REVIEW article

Front. Bioeng. Biotechnol., 05 April 2023
Sec. Biomaterials
This article is part of the Research Topic Inorganic/Organic Composite Biomaterials for Bone Treatment, Replacement and Regeneration View all 7 articles

Role of carboxylic organic molecules in interfibrillar collagen mineralization

  • 1Rudolfs Cimdins Riga Biomaterials Innovations and Development Centre of RTU, Institute of General Chemical Engineering, Faculty of Materials Science and Applied Chemistry, Riga Technical University, Riga, Latvia
  • 2Baltic Biomaterials Centre of Excellence, Headquarters at Riga Technical University, Riga, Latvia

Bone is a composite material made up of inorganic and organic counterparts. Most of the inorganic counterpart accounts for calcium phosphate (CaP) whereas the major organic part is composed of collagen. The interfibrillar mineralization of collagen is an important step in the biomineralization of bone and tooth. Studies have shown that synthetic CaP undergoes auto-transformation to apatite nanocrystals before entering the gap zone of collagen. Also, the synthetic amorphous calcium phosphate/collagen combination alone is not capable of initiating apatite nucleation rapidly. Therefore, it was understood that there is the presence of a nucleation catalyst obstructing the auto-transformation of CaP before entering the collagen gap zone and initiating rapid nucleation after entering the collagen gap zone. Therefore, studies were focused on finding the nucleation catalyst responsible for the regulation of interfibrillar collagen mineralization. Organic macromolecules and low-molecular-weight carboxylic compounds are predominantly present in the bone and tooth. These organic compounds can interact with both apatite and collagen. Adsorption of the organic compounds on the apatite nanocrystal governs the nucleation, crystal growth, lattice orientation, particle size, and distribution. Additionally, they prevent the auto-transformation of CaP into apatite before entering the interfibrillar compartment of the collagen fibril. Therefore, many carboxylic organic compounds have been utilized in developing CaP. In this review, we have covered different carboxylate organic compounds governing collagen interfibrillar mineralization.

Introduction

Bone is a heterogenous and anisotropic nanocomposite. The components are arranged hierarchically into several structural levels shown in Figure 1A. The macro-structure consists of cancellous and cortical bone which is divided into microstructure composed of the Haversian system and osteons. The microstructure is divided into sub-microstructures consisting of lamella that are further divided into fibrillar collagen and apatite nanocrystal nanostructure (Fratzl and Weinkamer, 2007). The final sub-nanostructure consists of elements such as minerals, collagen, non-collagenous proteins, and small organic moieties (Heikkilä, 2011). The remarkable mechanical and remodeling capabilities of bone arise from the nanostructure level of collagen fibril and apatite nanocrystal (Liu et al., 2016).

FIGURE 1
www.frontiersin.org

FIGURE 1. (A) Hierarchical organization of bone from macro to the nanoscale. Image inspired by the previous publication of (Rho et al., 1998). (B) Mitochondrial-dependent cellular mechanism of apatite nanocrystal formation. The image is inspired by the fifth jubilee lecture on mitochondria and calcium ion transport (Lehninger, 1970).

The mineral component of bone is formed by a mitochondrial-dependent cellular process as indicated in Figure 1B. In the late ’90s, Albert L. Leininger and coworkers first observed amorphous calcium phosphate (ACP) synthesis in the mitochondria of cells. According to their observations, Ca2+ and phosphate ions in blood plasma are transported into the cell cytoplasm and pumped into the inner wall of mitochondria on a specific carrier by energy-yielding electron transport (Rossi et al., 1967). The ions are accumulated in the mitochondria and once the solubility (concerning ACP) is exceeded, the precipitation occurs in the form of ACP micro-packets. These micro-packets are believed to be stabilized in the mitochondria by an organic moiety termed the “Howard factor.”

In collagen, the charged amino acids are present in both the 67 nm overlap and 40 nm gap zone of collagen providing nucleation sites that regulate the conversion of ACP into an organized array of apatite nanocrystals (Nudelman et al., 2010). It is believed that the net positive charge on the C-terminal of the collagen molecule allows ACP to settle in the collagen fibril. However, auto-transformation of ACP into apatite nanocrystal before entering the interfibrillar compartment of the collagen fibril was observed. Studies have shown that organic carboxylic compounds regulate the conversion of ACP to apatite by hindering auto-transformation. Therefore, many carboxylic compounds have been utilized in developing calcium phosphates carboxylate (Xie and Nancollas, 2010; Yokoi et al., 2022).

Despite these discoveries, the complex process of collagen interfibrillar mineralization is not known completely understood. In the first section of this review, we have focused on the structural and chemical aspects of collagen. In the second half of this review, we have focused on the postulated mechanisms and role of the different carboxylic organic compounds responsible for interfibrillar collagen mineralization.

Structural and chemical properties of collagen

Collagen type I accounts for 90% of the total organic component of the bone (Fuchs et al., 2009). Structurally collagen consists of a subunit known as tropocollagen which is 300 nm long and 1.5 nm wide “rod” consisting of three polypeptide strands. Each polypeptide strand is a left-handed helix, and all three polypeptide strands are twisted to form a right-handed triple helix (Quan and Sone, 2013) as shown in Figure 2. The collagen fiber bends in a tube-like pattern indicating that the composition is not homogenous laterally, but consists of a hard shell and soft core (Gutsmann et al., 2003). In collagen, 64% of non-polar amino acids comprise glycine, proline, and alanine whereas the hydroxyl residue accounts for 16% and majorly consists of hydroxyproline and serine. The acidic, basic, and amide side chains account for the remaining 20% of the collagen structure. Collagen possesses two distinct hydration phenomena depending upon the pH 1) Swelling induced in the neutral salt solution, described as lyophilic or Hofmeister effect; 2) Swelling in acidic or basic solutions, described as the Donnan effect (Bear, 1952).

FIGURE 2
www.frontiersin.org

FIGURE 2. Schematic illustration of the hierarchical structure of collagen.

In bone, the collagen triple helix is arranged in a parallel staggered array in which collagen molecules are shifted by a distance D concerning their adjacent collagen molecule, after their self-assembly into collagen fibrils as indicated in Figure 2 (Glimcher et al., 1981). One D-repeat consists of a complete collagen sequence of 67 nm and the distance between two tropocollagen subunits measures 40 nm termed a gap zone (Landis et al., 2006). The nucleation site of apatite nanocrystal lies in the gap zone of collagen where it achieves the c-axis orientation parallel to the long axis of collagen (Parvizi and Kim, 2010). The intermediate state of CaP such as ACP and/or octa-calcium phosphates (OCP) (Lehninger, 1970; Brown et al., 1987) are presumed to be nucleated in the gap zone of collagen that results in apatite nanocrystal formation.

The remarkable mechanical property of bone arises from the complex association of the apatite nanocrystal and collagen nanocomposite. The initial studies of interfibrillar collagen mineralization were conducted by transmission electron microscopy (TEM) (Weiner and Traub, 1986) followed by electron tomography (ET) analysis (Landis et al., 1993; Landis et al., 1996). These studies revealed that the orientation of apatite nanocrystals may be regulated by confinement in the collagen fibrils forming a deck of card conformation. The cylindrical nanopores in the collagen can direct the oriented growth of apatite nanocrystals in vivo (Olszta et al., 2007). However, this suggestion cannot be considered without detailed ultrastructure of the collagen gap zone. Recently, the detailed model of interfibrillar collagen mineralization was presented by Xu and coworkers. The analysis was performed on the surgical waste material from the tibia fracture of a ten-year-old healthy female. X-ray diffraction (XRD), Electron microscopy and tomography analysis have revealed, the dimension (∼65 nm × 20 nm × 3 nm) of the interfibrillar crystals that possess curved or propeller-like morphology. Extracellular apatite nanocrystals of similar dimensions were also observed which may potentially proliferate into the fibers. The charged amino acids in the collagen are considered to regulate and induce the nucleation of apatite nanocrystals. The study delivered three aspects a) Interfibrillar apatite nanocrystal orientation, b) structure of collagen gap zone, and c) apatite-collagen interaction (Xu et al., 2020).

Nucleation site in collagen

The ultrasound studies revealed that the apatite nanocrystal deposition in extracellular space and arrangement on collagen fibers was not random but aligned. The apatite nanocrystal was deposited specifically along the axial region of collagen fibers. Electron micrographs showed physiochemical interactions, organizing CaP in 700 Å axial repeat of the collagen fibers. Moreover, the c-axis of apatite nanocrystals is aligned to the long axis of the collagen which may be responsible for the nucleation of apatite nanocrystals in c-axis orientation (Landis, 1986). This eliminates the possibility of orientation through mechanical pressure generated by the dense packing of many apatite nanocrystal crystals.

