Magnesium Nanoparticles With Pd Decoration for Hydrogen Storage

In this work, Magnesium nanoparticles with Pd decoration, ranging from 40 to 70 nm, were successfully coprecipitated from tetrahydrofuran (THF) solution, assigned as the Mg–Pd nanocomposite. The Mg–Pd nanocomposite exhibits superior hydrogen storage properties. For the hydrogenated Mg–Pd nanocomposite at 150°C, the onset dehydrogenation temperature is significantly reduced to 216.8°C, with a lower apparent activation energy for dehydrogenation of 93.8 kJ/mol H₂. High-content γ-MgH₂ formed during the hydrogenation process, along with PH_0.706, contributes to the enhancing of desorption kinetics. The Mg–Pd nanocomposite can take up 3.0 wt% hydrogen in 2 h at a temperature as low as 50°C. During lower hydrogenation temperatures, Pd can dissociate hydrogen and create a hydrogen diffusion pathway for the Mg nanoparticles, leading to the decrease of the hydrogenation apparent activation energy (44.3 kJ/mol H₂). In addition, the Mg–Pd alloy formed during the hydrogenation/dehydrogenation process can play an active role in the reversible metal hydride transformation, destabilizing the MgH₂.

Introduction

Magnesium hydride has been favorable to be applied foreground in onboard hydrogen storage systems, due to its high gravimetric hydrogen storage capacity (7.6 wt%), natural abundance, and good reversibility. Unfortunately, pure MgH₂ shows slow sorption kinetics and high thermodynamic stability regarding the covered surface oxide layer and the low diffusion coefficient for H (Pistidda et al., 2014; Crivello et al., 2016; Yartys et al., 2019). In order to overcome these drawbacks of MgH₂ for practical applications, numerous studies attempted to enhance the hydrogen storage performance of MgH₂, such by as alloying Mg with other elements to alter the thermodynamic stability, doping with additives or catalysts, and reducing Mg particles to nano scale. “Nanosize effect” has been considered as an approach with the potential of leading to improvements in both kinetics and thermodynamics (Schneemann et al., 2018), which is based on (i) a larger surface area and thus more hydrogen dissociation sites (ii) the shortened hydrogen diffusion distances which in turn enhance kinetics, and (iii) the increased number of atoms at grain boundaries to enhance the hydrogen diffusion rates (Yao et al., 2011; Schneemann et al., 2018; Sun et al., 2018). Recently, an adapted Rieke method has emerged as an alternative to synthesize Mg nanoparticles to dramatically enhance the hydrogen sorption kinetics of Mg. For instance, Jeon et al. (2011) reported the synthesis of air-stable Mg nanoparticles (~4.9 nm) embedded in PMMA matrix, which enable both the storage of a high hydrogen capacity and rapid kinetics. Norberg et al. (2011) prepared Mg nanoparticles with controllable sizes by a similar method, and the ab-/desorption hydrogen kinetics were proven to be dramatically faster for nanoparticles with smaller sizes, as a result of the increase of the defect density formed in smaller nanoparticles. Recently, we have investigated that the Mg–TM (TM = Ni, Ti, Fe, Co, and V) nanocomposites can be coprecipitated from solution, in which the coprecipitated Ni, Ti, Fe, V, or Co has high catalytic efficiency in improvement of the ab-/desorption hydrogen kinetics of Mg nanoparticles (Liu et al., 2014a,b, 2015). The adapted Rieke method is considered as a better method for the preparation of nano-sized Mg with controllable sizes, and which can dope transition metal catalysts into a Mg/MgH₂ system by a simple chemical route. With regard to the nanoscaling, various catalysts for improving the hydrogen storage properties of MgH₂ have been investigated, such as transition metals/metal oxides/halogenides (Ma et al., 2009, 2013; Cui et al., 2014; Rizo-Acosta et al., 2018; Zhang et al., 2018; Liu et al., 2019b), rare earth metal oxides/halogenides (Singh et al., 2013; Lin et al., 2014, 2015; Wang et al., 2015), carbon materials (Lukashev et al., 2006; Liu et al., 2013; Rather et al., 2016), and other hydrides (Lu et al., 2010; Terent'ev et al., 2015; Jangir et al., 2018). In addition, some noble metals, such as Pd, have been reported to be effective for facilitating hydrogenation of MgH₂ (Du et al., 2007; Callini et al., 2010; Ham et al., 2013; Chung et al., 2015; Liu et al., 2019a). Liu et al. (2019a) reported that elemental Pd played a dominant role in accelerating the preferential diffusion of hydrogen atoms at the Pd/Mg interface, during the hydrogenation process. Callini et al. (2009) suggested the occurrence of Mg-alloying as a path for subsequent feasible H-exchange, when Pd was deposited on top of a thick MgO layer surrounding the Mg NPs core. Du et al. (2007) reported that the Pd-dopant provides a much lower activation barrier for both dissociation of molecular hydrogen and diffusion of atomic hydrogen on the Mg surface, based on ab initio density functional theory calculations.

Inspired by the above considerations, a Mg–Pd nanocomposite was coprecipitated from THF solution. The Mg nanoparticles were homogeneously decorated with nano-sized Pd. The hydrogen sorption properties were investigated, and the catalytic mechanisms of Pd were also proposed.

