Ferroelectric polarization reversals in C2N/α-In2Se3 van der Waals heterostructures: a conversion from the traditional type-II to S-scheme

Introduction: Ferroelectric substances, characterized by inherent spontaneous polarization, can boost photocatalytic efficiency by facilitating the separation of photogenerated carriers. However, conventional photocatalysts with perovskite-class ferroelectricity are generally constrained by their 3D arrangement, leading to less accessible active sites for catalysis and a smaller specific surface area compared to a 2D layout.

Methods: In my research, I developed a 2D ferroelectric heterostructure consisting of C₂N/α-In₂Se₃. I performed first-principle calculations on the 2D C₂N/α-In₂Se₃ heterostructure, specifically varying the out-of-plane ferroelectric polarization directions. I primarily focused on C₂N/α-In₂Se₃ (I) and C₂N/α-In₂Se₃ (II) heterostructures.

Results: My findings revealed that reversing the ferroelectric polarization of the 2D α-In₂Se₃ layer in the heterostructures led to a transition from the conventional type-II [C₂N/α-In₂Se₃ (I)] to an S-scheme [C₂N/α-In₂Se₃ (II)]. The S-scheme heterostructure [C2N/α-In₂Se₃ (II)] demonstrated a high optical absorption rate of 17% in visible light, marking it as a promising photocatalytic material.

Discussion: This research underscores the significance of ferroelectric polarization in facilitating charge transfer within heterogeneous structures. It provides a theoretical perspective for developing enhanced S-scheme photocatalysts, highlighting the potential of 2D ferroelectric heterostructures in photocatalytic applications.

1 Introduction

Photocatalysis is an emerging sustainable technology that utilizes semiconductor photocatalysts to drive chemical reactions by light irradiation. Upon photon absorption greater than the bandgap energy, photocatalysts generate electron-hole pairs that enable reduction-oxidation reactions on the surface. This allows the conversion of organic contaminants into less harmful products using solar energy (Wen et al., 2019). Titanium dioxide (TiO₂) is the most studied photocatalyst owing to its chemical stability, low cost, and lack of toxicity (Maness et al., 1999). However, the large bandgap of TiO₂ limits light harvesting to ultraviolet irradiation (Ma et al., 2016; Wang et al., 2018). Perovskite materials with the general formula of ABX₃ have emerged as promising photocatalysts for various applications in recent years (Grabowska, 2016; Zhang et al., 2016). The prototypical perovskite photocatalyst is methylammonium lead triiodide (MAPbI₃), which has a direct bandgap of 1.6 eV optimal for visible light absorption (He and Galli, 2014). The intrinsic properties of perovskites, including high optical absorption, a tunable bandgap, high charge carrier mobility, and long diffusion length, enable efficient generation and transportation of charge carriers upon light irradiation (Rehman et al., 2015). These merits make perovskites effective for photocatalytic redox reactions such as water splitting and CO₂ reduction under solar light (Zhang et al., 2016; Huang et al., 2023). Strategies including elemental doping, heterostructuring with other semiconductors, and nanostructuring have been applied to further enhance the photocatalytic performance and stability of perovskites (Chen et al., 2020).

The recent surge of interest in fabricating van der Waals (vdW) heterostructures by layering various two-dimensional (2D) materials is a testament to the method’s effectiveness in engendering outstanding diverse properties (Frisenda et al., 2018; Huo and Guo, 2022; Ren et al., 2023a; Wang et al., 2023). These heterostructures benefit from in-plane stability, secured by robust covalent bonds, while layers in the stacking direction are interconnected through the weaker vdW forces (Ajayan et al., 2016; Zhang et al., 2023). This harmonious blend of the superlative properties of multiple 2D materials endows vdW heterostructures with superior electronic characteristics (Geim and Grigorieva, 2013). The large surface area provides abundant catalytic active sites (Rezaie et al., 2021). Tunable bandgaps by controlling thickness, strain, and stacking order allows optimized solar light absorption (Liu et al., 2016). High carrier mobilities facilitate charge transfer to reactive sites (Jiang et al., 2019; Ren et al., 2023b). Constructing heterostructures using 2D materials can promote charge separation and extend carrier lifetime. Hence, the exploration for stable vdW heterostructures with superior electronic properties has emerged as a hotbed of research (Huang et al., 2023).

Layered carbon nitride (C₂N) has emerged as a promising metal-free photocatalyst for various energy conversion and environmental remediation applications (Huo and Guo, 2022). The graphitic structure of C₂N with conjugated tri-s-triazine units linked by tertiary amines enables strong visible light absorption, high chemical stability, and tunable electronic properties. The creation of this 2D C₂N material, facilitated by an efficient wet-chemical reaction method, opens new possibilities for its applications in photocatalysis (Zhang et al., 2015; Ashwin Kishore and Ravindran, 2017; Kishore and Ravindran, 2017). Recent studies have shown that modifying the textural and electronic properties of C₂N can further enhance its photocatalytic (Kumar et al., 2018; Tang et al., 2019; Tan et al., 2021). Overall, rationally designed C₂N-based photocatalysts have demonstrated great potential for solar fuel synthesis, CO₂ reduction, nitrogen fixation, and water treatment (Yu et al., 2018; Zhou and Han, 2020). Further work to understand the structure-activity relationships and in-depth mechanisms in C₂N photocatalysis could unlock its full potential for sustainable solar energy utilization.