The charged amino acids such as glutamic acid, hydroxyl-serine, aspartic acid, lysine, arginine, and histidine were found in several two-dimension structure of type-I collagen molecular segment as well as in the adjacent segments of the triple helix chain. The charge distribution of the peptide in the collagen chain offers charged domain that serves as center for apatite formation (Landis and Silver, 2009). The locations containing these specific amino acids have stereochemical configurations that provided binding sites for calcium and phosphate ions. Moreover, the ions are sufficiently close to stimulating ion interaction and formation of apatite nucleation sites (Höhling et al., 1974). In the quasi-hexagonal model, the lysine (at residue 108) and the glutamic acid (at residue 110) in a segment I and the glutamic acid (at residue 815) and arginine (at residue 816) in segment 4 result in a pocket that can accommodate calcium and phosphate ions. The ion binding efficiency also increases in the same gap zone through interaction with glutamic acid (at residue 116) in segment 1, arginine (at residue 350) in segment 2, arginine/aspartic acid (at residue 581 and 582, respectively) and glutamic acid/arginine (at residue 815 and 816, respectively) in segment 4 (Hulmes and Miller, 1979). The stereochemical configuration of the amino acids present within or between the collagen segments provided calcium and phosphate binding sites that aid in the formation of nucleation centers. Recently Silver and Landis (2011) provided more consideration in collagen mineralization; a) orientation of charged side chain, b) collagen crosslinking, and c) impact of non-collagenous molecules.

Experimental studies have shown that the synthetic ACP/collagen combination alone is not capable of initiating the nucleation of apatite rapidly (Bradt et al., 1999). Therefore, it was understood that there is the presence of a nucleation catalyst governing the process (Wang and Nancollas, 2008). The nucleation catalyst was defined as an organized organic molecule, containing specific reactive side chains arranged in specific stereochemical and electrochemical arrays establishing a nucleation site as shown in Figure 3. This allows precise cellular control and molecular localization of the interfibrillar collagen mineralization process (Bonar and Glimcher, 1970; Glimcher, 1979).

FIGURE 3
www.frontiersin.org

FIGURE 3. Nucleation sites in the hole zone of the alpha-collagen fibril. The image is inspired by the work of (Glimcher, 1984).

ACP and role of Howard factor

Studies of infant rib bone revealed the presence of a non-crystalline phase before the initiation of the “interfibrillar collagen mineralization front” (Robinson and Watson, 1952). Following, in 1956, Jackson and Randall (2008) studied the periosteal bone growth in fowl embryos and discovered an electron-opaque substance in a newly formed fibrous matrix. This opaque substance was considered an amorphous phase of mineral. Further, in 1959, a similar finding was reported while investigating parietal bone in mice. They the provided first morphological evidence of the ACP (Molnar, 1959).

Finally, in 1966, the first experimental studies on ACP were demonstrated (Harper and Posner, 2016). They observed that the non-crystalline counterpart was evenly distributed in osseous tissue in several mammalian species. Further, they described that 40% of the bone mineral in the femur of adult humans, cows, and rats was comprised of the non-crystalline phase (Termine and Posner, 1966). Additionally, Posner (1969) confirmed bone mineral as poorly crystalline calcium phosphate (PCCP) which was not identical to the structure and composition of hydroxyapatite (HaP). They proved that bone consists of physically and chemically divergent phases of CaP. Further studies concluded that the bone consists of a large amount of non-crystalline or ACP apart from apatite nanocrystals.

Along with ACP, parallel studies were undergoing to understand the role of cells in the formation of CaP. In the fifth Jubilee lecture of Lehninger (1970), the role of mitochondria and the active Ca2+ ion transport was demonstrated in detail. The major topics such as Ca2+ ion a) specificity, b) tissue distribution, c) transport mechanism, d) affinity binding, e) relaxation cycle in muscle, f) formation of calcium phosphate granules, and g) role of mitochondria in interfibrillar collagen mineralization was thoroughly discussed. The key findings are highlighted in the following paragraph.

The rat kidney mitochondria can accumulate enormous quantities of Ca2+ depending on the presence of respiratory substances such as isocitrate, succinate, adenosine triphosphate (ATP), Mg2+, and/or inorganic orthophosphate (Vasington and Murphy, 1962). In the following year, the relationship between the number of electrons flowing through the respiratory chain and the number of Ca2+ ion accumulation was identified. The stoichiometric uptake of both Ca2+ and phosphate ions was synergistic with electron transport in such a way that 1.7–2.0 Ca2+ ions and 1.0 phosphate ions accumulate per pair of electrons sloping each of three energy-conserving sites of the respiratory chain (Bielawski and Lehninger, 1966). Furthermore, it was also observed that the Ca2+ arouses respiration of mitochondria in such a way that two Ca2+ ions capitulate the same amount of oxygen as required by one Adenosine diphosphate (ADP) (Carafoli and Lehninger, 1964). The accumulation of Ca2+ ions is completed by the ejection of H+ ions (Rossi et al., 1966). This is one of the major findings of the relationship between Ca2+ and anion accumulation.

Mitochondria are accumulated with Ca2+ and diverse types of anions under different conditions. Thus, Ca2+ ions are bound to the inner membrane of mitochondria until a perfect anion is available and in the presence of the permanent anion, Ca2+ appears in the matrix. ATP or ADP is required in the formation of ACP that accumulates in the mitochondria. This leads to massive loading of mitochondria with ACP. However, the role of ATP in the process remains unknown (Lehninger, 1970).

Based on the experimental evidence of cellular machinery involved in CaP formation, Leininger and co-workers presented two theories on the formation of ACP and its conversion to apatite. According to the first theory, the formation of bone apatite in the presence of a biological inhibitor was presented as shown in Figure 4 (Scheme 1). The process is initiated in interstitial fluid, where the Ca2+ and phosphate ions in the presence of biological factor (presumed to be Howard factor) undergo localized concentration to exceed the solubility of ACP. The role of the Howard factor was crucial as it prevents the non-biological formation of apatite from free Ca2+ and phosphate ions. Further, the ACP micro-packets formed in association with the Howard factor undergo non-reversible hydrolysis followed by nucleation and are later converted to the apatite nanocrystal.

FIGURE 4
www.frontiersin.org

FIGURE 4. Possible mechanism of bone apatite formation from ACP in the presence of biological inhibitor. Scheme 1—apatite formation mechanism in extracellular fluid and Scheme 2—mitochondrial-dependent cellular mechanism of bone apatite formation. The images are inspired by the fifth jubilee lecture on mitochondria and calcium ion transport of (Lehninger, 1970).

The Second hypothesis describes the mitochondrial-dependent cellular mechanism as shown in Figure 4 (Scheme 2). According to this theory, the Ca2+ and phosphates ions in blood plasma are transported into the cell cytoplasm. Further, the ions are pumped into the inner wall of mitochondria on specific carriers by energy-yielding electron transport (Rossi et al., 1967). When the solubility product of ACP is exceeded, precipitation of micro-packets occurs. The Adenosine triphosphate (ATP) dependent process continues resulting in electron opaque granules composed of many ACP micro-packets which are stabilized by the Howard factor. The micro-packet of ACP can transfer from the mitochondria in two ways; 1) Direct transfer through a mitochondrial membrane or 2) by reverse phagocytosis, leading to out pocketing of membrane vesicles containing two or more micro-packets. After ejecting these micro packets into the extracellular site, they attach to the epitaxial structure of collagen and become part of an amorphous bone mineral fraction. These micro-packets were identified as Posner clusters which possess a neutral ion cluster of 10Å in the longest dimension with a probable chemical structure Ca9(PO4)6 (Betts et al., 1975).

In both, the hypothesis of the role of the Howard factor was crucial in stabilizing ACP. This Howard factor was discovered first, in urine samples (Howard and Thomas, 1968). It was classified as a small organic molecule synthesized by cells, organic in nature, highly acidic, chelating agent and its methylation causes loss of activity. Although there is no evidence about the exact chemical structure of the Howard factor in the literature. Further research was not performed to understand the exact chemical structure of the Howard factor.

Micro-vesicle theory

In 1967, Bonucci studied the early stage biomineralization in cartilage. The process was initiated by the formation of peri-circular, periodic acid-Schiff positive, osmiophilic, rounded bodies in which the nucleation of apatite nanocrystals was initiated. The crystallites were removed by decalcification leaving “ghost bodies,” which were organic in nature like protein absorbed on the surface of the apatite nanocrystals. The formations of these bodies seem unclear but were believed that these bodies can be formed enzymatically or were secreted by cells. Electron microscopy analysis did not show any structure in these bodies until the initiation of biomineralization. However, these bodies were formed by a homogeneous substance that possesses variable electron density (Bonucci, 1967). In the same year, Anderson also studied the development of cartilage and biomineralization. The electron microscopy studies revealed that the culture of human amniotic cells (FL strain) induces the deposition of a radial cluster-like apatite nanocrystal in the cartilage matrix. This bears a resemblance to the native pattern observed at the epiphysis. Both these studies observed electron-dense “leaf-like” structures with needle-like projections attached to the collagen fibrils in ossifying cartilage matrix, which was then classified as matrix vesicles (MV) (Anderson, 1967).

