Utilization of iron fillings solid waste for optimum biodiesel production

This study explores the innovative application of iron filings solid waste, a byproduct from mechanical workshops, as a heterogeneous catalyst in the production of biodiesel from waste cooking oil. Focusing on sustainability and waste valorization, the research presents a dual-benefit approach: addressing the environmental issue of solid waste disposal while contributing to the renewable energy sector. Particle size distribution analysis, X-ray diffraction (XRD), scanning electron microscopy (SEM), X-ray fluorescence (XRF), Thermal analysis (TG-DTA), and FTIR analysis were used to characterize the iron filings. The response surface methodology (RSM) was used to guide a series of experiments that were conducted to identify the optimum transesterification settings. Important factors that greatly affect the production of biodiesel are identified by the study, including catalyst loading, reaction time, methanol-to-oil ratio, reaction temperature, and stirring rate. The catalyst proved to be successful as evidenced by the 96.4% biodiesel conversion efficiency attained under ideal conditions. The iron filings catalyst’s reusability was evaluated, demonstrating its potential for numerous applications without noticeably decreasing activity. This work offers a road towards more environmentally friendly and sustainable chemical processes in energy production by making a strong argument for using industrial solid waste as a catalyst in the biodiesel manufacturing process.

GRAPHICAL ABSTRACT

1 Introduction

In the context of modern environmental and energy challenges, the efficient management and valorization of solid waste emerge as critical areas of focus. Defined by the Resource Conservation and Recovery Act (RCRA), solid waste encompasses a broad spectrum of discarded materials from residential, commercial, industrial, and agricultural sources (Epa and O. of Resource Conservation, 2014) These materials range in composition from semi-solid to liquid and gaseous states, each with distinct properties such as corrosivity, ignitability, reactivity, and toxicity, which can pose significant environmental and health risks (Dehghani et al., 2021). The decomposition of garbage into its chemical components significantly contributes to environmental contamination, a prominent concern in developing nations where the reuse of landfills is limited due to financial constraints, resulting in unmet environmental health standards. Moreover, the emission of gases from decomposing waste poses a considerable environmental risk. In the anaerobic conditions of landfills, bacteria thrive, producing methane as a byproduct, further exacerbating the issue (Abdel-Shafy and Mansour, 2018).

Among the various types of industrial byproducts, iron filings—ferromagnetic fragments generated from the mechanical processing of steel and iron—represent a substantial component of solid waste. Traditionally viewed as environmental pollutants due to their disposal challenges, these materials are now being re-evaluated for their potential in sustainable applications, particularly in the realm of green chemistry and energy production (Jabar Hussain and Al-Khafaji, 2022).

The heavy reliance on large amounts of human-generated energy, mirroring the characteristics of natural gases and fuels, has led to a notable increase in the global price of petroleum oil. Such energy sources come with intrinsic limitations and are only viable for limited periods. This reality has spurred intensive research into alternative, renewable fuels. Moreover, the widespread use of petrochemical oils, natural gas, and coal plays a significant role in climate change and environmental pollution. This situation underscores the critical need to transition to more sustainable and cleaner energy sources (Edenhofer et al., 2012). The escalating global demand for energy, coupled with the environmental impact of conventional fossil fuels, underscores the urgency for alternative, sustainable energy sources. Biofuels, such as biodiesel derived from biomass feedstock or waste oils, offer a promising solution (Dahman et al., 2019; Zhang et al., 2024). Biodiesel production, specifically through the process of transesterification, transforms fats or oils into a cleaner fuel alternative, potentially achieving carbon neutrality by balancing CO₂ emissions with absorption during biomass growth.

However, the biodiesel production process can be further optimized by leveraging solid wastes as catalysts in a heterogeneously catalyzed process. Heterogeneous catalysis offers distinct advantages over its homogeneous counterpart, including ease of separation, potential for catalyst reuse, and enhanced reaction efficiencies (Weldeslase et al., 2023; Ulukardesler, 2023; Veluru et al., 2022; Salihu et al., 2021; Nixon et al., 2022; Hasan and Ratnam, 2022; Shaban, 2012; Elgharbawy et al., 2021; Suzihaque et al., 2022; Monika and Pathak, 2023; A Alotaibi et al., 2024). Several researchers have investigated the use of solid waste as a catalyst in the synthesis of biodiesel. Eggshells, which are mostly calcium carbonate, have been discovered to be effective as catalysts in the biodiesel transesterification process. Waste chicken feathers have also been explored as potential acidic catalysts since they contain the protein keratin. Steel and dust solid wastes resulting from electric arc furnaces are also utilized as a perfect biodiesel catalyst. Waste mollusks and crabs’ shells, sanitary ware waste, ductile cast iron solid waste, kitchen food waste, banana peels, spent coffee grounds, geothermal solid waste, waste bull bone, Tomato pomace Waste, biocatalyst, and biomass-based SO₃H-functionalized graphene are used as a biodiesel catalyst (Hijosa-Valsero et al., 2019; Widayat et al., 2023; Haile, 2014; Meka Kedir and Girma Asere, 2022; Barik et al., 2018; Roushdy, 2022a; El-Khashab et al., 2022; Roushdy, 2022b; El-Gendy et al., 2014; Ali et al., 2021; Khodary et al., 2023; Saravanan et al., 2024; Huang et al., 2023a; Carvalho de Melo et al., 2023; Huang et al., 2023b). Exploring the use of iron filings to be used a heterogenous biodiesel catalyst aligns with the principles of circular economy and green chemistry, offering an innovative approach to waste valorization and sustainable energy production.

This work explores the use of solid waste iron filings as a heterogeneous catalyst for the generation of biodiesel from waste cooking oil. The goal of this research seeks to improve the production of renewable biofuels and contribute to the sustainable management of solid waste by examining important reaction parameters and using response surface methods for process optimization. The goal of the study is to demonstrate the double advantages of this strategy are reducing waste disposal problems and supporting renewable energy sources by looking at them through the lenses of environmental preservation and energy sustainability.

2 Materials and methods

2.1 The research raw materials

The following are the raw substances used in this study:

(a) Iron filings solid waste which is was collected from a steel industry located in Egypt.

(b) Methanol (MeOH) with a concentration of 99% was acquired from ALFA Chemical Group.

(c) Waste sunflower cooking oil acquired from an Egyptian restaurant.