Materials and Methods

Sample Preparation

As early as in 1972, Rieke et al. reported a general procedure for the preparation of highly reactive magnesium metal, which was prepared by reducing a magnesium halide with alkali metal in an ethereal solvent (Rieke and Hudnall, 1972). In this work, anhydrous MgCl₂, PdCl₂, lithium naphthalide (LiNp), and tetrahydrofuran (THF) solution were introduced to prepare the Mg–Pd nanocomposite by the coprecipitation method (an adapted Rieke method). During the sample preparation process, the real reducing agent is metal Li, while naphthalene is used as an electron carrier. Due to the presence of naphthalene, metal Li would dissolve in THF, forming a blackish green solution, which can speed up the reduction reaction of active Mg. In raw materials, Pd:Mg was kept in a weight ratio of 1:9. The reaction processes are as follows:

$\begin{array}{ll}{\text{MgCl}}_2+2\text{Li}\to {\text{Mg}}^{*}+2\text{LiCl}& (1)\end{array}$

$\begin{array}{ll}{\text{PdCl}}_2+2\text{Li}\to {\text{Pd}}^{*}+2\text{LiCl}& (2)\end{array}$

Naphthalene (5.52 g) and lithium (0.299 g) were dissolved in the freshly distilled THF (50 ml), forming a homogeneous blackish green solution (LiNp/THF). A mixed THF solution of MgCl₂ and PdCl₂ was prepared by anhydrous MgCl₂ (1.904 g) and PdCl₂ (0.09 g) dissolved in 200 ml THF at 60–70°C. The coprecipitation reaction process and the separation and drying process of nanocomposites were performed with reference to a relevant literature report (Liu et al., 2014b).

Sample Characterization

The crystal structure and the phase composition of the samples were analyzed by X-ray diffraction (XRD) with Cu Kα radiation (40 kV and 35 mA) using an ARL X'TRA diffractometer. The morphology and microstructure of as-prepared samples were observed by using a JEM-2100F transmission electron microscope (TEM). A Sieverts-type apparatus (AMC) was used to examine the hydrogen storage properties. The auto pressure—composition—temperature (PCT) measurements were performed under a hydrogen pressure up to 4 MPa. The hydrogen absorption kinetics was characterized under an initial hydrogen pressure of 3.0 MPa. The dehydrogenation experiments were performed using diffraction scanning calorimetry (DSC, Netzsch STA 449F3) at various heating rates under Ar gas flow.

Results and Discussion

Microstructural Characterization

Figure 1 presents the XRD patterns of the Mg–Pd nanocomposite in varying states. As shown in Figure 1A, almost all diffraction peaks of as-prepared nanocomposite can be characterized with the hexagonal Mg phase. Only a weak peak at ~42.9° can be indexed with MgO, and the characteristic diffraction peaks of Pd are absent. A small amount of MgO is likely due to the oxidation in the process of sample preparation for the XRD analysis, as a result of high chemical activity of Rieked Mg. The absence of Pd peaks suggests that Pd synthetized from solution is in the form of extremely fine particles or amorphous, and hence, it does not generate detectable diffraction intensity. A similar phenomenon has been found in our previous research work (Liu et al., 2014a, 2015). The lattice parameters of the Mg phase can be refined to be a = b = 0.3225 nm, and c = 0.5242 nm for the Mg–Pd nanocomposite, which are slightly larger than those of pure Mg reduced by the same method (a = b = 0.3196 nm, c = 0.5199 nm; Liu et al., 2014b), indicating that a part of the Pd atoms may get into the crystal lattice of the Mg during the preparation, resulting in the lattice expansion of Mg. In addition, the average crystallite of Mg can be determined to be about 22.5 nm by the Scherrer equation. When the Mg–Pd nanocomposite was hydrogenated under 3 MPa hydrogen pressure at 150°C for 2 h, the majority phases of the hydrogenated Mg–Pd nanocomposite are the tetragonal β-MgH₂ and the orthogonal γ-MgH₂, along with a small amount of MgO and PdH_0.706 phases, as shown in Figure 1B. The metastable γ-MgH₂, belonging to a-PbO₂-type orthorhombic crystal structure, is usually produced by ball milling (Varin et al., 2006; Ponthieu et al., 2013; Zhou et al., 2015) as well as under high compressive stress (Vajeeston et al., 2006; Siviero et al., 2009; Ham et al., 2013). Zhou et al. (2013) pointed out that the H octahedrons surrounding Mg atoms are deformed in the γ-MgH₂. Besides, the octahedral chain takes a zigzag form, while for the β-MgH₂, the chain is straight. Sander et al. studied hydrogen transport kinetics in β- (termed α-MgH₂ in their study) and γ-MgH₂ based on theoretical calculations and found that H vacancies' concentrations are higher and more mobile in the γ-MgH₂ than in the β-MgH₂ (Sander et al., 2016). Therefore, we can speculate that the metastable γ-MgH₂ structure is likely due to the deformations and structural defects formed in the MgH₂ lattice during the preparation (ball milling or under high compressive stress). The formation of the γ-MgH₂ phase is also found in the Mg–TM (TM = Ni, Ti, Fe, Co, and V) nanocomposites coprecipitated from solution (Liu et al., 2014a,b, 2015). Norberg et al. (2011) proposed that a high density of defects may form in the Mg lattice through the adapted Rieked method. In addition, Xiao et al. (2016) synthesized β-/γ-MgH₂ nanocomposites via a simple wet chemical route by ball milling MgH₂ with LiCl as an additive at room temperature followed by THF treatment and revealed that THF solution plays a vital role in the synthesis of the γ-MgH₂ phase. In this work, high-density defects formed in the nanocomposite and THF solution effect may contribute to the formation of the γ-MgH₂ phase at lower temperature. On hydrogen loading, the PdH_0.706 peaked at 38.7°C, corresponding to the (111) plane. The PdH_0.706 phase also could be found when Au/Mg/Pd films were hydrogenated at 200°C (Akyildiz et al., 2006). As the temperature was increased to 350°C, in addition to the main phase of β-MgH₂, MgPd, PdH0.706, and γ-MgH₂ phases were clearly detected in Figure 1C. The appearance of the Pd-richer intermetallic compound MgPd indicates that Pd is inter-mixing with Mg at the Pd–Mg interface, which is considered to be the equilibrium end product (Callini et al., 2010). The amount of γ-MgH₂ phase in hydrogenated nanocomposite decreased with increasing the hydrogenation temperature, due to the removal of the lattice deformation and structural defects in Mg at high temperature. Shena and Aguey-Zinsou, reported that the γ-MgH₂ was fully converted to β-MgH₂ after hydrogen cycling at 200°C, due to the annealing of defects and relief of strain (Shena and Aguey-Zinsou, 2017). After dehydrogenation at 350°C for 2 h under 0.05 MPa hydrogen pressure, the phases of Mg, MgO, and Mg₆Pd could be detected in the XRD pattern of Figure 1D. The formation of Mg₆Pd confirms an interaction between MgH₂ and MgPd or PdH_0.706 during the process of dehydrogenation, as in following equations:

$\begin{array}{ll}\text{ MgPd}+5{\text{MgH}}_2\to {\text{Mg}}_6\text{Pd}+5{\text{H}}_2& (3)\end{array}$

$\begin{array}{ll}{\text{PdH}}_{0.706}+6{\text{MgH}}_2\to {\text{Mg}}_6\text{Pd}+7.412{\text{H}}_2& (4)\end{array}$

Huot et al. (2009) found that the bulk Mg₆Pd could reversibly absorb hydrogen in three disproportionation reactions and finally be transformed to the MgPd phase again. MgPd or Pd_H0.706 interacting with MgH₂ may alter the thermodynamics of the dehydrogenation of MgH₂. Therefore, the thermodynamics of the Mg–Pd nanocomposite will be discussed in greater detail later.

FIGURE 1

Figure 1. X-ray diffraction (XRD) patterns for the Mg–Pd nanocomposite in varying states. (A) As prepared, (B,C) hydrogenated at 150 and 350°C for 2 h, and (D) dehydrogenated at 350°C for 2 h.

STEM micrographs and SAED pattern of the Mg–Pd nanocomposite are shown in Figure 2. The Mg–Pd nanocomposite is composed of irregularly shaped particles aggregating together, with their particle sizes ranging from 40 to 70 nm, as shown in Figure 2A, while for the pure Mg without doping catalysts, the nanoparticles were plate-shaped and stacked together forming a shape like a “chicken claws” structure (Liu et al., 2014b). The above result indicates that doping with Pd may dramatically affect the preferred orientation of Mg particle growth. As shown in the corresponding SAED pattern (Figure 2B), the diffraction rings or points can be indexed with Mg and MgO phase, without Pd, which is in accordance with the XRD result. In order to qualitatively evaluate the distribution of Pd in Mg particles, EDS elemental maps of Mg and Pd were performed. As can be seen, Pd is homogeneously distributed on the surface or inside Mg particles, without obvious reunion phenomenon. The actual Pd weight content in the nanocomposite is about 5 wt%, much lower than the initial doping amount. Only half the amount of Pd was embedded in or attached on the surface of Mg particles, and the rest might be lost during the centrifugation and repeated washing processes. The TEM micrograph and the corresponding SAED pattern of the Mg–Pd nanocomposite hydrogenated at 150°C for 2 h are shown in Figures 3A,B, respectively. As can be seen, the particle size of the hydrogenated Mg–Pd nanocomposite ranges from 20 to 30 nm, much lower than that hydrogenated before, which is likely due to a large number of nucleation sites at the Mg–Pd interface and high density of defects on the Mg particles. The same phenomenon was found in the previously reported Mg–TM (TM = Ni, Ti, Fe, Co, and V) nanocomposites (Liu et al., 2014a,b, 2015). As shown in the STEM images, Pd is homogeneously distributed on the surface or inside Mg particles, without obvious reunion phenomenon. Kumar et al. has reported that multinucleation sites for the Mg → MgH₂ hydrogenation process could be created by the uniformly distributed catalyst on the Mg nanoparticle surface, which could prevent grain growth (Kumar et al., 2017). A high density of defects on the Mg particles could also be found in the previously reported Mg–TM (TM = Ni, Ti, Fe, Co, and V) nanocomposites (Liu et al., 2014a,b, 2015) and Mg nanocrystals prepared by Norberg et al. (2011), which could provide more nucleation sites for the Mg → MgH₂ hydrogenation process. In addition, the particles' growth trend is not obvious at lower hydrogenation temperature (150°C), resulting in the refinement of MgH₂ particles. As shown in Figure 3B, no diffraction rings or points can be indexed with the β-/γ-MgH₂ phase, suggesting that the electron beam induces full dehydrogenation of MgH₂ during the TEM measurement under high-vacuum conditions. Besides, Pd or PdH_0.706 is not found, maybe due to the poor crystallinity.

FIGURE 2

Figure 2. (A) STEM micrograph and (B) SAED pattern of the Mg–Pd nanocomposite, along with (C,D) EDS elemental maps of Mg and Pd.

FIGURE 3

Figure 3. (A) Transmission electron microscope (TEM) micrograph and (B) SAED pattern of the Mg–Pd nanocomposite hydrogenated at 150°C for 10 h.