The properties, function, biogenesis, and biological models of micro-vesicles from chondrocytes and osteoblasts are recently reported in the review presented by Bottini et al. (2018). They proposed that one or more annexin family proteins were responsible for the uptake of Ca2+ ion in the MV as shown in Figure 5. They assumed that AnxA5 may act as a carrier protein that will transport Ca2+ ions from mitochondria to the inner leaflet of the plasma membrane where it can bind to phosphatidylserine (PS). It was postulated that the lipid rafts in the microvilli membrane form a complex of PS, AnxA5, Ca2+, and phosphate which accounts for the formation of the MV nucleation core. Further, it was speculated that the transport of Ca2+ and phosphate ions from mitochondria to intracellular vesicles (IV) towards the extracellular matrix may initiate biomineralization. The author also described another hypothesis in which empty MV budding from chondrocytes is released from the microvilli-like cell membrane. After they are released in the extracellular medium, Ca2+ and phosphate ions are accumulated following nucleation from apatite nanocrystal. Further, the MVs are ruptured by stress or by the activity of phospholipase and the apatite nanocrystals are released in the extracellular medium which mineralizes on collagen fibers (Bottini et al., 2018). Recently, Beck (2019) has described the role of scl34-Na+ phosphate transporter in the biomineralization of bone and tooth. The latest review covers the role of MV mediated mechanism with special reference to the crystal ghost in depth (Bommanavar et al., 2020).

FIGURE 5
www.frontiersin.org

FIGURE 5. Schematic representation of MV in biomineralization. The biomineralization by MV occurs in two steps, in step 1 apatite nanocrystal is formed via the influx of calcium and phosphate ions through AnXA5. The hydrolytic action of the enzyme phospholipase and the protease leads to the penetration of apatite crystal inside MV. Once the MV is released into the extracellular matrix they bind to collagen. This initiates step 2 resulting in biomineralization in presence of collagen. The image is inspired by the artwork of (Bottini et al., 2018) and (Bommanavar et al., 2020).

Phosphoprotein

The phosphoproteins containing serine and threonine amino acids are believed to play a role in interfibrillar collagen mineralization. Organic phosphate and carboxylic side chain groups of serine and threonine account for half of all amino acid residues of phosphoprotein in bone (Spector and Glimcher, 1972). The Ca-binding ability is one of the essential requirements for initiating the nucleation of CaP from solution. The phosphate and the carboxylic side chains of phosphoproteins in dentine have shown remarkable Ca-binding ability (Lee et al., 1977). However, Seyer and Glimcher (1977) have mentioned that Ca-binding with phosphoproteins may decrease interfibrillar collagen mineralization because the electrochemical or stereochemical binding of calcium leads to the unavailability of Ca2+ ions to react with the inorganic phosphates. This results in preventing one or more physicochemical steps (nucleation, crystal growth, or crystal multiplication) in apatite deposition. Therefore, to understand the interaction of Ca-bonded phosphoprotein with organic phosphates; experiments and 31P NMR analysis were performed.

Initially, the phosphoproteins were titrated with calcium chloride in presence of inorganic orthophosphates, and it was found that in the absence of calcium chloride, there was no shift in 31P NMR signals but on the other hand phosphorous peak was observed with broadening or shifting in the presence of calcium chloride. This confirms the formation of a ternary complex between the orthophosphate ions and the proteins phosphomonoester group (Lee et al., 1983). The phosphoprotein-regulated interfibrillar collagen mineralization process is shown in Figure 6. In 1982, Lian and associates have revealed in vivo evidence of phosphoproteins in interfibrillar collagen mineralization (Kiebzak et al., 1988).

FIGURE 6
www.frontiersin.org

FIGURE 6. Schema for the role of phosphoproteins interfibrillar collagen mineralization. The image is inspired by the artwork of (Glimcher, 1984).

Non-collagenous proteins

Collagen account total of 90% organic part of the bone and the remaining part is non-collagenous proteins and low-molecular-weight organic compounds. The non-collagenous proteins are usually referred to as small-integrin binding ligand, N-linked glycoprotein (SIBLING) proteins which consist of osteopontin (OSP), dentin matrix protein (DMP), bone sialoprotein (BSP), dentin sailophosphoprotein (DSPP), and matrix extracellular phosphoglycolproteins (MEPE). These proteins possess the collagen-binding ability as well as RGD sequence for cell binding. Moreover, these proteins share common features of glycosylation, and phosphorylation and have similarities in genomic organization and localization (Huang et al., 2008). A detailed description of the proteins is presented elsewhere (Kalka et al., 2019). Moreover, albumin and α2-HS-glycoproteins are present throughout the mineralized bone matrix (McKee et al., 1993). Studies have shown evidence of the involvement of these non-collagenous playing a vital role in interfibrillar collagen mineralization which is explained in the subsequent sections.

Albumin

Albumin is the major component of blood and one of the important non-collagenous proteins. It possesses a high affinity towards apatite surface inhibiting crystallization. Therefore, it is known as a factor regulation process of interfibrillar mineralization of collagen. Studies on the precipitation and growth mechanism of OCP in collagen, under the influence of serum albumin, revealed the inhibition capacity of albumin in two ways—the association of the carboxyl group of protein with the calcium of OCP and/or adsorption of albumin on the surface of OCP. There was electrostatic interaction between the positively charged OCP and collagen and negatively charged albumin at pH 6.5. The adsorption of albumin at the nucleation site of the collagen surfaces obstructs the nucleation sites of the substrate thus delaying the first nuclei formation. Crystallization of OCP is rapid on the collagen surface, therefore interfibrillar collagen mineralization is hampered. However, the addition of albumin would obstruct the nucleation sites leading to interfibrillar collagen mineralization (Combes et al., 1999).

α2-HS-glycoproteins

In 1944, Fetuin was first isolated from bovine serum and since then most commonly known as Fetuin-A or α2-HS-glycoprotein (Mori et al., 2012). α2-HS-glycoproteins in the serum inhibit calcium precipitation thus hindering apatite formation. This inhibitory effect was governed by acidic amino acids modulating apatite formation and inhibiting phase separation in serum during the interfibrillar collagen mineralization (Schinke et al., 1996). Further electron microscopy studies have shown that α2-HS-glycoproteins with ACP form soluble colloidal spheres. These spheres were termed calciprotein particles that are amorphous in nature with sizes ranging from 30 to 150 nm. The binding of acidic amino acid of α2-HS-glycoproteins with ACP inhibits unwanted mineralization outside the interfibrillar collagen (Heiss et al., 2003).

Oesteopontin and osteocalcin

OCP-osteocalcin complex directs collagen interfibrillar collagen mineralization. Transmission electron microscopy (TEM) analysis revealed that the carboxylate groups in glutamic acid in osteocalcin (OSC) deliver attachment sites to OCP (Pompe et al., 2015). Further, the OSC attaches to collagen and interacts with the Ca-sites of apatite platelets with a Ca-Ca distance of 9.5 Å. Therefore, it was claimed that OSC governs the function of Ca2+ ion transport and acts as an intermediary molecule in the nucleation of OCP and apatite in the fibrillar space of collagen (Simon et al., 2018). Further studies revealed the interaction of OSP and OSC with calcium ions induces stability and delays nucleation, whereas interaction with inorganic phosphates results in opposite effects. The study also indicates that OSC concentration negatively influences crystal size and rate of formation though OSC presence results in ordered apatite structures. On the contrary, OSP concentration promotes crystal formation and reduces the Ca:P ratio (Duman et al., 2019).

Dentin matrix protein

The carboxylic terminal present in the amino acids of the protein plays a crucial role in phosphorylation and binding with Ca2+ ions controlling interfibrillar collagen mineralization in dentin (George et al., 1993). Tsuji et al. (2008) synthesized artificial motifs analogous to dentin matrix protein. ACP in presence of these proteins increases the molecular mass and the fractal dimensions without affecting the gyration radii. The protein thus enables the conversion of ACP to apatite. The nucleation initiates at the small radius of the growing crystal till the crystal reaches a critical size (termed a critical radius), following rapid crystal growth. This critical radius can be expressed by the function of temperature, supersaturation, specific internal energies, and volume of growth units.

Low-molecular-weight organic compounds

Parathyroid hormone

The role of parathyroid hormone in calcium metabolism was discovered in 1909 (MacCallum and Voegtlin, 1909). The mechanism of action of the parathyroid hormone was well described in the previous review articles (Rasmussen, 1961; Potts et al., 1982). In 1956, Neuman et al. (1956) postulated a mechanism under the control of the parathyroid gland that was maintaining gradients of calcium ions between blood and bone. The cellular element in the bones secreted citrates in response to parathyroid activity. It was assumed that the citrates carrying calcium complex from serum to skeletal tissue get citrated and oxidized to form several calcium ions. If citrates were secreted in the form of citric acid, then due to the pH gradient ionized calcium ions will be transported to serum. The hypothesis was supported by the in vitro enzyme studies. It was found that the enzyme isocitrate dehydrogenase, which is required for citrate utilisation was absent in mature bone. Moreover, the parathyroid hormone destroys the chromophore groups of Coenzyme II. Blocking Coenzyme II-linked reactions shuts glucose metabolism to citrate production. This provides a captivating biochemical mechanism governed by parathyroid hormone in regulating citrate gradient that is responsible for maintaining steady but supersaturated levels of calcium ions in serum.

