- Hunan Provincial Key Laboratory of Efficient and Clean Utilization of Manganese Resources, College of Chemistry and Chemical Engineering, Central South University, Changsha, China
Porous organic polymers (POPs), known for its high surface area and abundant porosity, can be easily designed and constructed at the molecular level. The POPs offer confined molecular spaces for the interplay of photons, excitons, electrons and holes, therefore featuring great potential in catalysis. In this review, a brief summary on the recent development of some current state-of-the-art POPs for photocatalytic water splitting and their design principles and synthetic strategies as well as relationship between structure and photocatalytic hydrogen or oxygen evolution performance are presented. Future prospects including research directions are also proposed, which may provide insights for developing POPs for photocatalytic water splitting with our expectations.
Introduction
Visible-light-driven water splitting via photocatalysis has witnessed explosive advances in the past decade, accompanying the enormous growth of the photocatalyst design. Among the intensely investigated systems, porous organic polymers (POPs) have demonstrated their ability to be a versatile platform for water splitting (Figure 1A). POPs are a kind of covalently connected polymers with high specific surface area and permanent, nanometer-scale pores which are beneficial to exposing active sites for catalytic conversions (Zhang and Riduan, 2012). Unlike the other porous counterparts such as zeolites, silicas, metal–organic frameworks (MOFs), metal–organic cages, POPs are designable; that is, the nature of building blocks including geometry and dimensions can be controlled targeting different functions. Besides, POPs connected through strong covalent linkages always feature high chemical and thermal stability, which is a prerequisite for recyclable photocatalytic application. In general, typical POPs mainly include conjugated microporous polymers (CMPs) (Jiang et al., 2008; Cooper, 2009; Schmidt et al., 2009), covalent triazine frameworks (CTFs) (Kuhn et al., 2008; Bojdys et al., 2010), and covalent organic frameworks (COFs) (Cote, 2005; Tilford et al., 2006; Ding and Wang, 2013; Huang et al., 2016).
Figure 1. (A) Schematic diagram of photocatalytic water splitting, inset is a skeleton of POPs (B) Scheme of basic processes in photocatalytic water splitting using semiconductors.
Given the high-throughput research efforts on photocatalytic hydrogen evolution reaction (HER), Wang et al summarized the progress on conjugated polymer catalysts for HER in 2016 (Zhang et al., 2016). However, boosting works on this field have been disclosed and the researches on photocatalytic oxygen evolution reaction (OER) also have gained fundamental understanding lately. Therefore, it is essential to give another review about the latest developments. Herein we summarize the synthetic strategy, molecular design, and functional modulation of CMPs, COFs and CTF, and more importantly highlight their performance for water splitting.
Basic Principles of Photocatalytic Water Splitting
From a fundamental perspective, overall water splitting into hydrogen and oxygen requires a change on the standard Gibbs free energy of ΔG0 of 237 kJ/mol (Equation 1) (Ananyev and Dismukes, 2005). The minimum band gap could be calculated by assuming that the water splitting energy was entirely converted from electrical work (Equation 2). In other words, the band gap should be over 1.23 eV to meet the requirement of thermodynamics of water splitting when the semiconductors are used as photocatalysts. Meanwhile, the band gap of visible light response-semiconductors should be lower than 3.0 eV (Equation 3), since broader band gap would result in a low efficiency in utilization of the visible light (>400 nm).
From aspect of specific processes, when semiconductors are stimulated by the photons, the electrons in the HOMO are placidly transited to the LUMO by overcoming the hindrance of the band gap (Figure 1B). In this process, the hole (h+) would be retained in the HOMO while the electron (e−) emerges in the LUMO. In the “photo-excited” state, most of electron-hole pairs are rapidly combined. Part of the electron-hole pairs migrate to the surface and would be captured by water, causing the effective water splitting. For porous catalysts, the high surface area and well-defined pore structure would effectively facilitate the exposure of available surface electron-hole pairs and are beneficial for transmission of reactants. Therefore, three key processes are vital for water splitting. First, capturing of photons, then separation and transportation of electron-hole pairs, and water splitting by electron-hole pairs.
Sacrificial agents and co-catalyst are generally used in most situations to improve the water splitting efficiency of an organic and polymeric photocatalyst system. Sacrificial agents were used to prohibit undesirable charge recombination. In other words, these sacrificial agents can quickly capture the photoexcited holes or electrons, and therefore promote the transformation. In typical HER processes, methanol, triethanolamine (TEOA) and lactic acid etc are usually used as sacrificial agents of holes, which are easier to be oxidized than water. Similarly, in OER process, silver nitrate (AgNO3) and sodium iodate (NaI) are used as sacrificial agents of electrons to accelerate water oxidation. Co-catalyst is cooperated to the photocatalytic system to reduce the potentials of hydrogen reduction and provide more active sites. Besides, the co-catalyst can promote the separation of the photoexcited electron-hole pairs on the photocatalyst surface, leading to an enhanced photocatalytic system. In a general HER, H2PtCl6 is loaded on the surface of polymers by photo-deposition method (Kaur et al., 2011; Ou et al., 2017). In addition, the transition metals in VIII clan such as Ru (Wang et al., 2009), Ni (Chang et al., 2015), Au and Ag (Paramasivam et al., 2008) can also be used as co-catalysts for photocatalytic water splitting.
When we assess a photocatalyst of water splitting, the rate of hydrogen or oxygen evolution is the most commonly used indicator of photocatalytic activity. However, the rates of evolution are susceptible to photodynamic conditions. Apparent quantum yield (AQY) that represents the efficiency of the photocatalytic process is more sensible for comparison (Zhang et al., 2016), but unfortunately absent in many studies. The AQY is calculated based on the equation (Zhang et al., 2013) as follows:
The stability of photocatalysts that determined by long time experiment or repeat experiment is indispensable. Generally, POP photocatalysts are durable relative to their counterparts, and only slight weakened activities that mainly cause by the inevitable photocorrosion. Other factors such as light absorbance, surface area, morphology, energy band and charge carrier separation and transport abilities may also exert an effect on the photocatalytic water splitting. Based on these parameters, we overviewed a range of structurally diversified POPs, and gave an explicit comparison of their photocatalytic activities for water splitting.
