Optimizing an Injectable Composite Oxygen-Generating System for Relieving Tissue Hypoxia

\nTai-En HsiehTai-En Hsieh1Sheng-Ju LinSheng-Ju Lin1Li-Chi Chen,Li-Chi Chen1,2Chun-Chieh Chen,Chun-Chieh Chen3,4Po-Liang Lai,
Po-Liang Lai3,4*Chieh-Cheng Huang
Chieh-Cheng Huang1*
  • 1Institute of Biomedical Engineering, National Tsing Hua University, Hsinchu, Taiwan
  • 2Department of Life Science, National Tsing Hua University, Hsinchu, Taiwan
  • 3Department of Orthopaedic Surgery, Linkou Chang Gung Memorial Hospital, Taoyuan City, Taiwan
  • 4Bone and Joint Research Center, Linkou Chang Gung Memorial Hospital, Taoyuan City, Taiwan

Oxygen deficiency resulting from bone fracture-induced vascular disruption leads to massive cell death and delayed osteoblast differentiation, ultimately impairing new bone formation and fracture healing. Enhancing local tissue oxygenation can help promote bone regeneration. In this work, an injectable composite oxygen-generating system consisting of calcium peroxide (CaO2)/manganese dioxide (MnO2)-encapsulated poly lactic-co-glycolic acid (PLGA) microparticles (CaO2 + MnO2@PLGA MPs) is proposed for the local delivery of oxygen. By utilizing a series of methodologies, the impacts of each component used for MP fabrication on the oxygen release behavior and cytotoxicity of the CaO2 + MnO2@ PLGA MPs are thoroughly investigated. Our analytical data obtained from in vitro studies indicate that the optimized CaO2 + MnO2@PLGA MPs developed in this study can effectively relieve the hypoxia of preosteoblast MC3T3-E1 cells that are grown under low oxygen tension and promote their osteogenic differentiation, thus holding great promise in enhancing fractural healing by increasing tissue oxygenation.

Introduction

Bone fracture is one of the most common injuries of the musculoskeletal system (Claes et al., 2012). Although bone tissue possesses excellent self-healing capability, it has been reported that ~10% of patients with bone fracture exhibit healing problems, such as delayed union or non-union (Zeitouni et al., 2012; Wang et al., 2017). As oxygen is required in several basic cellular processes that are crucial for fracture healing (Lu et al., 2013), tissue hypoxia resulting from vascular disruption during fracture leads to cell death and delayed osteoblast differentiation, ultimately impairing new bone formation and fracture healing (Lu et al., 2013; Gómez-Barrena et al., 2015).

To address this issue, autologous bone grafts can be harvested and transplanted to the defect site to promote bone regeneration owing to their endogenous high-density vasculature, which can quickly anastomose with surrounding blood vessels (Zheng et al., 2010; Lee and Volpicelli, 2017). However, limited donor tissue availability and severe additional post-operative pain and complications restrict clinical applications of this approach (Ho et al., 2016). Other strategies, such as hyperbaric oxygen (HBO) therapy, have been employed to increase tissue oxygenation (Lu et al., 2013; Park and Park, 2018). As oxygen is still delivered via the vasculature, however, it is unlikely that poorly perfused injury tissue would benefit greatly from HBO treatment (Farris et al., 2016). Additionally, sustained oxygen delivery cannot be achieved by using HBO therapy, which can only be applied in a transient manner to avoid unwanted side effects (Farris et al., 2016). Hence, a sustained oxygen delivery strategy that can be used to improve local oxygen tension is warranted.

Several peroxide-based oxygen-evolving materials, such as calcium peroxide (CaO2) (Wang J. et al., 2011; Steg et al., 2015; Huang et al., 2016) and sodium percarbonate (Harrison et al., 2007; Ward et al., 2013; Chandra et al., 2015), have been utilized to chemically generate oxygen to enhance tissue oxygenation. Upon exposure to water, peroxide materials break down to yield hydrogen peroxide (H2O2), which can be further converted into molecular oxygen and water by catalysts (Farris et al., 2016; Gholipourmalekabadi et al., 2016). As the rate of oxygen generation depends on several environmental factors (Gholipourmalekabadi et al., 2016), such as humidity, pH, temperature, and the presence of catalysts, peroxide materials have been incorporated in a variety of biomaterials in the formats of films (Harrison et al., 2007), particles (Newland et al., 2018), and fibers (Wang J. et al., 2011) to achieve the sustained release of oxygen. This technique has been explored to provide oxygen for application in the field of regenerative medicine, including ischemic diseases (Harrison et al., 2007), cell transplantation (Pedraza et al., 2012; Coronel et al., 2017; Fan et al., 2018), wound healing (Chandra et al., 2015), and tissue engineering (Oh et al., 2009).

Although several peroxide-based oxygen delivery vehicles have been developed, some common limitations, especially the initial burst release of oxygen occurring in the first few hours and the production of cytotoxic H2O2 or other reactive oxygen species, remain major challenges (Farris et al., 2016; Gholipourmalekabadi et al., 2016; Park and Park, 2018). Even though the precise balance oxygen delivery and cytotoxicity can be overcome by utilizing various material-based strategies (Steg et al., 2015), most of these methods result in significantly increased size of the developed oxygen-delivery platform, thus reducing its feasibility in clinical application (Pedraza et al., 2012). Moreover, the capacity of these oxygen-generating carriers to promote osteogenic differentiation under low oxygen tension has not yet been investigated.