Citrate

Citrates are small organic moieties that originate in the citric acid cycle and play a critical role in the human metabolic pathway. In 1941, the presence of citrate in bone was first identified (Dickens, 1941). Since then, it is known that citrate concentration in hard tissues is in the range of 20–80 μmole/g which is 100–400 folds higher than in most of the soft tissues. It should also be indicated that the bone consists of 1.6% of citrate and about 90% of total body citrates are found in human bone (Granchi et al., 2019). Such a high concentration of citrates in bone indicates their vital role in mineralization. Recent NMR studies have shown the presence of citrate in bone (Davies et al., 2014). The lattice orientation, particle size, and distribution of the apatite are regulated by the complex interaction of the citrate with the apatite. The long axis of the citrate molecule is parallel to the surface of the apatite. The three carboxylic groups of citrates are at 0.3–0.45 nm from the apatite surface. The spacing of the carboxylic groups matches with the calcium ion along the c-axis of the apatite. Therefore, the crystal growth is inhibited in the direction of thickness but continued in the longitudinal direction. This assists in the formation of a plate-like apatite structure analogous to natural bone (Xie and Nancollas, 2010).

The occurrence of citrate in bone and its relationship was well described by Costello et al. (2012). The author coined the term “citration” which describes the relationship between citrate-apatite nanocrystals. In further studies, the author also described the potential mechanism of how citrate is involved in interfibrillar collagen mineralization (Costello et al., 2015). The collagen/apatite structure incorporated with citrate in the apatite crystal was depicted as shown in Figure 7.

FIGURE 7
www.frontiersin.org

FIGURE 7. The status of citrate in apatite/collagen component of bone. The image is inspired by the artwork of (Costello et al., 2018).

Succinate

Succinic acid (SA) is an intermediate of a citric acid cycle. It can be detected in the bones in exceedingly small concentrations. For instance, 1 g of bone consists of 3.6 mg of SA (Lees and Kuyper, 1957). Like citrates, the carboxylic groups in SA are chemisorbed on the apatite surface by coordinating with calcium ions and regulating the growth and morphology of the crystals. Studies on mineralization reported that SA binds to collagen by hydrogen bonding and encourages interfibrillar collagen mineralization. The interaction of SA with collagen improved the physicochemical properties of apatite and attract more calcium ions, thus leading to accelerated interfibrillar collagen mineralization. Moreover, the SA pre-treated demineralized dentin promoted dentin remineralization. The mechanical properties of the remineralized dentin were similar to natural dentin (Jin et al., 2022). Earlier efforts to synthesize OCP incorporated with SA have been commenced by Marković et al. (1994). They uncovered pH dependency on conversion from SA-OCP to apatite.

Amino acids

Apatite formation was observed near the crossband of collagen where basic and acidic amino acids are thought to be more concentrated (Robinson and Watson, 1955). Soon after this finding, Solomons and Irving (1958) studied the relationship of Є-amino acid of lysine and hydroxylysine in mineralization. The Є-amino acid may provide potential phosphate binding sites on the collagen, leading to its phosphorylation. This was assumed to be the first step in matrix interfibrillar collagen mineralization (Weidmann, 1963). Ikawa et al. (2009) have synthesized amino acid-containing ACP and investigated its transformation in a simulated body fluid. They found that the incorporation of amino acids enhanced the solubility of ACP and lead to faster conversion to apatite. The role of amino acids in mineralization is covered in-depth in a recent review by Tavafoghi and Cerruti (2016).

Pyrophosphate

Fleisch and Sylvia demonstrated in vitro nucleation and mineralization of apatite nanocrystals in presence of collagen (Herbert and Bisaz, 1962). They have proposed the role of pyrophosphate in regulating biomineralization. In the nucleating region of collagen, the precipitation of apatite nanocrystals occurs at the physiological concentration of the Ca2+ and phosphate ions. It was depicted that the inorganic pyrophosphates (PPi) present in blood plasma protect the nucleation site in the collagen inhibiting growth of apatite nanocrystals. For the mineralization of collagen, the pyrophosphates must be inactivated by the enzyme pyrophosphatase which was found in mineralized tissue (Herbert And Bisaz, 1962). Further studies conducted by Moochhala et al. (2008) explored the role of proteins and genes in controlling biomineralization. The enzyme nucleoside pyrophosphatase phosphodiesterase (NPP1) acts on nucleoside triphosphate to generate extracellular PPi. Harmey et al. (2004) have further demonstrated hyper-mineralization in enpp1 (NPP1) knockout mice, resulting in peripheral joint hyperostosis intervertebral fusion. Moreover, the role of the ank gene (ANKH in humans) in exporting PPi from cytoplasm to extracellular space was noticed. The ank protein was linked with tissue calcification in humans and mice. The third gene akp2 encodes tissue non-specific alkaline phosphatase (TNAP) which hydrolyses PPi, and polyphosphates to release inorganic phosphate. The TNAP activity promotes biomineralization by lowering PPi levels and increasing levels of inorganic phosphate.

Polymer-induced liquid precursors

Polymer-induced liquid precursors (PILP) are amorphous mineral precursors stabilized by charged polymers. In the early 1990s, the role of acidic macromolecules in the biomineralization of bone and seashells was known. The acidic macromolecule was known to control the morphology of the inorganic crystal. However, the function of the acidic macromolecule was not clarified. In 1998, Gower and Tirrell (1998) have discovered that the addition of a small amount of polyaspartic acid (pAap) results in CaCO3 helices and films. The polymer acts as a membrane and supports the deposition and growth of CaCO3. The charge polymer ion inhibits crystal nucleation by inducing liquid-liquid phase separation in the crystallizing fluid. Droplets from the fluidic amorphous phase accumulate and combine resulting in mineral films. Olszta et al. (2007) have postulated the role of PILP biomineralization of bone and teeth. They suggest that the apatite nanocrystal does not nucleate within the gap zone, rather a liquid amorphous phase is pulled into collagen fibers by capillary actions. Once the liquid precursor phase is converted to the solid amorphous phase, crystallization occurs resulting in mineralized collagen with apatite nanocrystals. A combination of polyanionic non-collagenous proteins was presumed to be analogous to PILP. This hypothesis was backed by cryo-TEM analysis by Nudelman et al. (2010). They discovered that the electrostatic interaction between pAap-ACP complex and the cationic amino acids in the gap zone of collagen assists infiltration of PILP. Citrate also plays a crucial role in PILP by enhancing the degree of collagen mineralization in vitro. The citrate reduces the interfacial energy between collagen and PILP leading to an increase in wettability (Shao et al., 2018). Polyacrylic acid (PAA) was also used successfully in PILP for the stabilization of ACP. PAA of various molecular weights was analyzed, and it was found that both low and high-concentration PAA stabilized ACP and allows infiltration in the collagen matrix. The unstable ACP results in extra fibrillar mineralization. On the contrary, extensively stabilized ACP did not initiate collagen mineralization. This suggests that the concentration of PAA plays a crucial role in regulating interfibrillar collagen mineralization (Shen et al., 2021).

Discussion

It is known that collagen plays a crucial role in the biomineralization process. The unique physiochemical properties of collagen offer this potential. Based on the physical characteristics of hydration a model of collagen interfibrillar biomineralization was demonstrated. Molecular dynamic studies have shown the balance between osmotic equilibrium and electroneutrality establishes Gibbs-Donnan equilibrium in a polyelectrolyte-directed system (Niu et al., 2017). Based on the chemical properties of collagen numerous models are presented. For instance, the amino acid residue in the two-dimension structure of type-I collagen molecular segment as well as in the adjacent segments of the triple helix chain. The charge distribution of the peptide in the collagen chain offers charged domain that serves as a center for apatite formation. However experimental studies have shown that the synthetic ACP/collagen combination alone is not capable of initiating the nucleation of apatite rapidly (Bradt et al., 1999). This indicates that collagen cannot initiate or regulate interfibrillar mineralization alone (Posner, 1969). Therefore, the role of non-collagenous proteins and other ECM molecules was considered to affect mineralization either by enhancing collagen mineral interaction or binding mineral ions. However, there are numerous postulations on this phenomenon, but the exact mechanism is poorly understood (Silver and Landis, 2011).

There are numerous mechanisms for how calcium phosphate is deposited on the collagen matrix. Different organic compounds are believed to regulate interfibrillar mineralization. Most of these compounds possess a carboxyl functional group. The carboxyl group is a combination of two functional groups in which a single carbon atom is attached to hydroxyl (−OH) and carbonate (=O) groups. This makes the carbonyl group polar, highly electronegative, and weakly acidic, capable of hydrogen bonding by accepting or donating proton (Klecker and Nair, 2017). The carboxylate anion has the capability of forming bonds with calcium by direct binding or by influencing electrostatic interactions away from the metal center (Chakrabarti, 1990). Moreover, the carboxylate ions also have the potential to react with phosphate via the formation of P-O-H-O-C bonding (Corbridge, 1971). Owing to these exclusive properties, carboxylate-incorporated calcium phosphate materials are gaining more interest.

