ORIGINAL RESEARCH article

Front. Chem., 17 October 2018
Sec. Catalysis and Photocatalysis
This article is part of the Research Topic Photocatalysis for Environmental Applications View all 16 articles

Titanium Phosphate Nanoplates Modified With AgBr@Ag Nanoparticles: A Novel Heterostructured Photocatalyst With Significantly Enhanced Visible Light Responsive Activity

\r\nManli RenManli RenJiaqiu BaoJiaqiu BaoPeifang WangPeifang WangChao WangChao WangYanhui Ao*Yanhui Ao*
  • Key Laboratory of Integrated Regulation and Resource Development on Shallow Lakes, Ministry of Education, College of Environment, Hohai University, Nanjing, China

AgBr@Ag modified titanium phosphate composites were fabricated through a two-step approach. The prepared samples were characterized by X-ray diffraction, scanning electron microscopy, and transmission electron microscopy. The optical properties of the composites were characterized by using UV-vis diffuse reflectance spectroscopy. The photocatalytic activities of the composites were investigated on the degradation of Rhodamine B and ciprofloxacin under visible light irradiation. AgBr@Ag/titanium phosphate was determined to exhibit considerably higher photocatalytic activity than the corresponding individual components. The mechanism on the enhancement of the photocatalytic activity was proposed based on the results of photoluminescence spectra and photocurrent measurements. Furthermore, the possible photocatalytic mechanisms of organic compounds degradation were also proposed.

Introduction

Environmental pollution has become a global problem due to the accelerated development of human society (Ye et al., 2012; Sun et al., 2017; Zhang et al., 2017; Li et al., 2018a; Lu et al., 2018). Therefore, it is urgent to solve this severe problem via green technology (Liu et al., 2012; Hao et al., 2016; Zou et al., 2016; Chen et al., 2018; Feng et al., 2018; Guo et al., 2018). Currently, photocatalysis technology has recieved intense attention as an efficient technology for solving the problem of environment (Fan et al., 2013; Ao et al., 2016; Wang et al., 2016; Dong et al., 2017; Hao et al., 2017). Furthermore, it is well known that composite photocatalysts always show higher activity than the corresponding single component (Ma et al., 2018; Wang et al., 2018; Zhang et al., 2018). The improved photocatalytic activity is due to the different electronic energy levels of different components, which create an internal electric field that can accelerate the separation rate of photogenerated electrons and holes, and reduce their recombination rate (Guo et al., 2017).

Recently, titanium phosphate has been widely studied for the treatment of organic compounds. Titanium phosphate [α-Ti(HPO4)2•H2O, hereafter TP] consists of layers of titanium atoms bonding on both plane sides of the monohydrogen phosphate groups. Water molecules located in the interlayer region to form a network of hydrogen-bonding with phosphate groups (Ekambaram et al., 2000; Guo et al., 2013; Guo and Han, 2014; Zhu et al., 2014). However, titanium phosphate can only absorb ultraviolet light (<5% of the sunlight). Furthermore, the high recombination rate of photoinduced electron-hole pairs is still exist, which would lead to lower photocatalytic activity. Thus, it is urgent to find effective ways to improve the activity of the TP.

Recently, silver halide materials have received intense attention due to their excellent visible light responsive photocatalytic activity. Silver halide@silver nanoparticles (AgNPs) based heterojunctions have been found to be excellent photocatalysts (Chen et al., 2015; Bai et al., 2016; Li et al., 2018b; Xuan et al., 2018). It has been proved that plasmon AgNPs on the surface of AgX can enhance the light absorption of the composites and accelerate the separation rate of the photogenerated charges (Daupor and Wongnawa, 2014; Li et al., 2015a,b; Ding et al., 2018; Xiao et al., 2018). Moreover, it was also considered that AgNPs decrease the recombination rate of Ag+ with photogenerated electrons, and allow the formation of Br0 species (photogenerated holes react with Br ions) that can degrade the organic compounds (Xia and Halas, 2005; Jiang et al., 2014; Zhang et al., 2015a). Therefore, it would be a good way to obtain higher visible light activated activity through the conbination of AgBr@Ag and TP.

In this work, we prepared visible light active AgBr@Ag/TP photocatalysts by a simple and feasible method. The morphology, crystal structure, optical properties, and composition of the photocatalysts were investigated. Moreover, the possible photocatalytic degradation mechanism of ciprofloxacin and the enhancement mechanism photocatalytic activity were proposed.

Experimental

All experimental details are shown in Supporting Information.

Results and Discussion

Characterization

The phase structure was characterized by XRD, and the obtained patterns are shown in Figure 1. The peaks at about 11.6, 21.0, 26.0, 35.4, and 35.8° are indexed to the (002), (200), (202), (006), and (020) directions, respectively. All peaks can be ascribed to TP (JCPDS Card No: 83-0109; Ortíz-Oliveros et al., 2014; Yada et al., 2014). Diffraction peaks are also detected at 26.73, 30.96, 44.35, 55.04, 64.49, and 73.26°, which can be indexed to the (111), (200), (220), (222), (400), and (420) directions of AgBr (JCPDS Card NO: 06-0438; Chen et al., 2015; Bai et al., 2016). Furthermore, with the increasing of AgBr mass, the intensity of the characteristic peaks of AgBr increased gradually. No diffraction peaks of Ag can be observed, possibly due to its low mass, high dispersion or small size (Wang et al., 2013, 2014).

