Recent advances in the removal of radioactive iodine by bismuth-based materials

Nowadays, the demand for nuclear power is continue increasing due to its safety, cleanliness, and high economic benefits. Radioactive iodine from nuclear accidents and nuclear waste treatment processes poses a threat to humans and the environment. Therefore, the capture and storage of radioactive iodine are vital. Bismuth-based (Bi-based) materials have drawn much attention as low-toxicity and economical materials for removing and immobilizing iodine. Recent advances in adsorption and immobilization of vapor iodine by the Bi-based materials are discussed in this review, in addition with the removal of iodine from solution. It points out the neglected areas in this research topic and provides suggestions for further development and application of Bi-based materials in the removal of radioactive iodine.

1 Introduction

Nuclear energy is one of the main sources of electrical energy in the world today. It is advantageous in safety, cleanliness, and lower total operating costs than almost all fossil fuels. The main issues that nuclear energy faced are operational safety and the disposal of radioactive waste (Kosaka et al., 2012; Woo, 2013). The released off-gas stream from the reprocessing of spent nuclear fuels and serious nuclear power plant accidents contains a variety of radioactive elements (⁹⁹Tc, ¹³⁷Cs, ⁹⁰Sr, ¹²⁹I, ¹³¹I, ³H¹⁴C, ⁸⁵Kr, actinides, lanthanides, etc.) (Soelberg et al., 2013; Subrahmanyam et al., 2015; Nandanwar et al., 2016; Riley et al., 2016). Radioactivity is a huge threat to humans and the environment due to its easy diffusion (Ojovan and Lee, 2011; Mowry et al., 2015; Yang et al., 2018; Chabauty et al., 2019). Among these radioactive elements, iodine compounds attract special attention because the iodine is concentrated in the thyroid, and its higher radioactivity can cause damage to the human body in a short time (Grossman et al., 1996; Goldsmith et al., 1999; Grossman et al., 2002; 2003; Lee et al., 2006; Thomas et al., 2009; Sava et al., 2013). The radioactivity is produced by ¹²⁹I, a long-period isotope with a half-life of 1.57 × 10⁷ years (Taylor, 1981; Michel et al., 2005; Zhang et al., 2011; Lin et al., 2019), and ¹³¹I, a short-lived isotope with a half-life of approximately 8.02 days (Thomas et al., 2009; Lee et al., 2018). In active waste gas, iodine mainly exists in the form of elemental substances, hydroiodic acid, and organic iodine (CH₃I) (Lin, 1981; Huang et al., 2010; Pillar et al., 2013). The initial form of iodine in spent nuclear fuel is cesium iodide. During the dissolution of spent nuclear fuel, iodine ions will react with free radicals produced by radiation to generate volatile elemental iodine. Part of elemental iodine will also react with organic impurities to generate organic iodine (Wren et al., 1999; Taghipour and Evans, 2000; Moriyama et al., 2010). These volatile iodine species make the separation and safe storage of radioactive iodine a great challenge.

There are two methods to collect gaseous radioisotopes: the wet scrubbing and the solid phase adsorption. The wet scrubbing includes Mercurex, Iodox, electrolytic and caustic scrubbing (Mailen and Horner, 1976; Horner et al., 1977; Riley et al., 2016). In these processes, the radioactive iodine species are chemically reacted with the liquid, whereas a large amount of secondary waste is produced (Riley et al., 2016). Compared with wet scrubbing, solid phase adsorption has attracted more attention because of its low cost, simple operation, and high adsorption efficiency (Munakata et al., 2003). Many kinds of materials have been applied in the adsorption of vapor radioactive iodine, including activated carbon (Deitz, 1987; Chien et al., 2011), graphene-based materials (Scott et al., 2015), zeolites (Chapman et al., 2010; Nenoff et al., 2014; Pham et al., 2016; Abney et al., 2017; Nan et al., 2018), metal-organic frameworks (MOFs) (Sava et al., 2012; Zhang et al., 2019; Miensah et al., 2022), covalent-organic frameworks (COFs) (Wang et al., 2018; Wang and Zhuang, 2019; Yang et al., 2019), layered double hydroxide-based materials (Ma et al., 2014; Lin et al., 2019), and aerogels (Subrahmanyam et al., 2015). In the adsorption of radioactive iodine, loading capacity and adsorption efficiency (separation capacity) are the main criteria for evaluating solid adsorbents, along with the stability under the harsh conditions of radioactive gas. For example, the activated carbon, especially loaded with KI/TEDA, has a strong iodine adsorption capacity due to its high porosity and large specific surface area (Deuber, 1986; Deitz, 1987; Pires et al., 2001; Ampelogova et al., 2002; Gonzalez-Garcia et al., 2013; Herdes et al., 2013; Zhou et al., 2014; Nandanwar et al., 2016). However, the thermal stability of activated carbon is poor, and its adsorption capacity is diminished at the operating temperature of spent fuel processing. Silver-based materials have been widely studied in iodine capture because silver can react with iodine to generate insoluble AgI (Kikuchi et al., 1978; Kindel et al., 1993; Sakurai and Takahashi, 1994; Funabashi et al., 1995; Modolo and Odoj, 1997; Mineo et al., 2002; Mineo et al., 2003; Takeshita and Azegami, 2004; Tanabe et al., 2010; Kulyukhin et al., 2012). Although silver-based materials have excellent performance in capturing ability and stability, the high cost and toxic of silver make it necessary to explore alternatives.

In recent years, Bi-based materials have received attentions from researchers due to their environmental and economic advantages including, 1) the toxicity of bismuth is relatively low, no occupational poisoning caused by bismuth or its compounds has been reported; 2) Bismuth is extremely weak in radioactivity with a half-life of about 1.9 × 10¹⁹ years; 3) bismuth is much cheaper than silver. In mechanism, bismuth can react with iodine to form BiI₃. In addition, Bi₂O₃ and Bi₂S₃ can also react with iodine (Liu et al., 2014; Cordova et al., 2020). In an aqueous solution, the formation of products (Bi_xO_yI_z) depends on the combined effects of the molar ratio of bismuth and iodine, temperature, pH, etc., (Kodama, 1992; Krumhansl and Nenoff, 2011).

Up to now, various types of Bi-based materials have been developed. Tesfay Reda et al. (2021a) divided the Bi-base materials in iodine capture into two categories: the materials applied in the capture of aqueous iodine and in the capture of vapor iodine. The Bi-based materials for capturing aqueous iodine were emphatically summarized. Ranjan et al. (2020) summarized the capture of pollutants in water by Bi-based materials. The study by Moore et al. (2020) mentioned four Bi-based compounds for iodine capture. The Bi-based materials were also summarized in an overview of metal Oxide-based materials (Muhire et al., 2022). Recently, the works about capturing vapor iodine by Bi-based materials is growing rapidly. Still, there is a lack of systematic study of these works. The main purpose of this review is to summarize recent advances in Bi-based materials for capturing radioactive iodine, especially the vapor iodine. Besides, the immobilization of radioactive iodine by Bi-based materials is also discussed. It aims to provide methods and suggestions for developing novel Bi-based iodine adsorption materials.

2 Vapor iodine capture

Gaseous iodine capture materials are mainly composed of active sites and carriers. The active sites capture iodine by chemical adsorption (like bismuth), and the carriers provide physical adsorption and load the active sites. Various materials have been developed to capture vapor radioactive iodine, and many of them were commercialized. Some of them, such as zeolites, carbon materials, MOFs, and some other materials, were used as carrier for bismuth and its compounds (shown in Figure 1).

FIGURE 1

FIGURE 1. Overview of Bi-based materials for gaseous iodine capture.

2.1 Capture mechanism

2.1.1 Carriers

The mechanism of most Bi-based materials capturing iodine composed by the primary chemical adsorption and the secondary physical adsorption. In the solid adsorbent, the main function of carriers is dispersing active sites. Some carriers (molecular sieves, carbon materials, organic polymers, etc.) also exhibit a certain degree of physical adsorption capacity due to their rich microporous structures. However, in the process of loading bismuth by impregnation, the microporous structure restricts bismuth from entering the materials, and the smaller pores are blocked which will decrease the specific surface area and increase the average pore diameter. On the contrary, mesoporous and macroporous structures have almost no physical adsorption capacity. The loading compounds are easier to enter the material, making the specific surface area and pore diameter smaller (Chang et al., 2022a). The observation of Bi⁰ nanoparticles by scanning electron microscopy (SEM) and transmission electron microscopy (TEM) (Tian et al., 2021a; Xian et al., 2022a; Tian et al., 2022) verified the above phenomena.

2.1.2 Active sites

Iodine reacts chemically with bismuth to mainly generate BiI_3, although other Bi_xO_yI_z compounds can be formed (Yang et al., 2015; Yang et al., 2016; Zou et al., 2019; Al-Mamoori et al., 2020). Bi₂O₃ and Bi₂S₃ also can react with iodine to form stable compounds. These materials’ adsorption mechanisms for iodide can be represented by the following equations (Dinh et al., 2020; Zou et al., 2021; Chen et al., 2022). In addition, bismuth exists in other forms of Bi(Ⅲ) in some materials (Dinh et al., 2020; Tesfay Reda et al., 2021b; Jung et al., 2021; Qin et al., 2022).

$\mathrm{B}\mathrm{i}+1.5{\mathrm{I}}_2={\mathrm{B}\mathrm{i}\mathrm{I}}_3$

${2\mathrm{B}\mathrm{i}}_2{\mathrm{O}}_3+2{\mathrm{I}}_2=4\mathrm{B}\mathrm{i}\mathrm{O}\mathrm{I}+{\mathrm{O}}_2$

${\mathrm{B}\mathrm{i}}_2{\mathrm{S}}_3+3{\mathrm{I}}_2+3{\mathrm{O}}_2={2\mathrm{B}\mathrm{i}\mathrm{I}}_3+3{\mathrm{S}\mathrm{O}}_2$

${\mathrm{B}\mathrm{i}}_2{\mathrm{S}}_3+3{\mathrm{I}}_2={2\mathrm{B}\mathrm{i}\mathrm{I}}_3+3\mathrm{S}$

The change of the bismuth state in these materials can be detected by powder X-ray diffraction (PXRD) and X-ray photoelectron spectroscopy (XPS). PXRD pattern can simply indicate the existence of Bi⁰ (2θ = 22.5, 27.2, 38.0, 39.7, 46.1, 46.7, 48.1, 55.8, 55.5, 55.8, 62.7, 64.6, 71.0, and 72.1°; PDF No. 85-1329), Bi₂O₃ (2θ = 27.9, 31.8, 32.8, 46.2, 46.9, 54.3, 55.5, 57.8, and 74.5°; PDF No. 78-1793), Bi₂S₃ (2θ = 22.4, 24.9, 28.6, 31.8, 32.9, 33.9, 45.5, and 46.4°; PDF No. 17-0320) particles loaded on the material before adsorption and the generation of BiI₃ (2θ = 12.8, 14.3, 25.7, 27.0, 35.3, 39.2, 41.5, 43.6, 46.1, 50.4, 53.0, 55.6, 58.4, 67.2, 69.5, 71.8, and 72.9°; PDF No. 74-0457) and BiOI (2θ = 29.7, 31.7, 37.0, 39.4, 43.8, 45.4, 51.6, and 55.2°; PDF No. 73-2062) after adsorption. XPS spectra analysis is used to investigate the change in the valence states of bismuth. Due to measurement errors and manual calibration, the peak positions in different reports may be slightly different. The binding energy of Bi⁰ 4f was about 157.2 and 162.6 eV (Xian et al., 2022b). The binding energy of Bi(Ⅲ) 4f is affected by its chemical environment. The duals peaks of Bi@Si-BEA and I-Bi@Si-BEA (Tian et al., 2022) at 159.0, 164.6 eV and 158.9, 164.3 eV were attributed to Bi₂O₃ and BiI₃, while another work deconvolved the characteristic peaks into four peaks (Tesfay Reda et al., 2022). The duals peaks of Bi₂S₃@ZIF-8 (Chen et al., 2022) at 158.5 and 163.8 eV were attributed to Bi₂S₃. Compared to BiI₃, the electronegativity of oxygen in BiOI was slightly higher than iodine, resulting in a slight increase in the binding energy of Bi 4f (Tian et al., 2021a). The analysis of I 3d peaks also varied in different works. For example, Qin et al. (2022) assigned the peaks at 618.8, 630.3, 619.6, and 631.1 eV to I⁻, I₃⁻, I₂, and I₅⁻, respectively. The dual peaks in Bi₂O₃@g-CNN-PILC were deconvoluted into four peaks at 618.87, 620.57, 630.37, and 631.8 eV which were attributed to I₃⁻ and I₅⁻. Tian et al. (2022) assumed that the two peaks at 619.3 eV and 630.8 eV could be attributed to I⁻. The variation in I 3d peaks may be caused by the adsorption form of iodine in different carriers.