The inherent polarization of ferroelectric materials unlocks new possibilities for engineering efficient photocatalysts by promoting the separation of photogenerated charge carriers. Xu et al. (2021) (Huang et al., 2018; Chen et al., 2019) demonstrated that the ferroelectric heterostructure of PbTiO₃/g-C₃N₄ showed enhanced photocatalytic hydrogen production and RhB degradation, benefitting from deliberate manipulation of the ferroelectricity. As is well known, α-In₂Se₃ is a ferroelectric material. Computational and experimental analyses have demonstrated that emerging 2D α-In₂Se₃ can generate spontaneous ferroelectric polarization due to its unique asymmetric structure, which is considered a promising photocatalyst for water splitting and CO₂ electrocatalytic reduction (Ju et al., 2019; Luo et al., 2020; Luo et al., 2021a; Ju et al., 2021). Recently, the COCN/α-In₂Se₃ heterostructure has achieved good results in the field of photocatalysis (Pan et al., 2023). In this paper, we employ first-principles calculations to present an in-depth exploration of a novel 2D vertical ferroelectric C₂N/α-In₂Se₃ vdW heterostructure. C₂N has a high recombination rate, which is not conducive to photolysis of water; researchers often use van der Waals methods to construct type-II to promote the separation of electrons and holes. The single-layer In₂Se₃ material has intrinsic out-of-plane ferroelectric properties. This kind of ferroelectric material can provide a built-in electric field, reduce the electron-hole recombination rate, and provide the possibility of S-scheme configuration. We can thus combine In₂Se₃ and C₂N, and use ferroelectric polarization reversal to construct a paradigm van der Waals heterostructure to explore the potential of the heterostructure in photocatalytic activity (Luo et al., 2021b).

Our objective is to offer a comprehensive understanding of the electronic, optical, and polarization flip characteristics intrinsic to the heterostructure. By building upon the existing knowledge framework around 2D materials, we aspire to contribute significant insights to the design and optimization of vdW heterostructures with the ultimate goal of maximizing their potential in nanotechnology and optoelectronics applications.

2 Computational methods

All of the simulations are performed on the Quantum Espresso package (Giannozzi et al., 2009) based on density functional theory (DFT). The Perdew-Burke-Ernzerhof (PBE) (Perdew et al., 1996) exchange correlation functional at the generalized gradient approximation (GGA) level was used together with ultrasoft pseudopotentials (USPP) (Kresse and Joubert, 1999). The long-range vdW interlayer interaction in the C₂N/α-In₂Se₃ heterostructure is described by Grimme’s DFT-D2 correction method (Grimme, 2006). The vacuum distance in c-direction was set 30 Å to avoid the interaction between the nearest neighboring units. The energy cutoffs of 60 and 600 Ry were chosen for the wave functions and the charge densities, respectively. During relaxation, the unit-cell lattice vectors, as well as the atomic coordinates, were fully relaxed until the force on each atom was less than 0.02 eV·Å⁻¹ and the electron energy was less than 10⁻⁶ eV. The band-gap and the optical absorption are modified by the Heyd-Scuseria-Ernzerhof (HSE06) (Heyd et al., 2003) hybrid exchange-correlation functional. Other calculations are modified by the PBE exchange correlation functional at the generalized gradient approximation (GGA) level. Ground-state calculations were carried out on a regular 3 × 3 × 1 mesh of k points, and the Fermi surface was broadened by the Gaussian smearing method (Marzari et al., 1999).

3 Results and discussion

Before delving into the C₂N/α-In₂Se₃ heterostructure, an investigation was conducted on the structural and electronic properties of individual C₂N and α-In₂Se₃ monolayers. The C₂N monolayer, belonging to the space group P6mm (183), features a uniform distribution of pores and nitrogen atoms. Distinguished by C-N separations of 1.33 Å and C-C separations of 1.42 and 1.46 Å, all the atoms within this single layer are positioned almost completely in the same plane. In the case of In₂Se₃, the most stable α- In₂Se₃ structure was analyzed, revealing a monolayer with the space group Cm (8). The optimized In-Se distance in the α-In₂Se₃ monolayer ranges from 2.54 to 2.91 Å. Optimized lattice parameters for both α-In₂Se₃ and C₂N monolayers are 4.07 and 8.33 Å, respectively, which are constant with the experimental results of 4.05 and 8.30 Å (Mahmood et al., 2015; Zhou et al., 2015). These findings align with experimental measurements and previous theoretical outcomes.