FIGURE 1
www.frontiersin.org

Figure 1. XRD patterns of pure titanium phosphate, Ag@AgBr and Ag@AgBr/TP. The star represents AgBr.

The morphologies of the composites were investigated by TEM and SEM. The obtained SEM image of pure TP is displayed in Figure 2a. It can be seen that the TP sample is composed of uniform plates with sub-micrometer width and 30~40 nm thickness. The SEM image of AgBr@Ag/TP-3 taken from Figure 2b displays smaller AgBr@Ag nanoparticles decorating the TP surface. The TEM image of pure TP is displayed in Figure 2c. It can also be seen that the titanium phosphate plate is hexagonal, which is in good agreement with the results of SEM. The TEM image of AgBr@Ag/TP is shown in Figure 2d. It can be seen that AgBr nanoparticles decorated the TP surface, indicating the formation of heterojunctions in the prepared samples (Cui et al., 2018). As shown in the inset of Figure 2d, the measured lattice spacings of 0.289 nm corresponds to the (200) lattice planes of AgBr.

FIGURE 2
www.frontiersin.org

Figure 2. (a) SEM image of pure titanium phosphate, (b) SEM image of Ag@AgBr/TP-3, (c) HRTEM image of pure titanium phosphate, (d) HRTEM image of Ag@AgBr/TP-3.

The elemental composition and chemical states of the elements in the composites were analyzed by XPS. The peaks of Br 3d, P 2p, Ag 3d, C 1s, Ti 2p, and O1s can be observed in Figures 3A,B shows the electron binding energies of Ag 3d5/2 and Ag 3d3/2 orbitals, which can be further divided into 366.6/367.4 and 372.6/373.4 eV, respectively. The peaks at 366.6 and 372.6 eV indicate the presence of Ag+. Both the peak separation (6.0 eV) and peak positions (367.4 and 373.4 eV) indicate the presence of metallic form (Ag0; Yang et al., 2015; Tang et al., 2017a,b). As shown in Figure 3C, two peaks at 68.0 and 67.0 eV corresponding to the binding energies of Br 3d3/2 and Br 3d5/2 can be found (Wang et al., 2009). All above results prove the presence of AgBr and Ag in the composite. In Figure 3D, the Ti peaks observed at 459.0 and 464.8 eV can be attributed to Ti 2p3/2 and Ti 2p1/2. The peak separation of 5.8 eV for binding energy between the two peaks indicates that Ti was mainly Ti4+ in the composite (Yada et al., 2014).

FIGURE 3
www.frontiersin.org

Figure 3. XPS spectra of Ag@AgBr/TP-3. (A) The survey XPS spectrum, (B) Ag 3d, (C) Br 3d, (D) Ti 2p peaks related to the photocatalyst.

The optical properties of photocatalysts significantly affect their photocatalytic performance (He et al., 2015). Therefore, optical properties of the composites were investigated by DRS and the obtained results are shown in Figure 4. Pure TP exhibited no absorption in the visible-light region, whereas the Ag@AgBr/TP composites had better absorption performance, possibly due to the deposition of AgBr and formation of AgNPs on the surface of the composites. Moreover, Ag@AgBr/TP-3 showed the highest absorption in visible light region, indicating that high absorption capability is ascribed to an optimal loading. In other words, when the loading of AgBr@Ag exceeds a critical value, the AgBr@Ag nanoparticles would agglomerate and decrease the absorption capability.

FIGURE 4
www.frontiersin.org

Figure 4. UV-vis diffuse reflectance spectra of titanium phosphate, Ag@AgBr and Ag@AgBr/TP.

Photocatalytic Activity

To investigate the photocatalytic performance of the composites, we conducted experiments on the degradation of colorless organic pollutant (CIP) under visible light irradiation. As shown in Figure 5, AgBr@Ag/TP-3 displayed the highest photocatalytic activity for CIP degradation among all samples. Approximately 51.4, 44.2, 61.3, 71.5, and 65.4% of CIP was degraded in 180 min by AgBr@Ag, AgBr@Ag/TP-1, AgBr@Ag/TP-2, AgBr@Ag/TP-3, and AgBr@Ag/TP-4, respectively. Furthermore, the TP showed a low photocatalytic efficiency for CIP degradation. The degradation curve of CIP by TP exhibits a fluctuating trend. There may be some CIP molecules desorbed from the surface of TP. These results show that the Ag@AgBr/TP photocatalysts are generally effective for the degradation of colorless organic compounds.