The Effects of Mg₆Pd on the Thermodynamics

Figure 4A displays the PCT curves of the Mg–Pd nanocomposite measured at different temperatures in a hydrogen pressure range from 0.02 to 4 MPa. The first hydrogen cycle at 350°C was conducted for the test sample to obtain a Mg–Mg₆Pd system. It can be found that only one plateau is present across the whole range of the hydrogen content in each PCT curve. Obvious plateaus of Mg₆Pd cannot be clearly identified. However, previous investigation (Huot et al., 2009) showed that the hydrogen absorption process of Mg₆Pd was divided into three stages:

$\begin{array}{ll}{\text{Mg}}_6\text{Pd }+2.35{\text{H}}_2\leftrightarrow 2.35{\text{MgH}}_2+{\text{Mg}}_{3.65}\text{Pd}& (5)\end{array}$

$\begin{array}{l}2.35{\text{MgH}}_2+{\text{Mg}}_{3.65}\text{Pd}+1.15{\text{H}}_2\leftrightarrow 3.5{\text{MgH}}_2\\ +0.5{\text{Mg}}_2{\text{Pd}}_5& (6)\end{array}$

$\begin{array}{ll}3.5{\text{MgH}}_2+0.5{\text{Mg}}_2{\text{Pd}}_5+1.15{\text{H}}_2\leftrightarrow \text{MgPd}+5{\text{MgH}}_2& (7)\end{array}$

A higher plateau should appear in the PCT curve, which is attributed to the transformation Mg₆Pd + 5H₂ ↔ MgPd + 5MgH₂. In addition, Shena and Aguey-Zinsou (2017) reported that P(H₂)_abs = 5 MPa is not sufficient to induce the formation of MgPd at the higher temperature of 350°C. In fact, at 350°C, 3 MPa is enough for the formation of MgPd, as shown in Figure 1C. This is in accordance with the one plateau observed in the PCT curve for the Mg–Mg₆Pd system, suggesting an excellent synergistic effect for Mg and Mg₆Pd during hydrogenation/dehydrogenation processes. The corresponding van't Hoff plot (ln P vs. 1/T) is used to estimate hydrogenation and dehydrogenation enthalpies, as shown in Figure 4B. The hydrogenation and dehydrogenation enthalpies are determined to be −71.5 and 72.7 kJ mol⁻¹ H₂, respectively, which are slightly lower than that of pristine MgH₂ (74.7 kJ mol^–1 H₂; Crivello et al., 2016). Zhang et al. found that MgH₂ is preferentially decomposed by virtue of the Mg–Pd alloy instead of self-decomposition, which can reduce thermal stability of the MgH₂ through interacting with MgH₂ and forming the Mg₆Pd phase (Zhang et al., 2015). Therefore, it is reasonable to suggest that the Mg–Pd alloy plays an active role in the reversible metal hydride transformation, destabilizing the MgH₂.

FIGURE 4

Figure 4. (A) PCT curves of the Mg–Pd nanocomposite measured at different temperatures and (B) the corresponding van't Hoff plots. Ab, absorption; De, desorption.

The Effects of γ-MgH₂ and PdH_0.706 on Dehydrogenation Performances

DSC curves and the corresponding ln(β/T_p²)−1,000/T_p plots for the hydrogenated Mg–Pd nanocomposite are shown in Figure 5. The Mg–Pd nanocomposite was hydrogenated at 150°C for 2 h, as the test sample. Figure 5A shows that there is a broader and asymmetrical endothermic peak corresponding to desorption of the γ-MgH₂ and β-MgH₂ phases in 238.5 and 248.9°C at heating rates of 3 and 5°C/min, respectively, while for the heating rates of 10°C/min, the final endothermic peak is a superposition of two contributing peaks of 265.3 and 281.8°C. The above results suggest that γ-MgH₂ decomposes along with the β-MgH₂, which may trigger the decomposition of the β-MgH₂ during the dehydrogenation process. The onset dehydrogenation temperature at a heating rate of 3°C/min is reduced to 216.8°C, representing a 94.3°C reduction as compared with the pure MgH₂ prepared through the same method (Liu et al., 2014b), and for the reported Mg–TM (TM = Ni, Ti, Fe, Co, and V) nanocomposites, the onset dehydrogenation temperatures were determined to be 244.6, 296.1, 246.5, 249.1, and 278.2°C, respectively (Liu et al., 2014a,b, 2015). The hydrogenated Mg–Pd nanocomposite exhibits superior hydrogen desorption kinetics compared with the previously reported Mg–TM (TM = Ni, Ti, Fe, Co, and V) nanocomposites. The pure MgH₂ is a single phase of β-MgH₂, without doping catalyst. The γ-MgH₂ phase is known to be less stable than the β-MgH₂ phase. The plane (110) of γ-MgH₂ has a predicted enthalpy of 44.66 kJ mol⁻¹ H₂, while for the same β-MgH₂ plane, the enthalpy is 78.16 kJ mol⁻¹ H₂ (Zhou et al., 2015). In addition, the heavily distorted MgH₆ octahedron in the γ-MgH₂ potentially can facilitate hydrogen diffusion (Sander et al., 2016). Shena and Aguey-Zinsou (2017) proposed that γ-MgH₂ can further facilitate hydrogen desorption from β-MgH₂, which can act as a pathway for faster hydrogen diffusion. In this work, a higher content of γ-MgH₂ is achieved in the hydrogenated products, as shown in Figure 1B. Therefore, it can be concluded that the γ-MgH₂ phase can significantly reduce the dehydrogenation temperature and improve the dehydrogenation kinetics by acting as a pathway for faster hydrogen diffusion. The PdH_0.706 phase in the hydrogenated products also is reported to be effective for improving desorption hydrogen kinetics and reducing the hydrogen desorption temperature, which may help the recombination process of H atoms into hydrogen molecules on the surface (Tang et al., 2008). Higuchi et al. (2002) reported that “cooperative phenomena” can explain the significant improvement in the dehydriding properties of the Pd/Mg/Pd films, in which hydrogen exhibits elastic interactions between MgH₂ and PdH_0.6. The activation energy, E_d, for the hydrogen desorption mechanism of the hydrogenated Mg–Pd nanocomposites is estimated by the Kissinger equation:

$\begin{array}{ll}\text{ln}(\beta /T_p^2)=\text{A}-E_d/(\text{R}{T}_p)& (8)\end{array}$

where β is the heating rate, T_p is the peak temperature, and A is a linear constant.

