MINI REVIEW article

Front. Bioeng. Biotechnol., 25 September 2020
Sec. Biomaterials

Polymeric Guide Conduits for Peripheral Nerve Tissue Engineering

  • 1College of Fisheries and Life Science, Shanghai Ocean University, Shanghai, China
  • 2Department of Orthopedics, Shanghai Jiao Tong University Affiliated Sixth People’s Hospital, Shanghai, China
  • 3Shanghai Sixth People’s Hospital East Affiliated to Shanghai University of Medicine & Health Sciences, Shanghai, China

Peripheral nerve injuries (PNIs) are usually caused by trauma, immune diseases, and genetic factors. Peripheral nerve injury (PNI) may lead to limb numbness, muscle atrophy, and loss of neurological function. Although an abundance of theories have been proposed, very few treatments can effectively lead to complete recovery of neurological function. Autologous nerve transplantation is currently the gold standard. Nevertheless, only 50% of all patients were successfully cured using this method. In addition, it causes inevitable damage to the donor site, and available donor sites in humans are very limited. Tissue engineering has become a research hotspot aimed at achieving a better therapeutic effect from peripheral nerve regeneration. Nerve guide conduits (NGCs) show great potential in the treatment of PNI. An increasing number of scaffold materials, including natural and synthetic polymers, have been applied to fabricate NGCs for peripheral nerve regeneration. This review focuses on recent nerve guide conduit (NGC) composite scaffold materials that are applied for nerve tissue engineering. Furthermore, the development tendency of NGCs and future areas of interest are comprehensively discussed.

Introduction

Peripheral nerve injuries (PNIs) are common clinical cases. These are usually caused by trauma, immune diseases (e.g., lupus erythematosus), and genetic factors (e.g., mutation in LAMA2). Damage to the peripheral nerves may cause nerve defects, breakage of internal blood vessels, and interruption of the interaction between neurons and tissues (Domínguez et al., 2013). Peripheral nerve defects, which are common in PNIs, can lead to limb numbness and muscle atrophy, and to the loss of neurological function (Lim et al., 2017).

Neurorrhaphy is usually applied to suture the nerve gap of the peripheral nerve injury (PNI) when the gap of the injured peripheral nerve is less than 5 mm (Li et al., 2013). When the nerve gap is greater than 5 mm, the direct end-to-end suture is not suitable for nerve repair (Li et al., 2013). Autologous nerve transplantation as the gold standard has achieved the best effect on the treatment of PNI; however, only 50% of cases have been successful (Manoukian et al., 2019a). In addition, autologous nerve transplantation may cause inevitable damage to the donor site and neuroma formation (Oprych et al., 2016). Furthermore, available donor sites in humans are very limited (Bozkurt et al., 2015). To achieve a better therapeutic effect on peripheral nerve regeneration, tissue-engineered grafting has been increasingly applied for the treatment of PNI as a potential treatment method (Huang et al., 2017). Tissue engineering, which is dedicated to artificial tissues and organs, arises at the historic moment. With more than 30 years of development, tissue engineering has played an extremely significant role in tissue or organ repair (Almansoori et al., 2020). Numerous studies (Oprych et al., 2016; Lackington et al., 2017; Vijayavenkataraman, 2020) have demonstrated that nerve guide conduits (NGCs) (Figure 1), as a kind of tissue-engineered implant, have enormous potential to bridge injury sites and provide a physical template for peripheral nerve regeneration. Various scaffold materials have been applied to prepare NGCs that mimic the natural microenvironment of peripheral nerves to guide neural outgrowth and extension (Song et al., 2018; Zhu et al., 2020).

FIGURE 1
www.frontiersin.org

Figure 1. Schematic illustration of PNI and NGCs (Vijayavenkataraman, 2020). (A) Peripheral nerve structure, (B) different types of PNI: Neurapraxia, Axonotmesis, and Neurotmesis; (C) different designs of NGCs: hollow, multi-channel, porous, grooved NGC, and NGC with fillers, and (D) surgical procedure of NGC grafting.

Polymeric scaffold materials, as cell and active molecular carriers, are particularly important in tissue engineering (Sanjairaj et al., 2017). Polymeric scaffold materials mainly include natural and synthetic polymers (Titorencu et al., 2016). NGCs made of natural polymers usually have excellent biocompatibility and can promote the adhesion and growth of cells. Synthetic polymers have good mechanical properties for fabrication into three-dimensional (3D) scaffolds (Sanjairaj, 2016). A suitable scaffold material should be beneficial for cell growth, axonal regeneration, and for rebalancing of the microenvironment with its superior mechanical properties. Additionally, it should play a role in inducing cell-specific differentiation. Thus, the biocompatibility, mechanical properties, and biodegradability of scaffold materials are primary indicators for judging the quality of different scaffold materials (Sanjairaj, 2016; Zhang et al., 2018; Zhang S. et al., 2019). Researchers have mixed natural polymers with synthetic polymers to overcome the shortcomings of pure polymer scaffold materials. Composite NGCs are new scaffolds that are composed of two or more different kinds of biomaterials according to specific proportions and methods (Vijayavenkataraman, 2020).

This review discusses recent polymeric scaffold materials (Table 1) that are applied in the fabrication of NGCs and their achievements in peripheral nerve regeneration. Moreover, we infer to prospects of these biomaterials and future development tendencies of NGCs.

TABLE 1
www.frontiersin.org

Table 1. Recent polymer scaffolds for peripheral nerve tissue engineering.

Natural Polymer-Based Conduits

Natural polymers have a wide application in tissue engineering because of their superior biodegradability and biocompatibility (Jiang et al., 2019). Collagen is a common structure that is highly concentrated in bone, skin, tendon, and vascular structures, and collagen type I is highly conserved (Friess, 1998) in different species. Collagen is an ideal polymer that may be used to fabricate NGCs because of its low immune response and high absorbability in the body (Liu et al., 2019), and has been commonly utilized as a carrier for drug delivery (Manoukian et al., 2019b; Qiu et al., 2020). Therefore, collagen is often used to fabricate NGCs for peripheral nerve regeneration. Bozkurt et al. (2008) used the freeze-drying method to prepare highly oriented 3D porcine collagen scaffolds and found excellent regeneration of Schwann cells (SCs) in vitro. Functional NGCs that support nerve cells and stem cells and NGCs loaded with drugs and nerve growth factors (NGF) are areas of interest for the future (Dan et al., 2018; Zhang et al., 2020). Collagen type-I matrix scaffolds loaded with SCs were fabricated by Georgiou et al. (2013), and the results showed that these scaffolds could promote the axonal regeneration in 5 mm defect rat sciatic nerve injury models. Foidl et al. (2018) prepared collagen scaffolds using the 4S-Starpolyethyleneglycole (4S-StarPEG) method as a cross-linker and found that the collagen loaded with NGF could release NGF slowly during the process of time. In conclusion, collagen, which may be loaded with SCs and NGF, shows great potential for peripheral nerve regeneration. Furthermore, the 3D printed hydrogel scaffolds showed excellent mechanical properties. Frayssinet et al. (2020) prepared collagen/Tyramine HA derivative (HA-Tyr) hydrogel scaffolds and found that hydrogels could maintain the vitality of cells.