POPs for Water Splitting
Conjugated Microporous Polymers
Conjugated microporous polymers (CMPs) are comprised of π-conjugated scaffold and large electron delocalized network structure, which would be in favor of efficient light absorption and charge carrier transportation (Figure 2A). Various design strategies have been presented to improve the photocatalytic activities of CMPs (Li et al., 2016a,c,d).
Figure 2. (A) Structures of the CMPs. (B) SEM images of sheet-like morphology, the scale bars are 200 nm (Wang et al., 2017b). Reproduced with Permission from Wiley-VCH.
Pyrene and perylene are typical electron-rich units with unique optical activities such as high light-absorption coefficient and electron donating ability. Pioneering pyrene-based donor-π (D-π) CMPs for photocatalytic water splitting were proposed (Sprick et al., 2015). However, the hydrogen evolution rate of bare powder is rather low [174 μmol/(h g)] under visible light irradiation. Jiang and co-workers developed a series of perylene-based CMPs with analogical D-π molecular structures, while the hydrogen production rate is still unattractive with a value to 13 μmol/(h g) (PrCMP-3) (Xu et al., 2017). These results demonstrate that the photocatalytic performance of full donor based CMPs are still not satisfied due to the lack of internal polarization for effective charge separation process. Therefore, there is still much room for improvement and requires further rationally designing pyrene or perylene-based CMPs.
Bearing this in the mind, Jiang's group developed a series of acceptor contained pyrene-based CMPs by introducing different percentile electron-withdrawing benzothiadiazole into the skeleton. To note that the most active photocatalyst of PyBt-2 derived from copolymerization of donor units (i.e., 1,3,6,8-tetrabromopyrene) and accepter monomers(i.e., 4,7-dibromobenzo[c][1,2,5]thiadiazol) through a π linkage of 1,4-phenylene, which shows significantly enhanced photocatalytic activity for visible-light driven hydrogen evolution at a rate of 296 μmol/(h g) and considerable activity of OER (Xu et al., 2018). Clearly, D-A conjugated CMPs exhibit exceptional photocatalytic activities that can be finely tuned by adjusting the ratio of donor and acceptor units. When polarized skeleton favors the separation of electron-hole pairs, and fully conjugated skeleton favors the charges transport. There is still a “balance” in the competition of these two contributions, which requires a proper ratio of donor and aci-cepter. Besides, the sequence of polymer chain remains chaos while considering the different reactivity of comonomers.
Recently, more CMPs–based photocatalysts are rationally designed through the copolymerization of various ratios of photovoltaic donor and acceptor comonomers. Notably, the CMP derived from 4,8-di(thiophen-2-yl)benzo[1,2-b:4,5b']dithiophene chromophore (DBD) shows a significantly high hydrogen production rate up to about 1,914 μmol/(h·g) (Li et al., 2016a). The incorporation of nitrogen-doped acceptor ligand such as pyrazine and dipyridyl was also proved effectively to enhance the photocatalytic activity, and the hydrogen evolution rate is up to 2,590 μmol/(h·g) (Li et al., 2016d). The CMPs containing dibenzothiophene dioxide (DBTD) exhibit an exceptionally high rate up to 4,600 μmol/(h·g). Besides, DBTD-CMP-1 was demonstrated as an efficient photocatalyst for cocatalyst-free HER that produces hydrogen at rate of 2,460 μmol/(h·g) under visible-light irradiation (Wang et al., 2018). Above all, numerous units with specific electronic properties and geometry are introduced into the backbone of the D-A CMP catalytic system, and the visible-light driven hydrogen evolution rate is accelerated significantly.
The introduction of alkynyl groups into the conjugated polymers is an effective and facile strategy for developing photocatalyst for water splitting. Enhancement of photocurrent intensity and negative shift of LUMO levels are caused by the presence of the alkynyl groups, and improve visible-light-drived H2 production activity (Zhang et al., 2017b). The alkynyl-based CMPs obtained from the oxidation coupling of 1,3,5-triethynylbenzene (TEB) and 1,3,5-tris-(4-ethynylphenyl)-benzene (TEPB) can split water into stoichiometric hydrogen and oxygen at moderate evolution rates (218 and 102 μmol/(h·g) with high AQYs for overall water splitting (10.3 and 7.6%) under visible-light irradiation. In the study, the sheet-like morphology of polymers may enable the photogenerated excitons to be easy to access the polymer surface to drive redox reactions (Figure 2B), suppressing undesirable electron–hole recombination (Wang et al., 2017b). Similarly, alkynyl-based B-FOBT-1,3,5 with D-A conjugated structures show very impressive activity at a hydrogen evolution rate of 9,600 μmol/(h·g), and this enhancement is contributed by the D-A structure which facilitates proton-coupled electron transfer (PCET) process (Xiang et al., 2018).
The photocatalytic CMPs are facile to integrate with various monomers and optimize with optional ratio of different monomers via Suzuki-coupling, oxidative coupling and Sonogashira coupling etc. The copolymerization extends delocalized π-conjugation that is advantageous for harvest of photons, and the tunable polarized skeleton offers high efficient separation of electron-hole pairs. Briefly, CMPs are fully accessible to the box of photoactive units for creation of high-performance D-A skeleton, and this advantage makes CMP a frontier material with high activity on water splitting.
Covalent Triazine Frameworks
Covalent triazine frameworks (CTFs) which feature high thermal and chemical stability, were generally constructed from triazine precursors or aromatic nitriles. From a chemical view, triazine known as a nitrogen-rich conjugated unit with electron withdrawing character may act as the redox active site for photocatalytic water splitting (Schwinghammer et al., 2013, 2014; Stegbauer et al., 2014). Given these properties, CTFs are widely employed as heterogeneous catalysts (Puthiaraj et al., 2016) and have shown attracting photocatalytic activities under visible light irradiation (Li et al., 2016b; Qu et al., 2016; Meier et al., 2017).
CTF-1 was prepared from terephthalonitrile via an ionothermal method as a black monolithic powder (Figure 3A; Kuhn et al., 2008), which lacks sufficient thermodynamic driving force for photocatalytic water splitting. The reason may be that the partial carbonization of CTFs, then results in the narrowed band gap. Bearing this in mind, Lotsch et al optimized the ionothermal method using of low reaction temperature and long reaction time. The Pale yellow PTO-300 sample was obtained and shows enhanced HER rate (up to 1,000 μmol/(h·g)) under simulated sunlight irradiation (Figure 3B) (Schwinghammer et al., 2015). Therefore, the appropriate band gap is prerequisite to photocatalytic hydrogen production after avoiding unexpected carbonization. PTO-300 is of low degree for polymerization and insufficient delocalized conjugated system, hence it can be expected that novel synthesis strategies of CTFs may lead to further developments of photocatalysis.
