Selective Catalytic Oxidation of Benzyl Alcohol to Benzaldehyde by Nitrates

In this paper, ferric nitrate was used to oxidize benzyl alcohol in a mild condition and demonstrated its better performance compared to HNO₃. In the reaction, the conversion rate and product selectivity could be both as high as 95% in N₂ atmosphere, while the benzaldehyde yield also reached 85% in air. Similar to Fe(NO₃)₃·9H₂O, the other metallic nitrates such as Al(NO₃)₃·9H₂O and Cu(NO₃)₂·3H₂O could also oxidize the benzyl alcohol with high activity. The applicability of Fe(NO₃)₃·9H₂O for other benzylic alcohol was also investigated, and the reaction condition was optimized at the same time. The results showed the Fe(NO₃)₃·9H₂O would be more conducive in oxidizing benzyl alcohol under the anaerobic condition. The experiments in N₂ or O₂ atmospheres were conducted separately to study the catalytic mechanism of Fe(NO₃)₃. The results showed the co-existence of Fe³⁺ and ${\text{NO}}_3^{-}$ will generate high activity, while either was with negligible oxidation property. The cyclic transformation of Fe³⁺ and Fe²⁺ provided the catalytic action to the benzyl alcohol oxidation. The role of ${\text{NO}}_3^{-}$ was also an oxidant, by providing HNO₂ in anaerobic condition, while ${\text{NO}}_3^{-}$ would be regenerated from NO in aerobic condition. O₂ did not oxidize the benzyl alcohol conversion directly, while it could still be beneficial to the procedure by eliminating the unwelcome NO and simultaneously reinforcing the circulation of Fe²⁺ and Fe³⁺, which therefore forms a green cyclic oxidation. Hence, the benzyl alcohol oxidation was suggested in an air atmosphere for efficiency and the need of green synthesis.

Introduction

Benzaldehyde (BzH) is one of the most important chemicals among the aromatic aldehyde family. It is used as the raw material for a large number of products, including perfume, beverage, pharmaceutical intermediates, and so on (Jachuck et al., 2006; Ragupathi et al., 2015; Ndolomingo and Meijboom, 2017; Zhu et al., 2017). Traditionally, BzH was synthesized by hydrolysis of benzal chloride or vapor/liquid-phase oxidation of toluene. In the former method, the chlorinated by-products and corresponding toxic acidic would be generated, which brought troubles to the industrial application (Mal et al., 2018; Lu et al., 2019), while the vapor/liquid oxidation of toluene was also limited because of the harsh reaction conditions and low selectivity (Miao et al., 2016). Recently, BzH production with benzyl alcohol oxidation was widely adopted in industry, based on its advantages of easy-control condition and high yield (Lv et al., 2018; Thao et al., 2018). In this method, potassium permanganate (KMnO₄) (Mahmood et al., 1999) and dichromate (K₂Cr₂O₇) (Thottathil et al., 1986) with a strong oxidizing property are chosen as oxidants. While those oxidants were not perfect industrial reagents, leading to a series of environmental issues and high cost.

Nitric acid (HNO₃), as a rather inexpensive and high-performance oxidant, is commonly used in industry (Joshi et al., 2005; Aellig et al., 2012). For example, the niacin (vitamin B3) is synthesized from substituted pyridines oxidized by HNO₃ (Yu et al., 2011). HNO₃ is also regarded as the initiator in benzyl alcohol oxidation in the presence of O₂ (Miao et al., 2011; Luo et al., 2012, 2014). In this approach, HNO₃ initiates the oxidation of alcohols by decomposing NO₂, which further formed HNO₂ with H₂O. HNO₂ subsequently attacks substrate and generates the products by a series of reactions with releasing NO_x. Finally, the HNO₃ is regenerated by the NO_x oxidation by O₂. However, the disadvantages of HNO₃ should not be ignored totally, due to the risks of pollution and corrosion. Green oxidants such as hydrogen peroxide (H₂O₂) (Cánepa et al., 2017) and O₂ (Yu et al., 2011; Cao et al., 2013, 2015; Zhu et al., 2017; Chen et al., 2018a,b; Yuan et al., 2018) have been attracting extensive attention for many years. It is noted that O₂ or H₂O₂ itself has almost no activity and its oxidative performance needs to be activated by other materials.

Besides oxidants, the catalytic systems, including homogeneous and heterogeneous, have been developed. In the past decade, the heterogeneous precious metals catalysts, like Au (Zhan et al., 2012; Albadi et al., 2014), Pt (Liu et al., 2017), Ru (Ganesamoorthy et al., 2013), and Pd (Villa et al., 2010), were employed for selective oxidation of benzyl alcohols to BzH, based on their excellent performances. However, the high cost and limited resource of noble metals hindered their practical application. Moreover, the catalytic activity of heterogeneous catalysts would be lower than their homogeneous counterparts after several recycles (Parmeggiani and Camilla, 2012). Hence, the metal-based homogeneous catalysts, including Ru (Shimizu et al., 2005), V (Hanson et al., 2008), Cu (Hansen et al., 2013; Jia et al., 2014), and Fe (Jiang et al., 2016; Li et al., 2016; Miao et al., 2016; Hu et al., 2018), continued to gain great interests.

Among those homogenous catalysts, non-toxic, abundant, and bio-friendly, iron-based metals have widely aroused attentions (Martin and Suárez, 2002; Wang et al., 2005; Zhang et al., 2013; Hu et al., 2016, 2018). Zhang and co-workers reported a series of Fe catalysts, such as FeBr₃, Fe₂O₃, and Fe₂(SO₄)₃, with performance catalyzing benzylamine to imine in air atmosphere (Zhang et al., 2013). Wang et al. (2005) found an effective FeCl₃/TEMPO/NaNO₂ catalyst for benzyl alcohol oxidation, whose yield of benzaldehyde was as high as 99.0%. In this catalytic system, NaNO₂ activated the catalytic reaction by releasing NO₂, which oxidized Fe²⁺-TEMPOH to Fe³⁺-TEMPO. Consequently, Fe³⁺-TEMPO oxidized the benzyl alcohol to be benzaldehyde (Wang et al., 2005). Zhang and co-workers introduced Fe into imidazolium and successfully prepared a nice iron-based catalyst [Imim-TEMPO][FeCl₄]/NaNO₂ (Miao et al., 2011), showing a good activity for the selective oxidation of aromatic alcohols under 5% NaNO₂. The catalytic mechanism of [Imim-TEMPO][FeCl₄]/NaNO₂ was similar to that of FeCl₃/TEMPO/NaNO₂, and the aromatic alcohol was oxidized in the process of redox between Fe³⁺ and NO₂. Martin and co-workers (Martin and Suárez, 2002) discovered an efficient system by combining Fe(NO₃)₃ and FeBr₃ for selective oxidation of benzylic alcohol to corresponding aldehyde. Though the Fe-based catalysts had good activity, problems are obvious. For example, the introduction of Br or co-catalyst (TEMPO) has increased the cost as well as environmental concerns, resulting in weaker competitive when industrial applications.

