A New Strategy to Regulate the Selectivity of Photo-Mediated Catalytic Reaction

  • Hefei National Laboratory for Physical Sciences at the Microscale, CAS Key Laboratory of Materials for Energy Conversion and Department of Chemical Physics, University of Science and Technology of China, Hefei, China

Here we developed a new method for regulating the selectivity of photo-mediated catalytic reaction by manipulating the surface charge of Au/TiO2 (gold/titanium dioxide) catalysts within chemical reaction timescales. Two kinds of photocatalytic reactions, hydrogenation of acetophenone and benzyl alcohol oxidation, have been applied to investigate the photocatalytic performance over Au/TiO2 catalysts with tunable surface charges. We found that a suitable timescale of switching surface charge on Au would benefit for the enhanced quantum efficiency and play different roles in the selectivity of desired products in hydrogenation and oxidation reactions. Au/TiO2 catalyst under 5 μs flashing light irradiation exhibits much higher selectivity of 1-phenylethanol in the hydrogenation of acetophenone than that under continuous light and 5 s flashing light irradiation; by contrast, Au/TiO2 catalysts under both flashing light and continuous light irradiation exhibit a similar selectivity of benzaldehyde in benzyl alcohol oxidation. Our findings will benefit for a better understanding of electronic structure–mediated reaction mechanism and be helpful for achieving highly efficient photocatalytic systems.

Introduction

Selectivity is one of the most important criteria for evaluating a catalytic system (Lee et al., 2009; Somorjai and Park 2008). The design and development of highly selective catalytic system will benefit for a green and cost-efficient catalytic application, because the reaction with higher selectivity generates fewer toxic by-products, benefits for the further separation and application of products, and utilizes the reactants more efficiently (Zaera 2009). In recent years, scientists have made great efforts into developing highly selective catalytic system, and several successful examples have been achieved. The concepts of single-atom catalysis and single-site catalysis have been developing rapidly in the past 10 years and now have been widely accepted and considered as highly effective catalysts for increasing the selectivity of desired products (Li et al., 2020; Wang et al., 2018; Yang et al., 2013). In the last 5 years, Chinese researchers have made a huge breakthrough in the selective conversion of syngas to light olefins by applying bifunctional catalysts, in which the zeolites would convert reaction intermediates generated from the oxides and totally change the product thermodynamic distributions (Cheng et al., 2016; Jiao et al., 2016). Wang’s group further introduced a concept of relay catalysis and achieved high-yield C2+ products based on these findings (Zhou et al., 2018). Similar to the bifunctional catalysts, an emerging approach named chemical looping partial oxidation (CLPO) has been developed and successfully applied to achieve near 100% CO selectivity for methane utilization, in which the redox cycle takes place in an interconnected reactor with a reducer and an oxidizer (Zeng et al., 2018; Liu et al., 2019). Until now, most successful attempts of highly selective systems are based on the optimization of catalytic active sites or the modulation of thermodynamic equilibrium, in which suitable and uniform active sites with lower energy barrier toward the designed pathway would benefit for achieving highly selective desired products, and the concept of “tandem catalysis” and “chemical looping” would optimize the product thermodynamic distributions. Notably, there are multi-steps or multi-pathways in one catalytic reaction, and the “suitable” active site might be only suitable for the rate-determining step rather than being suitable for all the steps. The design of the tunable active site within a chemical step timescale might be a good strategy to optimize the performance of catalytic reaction. More specifically, as shown in Figure 1, both active site 1 and active site 2 are not favorable to selectively form the desired product since the heights of energy barriers (Ea1 and Ea2) in the formation of desired products are much larger than those in the formation of by-products. By contrast, the tunable active site within a chemical reaction timescale would build up a new reaction pathway and greatly enhance the selectivity of the desired product. However, most chemical reaction timescales are within the range from μs to ms; it is almost impossible to manipulate the active site in such a short timescale.

FIGURE 1
www.frontiersin.org

FIGURE 1. Schematic diagram of catalytic reaction pathways over metal with the tunable active site within a chemical reaction timescale.