2.2 Characterization of solid waste

The solid waste was characterized using the same method and standards that were mentioned in the previous research paper (El-Khashab et al., 2022) in addition to Scanning Electron Microscopy (SEM), Thermogravimetry-differential thermal analysis (TG-DTA), and Fourier transform infrared spectrophotometer (FTIR) with details mentioned in Table 1.

Table 1

Table 1. Characterization methods for the utilized solid waste.

2.3 Arrangement and assembly of SFWCO

Sunflower waste cooking oil (SFWCO), once deemed worthless by many households, can be effectively purified to eliminate any suspended particulates, fried food remnants, and other contaminants. The purification process involves utilizing a centrifuge and filter to separate the impurities from the oil. Following this step, SFWCO undergoes 2 h of drying at 105°C to extract any remaining water content. This treatment paves the way for its efficient reuse in various applications.

2.4 Biodiesel production

The trial step that was utilized for the creation of biodiesel, as shown in Figure 1, can be illustrated as follows: The trans-esterification technique of biodiesel synthesis was used, and the reaction happened in a 250 mL round bottom flask coupled with a reflux condenser to prevent methanol escape. The flask was placed in a 1,000 mL beaker filled with water to serve as a heating medium, along with a thermometer placed in the water for measuring temperature while accounting for an additional 5°C higher than that of the flask.

Figure 1

Figure 1. Experimental setup.

To create biodiesel, the necessary components such as methanol, catalyst (iron filings), and oil were efficiently added to a batch reactor. Proper attention was paid to maintaining the required catalyst concentration and adhering to the right m:o ratio. Following this, the temperature of the reaction was appropriately adjusted while starting and setting the timer for a specific duration. Once complete, a filter media was used to remove the solid catalyst, which then left glycerol behind. With a separating funnel, any methanol that was found in excess amounts was completely removed through an 80°C—30-min drying process until finally, we could calculate how much biodiesel had been made based on its weight ratio when compared against SFWCO that was initially used. The conversion was calculated using Eq. 1 .

$BiodieselConversion\%=\frac{Weightofbiodieselproduced}{Weightofsunfloweroil}x100(1)$

2.5 Experimental design

To make a perfect design for the experimental work, the surface methodological technique (RSM) was used, along with the aid of Design Expert software version 13 for detailed analysis (Montgomery, 2013). RSM includes an array of statistical and mathematical approaches for developing empirical models. RSM aims to relate a response to the amounts of various input factors/variables that impact it through suitable experiment analysis and design. The reaction variables are labelled as A, B, C, D, and E, as indicated in Table 2. Biodiesel and glycerol conversions have been selected as reaction responses. The choice of reaction conditions and ranges were also chosen based on previous research (El-Khashab et al., 2022; Khodary et al., 2023; El-Sheltawy and Al-Sakkari, 2016; Talha and Sulaiman, 2016; Ling et al., 2019; Refaat, 2011).

Table 2

Table 2. Biodiesel reaction variables.

In the production of biodiesel, the M:O molar ratio is crucial. To convert one mole of TG into FAME or biodiesel, three moles of methanol are needed. This requires additional methanol to maintain the reaction rate. A molar ratio of M:O greater than 3:1 is necessary, with a range of 5:1 to 20:1 to analyze the impact of excess methanol on biodiesel yield. The yield of biodiesel directly increases with temperature between 50 and 70°C. This could be explained by the oil’s decreased viscosity. However, this effect becomes insignificant beyond 70°C.

Optimal conditions for biodiesel production are reaction time of 4 h, methanol to oil ratio of 20, catalyst loading of 5%, stirring rate of 800 rpm, and temperature of 70°C, resulting in a 99.58% yield. Lower limit conditions are reaction time of 1 h, methanol-to-oil ratio of 5, catalyst loading of 1%, stirring rate of 200 rpm, and temperature of 50°C, resulting in an 82.9% yield. Any increase in optimal conditions or decrease in lower limit conditions will not lead to significant yield improvement.

2.6 Optimum biodiesel sample analysis

To ascertain that the resulting product is biodiesel, the following tests were done using ASTM standards methods as mentioned in Table 3 then the results were compared with the biodiesel American and British standards.

Table 3

Table 3. Optimum biodiesel sample analysis.

2.7 Reusability test of iron filings solid waste catalyst

Under the optimal conditions, a reusability test was performed. The reaction product was filtered after the reaction was completed to eliminate the catalyst. Table 4 summarizes the approach employed. The catalyst strength and efficiency were determined by calculating the reaction conversion at the stage of reutilization.

Table 4

Table 4. Reusability test.

3 Results and discussion

3.1 Iron filings characterization

3.1.1 X-ray fluorescence for chemical analysis

Table 5 shows the chemical assessment of the iron-filled solid waste. The results show that the waste is largely made of 96.15% Fe₂O₃, with only trace levels of other oxides, as expected. CO₂ generation, the loss of combustible organic products, and moisture content loss might account for the loss observed during igniting. These findings provide persuasive proof that solid waste that contains iron has enormous potential as a biodiesel catalyst. Prior research has also shown that Fe₂O₃ is effective as a component for biodiesel, which supports its usage in this study.

Table 5

Table 5. Chemical analytics of iron filings.

3.1.2 Mineralogical examination

The conclusions of the iron fillings’ mineralogy assessment are shown in Figure 2. According to the results of the investigation, the predominant phase present is Periclase, namely, hematite (α-Fe₂O₃), which has a rhombohedral structure. The blue crystal is known as “JCPDS-00-024-0072,” while the green crystal is known as “JCPDS-00-033-0664,” also known as burnt ochre Hematite. The unusual form of these hematite crystals suggests that solid waste has significant promise as a biodiesel catalyst. Minor phases of quartz and calcite were also discovered throughout the study. These X-ray diffraction (XRD) study findings confirm and complement the X-ray fluorescence (XRF) analysis results, further enhancing solid waste characterization.

Figure 2

Figure 2. Mineralogical examination of the iron filings.

3.1.3 Screen analysis

The Malvern device was used to determine the size of the catalyst particles, which resulted in an average size of 549.9 nm, as shown in Figure 3. This observation indicates that the catalyst has a large surface area, which is critical for its effectiveness in promoting the reaction. A narrow particle size distribution and small particle size suggest a more reactive surface area available. As a result of its large surface area, this catalyst is expected to exhibit extraordinary activity, making it an excellent choice for the planned application.