FIGURE 5
www.frontiersin.org

Figure 5. Photocatalytic degradation of CIP over the as-prepared samples under visible light irradiation.

Intermediates Analysis

Prior to the complete mineralization of CIP, there are many degradation intermediates in the photocatalytic process. The sample solution was detected by HPLC/MS during the photocatalytic degradation. Some intermediates in the photocatalytic process were identified: A1 (m/z = 362.2), A2 (m/z = 334.2), A3 (m/z = 306.2), A4 (m/z = 291.2), and A5 (m/z = 263.2). These results show that A1~A5 are the main intermediates during the degradation process of CIP. As observed in many other oxidation system (Sturini et al., 2012), desethylene ciprofloxacin (A3) was dominant intermediate of CIP, and was formed by a net loss of C2H2 at the piperazinyl substituent of CIP. Prior to the formation of desethylene ciprofloxacin, two intermediates were detected. The hydroxyl keto-derivative of the piperazinyl substituent (A1) was detected to be the first oxidized intermediate on the way to the formation of A3. Apparently, the subsequent loss of CO from A1 results in the cleavage of the piperazinyl ring to form keto-derivatives A2 and A2', in which a carbonyl group remains on the N atom of aniline and alkylamine, respectively. A second loss of a CO molecule from A2 and A2' leads to the formation of desethylene ciprofloxacin (A3). The further oxidation of desethylene ciprofloxacin (A3) generated A4 with a keto group through the loss of a N atom. The decarbonylation of A4 forms aniline (A5), completely destroying the piperazinyl substituent of CIP. The probable pathways for CIP degradation are shown in Figure 6.

FIGURE 6
www.frontiersin.org

Figure 6. Suggested pathways for CIP degradation.

Possible Photocatalytic Mechanism

Several experiments were performed to further understand the mechanism on the enhancement of photocatalytic performance for the AgBr@Ag/TP composites. The photoluminescence (PL) spectrum was measured to investigate the recombination rate of the photogenerated electron-hole pairs. The photoluminescence spectra of the prepared samples are shown in Figure 7. The intensity of PL is directly proportional to the electron-hole recombination rate, and lower PL intensity means lower recombination rate (Zhang et al., 2015b; Shi et al., 2016). The main emission peak of pure TP centers at ~470 nm, which was ascribed to the band gap recombination of electron-hole pairs. The PL intensity decreases significantly after the deposition of AgBr@Ag. The decreasing emission intensity of the AgBr@Ag/TP suggests that the recombination of electron-hole pairs can be suppressed after the deposition of AgBr@Ag (Xu et al., 2013). Furthermore, it can be seen that the PL intensity increase as the amount of Ag@AgBr increase to a certain value, and AgBr@Ag/TP-3 composite showed the lowest PL intensity, which means Ag@AgBr/TP-3 composite has the lowest recombination rate of photogenerated electrons-hole pairs. Therefore, it would lead to the highest photocatalytic performance. However, the PL intensity increase as the amount of Ag@AgBr increase further. It can be ascribed to the reason that superfluous Ag@AgBr nanoparticles would aggregate thus cannot form effective heterojunctions with TP. The above results demonstrate that the deposition of AgBr on TP and the formation of AgNPs on the surface of the composite can decrease the recombination efficiency and enhance the separation efficiency of the photogenerated electrons and holes.

FIGURE 7
www.frontiersin.org

Figure 7. Photoluminescence spectra of the prepared samples.

It is well known that the efficiency of the electron-hole pairs separation significantly affects the photocatalytic performance (Jiang et al., 2011). The electrons in the valence band of photocatalysts can be activated and then transfer to the conduction band, leading to the formation of photocurrent. A higher photocurrent means higher electron-hole pairs separation rate, which induces to better photocatalytic performance (Xiang et al., 2011). Figure 8 shows the photocurrents for different samples under 20 s intermittent visible-light irradiation with a bias of 0.3 V. The photocurrents of AgBr@Ag/TP composites are all much higher than that of TP. Moreover, AgBr@Ag/TP-3 exhibits the highest value. The results are in good agreement with the photocatalytic activity, indicating that the efficient separation of photo-induced electrons and holes results in the high photocatalytic activity.

FIGURE 8
www.frontiersin.org

Figure 8. Photocurrent of the prepared samples under visible light irradiation.

It was demonstrated that the separation efficiency of photo-generated electrons and holes is important to the photocatalytic performance. Furthermore, the conduction band (CB) and valence band (VB) potential have a significantly effect on the separation of the photogenerated electron-hole pairs. The CB and VB potential of AgBr and TP can be obtained using Equations. (1) and (2) (Zhang et al., 2008):

Evb=X-E0+0.5Eg    (1)
Ecb=Evb-Eg    (2)

where Evb is the potential of VB, X is the absolute electronegativity of photocatalyst (X is 6.85 eV and 5.81 eV of TP and AgBr, respectively), Eg is the band gap energy and E0 is the energy of free electrons (~4.5 eV). Based on these equations, the CB potential (Ecb) and VB potential (Evb) of TP are calculated as 0.43 and 4.28 eV, while Ecb and Evb of AgBr are calculated as 0.01 eV and 2.62 eV, respectively.

