Oxygen evolution reaction (OER) has attracted great attention as an important half-reaction in the electrochemical splitting of water for green hydrogen production. However, the inadequacy of highly efficient and stable electrocatalysts has impeded the development of this technology. Amorphous materials with long-range disordered structures have exhibited superior electrocatalytic performance compared to their crystalline counterparts due to more active sites and higher structural flexibility. This review summarizes the preparation methods of amorphous materials involving oxides, hydroxide, phosphides, sulfides, and their composites, and introduces the recent progress of amorphous OER electrocatalysts in acidic and alkaline media. Finally, the existing challenges and future perspectives for amorphous electrocatalysts for OER are discussed. Therefore, we believe that this review will guide designing amorphous OER electrocatalysts with high performance for future energy applications.
Introduction
Current fossil fuel-based energy production has caused serious problems such as climate change and environmental pollution. To solve these problems, the demand for clean and renewable energy sources have been increased. Among the various energy sources, hydrogen is one of the most promising candidates that can substitute fossil fuels because of its abundance, high energy density and zero-emission combustion properties (Park et al., 2019). Most of the hydrogen is mainly produced by a steam reforming of natural gas, which emits a lot of greenhouse gases (Lim et al., 2022), therefore, it should be accompanied by the development of clean hydrogen production systems.
Water electrolysis has been garnering attention as the clean hydrogen production system that converts surplus electrical energy into chemical energy by splitting the water into hydrogen and oxygen without any pollutants. The water electrolysis consists of two coupled half-reactions, which are the hydrogen evolution reaction (HER) in the cathode and the oxygen evolution reaction (OER) in the anode. Between the reactions, OER requires a higher overpotential than HER due to the sluggish kinetics of the complicated reaction mechanism, and significantly lowers the efficiency of the overall water electrolysis system (Guo et al., 2022). Therefore, the development of highly active OER electrocatalysts is one of the most important steps to improve the efficiency of the water electrolysis system and replace fossil fuels with hydrogen.
Over the past few years, substantial efforts have been devoted to enhancing OER activities of the electrocatalysts, for example, the introduction of hetero atoms into the lattice or on the surface to enhance the intrinsic kinetic activity (Ramesh et al., 2018; Youk et al., 2019), and structural engineering of the electrocatalysts to increase the surface area and/or mass transport property (Chen et al., 2018). Among them, the development of amorphous-structured OER electrocatalysts is considered a promising strategy for enhancing the activity; it is based on that the surface of crystalline materials is electrocatalytically activated while becoming amorphous during OER (Tang et al., 2022).
Amorphous materials with long-range disordered structures have exhibited superior electrocatalytic OER performance compared to their crystalline counterparts due to the following advantages (Figure 1A). First, the amorphous structure has a large number of active sites from rich dangling bonds and coordinatively unsaturated sites (Ying and Wang, 2021). Next, the atomic composition can be controlled over a wide range, which makes it possible to find the optimal composition for the best activity (Lemoine et al., 2021). In addition, abundant defects in amorphous materials can improve the diffusion property that facilitates the transportation of reactants and products (Zhai et al., 2021). Moreover, amorphous materials have higher structural flexibility through facile morphology engineering (Zhang D et al., 2021).
FIGURE 1. (A) Advantages of amorphous electrocatalysts compared to crystalline counterparts in OER (B) Precipitating metal nitrate deposition synthesis of amorphous metal oxyhydroxides and TEM of CoFe oxyhydroxide, reproduced with permission from Kim et al. (2019) (C) Surface valence states and electrocatalytic performance of amorphous NiFe alloy, reproduced with permission from Cai et al. (2020).
In this review, we summarize the various preparation methods of amorphous materials involving oxides, hydroxide, phosphides, sulfides, and their composites, and introduce the latest developments of amorphous OER electrocatalysts in acidic and alkaline media. Finally, the existing challenges facing the development of amorphous OER electrocatalysts and future perspectives are discussed. This review will provide systematic insights and in-depth understanding, and therefore guide the design strategy of amorphous OER electrocatalysts with high performance for future energy applications.
Amorphous electrocatalysts in alkaline conditions
In alkaline electrolytes, earth-abundant metal catalysts (i.e., non-noble metal) have captured great attention in OER electrocatalysts due to their low cost, excellent cyclability, and tunable structures (Xu et al., 2019). Especially amorphous transition metal oxides have exhibited high OER activities, thus they have been considered promising electrocatalysts in alkaline media (Smith et al., 2013a; Indra et al., 2014). For example, photochemical metal-organic decomposition (PMOD) has been used to prepare amorphous Fe-based metal oxide electrocatalysts on a certain substrate (Smith et al., 2013b). Fe metal-organic precursor films are prepared on fluorine-doped tin oxide (FTO) substrates and are directly photolyzed into amorphous Fe2O3 by irradiation of 185- and 254 nm. PMOD also can prepare various types of amorphous metal oxides with different compositions. Amorphous mixed-metal oxides of Fe, Co., and Ni (a-FeCoNiOx) achieve an overpotential of 230 mV and Tafel slop of 31 mV dec−1 in 0.1 M KOH.
