PERSPECTIVE article

Front. Chem., 01 July 2021
Sec. Nanoscience
This article is part of the Research Topic Biobased Nanomaterials: New Trends and Applications View all 8 articles

Sustainable Wood Nanotechnologies for Wood Composites Processed by In-Situ Polymerization

  • Department of Fibre and Polymer Technology, Wallenberg Wood Science Center, KTH Royal Institute of Technology, Stockholm, Sweden

The development of large, multifunctional structures from sustainable wood nanomaterials is challenging. The need to improve mechanical performance, reduce moisture sensitivity, and add new functionalities, provides motivation for nanostructural tailoring. Although existing wood composites are commercially successful, materials development has not targeted nano-structural control of the wood cell wall, which could extend the property range. For sustainable development, non-toxic reactants, green chemistry and processing, lowered cumulative energy requirements, and lowered CO2-emissions are important targets. Here, modified wood substrates in the form of veneer are suggested as nanomaterial components for large, load-bearing structures. Examples include polymerization of bio-based monomers inside the cell wall, green chemistry wood modification, and addition of functional inorganic nanoparticles inside the cell wall. The perspective aims to describe bio-based polymers and green processing concepts for this purpose, along with wood nanoscience challenges.

Introduction

Bio-based materials are essential for a future sustainable society. With about three trillion trees on earth, wood is one of the most abundant renewable and sustainable material (Crowther et al., 2015). The eco-friendly aspect of sustainably sourced wood is related to its biological origin. The living tree is a renewable resource, and uses solar energy to manufacture the material and also store atmospheric carbon dioxide (CO2) in the process. Wood materials with long service life are therefore important for sustainable development through CO2 storage. In addition, wooden structures are excellent structural building materials, which can last for thousands of years (Yokoyama et al., 2009).

In pre-industrial age, timber was a key resource for fuel and construction. Despite good mechanical performance of wood structures, the construction of wooden buildings has in this perspective declined in the time frame after the 19th century, because of moisture, degradation and dimensional stability problems, quality variations and flammability challenges compared with alternative materials. Recently, however, engineered wood is revolutionizing the building sector, contributing toward sustainable development; the best example is tall wooden buildings in cities (Cornwall, 2016). Wood has much smaller carbon footprint than steel and concrete, and increased use may reduce CO2 emissions by 14% (Oliver et al., 2014).

The porosity of wood provides opportunities for new functionalities. It is possible to combine structural performance with functions to improve energy efficiency of buildings, and add specific properties such as magnetic, luminescent, electrical conductivity and hydrophobicity (Berglund and Burgert, 2018). Another important challenge for load-bearing wood biocomposites is to develop truly sustainable biocomposites based entirely on bio-based fibers and polymers, which are competitive with composites from fossil-based plastics. Although plant fibers may substitute synthetic fibers, bio-based polymers generally do not meet the overall properties and processing requirements for composites. In this perspective, aspects of wood nanotechnologies are discussed, as well as the associated nanoscience challenges and the need for sustainable tailoring methods.

Wood Composites Used in Load-Bearing Structures

Wood combines high mechanical performance with cost and sustainability advantages. The tree is a renewable resource, wood is available in large volumes at low cost, it has existing infrastructure for energy-efficient harvesting and processing, it is lightweight, and biodegradable. Engineered wood products are widely used for infrastructure applications, carrying substantial dynamic and static loads. There is a variety of engineered wood-based products, including solid structural wood products, laminar and structural composites. Solid-sawn timber is used for glued laminated beams (glulam) made by parallel assembly of sawn boards, and cross-laminated timber (CLT) made of layers assembled crosswise. Since the development of CLT in the 1990s, wooden buildings are constructed at increasing heights (Foster and Ramage, 2020). Other wood composites are fabricated from veneer to produce plywood (made by adhesive bonding of veneer lamellae stacked at different angles), and laminated veneer lumber (made of parallel veneers). These materials are generally used as panels or beams, with little geometrical complexity.

Molded, “wood-plastic composites” (WPCs) are prepared by mixing wood with fossil-based thermoplastics that serves as continuous matrix phase (polypropylene, polyethylene, etc.) (Bourmaud et al., 2018), but are insufficient for most major load-bearing infrastructure applications. There are also technologies for molded, formaldehyde-based thermoset wood fiber composites. In general, modulus for molded WPC and thermoset biocomposites rarely exceeds 7–8 GPa, and the tensile strength is typically 20–60 MPa. The fiber content in molded wood composites can be as high as 50–80 wt%, but the motivation for their use is often low cost. The performance of molded wood composites is often hampered by poorly controlled fiber orientation, and low fiber aspect ratio. The wood fibers tend to be weak, since they are mechanically damaged during processing. These factors in combination, result in poor wood fiber reinforcement efficiency. It is common to add maleic anhydride-grafted polypropylene or polyethylene coupling agents to melt-processed composites, to improve fiber dispersion and interfacial shear strength between the matrix and the wood reinforcement (Keener et al., 2004).

Targets for Sustainable Wood Nanotechnologies

Increased use of existing, load-bearing forest products, including sawn timber, glulam, LVL-beams, plywood and oriented strand boards (OSB), would contribute toward sustainable development when materials from concrete, gypsum and fossil-based plastics are replaced. Here, we discuss new wood modification concepts at the nanoscale, and possibilities for materials development.

In an attempt to define sustainable wood nanotechnology for the present purpose, the term is here limited to materials or components based on cellular wood structures, so that e.g. wood fiber materials and nanocellulosics are excluded, somewhat arbitrarily. Sustainable wood nanotechnologies are technologies related to wood substrate (e.g., veneer) modification by nanoparticles, and green modification of the wood cell wall nanostructure by chemical or physical means, to extend the range of wood properties. An important example is the impregnation of the wood cell wall by monomers or polymer precursors, followed by polymerization. Although formaldehyde-based resins and adhesives in use today can impregnate the cell wall (Stoeckel et al., 2013; Jones and Sandberg, 2020), which in principle is a nanotechnology, they are problematic in the context of sustainable development. Formaldehyde emission is a health hazard, a technical difficulty, and problematic for the perception of eco-friendly materials.

Targets for wood nanotechnologies include improved mechanical performance, since this can reduce the amount of material needed. Wood modification needs to be based on green chemistry principles (Anastas, 2007), and the use of bio-based polymers and nanoparticle technology leading to reduced overall environmental impact. Besides addressing the inherent weaknesses of wood, new functionalities such as heat storage, optical transmittance, fire retardancy and luminescence, can be integrated in the load-bearing wood structure so that eco-indicators for the whole building is improved (Li et al., 2018a). One needs to keep in mind, however, that successful wood nanotechnology depends on the nanoscience of processing-nanostructure and structure-property relationships.

In recent years, bio-based and biodegradable polymers have been considered for replacement of fossil-based polymers in load-bearing biocomposites. Furfuryl alcohol is a bio-based resin used as a substitute for phenol formaldehyde resins (Lande et al., 2008), although the black color and toxicity (monomer and catalysts) are problematic. Other bio-based polymers considered for plant fiber composites include thermosets based on vegetable oils (Williams and Wool, 2000; O’Donnell et al., 2004).

The Life Cycle of Wood Substrate Biocomposites

The present focus is on wood substrate biocomposites where monomers or thermoset precursors are used to impregnate a wood substrate, followed by polymerization. The entire life cycle of the material is illustrated in Figure 1, starting with trees as renewable resources, from which wood-based material components are obtained. They can be modified and processed to form biocomposite products. Note that the composite material is often created during processing of the “product”, e.g., a panel of certain shape. It is used in an application, and after service it can be recycled, reused, upcycled or disposed in different ways. The end-of-life management is dependent on the quality and the possible contaminations of the fiber reinforcement. Sustainable development means economic growth without depletion of natural resources, while retaining ecological balance (Ashby, 2016). Thus, materials from renewable resources is not enough. We need to consider recycling, energy demand from tree to material or product, greenhouse gas emissions, toxicity aspects, and end-of-life management (Ashby, 2013). The CED, cumulative energy demand (sum of energy required during all processing stages), of the product is an important eco-indicator. Low CED is needed in high-performance, sustainable lightweight materials with properties transcending current materials. We need material components from renewable feedstock (Narayan, 2011), green chemistry modification, and low-energy processing.

FIGURE 1
www.frontiersin.org

FIGURE 1. Life cycle for wood-based biocomposites. Sustainable development requires that cumulative energy demand and carbon dioxide emissions are decreased, compared with existing materials.

Lignocellulosic biomass is limited by moisture sensitivity and incompatibility with hydrophobic polymer systems. For wood, the substrate needs modification to address these challenges. Wood contains many different functional groups such as carboxylic acids, aliphatic alcohols, and phenols, useful for this purpose. Often, new chemical treatments are attempted based only on chemical structures of wood biopolymers. This is not sufficient, since the interior parts of the wood substrate, e.g., the wood cell wall, are not readily accessible. Chemical complexity and heterogeneity also means that specific reactions are not straightforward to achieve. The nature of the reaction system is important, and will control both chemical and physical accessibility, for instance by its ability to swell the wood cell wall into a more accessible gel structure.