Figure 3. (A) Notional structures of CTFs (CTF-1: n = 1; CTF-2: n = 2; CTF-3: n = 3. CTF-4: n = 4). (B) UV/vis absorptions and photographs (inset) of PTO-300, PTO-350, and CTF-1. (Schwinghammer et al., 2015). Reproduced with Permission from The Royal Society of Chemistry. (C) HER compare of CTF-1~ CTF-4 and Suzuki coupled CTF-2~ CTF-4 (Meier et al., 2017). Reproduced with Permission from Elsevier.
Latterly, more methods for constructing CTFs were proposed such as microwave assist-ionothermal method (Zhang et al., 2010a) and the use of strong Brønsted acid (Ren et al., 2012; Zhu et al., 2012). CTF-T1 was obtained from trifluoromethanesulfonic acid (TfOH) catalyzed trimerization of terephthalonitrile at room temperature, and gives an acceptable band gap of 2.94 eV (Bi et al., 2015). HER rate is competitive to g-C3N4 (Wang et al., 2009) and titanium dioxide nanocrystals (Chen et al., 2011), and considerably higher than ionothermal obtained triazine-based oligomers (Schwinghammer et al., 2015), the AQY of CTF-T1 is about 2.4% at 420 nm. Photocatalytic OER of CTF-T1 was also tested, however, the evolution rate is only 9 μmol/(h·g). Cooper et al synthesized a series of CTFs from CTF-1 to CTF-4, either by TfOH catalyzed trimerization of nitriles or by Suzuki-Miyaura polymerization (Figure 3A; Meier et al., 2017). The obtained CTFs show different band gaps with those of CTFs from Suzuki-Miyaura coupling, which is originated from the difference on the end-group nature and the defects in the materials. CTF-2 shows the highest HER (296 μmol/(h·g)) among the as-made materials while the HER of CTF-2-Suzuki is lower due to its low surface area (Figure 3C). It is attracting that the extension of phenylene spacer reduces thermodynamic driving force for water splitting but simultaneously broaden the visible-light absorbance. The photocatalytic activity of CTF photocatalytic system can be facilely regulated by a synergetic effect of light absorbance, band gap and surface area.
The next generation of porous materials, however, already seems to be underway, as represented by “porous photocatalysts for oxygen evolution” (Garcia-Esparza et al., 2017; Wang et al., 2017c; Zhang et al., 2017a). Considering the easy tailorable building blocks, CTF gives a synthetically versatile platform for photocatalytic water splitting. The nitrogen-rich framework provides active site for doping and coordination site for modification with metal-photocatalyst that facilitate to enhance the activity of CTF. Over the last couple of years, CTF attracts colossal interests by its extremely high activity on oxygen evolution. The narrow band gap and deep HOMO have indicate the strong oxidative activity of CTF, and a promising photocatalyst for water oxidation.
Typically, Wang et al described the preparation of cobalt-modified CTP-2 through trimerizations of 4,4'-biphenyldicarbonitrile and it shows the considerable photocatalytic activity of OER at a rate of 30 μmol/(h·g) under visible light irradiation (Lan et al., 2018). Moreover, a crystalline CTF-1-100W was prepared under mild microwave-assistance in the presence of TfOH, and the ordered in-plane skeleton has been retained with minimal carbonization. With a sufficient harvest of visible-light photon, appropriate energy band and low HOMO are the dominant factors for OER, and highest AQY (3.8% at 420 nm) of photocatalytic oxygen evolution is achieved. Remarkably, the CTF-1-100W is also efficient for HER with evolution rate of 5,500 μmol/(h·g) and AQY of 6% under visible-light irradiation (Xie et al., 2018). The photocatalytic activities can be significantly improved by doping methods (Figure 4A; Zhang et al., 2014; Ran et al., 2015). Li et al developed a sulfur-doped CTFS10 by annealing treatment with sulfur (Li et al., 2016b), and the rate of HER is estimated at 2,000 μmol/(h·g), which is four times higher than CTF-T1. The CTFS show smaller impedance of charge (Figure 4B) and lower intensity of photoexcited luminescence (Figure 4C) than CTF-T1, since introduction of electron-rich sulfur promotes the coupling between the triazine ring and the phenyl rings and impedes the recombination of photoexcited electron-hole pairs.
Figure 4. (A) Scheme of sulfur doping method on CTFs (B) EIS Nyquist plots and (C) Photocurrent response of CTF-T1 and CTFS (Li et al., 2016b). Reproduced with Permission from The Royal Society of Chemistry.
The modification of chemical composition and physical structure is a prospective strategy to enhance the activity of organic photocatalysts (Sun and Liang, 2017). The MoS2 quantum dots (QDs) was modified on CTF-T1 via the in situ photo-deposition method, which endow the synergistic composite an 8 times higher rate of HER than the pure CTF-T1 (Jiang et al., 2018). The strong electron interaction between MoS2 and CTF-T1 is a possible result from the formation of heterojunction (Christoforidis and Fornasiero, 2017), However, further investigation is still needed on these composite photocatalysts and the detailed mechanism remains unclear.
Most CTFs with good photocatalytic activity are amorphous in nature. The crystallinity facilitates the expose of photocatalytic activities of polymeric semiconductor (Wang et al., 2012; Zhang et al., 2015) due to their open-pore arrays. The strong Brønsted acid catalyst was used to reduce the carbonization, while damages the crystallinity of CTFs. Recently some novel synthesis method has been proposed such as low temperature polycondensation approaches (Wang et al., 2017a; Yu et al., 2018). The crystalline CTFs obtained by these mild approaches may show great potentials in photocatalytic water splitting. In addition, structural design and the synthetic process still challenge for CTFs, and more attentions still need to be paid to clarifying the relationships between its structure and photocatalytic properties.
Covalent Organic Frameworks
Covalent organic frameworks (COFs) represent a high crystalline type of POPs (Huang et al., 2016), which are precisely integrated into extended periodic skeletons via reverible condensation reaction such as Schiff base reaction (Cote, 2005). In comparison with other POPs, COFs featured attracting uniform porous structure and high ordered skeleton (Ding and Wang, 2013).