Recently, we developed a new method for manipulating the surface charges of photocatalyst within chemical reaction timescales by applying a home-modified LED light source (Qian and Huang 2019), in which the electronic structures of supported metal NPs could be tunable within the timescale from s to μs. These findings provide us a great opportunity to design a reaction channel like chemical loop by alternately controlling the electronic structures of metal NPs within the timescale of an elementary reaction, which might be helpful to design a highly active catalytic system. In this study, we investigated the catalytic performance of metal with tunable charge by applying both hydrogenation of acetophenone and benzyl alcohol oxidation over Au/TiO2 photocatalysts. Similar to our previous findings, a suitable timescale of switching surface charge on Au would benefit for the enhanced quantum efficiency in both hydrogenation of acetophenone and benzyl alcohol oxidation. Interestingly, Au/TiO2 catalyst under 5 μs flashing light irradiation exhibits much higher selectivity of 1-phenylethanol in the hydrogenation of acetophenone than Au/TiO2 catalyst under continuous light and 5 s flashing light irradiation; by contrast, Au/TiO2 catalysts under both flashing light and continuous light irradiation exhibit a similar selectivity of benzaldehyde in benzyl alcohol oxidation. Our results provide a new method for regulating the selectivity of photo-mediated catalytic reaction by manipulating the surface charge of supported metal NPs, which would be helpful for further achieving highly efficient photocatalytic systems.

Experimental Section

Photocatalyst synthesis: Au/TiO2 heterostructure with 3% weight percentages (3%) of Au on TiO2 (anatase) was prepared using deposition precipitation (DP) method (Qian et al., 2013; Qian et al., 2018). During the DP procedure, HAuCl4•3H2O (≥99.9%, Aldrich) was dissolved in Nanopure water to prepare a 0.020 M aqueous solution of HAuCl4. The aqueous solution of HAuCl4, TiO2 (≥99.5% trace metals basis, Aldrich), and distilled water was added to a flask and stirred vigorously at 323 K for 30 min. An appropriate amount of ammonium hydroxide (ACS reagent) was added to adjust the pH value of the system to ∼8, and the system was stirred at 333 K for 4 h. The solid was centrifuged, washed with Nanopure water three times, dried at 333 K for 12 h, and then calcined at 473 K for 4 h.

Home-modified LED light source: 365 nm LED light (Thorlabs M365LP1) was connected with an advanced four-channel LED driver (Thorlabs DC4104). The external control mode was chosen in our study, in which the LED light was controlled by square wave signals generated by a 30-MHz synthesized function generator. The irradiation time is equal to the dark period within one cycle by applying a square wave signal, and the circulating period was further controlled by changing the frequencies of generated signals. In our research, the cyclic frequency was designed from 0.1 to 1 × 105 Hz, resulting that the cycle time is from 10 s to 10 μs and the irradiation time is from 5 s to 5 μs in each cycle (Qian and Huang 2019).

Photocatalytic Reaction Test

The hydrogenation of acetophenone was performed following the method described in the previous report and conducted under an argon atmosphere at 30°C (Ke et al., 2012). Typically, 3 mmol acetophenone was dissolved into 30 ml isopropanol, and 3 ml solution of 0.1 M KOH in isopropanal and 50 mg of the 3% Au/TiO2 catalyst were added into the mixture that was then stirred by a magnetic stirrer during the reaction and illuminated by a 365-nm LED light with controllable frequencies. The light intensity was 0.28 W/cm2, and the irradiation area is about 6.5 cm2. During these reactions, 0.5 ml of the mixture were collected at a given irradiation time and filtered through centrifugation to remove the Au/TiO2 catalyst. The filtrates were analyzed by a gas chromatograph GC-7806 equipped with HP-5 column.

The benzyl alcohol oxidation was performed following the method described in the previous report and conducted under an O2 atmosphere at 30°C (Tanaka et al., 2012). Typically, 100 mg of the 3% Au/TiO2 catalyst were added into 10 ml distilled water, bubbled with O2, and sealed with a rubber septum. 20 μmol benzyl alcohol was injected into the suspension and then illuminated by a 365-nm LED light with controllable frequencies. The light intensity was 0.28 W/cm2, and the irradiation area is about 2 cm2. During these reactions, the amount of carbon dioxide (CO2) in the gas phase was measured using a gas chromatograph GC-7806 equipped with a Porapak QS column. The amounts of benzyl alcohol and benzaldehyde in the liquid phase were determined with a Shimadzu GC-7806 gas chromatograph equipped with a DB-1 capillary column. Toluene was used as an internal standard sample.