The reactivity of the amino group in chitosan is stronger than that in chitin, which results in the polysaccharide having an excellent biological function and renders it chemically modifiable. Therefore, chitosan is considered to be a functional biomaterial with greater application potential than cellulose (Li et al., 2018). Owing to its ability to facilitate the attachment and proliferation of Schwann cells, chitosan has great potential for peripheral nerve regeneration (Wach et al., 2020). Owing to the lack of cues for inducing cell migration and differentiation on the chitosan scaffold surface, pure chitosan scaffolds fail to meet expectations (Shrestha et al., 2018). Si et al. (2019) prepared chitosan/collagen composite NGCs through lyophilization and a phase separation composite method. Their study demonstrated that the addition of chitosan resulted in an increase in the mechanical properties of the scaffolds.

Alginate (Alg) is a common natural polymer, which is an anionic and hydrophilic polysaccharide that has adjustable biodegradability and drug release properties (Wu et al., 2010; Zuo et al., 2015). Alg can crosslink with divalent metal ions, especially Ca2+, to form hydrogels in a solution (Roca et al., 2020). Many studies have demonstrated that natural polymer-based hydrogels can promote the growth of nerve cells and axonal extension for peripheral nerve regeneration (Wu et al., 2019). Hydrogels can provide the nerve with a suitable 3D microenvironment owing to the similar characteristics of nerve tissue in vivo. The hydrogel expands to a soft biomaterial by absorbing fluid, which results in the soft and elastic hydrogel minimizing irritability to the neighboring tissues for nerve regeneration (Samadian et al., 2020). The hydrogel could be fabricated as scaffolds of excellent mechanical properties for peripheral nerve regeneration via the 3D-printing method.

Silk fibroin (SF) is a non-toxic and non-immunogenic structural protein (Tang et al., 2012; Kundu et al., 2013). SF has superior mechanical properties compared to other natural polymers (Chien-Yu et al., 2016). Jiao et al. (2017) fabricated SF/Alg composite scaffolds loaded with NGF, which significantly improved the motor function of rats, via a freeze-drying method. Gan et al. (2016) developed another nerve guide conduit (NGC) made of cellulose and soy protein isolate (SPI) through a chemical precipitation method that successfully bridged and repaired the nerve defect in 10 mm defect rat sciatic nerve injury models. The cellulose/SPI scaffolds showed a great effect on peripheral nerve regeneration.

Synthetic Polymer-Based Conduits

Synthetic polymers are widely used to fabricate NGCs for peripheral nerve regeneration because they have better mechanical properties to be easily fabricated into 3D structures compared to natural polymers. The recovery period of PNI is usually approximately 3–6 months (Rhatomy et al., 2019); thus, a second surgery could be avoided using biodegradable synthetic polymers. Poly (ε-caprolactone) (PCL), an FDA-approved material, is one of the most common synthetic polymers used for the fabrication of NGCs. PCL has excellent processability and compatibility (Mobini et al., 2017). The NGCs made of PCL have excellent mechanical properties to offer topographical cues to axons for peripheral nerve regeneration; however, poor biodegradability is a major shortcoming (Rhatomy et al., 2019) for the wide application of PCL. Sun et al. (2006) transplanted PCL (Mw ¼ 66,000) scaffolds into rats and found that scaffolds remained structurally intact for 24 months. Poly(acrylic acid) (PAA), an FDA-approved anionic polymer, has been widely used for tissue engineering (Jaiswal and Koul, 2013; Meng et al., 2015). The cortical gel layer has the function of cation-exchange, which could affect nerve excitation and conduction (Noor Fitrah et al., 2019). However, PAA has poor mechanical properties and is difficult to fabricate into scaffolds (Qiao et al., 2018).

Although poly(L-lactic acid) (PLLA) has a higher degradation rate than PCL, the NGCs fabricated using PCL are harmful to the body because of their high crystallinity (Frydrych et al., 2015). Poly(lactic-co-glycolic acid) (PLGA) is a synthetic polymer that combines PLLA and polyglycolic acid (PGA), and the degradation of PLGA can be increased by decreasing the ratio of PLLA (Gentile et al., 2014). PLGA (PAA: PLLA 50:50) scaffolds have been widely used for fabricating NGCs, and these NGCs have been demonstrated to promote axonal regeneration (Lackington et al., 2019). The degradation byproducts of PLGA are lactic and glycolic acid that have high acidity, and metabolization is difficult in vivo (Kühne et al., 2018). However, PLGA, as a widely studied material, has been used in many commercial conduits without causing metabolic problems due to the degradation byproducts.

Numerous experiments have demonstrated that the proliferation and growth of nerve cells and axonal extension could be improved through appropriate electrical stimulation (ES) (Li et al., 2008). Therefore, the electrical conductivity of scaffold materials is equally important. Conducting polymers () as biocompatible biomaterials possess cell adhesion, excellent mechanical properties, and adjustable surface hydrophilicity (Jing et al., 2018; Sadeghi et al., 2018). CPs can directly condition the state and migration of cells, transmit electrical signals, and provoke ES (Wu et al., 2016). Common CPs include polypyrrole (PPy), polythiophene (PT), and poly(p-phenylene-vinylene) (PPV). PPy is one of the most important CPs that can be fabricated into NGCs for peripheral nerve regeneration. Schmidt et al. (1997) prepared PPy scaffolds that can promote the extension of neurites and the differentiation of nerve cells. Although PPy possesses semiconductivity and readily modifiable surfaces, the short-time conductivity of PPy did not adequately support in vivo ES, and poor biodegradability would inevitably cause a second surgical procedure (Marakova et al., 2019).

Piezoelectric polymers are a type of special material that can produce variable electrical charges on surface under mechanical distortion without energy sources or electrodes (Ribeiro et al., 2014). Therefore, mechanical properties can be transformed into electrical properties without external electrical devices, electrodes, etc. Yang et al. (2005) evaluated a large number of polymers and ceramics to provide peripheral nerve regeneration with piezoelectric nerve conduits, and polyvinylidene fluoride (PVDF) was found as a promising polymer. PVDF is a strong piezoelectric material; thus, it has often been reported to fabricate NGCs in service documents. PVDF possesses superior properties, including great chemical resistance, piezoelectric behavior, and thermal stability (Cui et al., 2013; Tsonos et al., 2015). PVDF has been demonstrated to improve axonal regeneration for central nerve injuries and PNI (Lee et al., 2016). Guo et al. (2012) reported that PVDF nanoscaffolds promoted the activity and function of fibroblasts. Lins et al. (2016) found that PVDF could be used for NGCs to simulate the native extracellular matrix and found the growth and differentiation of monkey neural stem cells into neuronal and glial cells. Lee et al. (2011) prepared electrospun fibrous scaffolds using PVDF–trifluoroethylene (PVDF–TrFE). The results showed that the dorsal root ganglion neurons attached to scaffolds and the neurites extended to them in repeated experiments. Non-solvent induced phase separation (NIPS) and thermally induced phase separation (TIPS) are both efficient and controllable ways to fabricate NGCs with an interconnected porous network for peripheral nerve regeneration (Yousefi et al., 2014). Theoretically, the TIPS method removes thermal energy from the dope solution, whereas the NIPS method promotes solvent and non-solvent interactions (Jung et al., 2016). Abzan et al. (2018) fabricated porous PVDF scaffolds using the N-TIPS method, and the PVDF scaffolds with a higher amount of the β phase promoted better the cell attachment and proliferation of PC12 cells. In conclusion, PVDF is a suitable scaffold material for peripheral nerve regeneration. However, a second surgical procedure may be inevitable because of the poor biodegradation of PVDF (Abzan et al., 2019).