In the past 20 years, the research is focused on finding the role of carboxylic compounds in interfibrillar collagen mineralization (Ikawa et al., 2008; Sakamoto et al., 2008; Ishikawa and Oaki, 2014; Josipović et al., 2020; Veiga et al., 2020; Wang et al., 2020). Recent studies have also provided new findings such as A) Influence of carboxylic ions in the conversion of ACP to OCP (Sugiura et al., 2015). B) The density of carboxylic ions plays a crucial role in controlling the growth and mineralization of calcium phosphates (Zhang et al., 2022). C) In the early nucleation, citrate binds to ACP and controls the size and morphology of apatite crystal (Xie and Nancollas, 2010). D) One-sixth of the available apatite surface area in bone is covered by citrate (Xie and Nancollas, 2010). E) Carboxylate ions can only be incorporated into the hydrated layer of CaP (Yokoi et al., 2022). F) Collagen matrix is denser and irregularly distributed in the bone as compared to the majority of other soft tissues (Tzaphlidou, 2008).

Conclusion

Interfibrillar collagen mineralization has gained attention in the past 20 years, the major reason is the abundance of both apatite nanocrystals and collagen in bone. Studies have indicated the role of physiochemical properties of collagen as well as non-collagenous proteins and low molecular weight compounds regulating the process. New insights such as the role of genes and enzymes in this process are also discovered. Overall, the process of interfibrillar collagen mineralization is complex. However, advanced analysis techniques such as cryo-TEM, Cryo-scanning electron microscopy, X-Ray tomography, molecular dynamics, gene knockout, metabolomics, proteomics, DNA and RNA sequencing, etc. allow investigation of mechanism within nanometer resolution while maintaining the structure close to the native structure. These advanced analysis techniques with a combination of both in vivo and in vitro analysis potentially answer all the underlying questions in the future. However, the process is currently in the preliminary stage, but the technological advancement will soon decode the process of interfibrillar collagen mineralization.

Author contributions

AI: Conceptualisation, literature review, writing-original draft preparation. RC: Writing-review and editing. KR: Writing-review and editing. JL: Conceptualisation, writing-review, and editing. All authors provided critical feedback and helped to shape the research, analysis, and manuscript.

Acknowledgments

The authors acknowledge financial support from the European Union’s Horizon 2020 research and innovation programme under the grant agreement No. 857287 (BBCE – Baltic Biomaterials Centre of Excellence) and the Baltic Research Programme project No. EEA-RESEARCH-85 “Waste-to-resource: eggshells as a source for next generation biomaterials for bone regeneration (EGGSHELL)” under the EEA Grant of Iceland, Liechtenstein, and Norway No. EEZ/BPP/VIAA/2021/1.

Conflict of interest

The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.

Publisher’s note

All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article, or claim that may be made by its manufacturer, is not guaranteed or endorsed by the publisher.

References

Anderson, H. C. (1967). Electron microscopic studies of induced cartilage development and calcification. J. Cell. Biol. 35, 81–101. doi:10.1083/JCB.35.1.81

PubMed Abstract | CrossRef Full Text | Google Scholar

Bear, R. S. (1952). The structure of collagen fibrils. Adv. Protein Chem. 7, 69–160. doi:10.1016/S0065-3233(08)60018-2

PubMed Abstract | CrossRef Full Text | Google Scholar

Beck, L. (2019). Expression and function of Slc34 sodium–phosphate co-transporters in skeleton and teeth. Pflugers Arch. Eur. J. Physiol. 471, 175–184. doi:10.1007/S00424-018-2240-Y

CrossRef Full Text | Google Scholar

Betts, F., Blumenthal, N. C., Posner, A. S., Beckert, G. L., and Lehningert, A. L. (1975). Atomic Structure of Intracellular Amorphous Calcium Phosphate Deposits (x-ray diffraction/radial distribution analysis/ion clusters/soft-tissue calcification/micropackets). 72, 2088–2090. Available at: https://www.pnas.org (Accessed June 7, 2022).

Google Scholar

Bielawski, J., and Lehninger, A. L. (1966). Stoichiometric relationships in mitochondrial accumulation of calcium and phosphate supported by hydrolysis of adenosine triphosphate. J. Biol. Chem. 241, 4316–4322. doi:10.1016/S0021-9258(18)99724-3

PubMed Abstract | CrossRef Full Text | Google Scholar

Bommanavar, S., Hosmani, J., Togoo, R. A., Baeshen, H. A., Raj, A. T., Patil, S., et al. (2020). Role of matrix vesicles and crystal ghosts in bio-mineralization. J. Bone Min. Metab. 38, 759–764. doi:10.1007/S00774-020-01125-X

CrossRef Full Text | Google Scholar

Bonar, L. C., and Glimcher, M. J. (1970). Thermal denaturation of mineralized and demineralized bone collagens. J. Ultrasructure Res. 32, 545–557. doi:10.1016/S0022-5320(70)80027-2

CrossRef Full Text | Google Scholar

Bonucci, E. (1967). Fine structure of early cartilage calcification. J. Ultrasructure Res. 20, 33–50. doi:10.1016/S0022-5320(67)80034-0

CrossRef Full Text | Google Scholar

Bottini, M., Mebarek, S., Anderson, K. L., Strzelecka-Kiliszek, A., Bozycki, L., Simão, A. M. S., et al. (2018). Matrix vesicles from chondrocytes and osteoblasts: Their biogenesis, properties, functions and biomimetic models. Biochim. Biophys. Acta - Gen. Subj. 1862, 532–546. doi:10.1016/J.BBAGEN.2017.11.005

PubMed Abstract | CrossRef Full Text | Google Scholar

Bradt, J. H., Mertig, M., Teresiak, A., and Pompe, W. (1999). Biomimetic mineralization of collagen by combined fibril assembly and calcium phosphate formation. Chem. Mat. 11, 2694–2701. doi:10.1021/CM991002P

CrossRef Full Text | Google Scholar

Brown, W., Eidelman, N., and Tomazic, B. (1987). Octacalcium phosphate as a precursor in biomineral formation. Adv. Dent. Res. 1 (2), 306–313. doi:10.1177/08959374870010022201

PubMed Abstract | CrossRef Full Text | Google Scholar

Carafoli, E., and Lehninger, A. L. (1964). Binding of adenine nucleotides by mitochondria during active uptake of Ca++. Biochem. Biophys. Res. Commun. 16, 66–70. doi:10.1016/0006-291X(64)90212-8

PubMed Abstract | CrossRef Full Text | Google Scholar

Chakrabarti, P. (1990). Interaction of metal ions with carboxylic and carboxamide groups in protein structures. Protein Eng. Des. Sel. 4, 49–56. doi:10.1093/PROTEIN/4.1.49

CrossRef Full Text | Google Scholar

Combes, C., Rey, C., and Freche, M. (1999). In vitro crystallization of octacalcium phosphate on type I collagen: Influence of serum albumin. J. Mat. Sci. Mat. Med. 10, 153–160. doi:10.1023/A:1008933406806

CrossRef Full Text | Google Scholar

Corbridge, D. E. C. (1971). The structural chemistry of phosphates. Bull. Minéralogie 94, 271–299. doi:10.3406/BULMI.1971.6534

CrossRef Full Text | Google Scholar

Costello, L. C., Chellaiah, M. A., Zou, J., Reynolds, M. A., and Franklin, R. B. (2015). In vitro BMP2 stimulation of osteoblast citrate production in concert with mineralized bone nodule formation. J. Regen. Med. Tissue Eng. 4, 2. doi:10.7243/2050-1218-4-2

PubMed Abstract | CrossRef Full Text | Google Scholar

Costello, L. C., Franklin, R. B., Reynolds, M. A., and Chellaiah, M. (2012). The important role of osteoblasts and citrate production in bone formation: “Osteoblast citration” as a new concept for an old relationship. Open Bone J. 4, 27–34. doi:10.2174/1876525401204010027

CrossRef Full Text | Google Scholar

Costello, L. C., Franklin, R. B., and Reynolds, M. A. (2018). The important role and implications of citrate in the composition, structure, and function of oral/periodontal/craniofacial tissues. Madridge J. Dent. Oral Surg. 3, 85–90. doi:10.18689/MJDL-1000120

PubMed Abstract | CrossRef Full Text | Google Scholar

Davies, E., Müller, K. H., Wong, W. C., Pickard, C. J., Reid, D. G., Skepper, J. N., et al. (2014). Citrate bridges between mineral platelets in bone. Proc. Natl. Acad. Sci. U. S. A. 111. doi:10.1073/PNAS.1315080111/-/DCSUPPLEMENTAL/PNAS.201315080SI