The addition of hetero atoms breaks the crystallization of perovskite oxides (ABO3) to amorphous phases, generating rich dangling bonds and defects for enhanced OER performance (Yang et al., 2018; Guo et al., 2019). Shao and co-workers introduced FeCl3 for both top-down and bottom-up amorphization of LaNiO3 by the loss of La ion (Chen G. et al., 2019). For the top-down synthesis of amorphous LaNiFe hydroxide, crystalline LaNiO3 was firstly prepared by sol-gel reaction of La and Ni nitrates with EDTA-citrate complexing agent in an aqueous solution. The evaporation at 90°C yielded a resultant gel followed by heat treatment at 800°C to form bulk perovskite powder. The powder was grounded and added in solution with FeCl3 with ultrasonication, resulting in amorphous LaNiFe hydroxide. For bottom-up synthesis, La, Fe, and Ni nitrates were dissolved in water and precipitated by excess KOH solution, preparing amorphous LaNiFe hydroxide. Fe octahedra interstitials transform corner-shared octahedra structures of crystallites into edge-shared octahedra with high-valence Ni3+ sites. Furthermore, the X-ray absorption spectrum (XAS) reveals the valence state of +3 in the top-down sample, but of +2 in the bottom-up sample. Enhanced OER activity is attributed to the disordered structures that can bond OH− with bridging and terminal geometries. Especially, amorphous NiFeOx prepared by the top-down approach shows an extremely low overpotential of 189 mV at 10 mA cm−2, which is lower than that of the crystalline counterpart of 338 mV at 10 mA cm−2.
Yu and co-workers exploited a co-precipitation method for scalable synthesis of amorphous metal oxides (Duan et al., 2019b). The supersaturated solution containing Ni, Fe, and Mo precursors precipitated into NiFeMo oxides 515 g of catalysts in one batch within minutes. They also found that the surfaces of the amorphous metal oxides are quickly self-reconstructed during the OER process into metal oxyhydroxides, but the crystalline counterpart shows sluggish reconstruction. Amorphous NiFeMo oxyhydroxide layers have rich oxygen vacancies, enhancing OER activity with 280 mV overpotential at 10 mA cm−2 in 0.1 M KOH. Precipitating metal nitrate precursors also can directly transform to amorphous Fe, Co., and Ni-based metal oxyhydroxide on the various substrates (Thangavel et al., 2021). The metal nitrate solutions dropped on the substrates such as FTO, Ni foam (NF), and carbon felt (CF) are precipitated to metal hydroxides in KOH solution and the sequential electrooxidation process synthesizes metal oxyhydroxides (Figure 1B). This method allows the easy control of metal compositions (Kim et al., 2019). Among prepared catalysts with various compositions, the NiFe (2:8) electrocatalyst on NF shows the best OER performance with a low overpotential of 280 mV at 100 mA cm−2 in 1.0 M KOH.
To understand the mechanism of the reconstruction of oxides, Xu and co-workers investigated the correlation of Ni substitution and reconstruction of metastable multi-metal oxides to amorphous oxyhydroxide surface via density functional theory (DFT) calculation and experimental characterizations (Duan et al., 2019a). They prepared amorphous ZnCo2-xNixO4 by adding Ni precursor to the solution containing Zn and Co. precursors for crystalline ZnCo2O4, which was dried at 170°C and calcined at 300°C. The replacement of Ni with Co. in ZnCo2O4 distorts the crystalline structure, resulting in metastable spinel oxides. The component ratio is tailored in ZnCo2-xNixO4 with different x, which shifts the relative position of O p-band versus the metal d-band. The increase of x values (x > 0.4) renders a higher O p-band center than the metal d-band, leading to active lattice oxygen that is reconstructible into oxyhydroxide on the surface after OER cycling. The ZnCo1.2Ni0.8O4 catalyst exhibits decreased overpotential from 391 to 313 mV at 25 μA cm−2 after amorphization, which is comparable to IrO2.