To address the abovementioned issues, we present an innovative implantable composite oxygen-generating system that can be easily delivered by local injection, and characterize its function in relieving cellular hypoxia and promoting osteogenic differentiation (Figure 1A). To fabricate a composite oxygen-generating system, CaO2 and manganese dioxide (MnO2) (Peng et al., 2017) were used as a source of H2O2 and a catalyst, respectively. In aqueous environments, H2O2 is first formed and then decomposes into oxygen. In addition to oxygen generation, the calcium ions (Ca2+) produced during CaO2 hydrolysis may be utilized as a calcium source for new bone formation (Teotia et al., 2016). To prolong the duration of oxygen evolution, CaO2 and MnO2 powders were embedded into poly(lactic-co-glycolic acid) (PLGA) microparticles (MPs; CaO2 + MnO2@PLGA MPs) using a microfluidic device (Figure 1A). To achieve the precise balance between oxygen generation and the caused cytotoxicity, a multifactor experimental design was employed, resulting in a more comprehensive understanding of the fashions in which oxygen evolves and the byproducts are generated from the MPs during the reaction. This study lays the solid foundation for the future development of more sophisticated and clinically applicable oxygen-generating biomaterials. We hypothesize that the developed injectable oxygen-generating system can be employed to increase local oxygen tension and thus enhance the osteogenesis of preosteoblasts and their mineral deposition in vitro, thereby holding great promise in promoting new bone formation and fracture healing.

FIGURE 1
www.frontiersin.org

Figure 1. Effects of PLGA concentration on the oxygen release behavior of CaO2 + MnO2@PLGA MPs. (A) Schematic diagram showing the structure and composition of the developed CaO2 + MnO2@PLGA MPs that act as an oxygen-generating system to enhance tissue oxygenation. (B) SEM images of CaO2 + MnO2@PLGA MPs prepared using various PLGA concentrations. (C) The in vitro release profiles and (D) the corresponding AUCs of oxygen release from CaO2 + MnO2@PLGA MPs incubated in PBS at 37°C. (E) Variation in pH and (F) accumulation of H2O2 in test saline following treatment with various MPs. (G) Results of the CCK-8 assay, (H) LDH assay, and (I) live/dead staining following treatment with various MPs. *p < 0.05; **p < 0.01; ***p < 0.005; ns, not significant.

Materials and Methods

Materials

CaO2, MnO2, polyvinyl alcohol (PVA), ascorbic acid, β-glycerophosphate, Alizarin red S, and hexadecylpyridinium chloride monohydrate were purchased from Sigma-Aldrich (St. Louis, MO, USA). PLGA (with a lactide:glycolide molar ratio of 75:25) was acquired from Green Square Material (Taipei, Taiwan). The mouse preosteoblast MC3T3-E1 cells were purchased from the American Type Culture Collection (ATCC CRL-2593, Manassas, VA, USA), while cell culture reagents were procured from Thermo Fisher Scientific (Waltham, MA, USA). All other chemicals and reagents used were of analytical grade.

CaO2 + MnO2@PLGA MP Preparation

An oil-in-water single-emulsion microfluidic system with poly(vinyl chloride) tubes, glass capillaries, and 23G needles was used to prepare the CaO2 + MnO2@PLGA MPs. The oil phase, a solution of PLGA in dichloromethane (DCM) that contained CaO2 and MnO2 powder, was introduced into the microfluidic system at a flow rate of 0.25 mL/min to form single-emulsion droplets in a water phase that contained 5 wt% PVA at a flow rate of 5 mL/min. The formed emulsified CaO2 + MnO2@PLGA MPs were added to a larger water phase, which was stirred for 4 hours, allowing the solvent to evaporate. The CaO2 + MnO2@PLGA MPs were then washed in deionized water to remove the outer PVA before being stored at 4°C for further use. The morphology of the prepared CaO2 + MnO2@PLGA MPs was examined under a scanning electron microscope (SEM; JSM-5600, JEOL, Tokyo, Japan). Additionally, the specific surface areas of the developed MPs were assessed by nitrogen adsorption using an ASAP 2020 analyzer (Micromeritics, Norcross, GA, USA).

Oxygen Release Behavior of CaO2 + MnO2@PLGA MPs

The prepared CaO2 + MnO2@PLGA MPs were transferred into phosphate-buffered saline (PBS) and incubated in a hypoxia chamber with 1% oxygen at 37°C (ProOx 110, BioSpherix, Parish, NY, USA). The dissolved oxygen concentrations were monitored using an InLab OptiOx DO sensor (Mettler Toledo, Greifensee, Switzerland). The pH value and the concentration of accumulated H2O2 in PBS samples during oxygen evolution were evaluated using a pH meter (ST3100; OHAUS, Parsippany, NJ, USA) and the Amplex Red (Life Technologies) assay, respectively.

Cytotoxicity of CaO2 + MnO2@PLGA MPs

Preosteoblast MC3T3-E1 cells were utilized to evaluate the cytotoxicity of CaO2 + MnO2@PLGA MPs. Cells were seeded at 7.5 × 103 cells per well in 48-well plates that contained Minimum Essential Medium α (αMEM) supplemented with 10% fetal bovine serum (FBS; GE Healthcare Bio-Sciences, Pittsburgh, PA, USA) and incubated for 24 h. Subsequently, the prepared CaO2 + MnO2@PLGA MPs were employed for treating cells by direct transfer into each well. After incubation for another 24 h, the viability of the MC3T3-E1 cells was evaluated using a live/dead viability kit (Thermo Fisher Scientific), and the cells were photographed by a fluorescence microscope (Axio Observer 7; Carl Zeiss). Additionally, the cell viability and cytotoxicity were quantified using a Cell Counting Kit-8 (CCK-8; Dojindo Laboratories, Kumamoto, Japan) (Park et al., 2018) and a Cytotoxicity Lactate Dehydrogenase (LDH) Assay Kit (Dojindo Laboratories), respectively.