Figure 3

Figure 3. Cumulative screen examination curve of the iron filings.

3.1.4 Microstructure and morphological analysis

Figure 4 illustrates that the catalyst’s surface is non-uniform, with varied shapes and active centers, indicating that it would be an excellent biodiesel catalyst.

Figure 4

Figure 4. SEM examination for iron fillings.

3.1.5 Thermogravimetry-differential thermal analysis (TG-DTA)

Figure 5 shows the TG-DTA analyses for the solid waste.

• There are three main regions of decomposition shown in the thermograph as follows and after these losses of weight then above 600°C, the sample remains stable.

1- A weight loss of 10 wt% at 300°C because of weakly bonded or physically adsorbed water removal (Darezereshki, 2011).

2- A weight loss of 55 wt% at 320°C–370°C and another 25 wt% weight loss at 370°C–420°C because of chemically adsorbed water removal because of the silanol group (Si–OH) condensation (Darezereshki, 2011; Qu et al., 2017).

3- A weight loss of 10 wt% at 420°C–600°C because of chemical components decomposition and crystalline phase transformation (Darezereshki, 2011).

• The DTA graph shows endothermic peaks as follows and after these peaks, the sample is stable as the curve becomes parallel to the x-axis.

1- A peak at 150°C corresponds to 0.5 wt% weight loss due to the loss of moisture from the solid waste sample.

2- A peak at 300°C–370°C corresponds to 18 wt% weight loss because of the loss of combustible organic products.

3- A peak at 370°C–440°C corresponds to 5 wt% weight loss because of the transition phase.

4- A peak at 680°C.

Figure 5

Figure 5. Thermal analysis (TG-TDA) of the iron fillings.

It is noticed because of the crystallization and phase transition there is no associate signal was noticed in TGA when compared with the DTA curve. The obtained results were comparable with the results obtained by the thermal analysis of α-Fe₂O₃ as mentioned by Lassoued et al. (2017a) and Waseem et al. (2014).

3.1.6 Fourier transform infrared spectrophotometer (FTIR)

Figure 6 shows the FTIR for the iron filling within the range of 400–4,000 cm⁻¹. The list of peaks is shown in the following table. Based on FTIR analysis the strong band below 700 cm⁻¹ is assigned for Fe-O stretching mode (Farahmandjou and Soflaee, 2015). The absorption peaks at the wavelengths of 460.9, 509.1, and 616.2 cm⁻¹ correspond to the Fe-O stretching mode of Fe₂O₃ and the vibration of Fe-O in the rhombohedral lattice of hematite which is an important characteristic of the crystalline of α-Fe₂O₃ compound (Lassoued et al., 2017b; Jing and Wu, 2004). The absorption peak at the wavelength of 870.8 may be due to the presence of an oxygen-containing function group of calcite (Gawad et al., 2022) or aromatic C-H stretching vibration because of the presence of organic impurities in the sample (Mansour et al., 2022).

Figure 6

Figure 6. FTIR of solid waste.

3.2 Process modelling using design expert programme

The previous experiments allowed us to calculate the rates of conversion of both biodiesel & glycerol. With the utilization of Design Expert, models were created by showing how process or reaction factors impact biodiesel and glycerol conversion. The ANOVA approach was utilized with a 95% confidence level to assess the significance and appropriateness of these models, taking P and F values into account. The findings of the investigation indicated that the quadratic model showed the highest efficiency in predicting biodiesel conversion and the most favorable outcomes for glycerol conversion. Nevertheless, several components within the models were considered statistically insignificant as their p-values exceeded the threshold of 0.05.

Consequently, these unnecessary components were eliminated, resulting in simplified versions of the models expressed by Eqs 2, 3. Furthermore, the ANOVA analysis is summarized in Tables 6, 7. Finally, Figures 7, 8 compare estimated and experimental data for conversions of biodiesel and glycerol. The reasonable consistency seen in both figures and R values in Tables 6, 7 verifies the models’ appropriateness.

$X=-0.916A+0.611B+0.132C+0.164D+0.009E+0.032AD-0.0015AE-0.0004BE-0.00009DE+{0.00002E}^2+68.85(2)$

$Y=+0.177A-0.617B-0.3C-0.319D+0.017E-0.006AD+0.0002AE+0.0005BE+0.0002DE-0.00002E^2+40.108(3)$

Table 6

Table 6. Analysis of variance analysis results for biodiesel response (Reduced Quadratic Model).

Table 7

Table 7. Analysis of variance analysis results for glycerol response (Reduced Quadratic Model).

Figure 7

Figure 7. Actual and predicted biodiesel yield.

Figure 8

Figure 8. Actual and predicted glycerol yield.

The variable X represents biodiesel conversion in the context of the study, whereas the variable Y represents glycerol conversion. Both conversions are influenced by the reaction variables. All these reaction parameters were shown to have a positive stimulus on the conversion of biodiesel, indicating that increasing these components improves the conversion process. They have an adverse influence on the conversion of glycerol, implying that greater values of these parameters result in lower conversion of glycerol. In the following Table 8, Actual and predicted results for Biodiesel and glycerol yield with the experimental errors according to the suggested models. As shown in Table 8 the predicted values and the experimental or actual values of the responses are near to each other with a small absolute error rate for each run and a small mean error of 1.14 and 4.48 for biodiesel and glycerol yield responses respectively.

Table 8

Table 8. Actual and predicted results for biodiesel and glycerol yield with the errors.

3.3 Relation between one reaction variable and both biodiesel and glycerol responses

The impact of each reaction parameter on the conversions of glycerol and biodiesel is displayed in Figures 9, 10. The amount of catalyst added to the reaction mixture and the reaction time has approximately no effect because it is not a significant factor, as indicated by the ANOVA analysis as they are non-significant factors. The two figures show that the reaction temperature, the M:O ratio, and the stirring rate have the greatest impact on both biodiesel and glycerol conversions.

Figure 9

Figure 9. Reaction parameters influence the yield of biodiesel.

Figure 10

Figure 10. Reaction parameters influence the yield of glycerol.

3.4 Relation between all reaction variables and both biodiesel and glycerol responses

The relationship between the biodiesel yield and methanol, as well as the methanol-to-oil ratio, reaction temperature, reaction time, and stirring rate, is shown in Figures 11, 12. On the other hand, Figures 13, 14 illustrate the relationship between glycerol production and the methanol-to-oil ratio, reaction temperature, reaction time, and stirring rate.