The reported Fe-based catalytic systems usually contain ${\text{NO}}_2^{-}$. In fact, ${\text{NO}}_2^{-}$ releases active NO₂ and initiate the alcohol oxidation by several redox reactions. Inspired by this, we are intrigued whether the combination of metal iron (Mⁿ⁺) and ${\text{NO}}_3^{-}$/${\text{NO}}_2^{-}$ can construct an efficient catalytic system for the alcohol oxidation. Studies from Jachuck et al. (2006) and Dressen et al. (2009) verified that Fe(NO₃)₃ could successfully oxidize benzyl alcohol to benzaldehyde under microwave irradiation. They deemed Fe³⁺ in the oxidation of benzyl alcohol as catalyst, because overall Fe³⁺ remained in its original oxidative state. However, this study was limited in microwave irradiation and lacked the universality for actual application. Besides, the oxidation performances of other system composed of metal iron (Cu, Al, Mg, Co, Ni) and ${\text{NO}}_3^{-}$ /${\text{NO}}_2^{-}$ were unclear, and the role of Mⁿ⁺ had not been reported.

Hence, we studied the performance of Fe(NO₃)₃·9H₂O by continuous heating in O₂ and N₂ (He) atmosphere. Interestingly, the results were different from the phenomenon in microwave irradiation. The catalytic performance of Fe(NO₃)₃·9H₂O in N₂ was significantly improved compared to that in O₂. Further, the oxidation performance of other nitrates was studied. To expand the applicability of the combination of Mⁿ⁺ and ${\text{NO}}_3^{-}$, we conducted systematic research using Fe(NO₃)₃9H₂O as an example. The reaction conditions such as temperature and solvent were optimized. The optimized conditions were applied to the oxidation of a variety of alcohols. Finally, the catalytic mechanism was put forward.

Experimental

Materials

Benzyl alcohol, nitrates with crystalline waters, and other reagents were analytical grade. Gas chromatography (GC) analysis was performed on SHIMAZDU GC-2014 equipped with a HP-5 column (30 m × 0.32 mm × 0.25 um) and a flame ionization detector.

The Oxidation of Benzyl Alcohol

Typically, 3 mmol of benzyl alcohol, 3 mmol of naphthalene as an internal standard, and 15 mL of 1,4-dioxane as solvent were added to a 25 mL three-necked flask. Then the three-necked flask provided with a reflux condenser was evacuated using an aspirator and followed by the attachment of a nitrogen balloon. Subsequently, the solution was heated to the desired temperature. When the temperature of solution reached the set point, 2 mmol of ferric nitrate (Fe(NO₃)₃·9H₂O) was added into it. Samples were taken at appropriate intervals through a silicon septum using a hypodermic needle and were filtered with a membrane filter (PVDF) with 13 mm × 0.22 μm pore prior to GC analysis.

The Product Analysis

The analysis of benzyl alcohol and oxidation products was carried out on Aglient 7980 series with a HP-5 column and a flame ionization detector. The condition of GC for the HP-5 capillary column (30 m, DF = 0.25 mm, 0.25 mm i.d.), and temperature program was carried out (initial temperature = 100°C, 3 min; final temperature = 250°C, heating rate = 10°C min⁻¹, temperature of injector = 280°C, temperature of detector = 280°C). The quantitative results of products were based on the internal standard method, using naphthalene as an internal standard. The typical analytic procedure was as following: (1) 0.4 ml sample was taken from reaction solutions and was then filtered with a membrane filter (PVDF) with 13 mm × 0.22 μm; (2) then, the sample would be diluted 10-fold before GC analysis; (3) when the GC temperature reached the set points, the diluted solution was injected into this equipment to analyze products according to the different retention times and response peak area. The typical results of GC measurements and internal standard working curve were shown in Figure S1. The results reported as conversion and selectivity are expressed in mol%, based on the total benzyl alcohol intake. The calculation of the conversion and selectivity was as follows:

$\begin{array}{l}\text{Conversion of benzyl alcohol}\\ =\frac{\text{Moles of benzyl alcohol reacted }}{\text{Initial moles of benzyl alcohol}}\times \text{100}\%& (1)\end{array}$

$\begin{array}{l}\text{Selectivity of benzaldehyde}\\ =\frac{\text{Moles of benzaldehyde formed}}{\text{Moles of benzyl alcohol reacted}}\times \text{ 100}\%& (2)\end{array}$

$\begin{array}{ll}\text{Yield of benzaldehyde}=\text{ Conversion }\times \text{Selectivity}& (3)\end{array}$

Results and Discussion

The Oxidation of Benzyl Alcohol by Ferric Nitrate

Figures 1A,B showed the oxidation results of benzyl alcohol to benzaldehyde in the presence of ferric nitrate and nitric acid. In N₂ condition, the conversion of benzyl alcohol catalyzed by ferric nitrate was 94.9% after 6 h. To ensure reproducibility, the experimental error-based three parallel experiments was shown in Figure S2 and the carbon balance during experiments was also evaluated (Table S1). The results showed that performance of Fe(NO₃)₃ had a good testing repeatability and was highly efficient. Interestingly, the benzyl alcohol conversion catalyzed by Fe(NO₃)₃ could be as high as 96.84% with 94.5% selectivity when replacing N₂ with He. Compared with HNO₃, ferric nitrate exhibited an excellent activity in the benzyl alcohol oxidation. The conversion of benzyl alcohol catalyzed by ferric nitrate was 46.2%—higher than that by nitric acid. Similarly, under aerobic conditions (O₂), the conversion of benzyl alcohol catalyzed by ferric nitrate was about 13% higher than that by nitric acid with similar selectivity. The results indicated the oxidation performance of ferric nitrate was markedly better than that of nitric acid, no matter under anaerobic or aerobic conditions.

FIGURE 1

Figure 1. The conversion (A) and selectivity (B) for benzyl alcohol oxidation to benzaldehyde with Fe(NO₃)₃·9H₂O and HNO₃. Fe(NO₃)₃ denotes Fe(NO₃)₃·9H₂O unless otherwise noted.