Alleviation of Cellular Hypoxia by CaO2 + MnO2@PLGA MPs

To detect cellular hypoxia, MC3T3-E1 cells that were preincubated with Image-iT Green Hypoxia Reagent (Thermo Fisher Scientific) (Ayuso et al., 2016), a cell-permeable fluorogenic probe, were maintained in 1% oxygen (Heracell VIOS 160i incubator; Thermo Fisher Scientific) for 24 h. The cells were then treated with CaO2 + MnO2@PLGA MPs for an additional 24 h. Thereafter, the test cells were observed using a fluorescence microscope. Alternatively, test cells that were maintained under hypoxic conditions (1% oxygen) and treated with CaO2 + MnO2@PLGA MPs were fixed in 4% paraformaldehyde and then stained with a primary antibody against hypoxia-inducible factor (HIF)-1α (Abcam, Cambridge, MA, USA). After incubation with a secondary antibody and counterstaining with 4′,6-diamidino-2-phenylindole (Thermo Fisher Scientific), the samples were observed using a fluorescence microscope.

Osteogenic Differentiation of MC3T3-E1 Cells

The effects of CaO2 + MnO2@PLGA MP treatment on the osteogenic differentiation of preosteoblast MC3T3-E1 cells under hypoxic conditions (1% oxygen) were investigated by evaluating the degree of in vitro mineralization. After incubating 7.5 × 103 cells in each well of a 48-well plate for 24 h, the culture medium was replaced with αMEM supplemented with 10% FBS, 50 μg/mL ascorbic acid, 5 mM β-glycerophosphate, and test MPs. The cells were then cultivated in 1% oxygen for 20 days (Lin et al., 2018). The culture media together with the test MPs were replaced every 3 days throughout the entire experimental course. To assess the in vitro mineralization, cells were fixed in ice-cold 70% ethanol for 1 h and incubated with 40 mM Alizarin red S solution for 20 min. The stained calcium mineral deposition was observed under a microscope followed by dissolving in 10 wt% hexadecylpyridinium chloride solution and quantified by absorbance measurement at 562 nm using a microplate reader (SpectraMax iD3, Molecular Devices, Sunnyvale, CA, USA) (Sun et al., 2013).

Animal Study

All animal experimental procedures were approved by the Institutional Animal Care & Utilization Committee, National Tsing Hua University, Hsinchu, Taiwan. Female BALB/c mice at 8 weeks of age were purchased from National Laboratory Animal Center, Nangang, Taiwan. The animals were anesthetized by inhalation of 2% isoflurane. After removing the hair of the dorsal side, the skin of the injection sites was sterilized using an alcohol swab. Test MPs (10 mg) were suspended in 200 μL normal saline and injected subcutaneously into the dorsal flanks of mice using a 23-gauge needle (n = 4). After 14 days, the mice were euthanized by CO2 inhalation. The dorsal tissue was harvested and embedded in optimum cutting temperature compound. Ten-micrometer thick tissue sections were cut using a cryostat microtome (CM1950, Leica, Wetzlar, Germany) and stained with hematoxylin and eosin (H&E). Photomicrographs of the stained sections were taken and processed for nuclei counting using ImageJ (Schneider et al., 2012). Briefly, five randomly selected views surrounding the implanted MPs were converted to greyscale and processed by the Watershed ImageJ plugin followed by cell nuclei counting using the Particle Analyzer tool.

Statistical Analysis

All statistical analyses were performed using GraphPad Prism software (version 8.1; San Diego, CA, USA). The experimental data are presented as the mean ± standard deviation. A two-tailed Student's t-test was used for comparisons between two groups. One-way analysis of variance (ANOVA) with Bonferroni correction was used for comparisons of three or more groups. A p < 0.05 indicated a significant difference.

Results and Discussion

Concentration of PLGA Modulates Oxygen Release Behavior

In the first step of the reaction, CaO2 can produce both calcium hydroxide [Ca(OH)2] and H2O2 upon reaction with water. Therefore, the speed of water infiltration into MPs may determine the reaction rate as well as the duration of oxygen generation. In addition, the alteration of the pH environment caused by the produced Ca(OH)2 and accumulation of H2O2 may have potential harmful effects on the surrounding tissue (Gholipourmalekabadi et al., 2016). To maximize the oxygen-producing capability of MPs while minimizing their cytotoxic effects, the optimization of several parameters was performed.

As the polymeric matrix of PLGA can modulate the hydrolytic reaction of CaO2 by restricting the permeation of water molecules into MPs, we first investigated the effect of PLGA concentration on the morphology of MPs. As indicated by the SEM images in Figure 1B, the MPs that were prepared using 5% or 10% PLGA exhibited a porous surface architecture. In the 15 and 20% PLGA groups, however, less pores were observed. Determined using the Brunauer–Emmett–Teller method (Wang Y.-T. et al., 2011), the specific surface areas of the MPs (0.537 m2/g for 5% PLGA group, 0.406 m2/g for 10% PLGA group, 0.295 m2/g for 15% PLGA group, and 0.0855 m2/g for 20% PLGA group) further revealed their differences in porosity. During MP preparation, the emulsion was gently stirred in PVA solution for 4 h to remove the DCM by evaporation. Owing to the hydrophobicity of PLGA polymer, water may infiltrate more easily into MPs that were prepared using a low concentration of PLGA to initiate the reaction of oxygen production before complete solidification of the MPs, thus resulting in their porous morphology. In contrast, a high concentration of PLGA may act as a barrier to prevent the further penetration of water, thereby presenting a less porous architecture.

Next, to investigate their oxygen evolution profile, test MPs were suspended in PBS and incubated in a hypoxia chamber with 1% oxygen at 37°C. As indicated by the obtained oxygen release profiles (Figure 1C) and their corresponding areas under the curve (AUCs; the total area under the dissolved oxygen concentration vs. time curve; Figure 1D), the duration and amount of oxygen production were effectively modulated by the concentration of PLGA used to prepare MPs, which all encapsulated the same weight of CaO2 (7.5 mg/mL). The MPs prepared using 10% PLGA exhibited a longer period (~120 h) of oxygen generation than those fabricated using 5% PLGA (96 h). As the concentration of PLGA further increased up to 20%, the period and amount of oxygen production decreased significantly owing to the reduced surface areas of MPs (Figure 1B) and the hydrophobic characteristics of PLGA, which prevent water infiltration.

