The Potential Role of Marine Fungi in Plastic Degradation – A Review

Zeghal, Emna; Vaksmaa, Annika; Vielfaure, Hortense; Boekhout, Teun; Niemann, Helge

doi:10.3389/fmars.2021.738877

REVIEW article

Front. Mar. Sci., 29 November 2021

Sec. Aquatic Microbiology

Volume 8 - 2021 | https://doi.org/10.3389/fmars.2021.738877

The Potential Role of Marine Fungi in Plastic Degradation – A Review

$\r\nEmna Zeghal*$ Emna Zeghal^1*

Annika Vaksmaa^1*

Hortense Vielfaure^1,2

Teun Boekhout^3,4

Helge Niemann^1,5,6

¹Department of Marine Microbiology and Biogeochemistry, Royal Netherlands Institute for Sea Research (NIOZ), Texel, Netherlands
²Université de Paris, INSERM U1284, Center for Research and Interdisciplinarity (CRI), Paris, France
³Westerdijk Fungal Biodiversity Institute, Utrecht, Netherlands
⁴Institute for Biodiversity and Ecosystem Dynamics (IBED), University of Amsterdam, Amsterdam, Netherlands
⁵Department of Earth Sciences, Faculty of Geosciences, Utrecht University, Utrecht, Netherlands
⁶CAGE – Centre for Arctic Gas Hydrate, Environment and Climate, Arctic University of Norway, Tromsø, Norway

Plastic debris has been accumulating in the marine realm since the start of plastic mass production in the 1950s. Due to the adverse effects on ocean life, the fate of plastics in the marine environment is an increasingly important environmental issue. Microbial degradation, in addition to weathering, has been identified as a potentially relevant breakdown route for marine plastic debris. Although many studies have focused on microbial colonization and the potential role of microorganisms in breaking down marine plastic debris, little is known about fungi-plastic interactions. Marine fungi are a generally understudied group of microorganisms but the ability of terrestrial and lacustrine fungal taxa to metabolize recalcitrant compounds, pollutants, and some plastic types (e.g., lignin, solvents, pesticides, polyaromatic hydrocarbons, polyurethane, and polyethylene) indicates that marine fungi could be important degraders of complex organic matter in the marine realm, too. Indeed, recent studies demonstrated that some fungal strains from the ocean, such as Zalerion maritimum have the ability to degrade polyethylene. This mini-review summarizes the available information on plastic-fungi interactions in marine environments. We address (i) the currently known diversity of fungi colonizing marine plastic debris and provide (ii) an overview of methods applied to investigate the role of fungi in plastic degradation, highlighting their advantages and drawbacks. We also highlight (iii) the underestimated role of fungi as plastic degraders in marine habitats.

Ocean Plastic Pollution

Plastics are man-made materials of mostly petrochemical origin – so-called conventional plastics that are commonly considered as non-biodegradable (Wayman and Niemann, 2021). Most conventional plastics comprise a carbon-carbon backbone, e.g., polyethylene (PE), polypropylene (PP) and polystyrene (PS), while other plastics feature heteroatoms, e.g., polyethylene terephthalate (PET), polyurethane (PU) or polyamides (PA, Nylon). Conventional plastics are used in nearly all industrial sectors, most importantly packaging, construction and transport. The global annual production of plastics reached 359 Mt in 2018 (PlasticsEurope, 2020). Recently, biopolymer alternatives, based on renewable sources (e.g., starch and cellulose) have been developed, but their global market share is still small. In 2020, the global production of bioplastics amounted to approximately 2 Mt (Bioplastics Market Data update, 2020). Among the plastic types produced from renewable carbon sources, approximately half are biodegradable, while the second half is non-biodegradable.

A substantial fraction of plastic waste is mismanaged (Geyer et al., 2017), and it has been estimated that this fraction represented an average of 80 Mt (60 to 99 Mt) accumulated in total (Lebreton and Andrady, 2019). Mismanaged plastic waste ends up in all ecosystem compartments, such as soils (Chae and An, 2018), lakes (Mason et al., 2016) and rivers (Lebreton et al., 2017). Thus, freshwater bodies function as a transport vector for plastic ultimately reaching the ocean though the magnitude of this transport mechanism is discussed controversially (Weiss et al., 2021). In addition, plastic litter can be airborne, thus, the atmospheric deposition of plastic litter is a potentially important source for the ocean’s plastic budget (Liss, 2020). Indeed, plastic litter has emerged as a major pollution issue in marine environments (Eriksen et al., 2014; UNEP, 2014; van Sebille et al., 2015; Wayman and Niemann, 2021). Plastic debris forms the most abundant component of marine litter, accounting for up to 95% of waste found on shorelines, ocean surface water and the seafloor (Galgani et al., 2015). In fact, sedimented plastic litter might become a stratigraphic marker horizon of the Anthropocene epoch (Zalasiewicz et al., 2016). It has been estimated that 0.1% (Cózar et al., 2015) to up to 4.6% (Jambeck et al., 2015) of the global plastic production enters the ocean. As a result, the total accumulated plastic waste in the ocean might have reached 320 Mt in the year 2015 (Wayman and Niemann, 2021).

Plastic floating at the ocean surface is typically dominated by PE and PP, roughly in accordance with global production figures (Erni-Cassola et al., 2019). However, plastic debris in the ocean varies in size: macroplastics (>5 mm), microplastics (1 μm – 5 mm) and nanoplastics (<1 μm) (Wayman and Niemann, 2021). Several studies have tried to quantify the different size fractions to estimate the total concentration of plastics and the fate of it in marine environments. For example, in the Mediterranean Sea, the density of floating microplastic was about 2.5 × 10⁵ items per km² (Cózar et al., 2015). The abundance of floating plastic in the ocean is usually determined by surface trawling with nets (typically > 300 μm mesh size). Consequently, these methods discriminate against smaller size classes, which could account for an important fraction of the floating plastic budget (Poulain et al., 2019). Furthermore, surface trawls do not account for submerged and sedimented plastics debris (Woodall et al., 2014). Finally, the distribution of floating plastic is not homogenous, as large quantities concentrate in subtropical ocean gyres and enclosed basins, making balanced sampling efforts over large areas difficult (Lindeque et al., 2020).