Therefore, a possible mechanism on the photocatalytic degradation of RhB by AgBr@Ag/TP under the irradiation of visible light is illustrated in Figure 9. The plasmon induced holes can react with Br and form active Br0 atoms. The Br0 atoms exhibit an excellent oxidation capability to oxidize organic compounds. Meanwhile, plasmon induced electrons are formed on the surface of AgNPs, part of these electrons are trapped by O2 to produce •O2-, mainly contributing to the organic compounds removal (Ye et al., 2012; Zhang and Yates, 2012; Cheng et al., 2015; Ding et al., 2018). Besides, the other electrons would transfer to the conduction band of AgBr, and then further transfer from AgBr to the conduction band of TP. Meanwhile, the h+ stored in valence band of AgBr and TP was also involved in the organic compounds photocatalytic degradation, though they are not the dominant active species. The relevant equations are shown as following:

Ag+visible-lighte-+h+    (3)
e-+O2O2-    (4)
h++Br-Br0    (5)
CIP+O2-(orBr0)degradation products    (6)

Based on above results, the possible mechanism on the enhancement of photocatalytic activity for AgBr@Ag/TP composites can be proposed. AgBr@Ag nanoparticles deposited on TP improve the light absorption capability, as confirmed by UV-vis DRS studies. Furthermore, the heterojunctions between AgNPs, AgBr, and TP are conducive to improving the transfer rate and separation efficiency of the electron-hole pairs, and hindering the recombination of the pairs, thus inducing to the enhancement of the photocatalytic activity.

FIGURE 9
www.frontiersin.org

Figure 9. Schematic diagram of the possible photocatalytic degradation mechanism over Ag@AgBr/TP under visible light irradiation.

Conclusions

AgBr@Ag/TP composites exhibited higher photocatalytic performance than pure TP and AgBr@Ag, and can degrade a typical antibiotic (CIP) under the irradiation of visible light. The excellent photocatalytic activity can be ascribed to their enhanced visible-light absorption, low recombination and high transferring rate of the photo-generated charges, as shown by DRS, PL, and photocurrent experiments.

Author Contributions

YA and CW designed the project and guided the work. MR and JB conducted the experiments and characterizations of the samples. PW revised and polished the manuscript.

Conflict of Interest Statement

The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.

Acknowledgments

We are grateful for grants from National Science Funds for Creative Research Groups of China (No. 51421006), Natural Science Foundation of China (51679063), the Fundamental Research Funds for The Central Universities (2018B14514), the Key Program of National Natural Science Foundation of China (No. 91647206), the National Key Plan for Research and Development of China (2016YFC0502203), and PAPD.

Supplementary Material

The Supplementary Material for this article can be found online at: https://www.frontiersin.org/articles/10.3389/fchem.2018.00489/full#supplementary-material

References

Ao, Y., Wang, K., Wang, P., Wang, C., and Hou, J. (2016). Synthesis of novel 2D-2D p-n heterojunction BiOBr/La2Ti2O7 composite photocatalyst with enhanced photocatalytic performance under both UV and visible light irradiation. Appl. Catal. B-Environ. 194, 157–168. doi: 10.1016/j.apcatb.2016.04.050

CrossRef Full Text | Google Scholar

Bai, Y. Y., Lu, Y., and Liu, J. K. (2016). An efficient photocatalyst for degradation of various organic dyes: Ag@ Ag2MoO4-AgBr composite. J. Hazard. Mater. 307, 26–35. doi: 10.1016/j.jhazmat.2015.12.052

PubMed Abstract | CrossRef Full Text | Google Scholar

Chen, D., Wang, Z., Du, Y., Yang, G., Ren, T., and Ding, H. (2015). In situ ionic-liquid-assisted synthesis of plasmonic photocatalyst Ag/AgBr/g-C3N4 with enhanced visible-light photocatalytic activity. Catal. Today. 258, 41–48. doi: 10.1016/j.cattod.2015.03.031

CrossRef Full Text | Google Scholar

Chen, P., Dong, F., Ran, M., and Li, J. (2018). Synergistic photo-thermal catalytic NO purification of MnOx/g-C3N4: enhanced performance and reaction mechanism. Chin. J. Catal. 39, 619–629. doi: 10.1016/S1872-2067(18)63029-3

CrossRef Full Text | Google Scholar

Cheng, Z., Wang, Z., Shifa, T. A., Wang, F., Zhan, X., Xu, K., et al. (2015). Au plasmonics in a WS2-Au-CuInS2 photocatalyst for significantly enhanced hydrogen generation. Appl. Phys. Lett. 107, 253–278. doi: 10.1063/1.4937008