Material characterization: Powder X-ray diffraction (XRD) patterns were recorded in the 2θ at the range of 20°–80° on a Philips X’Pert Pro Super diffractometer with Cu Kα radiation (λ = 0.15406 nm) operating at 40 kV and 50 mA. Transmission electron microscopy (TEM) and high-resolution transmission electron microscopy (HRTEM) images were obtained on a JEM-2100F high-resolution transmission electron microscope.

Quantum yield measurement was performed following the method described in the previous report (Han et al., 2012). The intensities of incident lights were measured by Extech LT300 Light Meter. The number of incident photons of flashing light was normalized by a theoretical continuous light intensity.

P=chnλt,
qp=nt(s),
=2kqp,

where λ is taken to be 365 nm, h is Planck’s constant (in J/s), c is the speed of light (in m/s), n is the number of photons, t is the time (in second), and qp is the photon flux (number of photons per second).

Results and Discussion

3%-Au/TiO2 catalyst was prepared by the DP method with anatase TiO2 as support. Figure 2A shows the X-ray diffraction (XRD) patterns of the Au/TiO2 catalyst. All the diffraction peaks could be assigned to the anatase TiO2 (JCPDS card no. 89–4,921), and no diffraction peaks attributing to Au could be identified, which suggests that the supported Au NPs should be dispersed on the TiO2 support (Zhou et al., 2020). Figure 2B displays the transmission electron microscopy (TEM) images and size distribution of supported Au NPs. More than 150 Au NPs have been counted for the size distribution calculation, and the average particle size of 3% Au/TiO2 is 3.6 ± 1.0 nm (Figure 2C).

FIGURE 2
www.frontiersin.org

FIGURE 2. XRD (A), TEM image (B–D), and Au NP size distribution (E) of Au/TiO2 photocatalysts.

We further separately investigated the photocatalytic performances of both hydrogenation of acetophenone and benzyl alcohol oxidation over 3%-Au/TiO2 catalysts by applying our home-modified LED light with desirable irradiation times. The hydrogenation of acetophenone was conducted under an argon atmosphere at 30°C by following the method described in the previous report (Ke et al., 2012). No detectable 1-phenylethanol has been found over Au/TiO2 catalyst without light irradiation, suggesting that supported Au NPs could not catalyze hydrogenation of acetophenone to 1-phenylethanol. As shown in Figure 3, the amount of 1-phenylethanol production increases linearly under 365 nm continuous LED light irradiation, indicating that the reaction rate of 1-phenylethanol production does not change within our experimental conditions. The catalytic performances of hydrogenation of acetophenone over 3%-Au/TiO2 catalyst have also been conducted under our home-designed flashing light irradiation for 24 h, all the catalysts display a linear relationship between the time and the amount of 1-phenylethanol production, and the reaction rates of 1-phenylethanol production are 0.97 ± 0.06, 0.57 ± 0.03, 0.73 ± 0.04, 0.77 ± 0.03, 0.81 ± 0.03, and 0.82 ± 0.03 mmol×g−1cat×h−1 under continuous light, 5 s flashing light, 5 ms flashing light, 500 μs flashing light, 50 μs flashing light, and 5 μs flashing light, respectively. We further measured the intensities of incident lights and calculated the quantum efficiencies by following the method described in the previous reports. The quantum yields of 1-phenylethanol production at 365 nm are 0.48 ± 0.03%, 0.57 ± 0.04%, 0.74 ± 0.04%, 0.77 ± 0.03%, 0.81 ± 0.04%, and 0.82 ± 0.03% under continuous light, 5 s flashing light, 5 ms flashing light, 500 μs flashing light, 50 μs flashing light, and 5 μs flashing light, respectively, as shown in Figure 4. Similar to our previous findings in the hydrogen evolution, the quantum yields of 1-phenylethanol production under flashing lights are higher than those under continuous light. Specifically, 5 s flashing light displays a similar quantum yield with continuous light, and the quantum yield gradually increases with decreasing the irradiation time in each cycle of flashing light. 5 μs flashing light irradiation exhibits the highest quantum yield among all the flashing lights irradiations, which is 1.7 times as high as that under continuous light. These findings suggest that the quantum efficiency of photons in the hydrogenation of acetophenone has been successfully promoted by controlling photo-generated charge carriers in the timescale of hydrogenation reaction.

FIGURE 3
www.frontiersin.org

FIGURE 3. Hydrogenation of acetophenone activities over Au/TiO2 under and without 365 nm continuous light irradiations.

FIGURE 4
www.frontiersin.org

FIGURE 4. Quantum yields of 1-phenylethanol formation of hydrogenation of acetophenone over 3%-Au/TiO2 catalysts under flashing light with different cyclic frequency irradiations.