Microbial Biofilms on Marine Plastic Debris

Rapid microbial colonization occurs on any available material that ends up in the ocean, whether it is of natural or synthetic origin (such as plastic debris). From a microbial perspective, transiting from pelagic to a particle-attached lifestyle provides advantages; e.g., better access to nutrients, and protection against UV exposure and grazing (de Carvalho, 2018). Several studies have investigated the composition of microbial communities living on plastic materials in different marine environments (Zettler et al., 2013; Amaral-Zettler et al., 2015; Eich et al., 2015; Oberbeckmann et al., 2016; Debroas et al., 2017; Dussud et al., 2018; Ogonowski et al., 2018; Miao et al., 2019; Dudek et al., 2020; Krause et al., 2020; Vaksmaa et al., 2021b). Some of these reported a difference in community structure when comparing microbes in biofilms on plastics to those in the surrounding seawater or those attached to natural surfaces. A detailed overview of this matter is compiled in Wright et al. (2020). However, most studies applied amplicon sequencing of the 16S rRNA gene, and focused on bacterial and archaeal communities in biofilms attached to the plastic debris. In contrast, fungal community composition on plastic in the marine environment has, until now, been investigated seldomly (Table 1).

TABLE 1

Table 1. Studies on the diversity of fungal communities on microplastics in marine environments.

A Brief Introduction to the Fungal Kingdom

The fungal kingdom constitutes a major lineage within the domain Eukarya and diverged from a common ancestor with the animals >800 million years ago (Parfrey et al., 2011; Chang et al., 2015). Fungi exhibit highly diverse lifestyles and can cope with different redox conditions. The majority of fungi seemingly prefer oxic environments, however some fungal species inhabit oxygen minimum zones (Stief et al., 2014). Furthermore, anaerobic fungi (mainly studied in gut microbiomes) have been identified (Gruninger et al., 2014; Mura et al., 2019). Morphologically, fungi may be unicellular (e.g., yeasts and cells with a flagellum such as zoospores), filamentous (e.g., molds and mushrooms) or dimorphic (i.e., they exists in two forms, yeast-like single cells or hyphae forming) (Boyce and Andrianopoulos, 2015). They can be found as free-living organisms, in mutualistic symbiotic associations (such as those forming mycorrhizas, lichens, in gut microbiomes) (Watkinson, 2016) or as parasitic pathogens of several plants and animals, including humans (Szabo and Bushnell, 2001). Fungi are ubiquitous and occur throughout terrestrial, freshwater and marine environments (Sutherland, 1916; Raghukumar, 2017; Walker et al., 2017; Gladfelter et al., 2019).

Taxonomically, nineteen major fungal phyla are recognized: Aphelidiomycota, Ascomycota, Basidiobolomycota, Basidiomycota, Blastocladiomycota, Calcarisporiellomycota, Caulochytriomycota, Chytridiomycota, Entomophthoromycota, Entorrhizomycota, Glomeromycota, Kickxellomycota, Monoblepharomycota, Mortierellomycota, Mucoromycota, Neocallimastigomycota, Olpidiomycota, Rozellomycota, and Zoopagomycota (Wijayawardene et al., 2020). However, the phylogeny and taxonomy of the fungal kingdom has been a matter of debate (Hibbett et al., 2007; Spatafora et al., 2016, 2017). Some fungal phyla are rarely sampled and our understanding of the deeply branching groups is insufficient (Naranjo-Ortiz and Gabaldón, 2019). Lately, the number of available fungal genomes has been increasing. But these new data showed that complex inter-species relationships occur, such as introgression and hybridization (Gabaldón, 2020), that blur the definition of a species. The estimated total number of fungal species could range from 2 to 4 million (Hawksworth and Lücking, 2017), but only ∼100000 have been described (Wu et al., 2019) of which only ∼1100 species originate from marine environments (Amend et al., 2019).

Recently, an online database, www.marinefungi.org, containing marine fungal species was created (Jones et al., 2019). Many fungal species are found in both, terrestrial and marine environments (Gladfelter et al., 2019). It has been proposed that early diverging fungi, Chytridiomycota and Rozellomycota, originate from aquatic environments (Berbee et al., 2017, 2020). These phyla also have members found in the present-day ocean. On the other hand, fungi from the Ascomycota and Basidiomycota phyla, commonly present in marine environments, are proposed to originate from terrestrial ancestors. Because of this difference in origin (terrestrial vs. aquatic), a clear definition of “marine fungus” is challenging. The recent definition suggests that a marine fungus is “any fungus that is recovered repeatedly from marine habitats and: (1) is able to grow and/or sporulate (on substrata) in marine environments; or (2) forms symbiotic relationships with other marine organisms; or (3) is shown to adapt and evolve at the genetic level or is metabolically active in marine environments” (Pang et al., 2016). Marine fungi are found ubiquitously in the ocean (Comeau et al., 2016; Tisthammer et al., 2016; Raghukumar, 2017) including coastal environments (Taylor and Cunliffe, 2016; Picard, 2017; Banos et al., 2020), mangroves (Hyde and Lee, 1995; Alias et al., 2010; Pang et al., 2010; Lee et al., 2019), the water column (Richards et al., 2015; Tisthammer et al., 2016; Morales et al., 2019) and sediments (Kohlmeyer and Kohlmeyer, 1979a; Khudyakova et al., 2000; Mouton et al., 2012; Tisthammer et al., 2016). Marine fungi have also been detected in extreme marine habitats such as the deep sea biosphere (Orsi et al., 2013; Rédou et al., 2015), the Arctic (Rämä et al., 2017; Hassett et al., 2019) and oxygen minimum zones (Cathrine and Raghukumar, 2009; Jebaraj et al., 2010; Manohar et al., 2015).

