Modulating the Electron Transporting Properties of Subphthalocyanines for Inverted Perovskite Solar Cells

The lack of organic non-fullerene ETMs with good electron transport and device stability is an important problem for the further development and commercialization of perovskite solar cells. Herein, the use of SubPcs as ETMs in PSCs is explored. To this end, we analyze the influence of SubPc peripheral functionalization on the efficiency and stability of p-i-n PSCs. Specifically, ETMs based on three SubPcs (with either six or twelve peripheral fluorine and chlorine atoms) have been incorporated into PSCs with the perovskite layer deposited by solution processing (CsFAMAPbIBr). The device performance and morphology of these devices are deeply analyzed using several techniques, and the interfacial effects induced by the SubPcs are studied using photoluminescence and TR-PL. It is observed that the device stability is significantly improved upon insertion the SubPc layer. Moreover, the impact of the SubPc layer-thickness is assessed. Thus, a maximum power conversion efficiency of 13.6% was achieved with the champion device.

Introduction

Due to their excellent properties, low cost, and facile preparation (Heo et al., 2013; Hodes, 2013), organic-inorganic metal halide perovskite solar cells (PSCs) have witnessed an unprecedentedly extensive research activity over the past decade (Snaith, 2018; Lu et al., 2020; Vasilopoulou et al., 2020; Li et al., 2021). Thus, within only a few years, PSCs have reached impressive power conversion efficiency (PCE) values of up to 25.5% by employing the conventional n-i-p configuration (Best Research-Cell Efficiency Chart, 2021). However, the cost-effective mass production and flexible applications of PSCs still remain problematic since, in such n-i-p devices, the metal oxide layer (typically TiO₂) suffers from low stability under UV irradiation and requires high-temperature treatments (Leijtens et al., 2013; Di Giacomo et al., 2016). Consequently, inverted PSCs, also known as p-i-n devices, have recently piqued special attention within the solar cell community since they present more advantageous properties, such as low-temperature processing, the potential to construct tandem solar cells, negligible hysteresis, and compatibility with printing technology (Lin et al., 2020). Nonetheless, despite showing these features, the PCEs of p-i-n PSCs still lag behind in comparison with those of the n-i-p configuration. Such a gap in efficiency mainly stems from the recombination losses ascribed to defects on the perovskite (PVK) surface and at the grain boundaries, and the mismatched energy-level between the PVK and the fullerene-based electron transport material (ETM) (Xu et al., 2015; Luo et al., 2020; Wu et al., 2020), which, in addition, exhibit additional shortcomings such as intrinsic degradation by light-induced dimerization, extrinsic degradation by oxygen and water, and high-energy inputs in their synthesis, purification, and functionalization (Gil-Escrig et al., 2016; Zhao et al., 2016; Said et al., 2019; Zhang et al., 2019). As a result, the search for non-fullerene acceptors (NFA) that simultaneously improve the PVK stability/morphology, exhibit good stability against light and moisture, and display tunable energy levels has become a hot topic in the field of PSCs.

Porphyrinic macrocycles, such as phthalocyanines (Pcs) or porphyrins (Ps), currently represent a fundamental family of compounds for the construction of organic solar cells (OSCs) (Imahori and Fukuzumi, 2004; Walter et al., 2010; Li and Diau, 2013). In this sense, given the donor properties of these materials, Pcs and Ps are typically employed as p-type semiconductors (Urbani et al., 2019). However, when changing to their contracted homologues, such as Subphthalocyanines (SubPcs; Figure 1), porphyrinic materials can become excellent acceptors if appropriately functionalized (Claessens et al., 2014). Indeed, SubPcs peripherally decorated with electron-withdrawing groups (i.e., halogen atoms or diimides) actually hold a privileged position among the most versatile and promising n-type semiconductors by producing excellent PCEs in a variety of fullerene-free solar cells, ranging from planar- and bulk-heterojunction to tandem solar cells (Cnops et al., 2014; Cnops et al., 2015; Duan et al., 2017; Huang T. et al., 2019; Huang X. et al., 2019; Cai et al., 2020).

FIGURE 1

FIGURE 1. Synthetic route and UV/Vis absorbance spectra in solution (THF) (right) and in a thin film (left) of Cl-SubPcF₆, Cl-SubPcF_12, and Cl-SubPcCl₁₂.