More interestingly, we observed an increment of the selectivity of 1-phenylethanol formation with decreasing the irradiation time in each cycle of flashing light. As shown in Figure 5, the selectivities of 1-phenylethanol production in hydrogenation of acetophenone are 0.60 ± 0.04, 0.59 ± 0.04, 0.71 ± 0.03, 0.69 ± 0.05, 0.80 ± 0.04, and 0.83 ± 0.04 under continuous light, 5 s flashing light, 5 ms flashing light, 500 μs flashing light, 50 μs flashing light, and 5 μs flashing light, respectively. 5 s flashing light displays similar 1-phenylethanol selectivity with continuous light; by contrast, the 1-phenylethanol selectivity over 3%-Au/TiO2 catalyst under 5 μs flashing light irradiation could reach to 83%, which is much higher than those under continuous light and 5 s flashing light irradiations. Besides the quantum efficiency of photons, the selectivity of the desirable product has also been promoted by establishing a suitable timescale of switching the surface charge on supported Au with our home-modified LED irradiation.

FIGURE 5
www.frontiersin.org

FIGURE 5. Selectivities of 1-phenylethanol formation of hydrogenation of acetophenone over 3%-Au/TiO2 catalysts under flashing light with different cyclic frequency irradiations.

The photocatalytic performances of benzyl alcohol oxidation over 3%-Au/TiO2 catalysts have also been investigated by following the method described in the previous report, as shown in Figure 6. Supported Au NPs could catalyze the formation of benzaldehyde without light irradiation; however, compared to the catalytic performance under the 365 nm light irradiation, the contribution from the dark reaction could be ignored. Notably, different from the linear increment of 1-phenylethanol production in the hydrogenation of acetophenone, the amount of benzaldehyde production increases nonlinearly in the benzyl alcohol oxidation, suggesting that the reaction rate of benzaldehyde production is strongly related to the concentration of the reactants, which is consistent with a previous kinetics study of benzyl alcohol oxidation (first-order reaction) (Galvanin et al., 2018). The catalytic performances under different flashing light irradiations within 120 min have also been investigated, as shown in Figure 7; the calculated reaction rates of benzaldehyde production are 91.2 ± 2.3, 48.4 ± 1.9, 89.0 ± 3.4, 85.0 ± 3.1, 78.0 ± 2.2, and 71.4 ± 1.7 μmol×g−1cat×h−1 under continuous light, 5 s flashing light, 5 ms flashing light, 500 μs flashing light, 50 μs flashing light, and 5 μs flashing light, respectively. We further measured the intensities of incident lights and calculated the quantum efficiencies by following the method described in the previous reports. The quantum yields of benzaldehyde production at 365 nm are 0.30 ± 0.01%, 0.32 ± 0.01%, 0.58 ± 0.02%, 0.56 ± 0.02%, 0.51 ± 0.02%, and 0.47 ± 0.01% under continuous light, 5 s flashing light, 5 ms flashing light, 500 μs flashing light, 50 μs flashing light, and 5 μs flashing light, respectively. The quantum yields of benzaldehyde production under flashing lights are higher than those under continuous light, which is consistent with our previous findings in hydrogen evolution and hydrogenation of acetophenone; 5 s flashing light displays a similar quantum yield with continuous light, while a suitable timescale 5 ms flashing light exhibits the highest quantum yield of benzaldehyde production.

FIGURE 6
www.frontiersin.org

FIGURE 6. Activities of benzyl alcohol oxidation over Au/TiO2 under and without 365 nm continuous light irradiations.

FIGURE 7
www.frontiersin.org

FIGURE 7. Quantum yields of benzaldehyde production of benzyl alcohol oxidation over 3%-Au/TiO2 catalysts under flashing light with different cyclic frequency irradiations.

Figure 8 displays the selectivity of benzaldehyde production over 3%-Au/TiO2 catalyst with a tunable timescale of flashing light irradiation within the first half hour. The selectivities of benzaldehyde production in benzyl alcohol oxidation are 0.35 ± 0.03, 0.33 ± 0.01, 0.33 ± 0.02, 0.34 ± 0.02, 0.35 ± 0.03, and 0.35 ± 0.04 under continuous light, 5 s flashing light, 5 ms flashing light, 500 μs flashing light, 50 μs flashing light, and 5 μs flashing light, respectively. Different from the increment of the selectivity of 1-phenylethanol formation with decreasing the timescale of flashing light, Au/TiO2 catalysts under different flashing light irradiations exhibit a similar benzaldehyde selectivity in the benzyl alcohol oxidation, which suggests that the influence of surface electronic structure of supported Au on the benzyl alcohol oxidation should be different from that on the hydrogenation of acetophenone.