Wood Structure and Alternatives for Eco-Friendly Biocomposites

Wood is an excellent substrate for load-bearing applications. By filling the pore space in wood with reactants (monomers, thermoset precursors), followed by polymerization, large-scale biocomposites can be prepared for applications in infrastructure. An interesting feature of wood for the sake of modification is its hierarchical structure, which extends from the macroscale to the nanoscale assembly of the cell wall layers and biopolymers (Fratzl and Weinkamer, 2007), see Figure 2. Wood cells are elongated tubular fibers, consisting of a cell wall and a central “lumen” void space. Wood fibers are a few millimeters in length and around 20–50 µm in diameter. The main biological functions of the wood tissue are water transport and mechanical support. In softwoods, fiber tracheids grow thin walls and wide lumen during spring (earlywood) to provide water transport, and thick wall and narrow lumen in the autumn (latewood) for mechanical stability (Figure 2A). In the native tree, the cell wall is itself a nanocomposite with strong, aligned cellulose fibrils embedded in a matrix of lignin, hemicellulose and water. Wood cellulose fibrils consist of axially aligned, extended cellulose chain molecules (Sacui et al., 2014), and have a diameter of 3–4 nm, with an estimated Young’s modulus of 140–200 GPa and a tensile strength of perhaps 7.5 GPa (Nishino et al., 1995; Šturcová et al., 2005; Dufresne, 2017). The fibrils show preferential axial orientation in the cell wall layers, see Figure 2C, and provide strength and stiffness to the cell wall.

FIGURE 2
www.frontiersin.org

FIGURE 2. (A) Illustration of softwood microstructure and major cell wall components, the starting tissue for nanostructural modification. The cell wall is dominated by the middle lamella, and the thick secondary wall. The cellulose nanofibrils are reinforcing a hydrated mixture of hemicellulose and lignin polymers in the cell wall. (B) Wood substrate before and after delignification treatment. Porosity is generated also at nanoscale inside the cell wall. (C) Illustration of wood cell wall swelling, which facilitates chemical modification.

The cellulose nanofibrils, CNF, can be disintegrated from chemical wood pulp fibers and used as reinforcement in biocomposites via bottom-up approaches (Kontturi et al., 2018). Disintegration takes place by mechanical means and is facilitated by chemical pretreatment (Pääkko et al., 2007; Saito et al., 2007). Lightweight CNF-based materials can be prepared by a prepreg-approach with potential for semi-structural applications (Ansari and Berglund, 2018). For random-in-plane CNF orientation and 50 vol% CNF, the modulus can approach 10 GPa and the strength exceed 150 MPa. The high energy demand, however, for extracting nanocellulose from the wood pulp fiber cell wall, combined with numerous composite preparation steps (CNF filtering, controlled drying, thermoset precursor impregnation, prepreg stacking and elevated temperature molding), and lack of recycling methods constitute major obstacles to the sustainability of CNF biocomposites. Cumulative energy demand, green-house gas emissions and water depletion indicators are unfavorable for CNF as compared with wood or wood fibers (Oliaei et al., 2021). From a sustainability and processability perspectives, CNF fibrils are problematic for large-scale building materials, but are better suited for films, coatings, aerogels, hydrogels, high-technology devices, or as minor additives in packaging materials.

Wood fibers are generally more eco-friendly than CNF for semi-structural applications, in terms of the eco-indicators mentioned previously. Optically transparent paper and biocomposites are examples of functional materials with good mechanical properties. These materials can be prepared from bleached wood pulp fibers, and offer recyclability potential (Yano et al., 2014; Ansari et al., 2015; Yang and Berglund, 2020b; Yang and Berglund, 2020a). One advantage of wood fiber biocomposites is the possibility to achieve high fiber volume fraction (>50 vol%) for complex, molded geometries by the use of existing processing methods for composites. The main disadvantage is that it is difficult to control fiber orientation in wood fiber biocomposites (Keplinger et al., 2019). If wood substrates are used as the reinforcement, this problem is solved since fibers are highly oriented in the original wood tissue.

Functionalized Wood Composites With Controlled Nanostructure

Wood substrates, such as veneer, are suitable for sustainable wood composites development. The basic idea is to use the structure of wood as a substrate and reinforcement in wood composites (Berglund and Burgert, 2018), rather than fibers or fibrils. Although fibers and fibrils are suitable for geometrically complex molded composites, wood composites are better for very large load-bearing structures with low eco-indicator values (CED, greenhouse gas emissions, etc.). Top-down modification approaches take advantage of the existing cell wall nanostructure and hierarchical porosity (microscale pore channels at the center of fiber cells, and nanopores inside the cell wall), while preserving the anisotropy of oriented fibers (Chen C. et al., 2020). This porosity provides opportunity for a great variety of functionalization approaches, at different scales. Since the native cell wall is virtually non-porous in the dried state, accessibility is a challenge.

The challenge of cell wall accessibility can be addressed by partial removal of cell wall components. Delignification treatments enable full or partial removal of lignin and hemicelluloses while preserving the oriented wood cellular structure and fibrils (Yano et al., 2001; Frey et al., 2018), see Figure 2B. The remaining lignin content is usually around 1–2% (Keplinger et al., 2020). Hemicelluloses are also affected by delignification and the hemicellulose content is reduced. Delignification generates porosity in the cell wall, and the wood substrate can reach specific surface areas up to 300 g/m2 for swollen cell walls, which is favorable for cell wall accessibility (Stamm and Millett, 1941). A swelling agent, such as acetic acid, can expand the cell wall and further facilitate impregnation of molecules or nanoparticles (Figure 2C). Chemical modification effects can then be improved, such as graft density of polymer chains chemically linked to the interior of the cell wall. (Olsén et al., 2020). The delignified cell wall is mesoporous and highly sensitive to drying methods. Drying from water can completely collapse the structure, due to capillary effects. For preservation of porosity and specific surface area, solvent-exchange from water to more non-polar liquids, followed by drying, is a successful approach (Grönquist et al., 2019; Han et al., 2019; Vitas et al., 2019). Although sequential solvent-exchange procedures are helpful (Yamasaki et al., 2019), solvent exchange is not suitable for industrial processing and increases eco-indicator values, but is a valuable tool in nanoscience investigations.

The delignified porous wood substrate has poor mechanical properties, because the lignin has been removed, which has an important role for inter-fiber bonding. Filling the lumen with a polymer matrix, see Figure 3A, improves mechanical properties compared with wood (Jungstedt et al., 2020). Densification methods show that strong, anisotropic, homogenous materials can be made from delignified substrates (Yano, 2001; Zhu et al., 2017; Song J. et al., 2018; Frey et al., 2018; Fu et al., 2020; Li et al., 2020). Resin impregnation of the lumen porosity in delignified substrates reduces moisture sensitivity and improves mechanical performance. Frey et al. produced biocomposites with wood content of up to 80 wt%, tensile strength up to 600 MPa and elastic modulus of 70 GPa (Frey et al., 2019). Conducting polymers, metals, and other stimuli-responsive polymer systems have also been successfully infiltrated into lumen space of wood cells to add functionalities (Trey et al., 2012; Keplinger et al., 2016; Wan et al., 2017).

FIGURE 3
www.frontiersin.org

FIGURE 3. (A) Chemical modification strategies for wood substrate functionalization. (B) Life cycle of fully bio-based transparent wood biocomposites. The bio-based transparent wood was prepared via green delignification treatment (peracetic acid) followed by solvent-free succinylation (succinic anhydride derived from bio-based succinic acid). A bio-based limonene acrylate monomer, designed from renewable limonene oxide (derived from limonene) and acrylic acid (derived from lactic acid), was impregnated and polymerized inside the wood substrate (Montanari et al., 2021).

The chemical functionalization philosophy is to target cell wall biopolymers. Hydroxyl groups in particular, can be readily replaced by other functional groups via esterification, etherification or graft polymerization. Functionalization can be carried out inside the cell wall, on the inner cell wall surface (lumen-cell wall interface), or in the lumen space (Figure 3A). Cell wall modification has been extensively used to improve dimensional stability and moisture stability. For example, cell wall hydroxyls can be substituted by less polar groups, such as acetyls or even silanes (Donath et al., 2004; Hill, 2006). Acetylation with acetic anhydride is an industrial process, which aims to reduce hydrophilicity of wood by substitution of hydroxyls by acetyl functionalities (Fuchs, 1928; Stamm and Tarkow, 1947; Rowell, 2006). It is a bulking treatment, since the space occupied by water in the native tree is reduced by introduction of acetyls. Another bulking approach relies on the impregnation of monomers or oligomers inside the cell wall (Stamm and Seborg, 1939).

The wood substrate can then be impregnated by monomers, either in the lumen space only or also inside the cell wall (Figure 3A). Various in-situ polymerization or grafting polymerization approaches are used to anchor polymer chains within the cell wall (Bach et al., 2005; Cabane et al., 2014; Ermeydan et al., 2014; Burgert et al., 2015; Keplinger et al., 2015). Surface-initiated radical polymerization is a good grafting technique (Cabane et al., 2016), since it is not sensitive to residual moisture. Polymer grafting or cell wall modification can also be used to improve molecular interactions with other polymers in biocomposites (Roy et al., 2009; Carlmark et al., 2012; Herrera et al., 2020). In an unusual cell wall modification procedure, dissolution−regeneration of cellulose nanofibers in lumen space was used to design porous, soft, compressible wood substrates which can serve as aerogels, or compressible materials (Chen et al., 2018; Garemark et al., 2020; Sun et al., 2020).