Considering the lattice mismatch experimentally, a 1 × 1 C₂N and 2 × 2 α-In₂Se₃ were adopted to construct a van der Waals heterostructure. The top and side views of optimized structure are illustrated in Figures 1A, B. Evident from Figure 1B, that α-In₂Se₃ monolayer displaies non-centro symmetryis and has a dipole moment in the c-direction (out-of-plane ferroelectric). Hence, there are two stacking models in which α-In₂Se₃ comes into contact with C₂N to establish a heterostructure. Their structures are displayed in Figures 1C, D with opposite polarization directions. The structure in Figure 1C is defined as C₂N/α-In₂Se₃ (I) and the structure in Figure 1D as C₂N/α-In₂Se₃ (II). The lattice mismatch of the two C₂N/α-In₂Se₃ heterostructures were calculated to be about 2.2%, enabling the construction of a matchable periodic interface for both structures. To get the lowest energy configuration, firstly, the minimum energy configuration in the c-direction was identified. Figure 1F shows the binding energy varies with layer spacing. The determination of the binding energy involves computations of the heterostructure’s energy and that of its monolayer, utilizing the equation ${\mathrm{E}}_{\mathrm{b}}={\mathrm{E}}_{\mathrm{C}2\mathrm{N}/\mathrm{\alpha }-\text{In}2\text{Se}3}-{\mathrm{E}}_{\mathrm{C}2\mathrm{N}}-{\mathrm{E}}_{\mathrm{\alpha }-\text{In}2\text{Se}3}$ to derive the differential. The binding energy trends of the two heterostructures closely mirror each other, initially presenting a parabolic decrease followed by a linear upswing. The binding energy of the two heterostructures exhibit nearly identical trends, first decreasing parabolically then increasing linearly. C₂N/α-In₂Se₃ (I) possesses the lowest binding energy at a layer spacing of 3.455 Å. C₂N/α-In₂Se₃ (II) possesses the lowest binding energy at 3.457 Å. Meanwhile, compared with C₂N/α-In₂Se₃ (I), C₂N/α-In₂Se₃ (II) had lower binding energy, which was the best configuration. The binding energies of the two are −604 and −660 meV respectively. The two E_b values are comparable to these of BlueP/g-GeC (−93.40 meV) (Gao et al., 2019) and much larger than that of BlueP/Sc₂CF₂ (−143.74 meV) (Li et al., 2020), indicating their good thermodynamic stability. We also investigated the influence of different stacking methods on the energy of C₂N/α-In₂Se₃ heterostructure and calculated the stacking-dependent potential energy surface shown in Figure 1E, which illustrates how the energy varies with interlayer sliding. When the structure is most stable during interlayer sliding, each C₂N atom aligns with an α-In₂Se₃ atomic gap. The lowest energy structure was found to be as shown in Figures 1A, B.

FIGURE 1

FIGURE 1. (A) The top view of the C₂N/α-In₂Se₃ heterostructure structure. (B) The side view of the C₂N/α-In₂Se₃ heterostructure structure. (C) The side view of the C₂N/α-In₂Se₃ (I) heterostructure. (D) The side view of the C₂N/α-In₂Se₃ (II) heterostructure. (E) The stacking-dependent potential energy surface of the C₂N/α-In₂Se₃ heterostructure structure. (F) The binding energy evolution as a function of interlayer spacing.

In the investigation of the electronic structure of C₂N/α-In₂Se₃ heterostructures, the calculated projected band structures with PBE functional are presented in Figures 2A, D. A marked difference can be observed in the band structures of these two C₂N/α-In₂Se₃ heterostructures. Detailed bandgap information and work function information are described in Table 1. In Figure 2A, the conduction band minimum (CBM) of C₂N is lower than that of α-In₂Se₃, while the valence band maximum (VBM) of α-In₂Se₃ is higher than that of C₂N. For the C₂N/α-In₂Se₃ (II) heterostructure, however, both the CBM and VBM of C₂N are higher than that of α-In₂Se₃, which is different to that of C₂N/α-In₂Se₃ (I). But the two heterostructures maintain type-II band alignment. Furthermore, Figures 2B, C show the partial charge density of VBM and CBM for C₂N/α-In₂Se₃ (I). Like the band structure of C₂N/α-In₂Se₃ (I), the charge of CBM is localized on C₂N, while the charge of VBM is localized on α-In₂Se₃. Upon reversal of the ferroelectric polarization in the α-In₂Se₃ layer [C₂N/α-In₂Se₃ (II)], the contribution of CBM and VBM also switches. The partial charge density of C₂N/α-In₂Se₃ (II) can be seen in Figures 2E, F, where the CBM and VBM are contributed to by C₂N and In₂Se₃, respectively, which is opposite to that of C₂N/α-In₂Se₃ (I). Interestingly, although the type-II band alignment is preserved, the contribution is now opposite to that of C₂N/α-In₂Se₃ (I). Electrons and holes are separated in type-II band alignment and located in different layers of heterostructure, which greatly benefits photocatalytic devices (Ma et al., 2021; Ju et al., 2022).

FIGURE 2

FIGURE 2. (A,D) The projected band structure of C₂N/α-In₂Se₃ (I) and C₂N/α-In₂Se₃ (II). The red line indicates the contribution of α-In₂Se₃, and the blue line represent the contribution of C₂N. (B,C) The partial charge density of the valence band maximum (VBM) and conduction band minimum (CBM) for C₂N/α-In₂Se₃ (I) with isosurface = 0.0014 e/ų. (E,F) The partial charge density of the VBM and CBM for C₂N/α-In₂Se₃ (II) with isosurface = 0.0012 e/ų.

TABLE 1

TABLE 1. Lattice constants, bandgaps, and work functions for each structure.

To obtain a thorough comprehension of the interfacial impact, an analysis was conducted on the average planar electrostatic potential along c-direction. The calculation of the work function is done by the formula ${\mathrm{W}}_{\mathrm{F}}={\mathrm{E}}_{\mathrm{v}}-{\mathrm{E}}_{\mathrm{F}}$. As depicted in Figure 3, the work function (W_F) of the C₂N monolayer is 5.61 eV, while the two surfaces of α-In₂Se₃ exhibit W_F of 4.73 and 5.94 eV. At the interface of the heterostructure, electrons typically migrate from the material with a lower W_F to the one with a higher W_F. But when a two-dimensional material has different surface work functions on each side, charge transfer occurs when it contacts a two-dimensional material with the same surface work function on both sides. However, it should be noted that the charge transfer in this case may differ from that which would occur when the two materials are considered separately. Therefore, a comprehensive analysis of both the impact of the surface work function on each side of the two-dimensional material and the effects of charge transfer during material contact is necessary to gain a comprehensive understanding of the material’s electrical properties.

