Lingmin Xu
Yana Shang*Jinhong YangZhenyi ChenFufei PangHuanhuan LiuYanhua DongNa ChenJianxiang WenTingyun Wang- Key Laboratory of Specialty Fiber Optics and Optical Access Networks, Joint International Research Laboratory of Specialty Fiber Optics and Advanced Communication, Shanghai Institute for Advanced Communication and Data Science, Shanghai University, Shanghai, China
A unique orbital angular momentum (OAM) optical amplifier based on a ring-core fiber doped with lead sulfide (PbS) is realized for the first time in this study. The PbS-doped ring-core fiber is fabricated using the modified chemical vapor deposition method. The cross-sectional microscope image of the fiber is obtained. The difference in the refractive index between the ring core and the fiber cladding measured by a three-dimensional refractive index tester reaches 1%. The sulfur and lead content in the ring-core of the PbS-doped ring-core fiber is confirmed by energy spectrum analysis. A first-order OAM optical amplifier is built based on the PbS-doped ring-core fiber. The experiment confirms that the air-hole PbS-doped ring-core fiber can support the OAM |l| = 1 modes. In addition, 2.3 dB of on–off gain is obtained for the OAM |l| = 1 modes at 1,550 nm. The fluorescence spectrum obtained using the backward pumping method ranges from 1,100 to 1,600 nm.
Introduction
Mode division multiplexing (MDM) can be used to considerably expand the capacity of optical communications by using orthogonal modes to transmit signals [1, 2]. In 2004, a new MDM communication scheme based on the photon orbital angular momentum (OAM) was proposed [3]. The initial studies had focused on the transmission of OAM modes in free space and suffered from short transmission distances. Since 2009, the index separation between adjacent OAM vector modes has been considerably enhanced by ring-core optical fiber structures [4–10]. In 2013, Bozinovic et al. [11] implemented OAM mode multiplexing in a ring-core optical fiber with a length of more than 1.1 km. This shows that OAM can provide additional options for data multiplexing in future fiber optic networks. A variety of OAM amplifiers based on erbium-doped fibers have been theoretically designed [12–14] to address the unavoidable signal-transmission loss in long-distance communications. In the year 2017, Jung et al. [15] built the air-hole erbium-doped fiber amplifier (EDFA) to amplify the OAM |l| = 1 modes for the first time. The gain of the OAM |l| = 1 modes with a cladding pump was up to 15.7 dB for the wavelength ranging from 1,545 to 1,600 nm. Xing et al. [16] used the erbium-doped few-mode fiber to build the all-fiber amplifier and realized the first-order OAM mode amplification in the year 2018, and the gain was 37.2 dB.
However, the bandwidth of EDFA cannot cover the entire communication band of the OH-free silica fiber. Therefore, an alternative active material is proposed for optical fiber amplifiers [17–19]. Because lead-sulfide (PbS) quantum dots have strong quantum-confined effects, the luminescence center of PbS quantum dots ranges from 1,000 to 1,800 nm, which is sufficient to realize the tunable photoluminescence in the near-infrared [20, 21]. PbS nanomaterials have great application prospects in optical amplifiers, lasers [22, 23], and sensors. The optical-gain performance has been observed in a glass medium doped using PbS quantum dots [24, 25]. The amplification in PbS quantum dot-doped fibers in common communication bands has been considerably enhanced through improvements in various PbS-based doping methods [26–30]. In the year 2018, Huang et al. [31] presented a new method, named “melt-in-tube,” for preparing PbS quantum dot doped fiber. The PbS quantum dots with diameters from 1.0 to 5.0 nm were uniformly precipitated in the PbS quantum-dots doped glass fiber core. However, the fiber loss was considerable, i.e., >14 dB/m.
In this study, we realize the amplification of the first-order OAM, which is based on an air-hole PbS-doped ring-core fiber. The fiber is fabricated using the modified chemical vapor deposition (MCVD) technology. The fluorescence spectrum ranges from 1,100 to 1,600 nm. Under the pumping of a 980 nm laser, the on–off gain (up to 2.3 dB) of the OAM |l| = 1 modes with a signal light at 1,550 nm could be achieved.
Design and Fabrication of Air-Hole PbS-Doped Fiber
Preparation of Optical Fiber
A considerable number of studies and experiments have shown that the effective index separation of OAM modes should be >10−4 to support OAM mode transmission in the long haul. This can be realized by introducing a high index ring into the traditional fiber structure [5].
