Urticadioica Linn. leaves and their synergistic effects with antibiotics. J. Rad. Res. Appl. Sci. 9, 217–227. doi: 10.1016/j.jrras.2015.10.002

CrossRef Full Text | Google Scholar

Kalyaanamoorthy, S., Minh, B. Q., Wong, T. K. F., von Haeseler, A., Jermiin, L. S. (2017). Model Finder: fast model selection for accurate phylogenetic estimates. Nat. Methods 14 (6), 587–589. doi: 10.1038/nmeth.4285

PubMed Abstract | CrossRef Full Text | Google Scholar

Karthik, L., Kumar, G., Kirthi, A. V., Rahuman, A. A., Rao, K. V. B. (2014). Streptomyces sp. LK3 mediated synthesis of silver nanoparticles and its biomedical application. Bioprocess Biosystem Eng. 37, 261–267. doi: 10.1007/s00449-013-0994-3

CrossRef Full Text | Google Scholar

Katoh, K., Standley, D. M. (2013). MAFFT multiple sequence alignment software version 7: improvements in performance and usability. Mol. Biol. Evol. 30 (4), 772–780. doi: 10.1093/molbev/mst010

PubMed Abstract | CrossRef Full Text | Google Scholar

Kim, W. K., Park, M. S., Hahm, S. S., Yu, S. H. (2006). Two new records of penicillium associated with blue moldy bulbs of lily in Korea. Microbiology. 34 (4), 176–179. doi: 10.4489/MYCO.2006.34.4.176

CrossRef Full Text | Google Scholar

Kim, W. K., Sang, H. K., Woo, S. K., Park, M. S., Paul, N. C., Yu, S. H. (2007). Six species of Penicillium associated with blue mold of grape. Mycobiology. 35 (4), 180–185. doi: 10.4489/MYCO.2007.35.4.180

PubMed Abstract | CrossRef Full Text | Google Scholar

Kumar, S. A., Abyaneh, M. K., Gosavi, S. W., Kulkarni, S. K., Pasricha, N., Ahmad, A., et al. (2007). Nitrate reductase-mediated synthesis of silver nanoparticles from AgNO3. Biotechnol. Lett. 29, 439–445. doi: 10.1007/s10529-006-9256-7

PubMed Abstract | CrossRef Full Text | Google Scholar

Larsen, T. O., Lange, L., Schnorr, K., Stender, S., Frisvad, J. C. (2007). Solistatinol, a novel phenolic compactin analogue from Penicillium solitum. Tetrahedron Lett. 48 (7), 1261–1264. doi: 10.1016/j.tetlet.2006.12.038

CrossRef Full Text | Google Scholar

Majeed, A., Muhammad, Z. (2018). Potato production in Pakistan: challenges and prospective management strategies–A review. Pak. J. Bot. 50 (5), 2077–2084.

Google Scholar

Minh, B. Q., Schmidt, H. A., Chernomor, O., Schrempf, D., Woodshams, M. D., Haeseler, A. V., et al. (2020). IQ-TREE 2: new models and efficient methods for phylogenetic inference in the genomic era. Mol. Biol. Evol. 37 (5), 1530–1534. doi: 10.1093/molbev/msaa015

PubMed Abstract | CrossRef Full Text | Google Scholar

Mourdikoudis, S., Pallares, R. M., Thanh, N. T. (2018). Characterization techniques for nanoparticles: comparison and complementarity upon studying nanoparticle properties. Nanoscale. 10 (27), 12871–12934. doi: 10.1039/C8NR02278J

PubMed Abstract | CrossRef Full Text | Google Scholar

Nanda, A., Majeed, S., Abdullah, M. S., Nayak, B. K., Rizvi, E. H. (2015). Efficacy of nanosilver from soil fungus enhancing the antiseptic activity of Ciprofloxacin against pathogenic bacteria. Der. Pharma Chem. 7 (6), 141–146.

Google Scholar

Nassar, A. A., Eid, A. M., Atta, H. M., El Naghy, W. S., Fouda, A. (2023). Exploring the antimicrobial, antioxidant, anticancer, biocompatibility, and larvicidal activities of selenium nanoparticles fabricated by endophytic fungal strain Penicillium verhagenii. Sci. Rep. 13 (1), 9054. doi: 10.1038/s41598-023-35360-9

PubMed Abstract | CrossRef Full Text | Google Scholar

Nayak, R. R., Pradhan, N., Behera, D., Pradhan, K. M., Mishra, S., Sukla, L. B., et al. (2011). Green synthesis of silver nanoparticle by Penicillium purpurogenum NPMF: the process and optimization. J. Nanoparticle Res. 13 (8), 3129–3137. doi: 10.1007/s11051-010-0208-8

CrossRef Full Text | Google Scholar

Niraimathi, K. L., Sudha, V., Lavanya, R., Brindha, P. (2013). Biosynthesis of silver nanoparticles using Alternanthera sessilis (Linn.) extract and their antimicrobial, antioxidant activities. Colloids Surfaces B Biointer 102, 288–291. doi: 10.1016/j.colsurfb.2012.08.041

CrossRef Full Text | Google Scholar

Patil, H. V., Nithin, K. S., Sachhidananda, S., Chandrashekara, K. T., Kumar, S. (2019). Mycofabrication of bioactive silver nanoparticle: Photo catalyzed synthesis and characterization to attest its augmented bio-efficacy. Arabian J. Chem. 12 (8), 4596–4611. doi: 10.1016/j.arabjc.2016.07.009

CrossRef Full Text | Google Scholar

R Core Team (2023). R: a language and environment for statistical computing (Vienna: R Foundation for Statistical Computing). Available at: https://www.r-project.org.