Recently, Lotsch and co-workers developed a series of azine COFs (Figure 5A) (Vyas et al., 2015) and the resultant N3-COF exhibits a hydrogen evolution rate at 1,703 μmol/(h·g) (Figure 5B). The activities of N1-COF~N3-COFs are positively correlated with crystallinity that increase along the series (Figure 5C). In order to further verify how the nitrogen content influence the activity of this photocatalytic system, another PTP-COF was also investigated (Figure 5D) (Haase et al., 2017). The nitrogen atoms in peripherals lead to irregular stacking of frameworks that causing a poor crystallinity, thus HER rate is sharp decrease to 84 μmol/(h·g) which an order of magnitude lower than the N3-COF (Figure 5E). As the unsatisfied activity of PTP-COF, it has more fluorescence-consuming recombination of electron-hole pairs than N3-COF, which are evidenced by the fluorescence decay (Figure 5F). Substitution of C-H units with N atoms on central aryl ring decreased the dihedral angle between the central aryl ring and the peripheral phenyl ring in the COF nodes, thus the enhanced activity is dominated by the increase in planarity of conjugated skeleton and crystallinity of material. The high planarity of conjugation increases charge carrier mobility, and crystallinity of COFs facilitates to prevent photoexcited electrons-holes recombination and decrease the trapping at defect sites.
Figure 5. (A) Structures of the Nx-COFs (X = Y = Z = C-H: N0-COF; X = N, Y = Z = C-H: N1-COF; X = Y = N, Z = C-H: N2-COF; X = Y = Z = N: N3-COF). PXRD patterns (B) and hydrogen evolution rates (C) of N0-COF to N3-COF (Vyas et al., 2015). Reproduced with Permission from Nature Publishing Group (D) Structures of the PTP-COF. Hydrogen evolution rates (E) and time correlated single-photon counting (TCSPC) decay trace (F) of PTP-COF (Haase et al., 2017). Reproduced with Permission from The Royal Society of Chemistry.
Three azine-linked COFs were constructed with pyrene building blocks that vary in number of substituted nitrogen atoms in peripheral phenyl ring (Figure 6A) (Stegbauer et al., 2018). The photocatalytic activities of A-TEXPY-COFs are highly relevant with the stability of intermediate of water splitting. Upon increasing stabilization of radical anion that conceivable intermediate of electron-rich n-type semiconductor, the rate of hydrogen evolution is dramatically higher (Figures 6B, C). The theoretical calculation of the stabilization of intermediate could be an effective guidance for molecular designation of high-performance photocatalytic COF.
Figure 6. (A) Structures of the A-TEXPY-COFs (X = Y = C-H: A-TEBPY-COF; X = N, Y = C-H: A-TENPY-COF; X = Y = N: A-TEPPY-COF). (B) Hydrogen evolution rates of A-TEXPY- COFs. (C) Comparison of vertical radical cation and radical anion stabilization energies relative to the A-TEBPY COF system (Stegbauer et al., 2018). Reproduced with Permission from Wiley.
The β-ketoenamine linked COFs are constructed by Schiff-base condensation of alkynyl functionalized amines with 1,3,5-triformylphloroglucinol (Figure 7A). The diacetylene functionalized COF exhibits relative high rates of HER (at average 324 μmol/(h·g)) (Figures 7B, C). Most importantly, a high AQY at 1.8% was obtained under 520 nm light irradiation (Pachfule et al., 2018). Similar to the CMP, design principle that introducing alkynyl group is an efficient strategy to promote the hydrogen production activity. This reduces the LUMO and broadens the visible-light absorbance of the polymer.
Figure 7. (A) Structures and (B,C) hydrogen evolution rates of TP-BDDA-COF, TP-EDDA-COF and TP-DTP-COF (Pachfule et al., 2018). Reproduced with Permission from American Chemical Society.
Up to now most studies on COFs for photocatalytic hydrogen production use platinum as the co-catalyst. More recently, Lotsch and co-workers presented a noble-metal-free photocatalytic hydrogen production using N2-COF as photocatalyst (Figure 8A) (Banerjee et al., 2017). Interestingly, non-precious-metal-based cobaloxime was used as co-catalyst, and a higher hydrogen evolution rate at 782 μmol/(h·g) was achieved compared to that using platinum as co-catalyst (Figure 8B). This result is attributable to the more efficient monometallic electron transfer from COF to the cobalt co-catalyst, and cobalt is the primary active site.
Figure 8. (A) Schematic representation of photocatalytic hydrogen evolution with N2-COF and Co-co-catalyst. (B) Hydrogen evolution rate of N2-COF and Cobalt co-catalyst as well as N2-COF and metallic platinum in the presence of TEOA (Banerjee et al., 2017). Reproduced with Permission from American Chemical Society.
COFs are supramolecular architectures as they are precise predesigned and regular integrated, and their optical and electronic properties can be easily optimized. By virtue of their explicit structure, lots of theoretical calculation has been presented to reveal the structure-properties relationship, as they accurately predict the energy band and the stability of the intermediate.
Conclusion and Comparison
Above all, the development of POPs for photocatalytic water splitting is promising while still challenging. Rapid progress in the past 2–3 years in the design and synthesis of POPs has revealed their great potential as tailorable materials platforms for structural and functional design of high performance catalyst. This minireview has given a slight inspiration on design, synthesis and modulation of POPs for photocatalytic hydrogen production and oxygen production. Nowadays, metal oxides as photocatalyst are most extensively studied for hydrogen production (Kudo and Miseki, 2009; Chen et al., 2010), and carbon nitrogen materials are high efficiency photocatalysts which attract much attention in recent years (Lin et al., 2016; Zhang et al., 2018). As a competitor to these state-of the-art photocatalysts, plenty of well-designed POPs with diverse building blocks, synthetic methods and versatile functionality are disclosed. More specifically, CMPs are facility to processing from diverse monomers, and allow the easy introduction of task-specific functional group to modulate its photocatalytic properties. The exploration on synthetic strategies such as acid catalyzed synthesis would improve the photo catalytic activities of CTFs. Advances in the synthesis methods and the exploration of new materials would provide the potential for further developments of effective photocatalysts. More importantly, the CTF has shown good activities in the oxygen production process. Besides, structural and functional design of CTF is emerged to initiate hotspot of photocatalytic research prospectively. Noticeably, the doping and modified process with remarkable improvement indicates an effective approach to enhance the properties of CTF. The COFs have prominent activities of photocatalytic hydrogen production where ordered conjugated networks facilitate to enhance the efficiency of visible-light photocatalysis and achieve high AQY under visible light irradiation. Precisely modulations of photocatalytic COFs are being discussed, revealing the structure-properties relationship and the design-regulation strategies of COFs.