CrossRef Full Text | Google Scholar

Cui, X., Tian, L., Xian, X., Tang, H., and Yang, X. (2018). Solar photocatalytic water oxidation over Ag3PO4/g-C3N4 composite materials mediated by metallic Ag and graphene. Appl. Surf. Sci. 430, 108–115. doi: 10.1016/j.apsusc.2017.07.290

CrossRef Full Text | Google Scholar

Daupor, H., and Wongnawa, S. (2014). Urchinlike Ag/AgCl photocatalyst: synthesis, characterization, and activity. Appl. Catal. A-Gen. 473, 59–69. doi: 10.1016/j.apcata.2013.12.036

CrossRef Full Text | Google Scholar

Ding, K., Yu, D., Wang, W., Gao, P., and Liu, B. (2018). Fabrication of multiple hierarchical heterojunction Ag@AgBr/BiPO4/r-GO with enhanced visible-light-driven photocatalytic activities towards dye degradation. Appl. Surf. Sci. 445, 39–49. doi: 10.1016/j.apsusc.2018.03.131

CrossRef Full Text | Google Scholar

Dong, W. H., Wu, D. D., Luo, J. M., Xing, Q. J., Liu, H., Zou, J. P., et al. (2017). Coupling of photodegradation of RhB with photoreduction of CO2 over rGO/SrTi0.95Fe0.05O3−δ catalyst: a strategy for one-pot conversion of organic pollutants to methanol and ethanol. J. Catal. 349, 218–225. doi: 10.1016/j.jcat.2017.02.004

CrossRef Full Text | Google Scholar

Ekambaram, S., Christian, S.erre, Gérard Férey, a., and Slavi, C.Sevov (2000). Hydrothermal synthesis and characterization of an ethylenediamine-templated mixed-valence titanium phosphate. Chem. Mater. 31, 444–449. doi: 10.1021/cm990492i

CrossRef Full Text | Google Scholar

Fan, W., Zhang, Q., and Wang, Y. (2013). Semiconductor-based nanocomposites for photocatalytic H2 production and CO2 conversion. Phys. Chem. Chem. Phys. 15, 2632–2649. doi: 10.1039/c2cp43524a

PubMed Abstract | CrossRef Full Text | Google Scholar

Feng, X.Y., Wang, P.F., Hou, J., Qian, J., Wang, C., and Ao, Y. H. (2018). Oxygen vacancies and phosphorus codoped black titania coated carbon nanotube composite photocatalyst with efficient photocatalytic performance for the degradation of acetaminophen under visible light irradiation. Chem. Engin. J. 352:947–956. doi: 10.1016/j.cej.2018.06.037

CrossRef Full Text | Google Scholar

Guo, H., Niu, C. G., Wen, X. J., Zhang, L., Liang, C., Zhang, X. G., et al. (2017). Construction of highly efficient and stable ternary AgBr/Ag/PbBiO2Br Z-scheme photocatalyst under visible light irradiation: performance and mechanism insight. J. Colloid Interface Sci. 513, 852–865. doi: 10.1016/j.jcis.2017.12.010

PubMed Abstract | CrossRef Full Text | Google Scholar

Guo, S. Y., and Han, S. (2014). Constructing a novel hierarchical 3D flower-like nano/micro titanium phosphate with efficient hydrogen evolution from water splitting. J. Power Sources. 267, 9–13. doi: 10.1016/j.jpowsour.2014.05.011

CrossRef Full Text | Google Scholar

Guo, S. Y., Han, S., Chi, B., Pu, J., and Li, J. (2013). Synthesis of shape-controlled mesoporous titanium phosphate nanocrystals: the hexagonal titanium phosphate with enhanced hydrogen generation from water splitting. Int. J. Hydrogen Energy 39, 2446–2453. doi: 10.1016/j.ijhydene.2013.12.007

CrossRef Full Text | Google Scholar

Guo, Y., Wang, P., Qian, J., Ao, Y., Wang, C., and Hou, J. (2018). Phosphate group grafted twinned BiPO4 with significantly enhanced photocatalytic activity: synergistic effect of improved charge separation efficiency and redox ability. Appl. Catal. B-Environ. 234, 90–99. doi: 10.1016/j.apcatb.2018.04.036

CrossRef Full Text | Google Scholar

Hao, R., Wang, G., Jiang, C., Tang, H., and Xu, Q. (2017). In situ hydrothermal synthesis of g-C3N4/TiO2 heterojunction photocatalysts with high specific surface area for Rhodamine B degradation. Appl. Surf. Sci. 411, 400–410. doi: 10.1016/j.apsusc.2017.03.197

CrossRef Full Text | Google Scholar

Hao, R., Wang, G., Tang, H., Sun, L., Xu, C., and Han, D. (2016). Template-free preparation of macro/mesoporous g-C3N4/TiO2 heterojunction photocatalysts with enhanced visible light photocatalytic activity. Appl. Catal. B-Environ. 187, 47–58. doi: 10.1016/j.apcatb.2016.01.026