The impacts of MPs on the surrounding environment during oxygen evolution and the resultant cytotoxicity were also assessed. In the 5 and 10% PLGA groups, the relatively fast reaction led to dramatic changes in pH values (Figure 1E) and a significant accumulation of H2O2 (Figure 1F); both processes had an adverse effect on the viability of MC3T3-E1 cells, as indicated by the experimental results obtained from the CCK-8 assay, LDH assay, and live/dead staining (Figures 1G–I, respectively). As a result, MPs prepared using 15% PLGA that could evolve oxygen for ~100 h and had only limited cytotoxicity were chosen for the following experiments.

Amounts of Encapsulated CaO2 and MnO2 Control Oxygen Release Behavior

Next, the amount of CaO2 loaded in the MPs was optimized. As the CaO2 powder was used as the source of H2O2, which could be further converted to oxygen, we speculated that the more CaO2 was encapsulated, the more oxygen could be generated by the MPs. According to the oxygen generation profiles and their corresponding AUCs (Figures 2A,B), the total amount of oxygen evolved from the MPs elevated gradually as the amount of incorporated CaO2 increased, while the duration of oxygen generation was similar among all test groups. Additionally, the magnitude of alkalization and H2O2 accumulation in the PBS samples was positively correlated with the amount of encapsulated CaO2 (Figures 2C,D).

FIGURE 2
www.frontiersin.org

Figure 2. Effects of the amount of encapsulated CaO2 on the oxygen release behavior of CaO2 + MnO2@PLGA MPs. (A) The release profiles and (B) corresponding AUCs of oxygen release from MPs. (C) Variation in pH and (D) accumulation of H2O2 in PBS samples following treatment with MPs. (E) Results of the CCK-8 assay, (F) LDH assay, and (G) live/dead staining following treatment with MPs. *p < 0.05; ***p < 0.005; ns, not significant.

The MPs that were loaded with various amounts of CaO2 were then used to treat MC3T3-E1 cells. A significant cytotoxic effect was observed when 12 mg/mL or more CaO2 powder was encapsulated in the MPs (Figures 2E–G). Using the same methodology, the optimized amount of the catalyst MnO2 embedded in the MPs was determined to be 0.22 mg/mL (Supplementary Figure 1). Therefore, CaO2 + MnO2@PLGA MPs that were fabricated using 15% PLGA and loaded with 10 mg/mL CaO2 and 0.22 mg/mL MnO2 were employed for subsequent studies.

CaO2 + MnO2@PLGA MPs Relieve Cellular Hypoxia

The morphology and size of the as-prepared oxygen-generating MPs were examined by SEM. Figure 3A shows that the plain PLGA MPs were spherical in shape and had a diameter of 248 ± 19 μm (n = 5 batches). After encapsulating CaO2 and MnO2, however, the size of the PLGA MPs increased slightly (298 ± 62 μm in diameter). Before evaluating their capacity to alleviate cellular hypoxia, we first examined the optimal dose of CaO2 + MnO2@PLGA MPs for treating MC3T3-E1 cells. According to the results of live/dead staining (Figure 3B) and CCK-8 assay (Figure 3C), a dose of 1 mg/mL MPs did not exhibit significant cytotoxicity. To further confirm the safety of the determined dosage, the viability of the MC3T3-E1 cells that received 1 mg/mL MPs and were incubated for 3 and 7 days was evaluated. In this study, both the culture medium and the MPs were replaced every other day. During the entire culture period, the cells that were treated with the MPs exhibited a similar level of viability when compared to the untreated control (Figure 3D and Supplementary Figure 2), demonstrating the low cytotoxicity of the developed CaO2 + MnO2@PLGA MPs; thus, this dose was used in the subsequent reoxygenation and osteogenic differentiation studies.

FIGURE 3
www.frontiersin.org

Figure 3. In vitro cytotoxicity evaluation of the developed CaO2 + MnO2@PLGA MPs. (A) SEM images of the PLGA MPs. (B) Representative live/dead images and (C) corresponding results of the CCK-8 assay at 24 h following treatment with various doses of MPs. (D) Results of CCK-8 assay of MC3T3-E1 cells receiving MP treatment for 3 or 7 days. *p < 0.05; ns, not significant.

The availability of oxygen for cells that were incubated under low oxygen tension (1% O2) with or without CaO2 + MnO2@PLGA MPs was assessed using the hypoxia-responsive dye Image-iT Green Hypoxia Reagent, whose fluorescent signal increases with reduced oxygen levels (Stone et al., 2019). Cells that were maintained under normoxic conditions (21% O2) were used as a control. For cells cultivated under normal oxygen tension, only a basal level of fluorescent signal could be detected (Figures 4A,B). Conversely, the cells incubated under hypoxic conditions emitted strong green fluorescence, demonstrating the limited availability of oxygen for cells. Moreover, the hypoxic cells that were treated with CaO2 + MnO2@PLGA MPs exhibited significantly reduced fluorescent intensity, suggesting that the hypoxic environment could be effectively reversed by the developed MPs. It has been reported that the probe Image-iT Green Hypoxia Reagent is fluorogenic when atmospheric oxygen levels are lower than 5% (Stone et al., 2019). Therefore, the absence of a hypoxia signal in the cells further implied that the local oxygen tension could be increased to higher than 5% by applying the CaO2 + MnO2@PLGA MPs developed in this study.