In this study, PbS powder is doped into the ring core of the fiber to support the transmission and amplification of OAM modes. An air-hole ring-core fiber doped using PbS is fabricated via MCVD. The process involved the following steps: First, SiCl4 and GeCl4 are carried by high-purity oxygen into a silica substrate tube, along with PbS, which is vaporized by high-temperature heating. Second, the porous soot layer is deposited on the inner surface of the substrate tube. Third, at a high temperature of 2,000°C, the silica substrate tube is disposed via a vitrification process and collapsed into a PbS-doped optical fiber preform. Finally, the preform is drawn into an air-hole PbS-doped ring-core fiber with certain geometric parameters by using a drawing tower. During the drawing process, the structural parameters of the optical fiber can be controlled by the temperature of drawing, the preform feeding speed and the drawing speed.
The cross-sectional image of the fabricated fiber is observed via optical microscopy, and the refractive index profile of the fiber can be measured using a three-dimensional refractive-index tester (Model: SHR-1602, Shanghai University, China). As depicted in Figure 1, the interior of the ring has a diameter of 9.80 μm and is filled with air. The external diameter of the ring is 20.49 μm, and the thickness of the ring is 5.35 μm. In addition, the diameter of the cladding is 130.22 μm. The refractive-index difference between the ring and cladding of the fiber reaches 1% (the gray part in Figure 1 represents the air hole filled using index-matching oil). The total length of the sample fiber is about 60 m. The loss of the fiber at 1,500–1,570 nm is about 19 dB.
Figure 1. Refractive index profile of the fiber and the cross-sectional microscope image of the fiber.
Mode Simulation
The RF module of COMSOL software is used to simulate the waveguide mode of optical fiber. The amplitude of the field decays rapidly as a function of the cladding radius. The cladding radius of the sample fiber is large enough for the field of the confined modes to reach zero at the exterior boundaries. This constitutes a valid boundary condition. Parameters such as the refractive index, cladding radius, ring core radius, and air hole radius of the sample optical fiber are set in the simulation. In addition, we use triangular grids to divide each part of the optical fiber. The region of air hole, ring core and cladding are divided into 148, 230, and 2,028 grids, respectively. Thus, the HE11, TE01, TM01, HE21, HE31, EH11, HE51, and EH31 vector modes transmitted by the fabricated PbS-doped ring-core fiber can be analyzed using the COMSOL software. The effective indexes of the modes are listed in Table 1. The effective index separation of the OAM |l| = 1 modes is 0.65 × 10−4, via calculation.
Table 1. Effective index.
Characterization Analysis and Fluorescence Spectrum of Optical Fiber
Energy-spectrum analysis is used to prove that the PbS material is successfully doped in the fiber. The element content in the three points indicated on the high-index ring depicted in Figure 2 are analyzed and the results are shown in Table 2. It can be seen that in each of the selected regions, there exist the elements of Si, O, C, Pb, S, and Ge, thereby indicating that PbS is successfully doped into the air-hole ring-core fiber. However, the contents of elements Pb and S are different in different regions, indicating that the doping concentration of the PbS material is not uniform during the fiber-fabrication process.
Figure 2. Cross-sectional scanning electron microscope image of the optical fiber.
Table 2. Element content analysis results.
The fluorescence spectrum of the optical fiber is measured using the backward pumping method. A 980 nm laser is selected as the pump light source. Figure 3 shows the fluorescence spectra of the fiber measured using an optical spectrum analyzer under various pump powers ranging from 100 to 700 mW. The fluorescence spectra ranges from 1,100 to 1,600 nm. In addition, the fluorescence intensity gradually increases with the pump power. The fluorescence intensity increases by only a small amount when the pump power increases from 600 to 700 mW, and is almost unchanged and tends toward saturation when the pump power is further increased.
Figure 3. Fluorescence spectrum of the fiber.
OAM Mode Generation and Amplification
An amplification system for the OAM |l| = 1 modes is built using the fabricated fiber. The experimental setup is depicted in Figure 4. The Gaussian signal light is split into two beams using a 1 × 2 coupler. The first beam serves as an interference spherical reference beam. The second beam is converted into a vortex beam using a spiral phase plate. Both the signal light and pump light are coupled into the fabricated fiber using the DM. The OAM |l| = 1 modes are successfully amplified subsequently. In addition, the beam profiles of the first-order vortex beam and the interference could be observed using an infrared camera. The DM before the infrared camera is used to filter out the pump light.
Figure 4. Setup of the OAM amplifier [a, polarization controller; b, collimator; c, spiral phase plate; d, quarter-wave plate; e, lens; f, dichroic mirror (DM); g, objective; h, beam-splitter; i, linear polarizers; j, right-angle prism mirror].