CrossRef Full Text | Google Scholar

He, Y., Wang, Y., Zhang, L., Teng, B., and Fan, M. (2015). High-efficiency conversion of CO2 to fuel over ZnO/g-C3N4 photocatalyst. Appl. Catal. B-Environ. 168, 1–8. doi: 10.1016/j.apcatb.2014.12.017

CrossRef Full Text | Google Scholar

Jiang, J., Zhang, X., Sun, P., and Zhang, L. (2011). ZnO/BiOI heterostructures: photoinduced charge-transfer property and enhanced visible-light photocatalytic activity. J. Phys. Chem. 115, 20555–20564. doi: 10.1021/jp205925z

CrossRef Full Text | Google Scholar

Jiang, R., Li, B., Fang, C., and Wang, J. (2014). Metal/semiconductor hybrid nanostructures for plasmon-enhanced applications. Adv. Mater. 26, 5274–5309. doi: 10.1002/adma.201400203

PubMed Abstract | CrossRef Full Text | Google Scholar

Li, S., Hu, S., Jiang, W., Liu, Y., Liu, Y., Zhou, Y., et al. (2018a). Ag3VO4 nanoparticles decorated Bi2O2CO3 micro-flowers: an efficient visible-light-driven photocatalyst for the removal of toxic contaminants. Front. Chem. 6:255. doi: 10.3389/fchem.2018.00255

PubMed Abstract | CrossRef Full Text | Google Scholar

Li, S., Jiang, W., Hu, S., Liu, Y., and Liu, J. (2018b). Construction of a novel ternary Ag/AgBr/Ag2WO4 composite for efficient photocatalytic removal of Rhodamine B dye and tetracycline hydrochloride antibiotic. Mater. Lett. 224, 29–32. doi: 10.1016/j.matlet.2018.04.071

CrossRef Full Text | Google Scholar

Li, W., Ma, Z., Bai, G., Hu, J., Guo, X., Dai, B., et al. (2015a). Dopamine-assisted one-step fabrication of Ag@ AgCl nanophotocatalyst with tunable morphology, composition and improved photocatalytic performance. Appl. Catal. B-Environ. 174, 43–48. doi: 10.1016/j.apcatb.2015.02.029

CrossRef Full Text | Google Scholar

Li, X., Fang, S., Ge, L., Han, C., Qiu, P., and Liu, W. (2015b). Synthesis of flower-like Ag/AgCl-Bi2MoO6 plasmonic photocatalysts with enhanced visible-light photocatalytic performance. Appl. Catal. B-Environ. 176-177, 62–69. doi: 10.1016/j.apcatb.2015.03.042

CrossRef Full Text | Google Scholar

Liu, R., Wang, P., Wang, X., Yu, H., and Yu, J. (2012). UV- and visible-light photocatalytic activity of simultaneously deposited and doped Ag/Ag(I)-TiO2 photocatalyst. J. Phys. Chem. C 116, 17721–17728. doi: 10.1021/jp305774n

CrossRef Full Text | Google Scholar

Lu, L., Wang, G., Zou, M., Wang, J., and Li, J. (2018). Effects of calcining temperature on formation of hierarchical TiO2/g-C3N4 hybrids as an effective Z-scheme heterojunction photocatalyst. Appl. Surf. Sci. 441, 1012–1023. doi: 10.1016/j.apsusc.2018.02.080

CrossRef Full Text | Google Scholar

Ma, L., Wang, G., Jiang, C., Bao, H., and Xu, Q. (2018). Synthesis of core-shell TiO2@g-C3N4 hollow microspheres for efficient photocatalytic degradation of rhodamine B under visible light. Appl. Surf. Sci. 430, 263–272. doi: 10.1016/j.apsusc.2017.07.282

CrossRef Full Text | Google Scholar

Ortíz-Oliveros, H. B., Flores-Espinosa, R. M., Ordoñez-Regil, E., and Fernández-Valverde, S. M. (2014). Synthesis of α-Ti(HPO4)2·H2O and sorption of Eu (III). Chem. Eng. J. 236, 398–405. doi: 10.1016/j.cej,0.2013.09.103

CrossRef Full Text | Google Scholar

Shi, W., Lv, H., Yuan, S., Huang, H., Liu, Y., and Kang, Z. (2016). Near-infrared light photocatalytic ability for degradation of tetracycline using carbon dots modified Ag/AgBr nanocomposites. Sep. Purif. Technol. 174, 75–83. doi: 10.1016/j.seppur.2016.10.005

CrossRef Full Text | Google Scholar

Sturini, M., Speltini, A., Maraschi, F., Profumo, A., Pretali, L., Irastorza, E. A., et al. (2012). Photolytic and photocatalytic degradation of fluoroquinolones in untreated river water under natural sunlight. Appl. Catal. B-Environ. 119–120, 32–39. doi: 10.1016/j.apcatb.2012.02.008

CrossRef Full Text | Google Scholar

Sun, Y., Xiao, X., Dong, X. A., Dong, F., and Zhang, W. (2017). Heterostructured BiOI@La(OH)3 nanorods with enhanced visible light photocatalytic NO removal. Chin. J. Catal. 38, 217–226. doi: 10.1016/S1872-2067(17)62753-0