Highly active metal oxyhydroxides also can be converted from unstable metal sulfides or phosphides during the anodic oxygen evolution (Cai et al., 2017; Fan et al., 2018; Che et al., 2019; Huang et al., 2020). For example, Wang and co-workers prepared amorphous Ni-based bimetallic sulfide nanosheets with porosity by sulfidation of metal organic frameworks (Qin et al., 2019). First, NiCo-based metal organic framework (MOF) was synthesized using hydrothermal method of the solution containing Ni and Co. nitrates and 2-methyl imidazole at 140°C with same molar ratio of Ni and Co. Then, NiCo-MOF was sulfidized to amorphous holey NiCoS nanosheets in the ethanol solution with thioacetamide solution at 90°C, which can easily control pore size and density via tunable sulfidation time. The NiCoS phase is reconstructed into Ni-Co oxyhydroxide during the OER process. The synergistic effect of 2D morphology, electroactive Ni-Co oxyhydroxides, and unsaturated amorphous structures improve OER activity with an overpotential of 280 mV at 20 mA cm−2 in 1.0 M KOH, which is lower than that of crystalline NiCoO nanosheet (370 mV) and IrO2 (320 mV). Furthermore, Driess and co-workers reported an amorphous CoP catalyst by a hot injection method (Beltrán-Suito et al., 2019). They prepared two types of CoP materials by using the hot injection and pyrolysis of the molecular precursor. The product from hot injection has amorphous phases, whereas the pyrolyzed product has highly crystalline phases. Both amorphous and crystalline CoP catalysts readily transform to Co. oxyhydroxides on their surface as a result of the dissolution of p species. Inner metallic CoP core contributes high electronic conductivity from the active surface to the electrode substrates. More flexible surface and higher active sites of amorphous CoP than that of crystalline promote OER activity as well as HER in the alkaline electrolyte, and also show stable performance over 100 h.
Wu and co-workers employed amorphous iron borate (am-Fe-Bi) nanolattices which are capable of boosting OER (Zhao et al., 2018). Am-Fe-Bi electrocatalysts were self-assembled for the fabrication of nanolattices on NF and cross-linked on the surface via hydrothermal methods. Am-Fe-Bi have suitable values of d-band center and nanolattices expose more active sites, resulting in multi-functional electrocatalysts involving hydrogen and oxygen evolution, and oxygen reduction. The am-Fe-Bi shows superior OER activity with only 158 mV overpotential at 10 mV cm−2 that surpass RuO2 (228 mV at 10 mV cm−2)
Liu and co-workers prepared porous amorphous NiFe alloy with various molar ratios of Ni to Fe for improving OER performances (Cai et al., 2020). They simply synthesized the amorphous NiFe catalysts by reacting Ni and Fe acetates with the NaBH4 aqueous solution at room temperature and ambient pressure. The different stoichiometry of Ni and Fe precursors easily controlled the molar ratio of Ni to Fe of the alloy. The amorphous structures expose more active sites by applying anodic potential, which is attributed to their short-range ordering. The degree of surface oxidation of Ni and Fe is higher for the amorphous catalysts than for the crystalline counterpart (Figure 1C). Among the prepared catalysts, amorphous Ni3Fe has the highest OER activity with an overpotential of 242 mV at 10 mA cm−2 that is and excellent durability in 1.0 M KOH.
Mixed phase boundaries of amorphous and crystalline phases combine the benefits of rich defects, structural flexibility, and enhanced activity of the amorphous phase with stable crystallite in OER (Zhou and Fan, 2020). Song and co-workers investigated heterointerfaces of amorphous-crystalline phase boundary of Co2B for OER electrocatalysts (Han et al., 2019). Crystalline Co2B catalyst has been prepared by the reaction of CoCl2 and NaBH4 in 0.1 NaOH solution, and then precipitated powder was pyrolyzed at 600°C under Ar. Adding appropriate amounts of NH4F to CoCl2 solution during the synthesis procedure of Co2B led to fluorin-doped Co2B (F-Co2B). The fluorination of the catalyst surface is employed for the partial amorphization of Co2B, which break crystalline structures by incorporating F. The amorphous-crystalline heterointerfaces decrease energy barriers and increase the charge carrier density, resulting in the promotion of the overall OER kinetics. The engineering of the surface to partial amorphism enhances OER performance of Co2B with a superior overpotential of 320 mV at 10 mA cm−2 and the Tafel slope of 32 mV dec−1 compared with crystalline Co2B (370 and 44 mV dec−1) and RuO2 (350 and 128 mV dec−1)
Amorphous electrocatalysts in acidic conditions
A variety of transition metal-based catalysts has been developed for OER in alkaline electrolytes, whereas catalyst materials in acid electrolytes have been limited due to their instability in acid. Therefore, noble metal catalysts have been extensively explored to be studied in acid conditions. Amorphous Ru-based catalysts have attracted remarkable attention for OER in acid (Delmer et al., 2008; Zhang L et al., 2021). Huang and co-workers reported theoretical results by DFT that the locally flexible Te-bonding configuration of amorphous RuTe2 lattices induces the distortion-strain sensitizing Te-pπ coupling (Wang et al., 2019). Amorphous RuTe2 porous nanorods were prepared by hydrothermal synthesis at 180°C, in which Cl3H18N6Ru and K2TeO3 were used as precursors. The distorted Ru-Te bonding enhances electron transfer of Ru sites as well as OER performances (Figure 2A). Amorphous RuTe2 porous nanorods exhibited high OER activity with an overpotential of 245 mV in 0.5 M H2SO4 which is higher than that of crystalline ReTe2 (442 mV)and Ir/C (323 mV). Amorphous catalyst also achieved a low voltage of 1.52 V at 10 mA cm−2 in water splitting as both anode and cathode in the identical acid solution. Reconstructed amorphization of RuO2 promotes OER activity and stability in the harsh acidic condition (Zhuang et al., 2019). Zhang and co-workers prepared amorphous RuOx shells on the surface of Ru or Ru-based alloys via electrooxidation process in acid (An et al., 2022). The strong bond strength of Ru leads to the reconstruction of stable amorphous RuOx and inhibits steady-state dissolution on the surface. Among various Ru-based alloys (e.g., RuMn, RuCo, RuZn, and RuCr), amorphous RuOx on the RuMn surface enhances its durability, which is stable for 720 h at 10 mA cm−2 in 0.5 M H2SO4.