FIGURE 4
www.frontiersin.org

Figure 4. Alleviation of cellular hypoxia by CaO2 + MnO2@PLGA MPs. (A,B) Treating cells that were incubated under hypoxic conditions with the developed CaO2 + MnO2@PLGA MPs effectively relieved cellular hypoxia, as indicated by the reduced fluorescence intensity of hypoxia-sensing dye Image-iT Green and (C) the decreased nuclear translocation/accumulation of the key hypoxia-responsive transcription factor HIF-1α. *p < 0.05; ****p < 0.001.

To further confirm the potential of CaO2 + MnO2@PLGA MPs in alleviating cellular hypoxia, the test cells were fixed and immunostained for HIF-1α. Under normally oxygenated conditions, the key hypoxia-responsive transcription factor HIF-1α is rapidly degraded in cytosol by prolyl hydroxylase (Maes et al., 2012; Min et al., 2015); when exposed to a low oxygen tension environment, HIF-1α begins to accumulate and translocate into nuclei to modulate downstream genes that may help relieve cellular hypoxia (Maes et al., 2012; Min et al., 2015). Therefore, both the amount of HIF-1α protein and its subcellular location can be employed as markers to evaluate cellular hypoxia. As shown in Figure 4C, under normoxic circumstances, no significant accumulation of HIF-1α was observed in cells. Following incubation under low oxygen tension (1% O2), the MC3T3-E1 cells exhibited enhanced nuclear HIF-1α staining. When the oxygen-generating CaO2 + MnO2@PLGA MPs were used, a significant proportion of the nuclear HIF-1α signal was eliminated in the cells that were exposed to low oxygen tension, suggesting that the developed CaO2 + MnO2@PLGA MPs may function as a local oxygen-evolving system effectively to relieve tissue hypoxia. According to the oxygen evolution profiles (Figures 1C, 2A) obtained using a dissolved oxygen sensor, the concentration of dissolved oxygen in the CaO2 + MnO2@PLGA MP-treated solution increased substantially, suggesting that the generated oxygen molecules can dissolve into aqueous solution. Hence, these dissolved oxygen molecules can diffuse freely in the culture medium and thus can be utilized by cells to relieve cellular hypoxia.

CaO2 + MnO2@PLGA MPs Promote Osteogenic Differentiation of MC3T3-E1 Cells Under Hypoxia

It has been widely reported that low oxygen tension has a significantly deleterious effect on fractural heading and new bone formation through the inhibition of osteogenic differentiation of osteoblasts (Salim et al., 2004; Lu et al., 2013; Yang et al., 2013; Lin et al., 2014; Liu et al., 2019). To evaluate whether the developed MPs possess the potential to promote osteogenesis of hypoxic bone tissue, preosteoblast MC3T3-E1 cells that were incubated under low oxygen tension (1% O2) and treated with ascorbic acid and β-glycerophosphate to induce osteogenic differentiation and test MPs for improving local oxygenation were employed as an in vitro model. Calcium mineral deposition identified by Alizarin red staining was used as an index to assess the degree of in vitro mineralization and thus the osteogenic differentiation of MC3T3-E1 cells (Kuo et al., 2016). Cells that were cultivated under normal (20% O2) or low (1% O2) oxygen tension without MP treatment were used as controls.

According to the results of Alizarin red staining, more orange-red precipitate, namely higher calcium deposition, was observed in the cells cultivated under normal oxygenated conditions when compared to that in hypoxic culture (Figure 5A), suggesting that the low oxygen tension could apparently impair the osteogenic differentiation capacity of MC3T3-E1 cells. In the group that received test MPs, however, the osteogenic differentiation potential was restored significantly (Figure 5A). These results were further supported by the levels of calcium accumulation quantified by measuring the optical density at 562 nm (Figure 5B). Together with the previous results, these findings suggest that the developed CaO2 + MnO2@PLGA MPs can be utilized to enhance the oxygenation and thus in vitro osteogenic differentiation of preosteoblasts under low oxygen tension.

FIGURE 5
www.frontiersin.org

Figure 5. Enhanced osteogenesis of hypoxic MC3T3-E1 cells by CaO2 + MnO2@PLGA MPs. (A) Representative images of Alizarin red staining and (B) corresponding quantitative results showing calcium deposited by MC3T3-E1 cells following various treatments. *p < 0.05; **p < 0.01; ****p < 0.001.

The CaO2 + MnO2@PLGA MPs Are Biocompatible

The developed CaO2 + MnO2@PLGA MPs were implanted subcutaneously by local injection to evaluate their biocompatibility. Animals that received empty MPs that were composed of only PLGA, which is generally regarded as a biocompatible material and has been approved for clinical use by the US Food and Drug Administration (Gentile et al., 2014), were used as controls. At 2 weeks after implantation, the MPs in both groups were integrated into the subcutaneous tissue without inducing macroscopic inflammation (Figure 6A). The images of H&E staining (Figure 6B) and the corresponding results of cell nuclei counting (Figure 6C) revealed that the CaO2 + MnO2@PLGA MPs exhibited a similar trend of host cell infiltration when compared to the control group (p > 0.05), suggesting that the encapsulation of 10 mg/mL CaO2 and 0.22 mg/mL MnO2 did not result in significant alternation of PLGA MP biocompatibility. Therefore, we speculate that the developed CaO2 + MnO2@PLGA MPs can be biocompatible as empty PLGA MPs.

FIGURE 6
www.frontiersin.org

Figure 6. In vivo biocompatibility assessment of CaO2 + MnO2@PLGA MPs. Representative (A) photographs and (B) H&E staining images of mouse skin tissue after subcutaneous injection of test MPs and (C) corresponding quantification of infiltrating cells. Asterisks indicate the implanted MPs or the spaced originally occupied by MPs. ns, not significant.