The beam profile of the OAM |l| = 1 modes before entering the optical fiber input is depicted in Figure 5A, and their interference pattern in Figure 5B. The beam profile and the interference after exiting the output side of the air-hole PbS-doped ring-core fiber are depicted in Figures 5C,D, respectively. The interference with the spherical reference wave in Figure 5B proves that the OAM |l| = 1 modes are successfully generated by the spiral phase plate. The beam profile maintained the form of a complete ring after exiting the output side of the fiber, as depicted in Figure 5C. A dextral spiral interference fringe is formed when the beam exiting the output side of the fiber interfered with the spherical reference beam, as depicted in Figure 5D. It indicates that the optical fiber could successfully support the |l| = 1 OAM modes.
Figure 5. (A) Beam profile before entering the input side of the fiber. (B) Interference before entering the input side of the fiber. (C) Beam profile after exiting the output side of the fiber. (D) Interference after exiting the output side of the fiber.
The on-off gain of a fiber is defined as the ratio of the signal output to input power [32, 33]. In this paper, the signal power without the pump is taken as the input power and the signal power with the pump as the output power. The gray values measured by the near-infrared camera under different pump powers responses the signal intensity. The same test area (the strip is depicted as a green line in Figure 6A) is used throughout the experiment so that the on-off gain of the optical fiber could be obtained from the gray values. To analyze the on–off gain of the ring-core PbS-doped fiber, the intensity is measured across a strip passing through the center depicted as a green line in Figure 6A. The intensity values gradually increased as the pump power increased from 0 to 750 mW. The on–off gains could be calculated from the intensities. The on–off gains of the OAM |l| = 1 modes at various pump powers are shown in Figure 6B. The on–off gain of the OAM11 mode reaches 2.3 dB when the pump power is 750 mW. The small on-off gain of the fiber is mainly attributed to the low PbS doping concentration.
Figure 6. (A) Intensity on the green line. (B) On–off gain on the green line.
Conclusion
We experimentally doped the PbS into a ring-core fiber by using the MCVD method to realize the amplification of the OAM11 mode. The refractive index difference between the cladding and ring core of the fiber is 1%. The fluorescence spectrum of the fiber ranges from 1,100 to 1,600 nm, which is considerably larger than that of erbium-doped fibers and indicates that the fiber can be applied in wide-band amplification systems. This fiber not only supported the transmission of the OAM11 mode but also amplified the mode. The on–off gain of the OAM11 reaches up to 2.3 dB at 750 mW 980 nm pumping. The experiment can be optimized in the following two aspects to extend the applicability of the fiber to higher-order OAM modes: Firstly, a spatial light modulator can be used to replace the helical phase plate, so that the order of the OAM modes generated can be adjusted by the spatial light modulator. Secondly, increasing the refractive index difference between the core and the cladding appropriately can enhance the effective refractive index difference of the OAM modes and increase the number of OAM modes transmitted. In addition, the gain can be enhanced by optimizing the fiber fabrication technology to increase the PbS concentration. This type of PbS-doped ring-core optical fiber amplifier provides the possibility of realizing ultra-wideband OAM mode amplification in future all-fiber transmission systems.
Data Availability Statement
All datasets generated for this study are included in the article/supplementary material.
Author Contributions
FP and YS contributed to the conception of the study. LX contributed to conceive and design the experiments, analyzed the data, and wrote the manuscript. LX, JY, YD, and ZC contributed to perform the experiments. HL, NC, JW, and TW helped perform the analysis with constructive discussions.
Funding
This project was funded by National key research and development program of China (2018YFB1801800) and the program of National Natural Science Foundation of China (61675125, 61875118, 61635006, 61705126, and 61975113). The project was also supported by 111 Project (D20031).
Conflict of Interest
The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.
Acknowledgments
We would like to thank Editage (www.editage.cn) for English language editing.
References
1. Jung Y, Lim EL, Kang Q, May-Smith TC, Wong NHL, Standish R, et al. Cladding pumped few-mode EDFA for mode division multiplexed transmission. Opt Express. (2014) 22:29008–13. doi: 10.1364/OE.22.029008
2. Jain S, Jung Y, May-Smith TC, Alam SU, Sahu JK, Richardson DJ. Few-mode multi-element fiber amplifier for mode division multiplexing. Opt Express. (2014) 22:29031–6. doi: 10.1364/OE.22.029031
3. Gibson G, Courtial J, Padgett MJ, Vasnetsov M, Pas'ko V, Barnett SM, et al. Free-space information transfer using light beams carrying orbital angular momentum. Opt Express. (2004) 12:5448–56. doi: 10.1364/OPEX.12.005448
4. Ramachandran S, Kristensen P, Yan MF. Generation and propagation of radially polarized beams in optical fiber. Opt Lett. (2009) 34:2525–7. doi: 10.1364/OL.34.002525
5. Golowich SE, Kristensen P, Bozinovic N, Gregg P, Ramachandran S. Fibers supporting orbital angular momentum states for information capacity scaling. In: Frontiers in Optics. Rochester, NY (2012). p. FW2D.