Composite Polymer Scaffolds

To overcome the above shortcomings, researchers have mixed natural polymers with synthetic polymers and found that blends possess both good mechanical properties and cellular affinity. Researchers blended collagen and PCL to fabricate compound scaffolds, SCs were used for in vitro studies, and 8 mm long gap sciatic nerve injuries were used for in vivo studies. These studies demonstrated that collagen/PCL scaffolds had a better effect than pure PCL scaffolds on nerve regeneration (Yu et al., 2011). Electrospun matrices, which interact with cells, are ideal for cell adhesion and proliferation (Cui et al., 2019; Zhang J. et al., 2019). Altun et al. (2019) prepared BC/PCL blend nanofibrous scaffolds via the electrospinning method and the aligned BC/PCL nanoscaffolds significantly improved neurite outgrowth.

To enhance the electrical conductivity of NGCs, many electrically conductive carbon-based nanostructures have been mixed into varieties of scaffolds. Graphene (Gr) and its derivatives possess superior mechanical properties and electrical conductivity and have been demonstrated to be the most suitable biomaterials for use in peripheral nerve regeneration (Hua et al., 2009; Issa et al., 2016). Kurapati et al. (2018) found that Gr and its derivatives could be degraded into smaller nanosheets by activated neutrophils; hence, demonstrating their excellent biodegradability. Therefore, Gr could be combined with other polymers to enhance their mechanical and electrical properties. Gr and reduced graphene oxide (rGO) are electrically conductive materials. Wang et al. (2018) coated rGO on the Antheraea pernyi silk fibroin (ApF)/[Poly(L-lactic acid-co-caprolactone)] (PLCL) nanoscaffolds fabricated through the in situ redox reaction of rGO. The rGO/ApF/PLCL scaffolds remarkably promoted the migration and proliferation of SCs and induced the differentiation of PC12 cells.

Although graphene oxide (GO) is substantially a non-conductive material, it possesses higher compatibility with polymeric biomaterials and is easier to handle with superior dispersion in solutions than Gr. (Ning et al., 2011; Nezakati et al., 2014). Qian et al. (2018) invented a GO/PCL nanoscaffold using the integration-molding method and evaluated the regenerative effects of this scaffold in a 15 mm defect rat sciatic nerve injury model for the first time. The results showed prominent angiogenesis and satisfactory axon and myelin repair. The carboxyl groups of carboxylic graphene oxide (cGO) GO can be easily handled and have super dispersion in solutions when compared with graphene, and carbon nanotubes possess better surface hydrophilicity than GO; hence, Chen et al. (2019) fabricated cGO/PPy/PLLA composite scaffolds through the electrochemical deposition method. However, the application for peripheral nerve regeneration is limited owing to the agglomeration and weak compatibility of carbon nanotubes (Chen et al., 2019).

PVDF as a piezoelectric material has been widely used in tissue engineering, and it has high piezoelectric properties and great biocompatibility (Wang et al., 2017; Surmenev et al., 2019). The self-generating ability of PVDF provides researchers with new ideas for peripheral nerve regeneration. To achieve scaffolds with better biocompatibility, biodegradation, and mechanical properties, researchers designed a composite NGC that blended PCL with PVDF. Cheng et al. (2020) used the cast/annealing-solvent displacement method to fabricate porous PVDF/PCL composite scaffolds, and these NGCs successfully bridged the 15 mm defect in rat sciatic nerve injury. Abzan et al. (2019) fabricated PVDF/GO composite scaffolds for peripheral nerve regeneration through the NIPS method, and the incorporation of 5 wt% GO remarkably enhanced the piezoelectricity of the scaffolds. To improve the properties of NGCs, researchers have mixed many carbon-based nanostructures into PVDF membranes to fabricate composite scaffolds. Pei et al. (2015) prepared PVDF/RGO nanocomposite scaffolds using the in situ thermal reduction technology and found that RGO enhanced the formation of the β-phase and hydrophilicity of PVDF scaffolds.

Discussion

Tissue-engineered grafting is a potential treatment method has been increasingly applied to the treatment of PNI to achieve a better therapeutic effect on peripheral nerve regeneration. Several scaffold materials have been used to fabricate NGCs for peripheral nerve regeneration. Natural polymers possess superior biocompatibility and biodegradability; however, their poor mechanical properties make them difficult to fabricate into 3D scaffolds. Synthetic polymers with superior mechanical properties have been widely used to fabricate 3D NGCs for peripheral nerve regeneration. Nevertheless, their poor biocompatibility limits the application of pure synthetic scaffolds for peripheral nerve regeneration. Composite scaffold materials have enormous potential to enhance the properties of traditional biomaterials. Natural-synthetic composite scaffolds possess both great mechanical properties and cellular affinity, and a large number of studies have shown that composite scaffolds have great development prospects in tissue engineering. Numerous studies have demonstrated that NGCs have enormous potential for peripheral nerve regeneration, although the achievement of NGCs has not yet surpassed that of autologous nerve transplantation. This is the reason why autologous nerve transplantation continues to be the gold standard of PNI treatment.

Although there have been numerous studies on the mechanisms of PNI and rat sciatic nerve injury models, there is no alternative treatment method for peripheral nerve long segment defects. Thus, it is urgent to develop an ideal NGC approved by the FDA that possesses excellent biocompatibility, biodegradability, mechanical properties, and electrical conductivity to be applied to the human body. As mentioned above, natural polymers promote axonal regeneration owing to the delivery of nerve cells, NGF, and drugs. Synthetic polymers have provided NGCs with superior mechanical properties or electrical conductivity. Thus, polymeric materials have great potential for peripheral nerve regeneration. The piezoelectric polymer is a type of special material that could produce variable electrical charges on the surface under mechanical distortion without energy sources or electrodes. However, the poor biodegradability of piezoelectric polymers require a second surgical procedure. Additionally, the development of piezoelectric polymers with improved biodegradability and biocompatibility is a current hotspot for peripheral nerve regeneration materials research. 3D printing is a fabrication technology that precisely dispenses cell-laden biomaterials for the construction of complex 3D functional tissues or artificial organs. DLP printing, as a type of 3D printing, makes the application of pure GelMA NGCs possible, which supports the migration and proliferation of PC12 cells. This may mean that not only could DLP printing be applied for peripheral nerve regeneration, but additional 3D printing methods could also increase the performance of pure polymer scaffolds. The exploitation of more efficient printing methods compared to 3D-based printing methods has become a recent point of interest.