FIGURE 2. (A) Schematic diagram of the electronic activity enhancement, DFT calculation for acidic OER, and electrochemical characterization of a-RuTe2 nanorods, reproduced with permission from Wang et al. (2019) (B) Synthesis of amorphous Ir nanosheets, and their structural and electrochemical characterization, reproduced with permission from Wu et al. (2019) (C) Atomic coordination measurement and electrocatalytic performance of rutile IrO2 and amorphous Li-IrOx, reproduced with permission from Gao et al. (2019) (D) Structural transition during amorphization of δ-MnO2, reproduced with permission from Huynh et al. (2014).
Amorphous Ir-based materials also achieve significantly enhanced anodic performance in OER. For example, Li and co-workers have demonstrated the synthesis of amorphous noble metal nanosheets by the mixtures of metal acetylacetonates (acac) and alkali salts (Figure 2B). They prepared the homogeneous mixture of M (acac)3 (M = Ir, Ru, or Rh) and KNO3 dissolved in ethanol and water solution and dried for the mixture powder. It was thermal-treated at 300°C under air condition. Removal of KNO3 salt by ethanol/water washing yielded noble metal nanosheets. The series of bi-, and trimetallic amorphous nanosheets also have been able to be prepared based on Ir, Rh, and Ru with same procedure, among which amorphous Ir nanosheet exhibited superior OER performance in acid media; its overpotential is 255 mV at 10 mA cm−2 which is lower than that of crystalline Ir nanosheet (280 mV), RuO2 (301 mV), and IrO2 (373 mV) (Wu et al., 2019). Distorted Ir-O bonds in amorphous Ir oxides can affect oxidation states of Ir, and thus boost OER activity (Morimitsu and Oshiumi, 2009; Lee et al., 2018). Photochemically prepared amorphous IrOx exhibits higher OER activity than crystalline IrOx (Smith et al., 2014). Photoactive precursor, Ir (acac)3, was decomposed by light (λ < 254 nm) to the amorphous phase at room temperatures, which reaches a Tafel slope of 34 mV dec−1 and an overpotential of 220 mV at 10 mA cm−2 in 1.0 M H2SO4.
Hetero atoms have been also employed for the amorphization of crystalline IrO2 (Willinger et al., 2017). Liu and co-workers investigated the exploitation of alkali ions, especially lithium ion, to break the long-range order of rigid crystal structure of rutile IrO2, resulting in amorphous Li-IrOx. IrCl3 as a precursor reacted with LiOH in an aqueous solution followed by drying at 90°C, and then the resultant powder was calcined at 400°C under air condition, resulting in Li-IrOx with the molar ratio of Li to Ir of 0.6:1. Flexible disordered [IrO6] octahedrons of Li-IrOx shrink Ir-O bond and promotes outstanding OER activity with higher Ir oxidation states in 0.5 M H2SO4; an overpotential of Li-IrOx (200 mV at 10 mA cm−2) is lower than rutile IrO2 (300 mV) (Figure 2C) (Gao et al., 2019).
Dissolution of non-noble metal from the noble/non-noble composite oxides can successfully achieve amorphization of oxides (Chen Y. et al., 2019). Cherevko and co-workers prepared highly active amorphous IrOx by leaching non-noble elements in Ir-based perovskite materials and compared it with crystalline IrO2 and perovskite-based materials (Br2PrIrO6 and SrIrO3). They proposed a stability number (S-number) to evaluate the stability via the matric characterization of the relationship between the evolved oxygen and the dissolved Ir of given catalysts; S-number indicates the amount of evolved oxygen per Ir atom lost in electrolytes. They also suggested the mechanism of the participation of activated oxygen for the formation of oxygen vacancies and boosting the activity of amorphous IrOx (Geiger et al., 2018).