CrossRef Full Text | Google Scholar

Tang, H., Chang, S., Tang, G., and Liang, W. (2017a). AgBr and g-C3N4 co-modified Ag2CO3 photocatalyst: a novel multi-heterostructured photocatalyst with enhanced photocatalytic activity. Appl. Surf. Sci. 391, 440–448. doi: 10.1016/j.apsusc.2016.07.021

CrossRef Full Text | Google Scholar

Tang, H., Fu, Y., Chang, S., Xie, S., and Tang, G. (2017b). Construction of Ag3PO4 /Ag2MoO4 Z-scheme heterogeneous photocatalyst for the remediation of organic pollutants. Chin. J. Catal. 38, 337–347. doi: 10.1016/S1872-2067(16)62570-6

CrossRef Full Text | Google Scholar

Wang, J., Wang, G., Wei, X., Liu, G., and Li, J. (2018). ZnO nanoparticles implanted in TiO2 macrochannels as an effective direct Z-scheme heterojunction photocatalyst for degradation of RhB. Appl. Surf. Sci. 456, 666–675. doi: 10.1016/j.apsusc.2018.06.182

CrossRef Full Text | Google Scholar

Wang, P., Huang, B., Qin, X., Zhang, X., Dai, Y., and Whangbo, M. H. (2009). Ag/AgBr/WO3·H2O: visible-light photocatalyst for bacteria destruction. Inorg. Chem. 48, 10697–10702. doi: 10.1021/ic9014652

PubMed Abstract | CrossRef Full Text | Google Scholar

Wang, Q., Yun, G., Bai, Y., Ning, A. N., Lian, J., Huang, H., et al. (2014). Photodegradation of rhodamine B with MoS2/Bi2O2CO3 composites under UV light irradiation. Appl. Surf. Sci. 313, 537–544. doi: 10.1016/j.apsusc.2014.06.018

CrossRef Full Text | Google Scholar

Wang, W., Cheng, H., Huang, B., Lin, X., Qin, X., Zhang, X., et al. (2013). Synthesis of Bi2O2CO3/Bi2S3 hierarchical microspheres with heterojunctions and their enhanced visible light-driven photocatalytic degradation of dye pollutants. J. Colloid Interface Sci. 402, 34–39. doi: 10.1016/j.jcis.2013.03.054

PubMed Abstract | CrossRef Full Text | Google Scholar

Wang, X., Li, T., Yu, R., Yu, H., and Yu, J. (2016). Highly efficient TiO2 single-crystal photocatalyst with spatially separated Ag and F-bi-cocatalysts: orientation transfer of photogenerated charges and their rapid interfacial reaction. J. Mater. Chem. A 4, 8682–8689. doi: 10.1039/C6TA02039A

CrossRef Full Text | Google Scholar

Xia, Y., and Halas, N. J. (2005). Shape-controlled synthesis and surface plasmonic properties of metallic nanostructures. Mrs. Bull. 30, 338–348. doi: 10.1557/mrs2005.96

CrossRef Full Text | Google Scholar

Xiang, Q., Yu, J., and Jaroniec, M. (2011). Preparation and enhanced visible-light photocatalytic H2-production activity of graphene/C3N4 composites. J. Phys. Chem. C 115, 7355–7363. doi: 10.1021/jp200953k

CrossRef Full Text | Google Scholar

Xiao, J. Q., Lin, K. S., and Yu, Y. (2018). Novel Ag@AgCl@AgBr heterostructured nanotubes as high-performance visible-light photocatalysts for decomposition of dyes. Catal. Today 314, 10–19. doi: 10.1016/j.cattod.2018.04.019

CrossRef Full Text | Google Scholar

Xu, Y., Xu, H., Yan, J., Li, H., Huang, L., Xia, J., et al. (2013). A plasmonic photocatalyst of Ag/AgBr nanoparticles coupled with g-C3N4 with enhanced visible-light photocatalytic ability. Colloid. Surface. A 436, 474–483. doi: 10.1016/j.colsurfa.2013.06.005

CrossRef Full Text | Google Scholar

Xuan, N. P., Ba, M. N., Thi, H. T., and Doan, H. V. (2018). Synthesis of Ag-AgBr/Al-MCM-41 nanocomposite and its application in photocatalytic oxidative desulfurization of dibenzothiophene. Adv. Powder Technol. 29, 1827–1837. doi: 10.1016/j.apt.2018.04.019

CrossRef Full Text | Google Scholar

Yada, M., Inoue, Y., Sakamoto, A., Torikai, T., and Watari, T. (2014). Synthesis and controllable wettability of micro-and nanostructured titanium phosphate thin films formed on titanium plates. Acs. Appl. Mater. Inter. 6, 7695–7704. doi: 10.1021/am500974v