In several reports, the distinct lattice stripes could be observed in the high-resolution transmission electron microscopy (HRTEM) images. The lattice spacing of 0.328, 0.320, 0.31, 0.330, 0.30, and 0.256 nm corresponded to the planes of Bi⁰(Xian et al., 2022a; Xian et al., 2022b; Tian et al., 2022), Bi₂O₃(Tesfay Reda et al., 2022), Bi₂S₃(Jiang et al., 2022), BiI₃(Xian et al., 2022a; Tian et al., 2022), BiOI (Qin et al., 2022), and I₂(Xian et al., 2022a), respectively. Besides, Fourier transform infrared spectroscopy (FT-IR), Raman spectroscopy, and nuclear magnetic resonance (NMR) were also applied in the analysis of iodine adsorption by bismuth-based materials.

2.2 Bismuth-based Materials

2.2.1 Zeolites or molecular sieves

Zeolites are the microporous aluminosilicate solids, which are the most typical molecular sieves. Their covalent network structures are formed by linking the corner oxygen atoms of AlO₄ and SiO₄ tetrahedra. Due to their regular pore structures, acid resistance, high hydrothermal stability, and cation exchange capacities, zeolites are effective materials for adsorbing elemental iodine and its compounds. Several Ag-exchanged zeolites with different structures have been studied for this application, including mordenite (MOR) (Choi et al., 2001; Verger et al., 2001; Choi et al., 2003; Inagaki et al., 2008; Chapman et al., 2010; Zhao et al., 2011; Aspromonte et al., 2013; Soelberg et al., 2013; Nenoff et al., 2014; Bruffey et al., 2016; Chibani et al., 2016; Riley et al., 2016; Zakirova et al., 2017), NaX zeolite (Cheng et al., 2015), NaY zeolite, ZSM-5, ZSM-11 (Chebbi et al., 2017a; Chebbi et al., 2017b), ferrierite and β zeolite.

Compared with silver-exchanged zeolite, bismuth-exchanged zeolite has rarely been applied in the adsorption of vapor iodine. Al-Mamoori et al. (2020) developed bismuth-doped mordenite (Bi₅@Mordenite). After being exposed to iodine at 200°C for 6 h, its iodine adsorption capacity could reach a maximum of 538 mg I₂ per gram adsorbent (hereinafter referred to as mg/g), which doubled the iodine adsorption capacity of the raw zeolite (214 mg/g) and Ag@Mordenite (275 mg/g). The SEM and XPS results showed that the surface area and pore volume of zeolite increased due to the dealumination of zeolite in the process of loading bismuth in nitric acid. It is indicated that Bi-exchanged mordenite could be an alternative to Ag-exchanged mordenite for the capture of iodine.

In industrial processes, the humidity of radioactive iodine off-gas is relatively high which could diminish the iodine capture ability of most zeolites. Tian et al. (2022) introduced the all-silica beta zeolite to improve the hydrophobic properties. A bismuth-modified all-silica beta zeolite (Bi@Si-BEA) (Figures 2A, B) was synthesized through a wetness impregnation process followed by ultrasonication and H₂ reduction. The total iodine adsorption capacity can reach 650 mg/g at approximately 120°C. The synthesis process was scaled up for possible industrial applications. However, the mechanisms of effects from water vapor or other substances in off-gas require more investigation. Hydrophobic modification of the zeolite is another way to reduce the negative effect of water vapor. Recently, Jiang et al. (2022) developed a hydrophobic zeolite (NaY-NH₄F-Bi₂S₃) containing Bi₂S₃ by NH₄F solution etching and a hydrothermal method (Figures 2C, D). The maximum adsorption capacity of NaY-NH₄F-Bi₂S₃ (30 wt%) at equilibrium is 491 mg/g. The adsorption capacity and equilibration time of the zeolite (50 wt%) both decreased after granulation.

FIGURE 2

FIGURE 2. (A) Preparation of Bi@Si-BEA; (B) SEM image of Bi@Si-BEA (Tian et al., 2022); (C) Preparation of NaY-NH₄F-Bi₂S₃; (D) Mapping image of NaY-NH₄F-Bi₂S₃(30%) (Jiang et al., 2022).

Bismuth-modified SBA-15 is one of the relatively well-studied molecular sieves. Yang et al. (2015) first applied bismuth-doped mesoporous silica (SBA-15) in the field of iodine adsorption and long-term storage. Bismuth was incorporated into the SBA-15 material by previously modifying the silica surface with thiol groups and subsequent thermal treatment that led to the formation of a Bi₂S₃ phase. The as-synthesized sorbents could effectively capture iodine gas with the maximal loading capacity of 540 mg/g, which was attributed to the strong reaction tendency of bismuth sulfide with iodine gas, as well as elevated specific surface area and porosity of SBA-15. Furthermore, a chemically durable iodine-loaded material was made with a facile post-sorption process, during which the iodine-incorporated phase was effectively changed from BiI₃ to chemically durable Bi₅O₇I.

Furthermore, the bismuth-embedded SBA-15 is examined as a vapor iodine filtration material at a higher temperature up to 250°C (Kang et al., 2020). These Bi-based SBA-15 materials with high iodine capacities are a promising alternative for radioiodine storage, principally thanks to their high thermal stability. The authors also tried to reduce costs and scale up synthesis by optimizing the element ratio of raw materials and reaction conditions. However, the high price and the cumbersome preparation steps have limited this effort and the material’s further use.

Recently, Xian et al. (2022a) improved the impregnation reduction method to facilely fabricate Bi⁰-SBA-15, with Bi (NO₃)₃∙5H₂O as bismuth source and SnCl₂∙2H₂O as reductant (Figure 3). The reaction is represented by the following equation. The bismuth was loaded on the surface of SBA-15 in the form of flocculent and spherical nanoparticles, which provides abundant active sites. The capture capacity was up to 925 mg/g at 200°C within 60 min (Figure 3B). They also scaled up the synthesis with the same route to get a Bi⁰-SiO₂ which had a capture capacity of 1019 mg/g at 200°C (Xian et al., 2022b). Compared with SBA-15, commercial SiO₂ is affordable, easy to be scaled up, and time-saving but has a smaller specific surface area. The adsorption capacity after granulation needs to be further investigated.

$3\mathrm{S}\mathrm{n}{\mathrm{C}\mathrm{l}}_2+2\mathrm{B}\mathrm{i}{\left({\mathrm{N}\mathrm{O}}_3\right)}_3+18\mathrm{N}\mathrm{a}\mathrm{O}\mathrm{H}=2{\mathrm{B}\mathrm{i}}^0\left(\mathrm{s}\right)+6\mathrm{N}\mathrm{a}\mathrm{C}\mathrm{l}+6\mathrm{N}\mathrm{a}\mathrm{N}{\mathrm{O}}_3+3{\mathrm{N}\mathrm{a}}_2\mathrm{S}\mathrm{n}{\mathrm{O}}_3+9{\mathrm{H}}_2\mathrm{O}(\mathrm{l})$

FIGURE 3

FIGURE 3. (A) Preparation and Iodine Adsorption of Bi⁰-SBA-15; (B) Capture Capacity of Iodine at 200°C; (C) SEM image of 0.5Bi⁰-SBA-15 (Xian et al., 2022a).

Ding et al. (2023) prepared Bi⁰ modified SiO₂ with different morphologies (Bi⁰@SiO₂-P/R/S) by a similar method with the different proportion of raw materials. The maximum capture capacity was 960 mg/g for Bi⁰@SiO₂-P, and the minimum was 770 mg/g for Bi⁰@SiO₂-S, as the temperature increased from 75°C to 200°C where the morphologies had changed. They found that more ordered, straight-connected, and open pores are conducive to physical adsorption, while disordered structures are more thermally stable.

Chang et al. (2022a), Chang et al. (2022b) also prepared three-dimensional ordered macropores silica (3DOM-SiO₂) aerogels with tetraethyl orthosilicate (TEOS), the main raw materials of SBA-15, by the solvent template method, and doped Bi in the materials on this basis. The macropores (about 125 nm) in 3DOM effectively reduce gas diffusion resistance, and the micropores still work as the adsorption pores. The iodine capture capacity was about 696 mg/g at 200°C. The effects of calcination rate and calcination temperature on the structure of materials were also investigated. The lower calcination rate is conducive to the formation of micropores. The higher calcination temperature is not only conducive to the removal of water but also leads to the reduction of micropores due to the crystallization of silica.

2.2.2 Carbon materials

In 2020, Chee et al. (2020) developed a bismuth-decorated electrospinning carbon nanofiber to capture radioactive iodine. At 200°C, the capture capacity of Bi@ESCNF for iodine gas could reach 559 mg/g, thanks to the chemical reaction between Bi and iodine to generate stable BiI₃. Bi@ESCNF is a macroscopic membrane morphology more suitable for nuclear industry adsorption than another powdered adsorbent. By adding a hydrothermal step based on electrospinning, pre-oxidation, and carbonization process, Tian et al. (2021a) developed three new electrospinning carbon nanofibers (HT-Bi₂O₃-ESCNF, HT-Bi-Bi₂O₃-ESCNF, and HT-Bi-ESCNF). Under 200°C, they reached adsorption capacities of 364 mg/g, 461 mg/g, and 732 mg/g, respectively. SEM and TEM results showed that most Bi and Bi₂O₃ nanoparticles were uniformly and densely anchored on the surface of carbon fibers compared with Bi@ESCNF. Combining PXRD, SEM, TEM, BET, XPS, Raman spectra, and TGA characterizations indicated a small number of polyiodide anions formed by charge transfer between carbon fibers. Iodine molecules were firmly trapped on the carbon fibers, except for the BiI₃ and BiOI which were generated by the chemical reaction between Bi/Bi₂O₃ and I₂.

In another research, Zou et al. (2021) reported a composite with high iodine capture capacity. The Bi₂S₃ reduced graphene oxide (RGO) was produced via a solvothermal method which was shown in Figure 4. The adsorption capacities of iodine could reach 1042.8 mg/g at 200 °C for 2 h under a static air atmosphere. Graphitic carbon nitride (g-C₃N₄) or graphitic carbon nitride nanosheets (g-CNN) can be easily obtained by modifying melamine, which is eco-friendly and cheap. Tesfay Reda et al. (2022) synthesized Bi₂O₃@g–CNN and added pillared interlayered clays (PILC) to increase stability, as shown in Figure 5. The product, Bi₂O₃@g–CNN-PILC, had an iodine capture capacity of 830 ± 44 mg/g at 100°C within 8 h. Liu et al. (2022) prepared a bismuth-based porous carbon material (Bi@MVF) by directly carbonizing ZIF-8. Bismuth particles are uniformly embedded and allotted on the porous carbon network, and the capture capacity was up to 1560 mg/g at 120°C for 4 h.

FIGURE 4

FIGURE 4. (A) and (B) Preparation, Iodine Adsorption and Immobilization of Bi₂S₃-RGO; (C) FESEM image Bi₂S₃-RGO-I (Zou et al., 2021).

FIGURE 5

FIGURE 5. (A) SEM image Bi₂O₃@g-CNN-PILC; (B) Preparation of Bi₂O₃@g-CNN-PILC (Tesfay Reda et al., 2022).