Metabolically, fungi participate in different biogeochemical processes and occupy a plethora of ecological niches. Fungi play a major role in decomposing recalcitrant substrates, making them an integral part of food web structures, contributing to carbon cycling and nutrient regeneration in, at least, terrestrial environments. For example, saprophytic fungi accelerate carbon and nitrogen cycling and symbiotic fungi such as mycorrhiza networks, enhance primary production in symbionts and hosts (Lindahl et al., 2007; Walder et al., 2012). Similar to terrestrial systems, parasitic fungi in aquatic environments were found to have a great impact on pelagic food webs and thus biogeochemical cycling (Jobard et al., 2010; Sime-Ngando, 2012). Also some symbiotic interactions are known from the marine environment, for example, with phytoplankton seaweeds and sponges (Rasconi et al., 2011; Richards et al., 2012; Webster and Taylor, 2012; Du et al., 2019). Similar to terrestrial systems, fungi in coastal and surface marine environments were found to degrade wood (lignin, cellulose and hemicellulose) (Bucher et al., 2004) and remains of marine animals (Kohlmeyer and Kohlmeyer, 1979b,c; Raghukumar, 2017). Marine fungi were furthermore found to degrade complex components of algae such as agar (in laboratory conditions; Balabanova et al., 2018) and fungi dominate the microbial composition of bathypelagic marine snow where they might play the role as saprotrophs (Bochdansky et al., 2017). Fungi contribute to different nitrogen cycle processes such as nitrification (Falih and Wainwright, 1995) and denitrification (Shoun et al., 1992; Stief et al., 2014; Maeda et al., 2015) in both, terrestrial and the marine environment (Cathrine and Raghukumar, 2009). Marine fungi mobilize metals by excreting siderophores and act as bio-sorbents for some metals, thereby alleviating metal toxicity (Taboski et al., 2005; Vala, 2010). These processes influence the cycles of several elements among them: Fe, Mn, Hg, Ni, Zn, Ag, Cu, Cd, and Pb (Gadd, 2004). Finally, some fungi break down rocks and minerals to harvest nutrients (Ortega-Morales et al., 2016).

Life on Plastic Is Fantastic: Fungal Colonization of Marine Plastic Debris

Fungi in Marine Environments as Part of Marine Plastic Debris Associated Biofilms

Marine fungi are generally understudied, which is also reflected by the relatively limited number of studies targeting fungi on marine plastic debris (MPD) (Jacquin et al., 2019). Oberbeckmann et al. (2016) conducted a seasonal comparison of microbial communities including both bacteria and fungi on submerged PET bottles, glass slides, and seawater in the North Sea. Fungal communities were represented by Ascomycota, Basidiomycota and Chytridiomycota. The study showed that the PET-attached eukaryotic communities (fungi among them) varied significantly with season and location. Kettner et al. (2017, 2019) conducted exposure experiments with PE and PS in the Baltic Sea and the river Warnow and investigated colonization of these plastic surfaces by fungi. The fungal genus Chytridium, as well as fungi-like Rhinosporideacae, Rhizidiomyces, and Pythium taxa, had a high read count on both plastic types at both locations. However, a substantial number of sequences was assigned as unclassified fungi. The fungal community composition was significantly influenced by location but not polymer type. Furthermore, the alpha diversity was significantly lower for PE and PS compared to the surrounding water and wood particles. De Tender et al. (2017) conducted a 44-week experiment during which PE plastic sheets and dolly ropes were weighed down close to the sediment at a harbor and an offshore location in the North Sea. Similar to the Baltic Sea studies by Kettner et al. (2017, 2019), they found that the Ascomycota were highly abundant followed by a smaller fraction of Basidiomycota and Mucoromycota. Furthermore, a minor fraction of members of Ascomycota from the Lecanoromycetes class (Physconia, Candelariella, Caloplaca) were identified. Analyses on the beta diversity of the fungal community composition showed statistically significant effects of sample type (natural substrate vs. plastic polymers), environment, and exposure time. Some of the detected species were previously identified as potential PE degraders in terrestrial environments: Cladosporium cladosporioides (Bonhomme et al., 2003) and Fusarium redolens (Albertsson, 1980; Albertsson and Karlsson, 1990).

Recently, Lacerda et al. (2020) studied the fungal diversity associated with plastics in the surface waters of the Western South Atlantic and the Antarctic Peninsula by investigating three different molecular marker genes for fungal identification: ITS2 (Internal transcribed spacer), the variable regions V4 and V9 of the 18S rRNA gene sequence. To date, this is the only study aiming to resolve fungal diversity on plastic using multiple marker genes. Across the tested marker genes, a total of 64 different fungal orders were associated with plastics. The primers targeting the 18S rRNA gene (V4 and V9 regions) were able to detect a higher number of Chytridiomycota. Some taxa that were totally omitted by the ITS2 marker were detected, such as Rozellomycota, Zoopagomycota, Aphelidomycota, and Blastocladiomycota. Across all samples, the genus Aspergillus was the most abundant. Some of its OTUs were assigned at the species level, identifying A. vitricola, A. restricus, and A. wentii. None of the identified strains were previously reported as plastic degraders, although other Aspergillus species have been shown to be able to oxidize different plastic types (Table 2). Lacerda and colleagues also reported on fungal taxa, such as Aphelidomycota, Zoopagomycota, Mucoromycota, and Blastocladiomycota, that had previously not been detected to colonize plastic in the marine environment.

TABLE 2

Table 2. Selection of fungal strains that showed plastic degradation potential.