FIGURE 5

Figure 5. (A) Diffraction scanning calorimetry (DSC) curves and (B) the corresponding ln(β/T_p²) −1,000/T_p plots for the hydrogenated Mg–Pd nanocomposite at different heating rates.

Figure 5B shows the plot of ln(β/$T_p^2$) vs. 1,000/T_p for the hydrogenated Mg–Pd nanocomposites. The E_d value can be determined to be 93.8 kJ/mol H₂, which is much lower than that of the hydrogenated pure Mg (147.4 kJ/mol H₂; Liu et al., 2014b) and the reported Mg–TM (TM = Ni, Ti, Fe, Co, and V) nanocomposites (139.1, 170.9, 118.1, 110.1, and 147.7 kJ/mol H₂, respectively; Liu et al., 2014a,b, 2015). The lower dehydrogenation temperature and E_d value indicate that γ-MgH₂ and PH_0.706 phases formed during the hydrogenation process contribute to the enhancing desorption kinetics.

The Effects of Pd on Lower Temperature Hydrogenation Performances

Figure 6A shows the first isothermal hydrogen absorption curves of the Mg–Pd nanocomposite measured at 50, 75, 100, 125, and 150°C. As can be seen, the Mg–Pd nanocomposite exhibits excellent hydrogen absorption performance. The hydrogen storage capacity can reach up to 3.0 wt% in 2 h at 50°C. In contrast, the hydrogen capacity of the pure Mg is 2.6 wt% within 2 h at a higher temperature of 125°C. The result suggests that Pd exhibits high catalytic activity on accelerating the hydrogenation rate of Mg. The apparent activation energy of dehydrogenation can be calculated based on the Johnson–Mehl–Avrami–Kolmogorov (JMAK) model and the Arrhenius theory (Liu et al., 2014a,b, 2015). The Arrhenius-type plot of lnk vs. 1,000/T is drawn in Figure 6B. Thus, E_a of the Mg–Pd nanocomposite can be determined to be 44.3 kJ/mol H₂, much lower than that of the pure Mg (73.1 kJ/mol H₂; Liu et al., 2014b). Such a low energy barrier explains the excellent absorption kinetics of the Mg–Pd nanocomposite at low temperatures. As shown in the STEM images (Figure 2), Pd is homogeneously distributed on the surface or inside Mg particles, with the particle size ranging from 40 to 70 nm. The reported theoretical calculations indicate that the Pd-dopant can provide a much lower activation barrier for both dissociation of molecular hydrogen and diffusion of atomic hydrogen on the Mg surface (Du et al., 2007). Pd in the form of small particles dispersed on the Mg particles can catalyze the dissociation of H₂, and the adsorbed hydrogen atoms can be spilled over onto the surface of Mg nanoparticles, which is assigned as a “spillover” mechanism (Zaluskia et al., 1995). In addition, Pd may act as the “nanoportal” role, and hydride nucleation occurs only under Pd nanoparticles at lower hydrogenation temperature (Chung et al., 2015). Hence, it can be concluded that Pd homogeneously distributed on the surface or inside Mg particles can dissociate hydrogen and create a hydrogen diffusion pathway for the Mg nanoparticles.

FIGURE 6

Figure 6. (A) Hydrogen absorption curves of the Mg–Pd nanocomposite measured at different temperatures for 2 h and (B) the corresponding lnk −1,000/T plot.

Conclusions

In this work, a Mg–Pd nanocomposite was successfully coprecipitated from a homogeneous THF solution. STEM observations revealed that Pd was homogeneously distributed on the surface or inside Mg particles, with the particle size ranging from 40 to 70 nm. The Mg–Pd nanocomposite exhibits superior hydrogen storage properties. The hydrogen reaction enthalpies of the Mg–Pd nanocomposite are slightly lower than that of pristine MgH₂, indicating that the Mg–Pd alloy plays an active role in the reversible metal hydride transformation and destabilizes the MgH₂. For the hydrogenated Mg–Pd nanocomposite at 150°C, the onset dehydrogenation temperature is reduced to 216.8°C, representing a 94.3°C reduction as compared with the pure MgH₂ prepared through the same method. High-content γ-MgH₂ along with PH_0.706 is formed during the hydrogenation process, contributing to the enhancing desorption kinetics. The Mg–Pd nanocomposite can take up 3.0 wt% hydrogen in 2 h at temperature low as 50°C. During lower hydrogenation temperatures, Pd can dissociate hydrogen and create a hydrogen diffusion pathway for the Mg nanoparticles.

Data Availability Statement

All datasets generated for this study are included in the article/supplementary material.

Author Contributions

The manuscript was written through contributions of all authors. All authors have given approval to the final version of the manuscript.

Funding

This work was supported by the National Natural Science Foundation of China (51801100, 51771092, 21975125), Natural Science Foundation of the Jiangsu Higher Education Institutions of China (18KJB430014), Postgraduate Research & Practice Innovation Program of Jiangsu Province (SJCX18_0341), Six Talent Peaks Project in Jiangsu Province (2018, XNY-020), and the Priority Academic Program Development (PAPD) of Jiangsu Higher Education Institutions.

Conflict of Interest

The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.