Figure 11

Figure 11. As a 3D surface graph, the relationship between the biodiesel yield, reaction temperature, reaction time, methanol to oil ratio, and stirring rate.

Figure 12

Figure 12. As a contour plot, the relationship between the biodiesel yield, reaction temperature, reaction time, methanol to oil ratio, and stirring rate.

Figure 13

Figure 13. As a 3D surface graph, the relationship between the glycerol yield, reaction temperature, reaction time, methanol to oil ratio, and stirring rate.

Figure 14

Figure 14. As a contour plot, the relationship between the glycerol yield, reaction temperature, reaction time, methanol to oil ratio, and stirring rate.

3.5 Process optimization

The transesterification reaction optimization procedure sought to establish the best values for the independent variables, which included the M:O molar ratio, catalyst loading, reaction temperature, stirring rate, and reaction duration. These factors had an immediate impact on the dependent response variables, which were glycerol and biodiesel conversion. Design of experiment (Design Expert software) was utilized to make the optimization process. The program looked for the best settings to accomplish the intended response goals. A set of objectives was developed inside the program to discover the ideal circumstances for the independent variables. These goals were set with environmental and economic feasibility in mind. Temperature, stirring rate, and reaction time were tuned to be minimized to utilize the least amount of energy. This strategy is intended to enhance energy efficiency and minimize resource usage. The M:O molar ratio and the amount of catalyst, on the other hand, were controlled within a certain range, so any extra methanol might be collected for future use. Finally, the biodiesel output was set to be maximized, while the glycerol yield was to be minimized within the stated constraints of the independent variables’ objectives. Based on the previously stated goals, the design expert program developed 100 recommended solutions with varying degrees of desirability and then chose the best solution with the highest degree of desire. The best reaction conditions that lead to 96.4% biodiesel yield and 3.95% glycerol yield are reaction time equals 1 h, Methanol to oil ratio equals 30, catalyst loading 8%, temperature equals 52°C, and stirring rate equals 200 RPM.

3.6 Optimum biodiesel sample analysis

The physicochemical properties of this ideal sample were obtained through comparison to its guidelines ASTM D 6751 (A. D6751-15c, 2010) and EN14214 (Liquid Petroleum Products, 2013), as shown in Table 9. All measured qualities meet or exceed the relevant criteria. Table 10 shows the results of the best sample’s GC tests, as well as adherence to the guidelines of biodiesel EN 14105 (Biodiesel and Glycerol, 2011) and EN 14103 (Biodiesel, 2011).

Table 9

Table 9. Physicochemical guidelines and properties of biodiesel.

Table 10

Table 10. Results and standards for GC analysis.

The ideal sample’s GC test results are displayed in Table 10, which shows that the sample complies with EN 14103 (Biodiesel, 2011) and EN 14105 (Biodiesel and Glycerol, 2011) biodiesel requirements.

Based on research done by Kolobeng et al. (2022) who examined the different physical properties of biodiesel during storage, the increase in the moisture content in the biodiesel because of the moisture content of air accelerates biodiesel degradation. The results indicate that the biodiesel produced from waste cooking oil can be stored for 11 days after that its moisture content exceeds threshold of 0.5 mg/g so it must be blended with petroleum diesel before that time to delay the degradation and ensure good quality as indicated by standard ASTM D2709.

3.7 Catalyst reusability

The catalyst’s reusability test produced an intriguing discovery. It was discovered that the catalyst may be reused up to six times before it is necessary to replace it. Figure 15, which depicts the trend of catalyst performance through numerous reuse cycles, graphically represents this information. Two major causes can be ascribed to the shift in catalyst reactivity. First, glycerol tends to build on the active centers of the catalyst after repeated application. This glycerol build-up impairs the catalyst’s capacity to carry out the intended reactions. Second, some particle loss may occur in the catalyst during the filtration phase of the process. The catalytic activity of the remaining catalyst material is reduced because of these lost particles. These components work together to explain the observed variations in catalyst reactivity over time. As a result, after a specific number of cycles, it is advised that the catalyst be replaced with a new one. This enables peak performance and the necessary response efficiency.

Figure 15

Figure 15. Reusability test of iron fillings solid waste.

4 Comparison of the current study with the prior studies

As seen in Table 11, this study has various distinguishing qualities that set it apart from past studies. The benefits are as follows:

1- A solid waste-derived catalyst has been utilized, which eliminated the need for extra catalyst preparation. This streamlines the procedure and saves time and money.

2- The catalyst utilized in this work is heterogeneous, making separation from the reaction mixture easier. This streamlines the whole method and enables effective catalyst recovery and reuse.

3- The utilization of used cooking oil as a raw source in the creation of biodiesel. The work tackles both waste management problems and taps into a readily available resource by reusing this waste product.

4- The remarkable biodiesel conversion rates observed under minimum reaction conditions distinguish this work. This implies that the procedure uses less energy and is less expensive than other approaches.

5- This study’s emphasis on recycling hazardous solid waste and waste cooking oil for biodiesel generation is one of its most significant contributions. The researchers cut process expenses while simultaneously contributing to environmental conservation initiatives.

6- The iron fillings solid waste contains 96% Fe₂O₃ with other minor oxides making it a good biodiesel as iron oxide is proved by previous researchers to be a perfect biodiesel catalyst (Widayat and Nursafitri, 2019; Xie and Wang, 2020a; Dhawane et al., 2016; Basavegowda et al., 2017; Xie and Wang, 2020b; Panchal, 2018; Kumar et al., 2024; Ezzah-Mahmudah et al., 2016; Suzuta et al., 2012; Ibrahim et al., 2022).

7- Iron ferric oxide is considered a heterogeneous basic catalyst that is used to produce biodiesel in which alcohol and edible oil “triglyceride, TG” undergo nucleophilic reactions to form biodiesel “Fatty acid methyl ester, FAME” and glycerol as a byproduct. The mechanism of the transesterification reaction is illustrated in the following figure. Triglyceride is firstly converted to diglyceride then monoglyceride and finally the monoglyceride is converted to glycerol. An ester is formed in each conversion step so on molecule of TG produces three molecules of ester as shown in Figure 16 (Changmai et al., 2020).