FIGURE 3

FIGURE 3. (A) The electrostatic potential of the C₂N heterostructure. (B) The electrostatic potential of the α-In₂Se₃ heterostructure. (C) The electrostatic potential of the C₂N/α-In₂Se₃ (I) heterostructure. (D) The electrostatic potential of the C₂N/α-In₂Se₃ (II) heterostructure.

To elucidate the interlayer charge transfer mechanism, differential charge density calculations were performed, accompanied by a one-dimensional linear average along the c-direction, as depicted in Figures 4A, B. Positive values indicate charge accumulation, while negative values signify charge decay. The direction of the electric field is from positive charges to negative charges. It can be found that no matter whether it is before or after ferroelectric inversion, charge accumulation occurs on the α-In₂Se₃ side and charge loss occurs on the C₂N side. Notably, the direction of the built-in electric field remains unaltered before and after ferroelectric inversion, consistently pointing from C₂N to α-In₂Se₃. Moreover, a difference W_F (Δφ) of 1.343 and 1.023 eV was observed in C₂N/α- In₂Se₃ (I) and (II), respectively (Figures 3C, D), suggesting that the depolarization field in α-In₂Se₃ is either attenuated or amplified by varying interfacial interactions. When the built-in electric field aligns with the original electric field of α-In₂Se₃, Δφ is enhanced; otherwise, it weakens. Hindered by E_int, the diffusive motion of electrons and holes eventually reaches equilibrium due to diffusion forces. This structure, as a result, effectively promotes carrier separation in C₂N/α-In₂Se₃ heterostructures.

FIGURE 4

FIGURE 4. (A,B) The one-dimensional linear average differential charge density along the c-direction of C₂N/α-In₂Se₃ (I) and C₂N/α-In₂Se₃ (II). (C) The band edge alignments of the C₂N/α-In₂Se₃ (I) and C₂N/α-In₂Se₃ (II), and the solid red arrow shows the orientation of the inherent electric field.

At the interface between the two semiconductors, the direction of the built-in electric field reflects the band bending at the interface. Based on Figure 4C, it can be inferred that upon photoexcitation, α-In₂Se₃ in C₂N/α-In₂Se₃ (I) forms a potential well for photogenerated electrons and a potential barrier for photogenerated holes, while C₂N in C₂N/α-In₂Se₃ (I) forms a potential barrier for photogenerated electrons and a potential well for photogenerated holes. The drift and diffusion of photo-generated carriers in the valence band of α-In₂Se₃ and the conduction band of C₂N are double constrained by the potential barrier and the built-in electric field and cannot be well recombined, but after the ferroelectric reversal occurs. In C₂N/α-In₂Se₃ (II), though the potential barrier/well relationships remain unchanged, the built-in electric field facilitates the combination of photogenerated electrons in the α-In₂Se₃ potential well with photogenerated holes in the C₂N potential well, leaving only photogenerated carriers obstructed by the potential barrier, leading to the formation of an S-scheme heterostructure. The C₂N/α-In₂Se₃ (II) heterostructure meets simultaneous oxidation O₂ (−0.13 V), C₇H₈ (1.60 V), and OH⁻ (2.59 V). In practice, the experiment is carried out in the non-zero pH solution according to the formula below:

$\mathrm{E}\left(\text{NHE}\right)=\mathrm{E}\left(\text{RHE}\right)-0.0591\times \text{pH}(1)$

The catalytic potential at pH = 7 is also marked with a purple line in Figure 4C. It can be found that according to the specific reaction to be catalyzed, different pH environments can be selected to achieve the best results. S-scheme heterogeneous structures are more promising in photocatalysts compared to traditional type-II heterogeneous structures owing to their robust redox capabilities (Fu et al., 2019; Li et al., 2022; Li et al., 2023). Compared with the traditional type-II heterostructures, the photogenerated electrons and holes accumulate in the conduction band and valence band of the reduced semiconductor photocatalyst and the oxidized semiconductor photocatalyst, respectively, resulting in weakened redox ability. In the S-scheme heterostructure, the effective electrons and holes are preserved, and the meaningless photogenerated carriers are recombined.

Strain engineering, the deliberate introduction of strain in materials to modify their band structure, has emerged as an important tool in materials science (Hou et al., 2023). By manipulating the strain in a material, we can substantially alter its electronic, optical, and mechanical properties. Biaxial strain tuning was implemented on C₂N/α-In₂Se₃ (I) and C₂N/α-In₂Se₃ (II) heterostructures; the results are presented in Figures 5, 6, respectively. Under compressive strain, C₂N/α-In₂Se₃ (I) retained a type-II band alignment. However, tensile strain transformed the heterostructure into a type-I alignment. In contrast, the C₂N/α-In₂Se₃ (II) interface preserved a type-II band alignment under both compressive and tensile biaxial strains. Furthermore, the variation of bandgap size and bandgap type under the control of biaxial strain is demonstrated in Figure 7.