Despite having these precedents and observing that SubPcs are known to actively interact with the perovskite layer, forming strong Pb-halide bonds, the use of SubPcs as ETMs is still an unexplored territory that, just very recently, has started to be investigated (Chen et al., 2021; Labella et al., 2021). Indeed, our groups have reported that a double-layer ETM consisting of a hexachlorinated SubPc and C₆₀ leads to PCEs of up to 10.8%. In this work, the influence of the substituent at the boron atom (i.e., chlorine or fluorine) and the processing method of the PVK layer on the device performance and stability was analyzed. It was observed that the axial chlorine atom and solution-processed triple cation PVK (CsFAMAPbIBr) are the best options as they furnish higher efficiencies and stabilities. However, we unfortunately observed that the SubPc did not efficiently extract the charges from the PVK layer, possibly due to an insufficiently low lowest unoccupied molecular orbital (LUMO) level or to a non-optimal supramolecular organization of SubPc molecules.

With the aim of improving the device performance and further understanding the structure-efficiency relationship of SubPc-based ETMs in PSCs, herein we analyze the influence of SubPc peripheral functionalization on the efficiency and stability of p-i-n PSCs. For this purpose, we prepared and evaluated three different SubPcs (Figure 1) with varying electronic and supramolecular properties. In particular, we synthetize SubPcs functionalized with either six or twelve peripheral fluorine or chlorine atoms (Cl-SubPcF₆, Cl-SubPcF_12, and Cl-SubPcCl₁₂), since it has been previously demonstrated that they present good supramolecular organization and low-lying LUMO levels (Bukuroshi et al., 2021). In combination with C₆₀, these SubPc materials are then implemented as ETM in PSC devices based on a solution processed PVK (CsFAMAPbIBr) active layer. The PV performance of the studied PSCs is deeply characterized by current density–voltage (J–V) curves, external quantum efficiency (EQE), and maximum power point tracking (MPPT). In order to understand the SubPc structure’s influence on the device stability, water contact angle measurements in PVK/SubPc layers are also performed. Moreover, the morphology is observed by scanning-electron-microscopy (SEM) and the electron extraction properties of these novel ETMs are analyzed by steady-state photoluminescence (PL) and time-resolved photoluminescence (TRPL). Finally, the impact of SubPc layer-thickness is also assessed for the SubPc leading to the best efficiency. Thus, we achieved a maximum PCE of 13.6% with the best performing device, which, in addition, showed better stability than devices containing only C₆₀ as ETM.

Results and Discussion

Synthesis and Characterization of SubPc Materials

As shown in Figure 1, Cl-SubPcF₆, Cl-SubPcF_12, and Cl-SubPcCl₁₂ were synthesized from commercially available phthalonitrile precursors by cyclotrimerization. Such a reaction was accomplished following a previously reported method developed in our labs for the preparation of halogenated SubPcs (Labella et al., 2021). Thus, Cl-SubPcF₆, Cl-SubPcF_12, and Cl-SubPcCl₁₂ were obtained in a 72, 55, and 67% yield, respectively, after simple column chromatography purification. These derivatives exhibited good solubility in organic solvents as well as excellent stability against light, ambient moisture, and oxygen.

The aggregation properties of Cl-SubPcF₆, Cl-SubPcF_12, and Cl-SubPcCl₁₂ at the solid state were preliminary analyzed by comparing their absorbance spectra both in solution and in thin film configuration. As shown in Figure 1, in the solid state, all SubPcs display the expected Q band which, although experiencing a slight broadening, remains similar in shape in comparison with those of in-solution spectra. Nevertheless, a ∼15–20 nm red-shift in the absorption maxima is observed, which points out to the formation of columnar H-type-like aggregates in the solid state as a result of the SubPc bowl-shape and dipole moment (Guilleme et al., 2015; Mayoral et al., 2020; Zhang et al., 2020). Then, in order to investigate the electronic properties of SubPcs, their oxidation and reduction potentials were determined in THF by cyclic voltammetry (CV) using 0.1 M tetrabutylammonium hexafluorophosphate (TBAPF₆) as an electrolyte and ferrocene (Fc/Fc⁺) as the internal reference (See SI). Employing the equation described by Bazan et al. (Cardona et al., 2011), the LUMO energies (Figure 2B) were calculated for Cl-SubPcF₆, Cl-SubPcF_12, and Cl-SubPcCl_12. As expected, all SubPcs provided a good energy-alignment with the PVK layer. As a result of the higher number of peripheral halogen atoms, both Cl-SubPcF₁₂ and Cl-SubPcCl₁₂ exhibit the lowest LUMO energies (-4.19 eV and -4.18 eV, respectively), which is similar to that of C₆₀ (-4.20 eV). In contrast, Cl-SubPcF₆ exhibits a LUMO energy value of -3.89 eV, which is similar to that of the hexachlorinated SubPc (hereafter referred to as Cl-SubPcCl₆) employed in our previous work (LUMO energy of -3.84 eV). (Labella et al., 2021).