Compared with other typical catalysts, the catalytic activity of Fe(NO₃)₃ was also outstanding. The conversion of benzyl alcohol catalyzed by Fe(NO₃)₃ with any oxidant (96.84%) was close to that by CNT-HNO₃ (Luo et al., 2012) (96.2%), as shown in Table 1 (Entry 2). Besides, the performance of Fe(NO₃)₃ surpassed the typical metal-based catalyst, such as Au/γ-Al₂O₃ (73.4%) (Ndolomingo and Meijboom, 2017), Fe/MCM41 (55%) (Cánepa et al., 2017), or Fe-N-C (78.0%) (Xie et al., 2017). Moreover, Fe(NO₃)₃ also exhibited comparable activity with transition-metal oxides, such as Co₃O₄/RGO-_N (93.9%) (Nie et al., 2013), MnO_x (72.7%) (Jing et al., 2007). The excellent catalytic activity of Fe(NO₃)₃ may be attributed to the combined action of Fe³⁺ and ${\text{NO}}_3^{-}$. On the one hand, ${\text{NO}}_3^{-}$ could produce NO₂, and then NO₂ with H₂O was converted to HNO₂, which had been proved as a pivotal role in benzyl alcohol oxidation (Aellig et al., 2012; Luo et al., 2012). On the other hand, the valence change of Fe could catalyze benzyl alcohol oxidation according to the literatures (Miao et al., 2016; Hu et al., 2018). Coincidentally, the transformation between Fe³⁺ and Fe²⁺ was demonstrated by the K₃[Fe(CN)₆] solution. As shown in Figure S3, the Prussian blue precipitate appeared in the experimental process due to the existence of Fe²⁺. Therefore, Fe(NO₃)₃ exhibited the excellent oxidation activity via Fe³⁺ initiating a series of electron and proton transfer. It was noted that the anaerobic condition was beneficial to improve the oxidation performance of ferric nitric. The reason is discussed in detail in mechanism Part 3.4.

TABLE 1

Table 1. Catalytic results for benzyl alcohol oxidation with different catalysts.

The Performance of Other Metallic Nitrates

Subsequently, the catalytic performance of other nitrates was also studied. The benzyl alcohol oxidation catalyzed by other nitrates including was investigated, as shown in Figure 2. The result proves other nitrates are also capable for converting the benzyl alcohol to benzaldehyde. In Al(NO₃)₃ system, the conversion of benzyl alcohol and the selectivity to benzaldehyde was 88.1% and 80% after 6 h, lower than those in Fe(NO₃)₃ system. Similarly, Cu(NO₃)₂ could also oxidize the benzyl alcohol with the conversion of 82.3%. While the selectivity to benzadehyde was only 70%, and the other 30% was benzoic acid from the excessive oxidation. The catalytic performance of Co(NO₃)₂ significantly decreased. While Mg(NO₃)₂ and Zn(NO₃)₂ had almost no catalytic activity. The order of activity of different nitrates is Fe(NO₃)₃ > Al(NO₃)₃ > Cu(NO₃)₂ > Co(NO₃)₂ > Mg(NO₃)₂ ≈ Zn(NO₃)₂. Yuvaraj et al. (2003) tested the decomposition temperature of these nitrates by TG/DAT. And they found Fe(NO₃)₃ and Al(NO₃)₃ had the lowest the decomposition temperature (130°C), followed by Cu(NO₃)₂ (227°C) and Co(NO₃)₂ (247°C), and Zn(NO₃)₂ (367°C) was the highest. Their decomposition products were metal oxide, NO₂ and O₂. NO₂ and H₂O together would convert into HNO₂ which could attack the benzyl alcohol, finally producing benzaldehyde. Hence, the nitrates with lower decomposition temperature could easily produce NO₂ and oxidize more benzyl alcohol. As expected, the rank of conversion of benzyl alcohol in different nitrate system was related to the decomposition temperature of these nitrates.

FIGURE 2

Figure 2. The oxidation of benzyl alcohol to benzaldehyde by different nitrates. Reaction conditions: benzyl alcohol (3 mmol), 1,4-dioxane (15 mL), Fe(NO₃)₃ and Al(NO₃)₃ (2 mmol), or other nitrates (3 mmol), 80°C, 6 h ball N₂.

Effect of Reaction Conditions on Oxidation Performance of Fe(NO₃)₃

Fe(NO₃)₃ is an excellent catalyst among several nitrates; the effect of reaction condition and solvent on the performance of Fe(NO₃)₃ was investigated. As the results shown in Figure 3A, the higher temperature would markedly enhance the yields of benzaldehyde. Since high temperature would increase the risk of the over oxidation from benzaldehyde to benzoic acid, the optimum temperature was 80°C. Similarly, 2 mmol Fe(NO₃)₃ could selectively oxidize the benzyl alcohol to benzaldehyde with 91.5% yields shown in Figure 3B. Besides, the solvent had an important effect on the activity of Fe(NO₃)₃. The results in Figure 3C show the strong polar solvent could bring a mutual solution containing the aqueous (HNO₂) and organic phase (benzyl alcohol), which would be more favorable to form of benzyl nitrite, resulting in high conversion and selectivity.

FIGURE 3

Figure 3. The effect of different factors on the oxidation activity of Fe(NO₃)₃. Green square: conversion; Orange square: selectivity; (A) temperature; (B) dosage of Fe(NO₃)₃; (C) solvent polarity: n-hexane (H), dimethylbenzene (DB); 1,4-dioxane (D); N,N-dimethylformamide (DMF).

The Applicability of Fe(NO₃)₃ Catalyst

Subsequently, to demonstrate the general applicability of Fe(NO₃)₃, selective oxidation of substituted benzyl alcohols with different functional groups was investigated. The results presented in Table 2 showed all these primary benzylic alcohols could be converted to corresponding aldehydes. The oxidation results were somewhat related to the substituent groups on the phenyl ring. The alcohols with electron withdrawing groups (–NO₂, –Cl) gained lower yields of products than those with electron donating groups (–MeO, –OH). The effect rule of substituent groups in Fe(NO₃)₃ system is consistent with that in HNO₃ system (Joshi et al., 2005). The formation of benzyl nitrite, a vital intermediate product, can be regarded as the electrophilic substitution reaction of benzyl alcohol. Thus, the electron-donating substituents would enhance the yield of product by increasing the electron density on the benzyl ring and vice versa. The results proved that the electron density on the aromatic ring played a critical role in the oxidation of benzylic alcohol.

TABLE 2

Table 2. The oxidation of different alcohols by Fe (NO₃)₃.

Reaction Mechanism

Combined with the experimental results and literature reports, the following catalytic mechanism hypothesis was preliminarily put. Both Fe³⁺ and ${\text{NO}}_3^{-}$ may have an important effect on the oxidation process. Fe³⁺ provides catalytic function by the electron transferring, while the NO_x produced from the experimental process may have certain oxidation performance. To verify above possible speculations and analyze the catalytic mechanism, a series of experiments were designed, and the results were shown as follows.