Here is a comparison of the photocatalytic water splitting processes, and most recent photocatalysis performance is encompassed (Table 1).
Outlook
POPs have greatly enriched the photocatalyst family and synthetic methodologies as a promising alternative to state-of the-art metal photocatalysts, and competitive to the carbon nitrogen materials. Some basic principles for developing efficient POP photocatalysts for water splitting would be elucidated. Firstly, broad light absorbance and well-selected band gap (around 2~3 eV) allow effective utilization of the maximum portion of the visible light to facilitate HER and OER processes in the mesopores. Designation of rationally polarized skeleton and introduction of the functional group such as alkynyl are efficient approaches that aim to address harvest and utilization of visible-light. Secondly, atomic single-layer or few-layer ordered structures and more exposed active sites due to high surface areas ensure the high activities of POP photocatalysts, diverse topologies and morphologies emphasis on planarity conjugation and nanostructured crystalline remain to be pursued. Last, significant enhancements of photocatalytic activities would be expected via chemical modification on the backbone or composite metal active sites. Engineering hybrid photosystem is another pathway to the object of high efficiency water splitting, by fabricates heterojunction that combine two semiconductor which own different band gap (Tran et al., 2012). As organic semiconductor photocatalysts, combined the inorganic photocatalyst such as metal oxide that characterize lower overvoltage and higher current density (Osterloh, 2013; Ge et al., 2017) might offer a wealth of breakthrough on visible-light driven water splitting (Zhang et al., 2010b; Tian et al., 2015). However, combination of POP photocatalyst and metal oxides for photocatalytic water splitting still a nearly blank area. These remain mostly unexplored and should be pursued in the future. Overall, the emerged POP photocatalysts have shown considerable advantages including easily tunable morphology, porosity, chemical structure and energy band for photocatalytic water splitting. However, there are still some drawbacks for POPs in photocatalytic water splitting.
1. Most of photocatalytic water splitting process of POPs requires the presence of platinum, but for economic and sustainable developmental reason the efforts on exploring noble-metal-free photocatalytic water splitting of POPs are essential. Many pure CMPs are active in photocatalytic water splitting, but it is clear that residual palladium from the polymerization process has made a contribution. Besides, cheap and abundant cobalt has been used as co-catalyst in other POP photocatalytic systems, which is expected to instead of platinum. Sacrificial agent is commonly used to promote the decomposing of water. However, it is unrecyclable and pollutes environment.
2. Photocatalytic hydrogen production have been extensively investigated, while on contrary photocatalytic oxygen production remains stagnant. As water oxidation proceeds more difficultly in kinetic and energetic aspects, photocatalytic oxygen production is a more challenging study in the future. CTFs are demonstrated as candidate for highly efficient photocatalytic oxygen evolution. It can be envisaged that fast-developing synthetic strategies would offer CTF more expectant properties.
3. POPs possess considerable photocatalytic activity in water splitting, for all that, the apparent quantum yield is still lower compared with the carbon nitrogen materials (highest AQY at 60% under visible light irradiation of 420 nm) (Lin et al., 2016; Zhang et al., 2018). POPs are potentially tailored and optimized with high-performance for efficient water splitting, and functionally directed engineering on structure-properties is demanded.
In summary, POPs are promising and challenging for water splitting, this minireview would like to give a slight inspiration on design, synthesis and modulation of POPs in the field of photocatalytic water splitting. For competitive to state-of the-art metal photocatalysts and carbon nitrogen materials, more well-designed POPs with diverse building blocks, synthetic methods and functional groups are expected. Unlike the mature research of metal oxide photocatalysts, POPs are new emerged platform of water splitting. The drawbacks above impede the commercialization and industrialization of POP, more research of highly efficient photocatalytic water splitting system is still needed to challenge the practical requirements of energy and environment.
Author Contributions
CX and WZ contributed equally to the work. All the authors listed have made contribution to drafting and writing the manuscript.
Conflict of Interest Statement
The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.
Acknowledgments
We acknowledge financial support from the National Science Foundation of China (Nos. 21674129 and 21636010), the Hunan Provincial Science and Technology Plan Project, China (No.2016TP1007), and the Innovation Mover Program of Central South University (2018CX046). WZ acknowledges financial support from Fundamental Research Funds for the Central Universities of Central South University (2018zzts108).