FIGURE 2

FIGURE 2. p-i-n solar cells containing SubPc/C₆₀ as the ETL. (A) Scheme of the perovskite solar cell structure. (B) Energy level diagram of the device. (C) J–V curves and (D) EQE spectra and the corresponding integrated short circuit current of the most efficient devices containing 2 nm Cl-SubPcF₆, Cl-SubPcF₁₂ and Cl-SubPcCl₁₂. The J–V curve and the EQE spectrum of the control device (black line) were added for comparison.

Device Performance and Characterization

In order to evaluate the function of Cl-SubPcF₆, Cl-SubPcF_12, and Cl-SubPcCl₁₂ as ETMs, inverted PSCs were fabricated with the device structure of FTO/NiOx/PTAA/CsFAMAPbIBr/PEAI/SubPc/C₆₀/BCP/Cr/Au (Figure 2A), where NiOx and poly (triarylamine) (PTAA) were employed as hole transporting materials (HTMs) (Lian et al., 2020) and bathocuproine (BCP) was used to ensure the ohmic contact between C₆₀ and the top electrode (Chen et al., 2017). In addition, a 1 nm-thin layer of Cr was deposited to improve the device stability in air (Kaltenbrunner et al., 2015). In such devices, the triple cation PVK layer was deposited following an experimental procedure previously reported by some of us, and phenethylammonium iodide (PEAI) was further added to form a low-dimensional 2D PVK to improve the PVK surface and stability (Daskeviciute et al., 2021). According to our previous work, the ETM is based on a SubPc/C₆₀ double-layer deposited by thermal evaporation, with 2 nm being the optimal thickness for the SubPc material. The solar cells using only C₆₀ as a single ETL (i.e., 0 nm of SubPc material) were taken as a reference device.

Figure 2 illustrates the current density–voltage (J–V) characteristics (under AM 1.5G irradiation at 100 mWcm⁻²) of the champion devices using Cl-SubPcF₆, Cl-SubPcF_12, and Cl-SubPcCl₁₂ as ETMs. All relevant photovoltaic parameters including open-circuit voltage (V_OC), short-circuit current (J_SC), and fill factor (FF) of the devices are collected in Table 1. Moreover, the PCE distribution based on eight devices per device condition is shown in Supplementary Figure S1. As observed in Figure 1C, the photovoltaic performance of PSCs is strongly affected by the peripheral substituent, being Cl-SubPcF₆ the best-performing SubPc material by showing a PCE of 13.0%, with a remarkable V_OC of 1020 mV, a J_SC of 19.89 mA cm⁻², and a FF of 0.64. By contrast, Cl-SubPcF₁₂ and Cl-SubPcCl₁₂ showed lower PCEs values of 9.9% and 10.9%, respectively, mainly caused by the drop of V_OC values (920 mV), which might be attributed to a higher recombination at the perovskite/SubPc interface. Importantly, Cl-SubPcF₆ exhibits similar V_OC and J_SC but lower FF values than the reference, which furnished PCEs of about 14.5%. Importantly, it should be noted that Cl-SubPcF₆, Cl-SubPcF_12, and Cl-SubPcCl₁₂ exhibited higher J_SC values compared to that of previously tested Cl-SubPcCl₆ (Table 1), suggesting that these novel SubPc materials extract the charges more efficiently from the PVK. Further insights into J_SC were provided by recording the external quantum efficiency (EQE) curves (Figure 2D), whose integrated J_SC values match well to the J_SC values obtained from the J–V curve under AM 1.5G. In line with J–V curves, the EQE spectra show that the photoresponse from 350 to 800 nm is higher for Cl-SubPcCl₁₂ than for Cl-SubPcF₁₂ and Cl-SubPcF₆, indicating the improved electron collection of Cl-SubPcCl₁₂ in comparison with their F-based SubPc analogues.

TABLE 1

TABLE 1. PV parameters of the most efficient devices extracted from the corresponding J–V curves. FWD: forward scan (from J_SC to V_OC), REV: reverse scan (from V_OC to J_sc).

To investigate the hysteresis behavior of PSCs, their PCE were examined in both the forward and the reverse scan directions and the corresponding hysteresis index (HI) values were calculated with the reported formulae (Habisreutinger et al., 2018). As demonstrated in Figure 3A, Supplementary Figure S3 and Table 1, all devices exhibited similar J–V regardless of the scan direction, indicating almost negligible hysteresis effect in our devices with HI values of 0.02 (reference), 0.03 (Cl-SubPcF₆ and Cl-SubPcF₁₂) and none for Cl-SubPcCl_12. Subsequently, the stability of our devices was evaluated by monitoring the PCE at the maximum power output point as a function of time (Figure 3B). Remarkably, it was observed that the PCE of PSCs containing Cl-SubPcF₆ and Cl-SubPcCl₁₂ decreased over time much more slowly than the reference. Thus, it can be concluded that the integration of these SubPcs in the ETM significantly improves the device stability. By contrast, Cl-SubPcF₁₂ showed the lowest device stability, which could be the reason for the low efficiency observed with this material. With the aim of understanding such a stabilization upon the addition of SubPcs, the water contact angles of the PVK/SubPc and PVK reference samples were measured (Figure 3C). Compared with PVK (65.8°) and PVK/Cl-SubPcF₁₂ (66.9°), larger average contact angles of about 69.5° and 75.2° were obtained for the PVK/Cl-SubPcF₆ and PVK/Cl-SubPcCl₁₂, respectively. Thus, the more hydrophobic properties of Cl-SubPcF₆ and Cl-SubPcCl₁₂ could provide a better physical barrier to block H₂O and O₂ from penetrating the underlying PVK layer and contribute to the higher ambient stability of the corresponding PSCs.