Functional scaffold materials that could support nerve cells and stem cells, NGCs loaded with drugs and nerve growth factors, and 4D printing methods are areas of interest for the future. Therefore, functionalized NGCs comprise the most anticipated breakthrough materials for the treatment of PNI.

Author Contributions

YQ and HJ conceptualized the study. HJ, YQ, CF, and YO reviewed the literature and designed the figures and tables. HJ drafted the manuscript. YQ and YO revised the manuscript. All authors contributed to the article and approved the submitted version.

Funding

This study was sponsored by the Shanghai Sailing Program (No. 20YF1436000), the Projects of the National Natural Science Foundation of China (Grant Nos. 81830076 and 81672146), and the Interdisciplinary Program of Shanghai Jiao Tong University (Grant Nos. YG2019QNA24, YG2017MS22, YG2017MS64, and YG2017QN56).

Conflict of Interest

The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.

Acknowledgments

We appreciate the support from the Youth Science and Technology Innovation Studio of Shanghai Jiao Tong University School of Medicine.

References

Abzan, N., Kharaziha, M., and Labbaf, S. (2019). Development of three-dimensional piezoelectric polyvinylidene fluoride-graphene oxide scaffold by non-solvent induced phase separation method for nerve tissue engineering. Mater. Design 167:107636. doi: 10.1016/j.matdes.2019.107636

CrossRef Full Text | Google Scholar

Abzan, N., Kharaziha, M., Labbaf, S., and Saeidi, N. (2018). Modulation of the mechanical, physical and chemical properties of polyvinylidene fluoride scaffold via non-solvent induced phase separation process for nerve tissue engineering applications. Eur. Polym. J. 104, 115–127. doi: 10.1016/j.eurpolymj.2018.05.004

CrossRef Full Text | Google Scholar

Almansoori, A., Hwang, C., Lee, S.-H., Kim, B., Kim, H. J., and Lee, J. (2020). Tantalum – poly (L-lactic acid) nerve conduit for peripheral nerve regeneration. Neurosci. Lett. 731:135049. doi: 10.1016/j.neulet.2020.135049

PubMed Abstract | CrossRef Full Text | Google Scholar

Altun, E., Aydogdu, M., Ozmen Togay, S., Sengil, A., Ekren, N., Erginer Hasköylü, M., et al. (2019). Bioinspired scaffold induced regeneration of neural tissue. Eur. Polym. J. 114, 98–108. doi: 10.1016/j.eurpolymj.2019.02.008

CrossRef Full Text | Google Scholar

Bozkurt, A., Boecker, A., Tank, J., Altinova, H., Deumens, R., Dabhi, C., et al. (2015). Efficient bridging of 20 mm rat sciatic nerve lesions with a longitudinally micro-structured collagen scaffold. Biomaterials 75, 112–122. doi: 10.1016/j.biomaterials.2015.10.009

PubMed Abstract | CrossRef Full Text | Google Scholar

Bozkurt, A., Brook, G., Moellers, S., Lassner, F., Sellhaus, B., Weis, J., et al. (2008). In vitro assessment of axonal growth using dorsal root ganglia explants in a novel three-dimensional collagen matrix. Tissue Eng. 13, 2971–2979. doi: 10.1089/ten.2007.0116

PubMed Abstract | CrossRef Full Text | Google Scholar

Chen, X., Liu, C., Huang, Z., Pu, X., Shang, L., Yin, G., et al. (2019). Preparation of carboxylic graphene oxide−composited polypyrrole conduits and their effect on sciatic nerve repair under electrical stimulation. J. Biomed. Mater. Res. A 107, 2784–2795. doi: 10.1002/jbm.a.36781

PubMed Abstract | CrossRef Full Text | Google Scholar

Cheng, Y., Xu, Y., Qian, Y., Chen, X., Ouyang, Y., and Yuan, W.-E. (2020). 3D structured Self-Powered PVDF/PCL scaffolds for peripheral nerve regeneration. Nano Energy 69:104411. doi: 10.1016/j.nanoen.2019.104411

CrossRef Full Text | Google Scholar

Chien-Yu, S., Wang, Y., Wertheim, D., and Coombes, A. (2016). Production and in vitro evaluation of macroporous, cell-encapsulating alginate fibres for nerve repair. Mater. Sci. Eng. C 73, 653–664. doi: 10.1016/j.msec.2016.12.016

PubMed Abstract | CrossRef Full Text | Google Scholar

Cui, L., Zhang, J., Zou, J., Yang, X., Guo, H., Tian, H., et al. (2019). Electroactive composite scaffold with locally expressed osteoinductive factor for synergistic bone repair upon electrical stimulation. Biomaterials 230:119617. doi: 10.1016/j.biomaterials.2019.119617

PubMed Abstract | CrossRef Full Text | Google Scholar

Cui, Z., Drioli, E., and Lee, Y. M. (2013). Recent progress in fluoropolymers for membranes. Prog. Polym. Sci. 39, 164–198. doi: 10.1016/j.progpolymsci.2013.07.008

CrossRef Full Text | Google Scholar

Dan, W., Sun, J., Yang, Y., Wu, C., Chen, S., Guo, Z., et al. (2018). Cell alignment guided by nano/micro oriented collagen fibers and the synergistic vascularization for nervous cell functional expression. Mater. Today Chem. 8, 85–95. doi: 10.1016/j.mtchem.2018.03.001

CrossRef Full Text | Google Scholar

Domínguez, A., Álvarez, A., Hilario, E., Suarez-Merino, B., and Cerio, F. (2013). Central nervous system diseases and the role of the blood-brain barrier in their treatment. Neurosci. Discov. 1, 611–612. doi: 10.7243/2052-6946-1-3

CrossRef Full Text | Google Scholar

Foidl, B. M., Ucar, B., Schwarz, A., Rebelo, A. L., Pandit, A., and Humpel, C. (2018). Nerve growth factor released from collagen scaffolds protects axotomized cholinergic neurons of the basal nucleus of Meynert in organotypic brain slices. J. Neurosci. Methods 295, 77–86. doi: 10.1016/j.jneumeth.2017.12.003

PubMed Abstract | CrossRef Full Text | Google Scholar

Frayssinet, A., Petta, D., Illoul, C., Haye, B., Markitantova, A., Eglin, D., et al. (2020). Extracellular matrix-mimetic composite hydrogels of cross-linked hyaluronan and fibrillar collagen with tunable properties and ultrastructure. Carbohyd. Polym. 236:116042. doi: 10.1016/j.carbpol.2020.116042

PubMed Abstract | CrossRef Full Text | Google Scholar

Friess, W. (1998). Collagen – biomaterial for drug delivery1. Eur. J. Pharm. Biopharm. 45, 113–136. doi: 10.1016/S0939-6411(98)00017-4