Wood can be functionalized by nanoparticle impregnation. Inorganic nanoparticles dispersed in water can diffuse inside the nanoporous cell wall for improved wood preservation against microorganisms (e.g., copper carbonate), and against UV degradation (e.g., titanium dioxide) (Evans et al., 2008; Nikolic et al., 2015). Wood mineralization and impregnation approaches using inorganic nanoparticles have also been explored for fire-retardancy applications (Merk et al., 2015; Fu et al., 2017; Zhang et al., 2021). Magnetic particles can be attached on the inner side of the cell wall, at the lumen-cell wall interface, to produce magnetic wood materials for e.g., electromagnetic shielding applications (Merk et al., 2014; Trey et al., 2014; Segmehl et al., 2018). Carbonization strategies followed by nanoparticle infiltration is used to provide electrical properties for energy-storage applications (Chen C. et al., 2017; Luo et al., 2017; Song H. et al., 2018; Wang Y. et al., 2018; Tang et al., 2018; Zhu et al., 2018; Peng et al., 2019; Garemark et al., 2020). Since wood is designed for liquid transport in the tree stem, it can also be functionalized and serve as a membrane for water treatment or oil-water separation purposes (Chen F. et al., 2017; Vidiella del Blanco et al., 2017; Fu et al., 2018a; Guan et al., 2018; Vitas et al., 2018; Ding et al., 2020; Goldhahn et al., 2020; Kim et al., 2020).

The Case of Transparent Wood

Transparent wood biocomposites were recently developed for structural applications, to combine optical transmittance and structural integrity (Li Y. et al., 2016). Transparent wood is obtained by first removing light-absorbing chemical groups from wood via delignification or bleaching treatments (Zhu et al., 2016b; Li et al., 2017a). Then a polymer matrix, commonly acrylates or epoxies, with a refractive index similar to the wood cell wall, is impregnated in monomer form into the porous delignified wood substrate and polymerized to provide optical transmittance. Transparent wood biocomposites are interesting architectural load-bearing structures owing to good mechanical performance, low density (1.2 g/cm3), high optical transmittance (≈90%), low thermal conductivity (0.15 W m−1 K−1), and potential for industrial scaling (Li T. et al., 2016; Li et al., 2018c; Wang X. et al., 2018; Mi et al., 2020). Tensile strength up to ≈270 MPa and elastic modulus of ≈20 GPa could be achieved for transparent wood based on high-density wood species (Jungstedt et al., 2020). The optical properties of transparent wood are attractive because it provides both high transmittance and high haze (≈80%), which is advantageous for diffused lighting and solar cell applications (Zhu et al., 2016a; Li et al., 2017b; Li et al., 2019).

It was recently shown that haze, forward-scattered light, can be tuned by controlling scattering effects within the composite using chemical treatments (e.g., acetylation, bleaching) to improve compatibility at the wood-polymer interfaces (lumen-cell wall and inside the cell wall) or by reducing cellulose content (Li et al., 2018c; Jia et al., 2019; Höglund et al., 2020). Multifunctional transparent wood composites, which combine optical transmittance with other functions, have been reported for applications such as photochromic, electrochromic, heat-shielding, magnetic, and thermal energy storage (Gan et al., 2017a; Lang et al., 2018; Montanari et al., 2019; Qiu et al., 2019; Wang et al., 2019; Samanta et al., 2021). Multifunctional transparent wood composites have been designed by the addition of a functional third-phase component to the polymer matrix and/or the cell wall. For example, quantum dots were added to the polymer matrix to obtain luminescent structures useful in load-bearing lighting applications (Gan et al., 2017b; Li et al., 2017b). The main challenge for multifunctional wood composites is to successfully achieve diffusion of the active component into the cell wall. For instance, nanostructured and multifunctional transparent wood could be prepared by impregnation of a phase-change material inside the cell wall to maximize heat-storage performance (Montanari et al., 2019).

High optical transmittance becomes increasingly difficult as thickness is increased. The reason is that an increased fraction of incoming light is scattered at interfaces between phases of different optical properties. The polymer matrix needs well-matched refractive index to the wood substrate. Chemical treatments can reduce the problem, e.g., by facilitating monomer diffusion into the cell wall so that the defects (nanoscale voids, interface debonds) are minimized (Li et al., 2018b; Chen H. et al., 2019; Chen et al., 2020 H.). To circumvent thickness limitations from processing challenges (incomplete monomer impregnation), laminated plywood structures provide advantages, and can combine high optical transmittance with mechanical performance (Fu et al., 2018b).

Green Aspects of Wood Functionalization

In a long-term perspective, wood functionalization needs to meet the criteria of green chemistry. The 12 green principles (GPs) are:

Waste prevention GP-1.

Atom economy GP-2.

Less hazardous chemical synthesis GP-3.

Designing safer chemicals GP-4.

Safer solvents and auxiliaries design GP-5.

Energy efficiency GP-6.

Use of renewable feedstock GP-7.

Reduce derivatives GP-8.

Catalysis GP-9.

Design for degradation GP-10.

Real-time analysis for pollution prevention GP-11.

Inherently safer chemistry for accident prevention GP-12.

Wood and cellulose substrates for composites are from renewable resources, but this is not enough (Onwukamike et al., 2019), for sustainable development. Bio-based polymer systems are needed as well as green concepts for composites processing (Curzons et al., 2001). Figure 3B shows the life cycle of a sustainable transparent wood biocomposite, implementing green chemical modification treatments (delignification, succinylation) and impregnation by bio-based monomer. All reactions are carried out without solvent and comply with GP-110.

Biomass as feedstock for chemicals is attractive since CO2 becomes an intrinsic part of the biomass/biopolymer structures during biosynthesis. Bio-based polymers and chemicals can serve as building blocks for synthesis of chemicals and polymeric materials (Gallezot, 2007). Waste materials from food, agricultural or forest industries (roots, branches) are particularly interesting feedstock (GP-7). The cumulative energy demand for materials and chemicals from biomass waste can be dramatically lower than for petrochemical alternatives. If roots and branches are left in the forest, they will degrade and emit carbon dioxide. If they are burnt, the high moisture content leads to low efficiency, and carbon dioxide emissions. Several bio-based chemicals are industrially produced and commercially available and can be used for large-scale wood functionalization (GP-7) (E4tech et al., 2015; Ögmundarson et al., 2020). In the example in Figure 3B, all reactants are from renewable feedstock; green peracetic acid was used for delignification, succinic anhydride from bio-based succinic acid was used for moisture stabilization and compatibilization, while lactic acid and limonene are bio-based building blocks for the limonene acrylate monomer.

Wood modification is motivated by moisture stability, compatibilization with polymers and the opportunity to integrate new functions. Green chemistry means reactants from renewable resources (GP-7), selective modification (GP-1, GP-2, GP-8, and GP-9), nonhazardous (GP-3, GP-4, GP-5, and GP-12), high atom economy (GP-2), mild reaction conditions (GP-6, and GP-9), energy efficiency (GP-6), and at least the same performance as for non-sustainable pathways (Trost, 1991; Anastas and Warner, 1998; Anastas and Eghbali, 2010). Solvents should be replaced by environmentally friendly alternatives (GP-5, and GP-7), recycled, reduced, or completely removed in order to minimize waste and environmental impact (DeSimone, 2002; Capello et al., 2007; Prat et al., 2013). Here (Figure 3B), a selective and green functionalization using cyclic anhydrides (e.g., succinic anhydride) (GP-1–5, 6, 7, 10) was demonstrated under solvent-free conditions for reduced hygroscopicity and facile monomer impregnation (Montanari et al., 2020). This is important, since solvent-assisted monomer impregnation should be avoided in sustainable industrial production of wood composites. The fully bio-based transparent wood biocomposites showed improved optical and mechanical properties, due to high polymer modulus and excellent matching of the refractive index of cellulose (Montanari et al., 2021). Other functionalization strategies have been used to tailor plant fiber properties. For example, green polymer grafting approaches were applied to wood fiber and CNF surfaces through surface-initiated ring-opening polymerization of bio-derived lactones (Lönnberg et al., 2006; Herrera et al., 2020; Olsén et al., 2020). Green delignification treatments for wood substrates were explored such as peracetic acid, ionic liquids, and deep eutectic solvents (GP-4, GP-5, and GP-7) (Miyafuji, 2015; Chen Z. et al., 2019; Montanari et al., 2020). When the purpose of delignification is to remove light-absorbing components, eco-friendly bleaching processes can be employed to remove chromophores while retaining most of the lignin (Li et al., 2017a).