CrossRef Full Text | Google Scholar

Dickens, F. (1941). The citric acid content of animal tissues, with reference to its occurrence in bone and tumour. Biochem. J. 35, 1011–1023. doi:10.1042/BJ0351011

PubMed Abstract | CrossRef Full Text | Google Scholar

Duman, E., Şahin Kehribar, E., Ahan, R. E., Yuca, E., and Şeker, U. Ö. Ş. (2019). Biomineralization of calcium phosphate crystals controlled by protein-protein interactions. ACS Biomater. Sci. Eng. 5, 4750–4763. doi:10.1021/acsbiomaterials.9b00649

PubMed Abstract | CrossRef Full Text | Google Scholar

Fratzl, P., and Weinkamer, R. (2007). Hierarchical structure and repair of bone: Deformation, remodelling, healing. Springer Ser. Mat. Sci. 100, 323–335. doi:10.1007/978-1-4020-6250-6_15/COVER

CrossRef Full Text | Google Scholar

Fuchs, R. K., Warden, S. J., and Turner, C. H. (2009). Bone anatomy, physiology and adaptation to mechanical loading. Bone Repair Biomater. 25–68. doi:10.1533/9781845696610.1.25

CrossRef Full Text | Google Scholar

George, A., Sabsay, B., Simonian, P. A. L., and Veis, A. (1993). Characterization of a novel dentin matrix acidic phosphoprotein. Implications for induction of biomineralization. J. Biol. Chem. 268, 12624–12630. doi:10.1016/S0021-9258(18)31434-0

PubMed Abstract | CrossRef Full Text | Google Scholar

Glimcher, M. J. (1979). Phosphopeptides of enamel matrix. J. Dent. Res. 58, 790–809. doi:10.1177/00220345790580023101

PubMed Abstract | CrossRef Full Text | Google Scholar

Glimcher, M. J., Bonar, L. C., Grynpas, M. D., Landis, W. J., and Roufosse, A. H. (1981). Recent studies of bone mineral: Is the amorphous calcium phosphate theory valid? J. Cryst. Growth 53, 100–119. doi:10.1016/0022-0248(81)90058-0

CrossRef Full Text | Google Scholar

Glimcher, M. J. (1984). Recent studies of the mineral phase in bone and its possible linkage to the organic matrix by protein-bound phosphate bonds. Philos. Trans. R. Soc. Lond. Ser. B 304, 479–508. doi:10.1098/rstb.1984.0041

CrossRef Full Text | Google Scholar

Gower, L. A., and Tirrell, D. A. (1998). Calcium carbonate films and helices grown in solutions of poly(aspartate). J. Cryst. Growth 191, 153–160. doi:10.1016/S0022-0248(98)00002-5

CrossRef Full Text | Google Scholar

Granchi, D., Baldini, N., Ulivieri, F. M., and Caudarella, R. (2019). Role of citrate in pathophysiology and medical management of bone diseases. Nutrients 11, 2576. doi:10.3390/NU11112576

PubMed Abstract | CrossRef Full Text | Google Scholar

Gutsmann, T., Fantner, G. E., Venturoni, M., Ekani-Nkodo, A., Thompson, J. B., Kindt, J. H., et al. (2003). Evidence that collagen fibrils in tendons are inhomogeneously structured in a tubelike manner. Biophys. J. 84, 2593–2598. doi:10.1016/S0006-3495(03)75064-4

PubMed Abstract | CrossRef Full Text | Google Scholar

Harmey, D., Hessle, L., Narisawa, S., Johnson, K. A., Terkeltaub, R., and Millán, J. L. (2004). Concerted regulation of inorganic pyrophosphate and osteopontin by Akp2, Enpp1, and ank: An integrated model of the pathogenesis of mineralization disorders. Am. J. Pathol. 164, 1199–1209. doi:10.1016/S0002-9440(10)63208-7

PubMed Abstract | CrossRef Full Text | Google Scholar

Harper, R. A., and Posner, A. S. (2016). Measurement of non-crystalline calcium phosphate in bone mineral. Proc. Soc. Exp. Biol. Med. 122 (1), 137–142. doi:10.3181/00379727-122-31073

CrossRef Full Text | Google Scholar

Heikkilä, J. (2011). Use of bioactive glasses as bone substitutes in orthopaedics and traumatology. Bioact. Glas. Mat. Prop. Appl. 189–208. doi:10.1533/9780857093318.2.189

CrossRef Full Text | Google Scholar

Heiss, A., DuChesne, A., Denecke, B., Grötzinger, J., Yamamoto, K., Renneé, T., et al. (2003). Structural basis of calcification inhibition by α2-HS glycoprotein/fetuin-A: Formation of colloidal calciprotein particles. J. Biol. Chem. 278, 13333–13341. doi:10.1074/JBC.M210868200

PubMed Abstract | CrossRef Full Text | Google Scholar

Herbert, F., and Bisaz, S. (1962). Mechanism of calcification: Inhibitory role of pyrophosphate. Nat 195, 911. doi:10.1038/195911a0

CrossRef Full Text | Google Scholar

Höhling, H. J., Ashton, B. A., and Köster, H. D. (1974). Quantitative electron microscopic investigations of mineral nucleation in collagen. Cell. Tissue Res. 148, 11–26. doi:10.1007/BF00224315

PubMed Abstract | CrossRef Full Text | Google Scholar

Howard, J. E., and Thomas, W. C. (1968). Control of crystallization in urine. Am. J. Med. 45, 693–699. doi:10.1016/0002-9343(68)90205-2

PubMed Abstract | CrossRef Full Text | Google Scholar

Huang, B., Sun, Y., MacIejewska, I., Qin, D., Peng, T., McIntyre, B., et al. (2008). Distribution of SIBLING proteins in the organic and inorganic phases of rat dentin and bone. Eur. J. Oral Sci. 116, 104–112. doi:10.1111/J.1600-0722.2008.00522.X

PubMed Abstract | CrossRef Full Text | Google Scholar

Hulmes, D. J. S., and Miller, A. (1979). Quasi-hexagonal molecular packing in collagen fibrils. Nature 282, 878–880. doi:10.1038/282878A0

PubMed Abstract | CrossRef Full Text | Google Scholar

Ikawa, N., Hori, H., Kimura, T., Oumi, Y., and Sano, T. (2008). Templating route for mesostructured calcium phosphates with carboxylic acid- and amine-type surfactants. Langmuir 24, 13113–13120. doi:10.1021/la8008859

PubMed Abstract | CrossRef Full Text | Google Scholar

Ikawa, N., Kimura, T., Oumi, Y., and Sano, T. (2009). Amino acid containing amorphous calcium phosphates and the rapid transformation into apatite. J. Mat. Chem. 19, 4906–4913. doi:10.1039/B815154G

CrossRef Full Text | Google Scholar

Ishikawa, M., and Oaki, Y. (2014). Synthesis of Hydroxyapatite/Nanocellulose Composites.

Google Scholar

Jackson, S. F., and Randall, J. T. (2008). “Fibrogenesis and the Formation of Matrix in Developing Bone,” in John Wiley & Sons. 47–64. doi:10.1002/9780470715222.CH5

CrossRef Full Text | Google Scholar

Jin, W., Jin, Y., Duan, P., Wu, H., Zhang, L., Du, Q., et al. (2022). Promotion of collagen mineralization and dentin repair by succinates. J. Mat. Chem. B 10, 5826–5834. doi:10.1039/D2TB01005D

CrossRef Full Text | Google Scholar

Josipović, T. M., Kovačević, M., Mateša, S., Kostešić, M., Matijaković, N., Radatović, B., et al. (2020). The influence of different classes of amino acids on calcium phosphates seeded growth. Mater. (Basel) 13, 4798. doi:10.3390/MA13214798

CrossRef Full Text | Google Scholar

Kalka, M., Zoglowek, A., Ożyhar, A., and Dobryczycki, P. (2019). Proteins in Calcium Phosphates Biomineralization. Contemp. Top. about Phosphorus Biol. Mater. doi:10.5772/INTECHOPEN.86718

CrossRef Full Text | Google Scholar

Kiebzak, G. M., Smith, R., Gundberg, C. C., Howe, J. C., and Sacktor, B. (1988). Bone status of senescent male rats: Chemical, morphometric, and mechanical analysis. J. Bone Min. Res. 3, 37–45. doi:10.1002/jbmr.5650030107

CrossRef Full Text | Google Scholar

Klecker, C., and Nair, L. S. (2017). Matrix chemistry controlling stem cell behavior. Biol. Eng. Stem Cell. Niches, 195–213. doi:10.1016/B978-0-12-802734-9.00013-5

CrossRef Full Text | Google Scholar

Landis, W. J. (1986). A study of calcification in the leg tendons from the domestic Turkey. J. Ultrastruct. Mol. Struct. Res. 94, 217–238. doi:10.1016/0889-1605(86)90069-8

