ORIGINAL RESEARCH article

Front. Chem., 21 December 2018
Sec. Nanoscience
This article is part of the Research Topic Nonferrous Nanomaterials & Composites for Energy Storage and Conversion View all 48 articles

Highly Stable Gully-Network Co3O4 Nanowire Arrays as Battery-Type Electrode for Outstanding Supercapacitor Performance

\r\nChunli Guo*&#x;Chunli Guo1*Minshuai YinMinshuai Yin1Chun WuChun Wu2Jie LiJie Li1Changhui SunChanghui Sun3Chuankun Jia,*&#x;Chuankun Jia2,4*Taotao LiTaotao Li1Lifeng HouLifeng Hou1Yinghui Wei,Yinghui Wei1,5
  • 1College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan, China
  • 2College of Materials Science and Engineering, Changsha University of Science & Technology, Changsha, China
  • 3School of Chemistry and Chemical Engineering, Qilu Normal University, Jinan, China
  • 4Key Laboratory of Advanced Energy Materials Chemistry (Ministry of Education), Nankai University, Tianjin, China
  • 5College of Materials Science and Engineering, Taiyuan University of Science and Technology, Taiyuan, China

3D transition metal oxides, especially constructed from the interconnected nanowires directly grown on conductive current collectors, are considered to be the most promising electrode material candidates for advanced supercapacitors because 3D network could simultaneously enhance the mechanical and electrochemical performance. The work about design, fabrication, and characterization of 3D gully-network Co3O4 nanowire arrays directly grown on Ni foam using a facile hydrothermal procedure followed by calcination treatment will be introduced. When evaluated as a binder-free battery-type electrode for supercapacitor, a high specific capacity of 582.8 C g−1 at a current density of 1 A g−1, a desirable rate capability with capacity retention about 84.8% at 20 A g−1, and an outstanding cycle performance of 93.1% capacity retention after 25,000 cycles can be achieved. More remarkably, an energy density of 33.8 W h kg−1 at a power density of 224 W kg−1 and wonderful cycling stability with 74% capacity retention after 10,000 cycles can be delivered based on the hybrid-supercapacitor with the as-prepared Co3O4 nanowire arrays as a positive electrode and active carbon as negative electrode. All the unexceptionable supercapacitive behaviors illustrates that our unique 3D gully-network structure Co3O4 nanowire arrays hold a great promise for constructing high-performance energy storage devices.

Introduction

With the rapid depletion of fossil fuels and deterioration of the environment, an urgent demand has emerged for the development of sustainable and clean energy storage devices in terms of high power density, energy density, and good safety performance (Wang et al., 2012b; Ren et al., 2015; Zhang et al., 2018; Zeng et al., 2019). Because of the admirable supercapacitive behaviors, ecological features, and safety characteristics, supercapacitors have been extensively considered as the major devices for energy storage adhibition thanks to the great potential as power sources for various applications, from electric vehicles to smart grids (Raj et al., 2015; Yan et al., 2017; Wu et al., 2018). As documented in the previous investigations that the supercapacitive behaviors of these devices heavily rely on the properties of electrode materials (Chang et al., 2016; Cui et al., 2019). Therefore, the vital point to acquire wonderful behaviors of these devices is to hunt for proper materials and suitably design the electrode structure (Xu et al., 2017).

Because of the suitability for large-scale fabrication, high specific capacity, and rich redox reactions involving different ions, the transition metal oxides have been intensively studied as the most potential electrode materials in supercapacitors, which are divided into a capacitive electrode materials (MnO2 and RuO2) having a quasi-rectangular cyclic voltammetry (CV) curve and a battery-type electrode materials (cobalt and nickel based compounds) having a strong separated redox peaks by the shape of the CV curve (Huang et al., 2014; Shao et al., 2015; Wang et al., 2015; Dai et al., 2017, 2018; Jiang et al., 2017; Wu et al., 2019). In particular, cobalt oxide, as a typical battery-type electrode material, has attracted a great deal of attention due to its low cost, natural abundance, high surface area structural characteristics, and high theoretical capacity (Yuan et al., 2012; Kuang et al., 2015; Jiang et al., 2016). Wang et al. successfully prepared Co3O4 nanostructures with a specific capacity of 354.6 C g−1 at 0.5 A g−1, and the cycle performance in particular is about 97% after 2,000 cycles with a current density of 1 A g−1 (Wang et al., 2016). Well-crystalline porous cobalt oxide (Co3O4) nanorods (NRs) synthesized by hydrothermal method by Shin's group (Jang et al., 2017). A specific capacity about 316.4 C g−1 at 10 mV s−1 can be achieved based on porous Co3O4 NRs-300°C electrode. In addition, about 76% capacity retention of the porous Co3O4 NRs electrode can be maintained after 5,000 cycles. 3D-nanonet hollow structured Co3O4 electrode for battery-type supercapitor, prepared by a facile, low cost, and eco-friendly route under ambient temperature and pressure, can exhibit 410, 377.28, 346.68, and 328 C g−1 under various scan rates about 5, 10, 20, and 30 mV s−1, respectively (Wang et al., 2014). The as-prepared electrode also reveals good stability and keeps 90.2% of its initial capacity after 1,000 cycles at 5 A g−1. However, there is a big distance in the obtained Co3O4 electrode reaching to the theoretical specific capacity and a better cycling stability owing to the intrinsic highly resistive nature or the agglomeration of the Co3O4 nanomaterials during the electrode fabrication process (Rajeshkhanna et al., 2016; Wang et al., 2016; Kong et al., 2017).

One effective way proved to avoid the disadvantages caused by the binder addition and enhance the electrochemical performances of the Co3O4 electrodes is to grow the active electrode materials directly on conductive substrates such as Ni foam (Mao et al., 2016). Zhang et al. confirmed that Co3O4 nanowire array grown directly on Ni foam, fabricated by a simple hydrothermal method together with a post-annealing process, exhibited a specific capacity of 580 C g−1 at 1 A g−1 and a cycle performance of 90.6% after 5,000 cycles at 8 A g−1 (Zhang et al., 2012). Gao et al. also reported that 3D star-shaped Co3O4 nanowire growing on Ni foam prepared by a simple hydrothermal method displayed the specific capacity of 700 C g−1 at 1 A g−1. However, the specific capacity retention rate is 92.26% after only 1,000 cycles at a current density of 12.5 A g−1 (Gao et al., 2016). Qing et al. investigated that Co3O4 nanoflower structure on Ni foam showed a high specific capacity of 514.8 C g−1 at 1 A g−1, but its cycle performance was only 78.2% at 3 A g−1 after 1,000 cycles (Qing et al., 2011). As a result, the integrated electrodes exhibited the improvement of the specific capacity, but their poor cycling stability was far from solved, which partly resulted from the large volume changes of Co3O4 electrodes during the repeated cycle process (Yao et al., 2011), leading to structural instability, active material shedding off, and the capacity decay.