FIGURE 3

FIGURE 3. (A) J–V curve hysteresis of Cl-SubPcF₆. (B) stability of the PSCs containing 2 nm-vacuum deposited Cl-SubPcF₆, Cl-SubPcF₁₂ and Cl-SubPcCl₁₂ layers, measured under one sun illumination in power point tracking conditions in air. (C) Images of the water droplet contact angles on the surfaces of the perovskite (reference) and perovskite/SubPc, Cl-SubPcF₁₂, Cl-SubPcF₆, and Cl-SubPcCl₁₂ thin films.

Further insights into the electron extraction properties of the developed ETMs were provided by steady-state photoluminescence (PL) quenching measurements of the pristine PVK film and the PVK films covered with Cl-SubPcF₁₂, Cl-SubPcF₆, and Cl-SubPcCl₁₂. As shown in Figure 4A, significant quenching of PL emission by SubPc ETMs is observed. In order to evaluate the effect of the evaporated SubPc on the charge transfer, the PL spectra and TRPL decays were measured before (bare perovskite) and after the SubPc deposition (perovskite/SubPc). From this data, the % quenching of each sample was calculated with respect to the corresponding perovskite layer. In particular, Cl-SubPcF₆ exhibits the best quenching effect (see % quenching in Supplementary Table S1), indicating that Cl-SubPcF₆ possesses the most appealing merits for extracting electrons from the PVK. In addition, time-resolved PL (TRPL) decay measurements were conducted to further analyze the carrier dynamics behaviors. As shown in Figure 4B, the TRPL curves exhibited biexponential decays with fast and slow components (Bi et al., 2016). The pristine PVK film has an average lifetime of 99.0 ns. The conformal coating of ETMs on the PVK film promotes the PL decay to 25.8 ns for PVK/Cl-SubPcF₆, 70.0 ns for PVK/Cl-SubPcF₁₂ and 55.7 ns for PVK/Cl-SubPcCl₁₂, respectively. Thus, it can be concluded that the carriers generated from the PVK absorber are extracted more efficiently by the Cl-SubPcF₆, confirming that the Cl-SubPcF₆ ETM has a superior electron transfer property compared to the Cl-SubPcF₁₂ and Cl-SubPcCl₁₂.

FIGURE 4

FIGURE 4. Photoluminescence properties of PVK and PVK/SubPc samples deposited on glass: (A) PL spectra (λ_exc = 450 nm) and (B) time-resolved PL spectra (λ_exc = 640 nm, λ_em = 780 nm).

The thin film morphology of our devices was studied by scanning electron microscopy (SEM; Figure 5). A cross-sectional SEM image of the completed device (FTO/NiOx/PTAA/PVK/PEAI/SubPc/C₆₀/BCP/Cr/Au) is depicted in Figure 5A. For all ETMs, the images show a well-ordered structure where all layers, except the thin transport layers, are visible with a uniform and homogeneous morphology. Similar characteristics are observed in the reference device. On the other hand, top-view scanning electron microscope images were obtained from SubPc films deposited on top of PVK layers (Figure 5B). As shown in the images, the SubPc surface does not show any aggregation of the material, suggesting a conformal coating of the perovskite layer. Therefore, we can assume that the different performances observed with SubPcs Cl-SubPcF₁₂, Cl-SubPcF₆, and Cl-SubPcCl₁₂ mainly stem from the electronic features of the SubPc derivatives and not from differences in the morphology.

FIGURE 5

FIGURE 5. (A) Cross-sectional and (B) top-view SEM images of the reference and SubPc-containing devices.