To illustrate the role of Fe³⁺ and ${\text{NO}}_3^{-}$, Zn(NO₃)₂ or FeCl₃ was individually added to the reaction mixtures. The result showed benzyl alcohol conversion in both systems was very low (Figure 4), indicating that only Fe³⁺ or ${\text{NO}}_3^{-}$ had poor oxidation activity. While in Zn(NO₃)₂ + FeCl₃ system, the conversion of benzyl alcohol was as high as 95.8% with 93.6% selectivity, which was similar to that in Fe(NO₃)₃ system with the same amount of Fe³⁺ and ${\text{NO}}_3^{-}$. The results proved the Fe³⁺ and ${\text{NO}}_3^{-}$ together could oxidize the benzyl alcohol. To illuminate how Fe³⁺ and ${\text{NO}}_3^{-}$ together catalyze the benzyl alcohol, introducing urea as a known HNO₂ scavenger into Fe(NO₃)₃ system. The results in Figure 4 showed the catalytic activity of Fe(NO₃)₃ was almost prevented. This phenomenon proved that the oxidation process of Fe(NO₃)₃ was mainly achieved by HNO₂ attacking benzyl alcohol. The intermediate benzyl nitrite detected by GC-MS in our experiments further verified the reaction between benzyl alcohol and HNO₂. Besides, when butylated hydroxytoluene (BHT) as a radical trapping agent was added into the Fe(NO₃)₃ system, the conversion still kept a high level of 86.3%, proving that the benzyl alcohol oxidation catalyzed by Fe(NO₃)₃ is not a radical-involved reaction. Interestingly, the conversion would increase obviously, and the selectivity also kept at a high value (95%) when Fe³⁺ instead of H⁺ with the same mole of ${\text{NO}}_3^{-}$ as shown in Figure 4. Furthermore, the addition of Fe³⁺ into HNO₃ system also significantly enhanced the conversion of benzyl alcohol compared with the HNO₃ system. From these results, we speculated Fe³⁺ had a special catalytic function in the process of benzyl alcohol oxidation.

FIGURE 4

Figure 4. The conversion and selectivity for the oxidation of benzyl alcohol in different system. Benzyl alcohol (3 mmol), 1,4-dioxane (15 mL), 80°C, 6 h, ball N₂.

A series of experiments were conducted to further illuminate the catalysis of Fe³⁺. As the results shown in Figure 5A, the reaction rate increased as the amount of Fe³⁺ increased in FeCl₃-HNO₃ system. Meanwhile, the results shown in Figure 5B proved that the variation of selectivity was little. To quantify the effect of Fe³⁺, the turnover frequency (TOF) was calculated based on Fe content at the conversion lower than 25.0%, as shown in Figure 5C. The results proved the Fe³⁺ had a remarkable effect on the oxidation reaction. The TOF of Fe³⁺ in the FeCl₃-HNO₃ system further enlarged compared to that in the Fe(NO₃)₃ system. As shown in Figure 5D, the TOF of Fe³⁺ in the FeCl₃-HNO₃ system was almost unchanged (8.1 h⁻¹), even if the amount of Fe³⁺ increased from 0.5 to 1 mmol.

FIGURE 5

Figure 5. The oxidation results of benzyl alcohol in different catalyst systems. The TOF was defined as $\frac{benzylalcoholconverted(g)}{Fecontent(g)\times reactiontime}$ and were calculated at 15 min, for which the conversion was lower than 25.0%. (A) The benzyl alcohol conversion in 6 h. (B) The selectivity of benzaldehyde. (C) The benzyl alcohol conversion in 30 min. (D) TOF.

Furthermore, the change of Fe in benzyl alcohol oxidation was analyzed by experiments. The transformation between Fe³⁺ and Fe²⁺ was detected in situ by 1 mol/L KMnO₄ solution in the oxidation process. For comparison, the reaction solvent (1,4-dioxane) was added to the KMnO₄ solution, the solution was black-purple as shown in Figure 6. The color of KMnO₄ solution changed from black-purple to yellow when KMnO₄ solution was added into reaction solution at 2 h. This phenomenon showed the KMnO₄ was reduced by Fe²⁺, and the Fe²⁺ existed in the reaction process. However, the KMnO₄ solution changed from yellow to brown when it was added into the reaction solution at the reaction time of 6 h. The phenomenon illustrated that there were less Fe²⁺ in the reaction solution. Because the oxidation reaction of benzyl alcohol almost completed, most of Fe³⁺ did not convert anymore and Fe²⁺ would further oxidized to Fe³⁺ by the O₂ from the decomposition of Fe(NO₃)₃. So, the cyclic conversion of Fe³⁺ and Fe²⁺ really occurred in benzyl alcohol oxidation. According to the reported results, the valence transformation of metal iron such as Mn^III/Mn^II (Yang et al., 2014; Fei et al., 2017; Gurrala et al., 2018), Co^III/Co^II (Zhou et al., 2015; Cordoba et al., 2017; Li et al., 2017), Cr^III/ Cr^II (Thao et al., 2018) could catalyze the oxidation of alcohols. Especially, the transformation of Fe³⁺/Fe²⁺ possessed high catalytic activity by initiating a series of electron transfer (Hu et al., 2016, 2018; Miao et al., 2016). Combined with above results, Fe³⁺ could be regard as a catalyst and the electron transfer between of Fe³⁺ and Fe²⁺ would catalyze the oxidation process.

FIGURE 6

Figure 6. The phenomena in the experimental process at different moments after adding 1 mol/L KMnO₄ to the reaction solution.

Finally, the function of NO_x was investigated by a series of auxiliary experiments. As we know, nitric oxide (NO) would be immediately oxidized to nitrogen dioxide (NO₂) by O₂ (Wang et al., 2005; Shen et al., 2015, 2019; Miao et al., 2016; Hu et al., 2018; Dong et al., 2019; Zhao et al., 2019). O₂ was flowed into the reaction system in the experimental process to detect the NO. Brown fumes immediately occurred (Figure S4), proving the presence of NO in the inert atmosphere. Subsequently, NO was prepared by the reaction between Cu and 35 wt % nitric acid (3Cu + 8HNO₃ → 3Cu(NO₃)₂ + 2NO + 4H₂O). The oxidation of benzyl alcohol by NO was conducted and the detailed experimental process was shown in Figure S5. The conversion of benzyl alcohol by NO was only 1% at 6 h with 99% selectivity, as shown in Figure 7. The results indicated NO itself could not oxidize benzyl alcohol. Hence, the NO₂ from the decomposition of Fe(NO₃)₃ played the key role in oxidation process by forming HNO₂.