To address the above issues and achieve the excellent supercapacitive electrode materials, herein, we report our findings about the design, fabrication, and characterization of 3D gully-network structure Co3O4 nanowire arrays directly grown on Ni foam through a facile and scalable hydrothermal procedure followed by annealing treatment. It has been demonstrated that the direct growth of 3D gully-network structure on Ni foam could ensure that every nanowire possesses good mechanical adhesion and participates in electrochemical reactions, so a stable 3D mechanical network benefits most to its excellent cycling ability. More importantly, good electrical contact with the current collector, which would result in low contact resistance and wonderful supercapacitive behaviors in terms of high specific capacity, admirable rate capability as well as outstanding cycle stability.

Experimental

Preparation of 3D Gully-Network Co3O4 Nanowires on Ni Foam

All the purchased chemicals were analytical grade and used without further purification. The Ni foam was cleaned ultrasonically for 15 min in 3M HCl solution, absolute ethanol, and deionized water to remove the surface oxide layer and was dried in a vacuum oven for 2 h. 0.4851 g Co(NO3)2 and 0.0912 g urea were dissolved in 40 mL deionized water. Next, 0.0834 g cetyltrimethylammonium bromide (CTAB) and 0.0133 g sodium dodecyl benzene sulfonate (SDBS) were added to the above mixed solution and were stirred magnetically for 15 min, respectively. Then, both the mixed solution and the ready-prepared Ni foam were transferred into a 60 mL Teflon-lined stainless steel autoclave, sealed, and placed in an electric oven at 140°C for 4 h, and then allowed to cool to room temperature naturally. The precursors and precipitates were collected and washed three times with absolute ethanol and deionized water, respectively, then dried at 60°C overnight. Finally, the prepared precursor was annealed at 300°C in air for 2 h with a heating rate of 1°C min−1 to obtain 3D gully-network Co3O4 nanowires (NWAs) on Ni foam. The mass loading of Co3O4 NWAs on Ni foam was about 2.1 mg cm−2.

Preparation of the Hybrid-Supercapacitor

The hybrid-supercapacitor was assembled by the Co3O4 NWAs on Ni foam as the positive electrode, the activated carbon (AC) as the negative electrode, polypropylene separator as the separator, 6 M KOH as the electrolyte. Specifically, the negative electrode was prepared as follows: First, AC and polytetrafluoroethylene (PTFE) (mass fraction: 5%) were mixed in a ratio of 9:1 and ultrasonically diluted with anhydrous ethanol. The Ni foam (3 × 3 cm) was soaked in the mixed solution for 3 min. Finally, the AC was uniformly distributed on Ni foam after drying in air at 60°C for 6 h, and the mass loading of AC electrode was 2.4 mg cm−2. Positive and negative electrodes in hybrid-supercapacitor must meet charge balance (q+ = q). The charge contained in each electrode is calculated using the following equation [Equation (1)]:

= Qua × mua × S    (1)

Where Qua (C g−1) is the specific capacity per unit area of the electrode, mua (g) is the mass per area (cm2) of the active material and S (cm2) is the area of the electrode.

In order to achieve q+ = q, the area ratio satisfies equation (2):

S+S-=Qua- × mua-Qua+ × mua+    (2)

According to the specific capacity of both the positive and the negative electrode, the best positive and negative electrode area ratio was found to be S/S+ = 3. Finally assembled into hybrid-supercapacitor.

Materials Characterization

Scanning electron microscope (SEM) analyses were performed using a SU8010 SEM, operated at 10 kV. Transmission electron microscope (TEM) images and selected area electron diffraction (SAED) patterns were collected on JEOL-2100F at 200 kV. X-ray diffraction (XRD) using Cu-Ka radiation (Ka = 1.5418 Å). Raman scattering spectra were taken on a SPEX-1403 Raman spectrometer (Ar ion laser, 514.5 nm). X-ray photoelectron spectra (XPS) were recorded on an Axis Ultra, Kratos (UK) spectrometer, using a standard Al Kα X-ray source (150 W) and an analyzer pass energy of 30 eV. Samples were mounted using double-sided adhesive tape and binding energies are referenced to the C (1 s) binding energy of adventitious carbon contamination taken to be 284.8 eV.

Electrochemical Measurements

The CV, galvanostatic charge/discharge (GCD), and electrochemical impedance spectroscopy (EIS) techniques were used to evaluate the electrochemical performance of Co3O4 NWAs and hybrid-supercapacitor on a CHI660E electrochemical workstation at room temperature. Co3O4 NWAs were tested in a three-electrode system where Hg/HgO electrode is the reference electrode, Pt electrode (3 × 3 cm) is the counter electrode and the preparation electrode material is the working electrode. However, hybrid-supercapacitors were tested in a two-electrode system with Co3O4 NWAs as the positive electrode and AC as the negative electrode. All electrochemical tests were performed in 6M KOH. We calculated the specific capacity (Qsc) (C g−1), energy density (E) (Wh Kg−1), and power density (P) (W Kg−1) based on the discharge time in the GCD curve and calculate it according to Equations (3–5).

Qsc=Itm    (3)
E=12QscV    (4)
P=Et    (5)

Where I (A) is the discharge current, t (s) is the discharge time, V (V) is the voltage window, and m (g) is the mass of the electrode material.

Result and Discussion

Figure 1 was the SEM images of a precursor nanowire array on Ni foam. Figure 1a presents that the precursor nanowire array uniformly grows on the Ni foam surface. According to the missing part, the thickness of the nanowire array is about 15 μm. It is worth noting that the top of the nanowire is bent instead of perpendicular to the surface of the Ni foam. It is further observed (Figure 1a) that the tops of the nanowires were clustered together to form a ridge-like structure, and the connecting ridges eventually formed an irregular gully-network structure. Figure 1b confirms the top of each precursor nanowire gathering and fixing on the ridge to form a stable structure. Figure 1c shows that the precursor nanowires cross each other with a diameter of 50–100 nm, further improving the structure stability of the precursor nanowire array. Figure 1d displays the cross-sectional of the precursor nanowires. The cross-sectional presents a hexagon. It is possible to add anionic and cationic surfactants in a certain proportion during the preparation to make the solution more polar, which limits the lateral growth of nanowires (Stellner et al., 1986; Wu et al., 2013; Zhang et al., 2016). The precursor is converted into Co3O4 by the heat treatment. During the heat treatment, the precursor thermally decomposes to produce H2O and CO2 [reaction (6)], which is derived from the slow hydrolysis of urea [reaction (7)–(9)]. It has been reported that the slow hydrolysis of urea facilitates the growth of nanowires and has better crystallinity along the longitudinal axis. Synthesized ultra-long nanowires benefit from the addition of urea (Wang et al., 2012a). The hydrolyzed CO32- and OH combine with Co2+ to form the precipitate Co(CO3)0.5(OH)·0.11H2O (reaction (10): (Fan et al., 2017).