FIGURE 5

FIGURE 5. Demonstration of the band structure of C₂N/α-In₂Se₃ (I) under different biaxial strains.

FIGURE 6

FIGURE 6. Demonstration of the band structure of C₂N/α-In₂Se₃ (II) under different biaxial strains.

FIGURE 7

FIGURE 7. Demonstration of the band gap of C₂N/α-In₂Se₃ (I) and under C₂N/α-In₂Se₃ (II) different biaxial strains. Blue represents an indirect bandgap and red represents a direct bandgap.

The absorption coefficient is a critical factor in the S-scheme heterostructure. Therefore, the corresponding HSE absorption spectrums of C₂N, α-In₂Se₃ monolayers, and C₂N/α-In₂Se₃ heterostructures are shown in Figures 8A, B. The optical absorption coefficient α(ω) was obtained using the formula presented below:

$\mathrm{\alpha }\left(\mathrm{\omega }\right)=\sqrt{2}\mathrm{\omega }{\left[\sqrt{{\mathrm{\epsilon }}_1^2\left(\mathrm{\omega }\right)+{\mathrm{\epsilon }}_2^2\left(\mathrm{\omega }\right)}-{\mathrm{\epsilon }}_1\left(\mathrm{\omega }\right)\right]}^{1/2}(2)$

where ε₁(ω) and ε₂(ω) are the real part and imaginary part of the complex dielectric function, respectively. The dielectric function varies with energy as depicted in Figures 8C, D. The real component characterizes the refractive properties of light, whereas the imaginary constituent signifies the absorbance qualities. Figure 8A displays the calculated optical absorption coefficient α(ω) as a function of energy for both the C₂N/α-In₂Se₃ heterostructure and the respective isolated layers. As can be seen, the absorption coefficient of the C₂N/α-In₂Se₃ (I) heterostructure initially rises with increasing phonon energy. The absorption coefficients of the C₂N monolayer and C₂N/α-In₂Se₃ (I) heterostructure exhibit prominent peaks in visible light. While the absorption coefficient of the α-In₂Se₃ monolayer gradually increases in visible light. It retains excellent optical absorption properties even after ferroelectric polarization reversal. The optical absorption property of C₂N/α-In₂Se₃ (II) illustrates its potential in photocatalysts.

FIGURE 8

FIGURE 8. (A,B) The optical absorption of C₂N/α-In₂Se₃ (I) and C₂N/α-In₂Se₃ (II) heterostructures. (C,D) The dielectric function of C₂N/α-In₂Se₃ (I) and C₂N/α-In₂Se₃ (II) heterostructures.

4 Conclusion

In summary, the optoelectronic characteristics of two-dimensional C2N/α-In2Se3 heterogeneous structures with varied polarization orientations in the α-In2Se3 layer were methodically examined using first-principles calculations. The results demonstrate that the traditional type-II [C₂N/α-In₂Se₃ (I) heterostructure] with an indirect bandgap (0.63 eV) transformed into the promising S-scheme [C₂N/α-In₂Se₃ (II) heterostructure] with a direct bandgap (0.56 eV) when the ferroelectric polarization of α-In₂Se₃ was reversed from up to down. The work function and one-dimensional linear average differential charge density revealed the S-scheme heterostructure is a promising photocatalytic material. Concurrently, excellent optical absorption was exhibited, providing design insights for novel photocatalysts.

Data availability statement

The raw data supporting the conclusion of this article will be made available by the authors, without undue reservation.

Author contributions

The author confirms being the sole contributor of this work and has approved it for publication.

Funding

The author(s) declare that no financial support was received for the research, authorship, and/or publication of this article.

Conflict of interest

The author declares that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.

Publisher’s note

All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article, or claim that may be made by its manufacturer, is not guaranteed or endorsed by the publisher.

References

Ajayan, P., Kim, P., and Banerjee, K. (2016). Two-dimensional van der Waals materials. Phys. Today 69 (9), 38–44. doi:10.1063/pt.3.3297

CrossRef Full Text | Google Scholar

Ashwin Kishore, M., and Ravindran, P. (2017). Tailoring the electronic band gap and band edge positions in the C2N monolayer by P and as substitution for photocatalytic water splitting. J. Phys. Chem. C 121 (40), 22216–22224. doi:10.1021/acs.jpcc.7b07776

CrossRef Full Text | Google Scholar

Chen, F., Huang, H., Guo, L., Zhang, Y., and Ma, T. (2019). The role of polarization in photocatalysis. Angew. Chem. Int. Ed. 58 (30), 10061–10073. doi:10.1002/anie.201901361

CrossRef Full Text | Google Scholar

Chen, J., Ouyang, W., Yang, W., He, J. H., and Fang, X. (2020). Recent progress of heterojunction ultraviolet photodetectors: Materials, integrations, and applications. Adv. Funct. Mater. 30 (16), 1909909. doi:10.1002/adfm.201909909

CrossRef Full Text | Google Scholar

Frisenda, R., Navarro-Moratalla, E., Gant, P., De Lara, D. P., Jarillo-Herrero, P., Gorbachev, R. V., et al. (2018). Recent progress in the assembly of nanodevices and van der Waals heterostructures by deterministic placement of 2D materials. Chem. Soc. Rev. 47 (1), 53–68. doi:10.1039/c7cs00556c