Although non-noble metal catalysts are unstable in acid conditions, some researchers have discovered non-noble metal-based amorphous materials with excellent OER performance. For example, amorphous Mn-based oxides have been kinetically stable in acidic electrolytes due to self-healing properties to compensate for their dissolution (Huynh et al., 2014). Nocera and co-workers reported that sequential cathodization and anodization of δ-MnO2 generates disordered δ-MnO2 involving a morphological transition from plates to needles (Figure 2D) (Huynh et al., 2014). Activated amorphous δ-MnO2 on FTO shows two orders of magnitude higher for OER than untreated δ-MnO2 in the acidic condition (pH = 2.5) at an overpotential of 600 mV at 0.1 mA cm−2, which is much lower than that of unactivated MnOx (990 mV). In addition, Xiong and co-workers investigated highly active amorphous metallic NiFeP for OER in both alkaline and acid electrolytes (Hu et al., 2017). The metallic bonds of bulk electrocatalysts enhance macroscopic electrical conductivity, resulting in promoted OER reaction kinetics due to low resistance from the surface to current collectors. Coordinatively unsaturated Ni, Fe, and p in amorphous structures contribute to the increase of active sites in which the generated phosphate boosts the intrinsic activity of Fe sites. Amorphous NiFeP achieves an overpotential of 540 mV at 10 mA cm−2 and stable performance for over 30 h in the acid electrolyte.
Conclusion and outlook
This review summarized the recent advances in amorphous materials as OER electrocatalysts. We reviewed the synthesis of various amorphous materials (e.g., oxides, oxyhydroxides, sulfides, phosphides, and alloys) and their OER performances in acid and alkaline conditions. The structural flexibility of amorphous materials provides the possibility to expose more active sites for large electrochemical surface area, and geometrically boosts charge and mass transfer, leading to remarkably improved OER activity compared to crystalline counterparts. The rich intrinsic defect and dangling bonds of amorphous structures also enhance electrocatalytic properties.
Despite the promising achievements of amorphous electrocatalysts, some challenging issues still remain to be resolved. 1) The thermal instability of amorphous phases has limited the methodologies to design efficient catalysts with precise control of morphology (i.e., nanostructure, particle morphology and size, and porous structure) and chemical composition. In this aspect, the systematic research that is possible to successfully fabricate amorphous materials is highly required for designing optimized OER catalysts. 2) The exact active sites in amorphous electrocatalysts remain elusive which means that further studies are to be carried out to understand their reaction and mechanism. Unclarified active sites of amorphous materials are ascribed to in-situ transformations of amorphous materials into new amorphous phases during the electrooxidation process. Moreover, unclear atomic arrangements and structural models also make it difficult to elucidate the OER mechanism on amorphous structures through simulations. Hence, for a greater understanding of the active sites of amorphous materials, the cooperation of multiple measurement techniques (e.g., STEM, XAFS, Raman, and XPS) is highly desirable. Furthermore, operando characterizations should be useful to investigate in-situ surface amorphization of electrocatalysts in OER operation. Fulfilling rational synthesis methods and a clear understanding of the electrocatalytic properties of amorphous materials can extend their merits beyond OER to electrocatalytic applications such as the oxygen reduction reaction, CO2 reduction, and N2 reduction.
Author contributions
All authors listed have made a substantial, direct, and intellectual contribution to the work and approved it for publication.
Funding
This work was supported by a National Research Foundation of Korea (NRF) grant funded by the Korean government (MSIT) (NRF-2022R1F1A1076462). This work was also supported by “Research Base Construction Fund Support Program” funded by Jeonbuk National University in 2022.
Conflict of interest
The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.
Publisher’s note
All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article, or claim that may be made by its manufacturer, is not guaranteed or endorsed by the publisher.