References

Akyildiz, H., Ozenbas, M., and Ozturk, T. (2006). Hydrogen absorption in magnesium based crystalline thin films. Int. J. Hydr. Energy 31, 1379–1383. doi: 10.1016/j.ijhydene.2005.11.003

CrossRef Full Text | Google Scholar

Callini, E., Pasquini, L., Piscopiello, E., Montone, A., Vittori Antisari, M., and Bonetti, E. (2009). Hydrogen sorption in Pd-decorated Mg-MgO core-shell nanoparticles. Appl. Phys. Lett. 94:221905. doi: 10.1063/1.3147205

CrossRef Full Text | Google Scholar

Callini, E., Pasquini, L., Rude, L. H., Nielsen, T. K., Jensen, T. R., and Bonetti, E. (2010). Hydrogen storage and phase transformations in Mg–Pd nanoparticles. J. Appl. Phys. 108:073513. doi: 10.1063/1.3490206

CrossRef Full Text | Google Scholar

Chung, C. J., Nivargi, C., and Clemens, B. (2015). Nanometer-scale hydrogen 'portals' for the control of magnesium hydride formation. Phys. Chem. Chem. Phys. 17, 28977–28984. doi: 10.1039/C5CP04515K

PubMed Abstract | CrossRef Full Text | Google Scholar

Crivello, J. C., Dam, B., Denys, R. V., Dornheim, M., Grant, D. M., Huot, J., et al. (2016). Review of magnesium hydride-based materials: development and optimisation. Appl. Phys. A 122:97. doi: 10.1007/s00339-016-9602-0

CrossRef Full Text | Google Scholar

Cui, J., Liu, J., Wang, H., Ouyang, L., Sun, D., Zhu, M., et al. (2014). Mg–TM (TM: Ti, Nb, V, Co, Mo or Ni) core–shell like nanostructures: synthesis, hydrogen storage performance and catalytic mechanism. J. Mater. Chem. A 2, 9645–9655. doi: 10.1039/C4TA00221K

CrossRef Full Text | Google Scholar

Du, A. J., Smith, S. C., Yao, X. D., and Lu, G. Q. (2007). Hydrogen spillover mechanism on a Pd-doped Mg surface as revealed by ab initio density functional calculation. J. Am. Chem. Soc. 129, 10201–10204. doi: 10.1021/ja0722776

PubMed Abstract | CrossRef Full Text | Google Scholar

Ham, B., Junkaew, A., Arroyave, R., Chen, J., Wang, H., Wang, P., et al. (2013). Hydrogen sorption in orthorhombic Mg hydride at ultra-low temperature. Int. J. Hydr. Energy 38, 8328–8341. doi: 10.1016/j.ijhydene.2013.04.098

CrossRef Full Text | Google Scholar

Higuchi, K., Yamamotob, K., Kajiokaa, H., Toiyamaa, K., Hondaa, M., Orimoc, S., et al. (2002). Remarkable hydrogen storage properties in three-layered Pd/Mg/Pd thin films. J. Alloys Comp. 330, 526–530. doi: 10.1016/S0925-8388(01)01542-0

CrossRef Full Text | Google Scholar

Huot, J., Yonkeu, A., and Dufour, J. (2009). Rietveld analysis of neutron powder diffraction of Mg6Pd alloy at various hydriding stages. J. Alloys Comp. 475, 168–172. doi: 10.1016/j.jallcom.2008.07.034

CrossRef Full Text | Google Scholar

Jangir, M., Jain, A., Agarwal, S., Zhang, T., Kumar, S., Selvaraj, S., et al. (2018). The enhanced de/re-hydrogenation performance of MgH2 with TiH2 additive. Int. J. Energy Res. 42, 1139–1147. doi: 10.1002/er.3911

CrossRef Full Text | Google Scholar

Jeon, K. J., Moon, H. R., Ruminski, A. M., Jiang, B., Kisielowski, C., Bardhan, R., et al. (2011). Air-stable magnesium nanocomposites provide rapid and high-capacity hydrogen storage without using heavy-metal catalysts. Nat. Mater. 10, 286–290. doi: 10.1038/nmat2978

PubMed Abstract | CrossRef Full Text | Google Scholar

Kumar, S., Jain, A., Yamaguchi, S., Miyaoka, H., Ichikawa, T., Mukherjee, A., et al. (2017). Surface modification of MgH2 by ZrCl4 to tailor the reversible hydrogen storage performance. Int. J. Hydr. Energy 42, 6152–6159. doi: 10.1016/j.ijhydene.2017.01.193

CrossRef Full Text | Google Scholar

Lin, H.-J., Matsuda, J., Li, H.-W., Zhu, M., and Akiba, E. (2015). Enhanced hydrogen desorption property of MgH2 with the addition of cerium fluorides. J. Alloys Comp. 645, S392–S396. doi: 10.1016/j.jallcom.2014.12.102

CrossRef Full Text | Google Scholar

Lin, H.-J., Tang, J.-J., Yu, Q., Wang, H., Ouyang, L.-Z., Zhao, Y.-J., et al. (2014). Symbiotic CeH 2.73/CeO2 catalyst: a novel hydrogen pump. Nano Energy 9, 80–87. doi: 10.1016/j.nanoen.2014.06.026

CrossRef Full Text | Google Scholar

Liu, G., Wang, Y., Xu, C., Qiu, F., An, C., Li, L., et al. (2013). Excellent catalytic effects of highly crumpled graphene nanosheets on hydrogenation/dehydrogenation of magnesium hydride. Nanoscale 5, 1074–1081. doi: 10.1039/C2NR33347C

PubMed Abstract | CrossRef Full Text | Google Scholar

Liu, M., Xiao, X., Zhao, S., Chen, M., Mao, J., Luo, B., et al. (2019a). Facile synthesis of Co/Pd supported by few-walled carbon nanotubes as an efficient bidirectional catalyst for improving the low temperature hydrogen storage properties of magnesium hydride. J. Mater. Chem. A 7, 5277–5287. doi: 10.1039/C8TA12431K