8- The study explores the use of waste iron filling as an innovative, low-cost, and substitute high-cost source of ferric compound for the creation than using the resulting iron oxide as a catalyst used in the manufacturing of biodiesel.

Table 11

Table 11. Comparison of current research with another research.

Figure 16

Figure 16. Reaction mechanism.

Overall, this research proposes a viable alternative to biodiesel production by employing a solid waste catalyst, speeding the separation process, utilizing waste cooking oil, attaining high conversion rates, and promoting environmental sustainability. These elements, taken together, constitute a substantial improvement in biodiesel research.

5 Conclusion

The research delved into the innovative use of iron filings solid waste as a catalytic agent for biodiesel production, presenting a dual solution to environmental concerns and the quest for renewable energy sources. Through optimizing the biodiesel production process via a transesterification reaction, this study not only proposes a method to mitigate hazardous waste but also enhances the sustainability of energy production. This investigation, focusing on critical reaction parameters—temperature, stirring rate, methanol to oil ratio, catalyst loading, and reaction time—utilized Design Expert software to methodically analyze data, model outcomes, and refine the production process.

Particle size distribution analysis, X-ray diffraction (XRD), scanning electron microscopy (SEM), X-ray fluorescence (XRF), Thermal analysis (TG-DTA), and FTIR analysis were used to characterize the iron filings. These analyses proved that the solid waste contains 96.15% Fe₂O₃ with small particle size and large surface area which is a good indication that this solid can be used as a heterogeneous biodiesel catalyst.

The execution of 43 experimental trials, employing a variety of analytical tools such as 3D charts, 2D graphs, and contour figures, allowed for an in-depth examination of each parameter’s influence on biodiesel yield. The process modeling resulted in a reduced quadratic model representing the results with small errors between actual and predicted yield. The results showed that the amount of catalyst added to the reaction mixture and the reaction time have approximately no effect while the reaction temperature, the M:O ratio, and the stirring rate have the greatest impact on both biodiesel and glycerol conversions.

The optimization process resulted in the identification of one hundred potential solutions, balancing environmental impact and economic feasibility, ultimately leading to the selection of the most effective reaction conditions. The study established optimal conditions of a 30:1 methanol to oil molar ratio, 52°C reaction temperature, 8% catalyst loading, 1-h reaction time, and 200 rpm stirring rate, under which a 96.4% biodiesel conversion rate was achieved, fulfilling the set criteria for quality biodiesel. The resulting optimum biodiesel sample was tested by GC and physical properties determination and the results were compared with the American and British standards showing and proofing that the resulting sample is a good biodiesel fuel.

This research not only underscores the potential of repurposing iron filings solid waste for environmental benefit but also highlights the economic advantages of utilizing waste materials as raw inputs for biofuel production. The conclusion of the study, demonstrating the catalyst’s capacity for up to six reuses without significant efficiency loss, emphasizes the method’s practical viability and sustainability. In summary, these findings advocate for further exploration and application of this approach in industrial settings, reinforcing the concept that innovative, green chemistry can play a pivotal role in addressing environmental challenges and advancing renewable energy technologies.

Data availability statement

The original contributions presented in the study are included in the article/supplementary material, further inquiries can be directed to the corresponding authors.

Author contributions

FE-B: Data curation, Investigation, Methodology, Writing–original draft. AO: Funding acquisition, Resources, Writing–review and editing. DR: Funding acquisition, Resources, Writing–review and editing. MR: Conceptualization, Data curation, Formal Analysis, Investigation, Methodology, Project administration, Resources, Software, Supervision, Validation, Visualization, Writing–original draft, Writing–review and editing.

Funding

The authors declare that financial support was received for the research, authorship, and/or publication of this article. The authors wish to acknowledge the support from the UKRI project “Advancing Creative Circular Economies for Plastics via Technological-Social Transitions” (ACCEPT Transitions, EP/S025545/1). All data is provided in full in the results section of this paper.

Conflict of interest

The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.

The authors declared that they were an editorial board member of Frontiers, at the time of submission. This had no impact on the peer review process and the final decision.

Publisher’s note

All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article, or claim that may be made by its manufacturer, is not guaranteed or endorsed by the publisher.

References

A Alotaibi, M., Naeem, A., Wali Khan, I., Farooq, M., Ud Din, I., and Saharun, M. S. (2024). Optimization and cost analysis evaluation studies of the biodiesel production from waste cooking oil using Na–Si/Ce-500 heterogeneous catalyst. Biomass Bioenergy 182 (Mar), 107078. doi:10.1016/j.biombioe.2024.107078

CrossRef Full Text | Google Scholar

Abdel-Shafy, H. I., and Mansour, M. S. M. (2018). Solid waste issue: sources, composition, disposal, recycling, and valorization. Egypt. J. Petroleum 27 (4), 1275–1290. Egyptian Petroleum Research Institute. doi:10.1016/j.ejpe.2018.07.003

CrossRef Full Text | Google Scholar

A. D6751-15c (2010). Standard specification for biodiesel fuel blend stock (B100) for middle distillate fuels. ASTM Int., 1–11. doi:10.1520/D6751-23

CrossRef Full Text | Google Scholar

Ali, N. A., Khairuddin, N., and Siddique, B. M. (2021). Eggshell waste as a catalyst for biodiesel production: a preliminary study. IOP Conf. Ser. Mater Sci. Eng. 1195 (1), 012043. doi:10.1088/1757-899x/1195/1/012043

CrossRef Full Text | Google Scholar

ASTM D445-06 (2008). “Standard test method for kinematic viscosity of transparent and opaque liquids (and calculation of dynamic viscosity),” in Manual on hydrocarbon analysis. 6th Edition, 1–10.

Google Scholar

Barik, S., Paul, K. K., and Priyadarshi, D. (2018). “Utilization of kitchen food waste for biodiesel production,” in IOP conference series: earth and environmental science United Kingdom: (Institute of Physics Publishing). doi:10.1088/1755-1315/167/1/012036

CrossRef Full Text | Google Scholar

Basavegowda, N., Mishra, K., and Lee, Y. R. (2017). Synthesis, characterization, and catalytic applications of hematite (α-Fe2O3) nanoparticles as reusable nanocatalyst. Adv. Nat. Sci. Nanosci. Nanotechnol. 8 (2), 025017. doi:10.1088/2043-6254/aa6885

CrossRef Full Text | Google Scholar

Biodiesel, A. (2011). APPLICATION NOTE EN 14103 Determination of total FAME and linolenic acid methyl ester in FAME with AC Biodiesel All in One Solution, 1–3.