FIGURE 8
www.frontiersin.org

FIGURE 8. Selectivities of benzaldehyde production of benzyl alcohol oxidation over 3%-Au/TiO2 catalysts under flashing light with different cyclic frequency irradiations.

Our results demonstrate that a suitable timescale of modifying surface charges on supported Au would enhance the quantum efficiency of both hydrogenation and oxidation reactions but play different roles to the selectivity of desired products. We believe that the transferred electrons from TiO2 to Au with suitable lifetime contribute to this phenomenon, in which negative-charge Au, partial negative–charge Au, and neutral-charge Au have been established within the timescale from s to μs. Supported Au displays negative charge due to the existence of transferred electrons from TiO2 under the 365-nm continuous light irradiation, and exhibits an alternate appearance of negative charge, partial negative charge, and neutral charge with increasing the time of dark period in the flashing light. In the hydrogenation of acetophenone, the rate-determining step has been ascribed to the electron transfer process from catalyst to adsorbed acetophenone (Kohtani et al., 2012), and over-reduction will cause the formation of by-products like ethylbenzene, acetylcyclohexane, and 1-cyclohexylethanol (Fujita et al., 2016). In a cycle of our flashing light, the light irradiation period is similar to the continuous light irradiation, while the dark period with partial negative–charge and neutral-charge Au contributes to the enhanced quantum efficiency and promoted selectivity of 1-phenylethanol production. In particular, the transferred electrons from TiO2 to Au with suitable lifetime could directly catalyze hydrogenation of acetophenone in the dark period. Compared with the negative-charge Au under the 365-nm light irradiation, this partial negative–charge and neutral-charge Au represents low-density electrons and could prevent acetophenone from over-reduction. This is the reason that both the quantum efficiency and selectivity of 1-phenylethanol production obviously increase under our home-modified LED flashing light irradiation. In the benzyl alcohol oxidation, the photo-generated charge carriers would facilitate the formation of nonselective ˙OH radicals, which would cause an over-oxidation of benzyl alcohol and play negative role to selectively catalyze benzyl alcohol into benzaldehyde (Feng et al., 2011). Although the charge carriers within supported Au and TiO2 could facilitate the formation of ˙OH radicals in the dark period and increase the quantum yields of benzaldehyde production, different from the hydrogenation of acetophenone, the partial negative–charge and neutral-charge Au could only involve into the formation of ˙OH radicals rather than directly catalyzing benzyl alcohol oxidation. That is the reason we did not observe any change in the selectivity of benzaldehyde production.

Conclusion

By investigating the photocatalytic performance over supported Au under our home-modified flashing light irradiations, we developed a new strategy to control the reaction pathway by manipulating the electronic structures of supported Au within the reaction timescale. In particular, both the quantum efficiency and selectivity of 1-phenylethanol production in the hydrogenation of acetophenone over supported Au obviously increased under flashing light irradiations, while the selectivity of benzaldehyde production in the benzyl alcohol oxidation did not change under flashing light irradiations. We believe that these findings will benefit for a better understanding of electronic structure–mediated reaction mechanism and be helpful for achieving highly efficient photocatalytic systems.

Data Availability Statement

The original contributions presented in the study are included in the article/Supplementary Material; further inquiries can be directed to the corresponding author.

Author Contributions

All authors listed have made a substantial, direct, and intellectual contribution to the work and approved it for publication.

Funding

This work was financially supported by the National Natural Science Foundation of China (Grant Nos. 21872128 and 21703001), the Fundamental Research Funds for the Central Universities (WK2060030030), and the Anhui Provincial Natural Scientific Foundation project (1808085MB44).

Conflict of Interest

The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.

Publisher’s Note

All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article, or claim that may be made by its manufacturer, is not guaranteed or endorsed by the publisher.