CrossRef Full Text | Google Scholar

Liu, M., Xiao, X., Zhao, S., Saremi-Yarahmadi, S., Chen, M., Zheng, J., et al. (2019b). ZIF-67 derived Co@CNTs nanoparticles: remarkably improved hydrogen storage properties of MgH2 and synergetic catalysis mechanism. Int. J. Hydr. Energy 44, 1059–1069. doi: 10.1016/j.ijhydene.2018.11.078

CrossRef Full Text | Google Scholar

Liu, Y., Zou, J., Zeng, X., and Ding, W. (2014a). A co-precipitated Mg–Ti nano-composite with high capacity and rapid hydrogen absorption kinetics at room temperature. RSC Adv. 4, 42764–42771. doi: 10.1039/C4RA05382F

CrossRef Full Text | Google Scholar

Liu, Y., Zou, J., Zeng, X., and Ding, W. (2015). Study on hydrogen storage properties of Mg–X (X = Fe, Co, V) nano-composites co-precipitated from solution. RSC Adv. 5, 7687–7696. doi: 10.1039/C4RA12977F

CrossRef Full Text | Google Scholar

Liu, Y., Zou, J., Zeng, X., Wu, X., Li, D., and Ding, W. (2014b). Hydrogen storage properties of a Mg–Ni nanocomposite coprecipitated from solution. J. Phys. Chem. C 118, 18401–18411. doi: 10.1021/jp504918x

CrossRef Full Text | Google Scholar

Lu, J., Choi, Y. J., Fang, Z. Z., Sohn, H. Y., and Rönnebro, E. (2010). Hydrogenation of nanocrystalline Mg at room temperature in the presence of TiH2. J. Am. Chem. Soc. 132, 6616–6617. doi: 10.1021/ja910944w

PubMed Abstract | CrossRef Full Text | Google Scholar

Lukashev, R. V., Klyamkin, S. N., and Tarasov, B. P. (2006). Preparation and properties of hydrogen-storage composites in the MgH2-C system. Inorg. Mater. 42, 726–732. doi: 10.1134/S0020168506070077

CrossRef Full Text | Google Scholar

Ma, L. P., Kang, X. D., Dai, H. B., Liang, Y., Fang, Z. Z., Wang, P. J., et al. (2009). Superior catalytic effect of TiF3 over TiCl3 in improving the hydrogen sorption kinetics of MgH2: catalytic role of fluorine anion. Acta Mater. 57, 2250–2258. doi: 10.1016/j.actamat.2009.01.025

CrossRef Full Text | Google Scholar

Ma, T., Isobe, S., Wang, Y., Hashimoto, N., and Ohnuki, S. (2013). Nb-Gateway for hydrogen desorption in Nb2O5 catalyzed MgH2 nanocomposite. J. Phys. Chem. C 117, 10302–10307. doi: 10.1021/jp4021883

CrossRef Full Text | Google Scholar

Norberg, N. S., Arthur, T. S., Fredrick, S. J., and Prieto, A. L. (2011). Size-dependent hydrogen storage properties of Mg nanocrystals prepared from solution. J. Am. Chem. Soc. 133, 10679–10681. doi: 10.1021/ja201791y

PubMed Abstract | CrossRef Full Text | Google Scholar

Pistidda, C., Bergemann, N., Wurr, J., Rzeszutek, A., Møller, K. T., Hansen, B. R. S., et al. (2014). Hydrogen storage systems from waste Mg alloys. J. Power Sources 270, 554–563. doi: 10.1016/j.jpowsour.2014.07.129

CrossRef Full Text | Google Scholar

Ponthieu, M., Cuevas, F., Fernández, J. F., Laversenne, L., Porcher, F., and Latroche, M. (2013). Structural properties and reversible deuterium loading of MgD2–TiD2 nanocomposites. J. Phys. Chem. C 117, 18851–18862. doi: 10.1021/jp405803x

CrossRef Full Text | Google Scholar

Rather, S. U., Taimoor, A. A., Muhammad, A., Alhamed, Y. A., Zaman, S. F., and Ali, A. M. (2016). Kinetics of hydrogen adsorption on MgH2/CNT composite. Mater. Res. Bull. 77, 23–28. doi: 10.1016/j.materresbull.2016.01.025

CrossRef Full Text | Google Scholar

Rieke, R. D., and Hudnall, P. M. (1972). Activated metals. I. preparation of highly reactive magnesium metal. J. Am. Chem. Soc. 94, 7178–7179. doi: 10.1021/ja00775a066

CrossRef Full Text | Google Scholar

Rizo-Acosta, P., Cuevas, F., and Latroche, M. (2018). Optimization of TiH2 content for fast and efficient hydrogen cycling of MgH2-TiH2 nanocomposites. Int. J. Hydr. Energy 43, 16774–16781. doi: 10.1016/j.ijhydene.2018.04.169

CrossRef Full Text | Google Scholar

Sander, J. M., Ismer, L., and Van De Walle, C. G. (2016). Point-defect kinetics in α- and γ-MgH2. Int. J. Hydr. Energy 41, 5688–5692. doi: 10.1016/j.ijhydene.2016.01.156

CrossRef Full Text | Google Scholar

Schneemann, A., White, J. L., Kang, S., Jeong, S., Wan, L. F., Cho, E. S., et al. (2018). Nanostructured metal hydrides for hydrogen storage. Chem. Rev. 118, 10775–10839. doi: 10.1021/acs.chemrev.8b00313

PubMed Abstract | CrossRef Full Text | Google Scholar

Shena, C., and Aguey-Zinsou, K.-F. (2017). Can γ-MgH2 improve the hydrogen storage properties of magnesium? J. Mater. Chem. A 5, 8644–8652. doi: 10.1039/C7TA01724C