PubMed Abstract | CrossRef Full Text | Google Scholar

Fu, J., Xu, Q., Low, J., Jiang, C., and Yu, J. (2019). Ultrathin 2D/2D WO3/g-C3N4 step-scheme H2-production photocatalyst. Appl. Catal. B Environ. 243, 556–565. doi:10.1016/j.apcatb.2018.11.011

CrossRef Full Text | Google Scholar

Gao, X., Shen, Y., Ma, Y., Wu, S., and Zhou, Z. (2019). A water splitting photocatalysis: Blue phosphorus/g-GeC van der Waals heterostructure. Appl. Phys. Lett. 114 (9), 883. doi:10.1063/1.5082883

CrossRef Full Text | Google Scholar

Geim, A. K., and Grigorieva, I. V. (2013). Van der Waals heterostructures. Nature 499 (7459), 419–425. doi:10.1038/nature12385

PubMed Abstract | CrossRef Full Text | Google Scholar

Giannozzi, P., Baroni, S., Bonini, N., Calandra, M., Car, R., Cavazzoni, C., et al. (2009). Quantum espresso: A modular and open-source software project for quantum simulations of materials. J. Phys. Condens. matter 21 (39), 395502. doi:10.1088/0953-8984/21/39/395502

PubMed Abstract | CrossRef Full Text | Google Scholar

Grabowska, E. (2016). Selected perovskite oxides: Characterization, preparation and photocatalytic properties—a review. Appl. Catal. B Environ. 186, 97–126. doi:10.1016/j.apcatb.2015.12.035

CrossRef Full Text | Google Scholar

Grimme, S. (2006). Semiempirical GGA-type density functional constructed with a long-range dispersion correction. J. Comput. Chem. 27 (15), 1787–1799. doi:10.1002/jcc.20495

PubMed Abstract | CrossRef Full Text | Google Scholar

He, Y., and Galli, G. (2014). Perovskites for solar thermoelectric applications: A first principle study of CH3NH3AI3 (A= Pb and Sn). Chem. Mater. 26 (18), 5394–5400. doi:10.1021/cm5026766

CrossRef Full Text | Google Scholar

Heyd, J., Scuseria, G. E., and Ernzerhof, M. (2003). Hybrid functionals based on a screened Coulomb potential. J. Chem. Phys. 118 (18), 8207–8215. doi:10.1063/1.1564060

CrossRef Full Text | Google Scholar

Hou, Y., Ren, K., Wei, Y., Yang, D., Cui, Z., and Wang, K. (2023). Opening a band gap in biphenylene monolayer via strain: A first-principles study. Molecules 28 (10), 4178. doi:10.3390/molecules28104178

PubMed Abstract | CrossRef Full Text | Google Scholar

Huang, H., Tu, S., Du, X., and Zhang, Y. (2018). Ferroelectric spontaneous polarization steering charge carriers migration for promoting photocatalysis and molecular oxygen activation. J. colloid interface Sci. 509, 113–122. doi:10.1016/j.jcis.2017.09.005

PubMed Abstract | CrossRef Full Text | Google Scholar

Huang, L., Ren, K., Zhang, H., and Qin, H. (2023b). Enhanced mechanical and thermal properties of two-dimensional SiC and GeC with temperature and size dependence. Chin. Phys. B 32, 076103. doi:10.1088/1674-1056/acc78f

CrossRef Full Text | Google Scholar

Huang, Z., Ren, K., Zheng, R., Wang, L., and Wang, L. (2023a). Ultrahigh carrier mobility in two-dimensional IV–VI semiconductors for photocatalytic water splitting. Molecules 28 (10), 4126. doi:10.3390/molecules28104126

PubMed Abstract | CrossRef Full Text | Google Scholar

Huo, B., and Guo, C. Y. (2022). Advances in thermoelectric composites consisting of conductive polymers and fillers with different architectures. Molecules 27 (20), 6932. doi:10.3390/molecules27206932

PubMed Abstract | CrossRef Full Text | Google Scholar

Jiang, R., Wu, D., Lu, G., Yan, Z., and Liu, J. (2019). Modified 2D-2D ZnIn2S4/BiOCl van der Waals heterojunctions with CQDs: Accelerated charge transfer and enhanced photocatalytic activity under vis-and NIR-light. Chemosphere 227, 82–92. doi:10.1016/j.chemosphere.2019.04.038

PubMed Abstract | CrossRef Full Text | Google Scholar

Ju, L., Shang, J., Tang, X., and Kou, L. (2019). Tunable photocatalytic water splitting by the ferroelectric switch in a 2D AgBiP2Se6 monolayer. J. Am. Chem. Soc. 142 (3), 1492–1500. doi:10.1021/jacs.9b11614

PubMed Abstract | CrossRef Full Text | Google Scholar

Ju, L., Tan, X., Mao, X., Gu, Y., Smith, S., Du, A., et al. (2021). Controllable CO2 electrocatalytic reduction via ferroelectric switching on single atom anchored In2Se3 monolayer. Nat. Commun. 12 (1), 5128. doi:10.1038/s41467-021-25426-5

PubMed Abstract | CrossRef Full Text | Google Scholar

Ju, L., Tang, X., and Kou, L. (2022). Polarization boosted catalysis: Progress and outlook. Microstructures 2, 2022008. doi:10.20517/microstructures.2021.14

CrossRef Full Text | Google Scholar

Kishore, M. A., and Ravindran, P. (2017). Enhanced photocatalytic water splitting in a C2N monolayer by C-site isoelectronic substitution. ChemPhysChem 18 (12), 1526–1532. doi:10.1002/cphc.201700165