Scientific challenges remain for the development of wood composites with polymers from renewable resources (GP-7) (Mohanty et al., 2018). Sustainability of the final product is affected by factors such as feedstock, embodied energy, durability and disposal (Álvarez-Chávez et al., 2012). To be used in high-performance applications, bio-based polymers should offer long-service life for use in structural infrastructures. For scalable technologies, monomers need to be suitable for existing impregnation and polymerization methods for composites processing. Acrylates meet this need, and free radical polymerization is not sensitive to moisture or heterogeneous chemical environments. The bio-based transparent wood biocomposite design in Figure 3B exemplifies the impregnation and polymerization of a bio-derived monomer into a functionalized wood substrate. The limonene acrylate monomer can diffuse into the modified cell wall and polymerizes readily, resulting in high optical transmittance, low haze, and a high strength composite (Montanari et al., 2021). The resulting biocomposite product is a good candidate for sustainable wood nanotechnology.

Conclusion

Sustainable wood nanotechnologies for wood composites are interesting for infrastructure applications. Wood-polymer composites are structurally efficient by combining high mechanical performance with anisotropy and lightweight. By controlling the composite nanostructure and use lamination to produce large structures, we can extend the property range of wood and add new functions.

Potential wood nanotechnologies are analyzed, where the intrinsic nanostructure is modified. The fact that wood and cellulose are from renewable resources, however, is not enough for wood composites to qualify as truly eco-friendly materials. Excessive energy demands for the processing steps, greenhouse gas emissions, and water depletion effects can be compromising factors. Green chemistry principles are therefore discussed, as guidance for wood composites design and processing. An example of a fully bio-based transparent wood nanocomposite, prepared by a top-down approach, is provided. This improves energy efficiency, since there is no need for nanocellulose disintegration and bottom-up materials preparation. Veneer substrates are instead subjected to green delignification, followed by moisture stabilization by bio-based molecules, impregnation with bio-based monomers in a solvent-free process, and final curing. Optical and mechanical properties are excellent, because of the molecular and nanoscale tailoring. For future work, thermoplastic polymers are desirable, since this would facilitate composites recycling. Future research development should henceforth focus on sustainable tailoring, with systematic implementation of the green chemistry principles and life-cycle assessment with estimations of cumulative energy demand and CO2 emissions.

Data Availability Statement

The original contributions presented in the study are included in the article/Supplementary Material, further inquiries can be directed to the corresponding author.

Author Contributions

All authors listed have made a substantial, direct and intellectual contribution to the work, and approved it for publication.

Funding

This project has received funding from the European Research Council (ERC) under the European Union’s Horizon 2020 research and innovation program (grant agreement No. 742733). We acknowledge funding from KTH and Knut and Alice Wallenberg foundation through the Wallenberg Wood Science Center and the KAW Biocomposites program at KTH Royal Institute of Technology.

Conflict of Interest

The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.

References

Álvarez-Chávez, C. R., Edwards, S., Moure-Eraso, R., and Geiser, K. (2012). Sustainability of Bio-Based Plastics: General Comparative Analysis and Recommendations for Improvement. J. Clean. Prod. 23, 47–56. doi:10.1016/j.jclepro.2011.10.003

CrossRef Full Text | Google Scholar

Anastas, P., and Eghbali, N. (2010). Green Chemistry: Principles and Practice. Chem. Soc. Rev. 39, 301–312. doi:10.1039/b918763b

PubMed Abstract | CrossRef Full Text | Google Scholar

Anastas, P. T. (2007). Introduction: Green Chemistry. Chem. Rev. 107, 2167–2168. doi:10.1021/cr0783784

CrossRef Full Text | Google Scholar

Anastas, P. T., and Warner, J. C. (1998). Green Chemistry: Theory and Practice. Oxford [England]; New York: Oxford University Press.

Ansari, F., and Berglund, L. A. (2018). Toward Semistructural Cellulose Nanocomposites: The Need for Scalable Processing and Interface Tailoring. Biomacromolecules 19, 2341–2350. doi:10.1021/acs.biomac.8b00142

PubMed Abstract | CrossRef Full Text | Google Scholar

Ansari, F., Sjöstedt, A., Larsson, P. T., Berglund, L. A., and Wågberg, L. (2015). Hierarchical wood Cellulose Fiber/epoxy Biocomposites - Materials Design of Fiber Porosity and Nanostructure. Composites A: Appl. Sci. Manufacturing 74, 60–68. doi:10.1016/j.compositesa.2015.03.024

CrossRef Full Text | Google Scholar

Ashby, M. F. (2013). “The Material Life Cycle,” in Materials and the Environment (Amsterdam, Netherlands: Elsevier), 49–77. doi:10.1016/B978-0-12-385971-6.00003-8

CrossRef Full Text | Google Scholar

Ashby, M. F. (2016). “What Is a "Sustainable Development"?,” in Materials and Sustainable Development (Amsterdam, Netherlands: Elsevier), 27–38. doi:10.1016/B978-0-08-100176-9.00002-5

CrossRef Full Text | Google Scholar

Bach, S., Belgacem, M. N., and Gandini, A. (2005). Hydrophobisation and Densification of wood by Different Chemical Treatments. Holzforschung 59, 389–396. doi:10.1515/HF.2005.064

CrossRef Full Text | Google Scholar

Berglund, L. A., and Burgert, I. (2018). Bioinspired Wood Nanotechnology for Functional Materials. Adv. Mater. 30, 1704285. doi:10.1002/adma.201704285

CrossRef Full Text | Google Scholar

Bourmaud, A., Beaugrand, J., Shah, D. U., Placet, V., and Baley, C. (2018). Towards the Design of High-Performance Plant Fibre Composites. Prog. Mater. Sci. 97, 347–408. doi:10.1016/j.pmatsci.2018.05.005

CrossRef Full Text | Google Scholar

Burgert, I., Cabane, E., Zollfrank, C., and Berglund, L. (2015). Bio-inspired Functional wood-based Materials - Hybrids and Replicates. Int. Mater. Rev. 60, 431–450. doi:10.1179/1743280415Y.0000000009

CrossRef Full Text | Google Scholar

Cabane, E., Keplinger, T., Künniger, T., Merk, V., and Burgert, I. (2016). Functional Lignocellulosic Materials Prepared by ATRP from a wood Scaffold. Sci. Rep. 6, 31287. doi:10.1038/srep31287

PubMed Abstract | CrossRef Full Text | Google Scholar

Cabane, E., Keplinger, T., Merk, V., Hass, P., and Burgert, I. (2014). Renewable and Functional Wood Materials by Grafting Polymerization within Cell Walls. ChemSusChem 7, 1020–1025. doi:10.1002/cssc.201301107

PubMed Abstract | CrossRef Full Text | Google Scholar

Capello, C., Fischer, U., and Hungerbühler, K. (2007). What Is a green Solvent? A Comprehensive Framework for the Environmental Assessment of Solvents. Green. Chem. 9, 927. doi:10.1039/b617536h

CrossRef Full Text | Google Scholar

Carlmark, A., Larsson, E., and Malmström, E. (2012). Grafting of Cellulose by Ring-Opening Polymerisation - A Review. Eur. Polym. J. 48, 1646–1659. doi:10.1016/j.eurpolymj.2012.06.013

CrossRef Full Text | Google Scholar

Chen, C., Kuang, Y., Zhu, S., Burgert, I., Keplinger, T., Gong, A., et al. (2020a). Structure-property-function Relationships of Natural and Engineered wood. Nat. Rev. Mater. 5, 642–666. doi:10.1038/s41578-020-0195-z

CrossRef Full Text | Google Scholar

Chen, C., Song, J., Zhu, S., Li, Y., Kuang, Y., Wan, J., et al. (2018). Scalable and Sustainable Approach toward Highly Compressible, Anisotropic, Lamellar Carbon Sponge. Chem 4, 544–554. doi:10.1016/j.chempr.2017.12.028

CrossRef Full Text | Google Scholar

Chen, C., Zhang, Y., Li, Y., Dai, J., Song, J., Yao, Y., et al. (2017a). All-wood, Low Tortuosity, Aqueous, Biodegradable Supercapacitors with Ultra-high Capacitance. Energy Environ. Sci. 10, 538–545. doi:10.1039/C6EE03716J

CrossRef Full Text | Google Scholar

Chen, F., Gong, A. S., Zhu, M., Chen, G., Lacey, S. D., Jiang, F., et al. (2017b). Mesoporous, Three-Dimensional Wood Membrane Decorated with Nanoparticles for Highly Efficient Water Treatment. ACS Nano 11, 4275–4282. doi:10.1021/acsnano.7b01350

CrossRef Full Text | Google Scholar

Chen, H., Baitenov, A., Li, Y., Vasileva, E., Popov, S., Sychugov, I., et al. (2019a). Thickness Dependence of Optical Transmittance of Transparent Wood: Chemical Modification Effects. ACS Appl. Mater. Inter. 11, 35451–35457. doi:10.1021/acsami.9b11816

CrossRef Full Text | Google Scholar

Chen, H., Montanari, C., Yan, M., Popov, S., Li, Y., Sychugov, I., et al. (2020b). Refractive index of Delignified wood for Transparent Biocomposites. RSC Adv. 10, 40719–40724. doi:10.1039/d0ra07409h

CrossRef Full Text | Google Scholar

Chen, Z., Dang, B., Luo, X., Li, W., Li, J., Yu, H., et al. (2019b). Deep Eutectic Solvent-Assisted In Situ Wood Delignification: A Promising Strategy to Enhance the Efficiency of Wood-Based Solar Steam Generation Devices. ACS Appl. Mater. Inter. 11, 26032–26037. doi:10.1021/acsami.9b08244