Influence of the Cl-SubPcF₆ SubPc Layer Thickness

Once it was demonstrated that Cl-SubPcF₆ is the most efficient ETM, we explored whether lowering the SubPc layer thickness could result in an enhancement of the device performance. To this end, we prepared devices similar to those described earlier, but inserting 0.5 nm or 1 nm of SubPc between the PVK layer and C₆₀ ETM, instead of 2 nm. The J–V characteristics and the detailed photovoltaic parameters of these devices are shown in Figure 6 and summarized in Table 2, respectively. Interestingly, the PCE raised up to 13.6% upon decreasing the SubPc layer thickness from 2 to 1 nm and 0.5 nm. These higher efficiencies mainly arise from gains in the J_SC values, which, surprisingly, exceeded those of the reference device. However, the SubPc-containing devices still suffer from lower FF values than the reference. Similar to previous devices, the J–V curves recorded in the reverse scan direction reveal that these devices also exhibit negligible hysteresis, being almost 0 in the case of 0.5 nm layer thickness. On the other hand, PL (Figure 6C) and TRPL (Figure 6D) measurements of the PVK film covered 1 and 0.5 nm of Cl-SubPcF₆ confirmed the excellent ability of SubPc to extract charges by showing a strong quenching effect in the emission of the PVK as well as a shorter PL decay time.

FIGURE 6

FIGURE 6. p-i-n solar cells containing Cl-SubPcF₆/C₆₀ as the ETM with SubPc layer-thicknesses of 2 nm, 1 nm, and 0.5 nm. (A) J–V curves and (B) EQE spectra of the most efficient devices. The J–V curve and the EQE spectra of the control device (black line) were added for comparison. (C) PL spectra (λ_exc = 475 nm) and (D) time-resolved PL spectra (λ_exc = 640 nm, λ_em = 780 nm) of PVK and PVK/Cl-SubPcF₆ (2 nm, 1 and 0.5 nm) samples.

TABLE 2

TABLE 2. PV parameters of the most efficient devices extracted from the corresponding J–V curves. FWD: forward scan (from J_SC to V_OC), REV: reverse scan (from V_OC to J_SC).

Conclusion

In summary, three SubPc derivatives, namely Cl-SubPcF₆, Cl-SubPcF_12, and Cl-SubPcCl₁₂, have been developed as ETMs in PSCs. For this study, the SubPcs have been incorporated into double-layers with C₆₀ in inverted PSCs based on a triple cation solution-processed PVK (CsFAMAPbIBr). Cl-SubPcF₆ with the highest LUMO level provided better results than Cl-SubPcF₁₂ and Cl-SubPcCl₁₂. Thus, inverted PSCs using the Cl-SubPcF₆ ETM showed a leading efficiency of 13.0%, significantly higher than 10.9% for Cl-SubPcCl₁₂ and 9.9% for Cl-SubPcF₁₂. As deduced from the J–V curves and EQE spectra, as well as from the photoluminescence study, the higher performance of Cl-SubPcF₆ mainly arises from the excellent charge extraction capability of this material in comparison with that of Cl-SubPcF₁₂ and Cl-SubPcCl₁₂. Importantly, MPPT measurements revealed that the insertion of the Cl-SubPcF₆ layer between the PVK and C₆₀ significantly improves the device stability. Moreover, it was found that the reduction of SubPc layer thickness from 2 to 1 nm or 0.5 nm further increases the device efficiency, which reaches values of up to 13.6%. The SEM images of our devices also revealed that our fabrication method is very efficient for incorporating a SubPc as the electron transport layer of PSCs.

In light of these results, we strongly believe that SubPc has great potential as non-fullerene ETMs in PSCs and this work establishes fundamental guidelines in this sense. Further research employing novel SubPcs as ETM is ongoing in our laboratories.

Data Availability Statement

The original contributions presented in the study are included in the article/Supplementary Material; further inquiries can be directed to the corresponding authors.

Author Contributions

JL Synthesis, Device preparation, wrote the manuscript CM Device preparation PČ PL and PRTL studies EL-S Synthesis HK Device preparation MKN proposed the topic, directed the work, corrected the paper TT proposed the topic, directed the work, corrected the paper.

Funding

Financial support from the Spanish MINECO (CTQ 2017-85393-P) is acknowledged. By TT IMDEA Nanociencia acknowledges support from the “Severo Ochoa” Program for Centers of Excellence in R7&D (MINECO, Grant SEV 2016-0686). CM and MKN acknowledge the project German Research Foundation (DFG) (Project number 424101351)-Swiss National Foundation (SNF) (200021E_186,390).

Conflict of Interest

The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.

Publisher’s Note

All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors, and the reviewers. Any product that may be evaluated in this article, or claim that may be made by its manufacturer, is not guaranteed or endorsed by the publisher.

Acknowledgments

PČ acknowledge the funding of the Swiss-European Mobility Programme–Student Mobility for Studies’ grant. The authors acknowledge Raffaella Buonsanti for the use of the Fluorolog system and Hubert Girault for the use of the water contact-angle measurement system.

Supplementary Material

The Supplementary Material for this article can be found online at: https://www.frontiersin.org/articles/10.3389/fchem.2022.886522/full#supplementary-material

References

Best Research-Cell Efficiency Chart (2021). Best Research-Cell Efficiency Chart. Available at: https://www.nrel.gov/pv/cell-efficiency.html (Accessed December 20, 2021).