Conclusion

This study pursued to elucidate the relationship among the concentrations of each component used for CaO2 + MnO2@PLGA MP fabrication, the resultant oxygen release behaviors, and their corresponding cytotoxicity for the purpose of engineering an optimal injectable oxygen-generating carrier. A series of methodologies were used to evaluate the impacts of these parameters, and the obtained results evidently demonstrate that all the components of the MPs play crucial roles in modulating the oxygen release behavior and cytotoxicity, as measured by the dissolved oxygen concentration, pH value, H2O2 concentration, and cell viability. The resultant CaO2 + MnO2@PLGA MPs developed in this study could effectively relieve the hypoxia of MC3T3-E1 cells that were grown under low oxygen tension and promote their osteogenic differentiation, thus holding great promise in enhancing fractural healing by increasing tissue oxygenation.

Data Availability Statement

The datasets generated for this study are available on request to the corresponding author.

Ethics Statement

This animal study was reviewed and approved by Institutional Animal Care and Use Committee, National Tsing Hua University.

Author Contributions

T-EH, P-LL, and C-CH contributed to conception and design of the study. T-EH, S-JL, L-CC, and C-CC carried out the experimental work. T-EH, S-JL, L-CC, and C-CH perform the data analysis. P-LL and C-CH supervised the research design and wrote the manuscript. All authors approved the final version of the manuscript.

Funding

This work was supported by the Ministry of Science and Technology in Taiwan (MOST 109-2636-B-007-001; Young Scholar Fellowship Program), National Tsing Hua University (107Q2510E1 and 109Q2711E1), and Chang Gung Memorial Hospital-National Tsing Hua University Joint Research Program 2018 (CMRPG3H0211).

Conflict of Interest

The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.

Supplementary Material

The Supplementary Material for this article can be found online at: https://www.frontiersin.org/articles/10.3389/fbioe.2020.00511/full#supplementary-material

References

Ayuso, J. M., Virumbrales-Munoz, M., Lacueva, A., Lanuza, P. M., Checa-Chavarria, E., Botella, P., et al. (2016). Development and characterization of a microfluidic model of the tumour microenvironment. Sci. Rep. 6:36086. doi: 10.1038/srep36086

PubMed Abstract | CrossRef Full Text | Google Scholar

Chandra, P. K., Ross, C. L., Smith, L. C., Jeong, S. S., Kim, J., Yoo, J. J., et al. (2015). Peroxide-based oxygen generating topical wound dressing for enhancing healing of dermal wounds. Wound Repair Regen. 23, 830–841. doi: 10.1111/wrr.12324

PubMed Abstract | CrossRef Full Text | Google Scholar

Claes, L., Recknagel, S., and Ignatius, A. (2012). Fracture healing under healthy and inflammatory conditions. Nat. Rev. Rheumatol. 8, 133–143. doi: 10.1038/nrrheum.2012.1

PubMed Abstract | CrossRef Full Text | Google Scholar

Coronel, M. M., Geusz, R., and Stabler, C. L. (2017). Mitigating hypoxic stress on pancreatic islets via in situ oxygen generating biomaterial. Biomaterials 129, 139–151. doi: 10.1016/j.biomaterials.2017.03.018

PubMed Abstract | CrossRef Full Text | Google Scholar

Fan, Z., Xu, Z., Niu, H., Gao, N., Guan, Y., Li, C., et al. (2018). An injectable oxygen release system to augment cell survival and promote cardiac repair following myocardial infarction. Sci. Rep. 8:1371. doi: 10.1038/s41598-018-19906-w

PubMed Abstract | CrossRef Full Text | Google Scholar

Farris, A. L., Rindone, A. N., and Grayson, W. L. (2016). Oxygen delivering biomaterials for tissue engineering. J. Mater. Chem. B 4, 3422–3432. doi: 10.1039/C5TB02635K

PubMed Abstract | CrossRef Full Text | Google Scholar

Gentile, P., Chiono, V., Carmagnola, I., and Hatton, P. V. (2014). An overview of poly(lactic-co-glycolic) acid (PLGA)-based biomaterials for bone tissue engineering. Int. J. Mol. Sci. 15, 3640–3659. doi: 10.3390/ijms15033640

PubMed Abstract | CrossRef Full Text | Google Scholar

Gholipourmalekabadi, M., Zhao, S., Harrison, B. S., Mozafari, M., and Seifalian, A. M. (2016). Oxygen-generating biomaterials: a new, viable paradigm for tissue engineering? Trends Biotechnol. 34, 1010–1021. doi: 10.1016/j.tibtech.2016.05.012

PubMed Abstract | CrossRef Full Text | Google Scholar

Gómez-Barrena, E., Rosset, P., Lozano, D., Stanovici, J., Ermthaller, C., and Gerbhard, F. (2015). Bone fracture healing: cell therapy in delayed unions and nonunions. Bone 70, 93–101. doi: 10.1016/j.bone.2014.07.033

PubMed Abstract | CrossRef Full Text | Google Scholar

Harrison, B. S., Eberli, D., Lee, S. J., Atala, A., and Yoo, J. J. (2007). Oxygen producing biomaterials for tissue regeneration. Biomaterials 28, 4628–4634. doi: 10.1016/j.biomaterials.2007.07.003

PubMed Abstract | CrossRef Full Text | Google Scholar

Ho, S. S., Vollmer, N. L., Refaat, M. I., Jeon, O., Alsberg, E., Lee, M. A., et al. (2016). Bone morphogenetic protein-2 promotes human mesenchymal stem cell survival and resultant bone formation when entrapped in photocrosslinked alginate hydrogels. Adv. Healthc. Mater. 5, 2501–2509. doi: 10.1002/adhm.201600461

PubMed Abstract | CrossRef Full Text | Google Scholar

Huang, C.-C., Chia, W.-T., Chung, M.-F., Lin, K.-J., Hsiao, C.-W., Jin, C., et al. (2016). An implantable depot that can generate oxygen in situ for overcoming hypoxia-induced resistance to anticancer drugs in chemotherapy. J. Am. Chem. Soc. 138, 5222–5225. doi: 10.1021/jacs.6b01784