CrossRef Full Text | Google Scholar

Frydrych, M., Roman, S., Macneil, S., and Chen, B. (2015). Biomimetic poly(glycerol sebacate)/poly(l-lactic acid) blend scaffolds for adipose tissue engineering. Acta Biomater. 18, 40–49. doi: 10.1016/j.actbio.2015.03.004

PubMed Abstract | CrossRef Full Text | Google Scholar

Gan, L., Zhao, L., Zhao, Y., Li, K., Tong, Z., Yi, L., et al. (2016). Cellulose/soy protein composite-based nerve guidance conduits with designed microstructure for peripheral nerve regeneration. J. Neural Eng. 13:056019. doi: 10.1088/1741-2560/13/5/056019

CrossRef Full Text | Google Scholar

Gentile, P., Chiono, V., Carmagnola, I., and Hatton, P. (2014). An overview of poly(lactic-co-glycolic) acid (PLGA)-based biomaterials for bone tissue engineering. Int. J. Mol. Sci. 15, 3640–3659. doi: 10.3390/ijms15033640

PubMed Abstract | CrossRef Full Text | Google Scholar

Georgiou, M., Bunting, S., Davies, H., Loughlin, J., Golding, J., and Phillips, J. (2013). Engineered neural tissue for peripheral nerve repair. Biomaterials 34, 7335–7343. doi: 10.1016/j.biomaterials.2013.06.025

PubMed Abstract | CrossRef Full Text | Google Scholar

Guo, B., G, B. L., Lidija, G., and Albertsson, A.-C. (2013). Biodegradable and electrically conducting polymers for biomedical applications. Prog. Polym. Sci. 38, 1263–1286. doi: 10.1016/j.progpolymsci.2013.06.003

CrossRef Full Text | Google Scholar

Guo, H.-F., Li, Z.-S., Dong, S., Chen, W.-J., Deng, L., Wang, Y.-F., et al. (2012). Piezoelectric PU/PVDF electrospun scaffolds for wound healing applications. Colloids Surf. B Biointerfaces 96, 29–36. doi: 10.1016/j.colsurfb.2012.03.014

PubMed Abstract | CrossRef Full Text | Google Scholar

Hua, B., Xu, Y., Zhao, L., Li, C., and Shi, G. (2009). Non-covalent functionalization of graphene sheets by sulfonated polyaniline. Chem. Commun. 13, 1667–1669. doi: 10.1039/b821805f

PubMed Abstract | CrossRef Full Text | Google Scholar

Huang, L., Zhu, L., Shi, X., Xia, B., Liu, Z., Zhu, S., et al. (2017). A compound scaffold with uniform longitudinally oriented guidance cues and a porous sheath promotes peripheral nerve regeneration in vivo. Acta Biomater. 68, 223–236. doi: 10.1016/j.actbio.2017.12.010

PubMed Abstract | CrossRef Full Text | Google Scholar

Issa, A., AlMa’adeed, M., Mrlík, M., and Luyt, A. (2016). Electrospun PVDF graphene oxide composite fibre mats with tunable physical properties. J. Polym. Res. 23, 232. doi: 10.1007/s10965-016-1126-y

CrossRef Full Text | Google Scholar

Jaiswal, M., and Koul, V. (2013). Assessment of multicomponent hydrogel scaffolds of poly(acrylic acid-2-hydroxy ethyl methacrylate)/gelatin for tissue engineering applications. J. Biomater. Appl. 27, 848–861. doi: 10.1177/0885328211428524

PubMed Abstract | CrossRef Full Text | Google Scholar

Jiang, Z., Song, Y., Qiao, J., Yang, Y., Zhang, W., Liu, W., et al. (2019). Rat sciatic nerve regeneration across a 10-mm defect bridged by a chitin/CM-chitosan artificial nerve graft. Int. J. Biol. Macromol. 129, 997–1005. doi: 10.1016/j.ijbiomac.2019.02.080

PubMed Abstract | CrossRef Full Text | Google Scholar

Jiao, G., Pan, Y., Wang, C., Li, Z., Li, Z., and Guo, R. (2017). A bridging SF/Alg composite scaffold loaded NGF for spinal cord injury repair. Mater. Sci. Eng. C Mater. Biol. Appl. 76, 81–87. doi: 10.1016/j.msec.2017.02.102

PubMed Abstract | CrossRef Full Text | Google Scholar

Jing, W., Ao, Q., Wang, L., Huang, Z., Cai, Q., Chen, G., et al. (2018). Constructing conductive conduit with conductive fibrous infilling for peripheral nerve regeneration. Chem. Eng. J. 345, 566–577. doi: 10.1016/j.cej.2018.04.044

CrossRef Full Text | Google Scholar

Jung, J., Kim, J., Wang, H., Di Nicolò, E., Drioli, E., and Lee, Y. M. (2016). Understanding the non-solvent induced phase separation (NIPS) effect during the fabrication of microporous PVDF membranes via thermally induced phase separation (TIPS). J. Membrane Sci. 514, 250–263. doi: 10.1016/j.memsci.2016.04.069

CrossRef Full Text | Google Scholar

Kühne, B., Puig Miquel, T., Ruiz-Martínez, S., Crous-Masó, J., Planas, M., Feliu, L., et al. (2018). Comparison of migration disturbance potency of epigallocatechin gallate (EGCG) synthetic analogs and EGCG PEGylated PLGA nanoparticles in rat neurospheres. Food Chem. Toxicol. 123, 195–204. doi: 10.1016/j.fct.2018.10.055

PubMed Abstract | CrossRef Full Text | Google Scholar

Kundu, B., Rajkhowa, R., Kundu, S. C., and Wang, X. (2013). Silk fibroin biomaterials for tissue regenerations. Adv. Drug Deliv. Rev. 65, 457–470. doi: 10.1016/j.addr.2012.09.043

PubMed Abstract | CrossRef Full Text | Google Scholar

Kurapati, R., Mukherjee, S. P., Martín Jiménez, C., Bepete, G., Vazquez, E., Penicaud, A., et al. (2018). Single layer and few layer graphene are degraded by neutrophil myeloperoxidase. Angew. Chem. Int. Ed. Engl. 57, 11722–11727. doi: 10.1002/anie.201806906

PubMed Abstract | CrossRef Full Text | Google Scholar

Lackington, W., Koci, Z., Alekseeva, T., Hibbitts, A., Kneafsey, S., Chen, G., et al. (2019). Controlling the dose-dependent, synergistic and temporal effects of NGF and GDNF by encapsulation in PLGA microparticles for use in nerve guidance conduits for the repair of large peripheral nerve defects. J. Control. Release 304, 51–64. doi: 10.1016/j.jconrel.2019.05.001

PubMed Abstract | CrossRef Full Text | Google Scholar

Lackington, W., Ryan, A., and O’Brien, F. (2017). Advances in nerve guidance conduit-based therapeutics for peripheral nerve repair. ACS Biomater. Sci. Eng. 3, 1221–1235. doi: 10.1021/acsbiomaterials.6b00500