3Co(CO3)0.5(OH)·0.11H2OΔCo3O4+1.83H2O↑+1.5CO2    (6)
H2NCONH2+H2 2NH3+CO2    (7)
CO2+H2 CO32-+2H+    (8)
NH3+H2 NH4++OH-    (9)
Co2++0.5CO32-+OH-+0.11H2 Co(CO3)0.5(OH)·0.11H2O↓    (10)

The SEM images of Co3O4 NWAs on Ni foam obtained after annealing are shown in Figures 2b–f. Comparing Figures 2a,b, it can be seen that the gully-network structure does not change significantly before and after annealing. Because the gully-network structure makes the nanowires cross each other so that the nanowires can be fixed. Therefore, it has a good spatial buffer to adapt to the volume change in the annealing process. Further magnification of Figure 2c shows the sides of the gully-network structure, where the nanowires gather along the gully orderly and form a hemp rope structure at the top, so that the nanowire array forms a tight whole. As shown in Figure 2d, the Co3O4 nanowires diameter is 40–70 nm, which is 10–30 nm smaller than the precursor nanowire, owing to the loss of CO2 and H2O during annealing treatment (Guan et al., 2017).

FIGURE 1
www.frontiersin.org

Figure 1. (a–c) SEM images of precursor nanowire arrays on Ni foam at different magnifications, (d) the cross-sectional SEM image of the precursor nanowires.

FIGURE 2
www.frontiersin.org

Figure 2. (a) SEM images of precursor nanowire arrays on Ni foam, (b–d) SEM images of Co3O4 NWAs on Ni foam at different magnifications, (e) TEM images (inset: SAED pattern) of Co3O4 nanowires, (f) HRTEM image of Co3O4 nanowires and corresponding FFT images (inset).

Co3O4 nanowires further characterized by TEM equipped with HRTEM and SAED as shown in Figures 2e,f. The surface of the Co3O4 nanowires (Figure 2e) is uneven and highly porous, providing more specific surface area and active sites. The SAED plot (inset in Figure 2e) displays the single crystal diffraction spots of Co3O4 nanowires, and diffraction spots of (220) (311) (511) (400) and (440) are observed. The long axis direction of the nanowires is perpendicular to the (220) crystal plane and the nanowires grow along the (110) crystallographic axis. It is worth noting that the crystal growth direction is different from that in other articles along the (111) direction (Xia et al., 2012). HRTEM image of the middle part of the Co3O4 nanowire (Figure 2e) is shown in Figure 2f. The lattice spacing of the vertical lattice fringes is 0.202 and 0.143 nm corresponds to the (004) and (440) crystal planes of Co3O4 (JCPDS card no.42-1467). In addition, there are two crystal planes with the same lattice spacing of 0.233 nm on the HRTEM image, corresponding to the (222) and (2-2-2) crystal planes of Co3O4 with the crystal plane angle of 109.5°. The FTT corresponding to HRTEM is shown in the inset in Figure 2f, which exhibits the (222) and (2-2-2) crystal planes compared to SAED. Obviously noticed that there is no complete and clear lattice fringes in the dotted circle. The dashed circle may be a surface defect because of the loss of CO2 and H2O during the annealing treatment, which has high electrochemical activity and improves electrochemical performance.

XRD, Raman spectrum, and XPS are used to analysis the crystal structure of Co3O4 NWAs. The XRD pattern of the precursor in Figure S1A is consistent with Co(CO3)0.5(OH)·0.11H2O (JCPDS card no. 48-0083) (Xiong et al., 2012). After annealing, the XRD pattern is shown in Figure 3A. Except for the three diffraction peaks of the Ni foam (JCPDS card no. 04-0850) (Yu et al., 2015), the remaining diffraction peaks exactly corresponds to Co3O4 (JCPDS card no. 42-1467) (Che et al., 2014). Figure S1B indicates the Raman spectra with Raman peaks appearing at 476, 516, 605, 675 cm−1 corresponding to Eg, F2g1, F2g2, and A1g peaks of Co3O4 (Kim et al., 2011). To study the chemical bonding state of Co3O4 NWAs, XPS measurement is utilized. Three elements of Co, O, and C in the XPS spectrum (Figure 3B) can be noted and no other elements are found, indicating that there are no impurities in the synthesis of Co3O4 NWAs. Figure 3C shows the XPS spectrum of Co2p with two sets of peaks, Co 2p3/2 (781.2 eV/779.7 eV) and Co 2p1/2 (796.7 eV/795.0 eV), which are consistent with Co2+/Co3+ in Co3O4 NWAs, respectively (Hu et al., 2016; Zhang et al., 2019). Two satellite peaks of sat.Co 2p3/2 (786.6 eV) and sat.Co 2p1/2 (803.6 eV) are also observed (Li et al., 2014). The O 1 s spectrum (Figure 3D) consists of 529.7, 531.3, and 533.3 eV. These three peaks represent the O element in Co3O4, the O element in the water adsorbed on the surface, and the oxygen vacancies formed by gas escape during annealing, respectively (Xiong et al., 2009; Qu et al., 2017). Co3O4 NWAs is further demonstrated the successful synthesis by XPS.

FIGURE 3
www.frontiersin.org

Figure 3. (A) XRD patterns of Co3O4 NWAs on Ni foam, (B) XPS spectra of Co3O4 NWAs, (C) XPS survey scan of Co 2p, and (D) XPS survey scan of O 1 s.