References
An, L., Yang, F., Fu, C., Cai, X., Shen, S., Xia, G., et al. (2022). A functionally stable RuMn electrocatalyst for oxygen evolution reaction in acid. Adv. Funct. Mat. 32 (27), 2200131. doi:10.1002/adfm.202200131
Beltrán-Suito, R., Menezes, P. W., and Driess, M. (2019). Amorphous outperforms crystalline nanomaterials: Surface modifications of molecularly derived cop electro(pre)catalysts for efficient water-splitting. J. Mat. Chem. A 7 (26), 15749–15756. doi:10.1039/c9ta04583j
Cai, P., Huang, J., Chen, J., and Wen, Z. (2017). Oxygen-containing amorphous cobalt sulfide porous nanocubes as high‐activity electrocatalysts for the oxygen evolution reaction in an alkaline/neutral medium. Angew. Chem. Int. Ed. 17 (56), 4858–4861. doi:10.1002/anie.201701280
Cai, W., Chen, R., Yang, H., Tao, H. B., Wang, H.-Y., Gao, J., et al. (2020). Amorphous versus crystalline in water oxidation catalysis: A case study of NiFe alloy. Nano Lett. 20 (6), 4278–4285. doi:10.1021/acs.nanolett.0c00840
Che, Q., Li, Q., Tan, Y., Chen, X., Xu, X., and Chen, Y. (2019). One-step controllable synthesis of amorphous (Ni-Fe)sx/NiFe(OH)y hollow microtube/sphere films as superior bifunctional electrocatalysts for quasi-industrial water splitting at large-current-density. Appl. Catal. B Environ. 246, 337–348. doi:10.1016/j.apcatb.2019.01.082
Chen, B., Zhang, Z., Kim, S., Lee, S., Lee, J., Kim, W., et al. (2018). Ostwald ripening driven exfoliation to ultrathin layered double hydroxides nanosheets for enhanced oxygen evolution reaction. ACS Appl. Mat. Interfaces 10 (51), 44518–44526. doi:10.1021/acsami.8b16962
Chen G, G., Zhu, Y., Chen, H. M., Hu, Z., Hung, S. F., Ma, N., et al. (2019). An amorphous nickel-iron-based electrocatalyst with unusual local structures for ultrafast oxygen evolution reaction. Adv. Mat. 31 (28), 1900883. doi:10.1002/adma.201900883
Chen Y, Y., Li, H., Wang, J., Du, Y., Xi, S., Sun, Y., et al. (2019). Exceptionally active iridium evolved from a pseudo-cubic perovskite for oxygen evolution in acid. Nat. Commun. 10 (1), 572. doi:10.1038/s41467-019-08532-3
Delmer, O., Balaya, P., Kienle, L., and Maier, J. (2008). Enhanced potential of amorphous electrode materials: Case study of RuO2. Adv. Mat. 20 (3), 501–505. doi:10.1002/adma.200701349
Duan, Y., Sun, S., Sun, Y., Xi, S., Chi, X., Zhang, Q., et al. (2019a). Mastering surface reconstruction of metastable spinel oxides for better water oxidation. Adv. Mat. 31 (12), 1807898. doi:10.1002/adma.201807898
Duan, Y., Yu, Z. Y., Hu, S. J., Zheng, X. S., Zhang, C. T., Ding, H. H., et al. (2019b). Scaled‐up synthesis of amorphous NiFeMo oxides and their rapid surface reconstruction for superior oxygen evolution catalysis. Angew. Chem. Int. Ed. 58 (44), 15772–15777. doi:10.1002/anie.201909939
Fan, K., Zou, H., Lu, Y., Chen, H., Li, F., Liu, J., et al. (2018). Direct observation of structural evolution of metal chalcogenide in electrocatalytic water oxidation. ACS Nano 12 (12), 12369–12379. doi:10.1021/acsnano.8b06312
Gao, J., Xu, C.-Q., Hung, S.-F., Liu, W., Cai, W., Zeng, Z., et al. (2019). Breaking long-range order in iridium oxide by alkali ion for efficient water oxidation. J. Am. Chem. Soc. 141 (7), 3014–3023. doi:10.1021/jacs.8b11456
Geiger, S., Kasian, O., Ledendecker, M., Pizzutilo, E., Mingers, A. M., Fu, W. T., et al. (2018). The stability number as a metric for electrocatalyst stability benchmarking. Nat. Catal. 1 (7), 508–515. doi:10.1038/s41929-018-0085-6
Guo, Q., Li, X., Wei, H., Liu, Y., Li, L., Yang, X., et al. (2019). Sr, Fe, Co-doped perovskite oxides with high performance for oxygen evolution reaction. Front. Chem. 7, 224. doi:10.3389/fchem.2019.00224
Guo, T., Li, L., and Wang, Z. (2022). Recent development and future perspectives of amorphous transition metal-based electrocatalysts for oxygen evolution reaction. Adv. Energy Mat. 12 (24), 2200827. doi:10.1002/aenm.202200827
Han, H., Choi, H., Mhin, S., Hong, Y.-R., Kim, K. M., Kwon, J., et al. (2019). Advantageous crystalline-amorphous phase boundary for enhanced electrochemical water oxidation. Energy Environ. Sci. 12 (8), 2443–2454. doi:10.1039/c9ee00950g