PubMed Abstract | CrossRef Full Text | Google Scholar

Kresse, G., and Joubert, D. (1999). From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. b 59 (3), 1758–1775. doi:10.1103/physrevb.59.1758

CrossRef Full Text | Google Scholar

Kumar, R., Das, D., and Singh, A. K. (2018). C2N/WS2 van der Waals type-II heterostructure as a promising water splitting photocatalyst. J. Catal. 359, 143–150. doi:10.1016/j.jcat.2018.01.005

CrossRef Full Text | Google Scholar

Li, W., Li, X., Fu, X., Lou, Z., Zhu, Y., and Zhang, Y. (2023). Photo-induced conversion of type-II CoPc/BiOBr-NSs to S-scheme heterostructure for boosting CO2 photoreduction. Chem. Eng. J. 451, 138932. doi:10.1016/j.cej.2022.138932

CrossRef Full Text | Google Scholar

Li, X. H., Wang, B. J., Wang, G. D., and Ke, S. H. (2020). Blue phosphorene/Sc 2 CX 2 (X= O, F) van der Waals heterostructures as suitable candidates for water-splitting photocatalysts and solar cells. Sustain. Energy & Fuels 4 (10), 5277–5283. doi:10.1039/d0se01097a

CrossRef Full Text | Google Scholar

Li, X., Fang, G., Tian, Q., and Wu, T. (2022). Crystal regulation of BiVO4 for efficient photocatalytic degradation in g-C3N4/BiVO4 heterojunction. Appl. Surf. Sci. 584, 152642. doi:10.1016/j.apsusc.2022.152642

CrossRef Full Text | Google Scholar

Liu, Y., Weiss, N. O., Duan, X., Cheng, H. C., Huang, Y., and Duan, X. (2016). Van der Waals heterostructures and devices. Nat. Rev. Mater. 1 (9), 16042–16117. doi:10.1038/natrevmats.2016.42

CrossRef Full Text | Google Scholar

Luo, Y., Ren, C., Xu, Y., Yu, J., Wang, S., and Sun, M. (2021b). A first principles investigation on the structural, mechanical, electronic, and catalytic properties of biphenylene. Sci. Rep. 11 (1), 19008. doi:10.1038/s41598-021-98261-9

PubMed Abstract | CrossRef Full Text | Google Scholar

Luo, Y., Sun, M., Yu, J., and Schwingenschlogl, U. (2021a). Pd₄S₃Se₃, Pd₄S₃Te₃, and Pd₄Se₃Te₃: Candidate two-dimensional janus materials for photocatalytic water splitting. Chem. Mater. 33 (11), 4128–4134. doi:10.1021/acs.chemmater.1c00812

CrossRef Full Text | Google Scholar

Luo, Y., Wang, S., Shu, H., Chou, J. P., Ren, K., Yu, J., et al. (2020). A MoSSe/blue phosphorene vdw heterostructure with energy conversion efficiency of 19.9% for photocatalytic water splitting. Semicond. Sci. Technol. 35 (12), 125008. doi:10.1088/1361-6641/abba40

CrossRef Full Text | Google Scholar

Ma, S., Song, W., Liu, B., Zhong, W., Deng, J., Zheng, H., et al. (2016). Facet-dependent photocatalytic performance of TiO2: A dft study. Appl. Catal. B Environ. 198, 1–8. doi:10.1016/j.apcatb.2016.05.017

CrossRef Full Text | Google Scholar

Ma, Z., Wang, S., Li, C., and Wang, F. (2021). Strain engineering for C2N/Janus monochalcogenides van der Waals heterostructures: Potential applications for photocatalytic water splitting. Appl. Surf. Sci. 536, 147845. doi:10.1016/j.apsusc.2020.147845

CrossRef Full Text | Google Scholar

Mahmood, J., Lee, E. K., Jung, M., Shin, D., Jeon, I. Y., Jung, S. M., et al. (2015). Nitrogenated holey two-dimensional structures. Nat. Commun. 6 (1), 6486. doi:10.1038/ncomms7486

PubMed Abstract | CrossRef Full Text | Google Scholar

Maness, P. C., Smolinski, S., Blake, D. M., Huang, Z., Wolfrum, E. J., and Jacoby, W. A. (1999). Bactericidal activity of photocatalytic TiO2 reaction: Toward an understanding of its killing mechanism. Appl. Environ. Microbiol. 65 (9), 4094–4098. doi:10.1128/aem.65.9.4094-4098.1999

PubMed Abstract | CrossRef Full Text | Google Scholar

Marzari, N., Vanderbilt, D., De Vita, A., and Payne, M. (1999). Thermal contraction and disordering of the Al (110) surface. Phys. Rev. Lett. 82 (16), 3296–3299. doi:10.1103/physrevlett.82.3296

CrossRef Full Text | Google Scholar

Pan, L. Y., Liu, B., Yang, J., Yin, S. F., and Cai, M. Q. (2023). Ferroelectric polarization enhancing photocatalytic performance of 2D carbon and oxygen co-doping g-C3N4/α-In2Se3 heterostructure: A conversion of traditional type-II to S-scheme. Appl. Phys. Lett. 122 (24). doi:10.1063/5.0154934