Google Scholar

Biodiesel, A., and Glycerol, T. (2011) APPLICATION NOTE EN 14105 Determination of Free and Total Glycerol and mono-, di, - triglycerides in Fatty Acid Methyl Esters (FAME), 2–4.

Google Scholar

Carvalho de Melo, J. J., Passos da Silva, G. L., Mota, D. A., de Souza Brandão, L. M., de Souza, R. L., Pereira, M. M., et al. (2023). Use of bioprinted lipases in microwave-assisted esterification reactions. Catalysts 13 (2), 299. doi:10.3390/catal13020299

CrossRef Full Text | Google Scholar

Changmai, B., Vanlalveni, C., Ingle, A. P., Bhagat, R., and Rokhum, L. (2020). Widely used catalysts in biodiesel production: a review. RSC Adv. 10 (68), 41625–41679. doi:10.1039/d0ra07931f

PubMed Abstract | CrossRef Full Text | Google Scholar

Cheremisinoff, N. P. (1996). THERMAL ANALYSIS. Polym. Charact., 17–24. doi:10.1016/B978-081551403-9.50004-2

CrossRef Full Text | Google Scholar

D40052-15 (2013) Standard test method for density, relative density, and API gravity of liquids by digital density meter. West Conshohocken, Pennsylvania: ASTM International, 1–8. doi:10.1520/D4052-16.bubbles

CrossRef Full Text | Google Scholar

Dahman, Y., Syed, K., Begum, S., Roy, P., and Mohtasebi, B. (2019). Biofuels: their characteristics and analysis. Biomass, Biopolymer-Based Mater., 277–325. doi:10.1016/B978-0-08-102426-3.00014-X

CrossRef Full Text | Google Scholar

Darezereshki, E. (2011). One-step synthesis of hematite (α-Fe2O3) nano-particles by direct thermal-decomposition of maghemite. Mater Lett. 65 (4), 642–645. doi:10.1016/J.MATLET.2010.11.030

CrossRef Full Text | Google Scholar

Dehghani, M. H., Omrani, G. A., and Karri, R. R. (2021). “Solid waste—sources, toxicity, and their consequences to human health,” in Soft computing techniques in solid waste and wastewater management (Elsevier), 205–213. doi:10.1016/B978-0-12-824463-0.00013-6

CrossRef Full Text | Google Scholar

Dhawane, S. H., Kumar, T., and Halder, G. (2016). Parametric effects and optimization on synthesis of iron (II) doped carbonaceous catalyst for the production of biodiesel. Energy Convers. Manag. 122, 310–320. doi:10.1016/j.enconman.2016.06.005

CrossRef Full Text | Google Scholar

Edenhofer, O., Pichs-Madruga, R., Sokona, Y., Seyboth, K., Matschoss, P., Kadner, S., et al. (2012) Renewable energy sources and climate change mitigation: special report of the Intergovernmental Panel on Climate Change. Cambridge University Press.

Google Scholar

Edition, F. (2013) Final draft Uganda standard.

Google Scholar

El-Gendy, N. S., Hamdy, A., and Abu Amr, S. S. (2014). An investigation of biodiesel production from wastes of seafood restaurants. Int. J. Biomater. 2014, 1–17. doi:10.1155/2014/609624

PubMed Abstract | CrossRef Full Text | Google Scholar

Elgharbawy, A. S., Sadik, W. A., Sadek, O. M., and Kasaby, M. A. (2021) A review on biodiesel feedstocks and production technologies.

Google Scholar

El-Khashab, N. A., Naeem, M. M., and Roushdy, M. H. (2022). Optimum biodiesel production using ductile cast iron as a heterogeneous catalyst. ChemEngineering 6 (3), 40. doi:10.3390/chemengineering6030040

CrossRef Full Text | Google Scholar

El-Sheltawy, S. T., and Al-Sakkari, E. G. (2016). Recent trends in solid waste utilization for biodiesel production. J. Solid Waste Technol. Manag. 42 (1). doi:10.13140/RG.2.1.4444.3765

CrossRef Full Text | Google Scholar

Liquid Petroleum Products (2013) Liquid petroleum products - fatty acid methyl esters (FAME) for use in diesel engines and heating applications - requirements and test methods. Brussels: European Committee for Standardization.

Google Scholar

Ezzah-Mahmudah, S., Lokman, I. M., Saiman, M. I., and Taufiq-Yap, Y. H. (2016). Synthesis and characterization of Fe2O3/CaO derived from Anadara Granosa for methyl ester production. Energy Convers. Manag. 126, 124–131. doi:10.1016/j.enconman.2016.07.072

CrossRef Full Text | Google Scholar

Farahmandjou, M., and Soflaee, F. (2015). Low temperature synthesis of α-Fe2O3 nano-rods using simple chemical route low temperature synthesis of α-Fe 2 O 3 nano-rods using simple chemical route. Article J. Nanostructures 4, 413–418. doi:10.7508/jns.2014.04.002

CrossRef Full Text | Google Scholar

Gawad, A. A., Salama, T. M., Meshref, M., Mohamed, G. G., and Zedan, A. F. (2022). Coupling ATR-FTIR spectroscopy and chemometric analysis for rapid and non-destructive ink discrimination of forensic documents. Egypt J. Chem. 65 (8), 0–179. doi:10.21608/ejchem.2022.105668.4865

CrossRef Full Text | Google Scholar

Haile, M. (2014) Integrated volarization of spent coffee grounds to biofuels.