CrossRef Full Text | Google Scholar

Cornwall, W. (2016). Tall Timber. Science 353, 1354–1356. doi:10.1126/science.353.6306.1354

PubMed Abstract | CrossRef Full Text | Google Scholar

Crowther, T. W., Glick, H. B., Covey, K. R., Bettigole, C., Maynard, D. S., Thomas, S. M., et al. (2015). Mapping Tree Density at a Global Scale. Nature 525, 201–205. doi:10.1038/nature14967

PubMed Abstract | CrossRef Full Text | Google Scholar

Curzons, A. D., Mortimer, D. N., Constable, D. J. C., and Cunningham, V. L. (2001). So You Think Your Process Is green, How Do You Know? - Using Principles of Sustainability to Determine what Is green - a Corporate Perspective. Green. Chem. 3, 1–6. doi:10.1039/b007871i

CrossRef Full Text | Google Scholar

DeSimone, J. M. (2002). Practical Approaches to Green Solvents. Science 297, 799–803. doi:10.1126/science.1069622

PubMed Abstract | CrossRef Full Text | Google Scholar

Ding, Y., Tu, K., Burgert, I., and Keplinger, T. (2020). Janus wood Membranes for Autonomous Water Transport and Fog Collection. J. Mater. Chem. A. 8, 22001–22008. doi:10.1039/d0ta07544b

CrossRef Full Text | Google Scholar

Donath, S., Militz, H., and Mai, C. (2004). Wood Modification with Alkoxysilanes. Wood Sci. Technol. 38, 555–566. doi:10.1007/s00226-004-0257-1

CrossRef Full Text | Google Scholar

Dufresne, A. (2017). Nanocellulose: From Nature to High Performance Tailored Materials. Edition, 2. Berlin: De Gruyter. doi:10.1515/9783110480412

CrossRef Full Text

E4tech, , Re-Cord, , and Wur, (2015). From the Sugar Platform to Biofuels and Biochemicals. Available at: https://ec.europa.eu/energy/sites/ener/files/documents/EC Sugar Platform final report.pdf. Accessed February 24, 2021.

Google Scholar

Ermeydan, M. A., Cabane, E., Gierlinger, N., Koetz, J., and Burgert, I. (2014). Improvement of wood Material Properties via In Situ Polymerization of Styrene into Tosylated Cell walls. RSC Adv. 4, 12981. doi:10.1039/c4ra00741g

CrossRef Full Text | Google Scholar

Evans, P., Matsunaga, H., and Kiguchi, M. (2008). Large-scale Application of Nanotechnology for wood protection. Nat. Nanotech 3, 577. doi:10.1038/nnano.2008.286

PubMed Abstract | CrossRef Full Text | Google Scholar

Foster, R. M., and Ramage, M. H. (2020). “Tall Timber,” in Nonconventional and Vernacular Construction Materials (Amsterdam, Netherlands: Elsevier), 467–490. doi:10.1016/B978-0-08-102704-2.00017-2

CrossRef Full Text | Google Scholar

Fratzl, P., and Weinkamer, R. (2007). Nature's Hierarchical Materials. Prog. Mater. Sci. 52, 1263–1334. doi:10.1016/j.pmatsci.2007.06.001

CrossRef Full Text | Google Scholar

Frey, M., Schneider, L., Masania, K., Keplinger, T., and Burgert, I. (2019). Delignified Wood-Polymer Interpenetrating Composites Exceeding the Rule of Mixtures. ACS Appl. Mater. Inter. 11, 35305–35311. doi:10.1021/acsami.9b11105

CrossRef Full Text | Google Scholar

Frey, M., Widner, D., Segmehl, J. S., Casdorff, K., Keplinger, T., and Burgert, I. (2018). Delignified and Densified Cellulose Bulk Materials with Excellent Tensile Properties for Sustainable Engineering. ACS Appl. Mater. Inter. 10, 5030–5037. doi:10.1021/acsami.7b18646

CrossRef Full Text | Google Scholar

Fu, Q., Ansari, F., Zhou, Q., and Berglund, L. A. (2018a). Wood Nanotechnology for Strong, Mesoporous, and Hydrophobic Biocomposites for Selective Separation of Oil/Water Mixtures. ACS Nano 12, 2222–2230. doi:10.1021/acsnano.8b00005

CrossRef Full Text | Google Scholar

Fu, Q., Medina, L., Li, Y., Carosio, F., Hajian, A., and Berglund, L. A. (2017). Nanostructured Wood Hybrids for Fire-Retardancy Prepared by Clay Impregnation into the Cell Wall. ACS Appl. Mater. Inter. 9, 36154–36163. doi:10.1021/acsami.7b10008

CrossRef Full Text | Google Scholar

Fu, Q., Tu, K., Goldhahn, C., Keplinger, T., Adobes-Vidal, M., Sorieul, M., et al. (2020). Luminescent and Hydrophobic Wood Films as Optical Lighting Materials. ACS Nano 14, 13775–13783. doi:10.1021/acsnano.0c06110

PubMed Abstract | CrossRef Full Text | Google Scholar

Fu, Q., Yan, M., Jungstedt, E., Yang, X., Li, Y., and Berglund, L. A. (2018b). Transparent Plywood as a Load-Bearing and Luminescent Biocomposite. Composites Sci. Technol. 164, 296–303. doi:10.1016/j.compscitech.2018.06.001

CrossRef Full Text | Google Scholar

Fuchs, W. (1928). Zur Kenntnis des genuinen Lignins, I.: Die Acetylierung des Fichtenholzes. Ber. Dtsch. Chem. Ges. A/b 61, 948–951. doi:10.1002/cber.19280610512

CrossRef Full Text | Google Scholar

Gallezot, P. (2007). Process Options for Converting Renewable Feedstocks to Bioproducts. Green. Chem. 9, 295. doi:10.1039/b615413a

CrossRef Full Text | Google Scholar

Gan, W., Gao, L., Xiao, S., Zhang, W., Zhan, X., and Li, J. (2017a). Transparent Magnetic wood Composites Based on Immobilizing Fe3O4 Nanoparticles into a Delignified wood Template. J. Mater. Sci. 52, 3321–3329. doi:10.1007/s10853-016-0619-8

CrossRef Full Text | Google Scholar

Gan, W., Xiao, S., Gao, L., Gao, R., Li, J., and Zhan, X. (2017b). Luminescent and Transparent Wood Composites Fabricated by Poly(methyl Methacrylate) and γ-Fe2O3@YVO4:Eu3+ Nanoparticle Impregnation. ACS Sustain. Chem. Eng. 5, 3855–3862. doi:10.1021/acssuschemeng.6b02985

CrossRef Full Text | Google Scholar

Garemark, J., Yang, X., Sheng, X., Cheung, O., Sun, L., Berglund, L. A., et al. (2020). Top-Down Approach Making Anisotropic Cellulose Aerogels as Universal Substrates for Multifunctionalization. ACS Nano 14, 7111–7120. doi:10.1021/acsnano.0c01888

PubMed Abstract | CrossRef Full Text | Google Scholar

Goldhahn, C., Schubert, M., Lüthi, T., Keplinger, T., Burgert, I., and Chanana, M. (2020). Wood-gelatin Bio-Composite Membranes with Tunable Flux. ACS Sustain. Chem. Eng. 8, 7205–7213. doi:10.1021/acssuschemeng.0c01856

CrossRef Full Text | Google Scholar

Grönquist, P., Frey, M., Keplinger, T., and Burgert, I. (2019). Mesoporosity of Delignified Wood Investigated by Water Vapor Sorption. ACS Omega 4, 12425–12431. doi:10.1021/acsomega.9b00862

PubMed Abstract | CrossRef Full Text | Google Scholar

Guan, H., Cheng, Z., and Wang, X. (2018). Highly Compressible Wood Sponges with a Spring-like Lamellar Structure as Effective and Reusable Oil Absorbents. ACS Nano 12, 10365–10373. doi:10.1021/acsnano.8b05763

PubMed Abstract | CrossRef Full Text | Google Scholar

Han, X., Ye, Y., Lam, F., Pu, J., and Jiang, F. (2019). Hydrogen-bonding-induced Assembly of Aligned Cellulose Nanofibers into Ultrastrong and Tough Bulk Materials. J. Mater. Chem. A. 7, 27023–27031. doi:10.1039/C9TA11118B

CrossRef Full Text | Google Scholar

Herrera, N., Olsén, P., and Berglund, L. A. (2020). Strongly Improved Mechanical Properties of Thermoplastic Biocomposites by PCL Grafting inside Holocellulose Wood Fibers. ACS Sustain. Chem. Eng. 8, 11977–11985. doi:10.1021/acssuschemeng.0c02512

CrossRef Full Text | Google Scholar

Hill, C. A. S. (2006). Wood Modification: Chemical, Thermal and Other Processes. Chichester, UK: John Wiley & Sons. doi:10.1002/0470021748