In contrast to environmental studies, Kirstein et al. (2018) studied the microbial composition formed on microplastics under controlled laboratory conditions. Their set-up consisted of a flow-through system with North Sea water in which HDPE (High Density Polyethylene), LDPE (Low Density Polyethylene), PP, PS and PET were incubated in the dark. The 18S rRNA gene sequencing analysis of the eukaryotic community of biofilms revealed that the highest fungal read abundances belonged to Chytridiomycota (up to 3% of sequences on PET). This can be explained by this taxa’s dominance throughout aquatic environments (Comeau et al., 2016) or the compatibility of biofilm presence on PET and chytrid’s parasitic lifestyle.

Plastic Biodegradation Potential of Fungi

Biodegradation is the degradation of compounds and substrates mediated by living organisms, most commonly microorganisms. The soluble products of biodegradation (typically low molecular weight compounds) are absorbed or assimilated by the microorganisms. The biodegradation can be partial or complete. Complete biodegradation results in the formation of CO₂ and is also referred to as biomineralization. On the other hand, degradation of organic matter without a terminal electron acceptor, conditions that are countered in some reduced environments, leads to the formation of CH₄ and/or other short-chain hydrocarbons. In natural environments, biodegradation is mediated by enzymes or by other compounds (such as acids and peroxides), secreted by microorganisms.

Fungi are able to degrade synthetic compounds; e.g., persistent organic pollutants (POPs) (Singleton, 2001), polycyclic aromatic hydrocarbons (PAHs) (Cerniglia and Sutherland, 2001), benzene, toluene, ethylbenzene and xylenes (BTEX compounds) (Buswell, 2001) and pesticides (Pinto et al., 2012). The metabolic versatility of fungi and ability to degrade complex compounds indicates that biodegradation of plastics in the environment could be a potential metabolic trait of some fungi (Vaksmaa et al., 2021a). To date, some plastic degrading fungi have indeed been identified mostly from the Ascomycete phylum to which also Aspergillus, Fusarium, and Penicillium belong (Table 2 Fusarium sp. and F. oxysporum isolated from soil provoked weight loss of Nylon, PE, and PU) (Tachibana et al., 2010; Raghavendra et al., 2016). F. solani from a collection hydrolyzed PET to terephthalic acid (TPA) via a cutinase (Ronkvist et al., 2009). Furthermore, several strains belonging to Penicillium are considered as potential plastic degraders. P. chrysogenum, P. oxalicum, P. simplicissimum isolated from soil (Yamada-Onodera et al., 2001; Sowmya et al., 2012; Ojha et al., 2017) and Penicillium sp. isolated from seawater (Alshehrei, 2017) showed potential to degrade PE. Similar to Penicillium, different species belonging to the genus Aspergillus were found to be potential plastic degraders as well (Table 2). A. flavus isolated from soil (Deepika and Madhuri, 2015), wax moth gut (Zhang et al., 2020) and a marine environment (Sangeetha Devi et al., 2015; Alshehrei, 2017) exhibited the potential to degrade PE and A. niger isolated from soil (Deepika and Madhuri, 2015; Raghavendra et al., 2016) and seawater (Alshehrei, 2017) showed potential to degrade PE and PU. Also, A. terreus isolated from soil (Zahra et al., 2010), mangrove sediments (Ameen et al., 2015; Sangale et al., 2019) and seawater (Alshehrei, 2017) were potentially able to degrade PE. In addition to these species, several other types of Aspergillus strains were considered as potential PE and PU degraders. Many of the plastic degrading species that were isolated from terrestrial environments (Table 2) are also found in marine habitats. However, it has not been confirmed if all of the plastic degrading strains found in terrestrial environments perform equally well in the marine realm.

The enzymes utilized by plastic degrading fungi in the environment are typically not constrained. However, fungi produce a wide range of enzymes that have the potential to break down the chemical bonds of the plastic polymers (Figure 1). Amongst these are manganese peroxidase (MnP) and lignin peroxidase (LiP), which are commonly associated with lignin degradation (Xu et al., 2013). These enzymes catalyze oxidation-reduction reactions, involving free radicals, transforming several compounds into oxidized or polymerized products (Wei and Zimmermann, 2017). Peroxidase are also used in industrial applications for degrading recalcitrant organic pollutants, PAHs, industrial dyes and chlorophenols (Qin et al., 2014). Lignin peroxidase is characterized by a high redox potential, and enables oxidation of non-phenolic aromatic compounds. Another enzyme that might be involved in plastic degradation is laccase, a multicopper oxidase, which is a well classified lignin-modifying enzyme (Mehra et al., 2018) and mediates the oxidation of the polymers’ carbon backbone (Amobonye et al., 2021).

FIGURE 1

Figure 1. Schematic of important plastic types encountered in the marine environment. Fungal enzymes and fungal groups potentially involved in plastic degradation are displayed. Blue underline indicates fungi producing laccase. Green underline indicates fungi producing peroxidase, Yellow underline indicates fungi producing polyesterase and red underline indicates fungi producing cutinase. PE, polyethylene; PP, polypropylene; PS, polystyrene; PU, polyurethane; Nylon, polyamides; PET, polyethylene terephthalate.

Elevated laccase, manganese peroxidase and lignin peroxidase activities were observed during PE degradation by a fungal consortium in a mangrove (Ameen et al., 2015). It appears likely that these enzymes also play a role in potential plastic degradation in the ocean. Marine adapted fungi have the ability to regulate the expression of their enzymes according to salinity. Cultivated in marine conditions, Peniophora sp., for example, showed multigene transcription of ligninolytic laccase enzymes (Otero et al., 2017). Fungi isolated from marine environments can also produce enzymes that allow them to grow in liquid media with sole carbon sources such as agar, alginate, carrageenans, laminarians, and ulvans, i.e., polymers which are common in the marine realm (Wang et al., 2016). However, whether these compounds are also utilized by marine fungi in situ, i.e., in the ocean, still needs to be shown. Similarly to several biopolymers in the terrestrial realm, these marine polymers also feature chemical similarities with some plastic types (presence of aromatic compounds, presence of carbonyl groups). The ability of marine fungi to regulate their metabolism and to adapt to different environments and substrates indicates that the number of marine fungi with the potential to degrade plastics could be underestimated.