PubMed Abstract | CrossRef Full Text | Google Scholar

Landis, W. J., Hodgens, K. J., A Song, M. J., and McEWEN, B. F. (1996). Structural relations between bone as determined by high microscopic tomography collagen and mineral in voltage electron. Microsc. Res. Tech. 33–192. doi:10.1002/(SICI)1097-0029(19960201)33:2

CrossRef Full Text | Google Scholar

Landis, W. J., Silver, F. H., and Freeman, J. W. (2006). Collagen as a scaffold for biomimetic mineralization of vertebrate tissues. J. Mat. Chem. 16, 1495–1503. doi:10.1039/B505706J

CrossRef Full Text | Google Scholar

Landis, W. J., and Silver, F. H. (2009). Mineral deposition in the extracellular matrices of vertebrate tissues: Identification of possible apatite nucleation sites on type I collagen. Cells Tissues Organs 189, 20–24. doi:10.1159/000151454

PubMed Abstract | CrossRef Full Text | Google Scholar

Landis, W. J., Song, M. J., Leith, A., McEwen, L., and McEwen, B. F. (1993). Mineral and organic matrix interaction in normally calcifying tendon visualized in three dimensions by high-voltage electron microscopic tomography and graphic image reconstruction. J. Struct. Biol. 110, 39–54. doi:10.1006/JSBI.1993.1003

PubMed Abstract | CrossRef Full Text | Google Scholar

Lee, S. L., Glonek, T., and Glimcher, M. J. (1983). 31P nuclear magnetic resonance spectroscopic evidence for ternary complex formation of fetal dentin phosphoprotein with calcium and inorganic orthophosphate ions. Calcif. Tissue Int. 35, 815–818. doi:10.1007/BF02405129

PubMed Abstract | CrossRef Full Text | Google Scholar

Lee, S. L., Veis, A., and Glonek, T. (1977). Dentin phosphoprotein: An extracellular calcium-binding protein. Biochemistry 16, 2971–2979. doi:10.1021/BI00632A026

PubMed Abstract | CrossRef Full Text | Google Scholar

Lees, H., and Kuyper, A. C. (1957). The organic acids of bone. J. Biol. Chem. 225, 641–649. doi:10.1016/S0021-9258(18)64863-X

PubMed Abstract | CrossRef Full Text | Google Scholar

Lehninger, A. L. (1970). Mitochondria and calcium ion transport. Biochem. J. 119, 129–138. doi:10.1042/bj1190129

PubMed Abstract | CrossRef Full Text | Google Scholar

Liu, Y., Luo, D., and Wang, T. (2016). Hierarchical structures of bone and bioinspired bone tissue engineering. Small 12, 4611–4632. doi:10.1002/SMLL.201600626

PubMed Abstract | CrossRef Full Text | Google Scholar

MacCallum, W. G., and Voegtlin, C. (1909). On the relation of tetany to the parathyroid glands and to calcium metabolism. J. Exp. Med. 11, 118–151. doi:10.1084/JEM.11.1.118

PubMed Abstract | CrossRef Full Text | Google Scholar

Marković, M., Fowler, B. O., and Brown, W. E. (1994). Octacalcium phosphate carboxylates: IV. Kinetics of formation and solubility of octacalcium phosphate succinate. J. Cryst. Growth 135, 533–538. doi:10.1016/0022-0248(94)90144-9

CrossRef Full Text | Google Scholar

McKee, M. D., Farach-Carson, M. C., Butler, W. T., Hauschka, P. V., and Nanci, A. (1993). Ultrastructural immunolocalization of noncollagenous (osteopontin and osteocalcin) and plasma (albumin and α2HS-glycoprotein) proteins in rat bone. J. Bone Min. Res. 8, 485–496. doi:10.1002/JBMR.5650080413

CrossRef Full Text | Google Scholar

Molnar, Z. (1959). Development of the parietal bone of young mice. J. Ultrastruct. Res. 3, 39–45. doi:10.1016/s0022-5320(59)80012-5

PubMed Abstract | CrossRef Full Text | Google Scholar

Moochhala, S. H., Sayer, J. A., Carr, G., and Simmons, N. L. (2008). Renal calcium stones: Insights from the control of bone mineralization. Exp. Physiol. 93, 43–49. doi:10.1113/EXPPHYSIOL.2007.040790

PubMed Abstract | CrossRef Full Text | Google Scholar

Mori, K., Emoto, M., and Inaba, M. (2012). Fetuin-A and the cardiovascular system. Adv. Clin. Chem. 56, 175–195. doi:10.1016/B978-0-12-394317-0.00010-8

PubMed Abstract | CrossRef Full Text | Google Scholar

Neuman, W. F., Firschein, H., Chen, P. S., Mulryan, B. J., and DiStefano, V. (1956). On the mechanism of action of parathormone. J. Am. Chem. Soc. 78, 3863–3864. doi:10.1021/ja01596a089

CrossRef Full Text | Google Scholar

Niu, L. N., Jee, S. E., Jiao, K., Tonggu, L., Li, M., Wang, L., et al. (2017). Collagen intrafibrillar mineralization as a result of the balance between osmotic equilibrium and electroneutrality. Nat. Mat. 16, 370–378. doi:10.1038/NMAT4789

CrossRef Full Text | Google Scholar

Nudelman, F., Pieterse, K., George, A., Bomans, P. H. H., Friedrich, H., Brylka, L. J., et al. (2010). The role of collagen in bone apatite formation in the presence of hydroxyapatite nucleation inhibitors. Nat. Mat. 9, 1004–1009. doi:10.1038/NMAT2875

CrossRef Full Text | Google Scholar

Olszta, M. J., Cheng, X., Jee, S. S., Kumar, R., Kim, Y. Y., Kaufman, M. J., et al. (2007). Bone structure and formation: A new perspective. Mat. Sci. Eng. R. Rep. 58, 77–116. doi:10.1016/J.MSER.2007.05.001

CrossRef Full Text | Google Scholar

Parvizi, J., and Kim, G. K. (2010). Collagen. High. Yield Orthop. 107–109. doi:10.1016/B978-1-4160-0236-9.00064-X

CrossRef Full Text | Google Scholar

Pompe, W., Worch, H., Habraken, W. J. E. M., Simon, P., Kniep, R., Ehrlich, H., et al. (2015). Octacalcium phosphate – A metastable mineral phase controls the evolution of scaffold forming proteins. J. Mat. Chem. B 3, 5318–5329. doi:10.1039/C5TB00673B

CrossRef Full Text | Google Scholar

Posner, A. S. (1969). Crystal chemistry of bone mineral. Physiol. Rev. 49, 760–792. doi:10.1152/PHYSREV.1969.49.4.760

PubMed Abstract | CrossRef Full Text | Google Scholar

Potts, J. T., Kronenberg, H. M., and Rosenblatt, M. (1982). Parathyroid hormone: Chemistry, biosynthesis, and mode of action. Adv. Protein Chem. 35, 323–396. doi:10.1016/S0065-3233(08)60471-4

PubMed Abstract | CrossRef Full Text | Google Scholar

Quan, B. D., and Sone, E. D. (2013). Cryo-TEM analysis of collagen fibrillar structure. Methods Enzymol. 532, 189–205. doi:10.1016/B978-0-12-416617-2.00009-6

PubMed Abstract | CrossRef Full Text | Google Scholar

Rasmussen, H. (1961). Parathyroid hormone: Nature and mechanism of action. Am. J. Med. 30, 112–128. doi:10.1016/0002-9343(61)90068-7

PubMed Abstract | CrossRef Full Text | Google Scholar

Rho, J. Y., Kuhn-Spearing, L., and Zioupos, P. (1998). Mechanical properties and the hierarchical structure of bone. Med. Eng. Phys. 20, 92–102. doi:10.1016/S1350-4533(98)00007-1

PubMed Abstract | CrossRef Full Text | Google Scholar

Robinson, R. A., and Watson, M. L. (1952). Collagen-crystal relationships in bone as seen in the electron microscope. Anat. Rec. 114, 383–409. doi:10.1002/AR.1091140302

PubMed Abstract | CrossRef Full Text | Google Scholar

Robinson, R. A., and Watson, M. L. (1955). Crystalcollagen relationships in bone as observed in the electron microscope. III. Crystal and collagen morphology as a function of age. Ann. N. Y. Acad. Sci. 60, 596–630. doi:10.1111/J.1749-6632.1955.TB40054.X

PubMed Abstract | CrossRef Full Text | Google Scholar

Rossi, C. S., Carafoli, E., and Lehninger, A. L. (1967). Active ion transport by mitochondria. Symp. Biophys. Physiol. Biol. Transp. 63, 90–94. doi:10.1007/978-3-7091-5577-6_20

CrossRef Full Text | Google Scholar

Rossi, C. S., Bielawski, J., Carafoli, E., and Lehninger, A. L. (1966). The relationship of the Ca++ efflux rate to the “super-stoichiometry” of respiration-linked Ca++ accumulation by mitochondria. Biochem. Biophys. Res. Commun. 22, 206–210. doi:10.1016/0006-291X(66)90433-5