CrossRef Full Text | Google Scholar

Lasprilla, A., Martinez, G., Lunelli, B., Jardini, A., and Filho, R. (2011). Poly-lactic acid synthesis for application in biomedical devices – A review. Biotechnol. Adv. 30, 321–328. doi: 10.1016/j.biotechadv.2011.06.019

PubMed Abstract | CrossRef Full Text | Google Scholar

Lee, Y.-S., Collins, G., and Arinzeh, T. (2011). Neurite extension of primary neurons on electrospun piezoelectric scaffolds. Acta Biomater. 7, 3877–3886. doi: 10.1016/j.actbio.2011.07.013

PubMed Abstract | CrossRef Full Text | Google Scholar

Lee, Y.-S., Wu, S., Arinzeh, T., and Bunge, M. (2016). Enhanced noradrenergic axon regeneration into Schwann cell-filled PVDF-TrFE conduits after complete spinal cord transection. Biotechnol. Bioeng. 114:26088. doi: 10.1002/bit.26088

PubMed Abstract | CrossRef Full Text | Google Scholar

Lei, S., Gao, Q., Zhao, H., Xie, C., Jianzhong, F., Liu, Z., et al. (2018). Fiber-based mini tissue with morphology-controllable GelMA microfibers. Small 14:e1802187. doi: 10.1002/smll.201802187

PubMed Abstract | CrossRef Full Text | Google Scholar

Li, L., El-Hayek, Y., Liu, B., Chen, Y., Gomez, E., Wu, X., et al. (2008). Direct−current electrical field guides neuronal stem/progenitor cell migration. Stem Cells 26, 2193–2200. doi: 10.1634/stemcells.2007-1022

PubMed Abstract | CrossRef Full Text | Google Scholar

Li, R., Liu, H., Huang, H., Bi, W., Yan, R., Tan, X., et al. (2018). Chitosan conduit combined with hyaluronic acid prevent sciatic nerve scar in a rat model of peripheral nerve crush injury. Mol. Med. Rep. 17, 4360–4368. doi: 10.3892/mmr.2018.8388

PubMed Abstract | CrossRef Full Text | Google Scholar

Li, R., Liu, Z., Pan, Y., Chen, L., Zhang, Z., and Lu, L. (2013). Peripheral nerve injuries treatment: a systematic review. Cell Biochem. Biophys. 68, 449–454. doi: 10.1007/s12013-013-9742-1

PubMed Abstract | CrossRef Full Text | Google Scholar

Lim, E.-M., Nakanishi, S., Hoghooghi, V., Eaton, S., Palmer, A., Frederick, A., et al. (2017). AlphaB-crystallin regulates remyelination after peripheral nerve injury. Proc. Natl. Acad. Sci. U.S.A. 114, E1707–E1716. doi: 10.1073/pnas.1612136114

PubMed Abstract | CrossRef Full Text | Google Scholar

Lins, L., Wianny, F., Livi, S., Dehay, C., Duchet, J., and Gerard, J.-F. (2016). Effect of polyvinylidene fluoride electrospun fiber orientation on neural stem cell differentiation. J. Biomed. Mater. Res. B Appl. Biomater. 105, 2376–2393. doi: 10.1002/jbm.b.33778

PubMed Abstract | CrossRef Full Text | Google Scholar

Liu, X., Zheng, C., Luo, X., and Wang, X. (2019). Recent advances of collagen-based biomaterials: multi-hierarchical structure, modification and biomedical applications. Mater. Sci. Eng. C 99, 1509–1522. doi: 10.1016/j.msec.2019.02.070

PubMed Abstract | CrossRef Full Text | Google Scholar

Manoukian, O., Arul, M., Rudraiah, S., Kalajzic, I., and Kumbar, S. (2019a). Aligned microchannel polymer-nanotube composites for peripheral nerve regeneration: small molecule drug delivery. J. Control. Release 296, 54–67. doi: 10.1016/j.jconrel.2019.01.013

PubMed Abstract | CrossRef Full Text | Google Scholar

Manoukian, O., Baker, J., Rudraiah, S., Arul, M., Vella, A., Domb, A., et al. (2019b). Functional polymeric nerve guidance conduits and drug delivery strategies for peripheral nerve repair and regeneration. J. Control. Release 317, 78–95. doi: 10.1016/j.jconrel.2019.11.021

PubMed Abstract | CrossRef Full Text | Google Scholar

Marakova, N., Boeva, Z., Humpolíèek, P., Lindfors, T., Pacherník, J., Kašpárková, V., et al. (2019). Electrochemically prepared composites of graphene oxide and conducting polymers: cytocompatibility of cardiomyocytes and neural progenitors. Mater. Sci. Eng. C Mater. Biol. Appl. 105:110029. doi: 10.1016/j.msec.2019.110029

PubMed Abstract | CrossRef Full Text | Google Scholar

Meng, L., Klinkajon, W., K−hasuwan, P.r, Harkin, S., Supaphol, P., and Wnek, G. (2015). Electrospun crosslinked poly (acrylic acid) fiber constructs: toward a synthetic model of the cortical layer of nerve. Polym. Int. 64, 42–48. doi: 10.1002/pi.4793

CrossRef Full Text | Google Scholar

Mobini, S., Spearman, B., Lacko, C., and Schmidt, C. (2017). Recent advances in strategies for peripheral nerve tissue engineering. Curr. Opin. Biomed. Eng. 4, 134–142. doi: 10.1016/j.cobme.2017.10.010

CrossRef Full Text | Google Scholar

Nezakati, T., Cousins, B., and Seifalian, A. (2014). Toxicology of chemically modified graphene-based materials for medical application. Arch. Toxicol. 88, 1987–2012. doi: 10.1007/s00204-014-1361-0

PubMed Abstract | CrossRef Full Text | Google Scholar

Ning, D., Min, L., Lijie, Z., Chengfei, L., Sergio, L. R., and Isiah, M. W. (2011). Recent advances in graphene based polymer composites. J. Hazard. Mater. 192, 1350–1357. doi: 10.1016/j.progpolymsci.2010.07.005

CrossRef Full Text | Google Scholar

Noor Fitrah, A. B., Tan, H. L., Ideris, N., and Radacsi, N. (2019). Morphology and conductivity evaluation of electrospun polyacrylic acid (PAA) microfiber. Mater. Today 17, 574–583. doi: 10.1016/j.matpr.2019.06.337

CrossRef Full Text | Google Scholar

Oprych, K., Whitby, R., Mikhalovsky, S., Tomlins, P., and Adu, J. (2016). Repairing peripheral nerves: is there a role for carbon nanotubes? Adv. Healthc. Mater. 5, 1253–1271. doi: 10.1002/adhm.201500864

PubMed Abstract | CrossRef Full Text | Google Scholar

Pei, S., Ai, F., and qu, s (2015). Fabrication and biocompatibility of reduced graphene oxide/poly(vinylidene fluoride) composite membranes. RSC Adv. 5, 99841–99847. doi: 10.1039/C5RA19228E