Google Scholar

Hasan, N., and Ratnam, M. V. (2022). Biodiesel production from waste animal fat by transesterification using H2SO4and KOH catalysts: a study of physiochemical properties. Int. J. Chem. Eng. 2022, 1–7. doi:10.1155/2022/6932320

CrossRef Full Text | Google Scholar

Hijosa-Valsero, M., Garita-Cambronero, J., Paniagua-García, A. I., and Díez-Antolínez, R. (2019). Tomato waste from processing industries as a feedstock for biofuel production. Bioenergy Res. 12 (4), 1000–1011. doi:10.1007/s12155-019-10016-7

CrossRef Full Text | Google Scholar

Huang, J., Wang, J., Huang, Z., Liu, T., and Li, H. (2023a). Photothermal technique-enabled ambient production of microalgae biodiesel: mechanism and life cycle assessment. Bioresour. Technol. 369, 128390. doi:10.1016/j.biortech.2022.128390

PubMed Abstract | CrossRef Full Text | Google Scholar

Huang, J., Wang, J., Huang, Z., Liu, T., and Li, H. (2023b). Photothermal technique-enabled ambient production of microalgae biodiesel: mechanism and life cycle assessment. Bioresour. Technol. 369 (2), 128390. doi:10.1016/j.biortech.2022.128390

PubMed Abstract | CrossRef Full Text | Google Scholar

Ibrahim, N. A., Rashid, U., Hazmi, B., Moser, B. R., Alharthi, F. A., Rokhum, S. L., et al. (2022). Biodiesel production from waste cooking oil using magnetic bifunctional calcium and iron oxide nanocatalysts derived from empty fruit bunch. Fuel 317 (Jun), 123525. doi:10.1016/j.fuel.2022.123525

CrossRef Full Text | Google Scholar

Jabar Hussain, A., and Al-Khafaji, Z. S. (2022). Experimental investigation on applying waste iron filings in the engineering fields for protection the environment from contamination. Mater Today Proc. 61, 794–798. doi:10.1016/j.matpr.2021.09.039

CrossRef Full Text | Google Scholar

Jing, Z., and Wu, S. (2004). Synthesis and characterization of monodisperse hematite nanoparticles modified by surfactants via hydrothermal approach. Mater Lett. 58 (27–28), 3637–3640. doi:10.1016/J.MATLET.2004.07.010

CrossRef Full Text | Google Scholar

Khodary, K. E., Naeem, M. M., and Roushdy, M. H. (2023). Utilization of electric arc furnace dust as a solid catalyst in biodiesel production. Clean. Technol. Environ. Policy 25 (1), 299–309. doi:10.1007/s10098-021-02174-0

CrossRef Full Text | Google Scholar

Kolobeng, R., Ketlogetswe, C., Jonas, M., and Mautle, D. (2022). Effects of moisture content on biodiesel (B100) properties during storage: a comparative analysis between biodiesel produced from used cooking oil and beef tallow. Sustain. Energy Technol. Assessments 54, 102844. doi:10.1016/j.seta.2022.102844

CrossRef Full Text | Google Scholar

Kumar, S., Kumari, S., Kumari, A., Kondal, N., Choudhary, P., Dhiman, V., et al. (2024). Green synthesis of iron oxide nanoparticles from Calotropis procera latex: an eco-friendly catalyst for biodiesel production from Calotropis procera seed oil. Clean. Technol. Environ. Policy. doi:10.1007/s10098-023-02737-3

CrossRef Full Text | Google Scholar

Lassoued, A., Dkhil, B., Gadri, A., and Ammar, S. (2017a). Control of the shape and size of iron oxide (α-Fe2O3) nanoparticles synthesized through the chemical precipitation method. Results Phys. 7, 3007–3015. doi:10.1016/J.RINP.2017.07.066

CrossRef Full Text | Google Scholar

Lassoued, A., Dkhil, B., Gadri, A., and Ammar, S. (2017b). Control of the shape and size of iron oxide (α-Fe2O3) nanoparticles synthesized through the chemical precipitation method. Results Phys. 7, 3007–3015. doi:10.1016/J.RINP.2017.07.066

CrossRef Full Text | Google Scholar

Ling, J. S. J., Tan, Y. H., Mubarak, N. M., Kansedo, J., Saptoro, A., and Nolasco-Hipolito, C. (2019). A review of heterogeneous calcium oxide based catalyst from waste for biodiesel synthesis. SN Appl. Sci. 1 (8), 810–818. doi:10.1007/s42452-019-0843-3

CrossRef Full Text | Google Scholar

Mahapatra, D. (2016). A review on steam coal analysis -calorific value. Am. Int. J. Res. Sci. Technol. Eng. Math., 143–152. doi:10.13140/RG.2.2.23977.49762

CrossRef Full Text | Google Scholar

Mansour, A. T., Alprol, A. E., Abualnaja, K. M., El-Beltagi, H. S., Ramadan, K. M. A., and Ashour, M. (2022). The using of nanoparticles of microalgae in remediation of toxic dye from industrial wastewater: kinetic and isotherm studies. Materials 15 (11), 3922. doi:10.3390/ma15113922

PubMed Abstract | CrossRef Full Text | Google Scholar

Meka Kedir, W., and Girma Asere, T. (2022). Biodiesel production from waste frying oil using catalysts derived from waste materials. 9:(3), 939–952. doi:10.18596/jotcsa.997456

CrossRef Full Text | Google Scholar

Microbeam Analysis Scanning (2021). Microbeam analysis-Scanning electron microscopy-Qualification of the scanning electron microscope for quantitative measurements.COPYRIGHT PROTECTED DOCUMENT.

Google Scholar

Monika, S. B., and Pathak, V. V. (2023). Biodiesel production from waste cooking oil: a comprehensive review on the application of heterogenous catalysts. Energy Nexus 10, 100209. doi:10.1016/j.nexus.2023.100209

CrossRef Full Text | Google Scholar

Montgomery, D. C. (2013) Montgomery design and analysis of experiments. United States: Arizona State University.

Google Scholar

J. D. Nixon, A. Al-Habaibeh, V. Vukovic, and A. Asthana (2022). Energy and sustainable futures: proceedings of the 3rd ICESF (Cham: Springer Nature Switzerland). doi:10.1007/978-3-031-30960-1

CrossRef Full Text | Google Scholar

Panchal, B. (2018). Biodiesel synthesis with iron oxide nano-catalyst catalyzed pongamia pinnata seed oil and dimethyl carbonate. Am. J. Energy Eng. 6 (3), 21. doi:10.11648/j.ajee.20180603.11

CrossRef Full Text | Google Scholar

Products, P. (2004) Astm D93 flash point.