Analytical Tools for Assessing the Potential for Fungi-Mediated Plastic Degradation

Relatively little is known about the potential for microbial plastic biodegradation in the marine environment (Wayman and Niemann, 2021). However, the chemical structures of most plastic polymers render them rather durable, which makes it challenging to evaluate the biodegradability of conventional plastics and to identify the key organisms mediating this process. As the majority of studies evaluating plastic breakdown have been conducted in the terrestrial environment (Ru et al., 2020), the methods reviewed below do not focus solely on the marine systems (Table 3).

TABLE 3

Table 3. Most common methods used to assess plastic degradation advantages and disadvantages.

Gravimetric Measurements and Growth of Biomass

To date, the most commonly applied technique to assess plastic biodegradation is based on gravimetric measurement of weight/mass loss of the polymer over a specific time period during which the plastic is exposed to an environmental matrix or to cultured microbes. Weight loss of plastic has been demonstrated both in studies where plastics were exposed to soils, the marine water column and sediments (Syranidou et al., 2017; Welden and Cowie, 2017) as well as in studies focusing on the capability of a single strain to degrade specific plastic polymers (Table 2). However, in environmental studies, it remains unclear to which extent the observed plastic breakdown was due to solely fungal activity. In the environment, the observed breakdown may be facilitated by microorganisms other than fungi and/or by microbial consortia, and/or by abiotic factors, such as mechanical degradation. These factors remain inseparable from potential fungal biodegradation. In contrast, laboratory studies with single strains decrease the number of biotic and abiotic factors, that may contribute to the plastic degradation. Fungal isolates recovered from municipal solid waste revealed that Fusarium oxysporum, Aspergillus fumigatus, Lasiodiplodia crassispora, Aspergillus niger, Penicillium sp., and Trichoderma harzianum were all able to cause a weight loss of PE as well as PU (Raghavendra et al., 2016). A. niger showed the highest biodegradation efficiency leading to a weight loss of 2.9, 4.3, and 5.1% of LDPE sheets and 0.8, 1.5, and 2.2% of PU sheets exposed for 30, 60 and 90 days, respectively. Fusarium oxysporum as well as Aspergillus sp. have previously been shown to cause weight loss of LDPE (Das and Kumar, 2014). Trichoderma viride and Aspergillus nomius, isolated from landfill soil, caused weight loss of LDPE films of 5.1 and 6.6%, respectively, after 45 days (Munir et al., 2018). Cladosporium tenuissimum caused 25.9 and 65.3% of weight loss of PE-PU foams with and without flame retardants, respectively (Álvarez-Barragán et al., 2016). The marine fungus Zalerion maritimum exposed to PE microplastics caused mass loss of 56.7 ± 2.9% of the plastic, corresponding to 43% of removal after 2 weeks of exposure (Paço et al., 2017).

Although determining the weight loss of plastic is a straightforward method, it requires a long monitoring time, ranging from months to years to yield measurable gravimetric changes, while short term studies often yield inconclusive results (Lee et al., 1991). Gravimetric measurements require post incubation treatments, i.e., the removal of the biofilm from the incubated plastic. This can easily cause measurement artifacts; e.g., the incomplete removal of biofilm or accidental removal of a polymer respectively leads to an under or overestimation of weight loss. Weight loss measurements indicate that plastic polymers indeed disintegrate over time, however, this type of measurement does not reveal whether the polymer is broken down physiochemically (e.g., plastics release lower molecular weight compounds as a result of photooxidation; Wayman and Niemann, 2021) or if the plastic polymer was hydrolyzed and metabolized by microbes. Some plastics (e.g., polyvinyl chloride) contain high quantities of additives which, if soluble, can be released, and thus bias weight loss measurements. Also, biomass figures (i.e., cell numbers, culture dry weight) are typically not reported for culture-based studies, making these investigations quantitatively non-repeatable, thus, severely limiting comparability. Hence, gravimetric measurements are insufficient to identify plastic degrading organisms and microbial kinetics, but should be accompanied by other methods.

Determining microbial biomass growth on plastic as the sole carbon source (e.g., monitoring cell numbers) has been used to infer the biodegradability of a specific polymer. Together with monitoring the weight loss of the polymer, some studies have measured an increase in fungal biomass as an indicator for the activity of fungi (Paço et al., 2017), and interpreted that the increase in fungal biomass occurred at the expense of carbon originating from the plastics.

Clearance Zone Formation

The growth of fungi at the expense of plastic can be monitored visually with degradation assays based on plates coated with agar and solubilized plastic. Inoculation at the surface and utilization of the plastic leads to the formation of clearance zones, referred to as ‘halos.’ Appearance of ‘halos’ on plates with plastics as the sole carbon source is used as an indicator for plastic degradation. The fungal species Cladosporium cladosporioides, Xepiculopsis graminea, and Penicillium griseofulvum and Leptosphaeria sp., isolated from plastic debris from the lake Zurich, formed clearance zones on PU. However, none of these strains were able to degrade polyethylene (Brunner et al., 2018). Attempts to use polyethylene and clearance zone formation have been successful for Aspergillus niger and Aspergillus flavus (Deepika and Madhuri, 2015).

Clearance zone tests allow for rapid visual observations. However, the technique has the drawback that it requires dissolving the polymer in an organic solvent that can be applied to the petri dish at relatively cold temperatures to avoid agar melting. Furthermore, remnants of the solvents (rather than the plastic) may act as a carbon source for the fungi, leading to false-positive results. In addition, bias associated with clearance zone formation is relatively large, as clearance zones are not uniform in size or shape. Finally, fungi with hyphae may grow through the plastic, thus gain access to the agar below, which can also lead to false-positive results. As agar also represents a carbon source, this test alone does not prove microbial plastic degradation.