6. Huang G, Zhou S, Qin Y, Xue L, Man Y. Modal characteristics analysis of orbital angular momentum in a modified ring fiber. Laser Optoelectron Progress. (2015) 52:080604. doi: 10.3788/LOP52.080604
7. Ramachandran S, Gregg P, Kristensen P, Golowich SE. On the scalability of ring fiber designs for OAM multiplexing. Opt Express. (2015) 23:3721–30. doi: 10.1364/OE.23.003721
8. Brunet C, Ung B, Wang L, Messaddeq Y, LaRochelle S, Rusch LA. Design of a family of ring-core fibers for OAM transmission studies. Opt Express. (2015) 23:10553–63. doi: 10.1364/OE.23.010553
9. Gregg P, Kristensen P, Ramachandran S. OAM stability in fiber due to angular momentum conservation. In: Conference on Lasers and Electro-Optics. San Jose, CA (2014). SM2N.2. doi: 10.1364/CLEO_SI.2014.SM2N.2
10. Bozinovic N, Kristensen P, Ramachandran S. Are orbital angular momentum (OAM/Vortex) states of light long-lived in fibers? In: FIO/LS: Technical Digest. San Jose, CA (2011). p. LWL3.
11. Bozinovic N, Yue Y, Ren Y, Tur M, Kristensen P, Huang H, et al. Terabit-scale orbital angular momentum mode division multiplexing in fibers. Science. (2013) 340:1545–8. doi: 10.1126/science.1237861
12. Ma J, Xia F, Li S, Wang J. Design of orbital angular momentum (OAM) erbium doped fiber amplifier with low differential modal gain. In: Optical Fiber Communications Conference and Exhibition (OFC). Los Angeles, CA (2015). p. W2A.40.
13. Kang Q, Gregg P, Jung Y, Lim EL, Shaif-Ul A, Ramachandran S, et al. Amplification of 12 OAM states in an air-core EDF. In: Optical Fiber Communications Conference and Exhibition (OFC). Los Angeles, CA (2015). p. Tu3C.2.
14. Liu J, Wang H, Chen S, Zheng S, Zhu L, Wang A, et al. Demonstration of orbital angular momentum (OAM) fiber amplifier in data-carrying OAM-division multiplexing and wavelength-division multiplexing (WDM) system. Optical Fiber Communications Conference and Exhibition (OFC). Los Angeles, CA (2017). p. W2A.21.
15. Jung Y, Kang Q, Raghuraman S, Daryl H, Yoo S, Gregg P, et al. Optical orbital angular momentum amplifier based on an air-hole erbium-doped fiber. J Lightw Technol. (2017) 35:430–6. doi: 10.1109/JLT.2017.2651145
16. Xing J, Wen J, Wang J, Pang F, Chen Z, Liu Y, et al. All-fiber linear polarization and orbital angular momentum modes amplifier based on few-mode erbium-doped fiber and long period fiber grating. Chinese Opt Lett. (2018) 16:100604. doi: 10.3788/COL201816.100604
17. Jiangjiang F, Xiaohui L, Zhaojiang S, Chuang Z, Xuwei L, Deying L, et al. 2D ductile transition metal chalcogenides (TMCs): novel high-performance Ag2S nanosheets for ultrafast photonics. Adv Opt Mater. (2020) 8:1901762. doi: 10.1002/adom.201901762
18. Liu J, Li X, Guo Y, Qyyum A, Shi Z, Feng T, et al. SnSe2 nanosheets for subpicosecond harmonic mode-locked pulse generation. Small. (2019) 15:1902811. doi: 10.1002/smll.201902811
19. Zhao Y, Guo P, Li X, Jin Z. Ultrafast photonics application of graphdiyne in the optical communication region. Carbon. (2019) 149:336–41. doi: 10.1016/j.carbon.2019.04.075
20. Liu C, Heo J. Lead chalcogenide quantum dot-doped glasses for photonic devices. Int J Appl Glass Sci. (2013) 4:163–73. doi: 10.1111/ijag.12032
21. Tong X, Zhou Y, Jin L, Basu K, Adhikari R, Selopal GS, et al. Heavy metal-free, near-infrared colloidal quantum dots for efficient photoelectrochemical hydrogen generation. Nan Ene. (2017) 31:441–9. doi: 10.1016/j.nanoen.2016.11.053