References
Ananyev, G., and Dismukes, G. C. (2005). How fast can Photosystem II split water? Kinetic performance at high and low frequencies. Photosyn. Res. 84, 355–365. doi: 10.1007/s11120-004-7081-1
Banerjee, T., Haase, F., Savasci, G., Gottschling, K., Ochsenfeld, C., and Lotsch, B. V. (2017). Single-site photocatalytic H2 evolution from covalent organic frameworks with molecular cobaloxime co-catalysts. J. Am. Chem. Soc. 139, 16228–16234. doi: 10.1021/jacs.7b07489
Bi, J., Fang, W., Li, L., Wang, J., Liang, S., He, Y., et al. (2015). Covalent triazine-based frameworks as visible light photocatalysts for the splitting of water. Macromol. Rapid Commun. 36, 1799–1805. doi: 10.1002/marc.201500270
Bojdys, M. J., Jeromenok, J., Thomas, A., and Antonietti, M. (2010). Rational extension of the family of layered, covalent, triazine-based frameworks with regular porosity. Adv. Mater. 22, 2202–2205. doi: 10.1002/adma.200903436
Chang, C. J., Chu, K. W., Hsu, M. H., and Chen, C. Y. (2015). Ni-doped ZnS decorated graphene composites with enhanced photocatalytic hydrogen-production performance. Int. J. Hydr. Energ. 40, 14498–14506. doi: 10.1016/j.ijhydene.2015.05.141
Chen, X., Liu, L., Yu, P. Y., and Mao, S. S. (2011). Increasing solar absorption for photocatalysis with black hydrogenated titanium dioxide nanocrystals. Science 331, 746–750. doi: 10.1126/science.1200448
Chen, X., Shen, S., Guo, L., and Mao, S. S. (2010). Semiconductor-based photocatalytic hydrogen generation. Chem. Rev. 110, 6503–6570. doi: 10.1021/cr1001645
Christoforidis, K. C., and Fornasiero, P. (2017). Photocatalytic hydrogen production: a rift into the future energy supply. ChemCatChem 9, 1523–1544. doi: 10.1002/cctc.201601659
Cooper, A. I. (2009). Conjugated microporous polymers. Adv. Mater. 21, 1291–1295. doi: 10.1002/adma.200801971
Cote, A. P. (2005). Porous, crystalline, covalent organic frameworks. Science 310, 1166–1170. doi: 10.1126/science.1120411
Ding, S.-Y., and Wang, W. (2013). Covalent organic frameworks (COFs): from design to applications. Chem. Soc. Rev. 42, 548–568. doi: 10.1039/C2CS35072F
Garcia-Esparza, A. T., Shinagawa, T., Ould-Chikh, S., Qureshi, M., Peng, X., Wei, N., et al. (2017). An oxygen-insensitive hydrogen evolution catalyst coated by a molybdenum-based layer for overall water splitting. Angew. Chem. Int. Ed. 56, 5780–5784. doi: 10.1002/anie.201701861
Ge, M., Cai, J., Iocozzia, J., Cao, C., Huang, J., Zhang, X., et al. (2017). A review of TiO2nanostructured catalysts for sustainable H2generation. Int. J. Hydrogen Energy 42, 8418–8449. doi: 10.1016/j.ijhydene.2016.12.052
Haase, F., Banerjee, T., Savasci, G., Ochsenfeld, C., and Lotsch, B. V. (2017). Structure-property-activity relationships in a pyridine containing azine-linked covalent organic framework for photocatalytic hydrogen evolution. Faraday Discuss. 201, 259–276. doi: 10.1039/c7fd00051k
Huang, N., Wang, P., and Jiang, D. (2016). Covalent organic frameworks: A materials platform for structural and functional designs. Nat. Rev. Mater. 1:16068. doi: 10.1038/natrevmats.2016.68
Jiang, J., Su, F., Trewin, A., Wood, C. D., Jones, J. T. A., Khimyak, Y. Z., et al. (2008). Synthetic control of the pore dimension and surface area in conjugated microporous polymer and copolymer networks synthetic control of the pore dimension and surface area in conjugated microporous polymer and copolymer. Networks. 130, 7710–7720. doi: 10.1021/ja8010176
Jiang, Q., Sun, L., Bi, J., Liang, S., Li, L., Yu, Y., et al. (2018). MoS2Quantum dots-modified covalent triazine-based frameworks for enhanced photocatalytic hydrogen evolution. ChemSusChem 11, 1108–1113. doi: 10.1002/cssc.201702220
Kaur, P., Hupp, J. T., and Nguyen, S. T. (2011). Porous organic polymers in catalysis: Opportunities and challenges. ACS Catal. 1, 819–835. doi: 10.1021/cs200131g
Kudo, A., and Miseki, Y. (2009). Heterogeneous photocatalyst materials for water splitting. Chem. Soc. Rev. 38, 253–278. doi: 10.1039/b800489g
Kuhn, P., Antonietti, M., and Thomas, A. (2008). Porous, covalent triazine-based frameworks prepared by ionothermal synthesis. Angew. Chem. Int. Ed. 47, 3450–3453. doi: 10.1002/anie.200705710
Lan, Z. A., Fang, Y., Zhang, Y., and Wang, X. (2018). Photocatalytic oxygen evolution from functional triazine-based polymers with tunable band structures. Angew. Chem. Int. Ed. 57, 470–474. doi: 10.1002/anie.201711155
Li, L., Cai, Z., Wu, Q., Lo, W. Y., Zhang, N., Chen, L. X., et al. (2016a). Rational design of porous conjugated polymers and roles of residual palladium for photocatalytic hydrogen production. J. Am. Chem. Soc. 138, 7681–7686. doi: 10.1021/jacs.6b03472
Li, L., Fang, W., Zhang, P., Bi, J., He, Y., Wang, J., et al. (2016b). Sulfur-doped covalent triazine-based frameworks for enhanced photocatalytic hydrogen evolution from water under visible light. J. Mater. Chem. A 4, 12402–12406. doi: 10.1039/c6ta04711d
Li, L., Hadt, R. G., Yao, S., Lo, W. Y., Cai, Z., Wu, Q., et al. (2016c). Photocatalysts based on cobalt-chelating conjugated polymers for hydrogen evolution from water. Chem. Mater. 28, 5394–5399. doi: 10.1021/acs.chemmater.6b01477
Li, L., Lo, W. Y., Cai, Z., Zhang, N., and Yu, L. (2016d). Donor-acceptor porous conjugated polymers for photocatalytic hydrogen production: The importance of acceptor comonomer. Macromolecules 49, 6903–6909. doi: 10.1021/acs.macromol.6b01764
Lin, L., Ou, H., Zhang, Y., and Wang, X. (2016). Tri-s-triazine-based crystalline graphitic carbon nitrides for highly efficient hydrogen evolution photocatalysis. ACS Catal. 6, 3921–3931. doi: 10.1021/acscatal.6b00922