CrossRef Full Text | Google Scholar

Singh, R. K., Sadhasivam, T., Sheeja, G. I., Singh, P., and Srivastava, O. N. (2013). Effect of different sized CeO2 nano particles on decomposition and hydrogen absorption kinetics of magnesium hydride. Int. J. Hydr. Energy 38, 6221–6225. doi: 10.1016/j.ijhydene.2012.12.060

CrossRef Full Text | Google Scholar

Siviero, G., Bello, V., Mattei, G., Mazzoldi, P., Battaglin, G., Bazzanella, N., et al. (2009). Structural evolution of Pd-capped Mg thin films under H2 absorption and desorption cycles. Int. J. Hydr. Energy 34, 4817–4826. doi: 10.1016/j.ijhydene.2009.03.059

CrossRef Full Text | Google Scholar

Sun, Y., Ma, T., and Aguey-Zinsou, K.-F. (2018). Magnesium supported on nickel nanobelts for hydrogen storage: coupling nanosizing and catalysis. ACS Appl. Nano Mater. 1, 1272–1279. doi: 10.1021/acsanm.8b00033

CrossRef Full Text | Google Scholar

Tang, F., Parker, T., Li, H. F., Wang, G. C., and Lu, T. M. (2008). The Pd catalyst effect on low temperature hydrogen desorption from hydrided ultrathin Mg nanoblades. Nanotechnology 19:465706. doi: 10.1088/0957-4484/19/46/465706

PubMed Abstract | CrossRef Full Text | Google Scholar

Terent'ev, P. B., Gerasimov, E. G., Mushnikov, N. V., Uimin, M. A., Maikov, V. V., Gaviko, V. S., et al. (2015). Kinetics of hydrogen desorption from MgH2 and AlH3 hydrides. Phys. Metals Metallogr. 116, 1197–1202. doi: 10.1134/S0031918X15120121

CrossRef Full Text | Google Scholar

Vajeeston, P., Ravindran, P., Hauback, B. C., Fjellvåg, H., Kjekshus, A., Furuseth, S., et al. (2006). Structural stability and pressure-induced phase transitions inMgH2. Phys. Rev. B 73:224102. doi: 10.1103/PhysRevB.73.224102

CrossRef Full Text | Google Scholar

Varin, R. A., Czujko, T., and Wronski, Z. (2006). Particle size, grain size and gamma-MgH2 effects on the desorption properties of nanocrystalline commercial magnesium hydride processed by controlled mechanical milling. Nanotechnology 17, 3856–3865. doi: 10.1088/0957-4484/17/15/041

CrossRef Full Text | Google Scholar

Wang, H., Hu, J., Han, F., Lu, Y., Liu, J., Ouyang, L., et al. (2015). Enhanced joint catalysis of YH2/Y2O3 on dehydrogenation of MgH2. J. Alloys Comp. 645, S209–S212. doi: 10.1016/j.jallcom.2015.01.057

CrossRef Full Text | Google Scholar

Xiao, X., Liu, Z., Saremi-Yarahmadi, S., and Gregory, D. H. (2016). Facile preparation of β/γ-MgH(2) nanocomposites under mild conditions and pathways to rapid dehydrogenation. Phys. Chem. Chem. Phys. 18, 10492–10498. doi: 10.1039/C5CP07762A

PubMed Abstract | CrossRef Full Text | Google Scholar

Yao, X., Zhu, Z. H., Cheng, H. M., and Lu, G. Q. (2011). Hydrogen diffusion and effect of grain size on hydrogenation kinetics in magnesium hydrides. J. Mater. Res. 23, 336–340. doi: 10.1557/JMR.2008.0063

CrossRef Full Text | Google Scholar

Yartys, V. A., Lototskyy, M. V., Akiba, E., Albert, R., Antonov, V. E., Ares, J. R., et al. (2019). Magnesium based materials for hydrogen based energy storage: past, present and future. Int. J. Hydr. Energy 44, 7809–7859. doi: 10.1016/j.ijhydene.2018.12.212

CrossRef Full Text | Google Scholar

Zaluskia, L., Zaluskaa, A., Tessiera, P., Ström-Olsena, J. O., and Schulzb, R. (1995). Catalytic effect of Pd on hydrogen absorption in mechanically alloyed Mg2Ni, LaNi5 and FeTi. J. Alloys Comp. 217, 295–300. doi: 10.1016/0925-8388(94)01358-6

CrossRef Full Text | Google Scholar

Zhang, X., Leng, Z., Gao, M., Hu, J., Du, F., Yao, J., et al. (2018). Enhanced hydrogen storage properties of MgH 2 catalyzed with carbon-supported nanocrystalline TiO 2. J. Power Sources 398, 183–192. doi: 10.1016/j.jpowsour.2018.07.072

CrossRef Full Text | Google Scholar

Zhang, Y., Zhuang, X., Zhu, Y., Wan, N., Li, L., and Dong, J. (2015). Synergistic effects of TiH2 and Pd on hydrogen desorption performances of MgH2. Int. J. Hydr. Energy 40, 16338–16346. doi: 10.1016/j.ijhydene.2015.09.029

CrossRef Full Text | Google Scholar

Zhou, S., Ran, W., Yang, M., Wang, D., Chen, G., Zhang, Y., et al. (2013). Magnesium hydride of orthorhombic crystal from high-energy ball milling under hydrogen atmosphere. Adv. Mater. Res. 724–725, 1033–1036. doi: 10.4028/www.scientific.net/AMR.724-725.1033

CrossRef Full Text | Google Scholar

Zhou, S., Zhang, Q., Chen, H., Zang, X., Zhou, X., Wang, R., et al. (2015). Crystalline structure, energy calculation and dehydriding thermodynamics of magnesium hydride from reactive milling. Int. J. Hydr. Energy 40, 11484–11490. doi: 10.1016/j.ijhydene.2015.02.059

CrossRef Full Text | Google Scholar