PubMed Abstract | CrossRef Full Text | Google Scholar

Yang, X., Tang, H., Xu, J., Antonietti, M., and Shalom, M. (2015). Silver phosphate/graphitic carbon nitride as an efficient photocatalytic tandem system for oxygen evolution. ChemSusChem 8, 1350–1358. doi: 10.1002/cssc.201403168

PubMed Abstract | CrossRef Full Text | Google Scholar

Ye, L., Liu, J., Gong, C., Tian, L., Peng, T., and Zan, L. (2012). Two Different roles of metallic Ag on Ag/AgX/BiOX (X = Cl, Br) visible light photocatalysts: surface plasmon resonance and z-scheme bridge. ACS Catal. 2, 1677–1683. doi: 10.1021/cs300213m

CrossRef Full Text | Google Scholar

Zhang, L., Wang, G., Xiong, Z., Tang, H., and Jiang, C. (2018). Fabrication of flower-like direct Z-scheme β-Bi2O3/g-C3N4 photocatalyst with enhanced visible light photoactivity for Rhodamine B degradation. Appl. Surf. Sci. 436, 162–171. doi: 10.1016/j.apsusc.2017.11.280

CrossRef Full Text | Google Scholar

Zhang, W., Zhao, Z., Dong, F., and Zhang, Y. (2017). Solvent-assisted synthesis of porous g-C3N4 with efficient visible-light photocatalytic performance for NO removal. Chin. J. Catal. 38, 372–378. doi: 10.1016/S1872-2067(16)62585-8

CrossRef Full Text | Google Scholar

Zhang, X., Ai, Z., Falong Jia, A., and Zhang, L. (2008). Generalized one-pot synthesis, characterization, and photocatalytic activity of hierarchical BiOX (X = Cl, Br, I) nanoplate microspheres. J. Phys. Chem. C 112, 747–753. doi: 10.1021/jp077471t

CrossRef Full Text | Google Scholar

Zhang, X., Li, R., Jia, M., Wang, S., Huang, Y., and Chen, C. (2015a). Degradation of ciprofloxacin in aqueous bismuth oxybromide (BiOBr) suspensions under visible light irradiation: a direct hole oxidation pathway. Chem. Eng. J. 274, 290–297. doi: 10.1016/j.cej.2015.03.077

CrossRef Full Text | Google Scholar

Zhang, Y., Gu, J., Murugananthan, M., and Zhang, Y. (2015b). Development of novel α-Fe2O3 /NiTiO3 heterojunction nanofibers material with enhanced visible-light photocatalytic performance. J. Alloy. Compd. 630, 110–116. doi: 10.1016/j.jallcom.2014.12.193

CrossRef Full Text | Google Scholar

Zhang, Z., and Yates, J. T. (2012). Band bending in semiconductors: chemical and physical consequences at surfaces and interfaces. Chem. Rev. 112, 5520–5551. doi: 10.1021/cr3000626

PubMed Abstract | CrossRef Full Text | Google Scholar

Zhu, Y.-P., Ma, T.-Y., Ren, T.-Z., Li, J., Du, G.-H., and Yuan, Z.-Y. (2014). Highly dispersed photoactive zinc oxide nanoparticles on mesoporous phosphonated titania hybrid. Appl. Catal. B-Environ. 156–157, 44–52. doi: 10.1016/j.apcatb.2014.03.001

CrossRef Full Text | Google Scholar

Zou, J. P., Wu, D. D., Luo, J., Xing, Q. J., Luo, X. B., Dong, W. H., et al. (2016). A strategy for one-pot conversion of organic pollutants into useful hydrocarbons through coupling photodegradation of MB with photoreduction of CO2. ACS Catal. 6, 6861–6867. doi: 10.1021/acscatal.6b01729

CrossRef Full Text | Google Scholar

Keywords: heterojunction, titanium phosphate, AgBr@Ag, photocatalysis, visible light

Citation: Ren M, Bao J, Wang P, Wang C and Ao Y (2018) Titanium Phosphate Nanoplates Modified With AgBr@Ag Nanoparticles: A Novel Heterostructured Photocatalyst With Significantly Enhanced Visible Light Responsive Activity. Front. Chem. 6:489. doi: 10.3389/fchem.2018.00489

Received: 17 July 2018; Accepted: 25 September 2018;
Published: 17 October 2018.

Edited by:

Fan Dong, Chongqing Technology and Business University, China

Reviewed by:

Guohong Wang, Hubei Normal University, China
Qizhao Wang, Northwest Normal University, China

Copyright © 2018 Ren, Bao, Wang, Wang and Ao. This is an open-access article distributed under the terms of the Creative Commons Attribution License (CC BY). The use, distribution or reproduction in other forums is permitted, provided the original author(s) and the copyright owner(s) are credited and that the original publication in this journal is cited, in accordance with accepted academic practice. No use, distribution or reproduction is permitted which does not comply with these terms.

*Correspondence: Yanhui Ao, andyao@hhu.edu.cn

Disclaimer: All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article or claim that may be made by its manufacturer is not guaranteed or endorsed by the publisher.