Hu, F., Zhu, S., Chen, S., Li, Y., Ma, L., Wu, T., et al. (2017). Amorphous metallic NiFeP: A conductive bulk material achieving high activity for oxygen evolution reaction in both alkaline and acidic media. Adv. Mat. 29 (32), 1606570. doi:10.1002/adma.201606570
Huang, H., Cho, A., Kim, S., Jun, H., Lee, A., Han, J. W., et al. (2020). Structural design of amorphous CoMoP with abundant active sites and synergistic catalysis effect for effective water splitting. Adv. Funct. Mat. 30 (43), 2003889. doi:10.1002/adfm.202003889
Huynh, M., Bediako, D. K., and Nocera, D. G. (2014). A functionally stable manganese oxide oxygen evolution catalyst in acid. J. Am. Chem. Soc. 136 (16), 6002–6010. doi:10.1021/ja413147e
Indra, A., Menezes, P. W., Sahraie, N. R., Bergmann, A., Das, C., Tallarida, M., et al. (2014). Unification of catalytic water oxidation and oxygen reduction reactions: Amorphous beat crystalline cobalt iron oxides. J. Am. Chem. Soc. 136 (50), 17530–17536. doi:10.1021/ja509348t
Kim, Y. K., Kim, J. H., Jo, Y. H., and Lee, J. S. (2019). Precipitating metal nitrate deposition of amorphous metal oxyhydroxide electrodes containing Ni, Fe, and Co for electrocatalytic water oxidation. ACS Catal. 9 (10), 9650–9662. doi:10.1021/acscatal.9b02701
Lee, H., Kim, J. Y., Lee, S. Y., Hong, J. A., Kim, N., Baik, J., et al. (2018). Comparative study of catalytic activities among transition metal-doped IrO2 nanoparticles. Sci. Rep. 8 (1), 16777. doi:10.1038/s41598-018-35116-w
Lemoine, K. v., Gohari-Bajestani, Z., Moury, R., Terry, A., Guiet, A., Grenèche, J.-M., et al. (2021). Amorphous iron-manganese oxyfluorides, promising catalysts for oxygen evolution reaction under acidic media. ACS Appl. Energy Mat. 4 (2), 1173–1181. doi:10.1021/acsaem.0c02417
Lim, H. S., Kim, M., Kim, Y., Kim, H. S., Kang, D., Lee, M., et al. (2022). Sustainable hydrogen production from water splitting on a Co3O4@ LaCoO3 core-shell redox catalyst. ACS Appl. Energy Mat. 5 (7), 8437–8442. doi:10.1021/acsaem.2c00662
Morimitsu, M., and Oshiumi, N. (2009). Accelerated oxygen evolution and suppressed MnOOH deposition on amorphous IrO2–Ta2O5 coatings. Chem. Lett. 38 (8), 822–823. doi:10.1246/cl.2009.822
Park, J., Lee, S., Kim, H. E., Cho, A., Kim, S., Ye, Y., et al. (2019). Investigation of the Support effect in atomically dispersed Pt on WO3-x for utilization of Pt in the hydrogen evolution reaction. Angew. Chem. Int. Ed. 58 (45), 16038–16042. doi:10.1002/anie.201908122
Qin, C., Fan, A., Ren, D., Luan, C., Yang, J., Liu, Y., et al. (2019). Amorphous nims (M: Co, Fe or Mn) holey nanosheets derived from crystal phase transition for enhanced oxygen evolution in water splitting. Electrochim. Acta 323, 134756. doi:10.1016/j.electacta.2019.134756
Ramesh, R., Lee, S., Kim, S., Park, J., Lee, S., Kim, M. S., et al. (2018). Oxygen evolution reaction on Ni‐based two‐dimensional (2d) titanate nanosheets: Investigation on effect of Fe Co‐doping and Fe incorporation from electrolyte on the activity. ChemistrySelect 3 (18), 5130–5137. doi:10.1002/slct.201800594
Smith, R. D., Prévot, M. S., Fagan, R. D., Trudel, S., and Berlinguette, C. P. (2013a). Water oxidation catalysis: Electrocatalytic response to metal stoichiometry in amorphous metal oxide films containing iron, cobalt, and nickel. J. Am. Chem. Soc. 135 (31), 11580–11586. doi:10.1021/ja403102j
Smith, R. D., Prévot, M. S., Fagan, R. D., Zhang, Z., Sedach, P. A., Siu, M. K. J., et al. (2013b). Photochemical route for accessing amorphous metal oxide materials for water oxidation catalysis. Science 340 (6128), 60–63. doi:10.1126/science.1233638
Smith, R. D., Sporinova, B., Fagan, R. D., Trudel, S., and Berlinguette, C. P. (2014). Facile photochemical preparation of amorphous iridium oxide films for water oxidation catalysis. Chem. Mat. 26 (4), 1654–1659. doi:10.1021/cm4041715
Tang, Y., Zhang, T., Wu, X., and Deng, S. (2022). Active sites regulation for high-performance oxygen evolution reaction electrocatalysts. Front. Chem. 10, 889470. doi:10.3389/fchem.2022.889470