CrossRef Full Text

Höglund, M., Johansson, M., Sychugov, I., and Berglund, L. A. (2020). Transparent Wood Biocomposites by Fast UV-Curing for Reduced Light-Scattering through Wood/Thiol-ene Interface Design. ACS Appl. Mater. Inter. 12, 46914–46922. doi:10.1021/acsami.0c12505

CrossRef Full Text | Google Scholar

Jia, C., Chen, C., Mi, R., Li, T., Dai, J., Yang, Z., et al. (2019). Clear Wood toward High-Performance Building Materials. ACS Nano 13, 9993–10001. doi:10.1021/acsnano.9b00089

PubMed Abstract | CrossRef Full Text | Google Scholar

Jones, D., and Sandberg, D. (2020). A Review of Wood Modification Globally - Updated Findings from COST FP1407. Ipbe 1, 1–31. doi:10.37947/ipbe.2020.vol1.1

CrossRef Full Text | Google Scholar

Jungstedt, E., Montanari, C., Östlund, S., and Berglund, L. (2020). Mechanical Properties of Transparent High Strength Biocomposites from Delignified wood Veneer. Composites Part A: Appl. Sci. Manufacturing 133, 105853. doi:10.1016/j.compositesa.2020.105853

CrossRef Full Text | Google Scholar

Keener, T. J., Stuart, R. K., and Brown, T. K. (2004). Maleated Coupling Agents for Natural Fibre Composites. Composites Part A: Appl. Sci. Manufacturing 35, 357–362. doi:10.1016/j.compositesa.2003.09.014

CrossRef Full Text | Google Scholar

Keplinger, T., Cabane, E., Berg, J. K., Segmehl, J. S., Bock, P., and Burgert, I. (2016). Smart Hierarchical Bio-Based Materials by Formation of Stimuli-Responsive Hydrogels inside the Microporous Structure of Wood. Adv. Mater. Inter. 3, 1600233. doi:10.1002/admi.201600233

CrossRef Full Text | Google Scholar

Keplinger, T., Cabane, E., Chanana, M., Hass, P., Merk, V., Gierlinger, N., et al. (2015). A Versatile Strategy for Grafting Polymers to wood Cell walls. Acta Biomater. 11, 256–263. doi:10.1016/j.actbio.2014.09.016

PubMed Abstract | CrossRef Full Text | Google Scholar

Keplinger, T., Wang, X., and Burgert, I. (2019). Nanofibrillated Cellulose Composites and wood Derived Scaffolds for Functional Materials. J. Mater. Chem. A. 7, 2981–2992. doi:10.1039/C8TA10711D

CrossRef Full Text | Google Scholar

Keplinger, T., Wittel, F. K., Rüggeberg, M., and Burgert, I. (2020). Wood Derived Cellulose Scaffolds—Processing and Mechanics. Adv. Mater., 2001375. doi:10.1002/adma.202001375

CrossRef Full Text | Google Scholar

Kim, S., Kim, K., Jun, G., and Hwang, W. (2020). Wood-Nanotechnology-Based Membrane for the Efficient Purification of Oil-In-Water Emulsions. ACS Nano 14, 17233–17240. doi:10.1021/acsnano.0c07206

CrossRef Full Text | Google Scholar

Kontturi, E., Laaksonen, P., Linder, M. B., Nonappa Gröschel, A. H., Gröschel, O. J., and Ikkala, O. (2018). Advanced Materials through Assembly of Nanocelluloses. Adv. Mater. 30, 1703779. doi:10.1002/adma.201703779

CrossRef Full Text | Google Scholar

Lande, S., Westin, M., and Schneider, M. (2008). Development of Modified wood Products Based on Furan Chemistry. Mol. Crystals Liquid Crystals 484, 1/[367]–12/[378]. doi:10.1080/15421400801901456

CrossRef Full Text | Google Scholar

Lang, A. W., Li, Y., De Keersmaecker, M., Shen, D. E., Österholm, A. M., Berglund, L., et al. (2018). Transparent Wood Smart Windows: Polymer Electrochromic Devices Based on Poly(3,4-Ethylenedioxythiophene):Poly(Styrene Sulfonate) Electrodes. ChemSusChem 11, 854–863. doi:10.1002/cssc.201702026

PubMed Abstract | CrossRef Full Text | Google Scholar

Li, K., Wang, S., Chen, H., Yang, X., Berglund, L. A., and Zhou, Q. (2020). Self‐Densification of Highly Mesoporous Wood Structure into a Strong and Transparent Film. Adv. Mater. 32, 2003653. doi:10.1002/adma.202003653

CrossRef Full Text | Google Scholar

Li, T., Zhu, M., Yang, Z., Song, J., Dai, J., Yao, Y., et al. (2016a). Wood Composite as an Energy Efficient Building Material: Guided Sunlight Transmittance and Effective Thermal Insulation. Adv. Energ. Mater. 6, 1601122. doi:10.1002/aenm.201601122

CrossRef Full Text | Google Scholar

Li, Y., Cheng, M., Jungstedt, E., Xu, B., Sun, L., and Berglund, L. (2019). Optically Transparent Wood Substrate for Perovskite Solar Cells. ACS Sustain. Chem. Eng. 7, 6061–6067. doi:10.1021/acssuschemeng.8b06248

PubMed Abstract | CrossRef Full Text | Google Scholar

Li, Y., Fu, Q., Rojas, R., Yan, M., Lawoko, M., and Berglund, L. (2017a). Lignin-Retaining Transparent Wood. ChemSusChem 10, 3445–3451. doi:10.1002/cssc.201701089

PubMed Abstract | CrossRef Full Text | Google Scholar

Li, Y., Fu, Q., Yang, X., and Berglund, L. (2018a). Transparent wood for Functional and Structural Applications. Phil. Trans. R. Soc. A. 376, 20170182. doi:10.1098/rsta.2017.0182

PubMed Abstract | CrossRef Full Text | Google Scholar

Li, Y., Fu, Q., Yu, S., Yan, M., and Berglund, L. (2016b). Optically Transparent Wood from a Nanoporous Cellulosic Template: Combining Functional and Structural Performance. Biomacromolecules 17, 1358–1364. doi:10.1021/acs.biomac.6b00145

PubMed Abstract | CrossRef Full Text | Google Scholar

Li, Y., Vasileva, E., Sychugov, I., Popov, S., and Berglund, L. (2018b). Optically Transparent Wood: Recent Progress, Opportunities, and Challenges. Adv. Opt. Mater. 6, 1800059. doi:10.1002/adom.201800059

CrossRef Full Text | Google Scholar

Li, Y., Yang, X., Fu, Q., Rojas, R., Yan, M., and Berglund, L. (2018c). Towards Centimeter Thick Transparent wood through Interface Manipulation. J. Mater. Chem. A. 6, 1094–1101. doi:10.1039/C7TA09973H

CrossRef Full Text | Google Scholar

Li, Y., Yu, S., Veinot, J. G. C., Linnros, J., Berglund, L., and Sychugov, I. (2017b). Luminescent Transparent Wood. Adv. Opt. Mater. 5, 1600834. doi:10.1002/adom.201600834

CrossRef Full Text | Google Scholar

Lönnberg, H., Zhou, Q., Brumer, H., Teeri, T. T., Malmström, E., and Hult, A. (2006). Grafting of Cellulose Fibers with Poly(ε-Caprolactone) and Poly(l-Lactic Acid) via Ring-Opening Polymerization. Biomacromolecules 7, 2178–2185. doi:10.1021/bm060178z

PubMed Abstract | CrossRef Full Text | Google Scholar

Luo, W., Zhang, Y., Xu, S., Dai, J., Hitz, E., Li, Y., et al. (2017). Encapsulation of Metallic Na in an Electrically Conductive Host with Porous Channels as a Highly Stable Na Metal Anode. Nano Lett. 17, 3792–3797. doi:10.1021/acs.nanolett.7b01138

PubMed Abstract | CrossRef Full Text | Google Scholar

Merk, V., Chanana, M., Gierlinger, N., Hirt, A. M., and Burgert, I. (2014). Hybrid Wood Materials with Magnetic Anisotropy Dictated by the Hierarchical Cell Structure. ACS Appl. Mater. Inter. 6, 9760–9767. doi:10.1021/am5021793

CrossRef Full Text | Google Scholar

Merk, V., Chanana, M., Keplinger, T., Gaan, S., and Burgert, I. (2015). Hybrid wood Materials with Improved Fire Retardance by Bio-Inspired Mineralisation on the Nano- and Submicron Level. Green. Chem. 17, 1423–1428. doi:10.1039/c4gc01862a

CrossRef Full Text | Google Scholar

Mi, R., Chen, C., Keplinger, T., Pei, Y., He, S., Liu, D., et al. (2020). Scalable Aesthetic Transparent wood for Energy Efficient Buildings. Nat. Commun. 11, 3836. doi:10.1038/s41467-020-17513-w

PubMed Abstract | CrossRef Full Text | Google Scholar

Miyafuji, H. (2015). Application of Ionic Liquids for Effective Use of Woody Biomass. J. Wood Sci. 61, 343–350. doi:10.1007/s10086-015-1489-4

CrossRef Full Text | Google Scholar

Mohanty, A. K., Vivekanandhan, S., Pin, J.-M., and Misra, M. (2018). Composites from Renewable and Sustainable Resources: Challenges and Innovations. Science 362, 536–542. doi:10.1126/science.aat9072