CrossRef Full Text | Google Scholar

Qian, Y., Song, J., Zhao, X., Chen, W., Ouyang, Y., Yuan, W., et al. (2018). 3D fabrication with integration molding of a graphene oxide/polycaprolactone nanoscaffold for neurite regeneration and angiogenesis. Adv. Sci. 5:1700499. doi: 10.1002/advs.201700499

PubMed Abstract | CrossRef Full Text | Google Scholar

Qiao, K., Guo, S., Zheng, Y., Xu, X., Meng, H., Peng, J., et al. (2018). Effects of graphene on the structure, properties, electro-response behaviors of GO/PAA composite hydrogels and influence of electro-mechanical coupling on BMSC differentiation. Mater. Sci. Eng. C Mater. Biol. Appl. 93, 853–863. doi: 10.1016/j.msec.2018.08.047

PubMed Abstract | CrossRef Full Text | Google Scholar

Qiu, H., Guo, H., Li, D., Hou, Y., and Kuang, T. (2020). Intravesical hydrogels as drug reservoirs. Trends Biotechnol. 38, 579–583. doi: 10.1016/j.tibtech.2019.12.012

PubMed Abstract | CrossRef Full Text | Google Scholar

Rhatomy, S., Arif, A., Utomo, D., Mulyadi, D., Salipi, M., Setyawan, R., et al. (2019). Posterior cruciate ligament reconstruction augmentation on avulsion PCL: a case series. Int. J. Surg. 20, 15–19. doi: 10.1016/j.ijso.2019.09.003

CrossRef Full Text | Google Scholar

Ribeiro, C., Correia, D., Ribeiro, S., Sencadas, V., Botelho, G., and Lanceros-Méndez, S. (2014). Piezoelectric poly(vinylidene fluoride) microstructure and poling state in active tissue engineering. Eng. Life Sci. 15, 351–356. doi: 10.1002/elsc.201400144

CrossRef Full Text | Google Scholar

Roca, F., Lozano-Picazo, P., Pérez-Rigueiro, J., Tortuero, G., Pradas, M., and Martínez-Ramos, C. (2020). Conduits based on the combination of hyaluronic acid and silk fibroin: characterization, in vitro studies and in vivo biocompatibility. Int. J. Biol. Macromol. 148, 378–390. doi: 10.1016/j.ijbiomac.2020.01.149

PubMed Abstract | CrossRef Full Text | Google Scholar

Sadeghi, A., Moztarzadeh, F., and Mohandesi, J. (2018). Investigating the effect of chitosan on hydrophilicity and bioactivity of conductive electrospun composite scaffold for neural tissue engineering. Int. J. Biol. Macromol. 121, 625–632. doi: 10.1016/j.ijbiomac.2018.10.022

PubMed Abstract | CrossRef Full Text | Google Scholar

Samadian, H., Maleki, H., Fathollahi, A., Salehi, M., Gholizadeh, S., Derakhshankhah, H., et al. (2020). Naturally occurring biological macromolecules-based hydrogels: potential biomaterials for peripheral nerve regeneration. Int. J. Biol. Macromol. 154, 795–817. doi: 10.1016/j.ijbiomac.2020.03.155

PubMed Abstract | CrossRef Full Text | Google Scholar

Sanjairaj, V. (2016). 3D bioprinting of skin: a state-of-the-art review on modelling, materials, and processes. Biofabrication 8:032001. doi: 10.1088/1758-5090/8/3/032001

CrossRef Full Text | Google Scholar

Sanjairaj, V., Shuo, Z., Fuh, J., and Lu, W. (2017). Design of three-dimensional scaffolds with tunable matrix stiffness for directing stem cell lineage specification: an in silico study. Bioengineering 4:66. doi: 10.3390/bioengineering4030066

PubMed Abstract | CrossRef Full Text | Google Scholar

Schmidt, C., Shastri, V. P., Vacanti, J., and Langer, R. (1997). Stimulation of neurite outgrowth using an electrically conducting polymer. Proc. Natl. Acad. Sci. U.S.A. 94, 8948–8953. doi: 10.1073/pnas.94.17.8948

PubMed Abstract | CrossRef Full Text | Google Scholar

Shrestha, S., Shrestha, B., Kim, J.-I., ko, s.-w, Park, C., and Kim, C. (2018). Electrodeless coating polypyrrole on chitosan grafted polyurethane with functionalized multiwall carbon nanotubes electrospun scaffold for nerve tissue engineering. Carbon 136, 430–443. doi: 10.1016/j.carbon.2018.04.064

CrossRef Full Text | Google Scholar

Si, J., Yang, Y., Xing, X., Yang, F., and Shan, P. (2019). Controlled degradable chitosan/collagen composite scaffolds for application in nerve tissue regeneration. Polym. Degrad. Stab. 166, 73–85. doi: 10.1016/j.polymdegradstab.2019.05.023

CrossRef Full Text | Google Scholar

Song, W., Zhao, Y., Wu, Y., Li, Z., Lv, H., Li, S., et al. (2018). Fabrication, characterization and biocompatibility of collagen/oxidized regenerated cellulose-Ca composite scaffold for carrying Schwann cells. Int. J. Biol. Macromol. 119, 1195–1203. doi: 10.1016/j.ijbiomac.2018.08.055

PubMed Abstract | CrossRef Full Text | Google Scholar

Sun, H., Mei, L., Song, C., Cui, X., and Wang, P. (2006). The in vivo degradation, absorption and excretion of PCL-based implant. Biomaterials 27, 1735–1740. doi: 10.1016/j.biomaterials.2005.09.019

PubMed Abstract | CrossRef Full Text | Google Scholar

Surmenev, R., Orlova, T., Chernozem, R., Ivanova, A., Bartasyte, A., Mathur, D. S., et al. (2019). Hybrid lead-free polymer-based nanocomposites with improved piezoelectric response for biomedical energy-harvesting applications: a review. Nano Energy 62, 475–506. doi: 10.1016/j.nanoen.2019.04.090

CrossRef Full Text | Google Scholar

Tang, X., Xue, C., Wang, Y., Ding, F., Yang, Y., and Gu, X. (2012). Bridging peripheral nerve defects with a tissue engineered nerve graft composed of an in vitro cultured nerve equivalent and a silk fibroin-based scaffold. Biomaterials 33, 3860–3867. doi: 10.1016/j.biomaterials.2012.02.008

PubMed Abstract | CrossRef Full Text | Google Scholar

Titorencu, I., Albu, M., Nemecz, M., and Jinga, V. (2016). Natural polymer-cell bioconstructs for bone tissue engineering. Curr. Stem Cell Res. Ther. 12, 165–174. doi: 10.2174/1574888X10666151102105659

PubMed Abstract | CrossRef Full Text | Google Scholar

Tsonos, C., Pandis, C., Soin, N., Sakellari, D., Myrovali, E., Kripotou, S., et al. (2015). Multifunctional nanocomposites of poly(vinylidene fluoride) reinforced by carbon nanotubes and magnetite nanoparticles. Express Polym. Lett. 9, 1104–1118. doi: 10.3144/expresspolymlett.2015.99