PubMed Abstract | CrossRef Full Text | Google Scholar

Sakamoto, K., Yamaguchi, S., Kaneno, M., Fujihara, I., Satoh, K., and Tsunawaki, Y. (2008). Synthesis and thermal decomposition of layered calcium phosphates including carboxylate ions. Thin Solid Films 517, 1354–1357. doi:10.1016/J.TSF.2008.09.050

CrossRef Full Text | Google Scholar

Schinke, T., Amendt, C., Trindl, A., Pöschke, O., Müller-Esterl, W., and Jahnen-Dechent, W. (1996). The serum protein α2-HS glycoprotein/fetuin inhibits apatite formation in vitro and in mineralizing calvaria cells: A possible role in mineralization and calcium homeostasis. J. Biol. Chem. 271, 20789–20796. doi:10.1074/JBC.271.34.20789

PubMed Abstract | CrossRef Full Text | Google Scholar

Seyer, J. M., and Glimcher, M. J. (1977). Isolation, characterization and partial amino acid sequence of a phosphorylated polypeptide (E4) from bovine embryonic dental enamel. Biochim. Biophys. Acta - Protein Struct. 493, 441–451. doi:10.1016/0005-2795(77)90200-8

CrossRef Full Text | Google Scholar

Shao, C., Zhao, R., Jiang, S., Yao, S., Wu, Z., Jin, B., et al. (2018). Citrate improves collagen mineralization via interface wetting: A physicochemical understanding of biomineralization control. Adv. Mat. 30, 1704876. doi:10.1002/ADMA.201704876

CrossRef Full Text | Google Scholar

Shen, L., Bu, H., Zhang, Y., Tang, P., and Li, G. (2021). Molecular weight and concentration of poly (acrylic acid) dual-responsive homogeneous and intrafibrillar collagen mineralization using an in situ co-organization strategy. Polym. Compos. 42, 4448–4460. doi:10.1002/PC.26161

CrossRef Full Text | Google Scholar

Silver, F. H., and Landis, W. J. (2011). Deposition of apatite in mineralizing vertebrate extracellular matrices: A model of possible nucleation sites on type I collagen. Connect. Tissue Res. 52, 242–254. doi:10.3109/03008207.2010.551567

PubMed Abstract | CrossRef Full Text | Google Scholar

Simon, P., Grüner, D., Worch, H., Pompe, W., Lichte, H., El Khassawna, T., et al. (2018). First evidence of octacalcium phosphate@osteocalcin nanocomplex as skeletal bone component directing collagen triple–helix nanofibril mineralization. Sci. Rep. 81 (8), 13696. doi:10.1038/s41598-018-31983-5

CrossRef Full Text | Google Scholar

Solomons, C. C., and Irving, J. T. (1958). Studies in calcification the reaction of some hard- and soft-tissue collagens with 1-fluoro-2:4-dinitrobenzene. Biochem. J. 68, 499–503. doi:10.1042/BJ0680499

PubMed Abstract | CrossRef Full Text | Google Scholar

Spector, A. R., and Glimcher, M. J. (1972). The extraction and characterization of soluble anionic phosphoproteins from bone. Biochim. Biophys. Acta - Protein Struct. 263, 593–603. doi:10.1016/0005-2795(72)90040-2

CrossRef Full Text | Google Scholar

Sugiura, Y., Onuma, K., Nagao, M., and Yamazaki, A. (2015). The effects of immobilized carboxylic-functional groups on the dynamics of phase transformation from amorphous to octacalcium phosphate. Am. Mineral. 100, 1624–1632. doi:10.2138/AM-2015-5179

CrossRef Full Text | Google Scholar

Tavafoghi, M., and Cerruti, M. (2016). The role of amino acids in hydroxyapatite mineralization. J. R. Soc. Interface 13, 20160462. doi:10.1098/RSIF.2016.0462

PubMed Abstract | CrossRef Full Text | Google Scholar

Termine, J. D., and Posner, A. S. (1966). Infrared analysis of rat bone: Age dependency of amorphous and crystalline mineral fractions. Science 153, 1523–1525. doi:10.1126/SCIENCE.153.3743.1523

PubMed Abstract | CrossRef Full Text | Google Scholar

Tsuji, T., Onuma, K., Yamamoto, A., Iijima, M., and Shiba, K. (2008). Direct transformation from amorphous to crystalline calcium phosphate facilitated by motif-programmed artificial proteins. Proc. Natl. Acad. Sci. U. S. A. 105, 16866–16870. doi:10.1073/PNAS.0804277105/SUPPL_FILE/0804277105SI

PubMed Abstract | CrossRef Full Text | Google Scholar

Tzaphlidou, M. (2008). Bone architecture: Collagen structure and calcium/phosphorus maps. J. Biol. Phys. 34, 39–49. doi:10.1007/S10867-008-9115-Y

PubMed Abstract | CrossRef Full Text | Google Scholar

Vasington, F. D., and Murphy, J. V. (1962). Ca++ uptake by rat kidney mitochondria and its dependence on respiration and phosphorylation. J. Biol. Chem. 237, 2670–2677. doi:10.1016/S0021-9258(19)73805-8

PubMed Abstract | CrossRef Full Text | Google Scholar

Veiga, A., Castro, F., Rocha, F., and Oliveira, A. L. (2020). Recent advances in silk sericin/calcium phosphate biomaterials. Front. Mat. 7, 24. doi:10.3389/fmats.2020.00024

CrossRef Full Text | Google Scholar

Wang, L., and Nancollas, G. H. (2008). Calcium orthophosphates: Crystallization and dissolution. Chem. Rev. 108, 4628–4669. doi:10.1021/CR0782574

PubMed Abstract | CrossRef Full Text | Google Scholar

Wang, S., Yang, Y., Wang, R., Kong, X., and Wang, X. (2020). Mineralization of calcium phosphate controlled by biomimetic self-assembled peptide monolayers via surface electrostatic potentials. Bioact. Mat. 5, 387–397. doi:10.1016/J.BIOACTMAT.2020.03.003

CrossRef Full Text | Google Scholar

Weidmann, S. M. (1963). Calcification of skeletal tissues. Int. Rev. Connect. Tissue Res. 1, 339–377. doi:10.1016/B978-1-4831-6755-8.50013-9

PubMed Abstract | CrossRef Full Text | Google Scholar

Weiner, S., and Traub, W. (1986). Organization of hydroxyapatite crystals within collagen fibrils. FEBS Lett. 206, 262–266. doi:10.1016/0014-5793(86)80993-0

PubMed Abstract | CrossRef Full Text | Google Scholar

Xie, B., and Nancollas, G. H. (2010). How to control the size and morphology of apatite nanocrystals in bone. Proc. Natl. Acad. Sci. U. S. A. 107, 22369–22370. doi:10.1073/PNAS.1017493108

PubMed Abstract | CrossRef Full Text | Google Scholar

Xu, Y. F., Nudelman, F., Eren, E. D., Wirix, M. J. M., Cantaert, B., Nijhuis, W. H., et al. (2020). Intermolecular channels direct crystal orientation in mineralized collagen. Nat. Commun. 111, 5068. doi:10.1038/s41467-020-18846-2

CrossRef Full Text | Google Scholar

Yokoi, T., Shimabukuro, M., and Kawashita, M. (2022). Octacalcium phosphate with incorporated carboxylate ions: A review. Sci. Technol. Adv. Mat. 23, 434–445. doi:10.1080/14686996.2022.2094728

CrossRef Full Text | Google Scholar

Zhang, X., Wu, L., Feng, G., and Lei, S. (2022). Mineralization of calcium phosphate on two-dimensional polymer films with controllable density of carboxyl groups. J. Mat. Chem. B 10, 3793–3797. doi:10.1039/D2TB00195K

CrossRef Full Text | Google Scholar

Keywords: carboxylate organic compound, calcium phosphate, bone, interfibrillar collagen, mineralization

Citation: Indurkar A, Choudhary R, Rubenis K and Locs J (2023) Role of carboxylic organic molecules in interfibrillar collagen mineralization. Front. Bioeng. Biotechnol. 11:1150037. doi: 10.3389/fbioe.2023.1150037

Received: 23 January 2023; Accepted: 20 March 2023;
Published: 05 April 2023.

Edited by:

Jinhui Tao, Pacific Northwest National Laboratory (DOE), United States

Reviewed by:

Changyu Shao, Zhejiang University, China
Arun Prabhu Rameshbabu, Harvard Medical School, United States
Taifeng Wang, Intel, United States

Copyright © 2023 Indurkar, Choudhary, Rubenis and Locs. This is an open-access article distributed under the terms of the Creative Commons Attribution License (CC BY). The use, distribution or reproduction in other forums is permitted, provided the original author(s) and the copyright owner(s) are credited and that the original publication in this journal is cited, in accordance with accepted academic practice. No use, distribution or reproduction is permitted which does not comply with these terms.

*Correspondence: Janis Locs, janis.locs@rtu.lv

Disclaimer: All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article or claim that may be made by its manufacturer is not guaranteed or endorsed by the publisher.