Thangavel, P., Kim, G., and Kim, K. S. (2021). Electrochemical integration of amorphous NiFe (Oxy)Hydroxides on surface-activated carbon fibers for high-efficiency oxygen evolution in alkaline anion exchange membrane water electrolysis. J. Mat. Chem. A 9 (24), 14043–14051. doi:10.1039/d1ta02883a
Wang, J., Han, L., Huang, B., Shao, Q., Xin, H. L., and Huang, X. (2019). Amorphization activated ruthenium-tellurium nanorods for efficient water splitting. Nat. Commun. 10 (1), 5692. doi:10.1038/s41467-019-13519-1
Willinger, E., Massué, C., Schlögl, R., and Willinger, M. G. (2017). Identifying key structural features of irox water splitting catalysts. J. Am. Chem. Soc. 139 (34), 12093–12101. doi:10.1021/jacs.7b07079
Wu, G., Zheng, X., Cui, P., Jiang, H., Wang, X., Qu, Y., et al. (2019). A general synthesis approach for amorphous noble metal nanosheets. Nat. Commun. 10 (1), 4855. doi:10.1038/s41467-019-12859-2
Xu, S., Lv, C., He, T., Huang, Z., and Zhang, C. (2019). Amorphous film of cerium doped cobalt oxide as a highly efficient electrocatalyst for oxygen evolution reaction. J. Mat. Chem. A 7 (13), 7526–7532. doi:10.1039/c9ta00061e
Yang, C., Batuk, M., Jacquet, Q., Rousse, G., Yin, W., Zhang, L., et al. (2018). Revealing ph-dependent activities and surface instabilities for Ni-based electrocatalysts during the oxygen evolution reaction. ACS Energy Lett. 3 (12), 2884–2890. doi:10.1021/acsenergylett.8b01818
Ying, J., and Wang, H. (2021). Strategies for developing transition metal phosphides in electrochemical water splitting. Front. Chem. 9, 700020. doi:10.3389/fchem.2021.700020
Youk, S., Hwang, J., Lee, S., Kim, M. S., and Lee, J. (2019). Controlled leaching derived synthesis of atomically dispersed/clustered gold on mesoporous cobalt oxide for enhanced oxygen evolution reaction activity. Small Methods 3 (9), 1800293. doi:10.1002/smtd.201800293
Zhai, Y., Ren, X., Yan, J., and Liu, S. (2021). High density and unit activity integrated in amorphous catalysts for electrochemical water splitting. Small Struct. 2 (4), 2000096. doi:10.1002/sstr.202000096
Zhang D, D., Soo, J. Z., Tan, H. H., Jagadish, C., Catchpole, K., and Karuturi, S. K. (2021). Earth-abundant amorphous electrocatalysts for electrochemical hydrogen production: A review. Adv. Energy Sustain. Res. 2 (3), 2000071. doi:10.1002/aesr.202000071
Zhang L, L., Jang, H., Liu, H., Kim, M. G., Yang, D., Liu, S., et al. (2021). Sodium-decorated amorphous/crystalline RuO2 with rich oxygen vacancies: A robust ph-universal oxygen evolution electrocatalyst. Angew. Chem. Int. Ed. 60 (34), 18821–18829. doi:10.1002/anie.202106631
Zhao, W., Xu, T., Li, T., Wang, Y., Liu, H., Feng, J., et al. (2018). Amorphous iron (III)-Borate nanolattices as multifunctional electrodes for self-driven overall water splitting and rechargeable zinc–air battery. Small 14 (48), 1802829. doi:10.1002/smll.201802829
Zhou, Y., and Fan, H. J. (2020). Progress and challenge of amorphous catalysts for electrochemical water splitting. ACS Mat. Lett. 3 (1), 136–147. doi:10.1021/acsmaterialslett.0c00502
Keywords: amorphous electrocatalysts, oxygen evolution reaction, water splitting, electrolysis, amorphous material
Citation: Park J, Lee S and Kim S (2022) Recent advances in amorphous electrocatalysts for oxygen evolution reaction. Front. Chem. 10:1030803. doi: 10.3389/fchem.2022.1030803
Received: 29 August 2022; Accepted: 08 September 2022;
Published: 27 September 2022.
Edited by:
Hyung Ju Kim, Korea Research Institute of Chemical Technology (KRICT), South KoreaReviewed by:
Yitao Dai, University of Science and Technology of China, ChinaGun-hee Moon, Korea Institute of Science and Technology (KIST), South Korea
Copyright © 2022 Park, Lee and Kim. This is an open-access article distributed under the terms of the Creative Commons Attribution License (CC BY). The use, distribution or reproduction in other forums is permitted, provided the original author(s) and the copyright owner(s) are credited and that the original publication in this journal is cited, in accordance with accepted academic practice. No use, distribution or reproduction is permitted which does not comply with these terms.
*Correspondence: Seonggyu Lee, seonggyulee@kumoh.ac.kr; Seongseop Kim, seongseopkim@jbnu.ac.kr