Google Scholar

Rose, G. ,. K., Raman, S., Rishi, P., Soni, S. K. (2019). Optimization of the biological synthesis of silver nanoparticles using Penicillium oxalicum GRS-1 and their antimicrobial effects against common food-borne pathogens. Green Process. Synthesis 8 (1), 144–156. doi: 10.1515/gps-2018-0042

CrossRef Full Text | Google Scholar

Rudrappa, M., Kumar, R. S., Nagaraja, S. K., Hiremath, H., Gunagambhire, P. V., Almansour, A. I., et al. (2023). Myco-nanofabrication of silver nanoparticles by Penicillium brasilianum NP5 and their antimicrobial, photoprotective and anticancer effect on MDA-MB-231 breast cancer cell line. Antibiotics. 12 (3), 567. doi: 10.3390/antibiotics12030567

CrossRef Full Text | Google Scholar

Sarsar, V., Selwal, M. K., Selwal, K. K. (2015). Biofabrication, characterization and antibacterial efficacy of extracellular silver nanoparticles using novel fungal strain of Penicillium atramentosum KM. J. Saudi Chem. Society. 19 (6), 682–688. doi: 10.1016/j.jscs.2014.07.001

CrossRef Full Text | Google Scholar

Sasidharan, D., Namitha, T. R., Johnson, S. P., Jose, V., Mathew, P. (2020). Synthesis of silver and copper oxide nanoparticles using Myristica fragrans fruit extract: antimicrobial and catalytic applications. Sustain. Chem. Pharm. 16, 100255. doi: 10.1016/j.scp.2020.100255

CrossRef Full Text | Google Scholar

Shahzadi, I., Shah, A. S. M., Shah, M. M., Ismail, T., Fatima, N., Siddique, M., et al. (2022). Antioxidant, cytotoxic, and antimicrobial potential of silver nanoparticles synthesized using Tradescantia pallida extract. Front. Bioengr. Biotechnol. 10. doi: 10.3389/fbioe.2022.907551

CrossRef Full Text | Google Scholar

Thul, S. T., Sarangi, B. K., Pandey, R. A. (2013). Nanotechnology in agroecosystem: implications on plant productivity and its soil environment. Expert Opin. Environ. Biol. 2, 2–7. doi: 10.4172/2325-9655.1000101

CrossRef Full Text | Google Scholar

Wan Mat Khalir, W. K. A., Shameli, K., Jazayeri, S. D., Othman, N. A., Che Jusoh, N. W., Hassan, N. M. (2020). Biosynthesized silver nanoparticles by aqueous stem extract of Entada spiralis and screening of their biomedical activity. Front. Chem. 8. doi: 10.3389/fchem.2020.00620

CrossRef Full Text | Google Scholar

Yassin, M. A., Elgorban, A. M., El-Samawaty, A. E. M. A., Almunqedhi., B. M. A. (2021). Biosynthesis of silver nanoparticles using Penicillium verrucosum and analysis of their antifungal activity. Saudi J. Biol. Sci. 28 (4), 2123–2127. doi: 10.1016/j.sjbs.2021.01.063

PubMed Abstract | CrossRef Full Text | Google Scholar

Yassin, M. A., El-Samawaty, A. E. M. A., Dawoud, T. M., Abd-Elkader, O. H., Al Maary, K. S., Hatamleh, A. A., et al. (2017). Characterization and anti-Aspergillus flavus impact of nanoparticles synthesized by Penicillium citrinum. Saudi J. Biol. Sci. 24 (6), 1243–1248. doi: 10.1016/j.sjbs.2016.10.004

PubMed Abstract | CrossRef Full Text | Google Scholar

Yousaf, A., Waseem, M., Javed, A., Baig, S., Ismail, B., Baig, A., et al. (2022). Augmented anticancer effect and antibacterial activity of silver nanoparticles synthesized by using Taxus wallichiana leaf extract. Peer J. 10, e14391. doi: 10.7717/peerj.14391

CrossRef Full Text | Google Scholar

Zhang, D., Gao, F., Jakovlić, I., Hong, Z., Zhnag, J., Li, W. X., et al. (2020). PhyloSuite: an integrated and scalable desktop platform for streamlined molecular sequence data management and evolutionary phylogenetics studies. Mol. Ecol. resources. 20 (1), 348–355. doi: 10.1111/1755-0998.13096

CrossRef Full Text | Google Scholar

Zhang, T., Huang, C., Deng, C., Zhang, Y., Feng, Y., Hu, J., et al. (2020). First report of corm rot on saffron caused by Penicillium solitum in China. Plant Dis. 104, 579–579. doi: 10.1094/PDIS-09-19-1927-PDN

CrossRef Full Text | Google Scholar

Zhang, Y. J., Zhang, S., Liu, X. Z., Wen, H. A., Wang, M. (2010). A simple method of genomic DNA extraction suitable for analysis of bulk fungal strains. Lett. Appl. Microbiol. 51 (1), 114–118. doi: 10.1111/j.1472-765X.2010.02867.x

PubMed Abstract | CrossRef Full Text | Google Scholar

Zonooz, N. F., Salouti, M. (2011). Extracellular biosynthesis of silver nanoparticles using cell filtrate of Streptomyces sp. ERI-3. Scientia Iran. 18 (6), 1631–1635. doi: 10.1016/j.scient.2011.11.029

CrossRef Full Text | Google Scholar