PubMed Abstract | CrossRef Full Text | Google Scholar

Montanari, C., Li, Y., Chen, H., Yan, M., and Berglund, L. A. (2019). Transparent Wood for Thermal Energy Storage and Reversible Optical Transmittance. ACS Appl. Mater. Inter. 11, 20465–20472. doi:10.1021/acsami.9b05525

CrossRef Full Text | Google Scholar

Montanari, C., Ogawa, Y., Olsén, P., and Berglund, L. A. (2021). High Performance, Fully Bio‐Based, and Optically Transparent Wood Biocomposites. Adv. Sci. 8, 2100559. doi:10.1002/advs.202100559

CrossRef Full Text | Google Scholar

Montanari, C., Olsén, P., and Berglund, L. A. (2020). Interface Tailoring by a Versatile Functionalization Platform for Nanostructured wood Biocomposites. Green. Chem. 22, 8012–8023. doi:10.1039/D0GC02768E

CrossRef Full Text | Google Scholar

Narayan, R. (2011). Carbon Footprint of Bioplastics Using Biocarbon Content Analysis and Life-Cycle Assessment. MRS Bull. 36, 716–721. doi:10.1557/mrs.2011.210

CrossRef Full Text | Google Scholar

Nikolic, M., Lawther, J. M., and Sanadi, A. R. (2015). Use of Nanofillers in wood Coatings: a Scientific Review. J. Coat. Technol. Res. 12, 445–461. doi:10.1007/s11998-015-9659-2

CrossRef Full Text | Google Scholar

Nishino, T., Takano, K., and Nakamae, K. (1995). Elastic Modulus of the Crystalline Regions of Cellulose Polymorphs. J. Polym. Sci. B Polym. Phys. 33, 1647–1651. doi:10.1002/polb.1995.090331110

CrossRef Full Text | Google Scholar

O’Donnell, A., Dweib, M. A., and Wool, R. P. (2004). Natural Fiber Composites with Plant Oil-Based Resin. Compos. Sci. Technol. 64, 1135–1145. doi:10.1016/j.compscitech.2003.09.024

CrossRef Full Text | Google Scholar

Ögmundarson, Ó., Herrgård, M. J., Forster, J., Hauschild, M. Z., and Fantke, P. (2020). Addressing Environmental Sustainability of Biochemicals. Nat. Sustain. 3, 167–174. doi:10.1038/s41893-019-0442-8

CrossRef Full Text | Google Scholar

Oliaei, E., Berthold, F., Berglund, L. A., and Lindström, T. (2021). Eco-Friendly High-Strength Composites Based on Hot-Pressed Lignocellulose Microfibrils or Fibers. ACS Sustain. Chem. Eng. 9, 1899–1910. doi:10.1021/acssuschemeng.0c08498

CrossRef Full Text | Google Scholar

Oliver, C. D., Nassar, N. T., Lippke, B. R., and McCarter, J. B. (2014). Carbon, Fossil Fuel, and Biodiversity Mitigation with Wood and Forests. J. Sustain. For. 33, 248–275. doi:10.1080/10549811.2013.839386

CrossRef Full Text | Google Scholar

Olsén, P., Herrera, N., and Berglund, L. A. (2020). Polymer Grafting inside Wood Cellulose Fibers by Improved Hydroxyl Accessibility from Fiber Swelling. Biomacromolecules 21, 597–603. doi:10.1021/acs.biomac.9b01333

PubMed Abstract | CrossRef Full Text | Google Scholar

Onwukamike, K. N., Grelier, S., Grau, E., Cramail, H., and Meier, M. A. R. (2019). Critical Review on Sustainable Homogeneous Cellulose Modification: Why Renewability Is Not Enough. ACS Sustain. Chem. Eng. 7, 1826–1840. doi:10.1021/acssuschemeng.8b04990

CrossRef Full Text | Google Scholar

Pääkkö, M., Ankerfors, M., Kosonen, H., Nykänen, A., Ahola, S., Österberg, M., et al. (2007). Enzymatic Hydrolysis Combined with Mechanical Shearing and High-Pressure Homogenization for Nanoscale Cellulose Fibrils and strong Gels. Biomacromolecules 8, 1934–1941. doi:10.1021/bm061215p

PubMed Abstract | CrossRef Full Text | Google Scholar

Peng, X., Zhang, L., Chen, Z., Zhong, L., Zhao, D., Chi, X., et al. (2019). Hierarchically Porous Carbon Plates Derived from Wood as Bifunctional ORR/OER Electrodes. Adv. Mater. 31, 1900341. doi:10.1002/adma.201900341

CrossRef Full Text | Google Scholar

Prat, D., Pardigon, O., Flemming, H.-W., Letestu, S., Ducandas, V., Isnard, P., et al. (2013). Sanofi's Solvent Selection Guide: A Step toward More Sustainable Processes. Org. Process. Res. Dev. 17, 1517–1525. doi:10.1021/op4002565

CrossRef Full Text | Google Scholar

Qiu, Z., Xiao, Z., Gao, L., Li, J., Wang, H., Wang, Y., et al. (2019). Transparent wood Bearing a Shielding Effect to Infrared Heat and Ultraviolet via Incorporation of Modified Antimony-Doped Tin Oxide Nanoparticles. Composites Sci. Technol. 172, 43–48. doi:10.1016/j.compscitech.2019.01.005

CrossRef Full Text | Google Scholar

Rowell, R. M. (2006). Chemical Modification of wood: A Short Review. Wood Mater. Sci. Eng. 1, 29–33. doi:10.1080/17480270600670923

CrossRef Full Text | Google Scholar

Roy, D., Semsarilar, M., Guthrie, J. T., and Perrier, S. (2009). Cellulose Modification by Polymer Grafting: A Review. Chem. Soc. Rev. 38, 2046–2064. doi:10.1039/b808639g

PubMed Abstract | CrossRef Full Text | Google Scholar

Sacui, I. A., Nieuwendaal, R. C., Burnett, D. J., Stranick, S. J., Jorfi, M., Weder, C., et al. (2014). Comparison of the Properties of Cellulose Nanocrystals and Cellulose Nanofibrils Isolated from Bacteria, Tunicate, and wood Processed Using Acid, Enzymatic, Mechanical, and Oxidative Methods. ACS Appl. Mater. Inter. 6, 6127–6138. doi:10.1021/am500359f

CrossRef Full Text | Google Scholar

Saito, T., Kimura, S., Nishiyama, Y., and Isogai, A. (2007). Cellulose Nanofibers Prepared by TEMPO-Mediated Oxidation of Native Cellulose. Biomacromolecules 8, 2485–2491. doi:10.1021/bm0703970

PubMed Abstract | CrossRef Full Text | Google Scholar

Samanta, A., Chen, H., Samanta, P., Popov, S., Sychugov, I., and Berglund, L. A. (2021). Reversible Dual-Stimuli-Responsive Chromic Transparent Wood Biocomposites for Smart Window Applications. ACS Appl. Mater. Inter. 13, 3270–3277. doi:10.1021/acsami.0c21369

CrossRef Full Text | Google Scholar

Segmehl, J. S., Laromaine, A., Keplinger, T., May-Masnou, A., Burgert, I., and Roig, A. (2018). Magnetic wood by In Situ Synthesis of Iron Oxide Nanoparticles via a Microwave-Assisted Route. J. Mater. Chem. C 6, 3395–3402. doi:10.1039/C7TC05849G

CrossRef Full Text | Google Scholar

Song, H., Xu, S., Li, Y., Dai, J., Gong, A., Zhu, M., et al. (2018a). Hierarchically Porous, Ultrathick, "Breathable" Wood‐Derived Cathode for Lithium‐Oxygen Batteries. Adv. Energ. Mater. 8, 1701203. doi:10.1002/aenm.201701203

CrossRef Full Text | Google Scholar

Song, J., Chen, C., Zhu, S., Zhu, M., Dai, J., Ray, U., et al. (2018b). Processing Bulk Natural wood into a High-Performance Structural Material. Nature 554, 224–228. doi:10.1038/nature25476

CrossRef Full Text | Google Scholar

Stamm, A. J., and Millett, M. A. (1941). The Internal Surface of Cellulosic Materials. J. Phys. Chem. 45, 43–54. doi:10.1021/j150406a004

CrossRef Full Text | Google Scholar

Stamm, A. J., and Seborg, R. M. (1939). Resin-Treated Plywood. Ind. Eng. Chem. 31, 897–902. doi:10.1021/ie50355a023

CrossRef Full Text | Google Scholar

Stamm, A. J., and Tarkow, H. (1947). Dimensional Stabilization of Wood. J. Phys. Chem. 51, 493–505. doi:10.1021/j150452a016

CrossRef Full Text | Google Scholar

Stoeckel, F., Konnerth, J., and Gindl-Altmutter, W. (2013). Mechanical Properties of Adhesives for Bonding wood-A Review. Int. J. Adhes. Adhesives 45, 32–41. doi:10.1016/j.ijadhadh.2013.03.013

CrossRef Full Text | Google Scholar

Šturcová, A., Davies, G. R., and Eichhorn, S. J. (2005). Elastic Modulus and Stress-Transfer Properties of Tunicate Cellulose Whiskers. Biomacromolecules 6, 1055–1061. doi:10.1021/bm049291k