Google Scholar

Bi, D., Yi, C., Luo, J., Decoppet, J., Zhang, F., Zakeeruddin, S. M., et al. (2016). Polymer-templated Nucleation and Crystal Growth of Perovskite Films for Solar Cells with Efficiency Greater Than 21%. Nat. Energy 1, 16142. doi:10.1038/nenergy.2016.142

CrossRef Full Text | Google Scholar

Bukuroshi, E., Mizrahi, A., Gross, Z., and Bender, T. P. (2021). Variables of the Analytical Electrochemical Data Acquisition for Boron Subphthalocyanines. Eur. J. Inorg. Chem. 2021, 1090–1097. doi:10.1002/ejic.202001099

CrossRef Full Text | Google Scholar

Cai, C., Chen, S., Li, L., Yuan, Z., Zhao, X., Zhang, Y., et al. (2020). Subnaphthalocyanine Triimides: Potential Three-Dimensional Solution Processable Acceptors for Organic Solar Cells. J. Mat. Chem. C 8, 2186–2195. doi:10.1039/c9tc06238f

CrossRef Full Text | Google Scholar

Cardona, C. M., Li, W., Kaifer, A. E., Stockdale, D., and Bazan, G. C. (2011). Electrochemical Considerations for Determining Absolute Frontier Orbital Energy Levels of Conjugated Polymers for Solar Cell Applications. Adv. Mat. 23, 2367–2371. doi:10.1002/adma.201004554

CrossRef Full Text | Google Scholar

Chen, C., Zhang, S., Wu, S., Zhang, W., Zhu, H., Xiong, Z., et al. (2017). Effect of BCP Buffer Layer on Eliminating Charge Accumulation for High Performance of Inverted Perovskite Solar Cells. RSC Adv. 7, 35819–35826. doi:10.1039/C7RA06365B

CrossRef Full Text | Google Scholar

Chen, W., Han, B., Hu, Q., Gu, M., Zhu, Y., Yang, W., et al. (2021). Interfacial Stabilization for Inverted Perovskite Solar Cells with Long-Term Stability. Sci. Bull. 66, 991–1002. doi:10.1016/j.scib.2021.02.029

CrossRef Full Text | Google Scholar

Claessens, C. G., González-Rodríguez, D., Rodríguez-Morgade, M. S., Medina, A., and Torres, T. (2014). Subphthalocyanines, Subporphyrazines, and Subporphyrins: Singular Nonplanar Aromatic Systems. Chem. Rev. 114, 2192–2277. doi:10.1021/cr400088w

PubMed Abstract | CrossRef Full Text | Google Scholar

Cnops, K., Rand, B. P., Cheyns, D., Verreet, B., Empl, M. A., and Heremans, P. (2014). 8.4% Efficient Fullerene-free Organic Solar Cells Exploiting Long-Range Exciton Energy Transfer. Nat. Commun. 5, 3406–4406/6. doi:10.1038/ncomms4406

PubMed Abstract | CrossRef Full Text | Google Scholar

Cnops, K., Zango, G., Genoe, J., Heremans, P., Martinez-Diaz, M. V., Torres, T., et al. (2015). Energy Level Tuning of Non-fullerene Acceptors in Organic Solar Cells. J. Am. Chem. Soc. 137, 8991–8997. doi:10.1021/jacs.5b02808

PubMed Abstract | CrossRef Full Text | Google Scholar

Daskeviciute, S., Momblona, C., Rakstys, K., Sutanto, A. A., Daskeviciene, M., Jankauskas, V., et al. (2021). Fluorene-based Enamines as Low-Cost and Dopant-free Hole Transporting Materials for High Performance and Stable Perovskite Solar Cells. J. Mat. Chem. A 9, 301–309. doi:10.1039/d0ta08452b

CrossRef Full Text | Google Scholar

Di Giacomo, F., Fakharuddin, A., Jose, R., and Brown, T. M. (2016). Progress, Challenges and Perspectives in Flexible Perovskite Solar Cells. Energy Environ. Sci. 9, 3007–3035. doi:10.1039/C6EE01137C

CrossRef Full Text | Google Scholar

Duan, C., Zango, G., García Iglesias, M., Colberts, F. J. M., Wienk, M. M., Martínez-Díaz, M. V., et al. (2017). The Role of the Axial Substituent in Subphthalocyanine Acceptors for Bulk-Heterojunction Solar Cells. Angew. Chem. Int. Ed. 56, 148–152. doi:10.1002/anie.201608644