Scanning Electron Microscopy

Scanning electron microscopy (SEM) is used to create a surface image by directing a high-intensity electron beam at the surface and scanning over this surface. SEM allows high magnification, thus offers high resolution at the nanometer range. SEM-based observations are used to examine and evaluate the colonization of plastic films or particles by microorganisms and to simultaneously visualize cracks, pits and deformations on the plastic surface (Zettler et al., 2013; Vaksmaa et al., 2021a), which in return can indicate if the polymer is degraded. SEM has been applied in several studies to investigate fungi on plastics, for example, to visualize the growth of C. tenuissimum and C. pseudocladosporioides hyphae within PE-PU foams (Álvarez-Barragán et al., 2016). Furthermore, Paço et al. (2017) visualized the attachment of Z. maritimum on PE. With SEM, also surface roughness of single plastic fragments can be visualized. Floating marine plastics often feature signs of abrasion, cracking and ongoing fragmentation (Zettler et al., 2013; Vaksmaa et al., 2021b). Also, plastics exposed to the marine environment developed such signs during the incubation. For example, Welden and Cowie (2017) exposed PE, PP and Nylon to marine sediment for 12 months and found breaks and increased fraying on nylon ropes, surface scratching and roughening on PE filament rope, cracks, fissures and finer surface fibers scaling off from PP.

Scanning electron microscopy is a rapid technique, and allows to visualize surface attachment and morphological microstructures. Observations by SEM without chemical fixation can be achieved by applying FIB-SEM (Focused Ion Beam milling combined with Scanning Electron Microscopy). However, SEM does not allow phylogenetic identification of the microbes (unless the strain-specific morphological characteristics allow this) and the formation and attachment of biofilms is not necessarily an indication for biodegradation. Furthermore, though SEM is a valuable tool to visualize surface defects (e.g., cracks) of the plastic, it does not allow to scale in Z-direction (i.e., to measure the depth of cracks). Alternatively, this may be achieved by atomic force microscopy (AFM). For example, an increase in surface roughness and formation of cracks and grooves on PE films were investigated with AFM after exposure to two different Penicillium strains (Ojha et al., 2017).

Fourier-Transform Infrared Spectroscopy

Fourier-transform infrared spectroscopy (FTIR) is a technique used to obtain an infrared spectrum of absorption, emission, and photoconductivity of a material allowing to determine the chemical identity of most polymers. Furthermore, the FTIR spectrum enables detection and semi-quantification of changes of the original polymer configuration, for example, the introduction of carbonyl groups during polymer oxidation (Xu et al., 2019; Almond et al., 2020). The degree of carbonylation can be enumerated by determining the carbonyl index (calculated from the ratio between the integrated band absorbance of the carbonyl and that of the methylene peaks). Carbonyl indexes, as a measure of degradation, has been applied for a variety of polymers, such as PU (Filip, 1979; Álvarez-Barragán et al., 2016), PE (Paço et al., 2017), PS (Tian et al., 2017), and PP (Sheik et al., 2015). PE degradation has been evaluated by FTIR in co-cultures of bacteria and fungi, Lysinibacillus xylanilyticus and A. niger, isolated from soil (Esmaeili et al., 2013). For example, Penicillium variabile CCF3219 strain decreased the carbonyl peaks of pre-oxidized 14C-βPS after 16 weeks of incubation and ozonation pre-treatment enhanced subsequent biodegradation (Tian et al., 2017). An additional advantage of FTIR is that it can be used for small plastic particles (the diffraction limit in IR spectroscopy is ∼10–20 μm).

Fourier-transform infrared spectroscopy is a straightforward and reliable technique, however, it often yields non-quantitative results that are difficult to compare between studies. Also, the attachment of biofilm on the plastic surfaces affects the plastics optical properties in the IR range because proteinic and polysaccharide contents of the biomass will change the polymer’s IR spectrum (Bonhomme et al., 2003). Samples must hence be pretreated to remove biofilms, e.g., using hydrogen peroxide (Löder and Gerdts, 2015) or sodium dodecyl sulfate (Zhang et al., 2020). These chemicals have been described as the least aggressive. Nevertheless, chemical treatments can modify the molecular structure of plastic surfaces, which can introduce biases.

Assays With ¹³C or ¹⁴C Labeled Polymers

Isotopically labeled plastics can be traced into biodegradation products sensitively and quantitatively (Lanctôt et al., 2018; Taipale et al., 2019). The first studies involving isotopically labeled plastics were conducted with the radio isotope ¹⁴C. The fungus Fusarium redolens liberated ¹⁴C-CO₂, originating from pulverized ¹⁴C-labeled HDPE (Albertsson, 1978, 1980; Albertsson et al., 1978). ¹⁴C labeled ¹⁴C-CO₂ formation was also evaluated after photoirradiation of ¹⁴C-αPS and ¹⁴C-βPS, exposed to garden soil and activated sludge, showing higher ¹⁴C-CO₂ formation in treatments with photo oxidized polymer. The authors quantified degradation rates and showed that complete degradation of the ¹⁴C-αPS polymer in garden soil would require 20 to 80 years and in activated sludge from 11 to 24 years (Guillet et al., 1974). ¹⁴C labeled polystyrene was also used to test PS degradation capabilities of 17 different fungal species in a 14 days incubation experiment during which 0 to 0.24% of the ¹⁴C-PS was degraded (Kaplan et al., 1979). Because radioactivity can be measured and quantified extremely sensitively, radio isotope probing allows determining extremely low plastic degradation rates. Nevertheless, the use of radio-chemicals entails the necessity for specialized laboratory facilities and trained personnel, and the radio-labeled base materials for synthesizing polymers are extremely expensive or not available at all. This makes the use of radio isotopes mostly impractical. However, using plastics labeled with stable isotopes (e.g., containing a high degree of ¹³C or ²H) provides a good alternative. Similar to radio isotope probing, stable isotope probing (SIP) offers the advantages to allow tracing plastic derived matter into degradation products (Sander et al., 2019; Taipale et al., 2019), though the ubiquitous presence of ¹³C and ²H in most types of matter makes SIP assays less sensitive compared to approaches with radio isotopes. Nevertheless, no study using ¹³C or ²H labeled conventional plastics (PE, PP, PET, PS, PU, and nylon) for investigating interactions of marine fungi and plastics has been published yet. On the other hand, Zumstein et al. (2018) used ¹³C-PBAT (Polybutylene adipate terephthalate) to study its microbial degradation in soil.