Electrochemical performance evaluations of Co3O4 NWAs with gully-network structure are conducted by CV, GCD, and EIS techniques. As shown in Figure 4A, the CV curve of Co3O4 NWAs on Ni foam obtained in potential range of 0–0.6 V at the scan rate from 2 to 100 mv s−1 shows a pair of reversible redox peaks at 0.36 and 0.26 V, displaying a typical faraday behavior (Guan et al., 2017). It is known that the redox reaction occurs between Co3O4 and OH in the electrolyte. No OH in the electrolyte, no redox reaction occurs. To confirm the above conclusion, the electrochemical tests of Co3O4 NWAs under alkaline and neutral electrolyte conditions are shown in Figure S2. The results from Figure S2a show that the area of the CV curve in the alkaline electrolyte is significantly larger than that in the neutral electrolyte. It indicates that although the Co3O4 NWAs possesses a large specific surface area, the provided double layer capacitance is very limited, so the faraday behavior is dominant. Meanwhile, the reversible redox reactions occurred are as follows:

Co3O4 + OH- + H2 3CoOOH + e-    (11)
CoOOH + OH-  CoO2 + H2+ e-    (12)

It is noteworthy that the anode and cathode peaks move slightly toward the high and low potentials, respectively, as the scan rate increases. The above phenomenon can be ascribed to the internal ion diffusion resistances enhancing with the increase of the scan rates. However, there is no significant shift in the redox peak, indicating that the electrode exhibits good reaction kinetics (Wang et al., 2012b; Raj et al., 2015). In addition, the nanowire array has a porous structure, which facilitates rapid reversible oxidation-reduction reactions. Figure 4B displays the GCD curves of Co3O4 NWAs at different current densities under 0–0.5 V, which presents the excellent symmetry of the charge-discharge curves and no significant voltage drop can be observed, indicating the small electrode resistances of the electrodes. Figure 4C shows the specific capacity values at different current densities calculated from the discharge time in Figure 4B. It is clearly observed that a high specific capacity is 582.8 C g−1 at a current density of 1 A g−1 can be achieved. The specific capacity still maintains 84.8% with the value of 494 C g−1 when the current density increases to 20 A g−1, which reveals the excellent rate performance of the Co3O4 NWAs electrode. Furthermore, the long-term cycling stability of the Co3O4 NWAs electrode at 15 A g−1 is presented in Figure 4D. As the cycle progressed, the capacity showed a trend of first increase and then decrease behaviors. The initial increase can be attributed to the activation process of the Co3O4 NWAs electrode. After that, the slow decay started due to the inactivation of the structure. More remarkably, the capacity still maintains 93.1% after 25,000 cycles, indicating excellent long-term cycling stability. Compared with the related literatures, the 3D gully-network structure Co3O4 NWAs has the superior electrochemical performances, especially the cyclic stability (Table 1). The inset in Figure 4D shows the final GCD curve during the cycles, which is basically consistent with that before the cycles, demonstrating wonderful reversibility of the Co3O4 NWAs electrode. The SEM images before and after 25,000 cycles are exhibited in Figure 5, from which the microstructure of the Co3O4 NWAs remained essentially intact, indicating the outstanding stability of the gully-network structure. With the unique structure, the electrode would possess excellent adaptability to the volume expansion and contraction during the cycle, thus resulting in the brilliant cycling performance.

FIGURE 4
www.frontiersin.org

Figure 4. (A) CV curves of the Co3O4 NWAs electrode at various scan rates, (B) Galvanostatic charge-discharge curves of the Co3O4 NWAs electrode at different current densities, (C) Specific capacitance of the Co3O4 NWAs electrodes at different current densities. (D) Long-term cycling stability of the Co3O4 NWAs electrode at 15 A g−1(The inset shows the galvanostatic charge-discharge curves of the last 8 cycles).

TABLE 1
www.frontiersin.org

Table 1. Comparison of the specific capacity for Co3O4 nanomaterials.

FIGURE 5
www.frontiersin.org

Figure 5. SEM images of Co3O4 NWAs electrode before (a) and after (b) 25,000 cycles.

In order to determine the changes about the resistance of the Co3O4 NWA electrode, the EIS analysis are applied before and after 25,000 cycles (Figure 6). The Nyquist plot is divided into the high-frequency region of the curve portion and the low-frequency region of the straight-line portion. The high-frequency region is controlled by the electrode reaction kinetics to represent the charge transfer resistance (Rct), and the low-frequency region can be stand for the diffusion resistance (W) between the electrolyte and the electrode material. In addition, the intersection point between the impedance curve and the horizontal axis is the intrinsic resistance (Rs) of the electrode (Xiong et al., 2012; Yang et al., 2013; Cai et al., 2014; Xu et al., 2016). The inset of Figure 6 shows that the intrinsic resistance of Co3O4 NWAs decreases after 25,000 cycles (from 0.72 to 0.66 Ω). It may be that a portion of the Co3O4 NWAs breaks away from the Ni foam during the cycles, resulting in the intrinsic resistance decrease. The Rct (from 1 to 1.66 Ω) and W (from 0.06 to 0.21 Ω) before and after the cycle were observed to increase. This phenomenon is probably due to the breakage of fewer nanowires during the cycles, leading to the destruction of the path with the smallest electrical resistance transported between the Co3O4 NWAs and Ni foam and thereby increasing the charge transfer resistance and diffusion resistance. In general, the impedances are approximately the same before and after 25,000 cycles, which further proves that the gully-network structure of Co3O4 NWAs possess excellent cycling stability.

FIGURE 6
www.frontiersin.org

Figure 6. Nyquist plots of Co3O4 NWAs Electrodes before and after 25,000 cycles (inset is the enlarged view of the Nyquist diagram and equivalent circuit).

To explore the practical application of Co3O4 NWAs electrodes, the Co3O4 NWAs//AC hybrid-supercapacitor based on the Co3O4 NWAs positive electrode and AC negative electrode is successfully assembled. Figure 7A shows the CV curves of the Co3O4 and AC electrode materials at a scan rate of 20 mv s−1 in a three-electrode system. The voltage window of the AC negative electrode ranges from −1 to 0 V, and the curve exhibits a typical double-layer behavior with a quasi-rectangular shape. Meanwhile, the positive voltage window of the Co3O4 NWAs electrode is 0–0.6 V, and the obvious redox peaks suggest the faraday behavior. The CV curves of the voltage window ranging from 0–0.8 V to 0–1.6 V for the Co3O4 NWAs//AC hybrid-supercapacitor device at a scan rate of 20 mv s−1 are shown in Figure 7B. The area of the CV curve becomes larger as the voltage window increases and no obvious redox peaks appear, indicating a good capacitive behavior. A significant polarization occurs when the voltage window increases to 1.6 V, so the voltage window choose to be 0–1.5 V. Figure 7C displays the CV curves at different scan rates under 0–1.5 V, presenting that a square-like curve remains similar at high scan rates. The GCD curves at different current densities are shown in Figure 7D, which displays good supercapacitive behavior and agrees with the CV curve results. A specific capacity of 162 C g−1 at 0.2 A g−1 of the device can be achieved and still remains 78 C g−1 at a high current density of 10 A g−1. Figure 7E is Ragone plots of the Co3O4 NWAs//AC devices based on the GCD discharge time, which shows that an energy density of 33.8 W h kg−1 at a power density of 224 W kg−1 is obtained. Even at a high power density of 12,000 W kg−1, an energy density of 16.25 W h kg−1 can also be kept. The energy and power densities of the Co3O4 NWAs//AC hybrid-supercapacitor are much higher than those of some other electrode materials, such as Co3O4//AC (24.9 Wh Kg−1 at 225 W Kg−1) (Zhang et al., 2013), α-Co(OH)2/Co3O4//AC (19.2 Wh Kg−1 at 145 W Kg−1) (Jing et al., 2014), Co3O4@MnO2//MEGO (17.7 Wh Kg−1 at 750 W Kg−1) (Huang et al., 2014). To evaluate the practical application of the device, the cycle performance of the hybrid-supercapacitor device is measured at a current density of 2 A g−1 (Figure 7F). It can be observed that the hybrid-supercapacitor devices assembled with Co3O4 NWAs also exhibits excellent cycle behaviors, maintaining a specific capacity of 74% after 10,000 cycles. The gully-network structure of Co3O4 NWAs materials ensures the stability of the structure and reduces the loss of capacity during the cycles. Moreover, the Co3O4 NWAs//AC hybrid-supercapacitor devices successfully light four LED lamps (inset in Figure 7F), illustrating that the as-prepared Co3O4 NWAs//AC devices can be wildly utilized for practical applications.