PubMed Abstract | CrossRef Full Text | Google Scholar

Gil-Escrig, L., Momblona, C., Sessolo, M., and Bolink, H. J. (2016). Fullerene Imposed High Open-Circuit Voltage in Efficient Perovskite Based Solar Cells. J. Mat. Chem. A 4, 3667–3672. doi:10.1039/C5TA10574A

CrossRef Full Text | Google Scholar

Guilleme, J., Mayoral, M. J., Calbo, J., Aragó, J., Viruela, P. M., Ortí, E., et al. (2015). Non-Centrosymmetric Homochiral Supramolecular Polymers of Tetrahedral Subphthalocyanine Molecules. Angew. Chem. Int. Ed. 54, 2543–2547. doi:10.1002/anie.201411272

CrossRef Full Text | Google Scholar

Habisreutinger, S. N., Noel, N. K., and Snaith, H. J. (2018). Hysteresis Index: A Figure without Merit for Quantifying Hysteresis in Perovskite Solar Cells. ACS Energy Lett. 3, 2472–2476. doi:10.1021/acsenergylett.8b01627

CrossRef Full Text | Google Scholar

Heo, J. H., Im, S. H., Noh, J. H., Mandal, T. N., Lim, C.-S., Chang, J. A., et al. (2013). Efficient Inorganic-Organic Hybrid Heterojunction Solar Cells Containing Perovskite Compound and Polymeric Hole Conductors. Nat. Phot. 7, 486–491. doi:10.1038/nphoton.2013.80

CrossRef Full Text | Google Scholar

Hodes, G. (2013). Perovskite-based Solar Cells. Science 342, 317–318. doi:10.1126/science.1245473

PubMed Abstract | CrossRef Full Text | Google Scholar

Huang, T., Chen, H., Feng, J., Zhang, A., Jiang, W., He, F., et al. (2019). Rylene Annulated Subphthalocyanine: A Promising Cone-Shaped Non-fullerene Acceptor for Organic Solar Cells. ACS Mater. Lett. 1, 404–409. doi:10.1021/acsmaterialslett.9b00221

CrossRef Full Text | Google Scholar

Huang, X., Hu, M., Zhao, X., Li, C., Yuan, Z., Liu, X., et al. (2019). Subphthalocyanine Triimides: Solution Processable Bowl-Shaped Acceptors for Bulk Heterojunction Solar Cells. Org. Lett. 21, 3382–3386. doi:10.1021/acs.orglett.9b01130

PubMed Abstract | CrossRef Full Text | Google Scholar

Imahori, H., and Fukuzumi, S. (2004). Porphyrin- and Fullerene-Based Molecular Photovoltaic Devices. Adv. Funct. Mat. 14, 525–536. doi:10.1002/adfm.200305172

CrossRef Full Text | Google Scholar

Kaltenbrunner, M., Adam, G., Głowacki, E. D., Drack, M., Schwödiauer, R., Leonat, L., et al. (2015). Flexible High Power-Per-Weight Perovskite Solar Cells with Chromium Oxide-Metal Contacts for Improved Stability in Air. Nat. Mater 14, 1032–1039. doi:10.1038/nmat4388

PubMed Abstract | CrossRef Full Text | Google Scholar

Labella, J., Momblona, C., Klipfel, N., Kanda, H., Kinge, S., Nazeeruddin, M. K., et al. (2021). Subphthalocyanine-based Electron-Transport Materials for Perovskite Solar Cells. J. Mat. Chem. C 9, 16298–16303. Ahead of Print. doi:10.1039/d1tc02600c

CrossRef Full Text | Google Scholar

Leijtens, T., Eperon, G. E., Pathak, S., Abate, A., Lee, M. M., and Snaith, H. J. (2013). Overcoming Ultraviolet Light Instability of Sensitized TiO2 with Meso-Superstructured Organometal Tri-halide Perovskite Solar Cells. Nat. Commun. 4, 3885/1–3885/8. doi:10.1038/ncomms3885

CrossRef Full Text | Google Scholar

Li, D., Zhang, D., Lim, K. S., Hu, Y., Rong, Y., Mei, A., et al. (2021). A Review on Scaling up Perovskite Solar Cells. Adv. Funct. Mat. 31, 2008621. doi:10.1002/adfm.202008621

CrossRef Full Text | Google Scholar

Li, L. L., and Diau, E. W. (2013). Porphyrin-sensitized Solar Cells. Chem. Soc. Rev. 42, 291–304. doi:10.1039/C2CS35257E

PubMed Abstract | CrossRef Full Text | Google Scholar

Lian, X., Chen, J., Shan, S., Wu, G., and Chen, H. (2020). Polymer Modification on the NiOx Hole Transport Layer Boosts Open-Circuit Voltage to 1.19 V for Perovskite Solar Cells. ACS Appl. Mat. Interfaces 12, 46340–46347. doi:10.1021/acsami.0c11731