Google Scholar

Qu, H., Bhattacharyya, S., and Ducheyne, P. (2017). 4.34 sol–gel processed oxide controlled release materials. Compr. Biomater. II, 617–643. doi:10.1016/B978-0-12-803581-8.10217-6

CrossRef Full Text | Google Scholar

Refaat, A. A. (2011). Biodiesel production using solid metal oxide catalysts. Int. J. Environ. Sci. Tech. 8 (1), 203–221. doi:10.1007/bf03326210

CrossRef Full Text | Google Scholar

Roushdy, M. H. (2022a). Heterogeneous biodiesel catalyst from steel slag resulting from an electric arc furnace. Processes 10 (3), 465. doi:10.3390/pr10030465

CrossRef Full Text | Google Scholar

Roushdy, M. H. (2022b). Sanitary ware waste as a source for a valuable biodiesel catalyst. J. Chem. 2022, 1–12. doi:10.1155/2022/1232110

CrossRef Full Text | Google Scholar

Salihu, A., Mahmood, A. A., Gimba, S., Nzerem, P., and Okafor, I. (2021). Production of biodiesel from waste cooking oil by transesterification process using heterogeneous catalyst. Niger. J. Environ. Sci. Technol. 5 (2), 501–510. doi:10.36263/nijest.2021.02.0308

CrossRef Full Text | Google Scholar

Saravanan, R., Sathish, T., Ağbulut, Ü., Sathyamurthy, R., Sharma, P., Linul, E., et al. (2024). Waste bull bone based reusable and biodegradable heterogeneous catalyst for alternate fuel production from WCO, and investigation of its usability as fuel substitute. Fuel 355 (Jan), 129436. doi:10.1016/j.fuel.2023.129436

CrossRef Full Text | Google Scholar

Shaban, S. A. (2012) Biodiesel production from waste cooking oil.

Google Scholar

Suzihaque, M. U. H., Alwi, H., Kalthum Ibrahim, U., Abdullah, S., and Haron, N. (2022). Biodiesel production from waste cooking oil: a brief review. Mater Today Proc. 63, S490–S495. doi:10.1016/j.matpr.2022.04.527

CrossRef Full Text | Google Scholar

Suzuta, T., Toba, M., Abe, Y., and Yoshimura, Y. (2012). Iron oxide catalysts supported on porous silica for the production of biodiesel from crude Jatropha oil. JAOCS, J. Am. Oil Chemists’ Soc. 89 (11), 1981–1989. doi:10.1007/s11746-012-2101-3

CrossRef Full Text | Google Scholar

Talha, N. S., and Sulaiman, S. (2016). Overview of catalysts in biodiesel production. ARPN J. Eng. Appl. Sci. 11 (1), 439–442.

Google Scholar

Epa and O. of Resource Conservation (2014) RCRA resource conservation and recovery Act orientation manual 2014 RCRA orientation manual 2014 reducing priority chemicals saving resources and energy managing materials safely forming partnerships promoting recycling and eCycling recycled/recyclable-printed with vegetable oil based inks on 100% (minimum 50% postconsumer) recycled paper. Available at: www.epa.gov/epawaste.

Google Scholar

Ulukardesler, A. H. (2023). Biodiesel production from waste cooking oil using different types of catalysts. Processes 11 (7), 2035. doi:10.3390/pr11072035

CrossRef Full Text | Google Scholar

Undavalli, V. K., Ling, C., and Khandelwal, B. (2021). Impact of alternative fuels and properties on elastomer compatibility. Aviat. Fuels, 113–132. doi:10.1016/B978-0-12-818314-4.00001-7

CrossRef Full Text | Google Scholar

Veluru, S., Hamzah, H. T., Tukaram, B. M., Poiba, V. R., and Mahdi, H. S. (2022). A review on biodiesel production from various feedstocks by transesterification. IOP Conf. Ser. Mater Sci. Eng. 1258 (1), 012024. doi:10.1088/1757-899x/1258/1/012024

CrossRef Full Text | Google Scholar

Waseem, M., Munsif, S., and Rashid, U. (2014). Physical properties of α-Fe2O3 nanoparticles fabricated by modified hydrolysis technique. Appl. Nanosci. Switz. 4 (5), 643–648. doi:10.1007/s13204-013-0240-y

CrossRef Full Text | Google Scholar

Weldeslase, M. G., Benti, N. E., Desta, M. A., and Mekonnen, Y. S. (2023). Maximizing biodiesel production from waste cooking oil with lime-based zinc-doped CaO using response surface methodology. Sci. Rep. 13 (1), 4430. doi:10.1038/s41598-023-30961-w

PubMed Abstract | CrossRef Full Text | Google Scholar

Widayat, D. A. P., and Nursafitri, I. (2019). “Synthesis and catalytic evaluation of hematite (α-Fe2O3) magnetic nanoparticles from iron sand for waste cooking oil conversion to produce biodiesel through esterification-transesterification method,” in IOP conference series: materials science and engineering United Kingdom: (Institute of Physics Publishing). doi:10.1088/1757-899X/509/1/012035

CrossRef Full Text | Google Scholar

Widayat, W., Maheswari, N. T., Fitriani, W., Buchori, L., Satriadi, H., Kusmiyati, K., et al. (2023). Preparation of MgO-CaO/SiO2 catalyst from dolomite and geothermal solid waste for biodiesel production. Int. J. Renew. Energy Dev. 12 (3), 541–549. doi:10.14710/ijred.2023.51573

CrossRef Full Text | Google Scholar

Xie, W., and Wang, H. (2020a). Immobilized polymeric sulfonated ionic liquid on core-shell structured Fe3O4/SiO2 composites: a magnetically recyclable catalyst for simultaneous transesterification and esterifications of low-cost oils to biodiesel. Renew. Energy 145, 1709–1719. doi:10.1016/j.renene.2019.07.092

CrossRef Full Text | Google Scholar

Xie, W., and Wang, H. (2020b). Immobilized polymeric sulfonated ionic liquid on core-shell structured Fe3O4/SiO2 composites: a magnetically recyclable catalyst for simultaneous transesterification and esterifications of low-cost oils to biodiesel. Renew. Energy 145, 1709–1719. doi:10.1016/j.renene.2019.07.092

CrossRef Full Text | Google Scholar

Zhang, Q., Hong, X., Lei, J., Lei, Y., Yang, Y., Cheng, J., et al. (2024). Environmentally-friendly preparation of Sn(II)-BDC supported heteropolyacid as a stable and highly efficient catalyst for esterification reaction. J. Saudi Chem. Soc. 28 (3), 101832. doi:10.1016/j.jscs.2024.101832

CrossRef Full Text | Google Scholar