FIGURE 7
www.frontiersin.org

Figure 7. (A) The CV curve of AC electrode and Co3O4 NWAs electrode at a scan rate of 20 mV s−1, (B) CV curves of Co3O4 NWAs//AC device at different potential ranges, (C) CV curves of Co3O4 NWAs//AC device at different scan rates, (D) GCD curves of Co3O4 NWAs//AC device at different current densities, (E) Ragone plot of the Co3O4 NWAs//AC device, (F) Cycling performance of the Co3O4 NWAs//AC device at a current density of 2 A g−1 (inset is the photo of the lighted LED by the double Co3O4 NWAs//AC device).

The admirable electrochemical behaviors of the Ni foam supported Co3O4 battery-type electrode materials for hybrid-supercapacitor can be ascribed to the following aspect: Firstly, the highly stable gully-network of Co3O4 NWAs effectively alleviates the volume expansion and contraction during the long cycle measurements and prevents the agglomeration of active materials, generating the outstanding cycle stability. Meanwhile, its porous structure enables the electroactive material to be completely exposed in the electrolyte solution, which facilitates the diffusion of ions and electrons, and allows strong storage of ions, resulting in excellent cycle stability. Secondly, the highly porous interconnected nanowire arrays consisted of numerous highly crystalline nanoparticles can greatly facilitate electrolyte transport and increase the surface area, thus promoting the electrolyte to easily diffuse into the inner region of the electrode. Finally, the direct growth of Co3O4 NWAs on Ni foam can significantly improve electrical conductivity, creating an expressway for electric charge transfer and resulting in desirable rate capability.

Conclusion

3D gully-network structure Co3O4 NWAs directly grown on Ni foam have been successfully prepared via a facile and scalable hydrothermal procedure followed by calcination treatment. The unique porous gully-network structure of the Co3O4 NWAs electrode can offer large surface area, provide open channels for efficient ion transport as well as adaptability to the volume expansion and contraction during electrochemical reactions, which greatly improve the specific capacity, rate capability, and cycling stability of the Co3O4 NWAs electrode. When evaluated as a binder-free electrode for battery-type supercapacitor, unexceptionable faraday behaviors in terms of high specific capacity (582.8 C g−1 at a current density of 1 A g−1), desirable rate capability (with capacity retention about 84.8% at 20 A g−1), and outstanding cycle performance (93.1% capacity retention after 25,000 cycles) can be achieved. More remarkably, an energy density of 33.8 W h kg−1 at a power density of 224 W kg−1 and wonderful cycling stability with 74% capacity retention after 10,000 cycles can be acquired based on the hybrid-supercapacitor with the as-prepared Co3O4 NWAs positive electrode. All the excellent supercapacitive behaviors illustrates that our unique gully-network structure Co3O4 nanowire arrays hold a great promise for constructing high-performance energy storage devices.

Author Contributions

CG design and performed the experiments. CG, MY, CW, JL, and CS prepared the samples and analyzed the data. CG, CJ, TL, LH, and YW participated in interpreting and analyzing the data. All authors read and approved the final manuscript.

Conflict of Interest Statement

The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.

Acknowledgments

The authors acknowledge the National Science Foundation of China (Grants 21201129, 51208333, 51374151) and the National Natural Science Foundation of Shanxi Province (2013011012-3) for providing funding support to the current work. CJ is grateful for support of the 100 Talented Team of Hunan Province and the 111 project (B12015) at the Key Laboratory of Advanced Energy Materials Chemistry (Ministry of Education), Nankai University.

Supplementary Material

The Supplementary Material for this article can be found online at: https://www.frontiersin.org/articles/10.3389/fchem.2018.00636/full#supplementary-material

References

Balasubramanian, S., and Kamaraj, P. K. (2015). Fabrication of natural polymer assisted mesoporous Co3O4/carbon composites for supercapacitors. Electrochim. Acta 168, 50–58. doi: 10.1016/j.electacta.2015.04.019

CrossRef Full Text | Google Scholar

Cai, D., Huang, H., Wang, D., Liu, B., Wang, L., Liu, Y., et al. (2014). High-performance supercapacitor electrode based on the unique ZnO@Co3O4 core/shell heterostructures on nickel foam. ACS Appl. Mater. Interfaces 6, 15905–15912. doi: 10.1021/am5035494

PubMed Abstract | CrossRef Full Text | Google Scholar

Chang, B., Gu, Z., Guo, Y., Li, Z., and Yang, B. (2016). Glucose-assisted synthesis of Co3O4 nanostructure with controllable morphologies from nanosheets to nanowires. J. Alloy Compd. 676, 26–36. doi: 10.1016/j.jallcom.2016.03.056

CrossRef Full Text | Google Scholar

Che, H., Liu, A., Hou, J., Zhang, X., Bai, Y., Mu, J., et al. (2014). Synthesis of one-dimensional porous Co3O4 nanobelts and their ethanol gas sensing properties. Mater. Res. Bull. 59, 69–76. doi: 10.1016/j.materresbull.2014.06.033

CrossRef Full Text | Google Scholar

Cui, S., Li, T., Guo, C., Wang, L., Zhang, C., Yan, Z., et al. (2019). Synthesis of mesoporous Co3O4/NiCo2O4 nanorods and their electrochemical study. J. Nanosci. Nanotechno. 19, 47–56. doi: 10.1166/jnn.2019.16448

CrossRef Full Text | Google Scholar

Dai, S., Liu, Z., Zhao, B., Zeng, J., Hu, H., Zhang, Q., et al. (2018). A high-performance supercapacitor electrode based on N-doped porous graphene. J. Power Sources 387, 43–48. doi: 10.1016/j.jpowsour.2018.03.055