FIGURE 7

Figure 7. The performance of NO in benzyl alcohol oxidation process. Reaction condition: 3 mmol benzyl alcohol, 15.0 ml 1,4-dioxane, 80°C.

According to the above investigation, the mechanism of the benzyl alcohol oxidation in N₂ condition was put forward and shown in Scheme 1. At the suitable reaction temperature, the Fe(NO₃)₃ decomposes into Fe₂O₃, NO₂, and O₂ (Yuvaraj et al., 2003) by Equation 1. Subsequently, the HNO₂ and HNO₃ can be formed by the reaction between NO₂ and H₂O, see Equation 2. Then, the oxidation reaction successfully gets into the propagation stage and HNO₂ attacks the benzyl alcohol (PhCH₂OH) and gives benzyl nitrite (PhCH₂ONO). Benzyl nitrite decomposes into benzaldehyde (PhCHO) and HNO at experimental temperature by Equation 4. In the termination stage, as shown in Equation 6, Fe(NO₃)₂ can be formed by the reaction between the HNO₂ and Fe₂O₃ with consuming O₂. At the same time, Fe(NO₃)₂ is oxidized to Fe(NO₃)₃ by O₂. Consequently, from Reaction 1 to Reaction 7, ${\text{NO}}_3^{-}$ can be considered as the real oxidant, and the Fe ion acts a catalyst through the transformation between Fe²⁺ and Fe³⁺.

SCHEME 1

Scheme 1. The probable routes for oxidation of benzyl alcohol by Fe(NO₃)₃.

From the reaction mechanism, when the system was filled with O₂, the decomposition of Fe(NO₃)₃ would be hindered, leading to low conversion compared with anaerobic condition (N₂ or He). Interestingly, the O₂ was double-edged gas since it could oxidize the Fe²⁺ to Fe³⁺ and eliminate NO Equation 7. In the presence of adequate oxygen, the Fe²⁺ was completely oxidized into Fe³⁺, and oxidative state of Fe remained the same before and after the reaction. The conversion of benzyl alcohol in Fe(NO₃)₃-O₂ system was relatively low (Figure 8A), but it was still higher than that in HNO₃ system. Moreover, in Fe(NO₃)₃ system, the conversion of benzyl alcohol could reach 82% when O₂ replaced N₂ after the reaction continuing 2 h (Figure 8A). As expected, the conversion of benzyl alcohol in air (N₂ + O₂) condition was close to that in N₂ condition (Figure 8B). In the aerobic conditions, ${\text{NO}}_3^{-}$ would be regenerated and the Fe²⁺ was completely oxidized to Fe³⁺, indicating O₂ was the actual oxidation. Though the O₂ would be not good for the high conversion, it could build a green cyclic oxidation process via removing NO and regenerating Fe(NO₃)₃. Hence, the benzyl alcohol conversion would be relatively high in air atmosphere, which also meet the need of green synthesis due to removing the NO.

FIGURE 8

Figure 8. (A) The benzyl alcohol conversion under different conditions: (i) O₂; (ii) N₂ (1-2 h) and O₂ (2–6 h); (iii) N₂. (B) Comparison of the benzyl alcohol conversion in N₂ and air.

Conclusion

As a bio-friendly and economical material, ferric nitrate showed an outstanding oxidation performance for benzyl alcohol oxidation. The conversion of benzyl alcohol in ferric nitrate system reached 95%, which was 46% higher than that in nitric acid system under N₂ atmosphere. Other metallic nitrates that could release NO₂ at reaction temperature also had high properties for benzyl alcohol oxidation. Moreover, ferric nitrate is of excellent applicability for other primary benzylic alcohols oxidation under optimized condition. The mechanism study indicated ferric nitrate was as initiator in the reaction. In the procedure, it would decompose into Fe₂O₃ and NO₂ which immediately became HNO₂, attacking benzyl alcohol, and forming the benzaldehyde afterward. While in anaerobic atmosphere, ${\text{NO}}_3^{-}$ was the oxidant by providing HNO₂ and the transformation cycle between Fe³⁺ and Fe²⁺ generates a catalytic effectiveness. Hence, the balance of high conversion and green synthesis requirement would be obtained for the benzyl alcohol oxidation in the air atmosphere.

Data Availability Statement

The datasets generated for this study are available on request to the corresponding author.

Author Contributions

SX, GZ, and FP designed experiments. JW, PH, CL, HL, YW, and ZW carried out experiments. SX, GZ, XF, and FP analyzed experimental results, analyzed data, and wrote the manuscript.

Funding

This work was supported by Engineering Research Center of None-food Biomass Efficient Pyrolysis and Utilization Technology of Guangdong Higher Education Institutes (2016GCZX009), National Natural Science Foundation of China (No. 21905044), Natural Science Foundation of Guangdong Province (No. 2018A030310004), and Research Start-up Funds of Dongguan University of Technology (GC300501-077).

Conflict of Interest

The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.

Supplementary Material

The Supplementary Material for this article can be found online at: https://www.frontiersin.org/articles/10.3389/fchem.2020.00151/full#supplementary-material

References

Aellig, C., Ulrich, N., and Hermans, I. (2012). Acid-catalyzed decomposition of the benzyl nitrite intermediate in HNO₃-mediated aerobic oxidation of benzyl alcohol. ChemCatChem 4, 525–529. doi: 10.1002/cctc.201100439

CrossRef Full Text | Google Scholar

Albadi, J., Alihoseinzadeh, A., and Razeghi, A. (2014). Novel metal oxide nanocomposite of Au/CuO–ZnO for recyclable catalytic aerobic oxidation of alcohols in water. Catal. Commun. 49, 1–5. doi: 10.1016/j.catcom.2014.01.030

CrossRef Full Text | Google Scholar

Cánepa, A. L., Elías, V. R., Vaschetti, V. M., Sabre, E. V., Eimer, G. A., Casuscelli, S. G., et al. (2017). Selective oxidation of benzyl alcohol through eco-friendly processes using mesoporous V-MCM-41, Fe-MCM-41 and Co-MCM-41 materials. Appl. Catal. A Gen. 545, 72–78. doi: 10.1016/j.apcata.2017.07.039

CrossRef Full Text | Google Scholar

Cao, Y., Li, Y., Yu, H., Peng, F., and Wang, H. (2015). Aerobic oxidation of α-pinene catalyzed by carbon nanotubes. Catal. Sci. Technol. 5, 3935–3944. doi: 10.1039/C5CY00136F