Other Methods

Additional methods to evaluate plastic degradation include the following techniques: (i) Respiratory measurements of O₂ consumption or CO₂ production, which can provide quantitative information of degradation, but cannot discriminate between different respiration pathways. (ii) Tensile resistance alterations of plastic can be used as a measure of the strength/integrity of the plastics, which will decrease as a function of degradation (yet, also physiochemically induced degradation reduces tensile strength). (iii) Thermo Gravimetrical Analysis (TGA) characterizes the thermal stability of a polymer, which can potentially indicate its degradation (similar to tensile strength). (iv) Differential scanning calorimetric (DSC) analysis assesses the thermal properties of synthetic polymers, such as glass transition Temperature (T_g).

Lower T_g temperatures are often related to a decrease in the stability, indicating degradation (Lucas et al., 2008). (v) High-Temperature Gel Permeation Chromatography (HT-GPC) provides information on the molecular weight (Mn%) and molecular weight distribution of the polymer. A decrease in Mn% is evidence of chain cleavage that can be related to microbial degradation. Nevertheless, just as alterations of tensile resistance, glass transition Temperature, thermal stability and the molecular weight will also change in response to physicochemical processes Finally, none of the other methods described in this section is able to unambiguously prove the occurrence of complete microbial biodegradation, from initial depolymerization to mineralization and biomass assimilation.

Limitations of Studying Fungal Communities

In comparison to bacteria, fungi in the marine realm are understudied and often overlooked. It seems likely that fungi are relevant as saprotrophs in general and may act as plastic degraders, yet this needs to be demonstrated in future studies. However, in comparison to investigating bacterial communities, taxonomic and physiological characterization of (marine) fungi is not as straightforward and standardized methods are generally lacking. Indeed, molecular studies on fungi still encounter classic difficulties and biases related to molecular techniques such as polymerase chain reaction (PCR) bias, library preparation bias, sequencing bias, bioinformatics biases and unequal sequencing depth. Perhaps the most hindering factors in molecular studies of fungi are: (i) nucleic acid extraction method bias (ii) marker gene bias when using 18S rRNA or ITS spacer and (iii) primer bias. In addition, also (iv) culture-based methods are hindered by the fact that identification based on morphological features (alone) is difficult, growth conditions are hard to determine and fungi have complex life cycles.

(i) Fungal genomic DNA extraction is less straightforward in comparison to extracting DNA from bacteria. Fungal cell walls are made of chitin making them more robust than a peptidoglycan bacterial cell wall (Fredricks et al., 2005; Shin, 2018). Breaking down fungal cells requires further steps such as the addition of lysing agents (for example, adapting the lysis buffer or adding enzymes such as cutinases) and/or mechanical disruption (e.g., increasing bead-beating steps or introducing freeze-thaw cycles) to increase fungal DNA yields, while maintaining the integrity of the DNA. Furthermore, different fungal strains may require different extraction steps to be added, complicating DNA extraction from the whole fungal community in environmental samples.

(ii) Selection of a reliable marker gene (gene section) is influenced not only by the number of targeted taxa, but also the feasibility of down-stream analysis as this depends on the availability of data stored in publicly available databases. For prokaryotes, several and up to date databases exist for 16S rRNA gene sequences (and are publicly accessible), while far less information is available for 18S rRNA sequences. One of the most commonly used database is SILVA, but while the SILVA ref 138.1 release (Quast et al., 2013) contains 2,052,220 16S rRNA gene sequences (1,983,022 bacterial and 69,198 archaeal sequences), it only contains172,520 18S rRNA gene sequences, of which 30,386 were classified as fungi. SILVA also, hosts a repository of 9329 representative 18S rRNA gene sequences covering all of the fungal kingdom and includes a manually curated alignment, and reference phylogenetic tree (Yarza et al., 2017). An alternative database for the identification of fungi is the ITS sequence database UNITE, but the most recent release (Nilsson et al., 2018) contains a similarly low number of 30,555 fungal sequences. Reich and Labes (2017) reviewed the available molecular ecology tools including their advantages and drawbacks when applied to the community studies of marine fungi. Even when the available number of 18S rRNA gene sequences, ITS sequences and fungal genomes has increased substantially, these numbers stand in stark contrast to the estimated several million fungal species (Nilsson et al., 2015). About 50% of the described fungal species still lack any DNA sequence information in public databases (Xu, 2016). In order to fill the taxonomic marker-related gaps in public databases, it has been suggested to use third-generation sequencing and apply ribosomal tandem repeat sequencing to cover all ribosomal markers for fungi (Wurzbacher et al., 2019).