2.2.3 MOFs

In the past 20 years, various studies have been carried out on metal-organic frameworks (MOFs) owing to their extremely high specific surface areas (up to 10⁴ m² g⁻¹), high compositional flexibility, and selective gas absorption (Pei et al., 2014). The most commonly studied MOFs for the capture of iodine were the zeolitic imidazolate framework Zn(2-methylimidazolate)₂ (ZIF-8) and Cu₃(benzene-1,3,5-tricarboxylate)₂(H₂O)₃ (Cu-BTC) (Sava et al., 2011; Bennett et al., 2013; Hughes et al., 2013; Yuan et al., 2016; Sava Gallis et al., 2017; Chebbi et al., 2018).

Chen et al. (2022) modified Ding’s preparation process (Ding et al., 2018) and synthesized Bi₂S₃@ZIF-8 (BZ), as shown in Figure 6. The ZIF-8 nanocrystals grow uniformly on the surface of Bi₂S₃ nanorods, which inhibits the aggregation of Bi₂S₃ nanorods during adsorption. The maximum iodine adsorption capacity of BZ-4 reached 2637.0 mg/g. However, the adsorption equilibrium time was much longer than that of zeolite materials (6 h), and the temperature was only 76.85°C, which was lower than the temperature in the industrial process (about 140°C).

FIGURE 6

FIGURE 6. Fabrication of BZ core-shell nanocomposites (Chen et al., 2022).

Besides, some MOFs with bismuth ions directly act as connectors in the framework have been reported. They are mostly used for photocatalysis and gas adsorption. Jung et al. (2021) found that 2-mercapto-nicotinic acid (2-mna) is the best candidate for iodine capture out of several composite MOFs. Bi-mna provided strong chemisorption between bismuth and iodine, resulting in high thermal stability. Though the Bi-mna exhibited a lower adsorption capacity than ZIF-8 due to lower MOF density, it was sufficiently large (700 mg/g) for practical applications. Qin et al. (2022) investigated NOTT-220, a kind of MOF material consisting of biphenyl-3,3′,5,5′-tetracarboxylic acid and Bi³⁺ ions, as an iodine gas adsorbent. The adsorption capacities of iodine increased rapidly in 7 h and finally reached the maximum value of 955 mg/g at 75°C in 27 h.

2.2.4 Other materials

Yu Q et al. (2020) synthesized millimeter-sized spherical bismuth sulfide@polyacrylonitrile (Bi₂S₃@PAN) hybrid beads. Under 75°C, the iodine capture capacity of Bi₂S₃@PAN hybrid beads could reach 986 mg/g. Compared with most powder materials, the beads exhibit not only high iodine adsorption properties but also easy storage and manipulation.

Another report conducted by Tian et al. (2021b) developed bismuth and silver functionalized Ni foam composites (Bi-Ni foam and Ag-Ni foam). As illustrated in Figure 7A, Bi-Ni foam shows a higher iodine capture capacity (658 mg/g) but slower adsorption kinetics than Ag-Ni foam (456 mg/g). Due to the more active sites (Bi⁰ or Ag⁰ particles) and the external structure of the Ni foam skeleton, the physically adsorbed iodine is much less than the chemically adsorbed iodine (96% iodine captured in the term of stable form in the I-Bi-Ni foam). Besides, thanks to the nickel skeleton, the material has the advantages of convenient shaping and manipulation.

FIGURE 7

FIGURE 7. (A) Preparation and Iodine Adsorption of Bi-Ni and Ag-Ni foams; (B) SEM image of I-Bi-Ni foam (Tian et al., 2021b); (C) Preparation and Iodine Adsorption of Bi@AlCu-PILC; (D) SEM image of Bi@AlCu-PILC-I (Tesfay Reda et al., 2021b).

Zou et al. (2019) developed Bi-Bi₂O₃-TiO₂-C, which was prepared by a sol-gel method for capturing vapor iodine. Bi-Bi₂O₃-TiO₂-C exhibited an iodine adsorption capacity of up to 504 mg/g, which was almost two-fold higher than that of AgX. The authors proposed that majority of iodine was chemically captured in the form of BiI₃ while a small amount was also physically captured as I₂. In addition, TiO₂ contributes to an important portion of the captured iodine.

A bismuth-modified zinc aluminum layered double hydroxide (BiZnAl-LDH) was synthesized via co-precipitation by Dinh et al. (2020). The adsorption capacity for iodine reached 433 mg/g. The TGA curves showed that the removal of dehydroxylated hydrotalcite caused another mass loss between the removal of the physically and chemically adsorbed iodine, which is different from other materials.

By impregnating AlCu-oxides pillared Montmorillonite (MMN) with bismuth, Tesfay Reda et al. (2021b) produced Bi-based mesoporous material (Bi@AlCu-PILC), as shown in Figure 7B. AlCu-oxides formed pillars in the gallery of montmorillonite by ion exchange. After calcination, the bismuth was loaded onto these pillars. This single-phase material had high capture capacity (485 ± 54 mg/g under 75°C) and thermal stability.

Several authors have studied chalcogen aerogel containing bismuth as potential adsorbents for iodine, technetium, and uranium trapping. Riley et al. (2013) developed structured aerogels, Co_0.7Bi_0.3MoS₄ (CoBiMoS), which could remove more than 99.0% vapor iodine over the test duration. The adsorption mechanism has also been reported. Chalcogens enclosed in chalcogels are classified as weak Lewis bases according to the hard and soft acids and bases (HSAB) concept (Riley et al., 2011). Consequently, the chalcogens have a high affinity for iodine (I₂), which is known as a weak Lewis acid. The removal efficiency was governed by the affinity of I₂(g) and S other than the surface area of chalcogels. This aerogel has the potential for radionuclides removal from solution and gas. However, sulfur compounds could be formed considering the sulfur is part of the material, which will produce secondary pollution. The thermal stability of stored iodine over 150°C has not been examined in this study. However, chalcogels with other adsorbents (Zn₂Sn₂S₆ and Sb₄Sn₃S₁₂) (Subrahmanyam et al., 2015) have a quite low thermal stability of iodine capture (or the formed iodides). TGA results showed that beyond that temperature, iodine was released progressively.

2.3 Summary

The capture capacity of the materials mentioned above is summarized in Table 1. The performance of most materials are better than that of bare adsorbents or Ag-modified adsorbents, which is partly due to the reaction mechanism between bismuth and iodine. However, due to the different thermal stability of raw materials and other reasons, the optimal capture temperature varied widely. At the same time, the volume of the containers used in the static adsorption experiments and the mass of solid iodine added were also different. There are still few studies in this topic, making it difficult to compare the actual properties of different materials objectively. The density of different materials is also dissimilar, resulting in large differences in volume which is important in practical adsorption devices.

TABLE 1

TABLE 1. Bi-based materials for vapor iodine capture.

In practical industrial processes, the inevitably generated CH₃I must be removed because of its high toxicity and radioactivity. Compared to silver-based materials, the ability of Bi-based materials to adsorb CH₃I needs to be further investigated. Besides, many materials’ considerable capture capacities are owing to the large number of active sites on the materials’ surface. It is necessary to study how to test the performance in dynamic adsorption experiments while keeping the performance after granulation.

3 Materials stability and immobilization

3.1 Materials stability after adsorption

The stability of the materials after adsorption is mainly divided into chemical durability and thermal stability.

Physically adsorbed iodine will desorb over time, especially if the iodine-containing waste is exposed to hot air or solution. A higher ratio of physical adsorption capacity corresponds to the poor chemical durability of waste. Al-Mamoori et al. (2020) evaluated the chemical durability of Bi₅@Mordenite after adsorption. 30 mg of Bi₅@Mordenite-I was inserted in 3 ml of deionized water, and 36% of the iodine was released from Bi₅@Mordenite-I after 24 h of contact. The results demonstrated that Bi₅@Mordenite is unsuitable for storing radioactive iodine because of its low stability.

In the TGA of Bi-based materials and immobilization tests, BiOI and Bi₇O₅I showed better thermal stability. In most experiments, the BiI₃ decomposed in the range of 200°C–500°C with the reducing of iodine to bismuth ratio, which led to the escape of iodine. The mechanisms can be demonstrated by the following equations (Yang et al., 2016; Zou et al., 2019; Zou et al., 2021). To safely immobilize iodine, additional bismuth must be mixed with the waste of adsorption materials.

$2{\mathrm{B}\mathrm{i}\mathrm{I}}_3+{\mathrm{O}}_2=2\mathrm{B}\mathrm{i}\mathrm{O}\mathrm{I}+2{\mathrm{I}}_2$

$\frac{1}{3}\mathrm{B}\mathrm{i}{\mathrm{I}}_3+\frac{7}{3}{\mathrm{B}\mathrm{i}}_2{\mathrm{O}}_3={\mathrm{B}\mathrm{i}}_5{\mathrm{O}}_7\mathrm{I}$

$\mathrm{B}\mathrm{i}{\mathrm{I}}_3+0.5{\mathrm{O}}_2=\mathrm{B}\mathrm{i}\mathrm{O}\mathrm{I}+{\mathrm{I}}_2$

$5\mathrm{B}\mathrm{i}\mathrm{O}\mathrm{I}+{\mathrm{O}}_2={\mathrm{B}\mathrm{i}}_5{\mathrm{O}}_7\mathrm{I}+2{\mathrm{I}}_2$

$\frac{5}{2}{\mathrm{B}\mathrm{i}}_2{\mathrm{O}}_3+\frac{1}{2}{\mathrm{I}}_2={\mathrm{B}\mathrm{i}}_5{\mathrm{O}}_7\mathrm{I}+\frac{1}{4}{\mathrm{O}}_2$

The thermal stability of the waste includes that of bismuth-iodine compounds (Bi_xO_yI) and supports. Comparing TGA and adsorption results of different materials, under approximately 200°C, BiI₃ and BiOI are not easily oxidized. The slight weight loss is attributed to the loss of free water and physically adsorbed iodine. Such as Bi₂S₃-RGO-I, only 1.5% of weight was lost (the physically adsorbed water and iodine) till 200°C, and the left 83.5% weight was lost from 200°C to 450°C (the chemically adsorbed iodine). The TG-DSC results of Bi-Bi₂O₃-TiO₂-C showed a vast weight loss of 47.97% when heated from 200°C to 300°C, which suggested that the stability of the material was relatively low. The TGA curves showed that after iodine capture, Bi₂O₃@g–CNN-PILC (Tesfay Reda et al., 2022) only lost 18.7% of the total weight when heated up to 800°C, which exhibited excellent thermal stability.

3.2 Immobilization

For the above reasons, additional bismuth materials are necessary to prevent iodine overflow during immobilization. A study led by Yang et al. (2016) aimed to stabilize iodine confined in Bi-embedded SBA-15. The iodine-containing waste was mixed with low-temperature sintering glasses and Bi₂O₃, which were used as binders and stabilizing additives, respectively. A quite satisfactory leaching rate of iodine was measured by a PCT test ranging from 10⁻³ to 10⁻² g/m² day, which suggested that the glass composite waste form of bismuth embedded SBA-15 could be a potential candidate material for the stable storage of ¹²⁹I. However, the leaching experiment was not performed over an extended duration, and further investigation of stability over a longer period is necessary for better insight. Bi@AlCu-PILC (Tesfay Reda et al., 2021b) was transformed into a more stable form (Bi₅O₇I) by post-sorption treatment with Bi₂O₃ at 500°C, which had the potential to serve as a long-term disposable iodine waste form.

Some other studies have explored the use of bismuth-containing glass powder for solidification and sintering after adsorption. In these studies, bismuth was added in the immobilization and sintering process to prevent iodine’s escape, while majority of the adsorbents were silver-based materials. Chabauty et al. (2019) synthesized a materials of bismuth-silver phosphate glasses (AgPO₃-Bi), in which 12 wt% of iodine was chemically immobilized. Combining ³¹P MAS NMR, Raman spectroscopy, and X-ray absorption spectroscopy, it was found that the decomposition of Bi₂O₃ resulted in the formation of new bonds in the glass mixture with additional bismuth. Garino et al. (2011) mixed low-temperature sintering bismuth-silicon-zinc-oxide glass powder with AgI or AgI-Mordenite to create the artificial iodine waste form. According to the TGA results, the AgI-Bi-Si-Zn-oxide glass showed no weight loss when heated to 550°C at 10°C/min, while the mass loss of AgI-Mordenite was 18.2% when heated at 20°C/min to 600°C. In studies by Wei et al. (2020), He et al. (2022) and other researchers (Liu et al., 2021; Wei et al., 2021; Wu et al., 2021; Yan et al., 2021; Wu et al., 2022), B₂O₃-Bi₂O₃-ZnO composites were used for immobilization of iodine waste in the form of AgI with low sintering temperature. Yang et al. (2021); Yang et al. (2022) prepared a Bi-based silica ceramic composite (Si-Cs₃Bi₂I₉ perovskite) for iodine immobilization. Compared to other materials, this material had a high bismuth to iodine ratio but low stability. There was a significant loss of iodine and bismuth in the leaching experiment at room temperature or 90°C after 14 days.