CrossRef Full Text | Google Scholar

Vijayavenkataraman, S. (2020). Nerve guide conduits for peripheral nerve injury repair: a review on design, materials and fabrication methods. Acta Biomater. 106, 54–59. doi: 10.1016/j.actbio.2020.02.003

PubMed Abstract | CrossRef Full Text | Google Scholar

Wach, R., Adamus-Włodarczyk, A., Olejnik, A., Matusiak, M., Aranilla, C., and Ulanski, P. (2020). Carboxymethylchitosan hydrogel manufactured by radiation-induced crosslinking as potential nerve regeneration guide scaffold. React. Funct. Polym. 152:104588. doi: 10.1016/j.reactfunctpolym.2020.104588

CrossRef Full Text | Google Scholar

Wang, A., Liu, Z., Hu, M., Wang, C., Zhang, X., Shi, B., et al. (2017). Piezoelectric nanofibrous scaffolds as in vivo energy harvesters for modifying fibroblast alignment and proliferation in wound healing. Nano Energy 43, 63–71. doi: 10.1016/j.nanoen.2017.11.023

CrossRef Full Text | Google Scholar

Wang, J., Cheng, Y., Chen, L., Zhu, T., Ye, K., Jia, C., et al. (2018). In vitro and in vivo studies of electroactive reduced graphene oxide-modified nanofiber scaffolds for peripheral nerve regeneration. Acta Biomater. 84, 98–113. doi: 10.1016/j.actbio.2018.11.032

PubMed Abstract | CrossRef Full Text | Google Scholar

Wu, C., Zhu, Y., Chang, J., Zhang, Y., and Xiao, Y. (2010). Bioactive inorganic-materials/alginate composite microspheres with controllable drug-delivery ability. J. Biomed. Mater. Res. B Appl. Biomater. 94, 32–43. doi: 10.1002/jbm.b.31621

PubMed Abstract | CrossRef Full Text | Google Scholar

Wu, Y., Wang, L., Guo, B., Shao, Y., and Ma, P. (2016). Electroactive biodegradable polyurethane significantly enhanced Schwann cells myelin gene expression and neurotrophin secretion for peripheral nerve tissue engineering. Biomaterials 87, 18–31. doi: 10.1016/j.biomaterials.2016.02.010

PubMed Abstract | CrossRef Full Text | Google Scholar

Wu, Y., Xiang, Y., Fang, J., Li, X., Lin, Z., Dai, G., et al. (2019). The influence of the stiffness of GelMA substrate on the outgrowth of PC12 cells. Biosci. Rep. 39:BSR20181748. doi: 10.1042/BSR20181748

PubMed Abstract | CrossRef Full Text | Google Scholar

Yang, F., Murugan, R., and Wang, S. (2005). Electrospinning of nano/micro scale poly(L-lactic acid) aligned fibers and their potential in neural tissue engineering. Biomaterials 26, 2603–2610. doi: 10.1016/j.biomaterials.2004.06.051

PubMed Abstract | CrossRef Full Text | Google Scholar

Yousefi, A., Akbarzadeh, R., and Yousefi, A.-M. (2014). Effects of processing parameters in thermally induced phase separation technique on porous architecture of scaffolds for bone tissue engineering. J. Biomed. Mater. Res. B Appl. Biomater. 102, 1304–1315. doi: 10.1002/jbm.b.33101

PubMed Abstract | CrossRef Full Text | Google Scholar

Yu, W., Zhao, W., Zhu, C., Zhang, X., Ye, D., Zhang, W., et al. (2011). Sciatic nerve regeneration in rats by a promising electrospun collagen/poly(ε-caprolactone) nerve conduit with tailored degradation rate. BMC Neurosci. 12:68. doi: 10.1186/1471-2202-12-68

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhang, J., Li, J., Li, D., Xiao, C., Xiao, H., Yang, H., et al. (2019). Electrospun polymer biomaterials. Prog. Polym. Sci. 90, 1–34. doi: 10.1016/j.progpolymsci.2019.01.002

CrossRef Full Text | Google Scholar

Zhang, S., Sanjairaj, V., Chong, G., Fuh, Y., and Lu, W.-F. (2019). Computational design and optimization of nerve guidance conduits for improved mechanical properties and permeability. J. Biomech. Eng. 141:4043036. doi: 10.1115/1.4043036

CrossRef Full Text | Google Scholar

Zhang, S., Sanjairaj, V., Lu, W.-F., and Fuh, J. (2018). A review on the use of computational methods to characterize, design, and optimize tissue engineering scaffolds, with a potential in 3D printing fabrication. J. Biomed. Mater. Res. B Appl. Biomater. 107, 1329–1351. doi: 10.1002/jbm.b.34226

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhang, X., Qu, W., Li, D., Shi, K., Li, R., Han, Y., et al. (2020). Functional polymer−based nerve guide conduits to promote peripheral nerve regeneration. Adv. Mater. Interfaces 7:2000225. doi: 10.1002/admi.202000225

CrossRef Full Text | Google Scholar

Zhu, T., Cui, Y., Zhang, M., Zhao, D., and Liu, G. (2020). Engineered three-dimensional scaffolds for enhanced bone regeneration in osteonecrosis. Bioact. Mater. 5, 584–601. doi: 10.1016/j.bioactmat.2020.04.008

PubMed Abstract | CrossRef Full Text | Google Scholar

Zuo, Q., Guo, R., Liu, Q., Hong, A., Shi, Y., Kong, Q., et al. (2015). Heparin-conjugated alginate multilayered microspheres for controlled release of bFGF. Biomed. Mater. 10:035008. doi: 10.1088/1748-6041/10/3/035008

CrossRef Full Text | Google Scholar

Keywords: peripheral nerve regeneration, tissue engineering, nerve guide conduit, scaffold material, polymer

Citation: Jiang H, Qian Y, Fan C and Ouyang Y (2020) Polymeric Guide Conduits for Peripheral Nerve Tissue Engineering. Front. Bioeng. Biotechnol. 8:582646. doi: 10.3389/fbioe.2020.582646

Received: 13 July 2020; Accepted: 07 September 2020;
Published: 25 September 2020.

Edited by:

Jianxun Ding, Chinese Academy of Sciences, China

Reviewed by:

Zhang Peixun, Peking University People’s Hospital, China
Xi Zhang, Jilin University, China
Xiaojun Yu, Stevens Institute of Technology, United States
Vijayavenkataraman Sanjairaj, New York University Abu Dhabi, United Arab Emirates

Copyright © 2020 Jiang, Qian, Fan and Ouyang. This is an open-access article distributed under the terms of the Creative Commons Attribution License (CC BY). The use, distribution or reproduction in other forums is permitted, provided the original author(s) and the copyright owner(s) are credited and that the original publication in this journal is cited, in accordance with accepted academic practice. No use, distribution or reproduction is permitted which does not comply with these terms.

*Correspondence: Yun Qian, lollipopcloudland@foxmail.com; Yuanming Ouyang, ouyangyuanming@163.com

Disclaimer: All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article or claim that may be made by its manufacturer is not guaranteed or endorsed by the publisher.