Meier, C. B., Sprick, R. S., Monti, A., Guiglion, P., Lee, J. S. M., Zwijnenburg, M. A., et al. (2017). Structure-property relationships for covalent triazine-based frameworks: the effect of spacer length on photocatalytic hydrogen evolution from water. Polym 126, 283–290. doi: 10.1016/j.polymer.2017.04.017
Osterloh, F. E. (2013). Inorganic nanostructures for photoelectrochemical and photocatalytic water splitting. Chem. Soc. Rev. 42, 2294–2320. doi: 10.1039/c2cs35266d
Ou, H., Lin, L., Zheng, Y., Yang, P., Fang, Y., and Wang, X. (2017). Tri-s-triazine-based crystalline carbon nitride nanosheets for an improved hydrogen evolution. Adv. Mater. 29:1700008. doi: 10.1002/adma.201700008
Pachfule, P., Acharjya, A., Roeser, J., Langenhahn, T., Schwarze, M., Schomäcker, R., et al. (2018). Diacetylene functionalized covalent organic framework (COF) for photocatalytic hydrogen generation. J. Am. Chem. Soc. 140, 1423–1427. doi: 10.1021/jacs.7b11255
Paramasivam, I., Macak, J. M., and Schmuki, P. (2008). Photocatalytic activity of TiO2 nanotube layers loaded with Ag and Au nanoparticles. Electrochem. Commun. 10, 71–75. doi: 10.1016/j.elecom.2007.11.001
Puthiaraj, P., Lee, Y.-R., Zhang, S., and Ahn, W.-S. (2016). Triazine-based covalent organic polymers: design, synthesis and applications in heterogeneous catalysis. J. Mater. Chem. A 4, 16288–16311. doi: 10.1039/C6TA06089G
Qu, A., Xu, X., Zhang, Y., Li, Y., Zha, W., Wen, S., et al. (2016). A nitrogen-rich mesoporous polymer for photocatalytic hydrogen evolution from water. React. Funct. Polym. 102, 93–100. doi: 10.1016/j.reactfunctpolym.2016.03.005
Ran, J., Ma, T. Y., Gao, G., Du, X.-W., and Qiao, S. Z. (2015). Porous P-doped graphitic carbon nitride nanosheets for synergistically enhanced visible-light photocatalytic H2 production. Energy Environ. Sci. 8, 3708–3717. doi: 10.1039/C5EE02650D
Ren, S., Bojdys, M. J., Dawson, R., Laybourn, A., Khimyak, Y. Z., Adams, D. J., et al. (2012). Porous, fluorescent, covalent triazine-based frameworks via room-temperature and microwave-assisted synthesis. Adv. Mater. 24, 2357–2361. doi: 10.1002/adma.201200751
Schmidt, J., Werner, M., and Thomas, A. (2009). Conjugated microporous polymer networks via yamamoto polymerization. Macromolecules 42, 4426–4429. doi: 10.1021/ma9005473
Schwinghammer, K., Hug, S., Mesch, M. B., Senker, J., and Lotsch, B. V. (2015). Phenyl-triazine oligomers for light-driven hydrogen evolution. Energy Environ. Sci. 8, 3345–3353. doi: 10.1039/c5ee02574e
Schwinghammer, K., Mesch, M. B., Duppel, V., Ziegler, C., Senker, J., and Lotsch, B. V. (2014). Crystalline carbon nitride nanosheets for improved visible-light hydrogen evolution. J. Am. Chem. Soc. 136, 1730–1733. doi: 10.1021/ja411321s
Schwinghammer, K., Tuffy, B., Mesch, M. B., Wirnhier, E., Martineau, C., Taulelle, F., et al. (2013). Triazine-based carbon nitrides for visible-light-driven hydrogen evolution. Angew. Chem. Int. Ed. 52, 2435–2439. doi: 10.1002/anie.201206817
Sprick, R. S., Jiang, J. X., Bonillo, B., Ren, S., Ratvijitvech, T., Guiglion, P., et al. (2015). Tunable organic photocatalysts for visible-light-driven hydrogen evolution. J. Am. Chem. Soc. 137, 3265–3270. doi: 10.1021/ja511552k
Stegbauer, L., Schwinghammer, K., and Lotsch, B. V. (2014). A hydrazone-based covalent organic framework for photocatalytic hydrogen production. Chem. Sci. 5, 2789–2793. doi: 10.1039/c4sc00016a
Stegbauer, L., Zech, S., Savasci, G., Banerjee, T., Podjaski, F., Schwinghammer, K., et al. (2018). Tailor-made photoconductive pyrene-based covalent organic frameworks for visible-light driven hydrogen generation. Adv. Energy Mater.8:1703278. doi: 10.1002/aenm.201703278
Sun, S., and Liang, S. (2017). Recent advances in functional mesoporous graphitic carbon nitride (mpg-C3N4) polymers. Nanoscale 9, 10544–10578. doi: 10.1039/c7nr03656f
Tian, J., Leng, Y., Zhao, Z., Xia, Y., Sang, Y., Hao, P., et al. (2015). Carbon quantum dots/hydrogenated TiO2nanobelt heterostructures and their broad spectrum photocatalytic properties under UV, visible, and near-infrared irradiation. Nano Energy 11, 419–427. doi: 10.1016/j.nanoen.2014.10.025
Tilford, R. W., Gemmill, W. R., Zur Loye, H. C., and Lavigne, J. J. (2006). Facile synthesis of a highly crystalline, covalently linked porous boronate network. Chem. Mater. 18, 5296–5301. doi: 10.1021/cm061177g
Tran, P. D., Wong, L. H., Barber, J., and Loo, J. S. C. (2012). Recent advances in hybrid photocatalysts for solar fuel production. Energy Environ. Sci. 5, 5902–5918. doi: 10.1039/c2ee02849b
Vyas, V. S., Haase, F., Stegbauer, L., Savasci, G., Podjaski, F., Ochsenfeld, C., et al. (2015). A tunable azine covalent organic framework platform for visible light-induced hydrogen generation. Nat. Commun. 6, 1–9. doi: 10.1038/ncomms9508
Wang, K., Yang, L. M., Wang, X., Guo, L., Cheng, G., Zhang, C., et al. (2017a). Covalent triazine frameworks via a low-temperature polycondensation approach. Angew. Chem. Int. Ed. 56, 14149–14153. doi: 10.1002/anie.201708548
Wang, L., Wan, Y., Ding, Y., Wu, S., Zhang, Y., Zhang, X., et al. (2017b). Conjugated microporous polymer nanosheets for overall water splitting using visible light. Adv. Mater. 29, 1–8. doi: 10.1002/adma.201702428
Wang, Q., Hisatomi, T., Suzuki, Y., Pan, Z., Seo, J., Katayama, M., et al. (2017c). Particulate photocatalyst sheets based on carbon conductor layer for efficient Z-scheme pure-water splitting at ambient pressure. J. Am. Chem. Soc. 139, 1675–1683. doi: 10.1021/jacs.6b12164