4 Aqueous iodine capture

4.1 Capture mechanism and solubility

The adsorption mechanisms for aqueous iodide and iodate can be represented by the following equations (Liu et al., 2014; Xiong et al., 2017). According to thermodynamics, bismuth materials’ capture capacity is less affected by the other coexisting anions due to the existence of Bi-O-I and Bi-O-(IO₃) bonding.

${\mathrm{B}\mathrm{i}}_2{\mathrm{O}}_3+{\mathrm{H}}_2\mathrm{O}+2{\mathrm{I}}^{-}=2\mathrm{B}\mathrm{i}\mathrm{O}\mathrm{I}+2{\mathrm{O}\mathrm{H}}^{-}$

$2{\mathrm{B}\mathrm{i}}_2{\mathrm{O}}_3+2{\mathrm{I}}^{-}+{\mathrm{H}}_2\mathrm{O}={\mathrm{B}\mathrm{i}}_4{\mathrm{O}}_5{\mathrm{I}}_2+2{\mathrm{O}\mathrm{H}}^{-}$

${\mathrm{B}\mathrm{i}}_6{\mathrm{O}}_7+6{\mathrm{I}\mathrm{O}}_3^{-}+3{\mathrm{H}}_2\mathrm{O}+{\mathrm{O}}_2\to 6\mathrm{B}\mathrm{i}\mathrm{O}\left({\mathrm{I}\mathrm{O}}_3\right)+6{\mathrm{O}\mathrm{H}}^{-}$

Different from the capture of vapor iodine, the formation of Bi_xO_yI_z depends on the bismuth to iodine ratio in the solution. By leaching experiments, Krumhansl and Nenoff (2011) showed that the stability of Bi₅O₇I was better than BiOI as the bismuth to iodine ratio increased. Similar to the immobilization results, Bi₅O₇I is more stable than other Bi_xO_yI_z compounds at a higher temperature (Kodama, 1992). However, at a lower temperature, some other stable iodine waste form of BiOI (Krumhansl and Nenoff, 2011; Ng and Fan, 2016; Han et al., 2019; Wang et al., 2020; Yang et al., 2021) and Bi₄O₅I₂ (Liu et al., 2014; Liu et al., 2016; Xiong et al., 2017; Xiong et al., 2018; Zhao et al., 2021) were reported.

4.2 Removal of radioactive iodine in synthetic groundwater

Synthetic groundwater (SGW) refers to the groundwater at the Hanford Site (WA, United States), where multiple radionuclides and other hazardous contaminants are detected. Pearce et al. (2020), Lawter et al. (2021), and Cordova et al. (2020) tested different forms of bismuth (oxy)hydroxide and bismuth subnitrate to absorb iodine (mainly IO₃⁻) in SGW, and the results were concluded in Table 2. Except for BIN-S (silica substrate unwashed), other materials adsorbed substantially all of the iodine in the aqueous solution, which showed excellent application prospects.

TABLE 2

TABLE 2. Batch experiments of some Bi-based materials in synthetic groundwater.

4.3 Materials

A nitrate-containing bismuth compound, Bi₅(NO₃)O₇, was discussed for removing and solidifying aqueous iodine among other halogenide ions from solution. The NO₃⁻ ion was significant for the removal for its effective exchange with iodide ion. When 244 mg of Bi₅(NO₃)O₇ reacted with 0.1 mol/dm³ of iodide at 50°C and 75°C, over 99.99% of iodine ion was removed (Kodama, 1994). However, the reaction rate was very slow at 25°C, and the influence of pH, temperature, and solution to solid ratio has not yet been studied. These preliminary results only provided a starting point for further researches.

Another nitrate incorporated bismuth oxide, BiPbO₂NO₃ (BPN), was developed to remove iodide ions in a solution and fix them in the solidified material BiPbO₂I (BPI) by the ion exchange reaction (Amaya et al., 2000). An anion exchange capacity of 1.0 mEq/g and a distribution coefficient of larger than 0.1 m³/kg were obtained in solution at pH between 9 and 13. Takayuki (Soelberg et al., 2013) studied the leach resistance of BPI, in which the incorporation of lead helped to form strong interaction. It was concluded that BPI would be much more stable than AgI when interchanged with anions so that BPI waste can be stored for a long term without detaching the iodine. Nevertheless, same as Bi₅(NO₃)O₇, the loading capacity was low as the adsorption depends on the amounts of nitrates in the compound. Basic bismuth nitrate (BBN) crystals for iodide capture were prepared by Ng and Fan (2016). The shape of BBN could be controlled through modulation of the effect of the shape-directing agent 2,3-bis(2-pyridyl)pyrazine, and showed influence on the reaction rates. The reaction rates of the Reuleaux triangledisks were faster than the other two shapes

Lee and Takahashi (2020), Pearce et al. (2020) prepared bismuth-impregnated layered mixed metal oxide (MMO) and bismuth-loaded layered double hydroxide (BiCoAl-LDH). Except for adsorption tests and characterization, the Langmuir and pseudo-second-order kinetic models were fitted to the adsorption isotherms and the adsorption kinetics, respectively. Further investigation should focus on their thermal and chemical stability for application in an industrial environment with high temperature and acidic condition.

Fiber materials are widely used in the field of adsorption thanks to their excellent surface area, porous nature, and the presence of the functional group. By varieties of modifications, these materials have improved the selectivity to increase the capture capacity of iodine. Several polyacrylonitrile were modified with bismuth oxyhydroxide (PAN-BIN) (Cordova et al., 2020), cellulose-based hybrid material (FL-δ-Bi₂O₃) (Xiong et al., 2017), and nano-cellulose hydrogel coated titanate-bismuth oxide membrane (CH-TBM) (Hrizi et al., 2011). The XRD analysis and Raman spectrum suggested the main product generated by chemical adsorption is Bi₄O₅I₂, which was different from other materials.

With low solubility in water, Bi₂O₃ could capture iodine by reacting with I⁻ to form insoluble compounds, such as BiOI, Bi₅O₇I, and Bi₇I₃O₉ (Klimakov et al., 1974; Krämer, 1979; Kodama, 1992). Wang et al. (2020) activated Bi₂O₃ by milling to create more oxygen vacancy and found the adsorption capacity was extremely affected by pH and temperature. Other researchers prepared flowerlike nanostructured bismuth oxide (Liu et al., 2016) and fabricated microrosette-like-δ-Bi₂O₃ (Liu et al., 2014). The removal capacity was higher than untreated Bi₂O₃, indicating the effectiveness of structural modification. In order to achieve a high specific surface area and reduced crystalline size, Zhang and Jaroniec (2017) developed mesoporous δ-Bi₂O₃ with the templates of SBA-15. The removal capacity of mesoporous δ-Bi₂O₃ doubled the same compound in another study (Zhang et al., 2006) due to the nurtured porosity of the material. The Bi₂O₃ without other components showed better stability in acidic conditions than inorganic materials and fiber materials.

Han et al. (2019) developed graphene oxide modified-bismuth (Bi-GO) for iodide and iodate removal in solution and compared it with Ag-Z. The adsorption capacity for IO₃⁻ and I⁻ reached about 200-230 mg/g with more than 90% of iodate and iodide captured. Xu et al. (2019) modified the Iron-metal-organic framework (Fe-MOF) with bismuth, and the maximum capture capacities of Bi@MIL reached 96.7 mg/g.

Most Bi-based materials for capturing aqueous iodine in batch experiments had been listed by Tesfay Reda and Muhire (Tesfay Reda et al., 2021a; Muhire et al., 2022), so only the materials from the past 2 years were concluded in Table 3. Zhao developed a kind of polymer composite beads embedded by flower-like δ-Bi₂O₃ (δ-Bi₂O₃@PES), and the adsorption capacities for I⁻ and IO₃⁻ could reach 95.4 mg/g and 170.6 mg/g, respectively. In other experiments, I₂ is dissolved in organic solvents, and the adsorption capacity of different materials is between 180.23 mg/g to 532.9 mg/g. In the groundwater, iodine elements are comprised of 45%–84% iodate (with 15%–40% organo-iodine and <4% iodide) (Zhang et al., 2013), which requires further exploration of the above results in practical significance.

TABLE 3

TABLE 3. Recent Bi-based materials for iodine capture in solution.

5 Conclusion

With advantages of safety, green emission, and high economic efficiency, nuclear energy is one of the main energy sources in the world. The radioactive iodine and its compounds from serious nuclear accidents and the reprocessing of spent nuclear fuels demand efficient capture and safe storage. Compared with other mature adsorbents (such as activated carbon and Ag-based materials), Bi-based materials with lower toxicity, lower cost, and almost no radioactivity have attracted the researchers’ attention recently. These materials were applied in the capture of both aqueous iodine and vapor iodine.

The capture capacities of many Bi-based materials were higher than commercial adsorbents. Most Bi-based modified absorbents combined the advantages of high specific surface area and abundant active sites. It demonstrates that developing Bi-based modified materials based on existing supports is feasible. By characterization, leaching experiments, and immobilization experiments, it is indicated that Bi, Bi₂O_3, and Bi₂S₃ can react with iodine to generate Bi_xO_yI_z. At higher temperature, the stability of Bi₅O₇I is superior to BiOI and BiI₃, which means that chemisorbed iodine can be released and additional bismuth is needed for immobilization. Although the types of Bi-based materials are rich, there is a lack of systematic research and comparison. Besides, the research about the capture of Bi-based materials for CH₃I, one of the radioactive iodine components, needs to be further investigated. For already developed adsorbents, granulation and dynamic adsorption experiments are also of consequence.

Author contributions

CL and CX conceived the idea of the study, outlined the structure of this paper, and revised the manuscript draft. YH and ZT reviewed the literature and drafted the original manuscript. All authors approved the final version of the manuscript to be published.

Funding

This research is financially supported by the National Natural Science Foundation of China (Nos. 22176017 and U2067213).

Conflict of interest

The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.

Publisher’s note

All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article, or claim that may be made by its manufacturer, is not guaranteed or endorsed by the publisher.