PubMed Abstract | CrossRef Full Text | Google Scholar

Kuo, Z.-K., Lai, P.-L., Toh, E. K.-W., Weng, C.-H., Tseng, H.-W., Chang, P.-Z., et al. (2016). Osteogenic differentiation of preosteoblasts on a hemostatic gelatin sponge. Sci. Rep. 6:32884. doi: 10.1038/srep32884

PubMed Abstract | CrossRef Full Text | Google Scholar

Lee, J. C., and Volpicelli, E. J. (2017). Bioinspired collagen scaffolds in cranial bone regeneration: from bedside to bench. Adv. Healthc. Mater. 6:1700232. doi: 10.1002/adhm.201700232

PubMed Abstract | CrossRef Full Text | Google Scholar

Lin, S.-S., Ueng, S. W. N., Niu, C.-C., Yuan, L.-J., Yang, C.-Y., Chen, W.-J., et al. (2014). Hyperbaric oxygen promotes osteogenic differentiation of bone marrow stromal cells by regulating Wnt3a/β-catenin signaling—an in vitro and in vivo study. Stem Cell Res. 12, 260–274. doi: 10.1016/j.scr.2013.10.007

PubMed Abstract | CrossRef Full Text | Google Scholar

Lin, Y.-J., Chen, C.-C., Chi, N.-W., Nguyen, T., Lu, H.-Y., Nguyen, D., et al. (2018). In situ self-assembling micellar depots that can actively trap and passively release NO with long-lasting activity to reverse osteoporosis. Adv. Mater. 30:e1705605. doi: 10.1002/adma.201705605

PubMed Abstract | CrossRef Full Text | Google Scholar

Liu, H. X., Yang, M. S., Wu, G. F., Yang, L. J., Cao, Y. L., Liu, C., et al. (2019). Effects of different oxygen concentrations on the proliferation, survival, migration, and osteogenic differentiation of MC3T3-E1 cells. Connect. Tissue Res. 60, 240–253. doi: 10.1080/03008207.2018.1487413

PubMed Abstract | CrossRef Full Text | Google Scholar

Lu, C., Saless, N., Wang, X., Sinha, A., Decker, S., Kazakia, G., et al. (2013). The role of oxygen during fracture healing. Bone 52, 220–229. doi: 10.1016/j.bone.2012.09.037

PubMed Abstract | CrossRef Full Text | Google Scholar

Maes, C., Carmeliet, G., and Schipani, E. (2012). Hypoxia-driven pathways in bone development, regeneration and disease. Nat. Rev. Rheumatol. 8, 358–366. doi: 10.1038/nrrheum.2012.36

PubMed Abstract | CrossRef Full Text | Google Scholar

Min, Z., Shichang, Z., Chen, X., Yufang, Z., and Changqing, Z. (2015). 3D-printed dimethyloxallyl glycine delivery scaffolds to improve angiogenesis and osteogenesis. Biomater. Sci. 3, 1236–1244. doi: 10.1039/c5bm00132c

PubMed Abstract | CrossRef Full Text | Google Scholar

Newland, H., Eigel, D., Rosser, A. E., Werner, C., and Newland, B. (2018). Oxygen producing microscale spheres affect cell survival in conditions of oxygen-glucose deprivation in a cell specific manner: Implications for cell transplantation. Biomater. Sci. 6, 2571–2577. doi: 10.1039/c8bm00490k

PubMed Abstract | CrossRef Full Text | Google Scholar

Oh, S. H., Ward, C. L., Atala, A., Yoo, J. J., and Harrison, B. S. (2009). Oxygen generating scaffolds for enhancing engineered tissue survival. Biomaterials 30, 757–762. doi: 10.1016/j.biomaterials.2008.09.065

PubMed Abstract | CrossRef Full Text | Google Scholar

Park, S., and Park, K. M. (2018). Hyperbaric oxygen-generating hydrogels. Biomaterials 182, 234–244. doi: 10.1016/j.biomaterials.2018.08.032

PubMed Abstract | CrossRef Full Text | Google Scholar

Park, S. M., Lee, S. J., Lim, J., Kim, B. C., Han, S. J., and Kim, D. S. (2018). Versatile fabrication of size and shape-controllable nanofibrous concave microwells for cell spheroid formation. ACS Appl. Mater. Interfaces 10, 37878–37885. doi: 10.1021/acsami.8b15821

PubMed Abstract | CrossRef Full Text | Google Scholar

Pedraza, E., Coronel, M. M., Fraker, C. A., Ricordi, C., and Stabler, C. L. (2012). Preventing hypoxia-induced cell death in beta cells and islets via hydrolytically activated, oxygen-generating biomaterials. Proc. Natl. Acad. Sci. U.S.A. 109, 4245–4250. doi: 10.1073/pnas.1113560109

PubMed Abstract | CrossRef Full Text | Google Scholar

Peng, J., Dong, M., Ran, B., Li, W., Hao, Y., Yang, Q., et al. (2017). “One-for-all”-type, biodegradable prussian blue/manganese dioxide hybrid nanocrystal for trimodal imaging-guided photothermal therapy and oxygen regulation of breast cancer. ACS Appl. Mater. Interfaces 9, 13875–13886. doi: 10.1021/acsami.7b01365

PubMed Abstract | CrossRef Full Text | Google Scholar

Salim, A., Nacamuli, R. P., Morgan, E. F., Giaccia, A. J., and Longaker, M. T. (2004). Transient changes in oxygen tension inhibit osteogenic differentiation and Runx2 expression in osteoblasts. J. Biol. Chem. 279, 40007–40016. doi: 10.1074/jbc.M403715200