Wang, X., Maeda, K., Thomas, A., Takanabe, K., Xin, G., Carlsson, J. M., et al. (2009). A metal-free polymeric photocatalyst for hydrogen production from water under visible light. Nat. Mater. 8, 76–80. doi: 10.1038/nmat2317
Wang, Y., Wang, X., and Antonietti, M. (2012). Polymeric graphitic carbon nitride as a heterogeneous organocatalyst: from photochemistry to multipurpose catalysis to sustainable chemistry. Angew. Chemie Int. Ed. 51, 68–89. doi: 10.1002/anie.201101182
Wang, Z., Yang, X., Yang, T., Zhao, Y., Wang, F., Chen, Y., et al. (2018). Dibenzothiophene dioxide-based conjugated microporous polymers for visible-light-driven hydrogen production. ACS Catal.8, 8590–8596. doi: 10.1021/acscatal.8b02607
Xiang, Y., Wang, X., Rao, L., Wang, P., Huang, D., Ding, X., et al. (2018). Conjugated polymers with sequential fluorination for enhanced photocatalytic H2 evolution via proton-coupled electron transfer. ACS Energy Lett. 3, 2544–2549. doi: 10.1021/acsenergylett.8b01535
Xie, J., Shevlin, S. A., Ruan, Q., Moniz, S. J. A., Liu, Y., Liu, X., et al. (2018). Efficient visible light-driven water oxidation and proton reduction by an ordered covalent triazine-based framework. Energy Environ. Sci. 11, 1617–1624. doi: 10.1039/c7ee02981k
Xu, Y., Mao, N., Feng, S., Zhang, C., Wang, F., Chen, Y., et al. (2017). Perylene-containing conjugated microporous polymers for photocatalytic hydrogen evolution. Macromol. Chem. Phys. 218, 1–9. doi: 10.1002/macp.201700049
Xu, Y., Mao, N., Zhang, C., Wang, X., Zeng, J., Chen, Y., et al. (2018). Rational design of donor-Π-acceptor conjugated microporous polymers for photocatalytic hydrogen production. Appl. Catal. B Environ. 228, 1–9. doi: 10.1016/j.apcatb.2018.01.073
Yu, S.-Y., Mahmood, J., Noh, H.-J., Seo, J.-M., Jung, S.-M., Shin, S.-H., et al. (2018). Direct synthesis of covalent triazine-based framework from aromatic amides. Angew. Chemie Int. Ed. Engl. 57, 8438–42. doi: 10.1002/anie.201801128
Zhang, G., Lan, Z.-A., and Wang, X. (2016). Conjugated polymers: catalysts for photocatalytic hydrogen evolution. Angew. Chemie Int. Ed. Engl. 55, 15712–15727. doi: 10.1002/anie.201607375
Zhang, G., Lan, Z. A., and Wang, X. (2017a). Surface engineering of graphitic carbon nitride polymers with cocatalysts for photocatalytic overall water splitting. Chem. Sci. 8, 5261–5274. doi: 10.1039/c7sc01747b
Zhang, G., Lin, L., Li, G., Zhang, Y., Savateev, A., Zafeiratos, S., et al. (2018). Ionothermal synthesis of triazine-heptazine-based copolymers with apparent quantum yields of 60 % at 420 nm for solar hydrogen production from “sea water.” Angew. Chemie Int. Ed. Engl. 57, 9372–9376. doi: 10.1002/anie.201804702
Zhang, G., Zhang, M., Ye, X., Qiu, X., Lin, S., and Wang, X. (2014). Iodine modified carbon nitride semiconductors as visible light photocatalysts for hydrogen evolution. Adv. Mater. 26, 805–809. doi: 10.1002/adma.201303611
Zhang, J., Chen, Y., and Wang, X. (2015). Two-dimensional covalent carbon nitride nanosheets: Synthesis, functionalization, and applications. Energy Environ. Sci. 8, 3092–3108. doi: 10.1039/c5ee01895a
Zhang, J., Guo, F., and Wang, X. (2013). An optimized and general synthetic strategy for fabrication of polymeric carbon nitride nanoarchitectures. Adv. Funct. Mater. 23, 3008–3014. doi: 10.1002/adfm.201203287
Zhang, W., Li, C., Yuan, Y.-P., Qiu, L.-G., Xie, A.-J., Shen, Y.-H., et al. (2010a). Highly energy- and time-efficient synthesis of porous triazine-based framework: microwave-enhanced ionothermal polymerization and hydrogen uptake. J. Mater. Chem. 20:6413. doi: 10.1039/c0jm01392g
Zhang, X. H., Wang, X. P., Xiao, J., Wang, S. Y., Huang, D. K., Ding, X., et al. (2017b). Synthesis of 1,4-diethynylbenzene-based conjugated polymer photocatalysts and their enhanced visible/near-infrared-light-driven hydrogen production activity. J. Catal. 350, 64–71. doi: 10.1016/j.jcat.2017.02.026
Zhang, X. Y., Li, H. P., Cui, X. L., and Lin, Y. (2010b). Graphene/TiO2nanocomposites: synthesis, characterization and application in hydrogen evolution from water photocatalytic splitting. J. Mater. Chem. 20, 2801–2806. doi: 10.1039/b917240h
Zhang, Y., and Riduan, S. N. (2012). Functional porous organic polymers for heterogeneous catalysis. Chem. Soc. Rev. 41, 2083–2094. doi: 10.1039/C1CS15227K
Keywords: porous organic polymers, heterogeneous catalysis, photocatalyst, water splitting, oxygen evolution, hydrogen evolution
Citation: Xu C, Zhang W, Tang J, Pan C and Yu G (2018) Porous Organic Polymers: An Emerged Platform for Photocatalytic Water Splitting. Front. Chem. 6:592. doi: 10.3389/fchem.2018.00592
Received: 31 August 2018; Accepted: 13 November 2018;
Published: 04 December 2018.
Edited by:
Junguang Tao, Hebei University of Technology, ChinaReviewed by:
Urska Lavrencic Stangar, University of Ljubljana, SloveniaJingyu Wang, Huazhong University of Science and Technology, China
Copyright © 2018 Xu, Zhang, Tang, Pan and Yu. This is an open-access article distributed under the terms of the Creative Commons Attribution License (CC BY). The use, distribution or reproduction in other forums is permitted, provided the original author(s) and the copyright owner(s) are credited and that the original publication in this journal is cited, in accordance with accepted academic practice. No use, distribution or reproduction is permitted which does not comply with these terms.
*Correspondence: Guipeng Yu, gilbertyu@csu.edu.cn