References

Abney, C. W., Nan, Y., and Tavlarides, L. L. (2017). X-ray absorption spectroscopy investigation of iodine capture by silver-exchanged mordenite. Ind. Eng. Chem. Res. 56 (16), 4837–4846. doi:10.1021/acs.iecr.7b00233

CrossRef Full Text | Google Scholar

Al-Mamoori, A., Alsalbokh, M., Lawson, S., Rownaghi, A. A., and Rezaei, F. (2020). Development of bismuth-mordenite adsorbents for iodine capture from off-gas streams. Chem. Eng. J. 391, 123583. doi:10.1016/j.cej.2019.123583

CrossRef Full Text | Google Scholar

Alsalbokh, M., Fakeri, N., Rownaghi, A. A., Ludlow, D., and Rezaei, F. (2021). Aminosilane-grafted bismuth-alumina adsorbents: Role of amine loading and bismuth content in iodine immobilization from aqueous solutions. Chem. Eng. J. 409, 128277. doi:10.1016/j.cej.2020.128277

CrossRef Full Text | Google Scholar

Amaya, T., Mukunoki, A., Shibuya, M., and Kodama, H. (2000). Study of BiPbO₂NO₃ for I-129 fixation under reducing conditions. MRS Online Proc. Libr. 663, 43. doi:10.1557/PROC-663-43

CrossRef Full Text | Google Scholar

Ampelogova, N. I., Kritskii, V. G., Krupennikova, N. I., and Skvortsov, A. I. (2002). Carbon-fiber adsorbent materials for removing radioactive iodine from gases. At. Energy 92 (4), 336–340. doi:10.1023/a:1016558127710

CrossRef Full Text | Google Scholar

Aspromonte, S. G., Mizrahi, M. D., Schneeberger, F. A., López, J. M. R., and Boix, A. V. (2013). Study of the nature and location of silver in Ag-exchanged mordenite catalysts. Characterization by spectroscopic techniques. J. Phys. Chem. C 117 (48), 25433–25442. doi:10.1021/jp4046269

CrossRef Full Text | Google Scholar

Bennett, T. D., Saines, P. J., Keen, D. A., Tan, J.-C., and Cheetham, A. K. (2013). Ball-milling-induced amorphization of zeolitic imidazolate frameworks (ZIFs) for the irreversible trapping of iodine. Chem.-Eur. J. 19 (22), 7049–7055. doi:10.1002/chem.201300216

PubMed Abstract | CrossRef Full Text | Google Scholar

Bruffey, S. H., Jubin, R. T., and Jordan, J. A. (2016). Capture of elemental and organic iodine from dilute gas streams by silver-exchanged mordenite. Procedia Chem. 21, 293–299. doi:10.1016/j.proche.2016.10.041

CrossRef Full Text | Google Scholar

Chabauty, A. L., Campayo, L., Méar, F. O., and Montagne, L. (2019). Niobium- and bismuth-silver phosphate glasses for the conditioning of radioactive iodine. J. Non-Cryst. Solids 510, 51–61. doi:10.1016/j.jnoncrysol.2019.01.015

CrossRef Full Text | Google Scholar

Chang, S., Wang, K., Gao, L., Liu, J., Wang, L., Li, Y., et al. (2022a). Highly efficient adsorption of radioiodine by a three-dimensional ordered macroporous bismuth-silica composite aerogel. Chem. Eng. Sci. 260, 117856. doi:10.1016/j.ces.2022.117856

CrossRef Full Text | Google Scholar

Chang, S., Wang, K., Wang, L., Song, X., Liu, J., Chen, J., et al. (2022b). Effects of calcination rate and temperature on microstructure and gaseous iodine capture capacity of 3DOM-SiO₂ aerogels. Prog. Nucl. Energy 151, 104328. doi:10.1016/j.pnucene.2022.104328

CrossRef Full Text | Google Scholar

Chapman, K. W., Chupas, P. J., and Nenoff, T. M. (2010). Radioactive iodine capture in silver-containing mordenites through nanoscale silver iodide formation. J. Am. Chem. Soc. 132 (26), 8897–8899. doi:10.1021/ja103110y

PubMed Abstract | CrossRef Full Text | Google Scholar

Chebbi, M., Azambre, B., Cantrel, L., Huvé, M., and Albiol, T. (2017a). Influence of structural, textural and chemical parameters of silver zeolites on the retention of methyl iodide. Microporous Mesoporous Mat. 244, 137–150. doi:10.1016/j.micromeso.2017.02.056

CrossRef Full Text | Google Scholar

Chebbi, M., Azambre, B., Volkringer, C., and Loiseau, T. (2018). Dynamic sorption properties of metal-organic frameworks for the capture of methyl iodide. Microporous Mesoporous Mat. 259, 244–254. doi:10.1016/j.micromeso.2017.10.018

CrossRef Full Text | Google Scholar

Chebbi, M., Chibani, S., Paul, J.-F., Cantrel, L., and Badawi, M. (2017b). Evaluation of volatile iodine trapping in presence of contaminants: A periodic dft study on cation exchanged-faujasite. Microporous Mesoporous Mat. 239, 111–122. doi:10.1016/j.micromeso.2016.09.047

CrossRef Full Text | Google Scholar

Chee, T.-S., Tian, Z., Zhang, X., Lei, L., and Xiao, C. (2020). Efficient capture of radioactive iodine by a new bismuth-decorated electrospinning carbon nanofiber. J. Nucl. Mater. 542, 152526. doi:10.1016/j.jnucmat.2020.152526

CrossRef Full Text | Google Scholar

Chen, K., Wang, P., Gu, A., Djam Miensah, E., Gong, C., Mao, P., et al. (2022). Core-shell Bi₂S₃ nanorods loaded ZIF-8 nanocomposites for efficient and reversible capture of radioactive iodine. Microporous Mesoporous Mat. 339, 111983. doi:10.1016/j.micromeso.2022.111983

CrossRef Full Text | Google Scholar

Cheng, Q., Yang, W., Li, Z., Zhu, Q., Chu, T., He, D., et al. (2015). Adsorption of gaseous radioactive iodine by Ag/13X zeolite at high temperatures. J. Radioanal. Nucl. Chem. 303 (3), 1883–1889. doi:10.1007/s10967-014-3736-3

CrossRef Full Text | Google Scholar

Chibani, S., Chebbi, M., Lebègue, S., Cantrel, L., and Badawi, M. (2016). Impact of the Si/Al ratio on the selective capture of iodine compounds in silver-mordenite: A periodic DFT study. Phys. Chem. Chem. Phys. 18 (36), 25574–25581. doi:10.1039/c6cp05015h

PubMed Abstract | CrossRef Full Text | Google Scholar

Chien, C.-C., Huang, Y.-P., Wang, W.-C., Chao, J.-H., and Wei, Y.-Y. (2011). Efficiency of moso bamboo charcoal and activated carbon for adsorbing radioactive iodine. Clean-Soil Air Water 39 (2), 103–108. doi:10.1002/clen.201000012

CrossRef Full Text | Google Scholar

Choi, B.-S., Park, G.-I., Lee, J.-W., Yang, H.-Y., and Ryu, S.-K. (2003). Preparation and structural studies of organotin(IV) complexes formed with organic carboxylic acids. J. Radioanal. Nucl. Chem. 256 (1), 19–26. doi:10.1023/a:1023383505788

CrossRef Full Text | Google Scholar

Choi, B. S., Park, G. I., Kim, J. H., Lee, J. W., and Ryu, S. K. (2001). Adsorption equilibrium and dynamics of methyl iodide in a silver ion-exchanged zeolite column at high temperatures. Adsorpt.-J. Int. Adsorpt. Soc. 7 (2), 91–103. doi:10.1023/a:1011660121182

CrossRef Full Text | Google Scholar

Cordova, E. A., Garayburu-Caruso, V., Pearce, C. I., Cantrell, K. J., Morad, J. W., Gillispie, E. C., et al. (2020). Hybrid sorbents for ¹²⁹I capture from contaminated groundwater. ACS Appl. Mater. Interfaces 12 (23), 26113–26126. doi:10.1021/acsami.0c01527

PubMed Abstract | CrossRef Full Text | Google Scholar

Deitz, V. R. (1987). Interaction of radioactive iodine gaseous species with nuclear-grade activated carbons. Carbon 25 (1), 31–38. doi:10.1016/0008-6223(87)90037-6

CrossRef Full Text | Google Scholar

Deuber, H. (1986). Investigations on the retention of elemental radioiodine by activated carbons at high-temperatures. Nucl. Technol. 72 (1), 44–48. doi:10.13182/nt86-a33751

CrossRef Full Text | Google Scholar

Ding, Y.-H., Zhang, X.-L., Zhang, N., Zhang, J.-Y., Zhang, R., Liu, Y.-F., et al. (2018). A visible-light driven Bi₂S₃@ZIF-8 core–shell heterostructure and synergistic photocatalysis mechanism. Dalton Trans. 47 (3), 684–692. doi:10.1039/c7dt03256k

PubMed Abstract | CrossRef Full Text | Google Scholar

Ding, Y., Fan, W., Xian, Q., Dan, H., Zhu, L., and Duan, T. (2023). Capture of iodine gas by Bi⁰ modified silica with different morphologies: Influence of pore characteristic on the stable and unstable forms of adsorption. Chem. Eng. J. 451, 138887. doi:10.1016/j.cej.2022.138887

CrossRef Full Text | Google Scholar

Dinh, T. D., Zhang, D., and Tuan, V. N. (2020). High iodine adsorption performances under off-gas conditions by bismuth-modified ZnAl-LDH layered double hydroxide. RSC Adv. 10 (24), 14360–14367. doi:10.1039/d0ra00501k

PubMed Abstract | CrossRef Full Text | Google Scholar

Funabashi, K., Fukasawa, T., and Kikuchi, M. (1995). Investigation of silver-impregnated alumina for removal of radioactive methyl iodide. Nucl. Technol. 109 (3), 366–372. doi:10.13182/nt95-a35085

CrossRef Full Text | Google Scholar

Garino, T. J., Nenoff, T. M., Krumhansl, J. L., and Rademacher, D. X. (2011). Low-temperature sintering Bi–Si–Zn-Oxide glasses for use in either glass composite materials or core/shell ¹²⁹I waste forms. J. Am. Ceram. Soc. 94 (8), 2412–2419. doi:10.1111/j.1551-2916.2011.04542.x

CrossRef Full Text | Google Scholar

Goldsmith, J. R., Grossman, C. M., Morton, W. E., Nussbaum, R. H., Kordysh, E. A., Ouastel, M. R., et al. (1999). Juvenile hypothyroidism among two populations exposed to radioiodine. Environ. Health Perspect. 107 (4), 303–308. doi:10.1289/ehp.99107303

PubMed Abstract | CrossRef Full Text | Google Scholar

Gonzalez-Garcia, C. M., Roman, S., Gonzalez, J. F., Sabio, E., and Ledesma, B. (2013). Surface free energy analysis of adsorbents used for radioiodine adsorption. Appl. Surf. Sci. 282, 714–717. doi:10.1016/j.apsusc.2013.06.040

CrossRef Full Text | Google Scholar

Grossman, C. M., Morton, W. E., and Nussbaum, R. H. (1996). Hypothyroidism and spontaneous abortions among Hanford, Washington, downwinders. Arch. Environ. Health 51 (3), 175–176. doi:10.1080/00039896.1996.9936012

PubMed Abstract | CrossRef Full Text | Google Scholar

Grossman, C. M., Nussbaum, R. H., and Nussbaum, F. D. (2003). Cancers among residents downwind of the Hanford, Washington, plutonium production site. Arch. Environ. Health 58 (5), 267–274. doi:10.3200/aeoh.58.5.267-274

PubMed Abstract | CrossRef Full Text | Google Scholar

Grossman, C. M., Nussbaum, R. H., and Nussbaum, F. D. (2002). Thyrotoxicosis among Hanford, Washington, downwinders: A community-based health survey. Arch. Environ. Health 57 (1), 9–15. doi:10.1080/00039890209602911

PubMed Abstract | CrossRef Full Text | Google Scholar

Han, S., Um, W., and Kim, W.-S. (2019). Development of bismuth-functionalized graphene oxide to remove radioactive iodine. Dalton Trans. 48 (2), 478–485. doi:10.1039/c8dt03745k

PubMed Abstract | CrossRef Full Text | Google Scholar

He, X., Cheng, W., Yan, M., Song, W., Liu, Y., Zhang, Z., et al. (2022). Performance research and engineering application of B₂O₃-Bi₂O₃-ZnO glass powder for solidifying iodine-containing silver silica gel. J. Non-Cryst. Solids 576, 121305. doi:10.1016/j.jnoncrysol.2021.121305

CrossRef Full Text | Google Scholar

Herdes, C., Prosenjak, C., Román, S., and Müller, E. A. (2013). Fundamental studies of methyl iodide adsorption in DABCO impregnated activated carbons. Langmuir 29 (23), 6849–6855. doi:10.1021/la401334d

PubMed Abstract | CrossRef Full Text | Google Scholar

Horner, D. E., Mailen, J. C., and Posey, F. A. (1977). Electrolytic trapping of iodine from process gas streams. Washington, DC: U.S. Patent and Trademark Office. U.S. Patent No 4,004,993.