CrossRef Full Text | Google Scholar

Perdew, J. P., Burke, K., and Ernzerhof, M. (1996). Generalized gradient approximation made simple. Phys. Rev. Lett. 77 (18), 3865–3868. doi:10.1103/physrevlett.77.3865

PubMed Abstract | CrossRef Full Text | Google Scholar

Rehman, W., Milot, R. L., Eperon, G. E., Wehrenfennig, C., Boland, J. L., Snaith, H. J., et al. (2015). Charge-carrier dynamics and mobilities in formamidinium lead mixed-halide perovskites. Adv. Mater. 27 (48), 7938–7944. doi:10.1002/adma.201502969

PubMed Abstract | CrossRef Full Text | Google Scholar

Ren, K., Shu, H., Wang, K., and Qin, H. (2023b). Two-dimensional MX 2 Y 4 systems: Ultrahigh carrier transport and excellent hydrogen evolution reaction performances. Phys. Chem. Chem. Phys. 25 (6), 4519–4527. doi:10.1039/d2cp04224j

PubMed Abstract | CrossRef Full Text | Google Scholar

Ren, K., Zhang, G., Zhang, L., Qin, H., and Zhang, G. (2023a). Ultraflexible two-dimensional janus heterostructure superlattice: A novel intrinsic wrinkled structure. Nanoscale 15 (19), 8654–8661. doi:10.1039/d3nr00429e

PubMed Abstract | CrossRef Full Text | Google Scholar

Rezaie, A. A., Lee, E., Luong, D., Yapo, J. A., and Fokwa, B. P. (2021). Abundant active sites on the basal plane and edges of layered van der Waals Fe3GeTe2 for highly efficient hydrogen evolution. ACS Mater. Lett. 3 (4), 313–319. doi:10.1021/acsmaterialslett.1c00048

CrossRef Full Text | Google Scholar

Tan, L., Nie, C., Ao, Z., Sun, H., An, T., and Wang, S. (2021). Novel two-dimensional crystalline carbon nitrides beyond gC 3 N 4: Structure and applications. J. Mater. Chem. A 9 (1), 17–33. doi:10.1039/d0ta07437c

CrossRef Full Text | Google Scholar

Tang, H., Wang, R., Zhao, C., Chen, Z., Yang, X., Bukhvalov, D., et al. (2019). Oxamide-modified g-C3N4 nanostructures: Tailoring surface topography for high-performance visible light photocatalysis. Chem. Eng. J. 374, 1064–1075. doi:10.1016/j.cej.2019.06.029

CrossRef Full Text | Google Scholar

Wang, D., Liu, Z. P., and Yang, W. M. (2018). Revealing the size effect of platinum cocatalyst for photocatalytic hydrogen evolution on TiO2 support: A DFT study. ACS Catal. 8 (8), 7270–7278. doi:10.1021/acscatal.8b01886

CrossRef Full Text | Google Scholar

Wang, K., Ren, K., Hou, Y., Cheng, Y., and Zhang, G. (2023). Magnon-phonon coupling: From fundamental physics to applications. Phys. Chem. Chem. Phys. 25, 21802–21815. doi:10.1039/d3cp02683c

PubMed Abstract | CrossRef Full Text | Google Scholar

Wen, M., Li, G., Liu, H., Chen, J., An, T., and Yamashita, H. (2019). Metal–organic framework-based nanomaterials for adsorption and photocatalytic degradation of gaseous pollutants: Recent progress and challenges. Environ. Sci. Nano 6 (4), 1006–1025. doi:10.1039/c8en01167b

CrossRef Full Text | Google Scholar

Xu, T., Niu, P., Wang, S., and Li, L. (2021). High visible light photocatalytic activities obtained by integrating g-C3N4 with ferroelectric PbTiO3. J. Mater. Sci. Technol. 74, 128–135. doi:10.1016/j.jmst.2020.10.036

CrossRef Full Text | Google Scholar

Yu, S., Rao, Y. C., Wu, H. H., and Duan, X. M. (2018). C 2 N: an excellent catalyst for the hydrogen evolution reaction. Phys. Chem. Chem. Phys. 20 (44), 27970–27974. doi:10.1039/c8cp05022h

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhang, C., Xu, J., Song, H., Ren, K., Yu, Z. G., and Zhang, Y. W. (2023). Achieving boron–carbon–nitrogen heterostructures by collision fusion of carbon nanotubes and boron nitride nanotubes. Molecules 28 (11), 4334. doi:10.3390/molecules28114334

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhang, G., Liu, G., Wang, L., and Irvine, J. T. (2016). Inorganic perovskite photocatalysts for solar energy utilization. Chem. Soc. Rev. 45 (21), 5951–5984. doi:10.1039/c5cs00769k

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhang, R., Li, B., and Yang, J. (2015). Effects of stacking order, layer number and external electric field on electronic structures of few-layer C 2 N-h 2D. Nanoscale 7 (33), 14062–14070. doi:10.1039/c5nr03895b

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhou, J., Zeng, Q., Lv, D., Sun, L., Niu, L., Fu, W., et al. (2015). Controlled synthesis of high-quality monolayered α-in₂Se₃ via physical vapor deposition. Nano Lett. 15 (10), 6400–6405. doi:10.1021/acs.nanolett.5b01590

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhou, X., and Han, J. (2020). Design and simulation of C2N based solar cell by SCAPS-1D software. Mater. Res. Express 7 (12), 126303. doi:10.1088/2053-1591/abcdd6

CrossRef Full Text | Google Scholar