PubMed Abstract | CrossRef Full Text | Google Scholar

Lin, X., Cui, D., Luo, X., Zhang, C., Han, Q., Wang, Y., et al. (2020). Efficiency Progress of Inverted Perovskite Solar Cells. Energy Environ. Sci. 13, 3823–3847. doi:10.1039/d0ee02017f

CrossRef Full Text | Google Scholar

Lu, H., Krishna, A., Zakeeruddin, S. M., Grätzel, M., and Hagfeldt, A. (2020). Compositional and Interface Engineering of Organic-Inorganic Lead Halide Perovskite Solar Cells. iScience 23, 101359. doi:10.1016/j.isci.2020.101359

PubMed Abstract | CrossRef Full Text | Google Scholar

Luo, D., Su, R., Zhang, W., Gong, Q., and Zhu, R. (2020). Minimizing Non-radiative Recombination Losses in Perovskite Solar Cells. Nat. Rev. Mat. 5, 44–60. doi:10.1038/s41578-019-0151-y

CrossRef Full Text | Google Scholar

Mayoral, M. J., Guilleme, J., Calbo, J., Aragó, J., Aparicio, F., Ortí, E., et al. (2020). Dual-Mode Chiral Self-Assembly of Cone-Shaped Subphthalocyanine Aromatics. J. Am. Chem. Soc. 142, 21017–21031. doi:10.1021/jacs.0c07291

PubMed Abstract | CrossRef Full Text | Google Scholar

Said, A. A., Xie, J., and Zhang, Q. (2019). Recent Progress in Organic Electron Transport Materials in Inverted Perovskite Solar Cells. Small 15, 1900854. doi:10.1002/smll.201900854

PubMed Abstract | CrossRef Full Text | Google Scholar

Snaith, H. J. (2018). Present Status and Future Prospects of Perovskite Photovoltaics. Nat. Mater 17, 372–376. doi:10.1038/s41563-018-0071-z

PubMed Abstract | CrossRef Full Text | Google Scholar

Urbani, M., de la Torre, G., Nazeeruddin, M. K., and Torres, T. (2019). Phthalocyanines and Porphyrinoid Analogues as Hole- and Electron-Transporting Materials for Perovskite Solar Cells. Chem. Soc. Rev. 48, 2738–2766. doi:10.1039/c9cs00059c

PubMed Abstract | CrossRef Full Text | Google Scholar

Vasilopoulou, M., Fakharuddin, A., Coutsolelos, A. G., Falaras, P., Argitis, P., Yusoff, A. R. B. M., et al. (2020). Molecular Materials as Interfacial Layers and Additives in Perovskite Solar Cells. Chem. Soc. Rev. 49, 4496–4526. doi:10.1039/c9cs00733d

PubMed Abstract | CrossRef Full Text | Google Scholar

Walter, M. G., Rudine, A. B., and Wamser, C. C. (2010). Porphyrins and Phthalocyanines in Solar Photovoltaic Cells. J. Porphyr. Phthalocyanines 14, 759–792. doi:10.1142/S1088424610002689

CrossRef Full Text | Google Scholar

Wu, S., Zhang, J., Li, Z., Liu, D., Qin, M., Cheung, S. H., et al. (2020). Modulation of Defects and Interfaces through Alkylammonium Interlayer for Efficient Inverted Perovskite Solar Cells. Joule 4, 1248–1262. doi:10.1016/j.joule.2020.04.001

CrossRef Full Text | Google Scholar

Xu, J., Buin, A., Ip, A. H., Li, W., Voznyy, O., Comin, R., et al. (2015). Perovskite-fullerene Hybrid Materials Suppress Hysteresis in Planar Diodes. Nat. Commun. 6, 7081. doi:10.1038/ncomms8081

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhang, C., Nakano, K., Nakamura, M., Araoka, F., Tajima, K., and Miyajima, D. (2020). Noncentrosymmetric Columnar Liquid Crystals with the Bulk Photovoltaic Effect for Organic Photodetectors. J. Am. Chem. Soc. 142, 3326–3330. doi:10.1021/jacs.9b12710

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhang, H., Nazeeruddin, M. K., and Choy, W. C. H. (2019). Perovskite Photovoltaics: The Significant Role of Ligands in Film Formation, Passivation, and Stability. Adv. Mat. 31, 1805702. doi:10.1002/adma.201805702

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhao, D., Zhu, Z., Kuo, M. Y., Chueh, C. C., and Jen, A. K. Y. (2016). Hexaazatrinaphthylene Derivatives: Efficient Electron-Transporting Materials with Tunable Energy Levels for Inverted Perovskite Solar Cells. Angew. Chem. Int. Ed. 55, 8999–9003. doi:10.1002/anie.201604399

PubMed Abstract | CrossRef Full Text | Google Scholar