Google Scholar

Hrizi, C., Samet, A., Abid, Y., Chaabouni, S., Fliyou, M., and Koumina, A. (2011). Crystal structure, vibrational and optical properties of a new self-organized material containing iodide anions of bismuth(III), [C₆H₄(NH₃)₂]₂Bi₂I₁₀·4H₂O. J. Mol. Struct. 992 (1), 96–101. doi:10.1016/j.molstruc.2011.02.051

CrossRef Full Text | Google Scholar

Huang, R. J., Seitz, K., Buxmann, J., Pöhler, D., Hornsby, K. E., Carpenter, L. J., et al. (2010). In situ measurements of molecular iodine in the marine boundary layer: The link to macroalgae and the implications for O-3, IO, OIO and NO_x. Atmos. Chem. Phys. 10 (10), 4823–4833. doi:10.5194/acp-10-4823-2010

CrossRef Full Text | Google Scholar

Hughes, J. T., Sava, D. F., Nenoff, T. M., and Navrotsky, A. (2013). Thermochemical evidence for strong iodine chemisorption by ZIF-8. J. Am. Chem. Soc. 135 (44), 16256–16259. doi:10.1021/ja406081r

PubMed Abstract | CrossRef Full Text | Google Scholar

Inagaki, Y., Imamura, T., Idemitsu, K., Arima, T., Kato, O., Nishimura, T., et al. (2008). Aqueous dissolution of silver iodide and associated iodine release under reducing conditions with FeCl₂ solution. J. Nucl. Sci. Technol. 45 (9), 859–866. doi:10.1080/18811248.2008.9711487

CrossRef Full Text | Google Scholar

Jiang, M., Zhu, L., Zhao, Q., Chen, G., Wang, Z., Zhang, J., et al. (2022). Novel synthesis of NaY-NH₄F-Bi₂S₃ composite for enhancing iodine capture. Chem. Eng. J. 443, 136477. doi:10.1016/j.cej.2022.136477

CrossRef Full Text | Google Scholar

Jung, Y.-E., Kang, S.-W., and Yim, M.-S. (2021). Feasibility study of using Bi-mna metal–organic frameworks as adsorbents for radioiodine capture at high temperature. Ind. Eng. Chem. Res. 60 (16), 5964–5975. doi:10.1021/acs.iecr.1c00450

CrossRef Full Text | Google Scholar

Kang, S. W., Yang, J.-H., and Yim, M.-S. (2020). Examining practical application feasibility of bismuth-embedded SBA-15 for gaseous iodine adsorption. Nucl. Technol. 206 (10), 1593–1606. doi:10.1080/00295450.2020.1713680

CrossRef Full Text | Google Scholar

Kikuchi, M., Kitamura, M., Yusa, H., and Horiuchi, S. (1978). Removal of radioactive methyl iodide by silver impregnated alumina and zeolite. Nucl. Eng. Des. 47 (2), 283–287. doi:10.1016/0029-5493(78)90071-7

CrossRef Full Text | Google Scholar

Kindel, O., Hoeflich, V., Herrmann, F. J., and Patzelt, P. (1993). Removal of iodooraganic compounds from kerosene in nuclear fuel reprocessing. J. Radioanal. Nucl. Chem. 176 (3), 251–259. doi:10.1007/bf02163676

CrossRef Full Text | Google Scholar

Klimakov, A. M., Popovkin, B. A., and Novoselova, A. V. (1974). T-X projection of structural diagrams of BiL₃-Bi₂O₃ system. Russ. J. Inorg. Chem. 19, 2553–2556.

Google Scholar

Kodama, H. (1992). Solidification of iodide ion by reaction with Bi₂O₃. Bull. Chem. Soc. Jpn. 65 (11), 3011–3014. doi:10.1246/bcsj.65.3011

CrossRef Full Text | Google Scholar

Kodama, H. (1994). The removal and solidification of halogenide ions using a new inorganic compound. Bull. Chem. Soc. Jpn. 67 (7), 1788–1791. doi:10.1246/bcsj.67.1788

CrossRef Full Text | Google Scholar

Kosaka, K., Asami, M., Kobashigawa, N., Ohkubo, K., Terada, H., Kishida, N., et al. (2012). Removal of radioactive iodine and cesium in water purification processes after an explosion at a nuclear power plant due to the Great East Japan Earthquake. Water Res. 46 (14), 4397–4404. doi:10.1016/j.watres.2012.05.055

PubMed Abstract | CrossRef Full Text | Google Scholar

Krämer, V. (1979). Investigations of sulphide systems by thermal analysis and chemical vapour transport. J. Therm. Anal. 16 (2), 295–306. doi:10.1007/bf01910692

CrossRef Full Text | Google Scholar

Krumhansl, J. L., and Nenoff, T. M. (2011). Hydrotalcite-like layered bismuth–iodine–oxides as waste forms. Appl. Geochem. 26 (1), 57–64. doi:10.1016/j.apgeochem.2010.11.003

CrossRef Full Text | Google Scholar

Kulyukhin, S. A., Mizina, L. V., Zanina, E. V., Rumer, I. A., Konovalova, N. A., and Levushkin, D. S. (2012). Synthesis of sorbents based on coarsely dispersed silica gel, containing nanoparticles of Ag compounds, for localization of volatile radioactive iodine compounds from the water vapor-air medium. Radiochemistry 54 (4), 368–378. doi:10.1134/s1066362212040108

CrossRef Full Text | Google Scholar

Lawter, A. R., Levitskaia, T. G., Qafoku, O., Bowden, M. E., Colon, F. C., and Qafoku, N. P. (2021). Simultaneous immobilization of aqueous co-contaminants using a bismuth layered material. J. Environ. Radioact. 237, 106711. doi:10.1016/j.jenvrad.2021.106711

PubMed Abstract | CrossRef Full Text | Google Scholar

Lee, S.-H., and Takahashi, Y. (2020). Selective immobilization of iodide onto a novel bismuth-impregnated layered mixed metal oxide: Batch and EXAFS studies. J. Hazard. Mater. 384, 121223. doi:10.1016/j.jhazmat.2019.121223

PubMed Abstract | CrossRef Full Text | Google Scholar

Lee, U., Kim, M. J., and Kim, H. R. (2018). Radioactive iodine analysis in environmental samples around nuclear facilities and sewage treatment plants. Nucl. Eng. Technol. 50 (8), 1355–1363. doi:10.1016/j.net.2018.07.017

CrossRef Full Text | Google Scholar

Lee, W. E., Ojovan, M. I., Stennett, M. C., and Hyatt, N. C. (2006). Immobilisation of radioactive waste in glasses, glass composite materials and ceramics. Adv. Appl. Ceram. 105 (1), 3–12. doi:10.1179/174367606x81669

CrossRef Full Text | Google Scholar

Lin, C.-C. (1981). Volatility of iodine in dilute aqueous solutions. J. Inorg. Nucl. Chem. 43 (12), 3229–3238. doi:10.1016/0022-1902(81)80094-2

CrossRef Full Text | Google Scholar

Lin, G., Zhu, L., Duan, T., Zhang, L., Liu, B., and Lei, J. (2019). Efficient capture of iodine by a polysulfide-inserted inorganic NiTi-layered double hydroxides. Chem. Eng. J. 378, 122181. doi:10.1016/j.cej.2019.122181

CrossRef Full Text | Google Scholar

Liu, L., Liu, W., Zhao, X., Chen, D., Cai, R., Yang, W., et al. (2014). Selective capture of iodide from solutions by microrosette-like δ-Bi₂O₃. ACS Appl. Mater. Interfaces 6 (18), 16082–16090. doi:10.1021/am504000n

PubMed Abstract | CrossRef Full Text | Google Scholar

Liu, S., Kang, S., Wang, H., Wang, G., Zhao, H., and Cai, W. (2016). Nanosheets-built flowerlike micro/nanostructured Bi₂O_2.33 and its highly efficient iodine removal performances. Chem. Eng. J. 289, 219–230. doi:10.1016/j.cej.2015.12.101

CrossRef Full Text | Google Scholar

Liu, S., Zeng, Y., Liu, J., Li, J., Peng, H., Xie, H., et al. (2022). Efficient capture and stable storage of radioactive iodine by bismuth-based ZIF-8 derived carbon materials as adsorbents. Sep. Purif. Technol. 302, 122151. doi:10.1016/j.seppur.2022.122151

CrossRef Full Text | Google Scholar

Liu, Y., Li, B., Shu, X., Zhang, Z., Wei, G., Liu, Y., et al. (2021). Low-sintering-temperature borosilicate glass to immobilize silver-coated silica-gel with different iodine loadings. J. Hazard. Mater. 403, 123588. doi:10.1016/j.jhazmat.2020.123588

PubMed Abstract | CrossRef Full Text | Google Scholar

Ma, S., Islam, S. M., Shim, Y., Gu, Q., Wang, P., Li, H., et al. (2014). Highly efficient iodine capture by layered double hydroxides intercalated with polysulfides. Chem. Mater. 26 (24), 7114–7123. doi:10.1021/cm5036997

CrossRef Full Text | Google Scholar

Mailen, J. C., and Horner, D. E. (1976). Removal of radioiodine from gas streams by electrolytic scrubbing. Nucl. Technol. 30 (3), 317–324. doi:10.13182/nt76-a31646

CrossRef Full Text | Google Scholar

Michel, R., Handl, J., Ernst, T., Botsch, W., Szidat, S., Schmidt, A., et al. (2005). Iodine-129 in soils from Northern Ukraine and the retrospective dosimetry of the iodine-131 exposure after the Chernobyl accident. Sci. Total Environ. 340 (1), 35–55. doi:10.1016/j.scitotenv.2004.08.006

PubMed Abstract | CrossRef Full Text | Google Scholar

Miensah, E. D., Gu, A., Kokuloku, L. T., Chen, K., Wang, P., Gong, C., et al. (2022). Strategies for radioiodine capture by metal organic frameworks and their derived materials. Microporous Mesoporous Mat. 341, 112041. doi:10.1016/j.micromeso.2022.112041

CrossRef Full Text | Google Scholar

Mineo, H., Gotoh, M., Iizuka, M., Fujisaki, S., Hagiya, H., and Uchiyama, G. (2003). Applicability of a model predicting iodine-129 profile in a silver nitrate silica-gel column for dissolver off-gas treatment of fuel reprocessing. Sep. Sci. Technol. 38 (9), 1981–2001. doi:10.1081/ss-120020130

CrossRef Full Text | Google Scholar

Mineo, H., Gotoh, M., Iizuka, M., Fujisaki, S., and Uchiyama, G. (2002). A simple model predicting iodine profile in a packed bed of silica-gel impregnated with silver nitrate. J. Nucl. Sci. Technol. 39 (3), 241–247. doi:10.1080/18811248.2002.9715181

CrossRef Full Text | Google Scholar

Modolo, G., and Odoj, R. (1997). Investigations on the partitioning of ¹²⁹I from silver-impregnated silica in preparation for future transmutation. Nucl. Technol. 117 (1), 80–86. doi:10.13182/nt97-a35337

CrossRef Full Text | Google Scholar

Moore, R. C., Pearce, C. I., Morad, J. W., Chatterjee, S., Levitskaia, T. G., Asmussen, R. M., et al. (2020). Iodine immobilization by materials through sorption and redox-driven processes: A literature review. Sci. Total Environ. 716, 132820. doi:10.1016/j.scitotenv.2019.06.166

PubMed Abstract | CrossRef Full Text | Google Scholar

Moriyama, K., Tashiro, S., Chiba, N., Hirayama, F., Maruyama, Y., Nakamura, H., et al. (2010). Experiments on the release of gaseous iodine from gamma-irradiated aqueous CsI solution and influence of oxygen and methyl isobutyl ketone (MIBK). J. Nucl. Sci. Technol. 47 (3), 229–237. doi:10.1080/18811248.2010.9711949

CrossRef Full Text | Google Scholar

Mowry, C. D., Brady, P. V., Garino, T. J., and Nenoff, T. M. (2015). Development and durability testing of a low-temperature sintering Bi–Si–Zn oxide glass composite material (GCM) ¹²⁹I Waste Form. J. Am. Ceram. Soc. 98 (10), 3094–3104. doi:10.1111/jace.13751