References

Cheng, K., Gu, B., Liu, X., Kang, J., Zhang, Q., and Wang, Y. (2016). Direct and Highly Selective Conversion of Synthesis Gas into Lower Olefins: Design of a Bifunctional Catalyst Combining Methanol Synthesis and Carbon-Carbon Coupling. Angew. Chem. Int. Ed. 55 (15), 4725–4728. doi:10.1002/anie.201601208

PubMed Abstract | CrossRef Full Text | Google Scholar

Feng, W., Wu, G., Li, L., and Guan, N. (2011). Solvent-free Selective Photocatalytic Oxidation of Benzyl Alcohol over Modified TiO2. Green. Chem. 13 (11), 3265–3272. doi:10.1039/c1gc15595d

CrossRef Full Text | Google Scholar

Fujita, S.-i., Onodera, Y., Yoshida, H., and Arai, M. (2016). Selective Hydrogenation of Acetophenone with Supported Pd and Rh Catalysts in Water, Organic Solvents, and CO2-dissolved Expanded Liquids. Green. Chem. 18 (18), 4934–4940. doi:10.1039/c6gc00583g

CrossRef Full Text | Google Scholar

Galvanin, F., Sankar, M., Cattaneo, S., Bethell, D., Dua, V., Hutchings, G. J., et al. (2018). On the Development of Kinetic Models for Solvent-free Benzyl Alcohol Oxidation over a Gold-Palladium Catalyst. Chem. Eng. J. 342, 196–210. doi:10.1016/j.cej.2017.11.165

CrossRef Full Text | Google Scholar

Han, Z., Qiu, F., Eisenberg, R., Holland, P. L., and Krauss, T. D. (2012). Robust Photogeneration of H2 in Water Using Semiconductor Nanocrystals and a Nickel Catalyst. Science 338 (6112), 1321–1324. doi:10.1126/science.1227775

PubMed Abstract | CrossRef Full Text | Google Scholar

Jiao, F., Li, J., Pan, X., Xiao, J., Li, H., Ma, H., et al. (2016). Selective Conversion of Syngas to Light Olefins. Science 351 (6277), 1065–1068. doi:10.1126/science.aaf1835

PubMed Abstract | CrossRef Full Text | Google Scholar

Ke, X., Sarina, S., Zhao, J., Zhang, X., Chang, J., and Zhu, H. (2012). Tuning the Reduction Power of Supported Gold Nanoparticle Photocatalysts for Selective Reductions by Manipulating the Wavelength of Visible Light Irradiation. Chem. Commun. 48 (29), 3509–3511. doi:10.1039/c2cc17977f

PubMed Abstract | CrossRef Full Text | Google Scholar

Kohtani, S., Yoshioka, E., Saito, K., Kudo, A., and Miyabe, H. (2012). Adsorptive and Kinetic Properties on Photocatalytic Hydrogenation of Aromatic Ketones upon UV Irradiated Polycrystalline Titanium Dioxide: Differences between Acetophenone and its Trifluoromethylated Derivative. J. Phys. Chem. C 116 (33), 17705–17713. doi:10.1021/jp3056174

CrossRef Full Text | Google Scholar

Lee, I., Delbecq, F., Morales, R., Albiter, M. A., and Zaera, F. (2009). Tuning Selectivity in Catalysis by Controlling Particle Shape. Nat. Mater 8 (2), 132–138. doi:10.1038/nmat2371

PubMed Abstract | CrossRef Full Text | Google Scholar

Li, Z., Ji, S., Liu, Y., Cao, X., Tian, S., Chen, Y., et al. (2020). Well-Defined Materials for Heterogeneous Catalysis: From Nanoparticles to Isolated Single-Atom Sites. Chem. Rev. 120 (2), 623–682. doi:10.1021/acs.chemrev.9b00311

PubMed Abstract | CrossRef Full Text | Google Scholar

Liu, Y., Qin, L., Cheng, Z., Goetze, J. W., Kong, F. H., Fan, J. A., et al. (2019). Near 100% CO Selectivity in Nanoscaled Iron-Based Oxygen Carriers for Chemical Looping Methane Partial Oxidation. Nat. Commun. 10, 5503. doi:10.1038/s41467-019-13560-0

PubMed Abstract | CrossRef Full Text | Google Scholar

Qian, K., and Huang, W. (2019). A New Strategy to Enhance Quantum Efficiency of Photo-Mediated Hydrogen Evolution. Catal. Today 327, 334–339. doi:10.1016/j.cattod.2018.04.022