CrossRef Full Text | Google Scholar

Cao, Y., Luo, X., Yu, H., Peng, F., Wang, H., Ning, G., et al. (2013). sp 2-and sp 3-hybridized carbon materials as catalysts for aerobic oxidation of cyclohexane. Catal. Sci. Technol. 3, 2654–2660. doi: 10.1039/c3cy00256j

CrossRef Full Text | Google Scholar

Chen, C. T., Nguyen, C. V., Wang, Z. Y., Bando, Y., Yamauchi, Y., Bazziz, M. T. S., et al. (2018a). Hydrogen peroxide assisted selective oxidation of 5-hydroxymethylfurfural in water under mild conditions. ChemCatChem 10, 361–365. doi: 10.1002/cctc.201701302

CrossRef Full Text | Google Scholar

Chen, H., Shen, J., Chen, K., Qin, Y., Lu, X., Ouyang, P., et al. (2018b). Atomic layer deposition of Pt nanoparticles on low surface area zirconium oxide for the efficient base-free oxidation of 5-hydroxymethylfurfural to 2,5-furandicarboxylic acid. Appl. Catal. A Gen. 555, 98–107. doi: 10.1016/j.apcata.2018.01.023

CrossRef Full Text | Google Scholar

Choudhary, V. R., Dhar, A., Jana, P., Jha, R., and Uphade, B. S. (2005). A green process for chlorine-free benzaldehyde from the solvent-free oxidation of benzyl alcohol with molecular oxygen over a supported nano-size gold catalyst. Green Chem. 7, 768–770. doi: 10.1039/b509003b

CrossRef Full Text | Google Scholar

Cordoba, M., Miranda, C., Lederhos, C., Coloma-Pascual, F., Ardila, A., Fuentes, G., et al. (2017). Catalytic performance of Co3O4 on different activated carbon supports in the benzyl alcohol oxidation. Catalysts 7:384. doi: 10.3390/catal7120384

CrossRef Full Text | Google Scholar

Dong, G., Zhao, L., Wu, X., Zhu, M., and Wang, F. (2019). Photocatalysis removing of NO based on modified carbon nitride: the effect of celestite mineral particles. Appl. Catal. B Environ. 245, 459–468. doi: 10.1016/j.apcatb.2019.01.013

CrossRef Full Text | Google Scholar

Dressen, M. H. C. L., Stumpel, J. E., van de Kruijs, B. H. P., Meuldijk, J., Vekemans, J. A. J. M., and Hulshof, L. A. (2009). The mechanism of the oxidation of benzyl alcohol by iron(III)nitrate: conventional versus microwave heating. Green Chem. 11, 60–64. doi: 10.1039/B813030B

CrossRef Full Text | Google Scholar

Fei, J., Sun, L., Zhou, C., Ling, H., Yan, F., Zhong, X., et al. (2017). Tuning the synthesis of manganese oxides nanoparticles for efficient oxidation of benzyl alcohol. Nanoscale Res. Lett. 12:23. doi: 10.1186/s11671-016-1777-y

PubMed Abstract | CrossRef Full Text | Google Scholar

Ganesamoorthy, S., Tamizh, M. M., Shanmugasundaram, K., and Karvembu, R. (2013). Immobilization of Ru (III) complex on silica: a heterogenized catalyst for selective oxidation of alcohols in water at room temperature. Tetrahedron Lett. 54, 7035–7039. doi: 10.1016/j.tetlet.2013.10.070

CrossRef Full Text | Google Scholar

Gurrala, L., Nagpure, A. S., Gurav, H. R., and Chilukuri, S. (2018). Spinel-type mixed oxides for stable and selective partial oxidation of benzyl alcohol. Chemistryselect 3, 3751–3761. doi: 10.1002/slct.201800321

CrossRef Full Text | Google Scholar

Hansen, T. S., Sádaba, I., García-Suárez, E. J., and Riisager, A. (2013). Cu catalyzed oxidation of 5-hydroxymethylfurfural to 2,5-diformylfuran and 2,5-furandicarboxylic acid under benign reaction conditions. Appl. Catal. A Gen. 456, 44–50. doi: 10.1016/j.apcata.2013.01.042

CrossRef Full Text | Google Scholar

Hanson, S. K., Baker, R. T., Gordon, J. C., Scott, B. L., Sutton, A. D., and Thorn, D. L. (2008). Aerobic oxidation of pinacol by vanadium (V) dipicolinate complexes: evidence for reduction to vanadium (III). J. Am. Chem. Soc. 131, 428–429. doi: 10.1021/ja807522n

PubMed Abstract | CrossRef Full Text | Google Scholar

Hu, Y., Chen, L., and Li, B. (2016). Iron nitrate/TEMPO-catalyzed aerobic oxidative synthesis of quinazolinones from alcohols and 2-aminobenzamides with air as the oxidant. RSC Adv. 6, 65196–65204. doi: 10.1039/C6RA12164K

CrossRef Full Text | Google Scholar

Hu, Y., Chen, L., and Li, B. (2018). Fe(NO 3) 3 /2,3-dichloro-5,6-dicyano-1,4-benzoquinone (DDQ): an efficient catalyst system for selective oxidation of alcohols under aerobic conditions. Catal. Commun. 103, 42–46. doi: 10.1016/j.catcom.2017.09.019

CrossRef Full Text | Google Scholar

Jachuck, R. J. J., Selvaraj, D. K., and Varma, R. S. (2006). Process intensification: oxidation of benzyl alcohol using a continuous isothermal reactor under microwave irradiation. Green Chem. 8, 29–33. doi: 10.1039/B512732G

CrossRef Full Text | Google Scholar

Ji, H., Wang, T., Zhang, M., She, Y., and Wang, L. (2005). Simple fabrication of nano-sized NiO2 powder and its application to oxidation reactions. Appl. Catal. A Gen. 282, 25–30. doi: 10.1016/j.apcata.2004.11.043

CrossRef Full Text | Google Scholar

Jia, X., Ma, J., Wang, M., Du, Z., Lu, F., Wang, F., et al. (2014). Promoted role of Cu(NO3)2 on aerobic oxidation of 5-hydroxymethylfurfural to 2,5-diformylfuran over VOSO4. Appl. Catal. A Gen. 482, 231–236. doi: 10.1016/j.apcata.2014.05.031

CrossRef Full Text | Google Scholar

Jiang, X., Zhang, J., and Ma, S. (2016). Iron catalysis for room-temperature aerobic oxidation of alcohols to carboxylic acids. J. Am. Chem. Soc. 138, 8344–8347. doi: 10.1021/jacs.6b03948

PubMed Abstract | CrossRef Full Text | Google Scholar

Jing, H., Keqiang, S., Daiping, H., and Boqing, X. (2007). Amorphous manganese oxide for catalytic aerobic oxidation of benzyl alcohol. Chin. J. Catal. 28, 1025–1027. doi: 10.1016/S1872-2067(08)60001-7