CrossRef Full Text | Google Scholar

Muhire, C., Tesfay Reda, A., Zhang, D., Xu, X., and Cui, C. (2022). An overview on metal oxide-based materials for iodine capture and storage. Chem. Eng. J. 431, 133816. doi:10.1016/j.cej.2021.133816

CrossRef Full Text | Google Scholar

Munakata, K., Kanjo, S., Yamatsuki, S., Koga, A., and Ianovski, D. (2003). Adsorption of noble gases on silver-mordenite. J. Nucl. Sci. Technol. 40 (9), 695–697. doi:10.1080/18811248.2003.9715408

CrossRef Full Text | Google Scholar

Nan, Y., Liu, J., Tang, S., Lin, R., and Tavlarides, L. L. (2018). Silver-exchanged mordenite for capture of water vapor in off-gas streams: A study of adsorption kinetics. Ind. Eng. Chem. Res. 57 (3), 1048–1058. doi:10.1021/acs.iecr.7b04420

CrossRef Full Text | Google Scholar

Nandanwar, S. U., Coldsnow, K., Utgikar, V., Sabharwall, P., and Eric Aston, D. (2016). Capture of harmful radioactive contaminants from off-gas stream using porous solid sorbents for clean environment – a review. Chem. Eng. J. 306, 369–381. doi:10.1016/j.cej.2016.07.073

CrossRef Full Text | Google Scholar

Nenoff, T. M., Rodriguez, M. A., Soelberg, N. R., and Chapman, K. W. (2014). Silver-mordenite for radiologic gas capture from complex streams: Dual catalytic CH₃I decomposition and I confinement. Microporous Mesoporous Mat. 200, 297–303. doi:10.1016/j.micromeso.2014.04.041

CrossRef Full Text | Google Scholar

Ng, C. H. B., and Fan, W. Y. (2016). Shape-controlled preparation of basic bismuth nitrate crystals with high iodide-removal capacities. ChemNanoMat 2 (2), 133–139. doi:10.1002/cnma.201500179

CrossRef Full Text | Google Scholar

Ojovan, M. I., and Lee, W. E. (2011). Glassy wasteforms for nuclear waste immobilization. Metall. Mater. Trans. A-Phys. Metall. Mater. Sci. 42 (4), 837–851. doi:10.1007/s11661-010-0525-7

CrossRef Full Text | Google Scholar

Pearce, C. I., Cordova, E. A., Garcia, W. L., Saslow, S. A., Cantrell, K. J., Morad, J. W., et al. (2020). Evaluation of materials for iodine and technetium immobilization through sorption and redox-driven processes. Sci. Total Environ. 716, 136167. doi:10.1016/j.scitotenv.2019.136167

PubMed Abstract | CrossRef Full Text | Google Scholar

Pei, C., Ben, T., Xu, S., and Qiu, S. (2014). Ultrahigh iodine adsorption in porous organic frameworks. J. Mater. Chem. A 2 (20), 7179–7187. doi:10.1039/c4ta00049h

CrossRef Full Text | Google Scholar

Pham, T. C. T., Docao, S., Hwang, I. C., Song, M. K., Choi, D. Y., Moon, D., et al. (2016). Capture of iodine and organic iodides using silica zeolites and the semiconductor behaviour of iodine in a silica zeolite. Energy Environ. Sci. 9 (3), 1050–1062. doi:10.1039/c5ee02843d

CrossRef Full Text | Google Scholar

Pillar, E. A., Guzman, M. I., and Rodriguez, J. M. (2013). Conversion of iodide to hypoiodous acid and iodine in aqueous microdroplets exposed to ozone. Environ. Sci. Technol. 47 (19), 10971–10979. doi:10.1021/es401700h

PubMed Abstract | CrossRef Full Text | Google Scholar

Pires, J., Carvalho, A., and de Carvalho, M. B. (2001). Adsorption of volatile organic compounds in Y zeolites and pillared clays. Microporous Mesoporous Mat. 43 (3), 277–287. doi:10.1016/s1387-1811(01)00207-4

CrossRef Full Text | Google Scholar

Qin, H., Lv, Y., Kobayashi, H., Xiao, M., Song, H., and Yang, J. (2022). Fabrication of NOTT-220 @I₂ via iodine adsorption and immobilization in bismuth organic framework for efficient CO₂ photo-reduction. J. Alloys Compd. 920, 165900. doi:10.1016/j.jallcom.2022.165900

CrossRef Full Text | Google Scholar

Ranjan, M., Singh, P. K., and Srivastav, A. L. (2020). A review of bismuth-based sorptive materials for the removal of major contaminants from drinking water. Environ. Sci. Pollut. Res. 27 (15), 17492–17504. doi:10.1007/s11356-019-05359-9

PubMed Abstract | CrossRef Full Text | Google Scholar

Riley, B. J., Chun, J., Ryan, J. V., Matyas, J., Li, X. S., Matson, D. W., et al. (2011). Chalcogen-based aerogels as a multifunctional platform for remediation of radioactive iodine. RSC Adv. 1 (9), 1704–1715. doi:10.1039/c1ra00351h

CrossRef Full Text | Google Scholar

Riley, B. J., Chun, J., Um, W., Lepry, W. C., Matyas, J., Olszta, M. J., et al. (2013). Chalcogen-based aerogels as sorbents for radionuclide remediation. Environ. Sci. Technol. 47 (13), 7540–7547. doi:10.1021/es400595z

PubMed Abstract | CrossRef Full Text | Google Scholar

Riley, B. J., Vienna, J. D., Strachan, D. M., McCloy, J. S., and Jerden, J. L. (2016). Materials and processes for the effective capture and immobilization of radioiodine: A review. J. Nucl. Mater. 470, 307–326. doi:10.1016/j.jnucmat.2015.11.038

CrossRef Full Text | Google Scholar

Sakurai, T., and Takahashi, A. (1994). Catalytic effect of silver-impregnated silica-gel (AgS) on reaction of methyl iodide with nitrogen dioxide. J. Nucl. Sci. Technol. 31 (1), 86–87. doi:10.1080/18811248.1994.9735119

CrossRef Full Text | Google Scholar

Sava, D. F., Chapman, K. W., Rodriguez, M. A., Greathouse, J. A., Crozier, P. S., Zhao, H., et al. (2013). Competitive I₂ sorption by Cu-BTC from humid gas streams. Chem. Mater. 25 (13), 2591–2596. doi:10.1021/cm401762g

CrossRef Full Text | Google Scholar

Sava, D. F., Garino, T. J., and Nenoff, T. M. (2012). Iodine confinement into Metal–Organic Frameworks (MOFs): Low-temperature sintering glasses to form novel glass composite material (GCM) alternative waste forms. Ind. Eng. Chem. Res. 51 (2), 614–620. doi:10.1021/ie200248g

CrossRef Full Text | Google Scholar

Sava, D. F., Rodriguez, M. A., Chapman, K. W., Chupas, P. J., Greathouse, J. A., Crozier, P. S., et al. (2011). Capture of volatile iodine, a gaseous fission product, by zeolitic imidazolate framework-8. J. Am. Chem. Soc. 133 (32), 12398–12401. doi:10.1021/ja204757x

PubMed Abstract | CrossRef Full Text | Google Scholar

Sava Gallis, D. F., Ermanoski, I., Greathouse, J. A., Chapman, K. W., and Nenoff, T. M. (2017). Iodine gas adsorption in nanoporous materials: A combined experiment modeling study. Ind. Eng. Chem. Res. 56 (8), 2331–2338. doi:10.1021/acs.iecr.6b04189

CrossRef Full Text | Google Scholar

Scott, S. M., Hu, T., Yao, T., Xin, G., and Lian, J. (2015). Graphene-based sorbents for iodine-129 capture and sequestration. Carbon 90, 1–8. doi:10.1016/j.carbon.2015.03.070

CrossRef Full Text | Google Scholar

Soelberg, N. R., Garn, T. G., Greenhalgh, M. R., Law, J. D., Jubin, R., Strachan, D. M., et al. (2013). Radioactive iodine and krypton control for nuclear fuel reprocessing facilities. Sci. Technol. Nucl. Install. 2013, 1–12. doi:10.1155/2013/702496

CrossRef Full Text | Google Scholar

Subrahmanyam, K. S., Sarma, D., Malliakas, C. D., Polychronopoulou, K., Riley, B. J., Pierce, D. A., et al. (2015). Chalcogenide aerogels as sorbents for radioactive iodine. Chem. Mater. 27 (7), 2619–2626. doi:10.1021/acs.chemmater.5b00413

CrossRef Full Text | Google Scholar

Taghipour, F., and Evans, G. J. (2000). Radiolytic organic iodide formation under nuclear reactor accident conditions. Environ. Sci. Technol. 34 (14), 3012–3017. doi:10.1021/es990507d

CrossRef Full Text | Google Scholar

Takeshita, K., and Azegami, Y. (2004). Development of thermal swing adsorption (TSA) process for complete recovery of iodine in dissolver off-gas. J. Nucl. Sci. Technol. 41 (1), 91–94. doi:10.1080/18811248.2004.9715463

CrossRef Full Text | Google Scholar

Tanabe, H., Sakuragi, T., Yamaguchi, K., Sato, T., and Owada, H. (2010). Development of new waste forms to immobilize iodine-129 released from a spent fuel reprocessing plant. Adv. Sci. Technol. 73, 158–170. doi:10.4028/www.scientific.net/ast.73.158

CrossRef Full Text | Google Scholar

Taylor, D. M. (1981). The radiotoxicology of iodine. J. Radioanal. Chem. 65 (1), 195–208. doi:10.1007/bf02516104

CrossRef Full Text | Google Scholar

Tesfay Reda, A., Pan, M., Zhang, D., and Xu, X. (2021a). Bismuth-based materials for iodine capture and storage: A review. J. Environ. Chem. Eng. 9 (4), 105279. doi:10.1016/j.jece.2021.105279

CrossRef Full Text | Google Scholar

Tesfay Reda, A., Zhang, D., Xu, X., Pan, M., Chang, C., Muhire, C., et al. (2021b). Bismuth-impregnated aluminum/copper oxide-pillared montmorillonite for efficient vapor iodine sorption. Sep. Purif. Technol. 270, 118848. doi:10.1016/j.seppur.2021.118848

CrossRef Full Text | Google Scholar

Tesfay Reda, A., Zhang, D., Xu, X., and Xu, S. (2022). Highly stable iodine capture by pillared montmorillonite functionalized Bi₂O₃@g-C₃N₄ nanosheets. Sep. Purif. Technol. 292, 120994. doi:10.1016/j.seppur.2022.120994

CrossRef Full Text | Google Scholar

Thomas, G. D., Smith, S. M., and Turcotte, J. A. (2009). Using public relations strategies to prompt populations at risk to seek health information: The Hanford Community Health Project. Health promot. Pract. 10 (1), 92–101. doi:10.1177/1524839907307676

PubMed Abstract | CrossRef Full Text | Google Scholar

Tian, Z., Chee, T.-S., Meng, R., Hao, Y., Zhou, X., Ma, B., et al. (2022). Incipient wetness impregnation to prepare bismuth-modified all-silica beta zeolite for efficient radioactive iodine capture. Environ. Funct. Mater. 1 (1), 92–104. doi:10.1016/j.efmat.2022.05.006

CrossRef Full Text | Google Scholar

Tian, Z., Chee, T.-S., Zhang, X., Lei, L., and Xiao, C. (2021a). Novel bismuth-based electrospinning materials for highly efficient capture of radioiodine. Chem. Eng. J. 412, 128687. doi:10.1016/j.cej.2021.128687

CrossRef Full Text | Google Scholar

Tian, Z., Chee, T.-S., Zhu, L., Duan, T., Zhang, X., Lei, L., et al. (2021b). Comprehensive comparison of bismuth and silver functionalized nickel foam composites in capturing radioactive gaseous iodine. J. Hazard. Mater. 417, 125978. doi:10.1016/j.jhazmat.2021.125978

PubMed Abstract | CrossRef Full Text | Google Scholar

Verger, P., Aurengo, A., Geoffroy, B., and Le Guen, B. (2001). Iodine kinetics and effectiveness of stable iodine prophylaxis after intake of radioactive iodine: A review. Thyroid 11 (4), 353–360. doi:10.1089/10507250152039082