CrossRef Full Text | Google Scholar

Dai, S., Zhao, B., Qu, C., Chen, D., Dang, D., Song, B., et al. (2017). Controlled synthesis of three-phase NixSy/rGO nanoflake electrodes for hybrid supercapacitors with high energy and power density. Nano Energy 33, 522–31. doi: 10.1016/j.nanoen.2017.01.056

CrossRef Full Text | Google Scholar

Fan, H., Yang, J., Huang, L., Chen, M., Shao, H., Wang, J., et al. (2017). Controllable fabrication of hierarchical top-converged Co3O4 nanowire array with enhanced lithium storage performance. Mater. Chem. Phys. 198, 107–114. doi: 10.1016/j.matchemphys.2017.05.063

CrossRef Full Text | Google Scholar

Gao, L., Xu, S., Xue, C., Hai, Z., Sun, D., and Lu, Y. (2016). Self-assembly of hierarchical 3D starfish-like Co3O4 nanowire bundles on nickel foam for high-performance supercapacitor. J. Nanopart Res. 18:112. doi: 10.1007/s11051-016-3419-9

CrossRef Full Text | Google Scholar

Gao, X., Zhang, Y., Huang, M., Li, F., Hua, C., Yu, L., et al. (2014). Facile synthesis of Co3O4@NiCo2O4 core-shell arrays on Ni foam for advanced binder-free supercapacitor electrodes. Ceram Int. 40, 15641–15646. doi: 10.1016/j.ceramint.2014.07.084

CrossRef Full Text | Google Scholar

Guan, C., Zhao, W., Hu, Y., Lai, Z. Li, X., Sun, S., et al. (2017). Cobalt oxide and N-doped carbon nanosheets derived from a single two-dimensional metal-organic framework precursor and their application in flexible asymmetric supercapacitors. Nanoscale Horiz. 2, 99–105. doi: 10.1039/C6NH00224B

CrossRef Full Text | Google Scholar

Hu, Q., Gu, Z., Zheng, X., and Zhang, X. (2016). Three-dimensional Co3O4@NiO hierarchical nanowire arrays for solid-state symmetric supercapacitor with enhanced electrochemical performances. Chem. Eng. J. 304, 223–231. doi: 10.1016/j.cej.2016.06.097

CrossRef Full Text | Google Scholar

Huang, M., Zhang, Y., Li, F., Zhang, L., Wen, Z., and Liu, Q. (2014). Facile synthesis of hierarchical Co3O4@MnO2 core-shell arrays on Ni foam for asymmetric supercapacitors. J. Power Sources 252, 98–106. doi: 10.1016/j.jpowsour.2013.12.030

CrossRef Full Text | Google Scholar

Huang, M., Zhao, X., Li, F., Li, W., Zhang, B., and Zhang, Y. (2015). Synthesis of Co3O4/SnO2@MnO2 core-shell nanostructures for high-performance supercapacitors. J. Mater. Chem. A 3, 12852–12857. doi: 10.1039/C5TA02144H

CrossRef Full Text | Google Scholar

Jang, G. S., Ameen, S., Akhtar, M. S., Kim, E., and Shin, H. S. (2017). Electrochemical investigations of hydrothermally synthesized porous cobalt oxide (Co3O4) nanorods: supercapacitor application. Chem. Select. 2, 8941–8949. doi: 10.1002/slct.201701571

CrossRef Full Text | Google Scholar

Jiang, W., Hu, F., Yan, Q., and Wu, X. (2017). Investigation on electrochemical behaviors of NiCo2O4 battery-type supercapacitor electrodes: the role of an aqueous electrolyte. Inorg. Chem. Front. 4, 1642–1648. doi: 10.1039/C7QI00391A

CrossRef Full Text | Google Scholar

Jiang, Y., Chen, L., Zhang, H., Zhang, Q., Chen, W., Zhu, J., et al. (2016). Two-dimensional Co3O4 thin sheets assembled by 3D interconnected nanoflake array framework structures with enhanced supercapacitor performance derived from coordination complexes. Chem. Eng. J. 292, 1–12. doi: 10.1016/j.cej.2016.02.009

CrossRef Full Text | Google Scholar

Jing, M., Yang, Y., Zhu, Y., Hou, H., Wu, Z., Chen, Q., et al. (2015). Alternating voltage induced porous Co3O4 sheets: an exploration of its supercapacity properties. RSC Adv. 5, 177–183. doi: 10.1039/C4RA09869B

CrossRef Full Text | Google Scholar

Jing, M., Yang, Y., Zhu, Y., Hou, H., Wu, Z., and Ji, X. (2014). An asymmetric ultracapacitors utilizing α-Co(OH)2/Co3O4 flakes assisted by electrochemically alternating voltage. Electrochim. Acta 141, 234–40. doi: 10.1016/j.electacta.2014.07.075

CrossRef Full Text | Google Scholar

Kim, H., Seo, D. H., Kim, S. W., Kim, J., and Kang, K. (2011). Highly reversible Co3O4/graphene hybrid anode for lithium rechargeable batteries. Carbon 49, 326–332. doi: 10.1016/j.carbon.2010.09.033

CrossRef Full Text | Google Scholar

Kong, S., Yang, F., Cheng, K., Ouyang, T., Ye, K., Wang, G., et al. (2017). In-situ growth of cobalt oxide nanoflakes from cobalt nanosheet on nickel foam for battery-type supercapacitors with high specific capacity. J. Electroanal. Chem. 785, 103–108. doi: 10.1016/j.jelechem.2016.12.002

CrossRef Full Text | Google Scholar

Kuang, M., Li, T. T., Chen, H., Zhang, S. M., Zhang, L. L., and Zhang, Y. X. (2015). Hierarchical Cu2O/CuO/Co3O4 core-shell nanowires: synthesis and electrochemical properties. Nanotechnology 26:304002. doi: 10.1088/0957-4484/26/30/304002

PubMed Abstract | CrossRef Full Text | Google Scholar

Li, X., Yang, S., Sun, J., He, P., Pu, X., and Ding, G. (2014). Enhanced electromagnetic wave absorption performances of Co3O4 nanocube/reduced graphene oxide composite. Synthetic Met. 194, 52–58. doi: 10.1016/j.synthmet.2014.04.012

CrossRef Full Text | Google Scholar

Liu, W., Li, X., Zhu, M., and He, X. (2015). High-performance all-solid state asymmetric supercapacitor based on Co3O4 nanowires and carbon aerogel. J. Power Sources 282, 179–186. doi: 10.1016/j.jpowsour.2015.02.047

CrossRef Full Text | Google Scholar

Mao, Y. Q., Li, T. T., Guo, C. L., Zhu, F. C., Zhang, C. C., Wei, Y. H., et al. (2016). Cycling stability of ultrafine β-Ni(OH)2 nanosheets for high capacity energy storage device via a multilayer nickel foam electrode. Electrochim. Acta. 211, 44–51. doi: 10.1016/j.electacta.2016.06.027