CrossRef Full Text | Google Scholar

Joshi, S. R., Kataria, K. L., Sawant, S. B., and Joshi, J. B. (2005). Kinetics of oxidation of benzyl alcohol with dilute nitric acid. Indust. Eng. Chem. Res. 44, 325–333. doi: 10.1021/ie0303911

CrossRef Full Text | Google Scholar

Li, M., Wu, S., Yang, X., Hu, J., Peng, L., Bai, L., et al. (2017). Highly efficient single atom cobalt catalyst for selective oxidation of alcohols. Appl. Catal. A Gen. 543, 61–66. doi: 10.1016/j.apcata.2017.06.018

CrossRef Full Text | Google Scholar

Li, M., Xu, F., Li, H., and Wang, Y. (2016). Nitrogen-doped porous carbon materials: promising catalysts or catalyst supports for heterogeneous hydrogenation and oxidation. Catal. Sci. Technol. 6, 3670–3693. doi: 10.1039/C6CY00544F

CrossRef Full Text | Google Scholar

Liu, J., Zou, S., Lu, L., Zhao, H., Xiao, L., and Fan, J. (2017). Room temperature selective oxidation of benzyl alcohol under base-free aqueous conditions on Pt/TiO2. Catal. Commun. 99, 6–9. doi: 10.1016/j.catcom.2017.05.015

CrossRef Full Text | Google Scholar

Long, J., Xie, X., Xu, J., Gu, Q., Chen, L., and Wang, X. (2012). Nitrogen-doped graphene nanosheets as metal-free catalysts for aerobic selective oxidation of benzylic alcohols. ACS Catal. 2, 622–631. doi: 10.1021/cs3000396

CrossRef Full Text | Google Scholar

Lu, C., Hu, J. M., Meng, Y. N., Zhou, A. D., Zhang, F., and Zhang, Z. B. (2019). The synergistic effect of benzyl benzoate on the selective oxidation of toluene to benzaldehyde. Chem. Eng. Res. Des. 141, 181–186. doi: 10.1016/j.cherd.2018.10.019

CrossRef Full Text | Google Scholar

Luo, J., Peng, F., Yu, H., and Wang, H. (2012). Selective liquid phase oxidation of benzyl alcohol catalyzed by carbon nanotubes. Chem. Eng. J. 204–206, 98–106. doi: 10.1016/j.cej.2012.07.098

CrossRef Full Text | Google Scholar

Luo, J., Yu, H., Wang, H., Wang, H., and Peng, F. (2014). Aerobic oxidation of benzyl alcohol to benzaldehyde catalyzed by carbon nanotubes without any promoter. Chem. Eng. J. 240, 434–442. doi: 10.1016/j.cej.2013.11.093

CrossRef Full Text | Google Scholar

Lv, L. B., Yang, S. Z., Ke, W. Y., Wang, H. H., Zhang, B., Zhang, P., et al. (2018). Mono-atomic Fe centers in nitrogen/carbon monolayers for liquid-phase selective oxidation reaction. ChemCatChem 10, 3539–3545. doi: 10.1002/cctc.201800707

CrossRef Full Text | Google Scholar

Mahmood, A., Robinson, G. E., and Powell, L. (1999). An improved oxidation of an alcohol using aqueous permanganate and phase-transfer catalyst. Organ. Proc. Res. Dev. 3, 363–364. doi: 10.1021/op990021h

CrossRef Full Text | Google Scholar

Mal, D. D., Khilari, S., and Pradhan, D. (2018). Efficient and selective oxidation of toluene to benzaldehyde on manganese tungstate nanobars: a noble metal-free approach. Green Chem. 20, 2279–2289. doi: 10.1039/C8GC00123E

CrossRef Full Text | Google Scholar

Martin, S. E., and Suárez, D. F. (2002). Catalytic aerobic oxidation of alcohols by Fe(NO3)3–FeBr3. Tetrahedron Lett. 43, 4475–4479. doi: 10.1016/S0040-4039(02)00829-8

CrossRef Full Text | Google Scholar

Miao, C., Zhao, H., Zhao, Q., Xia, C., and Sun, W. (2016). NHPI and ferric nitrate: a mild and selective system for aerobic oxidation of benzylic methylenes. Catal. Sci. Technol. 6, 1378–1383. doi: 10.1039/C5CY01245G

CrossRef Full Text | Google Scholar

Miao, C. X., Wang, J.-Q., Yu, B., Cheng, W.-G., Sun, J., Chanfreau, S., et al. (2011). Synthesis of bimagnetic ionic liquid and application for selective aerobic oxidation of aromatic alcohols under mild conditions. Chem. Commun. 47, 2697–2699. doi: 10.1039/c0cc04644b

PubMed Abstract | CrossRef Full Text | Google Scholar

Ndolomingo, M. J., and Meijboom, R. (2017). Selective liquid phase oxidation of benzyl alcohol to benzaldehyde by tert-butyl hydroperoxide over gamma-Al2O3 supported copper and gold nanoparticles. Appl. Surf. Sci. 398, 19–32. doi: 10.1016/j.apsusc.2016.12.020

CrossRef Full Text | Google Scholar

Nie, R., Shi, J., Du, W., Ning, W., Hou, Z., and Xiao, F. S. (2013). A sandwich N-doped graphene/Co₃ O₄ hybrid: an efficient catalyst for selective oxidation of olefins and alcohols. J. Mater. Chem. A 1, 9037–9045. doi: 10.1039/c3ta11672g

CrossRef Full Text | Google Scholar

Öztürk, Ö. F., Zümreoglu-Karan, B., and Karabulut, S. (2008). Solvent-free oxidation of benzyl alcohol over chromium orthoborate. Catal. Commun. 9, 1644–1648. doi: 10.1016/j.catcom.2008.01.016

CrossRef Full Text | Google Scholar

Parmeggiani, C., and Camilla, F. (2012). Transition metal based catalysts in the aerobic oxidation of alcohols. Green Chem. 14, 547–564. doi: 10.1039/c2gc16344f

CrossRef Full Text | Google Scholar

Ragupathi, C., Judith Vijaya, J., Narayanan, S., Jesudoss, S. K., and John Kennedy, L. (2015). Highly selective oxidation of benzyl alcohol to benzaldehyde with hydrogen peroxide by cobalt aluminate catalysis: a comparison of conventional and microwave methods. Ceram Int. 41, 2069–2080. doi: 10.1016/j.ceramint.2014.10.002