PubMed Abstract | CrossRef Full Text | Google Scholar

Wang, C., Hu, H., Yan, S., and Zhang, Q. (2020). Activating Bi₂O₃ by ball milling to induce efficiently oxygen vacancy for incorporating iodide anions to form BiOI. Chem. Phys. 533, 110739. doi:10.1016/j.chemphys.2020.110739

CrossRef Full Text | Google Scholar

Wang, J., and Zhuang, S. (2019). Covalent organic frameworks (COFs) for environmental applications. Coord. Chem. Rev. 400, 213046. doi:10.1016/j.ccr.2019.213046

CrossRef Full Text | Google Scholar

Wang, P., Xu, Q., Li, Z., Jiang, W., Jiang, Q., and Jiang, D. (2018). Exceptional iodine capture in 2D covalent organic frameworks. Adv. Mater. 30 (29), 1801991. doi:10.1002/adma.201801991

PubMed Abstract | CrossRef Full Text | Google Scholar

Wei, G., Luo, F., Li, B., Liu, Y., Yang, J., Zhang, Z., et al. (2021). Immobilization of iodine waste forms: A low-sintering temperature with Bi₂O₃-B₂O₃-ZnO glass. Ann. Nucl. Energy 150, 107817. doi:10.1016/j.anucene.2020.107817

CrossRef Full Text | Google Scholar

Wei, G., Shu, X., Zhang, Z., Li, Q., Liu, Y., Wang, X., et al. (2020). B₂O₃–Bi₂O₃–ZnO based materials for low-sintering temperature immobilization of iodine adsorbed waste. J. Solid State Chem. 289, 121518. doi:10.1016/j.jssc.2020.121518

CrossRef Full Text | Google Scholar

Woo, T. H. (2013). Atmospheric modeling of radioactive material dispersion and health risk in Fukushima Daiichi nuclear power plants accident. Ann. Nucl. Energy 53, 197–201. doi:10.1016/j.anucene.2012.09.003

CrossRef Full Text | Google Scholar

Wren, J. C., Ball, J. M., and Glowa, G. A. (1999). The interaction of iodine with organic material in containment. Nucl. Technol. 125 (3), 337–362. doi:10.13182/NT99-A2952

CrossRef Full Text | Google Scholar

Wu, B., Yan, M., Luo, F., Shu, X., Liu, Y., Wei, G., et al. (2021). Low-temperature fabrication of glass-based iodine waste forms via a novel preparation method. J. Solid State Chem. 300, 122186. doi:10.1016/j.jssc.2021.122186

CrossRef Full Text | Google Scholar

Wu, D., Wei, G., Shu, X., Liu, Y., Han, W., Zhang, Z., et al. (2022). Immobilization of iodine waste at low sintering temperature: Phase evolution and microstructure transformation. Ann. Nucl. Energy 173, 109145. doi:10.1016/j.anucene.2022.109145

CrossRef Full Text | Google Scholar

Xian, Q., Chen, L., Fan, W., Liu, Y., He, X., Dan, H., et al. (2022a). Facile synthesis of novel Bi⁰-SBA-15 adsorbents by an improved impregnation reduction method for highly efficient capture of iodine gas. J. Hazard. Mater. 424, 127678. doi:10.1016/j.jhazmat.2021.127678

PubMed Abstract | CrossRef Full Text | Google Scholar

Xian, Q., Gan, Y., Yu, J., Xiao, X., Chen, Q., Dan, H., et al. (2022b). Scalable and economical Bi⁰-SiO₂ for the high efficient capture of iodine gas. J. Nucl. Mater. 567, 153849. doi:10.1016/j.jnucmat.2022.153849

CrossRef Full Text | Google Scholar

Xiong, Y., Dang, B., Wang, C., Wan, H., Zhang, S., Sun, Q., et al. (2017). Cellulose fibers constructed convenient recyclable 3D graphene-formicary-like delta-Bi₂O₃ aerogels for the selective capture of iodide. ACS Appl. Mater. Interfaces 9 (24), 20554–20560. doi:10.1021/acsami.7b03516

PubMed Abstract | CrossRef Full Text | Google Scholar

Xiong, Y., Wang, C., Wang, H., Jin, C., Sun, Q., and Xu, X. (2018). Nano-cellulose hydrogel coated flexible titanate-bismuth oxide membrane for trinity synergistic treatment of super-intricate anion/cation/oily-water. Chem. Eng. J. 337, 143–151. doi:10.1016/j.cej.2017.12.080

CrossRef Full Text | Google Scholar

Xu, W., Zhang, W., Kang, J., and Li, B. (2019). Facile synthesis of mesoporous Fe-based MOFs loading bismuth with high speed adsorption of iodide from solution. J. Solid State Chem. 269, 558–565. doi:10.1016/j.jssc.2018.10.028

CrossRef Full Text | Google Scholar

Yan, M., Wu, B., Luo, F., Shu, X., Liu, Y., Wei, G., et al. (2021). Bi₂O₃ doped B₂O₃-ZnO glass powder for immobilization of radioactive iodine waste at low temperature. Ann. Nucl. Energy 161, 108480. doi:10.1016/j.anucene.2021.108480

CrossRef Full Text | Google Scholar

Yang, J. H., Cho, Y.-J., Shin, J. M., and Yim, M.-S. (2015). Bismuth-embedded SBA-15 mesoporous silica for radioactive iodine capture and stable storage. J. Nucl. Mater. 465, 556–564. doi:10.1016/j.jnucmat.2015.06.043

CrossRef Full Text | Google Scholar

Yang, J. H., Park, H. S., Ahn, D.-H., and Yim, M.-S. (2016). Glass composite waste forms for iodine confined in bismuth-embedded SBA-15. J. Nucl. Mater. 480, 150–158. doi:10.1016/j.jnucmat.2016.08.001

CrossRef Full Text | Google Scholar

Yang, K., Wang, Y., Shen, J., Scott, S. M., Riley, B. J., Vienna, J. D., et al. (2022). Cs₃Bi₂I₉-hydroxyapatite composite waste forms for cesium and iodine immobilization. J. Adv. Ceram. 11 (5), 712–728. doi:10.1007/s40145-021-0565-z

CrossRef Full Text | Google Scholar

Yang, K., Zhu, W., Scott, S., Wang, Y., Wang, J., Riley, B. J., et al. (2021). Immobilization of cesium and iodine into Cs₃Bi₂I₉ perovskite-silica composites and core-shell waste forms with high waste loadings and chemical durability. J. Hazard. Mater. 401, 123279. doi:10.1016/j.jhazmat.2020.123279

PubMed Abstract | CrossRef Full Text | Google Scholar

Yang, Y., Xiong, X., Fan, Y., Lai, Z., Xu, Z., and Luo, F. (2019). Insight into volatile iodine uptake properties of covalent organic frameworks with different conjugated structures. J. Solid State Chem. 279, 120979. doi:10.1016/j.jssc.2019.120979

CrossRef Full Text | Google Scholar

Yang, Y., Zeng, Z., Zhang, C., Huang, D., Zeng, G., Xiao, R., et al. (2018). Construction of iodine vacancy-rich BiOI/Ag@AgI Z-scheme heterojunction photocatalysts for visible-light-driven tetracycline degradation: Transformation pathways and mechanism insight. Chem. Eng. J. 349, 808–821. doi:10.1016/j.cej.2018.05.093

CrossRef Full Text | Google Scholar

Yu, F., Chen, Y., Wang, Y., Liu, C., and Qin, J. (2020). Synthesis of metal–organic framework nanocrystals immobilized with 3D flowerlike Cu–Bi-layered double hydroxides for iodine efficient removal. J. Mater. Res. 35 (3), 299–311. doi:10.1557/jmr.2020.1

CrossRef Full Text | Google Scholar

Yu, Q., Jiang, X., Cheng, Z., Liao, Y., Pu, Q., and Duan, M. (2020). Millimeter-sized Bi₂S₃@polyacrylonitrile hybrid beads for highly efficient iodine capture. New J. Chem. 44 (39), 16759–16768. doi:10.1039/d0nj03229h

CrossRef Full Text | Google Scholar

Yuan, Y., Dong, X., Chen, Y., and Zhang, M. (2016). Computational screening of iodine uptake in zeolitic imidazolate frameworks in a water-containing system. Phys. Chem. Chem. Phys. 18 (33), 23246–23256. doi:10.1039/c6cp02156e

PubMed Abstract | CrossRef Full Text | Google Scholar

Zakirova, G. G., Mladentsev, D. Y., and Borisova, N. E. (2017). Synthesis of chelating tertiary phosphine oxides via palladium-catalysed C–P bond formation. Tetrahedron Lett. 58 (35), 3415–3417. doi:10.1016/j.tetlet.2017.07.055

CrossRef Full Text | Google Scholar

Zhang, L., and Jaroniec, M. (2017). SBA-15 templating synthesis of mesoporous bismuth oxide for selective removal of iodide. J. Colloid Interface Sci. 501, 248–255. doi:10.1016/j.jcis.2017.04.063

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhang, L., Wang, W., Yang, J., Chen, Z., Zhang, W., Zhou, L., et al. (2006). Sonochemical synthesis of nanocrystallite Bi₂O₃ as a visible-light-driven photocatalyst. Appl. Catal. A 308, 105–110. doi:10.1016/j.apcata.2006.04.016

CrossRef Full Text | Google Scholar

Zhang, S., Du, J., Xu, C., Schwehr, K. A., Ho, Y. F., Li, H. P., et al. (2011). Concentration-dependent mobility, retardation, and speciation of iodine in surface sediment from the Savannah River Site. Environ. Sci. Technol. 45 (13), 5543–5549. doi:10.1021/es1040442

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhang, S., Xu, C., Creeley, D., Ho, Y.-F., Li, H.-P., Grandbois, R., et al. (2013). Iodine-129 and iodine-127 speciation in groundwater at the Hanford site, U.S.: Iodate incorporation into calcite. Environ. Sci. Technol. 47 (17), 9635–9642. doi:10.1021/es401816e

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhang, X., da Silva, I., Fazzi, R., Sheveleva, A. M., Han, X., Spencer, B. F., et al. (2019). Iodine adsorption in a redox-active metal–organic framework: Electrical conductivity induced by Host−Guest charge-transfer. Inorg. Chem. 58 (20), 14145–14150. doi:10.1021/acs.inorgchem.9b02176

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhao, H., Nenoff, T. M., Jennings, G., Chupas, P. J., and Chapman, K. W. (2011). Determining quantitative kinetics and the structural mechanism for particle growth in porous templates. J. Phys. Chem. Lett. 2 (21), 2742–2746. doi:10.1021/jz201260n

CrossRef Full Text | Google Scholar

Zhao, Q., Chen, G., Wang, Z., Jiang, M., Lin, J., Zhang, L., et al. (2021). Efficient removal and immobilization of radioactive iodide and iodate from aqueous solutions by bismuth-based composite beads. Chem. Eng. J. 426, 131629. doi:10.1016/j.cej.2021.131629

CrossRef Full Text | Google Scholar

Zhou, J., Hao, S., Gao, L., and Zhang, Y. (2014). Study on adsorption performance of coal based activated carbon to radioactive iodine and stable iodine. Ann. Nucl. Energy 72, 237–241. doi:10.1016/j.anucene.2014.05.028

CrossRef Full Text | Google Scholar

Zou, H., Guo, J., Song, M., Yi, F., Wang, X., Pan, N., et al. (2021). Bi₂S₃-reduced graphene oxide composite for gaseous radioiodine capture and its immobilization within glass composite material. Prog. Nucl. Energy 135, 103705. doi:10.1016/j.pnucene.2021.103705

CrossRef Full Text | Google Scholar

Zou, H., Yi, F., Song, M., Wang, X., Bian, L., Li, W., et al. (2019). Novel synthesis of Bi-Bi₂O₃-TiO₂-C composite for capturing iodine-129 in off-gas. J. Hazard. Mater. 365, 81–87. doi:10.1016/j.jhazmat.2018.11.001

PubMed Abstract | CrossRef Full Text | Google Scholar