CrossRef Full Text | Google Scholar

Qing, X., Liu, S., Huang, K., Lv, K., Yang, Y., Lu, Z., et al. (2011). Facile synthesis of Co3O4 nanoflowers grown on Ni foam with superior electrochemical performance. Electrochim. Acta 56, 4985–4991. doi: 10.1016/j.electacta.2011.03.118

CrossRef Full Text | Google Scholar

Qu, C., Zhao, B., Jiao, Y., Chen, D., Dai, S., Deglee, B. M., et al. (2017). Functionalized bimetallic hydroxides derived from metal–organic frameworks for high-performance hybrid supercapacitor with exceptional cycling stability. ACS Energy Lett. 2, 1263–9. doi: 10.1021/acsenergylett.7b00265

CrossRef Full Text | Google Scholar

Raj, R. P., Ragupathy, P., and Mohan, S. (2015). Remarkable capacitive behavior of a Co3O4-polyindole composite as electrode material for supercapacitor applications. J. Mater. Chem. A 3, 24338–24348. doi: 10.1039/C5TA07046E

CrossRef Full Text | Google Scholar

Rajeshkhanna, G., Umeshbabu, E., and Rao, G. R. (2016). In situ grown nano-architectures of Co3O4 on Ni-foam for charge storage application. J. Chem. Sci. 129, 157–166. doi: 10.1007/s12039-016-1212-z

CrossRef Full Text

Ren, X. C., Guo, C. L., Xu, L. Q., Li, T. T., Hou, L. F., and Wei, Y. H. (2015). Facile synthesis of hierarchical mesoporous honeycomb-like NiO for aqueous asymmetric supercapacitors. ACS Appl. Mater. Inter. 7, 19930–1940. doi: 10.1021/acsami.5b04094

PubMed Abstract | CrossRef Full Text | Google Scholar

Shao, J., Zhou, X., Liu, Q., Zou, R., Li, W., Yang, J., et al. (2015). Mechanism analysis of the capacitance contributions and ultralong cycling-stability of the isomorphous MnO2@MnO2 core/shell nanostructures for supercapacitors. J. Mater. Chem. A 3, 6168–6176. doi: 10.1039/C4TA06793B

CrossRef Full Text | Google Scholar

Stellner, K. L., Amante, J. C., Scamehorn, J. F., and Harwell, J. H. (1986). Precipitation phenomena in mixtures of anionic and cationic surfactants in aqueous solutions. J. Colloid Interf. Sci. 123, 186–200. doi: 10.1016/0021-9797(88)90235-4

CrossRef Full Text | Google Scholar

Wang, B., Zhu, T., Wu, H. B., Xu, R., Chen, J. S., and Lou, X. W. (2012a). Porous Co3O4 nanowires derived from long Co(CO3)0.5(OH)·0.11H2O nanowires with improved supercapacitive properties. Nanoscale 4, 2145–2149. doi: 10.1039/c2nr11897a

PubMed Abstract | CrossRef Full Text | Google Scholar

Wang, G., Zhang, L., and Zhang, J. (2012b). A review of electrode materials for electrochemical supercapacitors. Chem. Soc. Rev. 41, 797–828. doi: 10.1039/C1CS15060J

PubMed Abstract | CrossRef Full Text | Google Scholar

Wang, X., Li, M., Chang, Z., Wang, Y., Chen, B., Zhang, L., et al. (2015). Orientated Co3O4 nanocrystals on MWCNTs as superior battery-type positive electrode material for a hybrid capacitor. J. Electrochem. Soc. 162, A1966–A1971. doi: 10.1149/2.0041511jes

CrossRef Full Text | Google Scholar

Wang, X., Wu, X., Xu, B., and Hua, T. (2016). Coralloid and hierarchical Co3O4 nanostructures used as supercapacitors with good cycling stability. Solid State Electron. 20, 1303–1309. doi: 10.1007/s10008-016-3125-7

CrossRef Full Text | Google Scholar

Wang, X., Xia, H., Wang, X., Gao, J., Shi, B., and Fang, Y. (2016). Facile synthesis ultrathin mesoporous Co3O4 nanosheets for high-energy asymmetric supercapacitor. J. Alloy Compd. 686, 969–975. doi: 10.1016/j.jallcom.2016.06.156

CrossRef Full Text | Google Scholar

Wang, Y., Lei, Y., Li, J., Gu, L., Yuan, H., and Xiao, D. (2014). Synthesis of 3D-nanonet hollow structured Co3O4 for high capacity supercapacitor. ACS Appl. Mater. Inter. 6, 6739–6747. doi: 10.1021/am500464n

PubMed Abstract | CrossRef Full Text | Google Scholar

Wu, C., Lou, X., and Jia, C. (2019). Porous Ni-Mo-Co hydroxide nanoflakes on carbon cloth for supercapacitor application. J. Nanosci. Nanotechno. 19, 272–6. doi: 10.1166/jnn.2019.16450

PubMed Abstract | CrossRef Full Text | Google Scholar

Wu, C., Zhu, Y., Ding, M., Jia, C., and Zhang, K. (2018). Fabrication of plate-like MnO2 with excellent cycle stability for supercapacitor electrodes. Electrochim. Acta 291, 249–255. doi: 10.1016/j.electacta.2018.08.126

CrossRef Full Text | Google Scholar

Wu, J. B., Li, Z. G., Huang, X. H., and Lin, Y. (2013). Porous Co3O4/NiO core/shell nanowire array with enhanced catalytic activity for methanol electro-oxidation. J. Power Sources 224, 1–5. doi: 10.1016/j.jpowsour.2012.09.085

CrossRef Full Text | Google Scholar

Xia, X. H., Tu, J. P., Zhang, Y. Q., Mai, Y. J., Wang, X. L., Gu, C. D., et al. (2012). Freestanding Co3O4 nanowire array for high performance supercapacitors. RSC Adv. 2, 1835–1841. doi: 10.1039/c1ra00771h

CrossRef Full Text | Google Scholar

Xiong, S., Chen, J. S., Lou, X. W., and Zeng, H. C. (2012). Mesoporous Co3O4 and CoO@C topotactically transformed from chrysanthemum-like Co(CO3)0.5(OH)·0.11H2O and their lithium-storage properties. Adv. Funct. Mater. 22, 861–71. doi: 10.1002/adfm.201102192

CrossRef Full Text | Google Scholar

Xiong, S., Yuan, C., Zhang, X., Xi, B., and Qian, Y. (2009). Controllable synthesis of mesoporous Co3O4 nanostructures with tunable morphology for application in supercapacitors. Chemistry 15, 5320–5326. doi: 10.1002/chem.200802671