CrossRef Full Text | Google Scholar

Qian, K., Luo, L., Bao, H., Hua, Q., Jiang, Z., and Huang, W. (2013). Catalytically Active Structures of SiO2-Supported Au Nanoparticles in Low-Temperature CO Oxidation. Catal. Sci. Technol. 3 (3), 679–687. doi:10.1039/c2cy20481a

CrossRef Full Text | Google Scholar

Qian, K., Zhao, E. W., He, S., and Wei, W. D. (2018). The Effect of Surface Electronic Structures of Au/TiO2 on Sonophotochemical Reactions. Chin. Chem. Lett. 29 (6), 783–786. doi:10.1016/j.cclet.2018.03.027

CrossRef Full Text | Google Scholar

Somorjai, G. A., and Park, J. Y. (2008). Molecular Factors of Catalytic Selectivity. Angew. Chem. Int. Edition 47 (48), 9212–9228. doi:10.1002/anie.200803181

CrossRef Full Text | Google Scholar

Tanaka, A., Hashimoto, K., and Kominami, H. (2012). Preparation of Au/CeO2 Exhibiting Strong Surface Plasmon Resonance Effective for Selective or Chemoselective Oxidation of Alcohols to Aldehydes or Ketones in Aqueous Suspensions under Irradiation by Green Light. J. Am. Chem. Soc. 134 (35), 14526–14533. doi:10.1021/ja305225s

CrossRef Full Text | Google Scholar

Wang, A., Li, J., and Zhang, T. (2018). Heterogeneous Single-Atom Catalysis. Nat. Rev. Chem. 2 (6), 65–81. doi:10.1038/s41570-018-0010-1

CrossRef Full Text | Google Scholar

Yang, X.-F., Wang, A., Qiao, B., Li, J., Liu, J., and Zhang, T. (2013). Single-Atom Catalysts: A New Frontier in Heterogeneous Catalysis. Acc. Chem. Res. 46 (8), 1740–1748. doi:10.1021/ar300361m

PubMed Abstract | CrossRef Full Text | Google Scholar

Zaera, F. (2009). Regio-, Stereo-, and Enantioselectivity in Hydrocarbon Conversion on Metal Surfaces. Acc. Chem. Res. 42 (8), 1152–1160. doi:10.1021/ar900049m

PubMed Abstract | CrossRef Full Text | Google Scholar

Zeng, L., Cheng, Z., Fan, J. A., Fan, L.-S., and Gong, J. (2018). Metal Oxide Redox Chemistry for Chemical Looping Processes. Nat. Rev. Chem. 2 (11), 349–364. doi:10.1038/s41570-018-0046-2

CrossRef Full Text | Google Scholar

Zhou, W., Kang, J., Cheng, K., He, S., Shi, J., Zhou, C., et al. (2018). Direct Conversion of Syngas into Methyl Acetate, Ethanol, and Ethylene by Relay Catalysis via the Intermediate Dimethyl Ether. Angew. Chem. Int. Ed. 57 (37), 12012–12016. doi:10.1002/anie.201807113

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhou, X., Qian, K., Zhang, Y., Li, D., Wei, Z., Wang, H., et al. (2020). Tuning the Size of Photo-Deposited Metal Nanoparticles via Manipulating Surface Defect Structures of TiO2 Nanocrystals. Chem. Commun. 56 (13), 1964–1967. doi:10.1039/c9cc09642f

CrossRef Full Text | Google Scholar

Keywords: selectivity, photo-mediated charge, reaction pathway, timescale of reaction, quantum efficiency

Citation: Qian K (2021) A New Strategy to Regulate the Selectivity of Photo-Mediated Catalytic Reaction. Front. Chem. 9:673857. doi: 10.3389/fchem.2021.673857

Received: 28 February 2021; Accepted: 18 June 2021;
Published: 09 August 2021.

Edited by:

Yihan Zhu, Zhejiang University of Technology, China

Reviewed by:

Zhuo Xiong, Huazhong University of Science and Technology, China
Guigao Liu, Nanjing University of Science and Technology, China

Copyright © 2021 Qian. This is an open-access article distributed under the terms of the Creative Commons Attribution License (CC BY). The use, distribution or reproduction in other forums is permitted, provided the original author(s) and the copyright owner(s) are credited and that the original publication in this journal is cited, in accordance with accepted academic practice. No use, distribution or reproduction is permitted which does not comply with these terms.

*Correspondence: Kun Qian, qiankun@ustc.edu.cn

Disclaimer: All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article or claim that may be made by its manufacturer is not guaranteed or endorsed by the publisher.