PubMed Abstract | CrossRef Full Text | Google Scholar

Schneider, C. A., Rasband, W. S., and Eliceiri, K. W. (2012). Nih image to imagej: 25 years of image analysis. Nat. Methods 9, 671–675. doi: 10.1038/nmeth.2089

PubMed Abstract | CrossRef Full Text | Google Scholar

Steg, H., Buizer, A. T., Woudstra, W., Veldhuizen, A. G., Bulstra, S. K., Grijpma, D. W., et al. (2015). Control of oxygen release from peroxides using polymers. J. Mater. Sci. Mater. Med. 26, 207. doi: 10.1007/s10856-015-5542-z

PubMed Abstract | CrossRef Full Text | Google Scholar

Stone, L. L. H., Chappuis, E., Marquez, M., McFalls, E. O., Kelly, R. F., and Butterick, T. (2019). Mitochondrial respiratory capacity is restored in hibernating cardiomyocytes following co-culture with mesenchymal stem cells. Cell Med. 11, 1–7. doi: 10.1177/2155179019834938

CrossRef Full Text | Google Scholar

Sun, H. L., Kim, J. K., Mortensen, R., Mutyaba, L. P., Hankenson, K. D., and Krebsbach, P. H. (2013). Osteoblast-targeted suppression of PPARγ increases osteogenesis through activation of mTOR signaling. Stem Cells 31, 2183–2192. doi: 10.1002/stem.1455

PubMed Abstract | CrossRef Full Text | Google Scholar

Teotia, A. K., Gupta, A., Raina, D. B., Lidgren, L., and Kumar, A. (2016). Gelatin-modified bone substitute with bioactive molecules enhance cellular interactions and bone regeneration. ACS Appl. Mater. Interfaces 8, 10775–10787. doi: 10.1021/acsami.6b02145

PubMed Abstract | CrossRef Full Text | Google Scholar

Wang, J., Zhu, Y., Bawa, H. K., Ng, G., Wu, Y., Libera, M., et al. (2011). Oxygen-generating nanofiber cell scaffolds with antimicrobial properties. ACS Appl. Mater. Interfaces 3, 67–73. doi: 10.1021/am100862h

PubMed Abstract | CrossRef Full Text | Google Scholar

Wang, X., Wu, X., Xing, H., Zhang, G., Shi, Q., Lingling, E., et al. (2017). Porous nanohydroxyapatite/collagen scaffolds loading insulin PLGA particles for restoration of critical size bone defect. ACS Appl. Mater. Interfaces 9, 11380–11391. doi: 10.1021/acsami.6b13566

PubMed Abstract | CrossRef Full Text | Google Scholar

Wang, Y.-T., Lu, A.-H., Zhang, H.-L., and Li, W.-C. (2011). Synthesis of nanostructured mesoporous manganese oxides with three-dimensional frameworks and their application in supercapacitors. J. Phys. Chem. C 115, 5413–5421. doi: 10.1021/jp110938x

CrossRef Full Text | Google Scholar

Ward, C. L., Corona, B. T., Yoo, J. J., Harrison, B. S., and Christ, G. J. (2013). Oxygen generating biomaterials preserve skeletal muscle homeostasis under hypoxic and ischemic conditions. PLoS ONE 8:e72485. doi: 10.1371/journal.pone.0072485

PubMed Abstract | CrossRef Full Text | Google Scholar

Yang, L. J., Zhu, L. X., Dong, W. R., Cao, Y. L., and Rong, Z. J. (2013). Oxygen-generating scaffolds: a new strategy for bone tissue engineering. Bone 57, 322–323. doi: 10.1016/j.bone.2013.07.034

PubMed Abstract | CrossRef Full Text | Google Scholar

Zeitouni, S., Krause, U., Clough, B. H., Halderman, H., Falster, A., Blalock, D. T., et al. (2012). Human mesenchymal stem cell-derived matrices for enhanced osteoregeneration. Sci. Transl. Med. 4:132ra155. doi: 10.1126/scitranslmed.3003396

PubMed Abstract | CrossRef Full Text | Google Scholar

Zheng, Z., Yin, W., Zara, J. N., Li, W., Kwak, J., Mamidi, R., et al. (2010). The use of BMP-2 coupled -nanosilver-PLGA composite grafts to induce bone repair in grossly infected segmental defects. Biomaterials 31, 9293–9300. doi: 10.1016/j.biomaterials.2010.08.041

PubMed Abstract | CrossRef Full Text | Google Scholar

Keywords: hypoxia, hypoxia-inducible factor, oxygen-generating biomaterials, peroxide, PLGA microparticles

Citation: Hsieh T-E, Lin S-J, Chen L-C, Chen C-C, Lai P-L and Huang C-C (2020) Optimizing an Injectable Composite Oxygen-Generating System for Relieving Tissue Hypoxia. Front. Bioeng. Biotechnol. 8:511. doi: 10.3389/fbioe.2020.00511

Received: 02 March 2020; Accepted: 30 April 2020;
Published: 26 May 2020.

Edited by:

Bin Li, Soochow University, China

Reviewed by:

Xing Zhang, Institute of Metals Research (CAS), China
ZuFu Lu, University of Sydney, Australia

Copyright © 2020 Hsieh, Lin, Chen, Chen, Lai and Huang. This is an open-access article distributed under the terms of the Creative Commons Attribution License (CC BY). The use, distribution or reproduction in other forums is permitted, provided the original author(s) and the copyright owner(s) are credited and that the original publication in this journal is cited, in accordance with accepted academic practice. No use, distribution or reproduction is permitted which does not comply with these terms.

*Correspondence: Po-Liang Lai, polianglai@gmail.com; Chieh-Cheng Huang, chiehcheng@mx.nthu.edu.tw

Disclaimer: All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article or claim that may be made by its manufacturer is not guaranteed or endorsed by the publisher.