PubMed Abstract | CrossRef Full Text | Google Scholar

Xu, J., Liu, Y., He, L., Zhang, C., and Zhang, Y. (2016). Facile synthesis of CuO mesocrystal/MWCNT composites as anode materials for high areal capacity lithium ion batteries. Ceram Int. 42, 12027–12032. doi: 10.1016/j.ceramint.2016.04.129

CrossRef Full Text | Google Scholar

Xu, J., Tang, H., Xu, T., Wu, D., Shi, Z., Tian, Y., et al. (2017). Porous NiO hollow quasi-nanospheres derived from a new metal-organic framework template as high-performance anode materials for lithium ion batteries. Ionics 23, 3273–3280. doi: 10.1007/s11581-017-2160-4

CrossRef Full Text | Google Scholar

Yan, Z. Y., Guo, C. L., Yang, F., Zhang, C. C., Mao, Y. Q., Cui, S. X., et al. (2017). Cliff-like NiO/Ni3S2 directly grown on ni foam for battery-type electrode with high area capacity and long cycle stability. Electrochim. Acta. 251, 235–243. doi: 10.1016/j.electacta.2017.08.102

CrossRef Full Text | Google Scholar

Yang, W., Gao, Z., Ma, J., Wang, J., Wang, B., and Liu, L. (2013). Effects of solvent on the morphology of nanostructured Co3O4 and its application for high-performance supercapacitors. Electrochim. Acta 112, 378–85. doi: 10.1016/j.electacta.2013.08.056

CrossRef Full Text | Google Scholar

Yao, Y., McDowell, M. T., Ryu, I., Wu, H., Liu, N., Hu, L., et al. (2011). Interconnected silicon hollow nanospheres for lithium-ion battery anodes with long cycle life. Nano Lett. 11, 2949–54. doi: 10.1021/nl201470j

PubMed Abstract | CrossRef Full Text | Google Scholar

Yu, M. Q., Li, Y. H., Yang, S., Liu, P. F., Pan, L. F., Zhang, L., et al. (2015). Mn3O4 nano-octahedrons on Ni foam as an efficient three-dimensional oxygen evolution electrocatalyst. J. Mater. Chem. A 3, 14101–14104. doi: 10.1039/C5TA02988K

CrossRef Full Text | Google Scholar

Yuan, C., Yang, L., Hou, L., Shen, L., Zhang, X., and Lou, X. W. (2012). Growth of ultrathin mesoporous Co3O4 nanosheet arrays on Ni foam for high-performance electrochemical capacitors. Energy Environ. Sci. 5, 7883–7. doi: 10.1039/c2ee21745g

CrossRef Full Text | Google Scholar

Zeng, L., Lou, X., Zhang, J., Wu, C., Liu, J., and Jia, C. (2019). Carbonaceous mudstone and lignin-derived activated carbon and its application for supercapacitor electrode. Surf. Coatings Technol. 357, 580–586. doi: 10.1016/j.surfcoat.2018.10.041

CrossRef Full Text | Google Scholar

Zhang, C., Xie, L., Song, W., Wang, J., Sun, G., and Li, K. (2013). Electrochemical performance of asymmetric supercapacitor based on Co3O4/AC materials. J. Electroanaly. Chem. 706, 1–6. doi: 10.1016/j.jelechem.2013.07.032

CrossRef Full Text | Google Scholar

Zhang, F., Yuan, C., Lu, X., Zhang, L., Che, Q., and Zhang, X. (2012). Facile growth of mesoporous Co3O4 nanowire arrays on Ni foam for high performance electrochemical capacitors. J. Power Sources 203, 250–256. doi: 10.1016/j.jpowsour.2011.12.001

CrossRef Full Text | Google Scholar

Zhang, Q., Chen, H., Luo, L., Zhao, B., Luo, H., Han, X., et al. (2018). Harnessing the concurrent reaction dynamics in active Si and Ge to achieve high performance lithium-ion batteries. Energy Environ. Sci. 11, 669–681. doi: 10.1039/C8EE00239H

CrossRef Full Text | Google Scholar

Zhang, Q., Liu, Z., Zhao, B., Cheng, Y., Zhang, L., Wu, H., et al. (2019). Design and understanding of dendritic mixed-metal hydroxide nanosheets@N-doped carbon nanotube array electrode for high-performance asymmetric supercapacitors. Energy Storage Mater. 16, 632–645. doi: 10.1016/j.ensm.2018.06.026

CrossRef Full Text | Google Scholar

Zhang, X., Xiao, J., Zhang, X., Meng, Y., and Xiao, D. (2016). Three-dimensional Co3O4 nanowires@amorphous Ni(OH)2 ultrathin nanosheets hierarchical structure for electrochemical energy storage. Electrochim. Acta 191, 758–66. doi: 10.1016/j.electacta.2016.01.159

CrossRef Full Text | Google Scholar

Zhao, C., Huang, B., Fu, W., Chen, J., Zhou, J., and Xie, E. (2015). Fabrication of porous nanosheetbased Co3O4 hollow nanocubes for electrochemical capacitors with high rate capability. Electrochim. Acta 178, 555–563. doi: 10.1016/j.electacta.2015.08.057

CrossRef Full Text | Google Scholar

Keywords: Co3O4 nanowire arrays, 3D gully-network structure, hybrid-supercapacitor, stable cycle performance, battery-type electrode

Citation: Guo C, Yin M, Wu C, Li J, Sun C, Jia C, Li T, Hou L and Wei Y (2018) Highly Stable Gully-Network Co3O4 Nanowire Arrays as Battery-Type Electrode for Outstanding Supercapacitor Performance. Front. Chem. 6:636. doi: 10.3389/fchem.2018.00636

Received: 17 September 2018; Accepted: 07 December 2018;
Published: 21 December 2018.

Edited by:

Qiaobao Zhang, Xiamen University, China

Reviewed by:

Shenglin Xiong Xiong, Shandong University, China
Yuxin Zhang, Chongqing University, China
Junmin Xu, Zhengzhou University, China
Wei Luo, Donghua University, China

Copyright © 2018 Guo, Yin, Wu, Li, Sun, Jia, Li, Hou and Wei. This is an open-access article distributed under the terms of the Creative Commons Attribution License (CC BY). The use, distribution or reproduction in other forums is permitted, provided the original author(s) and the copyright owner(s) are credited and that the original publication in this journal is cited, in accordance with accepted academic practice. No use, distribution or reproduction is permitted which does not comply with these terms.

*Correspondence: Chunli Guo, guochunli@tyut.edu.cn
Chuankun Jia, jack2012ding@gmail.com

These authors have contributed equally to this work

Disclaimer: All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article or claim that may be made by its manufacturer is not guaranteed or endorsed by the publisher.