(iii) Different nuclear ribosomal DNA marker genes are used for the identification of fungal species. However, environmental studies on fungal communities, apply most commonly the ITS and the 18S rRNA marker gene. The ITS region has been proposed as a universal barcode for fungal DNA as it may allow for a better resolution of fungal taxonomy than the 18S rRNA gene overall (Schoch et al., 2012). ITS barcoded sequencing has been successfully applied for both unicellular as well as for filamentous fungi (Vu et al., 2016, 2019). Many ITS targeting primers have been developed in recent years (Martin and Rygiewicz, 2005; Manter and Vivanco, 2007; Toju et al., 2012). However, choosing adequate thresholds for taxonomic assignments in ITS processing pipelines is delicate as the average intraspecific ITS variability is fluctuating (Smith et al., 2007; Simon and Weiß, 2008). For example, 0.2% for A. fumigatus, 3.1% for F. solani and up to 24.2% for the Ascomycota Xylaria hypoxylon (Nilsson et al., 2008). Vu et al. (2016, 2019) suggested that a threshold of 98.41% should be applied for ITS to distinguish between yeast species and a threshold of 99.6% should be applied to discriminate between filamentous fungi. Moreover, within an individual, ITS polymorphism (Alper et al., 2011) and ITS hybrid forms (Sriswasdi et al., 2019) were reported. Consequently, even when using fungal specific primers (ITS), intraspecific variability might not lead to species identification. Use of ITS shows even more limitations when dealing with marine fungi. Indeed, the ITS marker has a higher divergence rate compared to the 18S rRNA marker gene in marine fungal communities where early diverging fungi are abundant, and thus results into low classification success rates for ITS (Nilsson et al., 2019). For example, De Tender et al. (2017) could not assign 28 to 99% of the fungal reads acquired in their study when using ITS. To overcome this issue, it has been suggested to combine multiple marker genes for the molecular identification of the members of marine fungal communities. Banos et al. (2018) suggested to apply a fungi-specific 18S rRNA primers according to different environments, conditions or goals. This raises a new issue when using fungal specific ITS/18S primers, as different sets may overestimate some taxa and, in some cases, not target any fungus at all. By using a long read sequencing approach multiple marker genes can be retrieved at the same time, which allows for better taxonomic resolution (Heeger et al., 2018). Studies focusing on fungi colonizing plastic debris are scarce and the use of different marker genes and short read sequencing technology (Table 1) makes comparison between different datasets difficult. Unfortunately, no credible hypotheses on the presence or absence of a core fungal community living on plastic can be formulated yet.

(iv) Culture-based methods are time-consuming and the culture media will have a selective effect on fungal growth. There is no specific medium for marine fungi available to date, but only adaptions of media selective for terrestrial fungi. The morphological diversity associated with different developmental stages of the same species, complicates the identification of fungal isolates (Xu, 2016). Nevertheless, only culturing of strains isolated from environmental samples enables in-depth investigation of their physiological and metabolic capabilities. Overy et al. (2019) published a toolkit of best practices for the culturing and isolation of marine fungi. We thus argue that combining molecular and isolation/culturing effort is the best way to evaluate interactions between fungal communities and plastics in marine environments.

Conclusion-Outlook

This mini-review summarizes the current knowledge on marine fungi – PMD interactions; i.e., the ability of fungi to colonize plastics and specific strains known to degrade plastics as well as the methodological advances and difficulties in studying fungi – PMD interactions. Investigating the interaction of marine fungi and PMD is an emerging and exciting field of research when considering the high potential for plastic degradation of several fungal strains. Yet, for a well-constrained appraisal of marine fungi and their role as plastic degraders, several knowledge gaps still need to be filled. Firstly, a more general and fundamental understanding of fungi in the marine environment needs to be achieved by addressing fungal prevalence and diversity in the ocean. By using new molecular markers, the available sequence databases could be expanded for future classification of fungi detected on plastic polymers and to classify currently unclassified fungi. To address the biodegradation potential of fungi, comparable detection methods should be used to enable comparison between different strains, polymers and studies. Also, we suggest applying several complementary techniques for assessing biodegradation, particularly if the used techniques might cause false positives. Once fungal species degrading plastic in the marine environment are identified, future research should address the enzymatic potential of these fungi, which might then serve biotechnological applications for plastic waste bioremediation.

Author Contributions

EZ wrote the manuscript with contributions from all co-authors. HN supervised the project. All authors contributed to the article and approved the submitted version.

Funding

This study was financed through the European Research Council (ERC-CoG Grant No. 772923, project VORTEX).

Conflict of Interest

The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.

Publisher’s Note

All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article, or claim that may be made by its manufacturer, is not guaranteed or endorsed by the publisher.

References

Albertsson, A. (1978). Biodegradation of synthetic polymers. II. A limited microbial conversion of ¹⁴C in polyethylene to ¹⁴CO2 by some soil fungi. J. Appl. Poly. Sci. 22, 3419–3433.

Google Scholar

Albertsson, A., Baanhidi, Z., and Beyer-Ericsson, L. (1978). Biodegradation of synthetic polymers. III. The liberation of ¹⁴CO2 by molds like Fusarium redolens from ¹⁴C labeled pulverized high-density polyethylene. J. Appl. Poly. Sci. 22, 3435–3447.

Google Scholar

Albertsson, A.-C. (1980). The shape of the biodegradation curve for low and high density polyethenes in prolonged series of experiments. Eur. Poly. J. 16, 623–630. doi: 10.1016/0014-3057(80)90100-7

REVIEW article

The Potential Role of Marine Fungi in Plastic Degradation – A Review

Ocean Plastic Pollution

Microbial Biofilms on Marine Plastic Debris

A Brief Introduction to the Fungal Kingdom

Life on Plastic Is Fantastic: Fungal Colonization of Marine Plastic Debris

Fungi in Marine Environments as Part of Marine Plastic Debris Associated Biofilms

Plastic Biodegradation Potential of Fungi

Analytical Tools for Assessing the Potential for Fungi-Mediated Plastic Degradation

Gravimetric Measurements and Growth of Biomass

Clearance Zone Formation

Scanning Electron Microscopy

Fourier-Transform Infrared Spectroscopy

Assays With 13C or 14C Labeled Polymers

Other Methods

Limitations of Studying Fungal Communities

Conclusion-Outlook

Author Contributions

Funding

Conflict of Interest

Publisher’s Note

References

Assays With ¹³C or ¹⁴C Labeled Polymers