CrossRef Full Text | Google Scholar

Shen, X., Dong, G., Wang, L., Ye, L., and Sun, J. (2019). Enhancing photocatalytic activity of NO removal through an in situ control of oxygen vacancies in growth of TiO₂. Adv. Mater. Interf. 6:1901032. doi: 10.1002/admi.201901032

CrossRef Full Text | Google Scholar

Shen, Z., Chen, M., Fang, T., Li, M., Mo, W., Hu, B., et al. (2015). Transformation of ethers into aldehydes or ketones: a catalytic aerobic deprotection/oxidation pathway. Tetrahedron Lett. 56, 2768–2772. doi: 10.1016/j.tetlet.2015.04.033

CrossRef Full Text | Google Scholar

Shimizu, H., Onitsuka, S., Egami, H., and Katsuki, T. (2005). Ruthenium(salen)-catalyzed aerobic oxidative desymmetrization of meso-diols and its kinetics. J. Am. Chem. Soc. 127, 5396–5413. doi: 10.1021/ja047608i

PubMed Abstract | CrossRef Full Text | Google Scholar

Tamizhdurai, P., Sakthinathan, S., Chen, S. M., Shanthi, K., Sivasanker, S., and Sangeetha, P. (2017). Environmentally friendly synthesis of CeO2 nanoparticles for the catalytic oxidation of benzyl alcohol to benzaldehyde and selective detection of nitrite. Sci. Rep. 7:46372. doi: 10.1038/srep46372

PubMed Abstract | CrossRef Full Text | Google Scholar

Thao, N. T., Nhu, N. T., and Lin, K. S. (2018). Liquid phase oxidation of benzyl alcohol to benzaldehyde over sepiolite loaded chromium oxide catalysts. J. Taiwan Inst. Chem. Eng. 83, 10–22. doi: 10.1016/j.jtice.2017.11.034

CrossRef Full Text | Google Scholar

Thottathil, J. K., Moniot, J. L., Mueller, R. H., Wong, M. K., and Kissick, T. P. (1986). Conversion of L-pyroglutamic acid to 4-alkyl-substituted L-prolines. The synthesis of trans-4-cyclohexyl-L-proline. J. Organ. Chem. 51, 3140–3143. doi: 10.1021/jo00366a011

CrossRef Full Text | Google Scholar

Villa, A., Wang, D., Dimitratos, N., Su, D., Trevisan, V., and Prati, L. (2010). Pd on carbon nanotubes for liquid phase alcohol oxidation. Catal Today 150, 8–15. doi: 10.1016/j.cattod.2009.06.009

CrossRef Full Text | Google Scholar

Wang, N., Liu, R., Chen, J., and Liang, X. (2005). NaNO₂-activated, iron-TEMPO catalyst system for aerobic alcohol oxidation under mild conditions. Chem. Commun. 42, 5322–5324. doi: 10.1039/b509167e

CrossRef Full Text | Google Scholar

Xie, J., Yin, K., Serov, A., Artyushkova, K., Pham, H. N., Sang, X., et al. (2017). Selective aerobic oxidation of alcohols over atomically-dispersed non-precious metal catalysts. ChemSusChem 10, 359–362. doi: 10.1002/cssc.201601364

PubMed Abstract | CrossRef Full Text | Google Scholar

Yang, M., Ling, Q., Yang, H., Li, C., and Zhang, A. (2014). Enhanced catalytic activity of K-birnessite MnO2 confined in carbon nanotubes for selective oxidation of benzyl alcohol. Catal. Commun. 46, 238–241. doi: 10.1016/j.catcom.2013.12.031

CrossRef Full Text | Google Scholar

Yang, X., Wu, S., Hu, J., Fu, X., Peng, L., Kan, Q., et al. (2016). Highly efficient N-doped magnetic cobalt-graphene composite for selective oxidation of benzyl alcohol. Catal. Commun. 87, 90–93. doi: 10.1016/j.catcom.2016.09.015

CrossRef Full Text | Google Scholar

Yu, H., Peng, F., Tan, J., Hu, X., Wang, H., Yang, J., et al. (2011). Selective catalysis of the aerobic oxidation of cyclohexane in the liquid phase by carbon nanotubes. Angew. Chem. Int. Ed. 50, 3978–3982. doi: 10.1002/anie.201007932

PubMed Abstract | CrossRef Full Text | Google Scholar

Yuan, Z., Liu, B., Zhou, P., Zhang, Z., and Chi, Q. (2018). Aerobic oxidation of biomass-derived 5-hydroxymethylfurfural to 2, 5-diformylfuran with cesium-doped manganese dioxide. Catal. Sci. Technol. 8, 4430–4439. doi: 10.1039/C8CY01246F

CrossRef Full Text | Google Scholar

Yuvaraj, S., Fan-Yuan, L., Tsong-Huei, C., and Chuin-Tih, Y. (2003). Thermal decomposition of metal nitrates in air and hydrogen environments. J. Phys. Chem. B 107, 1044–1047. doi: 10.1021/jp026961c

CrossRef Full Text | Google Scholar

Zhan, G., Huang, J., Du, M., Sun, D., Abdul-Rauf, I., Lin, W., et al. (2012). Liquid phase oxidation of benzyl alcohol to benzaldehyde with novel uncalcined bioreduction au catalysts: high activity and durability. Chem. Eng. J. 187, 232–238. doi: 10.1016/j.cej.2012.01.051

CrossRef Full Text | Google Scholar

Zhang, E., Tian, H., Xu, S., Yu, X., and Xu, Q. (2013). Iron-catalyzed direct synthesis of imines from amines or alcohols and amines via aerobic oxidative reactions under air. Organ. Lett. 15, 2704–2707. doi: 10.1021/ol4010118

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhao, L., Dong, G., Zhang, L., Lu, Y., and Huang, Y. (2019). Photocatalytic nitrogen oxide removal activity improved step-by-step through serial multistep Cu modifications. ACS Appl. Mater. Interfaces 11, 10042–10051. doi: 10.1021/acsami.9b00111

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhou, W., Liu, J., Pan, J., Sun, F. A., He, M., and Chen, Q. (2015). Effect of Mg2+ on the catalytic activities of CoMgAl hydrotalcites in the selective oxidation of benzyl alcohol to benzaldehyde. Catal. Commun. 69, 1–4. doi: 10.1016/j.catcom.2015.05.012

CrossRef Full Text | Google Scholar

Zhu, S., Cen, Y., Yang, M., Guo, J., Chen, C., Wang, J., et al. (2017). Probing the intrinsic active sites of modified graphene oxide for aerobic benzylic alcohol oxidation. Appl. Catal. B Environ. 211, 89–97. doi: 10.1016/j.apcatb.2017.04.035

CrossRef Full Text | Google Scholar