22. Zhang Y, Li X, Qyyum A, Feng T, Guo P, Jiang J, et al. PbS nanoparticles for ultrashort pulse generation in optical communication region. Particle Particle Syst Charact. (2018) 35:1800341. doi: 10.1002/ppsc.201800341
23. Zhang Y, Li X, Qyyum A, Feng T, Guo P, Jiang J. Lead sulfide nanoparticles for dual-wavelength ultrashort pulse generation. Nanotechnology. (2019) 31:085202. doi: 10.1088/1361-6528/ab53b4
24. Wundke K, Auxier J, Schülzgen A, Peyghambarian N, Borrelli NF. Room-temperature gain at 1.3 μm in PbS-doped glasses. Appl Phys Lett. (1999) 75:3060–2. doi: 10.1063/1.125230
25. Heo J, Liu C. Pbs quantum-dots in glass matrix for universal fiber-optic amplifier. J Mater Sci Mater Electron. (2007) 18:135–9. doi: 10.1007/s10854-007-9172-1
26. Pang F, Sun X, Guo H, Yan J, Wang J, Zeng X, et al. A PbS quantum dots fiber amplifier excited by evanescent wave. Opt Express. (2010) 18:14024–30. doi: 10.1364/OE.18.014024
27. Wu Y, Shang Y, Kang Y, Pang F, Wen J, Chen N, et al. Tapered optical fiber deposited with PbS as an optical fiber amplifier based on atomic layer deposition. Opt Eng. (2018) 57:1. doi: 10.1117/1.OE.57.6.066102
28. Shen K, Baig S, Jiang G, Paik Y-h, Kim SJ, Wang MR. Improved light emitting UV curable PbS quantum dots-polymer composite optical waveguides. Opt Commun. (2017) 402:606–11. doi: 10.1016/j.optcom.2017.06.083
29. Cheng C, Wu C. PbS quantum-dot-doped fiber amplifier in NIR S-C-L ultra-broad waveband with low noise. Acta Opt Sin. (2018) 38:1006006. doi: 10.3788/AOS201838.1006006
30. Shang Y, Wen J, Dong Y, Zhan H, Luo Y, Peng G, et al. Luminescence properties of PbS quantum-dot-doped silica optical fibre produced via atomic layer deposition. J Lumin. (2017) 187:201–4. doi: 10.1016/j.jlumin.2017.03.009
31. Huang X, Fang Z, Kang S, Peng W, Dong G, Zhou B, et al. Controllable fabrication of novel all solid-state PbS quantum dot-doped glass fibers with tunable broadband near-infrared emission. J Mater Chem C. (2017) 5:7927–34. doi: 10.1039/C7TC02623D
32. Zheng J, Dong Y, Pan X, Wen J, Chen Z, Pang F, et al. Ultra-wideband and flat-gain optical properties of the PbS quantum dots-doped silica fiber. Opt Express. (2019) 27:37900–9. doi: 10.1364/OE.27.037900
Keywords: optical fiber amplifier, PbS-doped ring-core fiber, orbital angular momentum (OAM), on–off gain, fluorescence properties
Citation: Xu L, Shang Y, Yang J, Chen Z, Pang F, Liu H, Dong Y, Chen N, Wen J and Wang T (2020) Orbital Angular Momentum Optical Amplifier Based on PbS-Doped Ring-Core Fiber. Front. Phys. 8:198. doi: 10.3389/fphy.2020.00198
Received: 17 March 2020; Accepted: 04 May 2020;
Published: 03 June 2020.
Edited by:
Xiaohui Li, Shaanxi Normal University, ChinaReviewed by:
Yang Yue, Nankai University, ChinaGuobin Ren, Beijing Jiaotong University, China
Yongkang Gong, Cardiff University, United Kingdom
Copyright © 2020 Xu, Shang, Yang, Chen, Pang, Liu, Dong, Chen, Wen and Wang. This is an open-access article distributed under the terms of the Creative Commons Attribution License (CC BY). The use, distribution or reproduction in other forums is permitted, provided the original author(s) and the copyright owner(s) are credited and that the original publication in this journal is cited, in accordance with accepted academic practice. No use, distribution or reproduction is permitted which does not comply with these terms.
*Correspondence: Yana Shang, ynshang@shu.edu.cn