PubMed Abstract | CrossRef Full Text | Google Scholar

Sun, J., Guo, H., Ribera, J., Wu, C., Tu, K., Binelli, M., et al. (2020). Sustainable and Biodegradable Wood Sponge Piezoelectric Nanogenerator for Sensing and Energy Harvesting Applications. ACS Nano 14, 14665–14674. doi:10.1021/acsnano.0c05493

PubMed Abstract | CrossRef Full Text | Google Scholar

Tang, Z., Pei, Z., Wang, Z., Li, H., Zeng, J., Ruan, Z., et al. (2018). Highly Anisotropic, Multichannel wood Carbon with Optimized Heteroatom Doping for Supercapacitor and Oxygen Reduction Reaction. Carbon 130, 532–543. doi:10.1016/j.carbon.2018.01.055

CrossRef Full Text | Google Scholar

Trey, S., Jafarzadeh, S., and Johansson, M. (2012). In Situ Polymerization of Polyaniline in Wood Veneers. ACS Appl. Mater. Inter. 4, 1760–1769. doi:10.1021/am300010s

CrossRef Full Text | Google Scholar

Trey, S., Olsson, R. T., Ström, V., Berglund, L., and Johansson, M. (2014). Controlled Deposition of Magnetic Particles within the 3-D Template of wood: Making Use of the Natural Hierarchical Structure of wood. RSC Adv. 4, 35678–35685. doi:10.1039/C4RA04715J

CrossRef Full Text | Google Scholar

Trost, B. (1991). The Atom Economy-Aa Search for Synthetic Efficiency. Science 254, 1471–1477. doi:10.1126/science.1962206

PubMed Abstract | CrossRef Full Text | Google Scholar

Vidiella del Blanco, M., Fischer, E. J., and Cabane, E. (2017). Underwater Superoleophobic Wood Cross Sections for Efficient Oil/Water Separation. Adv. Mater. Inter. 4, 1700584. doi:10.1002/admi.201700584

CrossRef Full Text | Google Scholar

Vitas, S., Keplinger, T., Reichholf, N., Figi, R., and Cabane, E. (2018). Functional Lignocellulosic Material for the Remediation of Copper(II) Ions from Water: Towards the Design of a wood Filter. J. Hazard. Mater. 355, 119–127. doi:10.1016/j.jhazmat.2018.05.015

CrossRef Full Text | Google Scholar

Vitas, S., Segmehl, J., Burgert, I., and Cabane, E. (2019). Porosity and Pore Size Distribution of Native and Delignified Beech Wood Determined by Mercury Intrusion Porosimetry. Materials 12, 416. doi:10.3390/ma12030416

CrossRef Full Text | Google Scholar

Wan, J., Song, J., Yang, Z., Kirsch, D., Jia, C., Xu, R., et al. (2017). Highly Anisotropic Conductors. Adv. Mater. 29, 1703331. doi:10.1002/adma.201703331

CrossRef Full Text | Google Scholar

Wang, L., Liu, Y., Zhan, X., Luo, D., and Sun, X. (2019). Photochromic Transparent wood for Photo-Switchable Smart Window Applications. J. Mater. Chem. C 7, 8649–8654. doi:10.1039/c9tc02076d

CrossRef Full Text | Google Scholar

Wang, X., Zhan, T., Liu, Y., Shi, J., Pan, B., Zhang, Y., et al. (2018a). Large‐Size Transparent Wood for Energy‐Saving Building Applications. ChemSusChem 11, 4086–4093. doi:10.1002/cssc.201801826

PubMed Abstract | CrossRef Full Text | Google Scholar

Wang, Y., Lin, X., Liu, T., Chen, H., Chen, S., Jiang, Z., et al. (2018b). Wood-derived Hierarchically Porous Electrodes for High-Performance All-Solid-State Supercapacitors. Adv. Funct. Mater. 28, 1806207. doi:10.1002/adfm.201806207

CrossRef Full Text | Google Scholar

Williams, G. I., and Wool, R. P. (2000). Composites from Natural Fibers and Soy Oil Resins. Appl. Compos. Mater. 7, 421–432. doi:10.1023/A:1026583404899

CrossRef Full Text | Google Scholar

Yamasaki, S., Sakuma, W., Yasui, H., Daicho, K., Saito, T., Fujisawa, S., et al. (2019). Nanocellulose Xerogels with High Porosities and Large Specific Surface Areas. Front. Chem. 7, 1–8. doi:10.3389/fchem.2019.00316

PubMed Abstract | CrossRef Full Text | Google Scholar

Yang, X., and Berglund, L. A. (2020a). Recycling without Fiber Degradation-Strong Paper Structures for 3D Forming Based on Nanostructurally Tailored Wood Holocellulose Fibers. ACS Sustain. Chem. Eng. 8, 1146–1154. doi:10.1021/acssuschemeng.9b06176

CrossRef Full Text | Google Scholar

Yang, X., and Berglund, L. A. (2020b). Structural and Ecofriendly Holocellulose Materials from Wood: Microscale Fibers and Nanoscale Fibrils. Adv. Mater., 2001118. doi:10.1002/adma.202001118

CrossRef Full Text | Google Scholar

Yano, H., Hirose, A., Collins, P. J., and Yazaki, Y. (2001). Effects of the Removal of Matrix Substances as a Pretreatment in the Production of High Strength Resin Impregnated wood Based Materials. J. Mater. Sci. Lett. 20, 1125–1126. doi:10.1023/A:1010992307614

CrossRef Full Text | Google Scholar

Yano, H. (2001). Potential Strength for Resin-Impregnated Compressed wood. J. Mater. Sci. Lett. 20, 1127–1129. doi:10.1023/A:1010996424453

CrossRef Full Text | Google Scholar

Yano, H., Sasaki, S., Shams, M. I., Abe, K., and Date, T. (2014). Wood Pulp-Based Optically Transparent Film: A Paradigm from Nanofibers to Nanostructured Fibers. Adv. Opt. Mater. 2, 231–234. doi:10.1002/adom.201300444

CrossRef Full Text | Google Scholar

Yokoyama, M., Gril, J., Matsuo, M., Yano, H., Sugiyama, J., Clair, B., et al. (2009). Mechanical Characteristics of Aged Hinoki wood from Japanese Historical Buildings. Comptes Rendus Physique 10, 601–611. doi:10.1016/j.crhy.2009.08.009

CrossRef Full Text | Google Scholar

Zhang, L., Xu, J., Shen, H., Xu, J., and Cao, J. (2021). Montmorillonite-catalyzed Furfurylated wood for Flame Retardancy. Fire Saf. J. 121, 103297. doi:10.1016/j.firesaf.2021.103297

CrossRef Full Text | Google Scholar

Zhu, M., Li, T., Davis, C. S., Yao, Y., Dai, J., Wang, Y., et al. (2016a). Transparent and Haze wood Composites for Highly Efficient Broadband Light Management in Solar Cells. Nano Energy 26, 332–339. doi:10.1016/j.nanoen.2016.05.020

CrossRef Full Text | Google Scholar

Zhu, M., Li, Y., Chen, F., Zhu, X., Dai, J., Li, Y., et al. (2018). Plasmonic Wood for High-Efficiency Solar Steam Generation. Adv. Energ. Mater. 8, 1701028. doi:10.1002/aenm.201701028

CrossRef Full Text | Google Scholar

Zhu, M., Song, J., Li, T., Gong, A., Wang, Y., Dai, J., et al. (2016b). Highly Anisotropic, Highly Transparent Wood Composites. Adv. Mater. 28, 5181–5187. doi:10.1002/adma.201600427

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhu, M., Wang, Y., Zhu, S., Xu, L., Jia, C., Dai, J., et al. (2017). Anisotropic, Transparent Films with Aligned Cellulose Nanofibers. Adv. Mater. 29, 1606284. doi:10.1002/adma.201606284

CrossRef Full Text | Google Scholar

Keywords: wood nanotechnology, biocomposite, nanocellulose, nanostructure, building material, biopolymer, nanocomposite

Citation: Montanari C, Olsén P and Berglund LA (2021) Sustainable Wood Nanotechnologies for Wood Composites Processed by In-Situ Polymerization. Front. Chem. 9:682883. doi: 10.3389/fchem.2021.682883

Received: 19 March 2021; Accepted: 10 June 2021;
Published: 01 July 2021.

Edited by:

Francisco Martin-Martinez, Swansea University, United Kingdom

Reviewed by:

Miha Humar, University of Ljubljana, Slovenia
Renren Deng, Zhejiang University, China

Copyright © 2021 Montanari, Olsén and Berglund. This is an open-access article distributed under the terms of the Creative Commons Attribution License (CC BY). The use, distribution or reproduction in other forums is permitted, provided the original author(s) and the copyright owner(s) are credited and that the original publication in this journal is cited, in accordance with accepted academic practice. No use, distribution or reproduction is permitted which does not comply with these terms.

*Correspondence: Lars A. Berglund, blund@kth.se

Disclaimer: All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article or claim that may be made by its manufacturer is not guaranteed or endorsed by the publisher.